Introduction. Photoresist : Type: Structure:
|
|
- Reynard Merritt
- 6 years ago
- Views:
Transcription
1 Photoresist SEM images of the morphologies of meso structures and nanopatterns on (a) a positively nanopatterned silicon mold, and (b) a negatively nanopatterned silicon mold.
2 Introduction Photoresist : A photoresist is a light-sensitive material used in several industrial processes, such as photolithography and photoengraving to form a patterned coating on a surface. Type: Positive: exposed regions dissolve (best resolution) Negative: Unexposed regions dissolve ( Swelling) Structure: Resin: a binder that provides mechanical properties (adhesion, chemical resistance) Solvent: used to dissolve the resin, allowing the resin to be applied in a liquid state Photoactive Compound (PAC): Act to inhibit or promote the dissolution of the resin in the developer. PAC inhibits dissolution in positive
3 Positive Photoresist Chemistry Two-component DQN resists: DQN, corresponding to the photo-active compound, diazoquinone (DQ) and resin, novolac (N) Dominant for G-line (436nm) and I- line (365nm) exposure and not suitable for very short wavelength exposures Novolac (N): a polymer whose monomer is an aromatic ring with two methyl groups and an OH group. dissolves in an aqueous solution easily Diazoquinone(DQ) UV % Carboxylic weight acid ( dissolution enhancer) Photosensitive
4 Positive Chemistry 1. Photoresist DQ molecule will not dissolve in a base developer solution (ph >7). 2. UV light breaks the nitrogen molecule off forming an unstable molecule 2. To stabilize itself, one of the 6 carbon atoms in the ring pops out of the ring (leaving 5) 3. Once exposed to water (a developer /water mixture), an OH group attaches to the carbon atom, forming an acid. 4. The acid can then react and dissolve with the basic developer solution. Advantage: Unexposed areas unchanged by the presence of the developer, line width and shape of a pattern precisely retained. Novolac fairly resistant chemical attack, a good mask for the subsequent plasma etching
5 Photoresist material parameters a) Optical properties - resolution, photosensitivity, and index of refraction b) Mechanical/chemical properties - solids content, viscosity, adhesion, etch resistance, thermal stability, flow characteristics, and sensitivity to ambient gases c) Processing and safety related properties - including, cleanliness (particle count), metals content, process latitude, and shelf life. Resolution - specifies the consistent ability to print minimum size images under conditions of reasonable manufacturing variation. The resolution of a lithographic process can be limited by many aspects of the process, including: a) Hardware (e.g. diffraction of light, lens aberrations)
6 Performance of Photoresists Resolution (µm) - linearity/ minimum Sensitivity (mj/cm2) Focus margin (µm) Exposure margin (%) Dry etch resistance(x) Heat resistance Adhesion Standing wave effect (and bulk effect) (µm) BARC (bottom anti-reflective coating) compatibility Process margin/stability Photoresists Profile Shelf-life * Han Ku Cho, Samsung Electronics Co., Ltd, Lithography technology review of what it is and what to be, March 2003
7 Deep UV Photoresist Limitation of Novolac based Photoresist Strongly absorb below 250nm, KrF (248nm) marginally acceptable but not ArF (193nm) Photoresist Solution for Submicron Features PMMA PAGs ( Photoacid generator) replace PAC Contrast enhancement layers (CELs) Inorganic resist (Ag-doped Ge-Se) Silicon-containing resists (dry developable) Multi-layer photoresist
8 PMMA (Polymethyl methacrylate) Short-wavelength lithography: deep UV, extreme UV, electron-beam lithography Resin itself is photosensitive Advantage: high resolution Disadvantage: Plasma etch tolerance is very low and thick PMMA to protect the thin film Dissociation changes chemistry of the plasma etch and polymeric deposits on the surface of the substrate. Low sensitivity: Add PAG (chemically reactive dissociating) or elevate exposure temperature *Stephen A. Campbell, The Science and Engineering of Microelectronic Fabrication.
9 Contrast Enhance Layers (CELs) CEM photo-bleachable Spun onto the DQN PR after softbake Formed in-situ conformal contact mask Enhanced contrast Important for DUV resists with less optical intense and PR radiation absorption * %20Data%20Sheet%
10 Inorganic Resist Advantage: High contrast γ 7 Produce fine line Process: Ag-doped Ge-Se Ag plated on sputtered Ge-Se Photodoping create Ag2Se after exposure Dissolved in alkaline solution Disadvantage: Require thick planarizing underlayer due to thin film nature Pineholes and defects from Ge-Se *Stephen A. Campbell, The Science and Engineering of Microelectronic
11 Dry developable: Polysilynes Bi-layer process Silicon-containing resists on top of novolac based resist Highly resistant to plasma process Bleaching under DUV exposure due to cross-linked siloxane network Etch silicon selectively to silicon dioxide in HBr plasma * Roderick R. Kunz, et al, 193 nm Resists and Lithography, Polymers for Advanced Technologies, Volume 5, p p.12-21
12 Thank you
Lecture 8. Photoresists and Non-optical Lithography
Lecture 8 Photoresists and Non-optical Lithography Reading: Chapters 8 and 9 and notes derived from a HIGHLY recommended book by Chris Mack, Fundamental Principles of Optical Lithography. Any serious student
More informationOptical Proximity Correction
Optical Proximity Correction Mask Wafer *Auxiliary features added on mask 1 Overlay Errors + + alignment mask wafer + + photomask plate Alignment marks from previous masking level 2 (1) Thermal run-in/run-out
More informationUNIT 3. By: Ajay Kumar Gautam Asst. Prof. Dev Bhoomi Institute of Technology & Engineering, Dehradun
UNIT 3 By: Ajay Kumar Gautam Asst. Prof. Dev Bhoomi Institute of Technology & Engineering, Dehradun 1 Syllabus Lithography: photolithography and pattern transfer, Optical and non optical lithography, electron,
More informationPhotolithography 光刻 Part II: Photoresists
微纳光电子材料与器件工艺原理 Photolithography 光刻 Part II: Photoresists Xing Sheng 盛兴 Department of Electronic Engineering Tsinghua University xingsheng@tsinghua.edu.cn 1 Photolithography 光刻胶 负胶 正胶 4 Photolithography
More informationPhotolithography Overview 9/29/03 Brainerd/photoclass/ECE580/Overvie w/overview
http://www.intel.com/research/silicon/mooreslaw.htm 1 Moore s law only holds due to photolithography advancements in reducing linewidths 2 All processing to create electric components and circuits rely
More informationIntroduction to Photolithography
http://www.ichaus.de/news/72 Introduction to Photolithography Photolithography The following slides present an outline of the process by which integrated circuits are made, of which photolithography is
More informationDevelopment of Lift-off Photoresists with Unique Bottom Profile
Transactions of The Japan Institute of Electronics Packaging Vol. 8, No. 1, 2015 [Technical Paper] Development of Lift-off Photoresists with Unique Bottom Profile Hirokazu Ito, Kouichi Hasegawa, Tomohiro
More informationNanostructures Fabrication Methods
Nanostructures Fabrication Methods bottom-up methods ( atom by atom ) In the bottom-up approach, atoms, molecules and even nanoparticles themselves can be used as the building blocks for the creation of
More informationMEEN Nanoscale Issues in Manufacturing. Lithography Lecture 1: The Lithographic Process
MEEN 489-500 Nanoscale Issues in Manufacturing Lithography Lecture 1: The Lithographic Process 1 Discuss Reading Assignment 1 1 Introducing Nano 2 2 Size Matters 3 3 Interlude One-The Fundamental Science
More informationTop down and bottom up fabrication
Lecture 24 Top down and bottom up fabrication Lithography ( lithos stone / graphein to write) City of words lithograph h (Vito Acconci, 1999) 1930 s lithography press Photolithography d 2( NA) NA=numerical
More informationLecture 14 Advanced Photolithography
Lecture 14 Advanced Photolithography Chapter 14 Wolf and Tauber 1/74 Announcements Term Paper: You are expected to produce a 4-5 page term paper on a selected topic (from a list). Term paper contributes
More informationComposition and Photochemical Mechanisms of Photoresists
OpenStax-CNX module: m25525 1 Composition and Photochemical Mechanisms of Photoresists Andrew R. Barron This work is produced by OpenStax-CNX and licensed under the Creative Commons Attribution License
More informationNanotechnology Fabrication Methods.
Nanotechnology Fabrication Methods. 10 / 05 / 2016 1 Summary: 1.Introduction to Nanotechnology:...3 2.Nanotechnology Fabrication Methods:...5 2.1.Top-down Methods:...7 2.2.Bottom-up Methods:...16 3.Conclusions:...19
More informationFabrication of Sub-Quarter-Micron Grating Patterns by Employing Lithography
MCROU,!~'O~C ELSEVER Microelectronic Engineering 46 (1999) 173-177 Fabrication of Sub-Quarter-Micron Grating Patterns by Employing Lithography DUV Holographic L. A. Wang*, C. H. Lin and J. H. Chen nstitute
More informationDQN Positive Photoresist
UNIVESITY OF CALIFONIA, BEKELEY BEKELEY DAVIS IVINE LOS ANGELES IVESIDE SAN DIEGO SAN FANCISCO SANTA BABAA SANTA CUZ DEPATMENT OF BIOENGINEEING 94720-1762 BioE 121 Midterm #1 Solutions BEKELEY, CALIFONIA
More informationTechniken der Oberflächenphysik (Techniques of Surface Physics)
Techniken der Oberflächenphysik (Techniques of Surface Physics) Prof. Yong Lei & Dr. Yang Xu (& Liying Liang) Fachgebiet 3D-Nanostrukturierung, Institut für Physik Contact: yong.lei@tu-ilmenau.de; yang.xu@tu-ilmenau.de;
More informationOverview of the main nano-lithography techniques
Overview of the main nano-lithography techniques Soraya Sangiao sangiao@unizar.es Outline Introduction: Nanotechnology. Nano-lithography techniques: Masked lithography techniques: Photolithography. X-ray
More information5. Photochemistry of polymers
5. Photochemistry of polymers 5.1 Photopolymerization and cross-linking Photopolymerization The fundamental principle of photopolymerization is based on the photoinduced production of a reactive species,
More informationFabrication Engineering at the Micro- and Nanoscale, by Stephen Campbell, 4 th Edition, Oxford University Press
Fabrication Engineering at the Micro- and Nanoscale, by Stephen Campbell, 4 th Edition, Oxford University Press Errata, by Chris Mack, chris@lithoguru.com While teaching out of this book at the University
More informationJ. Photopolym. Sci. Technol., Vol. 22, No. 5, Fig. 1. Orthogonal solvents to conventional process media.
originates from the limited number of options regarding orthogonal solvents, i.e. solvents that do not dissolve or adversely damage a pre-deposited organic materials layer. The simplest strategy to achieve
More information520/ Photolithography (II) Andreas G. Andreou
520/580.495 Photolithography (II) Andreas G. Andreou Lecture notes from Positive Photoresists and Photolithography by R. Darling http://www.engr.washington.edu/~cam/processes A.G. Andreou 2000 1 Lecture
More informationUNIVERSITY OF CALIFORNIA College of Engineering Department of Electrical Engineering and Computer Sciences. Professor Ali Javey. Fall 2009.
UNIVERSITY OF CALIFORNIA College of Engineering Department of Electrical Engineering and Computer Sciences EE143 Professor Ali Javey Fall 2009 Exam 1 Name: SID: Closed book. One sheet of notes is allowed.
More informationUNIVERSITY OF CALIFORNIA College of Engineering Department of Electrical Engineering and Computer Sciences. Professor Ali Javey. Spring 2009.
UNIVERSITY OF CALIFORNIA College of Engineering Department of Electrical Engineering and Computer Sciences EE143 Professor Ali Javey Spring 2009 Exam 1 Name: SID: Closed book. One sheet of notes is allowed.
More informationChapter 3 : ULSI Manufacturing Technology - (c) Photolithography
Chapter 3 : ULSI Manufacturing Technology - (c) Photolithography 1 Reference 1. Semiconductor Manufacturing Technology : Michael Quirk and Julian Serda (2001) 2. - (2004) 3. Semiconductor Physics and Devices-
More informationUNIVERSITY OF CALIFORNIA College of Engineering Department of Electrical Engineering and Computer Sciences. Fall Exam 1
UNIVERSITY OF CALIFORNIA College of Engineering Department of Electrical Engineering and Computer Sciences EECS 143 Fall 2008 Exam 1 Professor Ali Javey Answer Key Name: SID: 1337 Closed book. One sheet
More informationSupplementary Information
ature anotechnology reference number: AO-06110617A Growth and alignment of polyaniline nanofibres with superhydrophobic, superhydrophilic and other properties an-rong Chiou 1,2,3, Chunmeng Lu 1, Jingjiao
More informationPattern Transfer- photolithography
Pattern Transfer- photolithography DUV : EUV : 13 nm 248 (KrF), 193 (ArF), 157 (F 2 )nm H line: 400 nm I line: 365 nm G line: 436 nm Wavelength (nm) High pressure Hg arc lamp emission Ref: Campbell: 7
More informationLithographic Effects Of Acid Diffusion In Chemically Amplified Resists
INTERFACE '95 This paper was published in the proceedings of the OCG Microlithography Seminar, Interface '95, pp. 217-228. It is made available as an electronic reprint with permission of OCG Microelectronic
More information4FNJDPOEVDUPS 'BCSJDBUJPO &UDI
2010.5.4 1 Major Fabrication Steps in CMOS Process Flow UV light oxygen Silicon dioxide Silicon substrate Oxidation (Field oxide) photoresist Photoresist Coating Mask exposed photoresist Mask-Wafer Exposed
More informationEnhanced Transmission by Periodic Hole. Arrays in Metal Films
Enhanced Transmission by Periodic Hole Arrays in Metal Films K. Milliman University of Florida July 30, 2008 Abstract Three different square periodic hole arrays were manufactured on a silver film in order
More informationCurrent Status of Inorganic Nanoparticle Photoresists
Prof. Christopher K. ber Department of Materials Science and Engineering, Cornell University, Ithaca NY Current Status of Inorganic Nanoparticle Photoresists Markos Trikeriotis, Marie Krysak, Yeon Sook
More informationWhite Paper Adhesives Sealants Tapes
Fundamental principles of UV reactive manufacturing processes Introduction While the UV systems technology and the appropriate chemistry have been developing continuously, the principle of irradiation
More informationPhotolithography II ( Part 1 )
1 Photolithography II ( Part 1 ) Chapter 14 : Semiconductor Manufacturing Technology by M. Quirk & J. Serda Bjørn-Ove Fimland, Department of Electronics and Telecommunication, Norwegian University of Science
More informationSwing Curves. T h e L i t h o g r a p h y T u t o r (Summer 1994) Chris A. Mack, FINLE Technologies, Austin, Texas
T h e L i t h o g r a p h y T u t o r (Summer 1994) Swing Curves Chris A. Mack, FINLE Technologies, Austin, Texas In the last edition of this column, we saw that exposing a photoresist involves the propagation
More informationnmos IC Design Report Module: EEE 112
nmos IC Design Report Author: 1302509 Zhao Ruimin Module: EEE 112 Lecturer: Date: Dr.Zhao Ce Zhou June/5/2015 Abstract This lab intended to train the experimental skills of the layout designing of the
More informationA Photonic Crystal Laser from Solution Based. Organo-Lead Iodide Perovskite Thin Films
SUPPORTING INFORMATION A Photonic Crystal Laser from Solution Based Organo-Lead Iodide Perovskite Thin Films Songtao Chen 1, Kwangdong Roh 2, Joonhee Lee 1, Wee Kiang Chong 3,4, Yao Lu 5, Nripan Mathews
More informationNano Materials. Nanomaterials
Nano Materials 1 Contents Introduction Basics Synthesis of Nano Materials Fabrication of Nano Structure Nano Characterization Properties and Applications 2 Fabrication of Nano Structure Lithographic techniques
More informationIC Fabrication Technology
IC Fabrication Technology * History: 1958-59: J. Kilby, Texas Instruments and R. Noyce, Fairchild * Key Idea: batch fabrication of electronic circuits n entire circuit, say 10 7 transistors and 5 levels
More informationSupplementary Figure 1 Detailed illustration on the fabrication process of templatestripped
Supplementary Figure 1 Detailed illustration on the fabrication process of templatestripped gold substrate. (a) Spin coating of hydrogen silsesquioxane (HSQ) resist onto the silicon substrate with a thickness
More informationLECTURE 5 SUMMARY OF KEY IDEAS
LECTURE 5 SUMMARY OF KEY IDEAS Etching is a processing step following lithography: it transfers a circuit image from the photoresist to materials form which devices are made or to hard masking or sacrificial
More informationPhotonics applications 5: photoresists
IMI-NFG s Mini Course on Chalcogenide Glasses Lecture 11 Photonics applications 5: photoresists Himanshu Jain Department of Materials Science & Engineering Lehigh University, Bethlehem, PA 18015 H.Jain@Lehigh.edu
More informationDevelopment of Photosensitive Polyimides for LCD with High Aperture Ratio. May 24, 2004
Development of Photosensitive Polyimides for LCD with High Aperture Ratio May 24, 2004 utline Why is polymer dielectric required for TFT LCD? Requirements of the polymer dielectrics What is polyimide?
More informationWoo Jin Hyun, Ethan B. Secor, Mark C. Hersam, C. Daniel Frisbie,* and Lorraine F. Francis*
Woo Jin Hyun, Ethan B. Secor, Mark C. Hersam, C. Daniel Frisbie,* and Lorraine F. Francis* Dr. W. J. Hyun, Prof. C. D. Frisbie, Prof. L. F. Francis Department of Chemical Engineering and Materials Science
More informationSimulation Based Formulation of a Non-Chemically Amplified Resist for 257 nm Laser Mask Fabrication
Simulation Based Formulation of a Non-Chemically Amplified Resist for 257 nm Laser Mask Fabrication Benjamen M. Rathsack, Cyrus E. Tabery, Timothy B. Stachowiak, Jeff Albelo 2 and C. Grant Willson Department
More informationNano fabrication by e-beam lithographie
Introduction to nanooptics, Summer Term 2012, Abbe School of Photonics, FSU Jena, Prof. Thomas Pertsch Nano fabrication by e-beam lithographie Lecture 14 1 Electron Beam Lithography - EBL Introduction
More informationFar IR Gas Lasers microns wavelengths, THz frequency Called Terahertz lasers or FIR lasers At this wavelength behaves more like
Far IR Gas Lasers 10-1500 microns wavelengths, 300 10 THz frequency Called Terahertz lasers or FIR lasers At this wavelength behaves more like microwave signal than light Created by Molecular vibronic
More informationTechnology offer: Environmentally friendly holographic recording material
Technology offer: Environmentally friendly holographic recording material Technology offer: Environmentally friendly holographic recording material SUMMARY Our research group has developed a new photopolymer
More informationFEM Modeling of Shrinkage Effects in Negative Tone Photoresists
FEM Modeling of Shrinkage Effects in Negative Tone Photoresists Master s Thesis/Masterarbeit in the field of Computational Engineering by Sean Dominic D Silva Department Informatik Lehrstuhl für Informatik
More informationSilicon VLSI Technology. Fundamentals, Practice and Modeling
Text Book: Silicon VLSI Technology Fundamentals, Practice and Modeling Authors: J. D. Plummer, M. D. Deal, and P. B. Griffin Photolithography (Chap. 1) Basic lithography process Apply photoresist Patterned
More informationTable of Contents. Foreword... Jörge DE SOUSA NORONHA. Introduction... Michel BRILLOUËT
Table of Contents Foreword... Jörge DE SOUSA NORONHA Introduction... Michel BRILLOUËT xi xvii Chapter 1. Photolithography... 1 Philippe BANDELIER, Anne-Laure CHARLEY and Alexandre LAGRANGE 1.1. Introduction...
More informationEE C245 ME C218 Introduction to MEMS Design Fall 2007
EE C245 ME C218 Introduction to MEMS Design Fall 2007 Prof. Clark T.-C. Nguyen Dept. of Electrical Engineering & Computer Sciences University of California at Berkeley Berkeley, CA 94720 Lecture 5: ALD,
More informationMICRO AND NANOPROCESSING TECHNOLOGIES
LECTURE 5 MICRO AND NANOPROCESSING TECHNOLOGIES Introduction Ion lithography X-ray lithography Soft lithography E-beam lithography Concepts and processes Lithography systems Masks and resists Chapt.9.
More informationSupplementary Information Our InGaN/GaN multiple quantum wells (MQWs) based one-dimensional (1D) grating structures
Polarized white light from hybrid organic/iii-nitrides grating structures M. Athanasiou, R. M. Smith, S. Ghataora and T. Wang* Department of Electronic and Electrical Engineering, University of Sheffield,
More informationCase Study of Electronic Materials Packaging with Poor Metal Adhesion and the Process for Performing Root Cause Failure Analysis
Case Study of Electronic Materials Packaging with Poor Metal Adhesion and the Process for Performing Root Cause Failure Analysis Dr. E. A. Leone BACKGRUND ne trend in the electronic packaging industry
More informationCURRENT STATUS OF NANOIMPRINT LITHOGRAPHY DEVELOPMENT IN CNMM
U.S. -KOREA Forums on Nanotechnology 1 CURRENT STATUS OF NANOIMPRINT LITHOGRAPHY DEVELOPMENT IN CNMM February 17 th 2005 Eung-Sug Lee,Jun-Ho Jeong Korea Institute of Machinery & Materials U.S. -KOREA Forums
More informationFabrication of ordered array at a nanoscopic level: context
Fabrication of ordered array at a nanoscopic level: context Top-down method Bottom-up method Classical lithography techniques Fast processes Size limitations it ti E-beam techniques Small sizes Slow processes
More informationIntroduction to Electron Beam Lithography
Introduction to Electron Beam Lithography Boštjan Berčič (bostjan.bercic@ijs.si), Jožef Štefan Institute, Jamova 39, 1000 Ljubljana, Slovenia 1. Introduction Electron Beam Lithography is a specialized
More informationNanotechnology Nanofabrication of Functional Materials. Marin Alexe Max Planck Institute of Microstructure Physics, Halle - Germany
Nanotechnology Nanofabrication of Functional Materials Marin Alexe Max Planck Institute of Microstructure Physics, Halle - Germany Contents Part I History and background to nanotechnology Nanoworld Nanoelectronics
More informationETCHING Chapter 10. Mask. Photoresist
ETCHING Chapter 10 Mask Light Deposited Substrate Photoresist Etch mask deposition Photoresist application Exposure Development Etching Resist removal Etching of thin films and sometimes the silicon substrate
More informationDainippon Screen Mfg. Co., Ltd , Takamiya, Hikone, Shiga , Japan. IMEC vzw, Kapeldreef 75, B-3001 Leuven, Belgium
Solid State Phenomena Vols. 145-146 (2009) pp 285-288 Online available since 2009/Jan/06 at www.scientific.net (2009) Trans Tech Publications, Switzerland doi:10.4028/www.scientific.net/ssp.145-146.285
More informationStudy on Improved Resolution of Thick Film Resist (Verification by Simulation)
Study on Improved Resolution of Thick Film Resist (Verification by Simulation) Yoshihisa Sensu, Atsushi Sekiguchi, Yasuhiro Miyake Litho Tech Japan Corporation 2-6-6 Namiki, Kawaguchi, Saitama, 332-0034,
More informationEUV Reflectometry for Determining the Optical Properties of Photoresists and Underlayer Materials Upon Irradiation at 13.5-nm
EUV Reflectometry for Determining the Optical Properties of Photoresists and Underlayer Materials Upon Irradiation at 13.5-nm Grace H. Ho, 1 Fu-H. Kang, 1 Yu-H. Shih, 1 Hok-S. Fung, Hwang-W. Fu, Rikimaru
More informationUHF-ECR Plasma Etching System for Dielectric Films of Next-generation Semiconductor Devices
UHF-ECR Plasma Etching System for Dielectric Films of Next-generation Semiconductor Devices 1 UHF-ECR Plasma Etching System for Dielectric Films of Next-generation Semiconductor Devices Katsuya Watanabe
More informationSupporting Information. Fast Synthesis of High-Performance Graphene by Rapid Thermal Chemical Vapor Deposition
1 Supporting Information Fast Synthesis of High-Performance Graphene by Rapid Thermal Chemical Vapor Deposition Jaechul Ryu, 1,2, Youngsoo Kim, 4, Dongkwan Won, 1 Nayoung Kim, 1 Jin Sung Park, 1 Eun-Kyu
More informationFormation and Surface Modification of Nanopatterned Thiol-ene Substrates using
Supporting Information Formation and Surface Modification of Nanopatterned Thiol-ene Substrates using Step and Flash Imprint Lithography Vaibhav S. Khire, 1 Youngwoo Yi, 2 Noel A. Clark, 2 and Christopher
More informationPhotoresist Profile. Undercut: negative slope, common for negative resist; oxygen diffusion prohibits cross-linking; good for lift-off.
Photoresist Profile 4-15 Undercut: negative slope, common for negative resist; oxygen diffusion prohibits cross-linking; good for lift-off undercut overcut Overcut: positive slope, common to positive resist,
More informationAdvanced Pharmaceutical Analysis
Lecture 2 Advanced Pharmaceutical Analysis IR spectroscopy Dr. Baraa Ramzi Infrared Spectroscopy It is a powerful tool for identifying pure organic and inorganic compounds. Every molecular compound has
More informationBasic Principles. Fundamental principles of UV reactive manufacturing processes
Basic Principles Fundamental principles of UV reactive manufacturing processes The Basics Fundamental principles of UV reactive manufacturing processes Chemical curing While the UV systems technology and
More informationA Novel Self-aligned and Maskless Process for Formation of Highly Uniform Arrays of Nanoholes and Nanopillars
Nanoscale Res Lett (2008) 3: 127 DOI 10.1007/s11671-008-9124-6 NANO EXPRESS A Novel Self-aligned and Maskless Process for Formation of Highly Uniform Arrays of Nanoholes and Nanopillars Wei Wu Æ Dibyendu
More informationCopyright 1999 by the Society of Photo-Optical Instrumentation Engineers.
Copyright 1999 by the Society of Photo-Optical Instrumentation Engineers. This paper was published in the proceedings of Advances in Resist Technology and Processing XVI, SPIE Vol. 3678, pp. 1-1011. It
More informationPlasma Deposition (Overview) Lecture 1
Plasma Deposition (Overview) Lecture 1 Material Processes Plasma Processing Plasma-assisted Deposition Implantation Surface Modification Development of Plasma-based processing Microelectronics needs (fabrication
More informationAdhesion Improvement on Smooth Cu Wiring Surfaces of Printed Circuit Boards
[Technical Paper] Adhesion Improvement on Smooth Cu Wiring Surfaces of Printed Circuit Boards Motoaki Tani*, Shinya Sasaki*, and Keisuke Uenishi** *Next-Generation Manufacturing Technologies Research Center,
More informationClean-Room microfabrication techniques. Francesco Rizzi Italian Institute of Technology
Clean-Room microfabrication techniques Francesco Rizzi Italian Institute of Technology Miniaturization The first transistor Miniaturization The first transistor Miniaturization The first transistor Miniaturization
More informationNext: 193nm Lithography
Lecture 16 Chemical Engineering for Micro/Nano Fabrication Next: 193nm Lithography Absorption coefficient [1/µm] Absorption of Photoresist Polymers 2.8 Poly-(4-hydroxystyrene) 2.4 Meta-cresol novolak 2.0
More informationFar IR (FIR) Gas Lasers microns wavelengths, THz frequency Called Terahertz lasers or FIR lasers At this wavelength behaves more like
Far IR (FIR) Gas Lasers 10-1500 microns wavelengths, 300 10 THz frequency Called Terahertz lasers or FIR lasers At this wavelength behaves more like microwave signal than light Created by Molecular vibronic
More informationNanosphere Lithography
Nanosphere Lithography Derec Ciafre 1, Lingyun Miao 2, and Keita Oka 1 1 Institute of Optics / 2 ECE Dept. University of Rochester Abstract Nanosphere Lithography is quickly emerging as an efficient, low
More informationLecture 150 Basic IC Processes (10/10/01) Page ECE Analog Integrated Circuits and Systems P.E. Allen
Lecture 150 Basic IC Processes (10/10/01) Page 1501 LECTURE 150 BASIC IC PROCESSES (READING: TextSec. 2.2) INTRODUCTION Objective The objective of this presentation is: 1.) Introduce the fabrication of
More informationKavli Workshop for Journalists. June 13th, CNF Cleanroom Activities
Kavli Workshop for Journalists June 13th, 2007 CNF Cleanroom Activities Seeing nm-sized Objects with an SEM Lab experience: Scanning Electron Microscopy Equipment: Zeiss Supra 55VP Scanning electron microscopes
More informationResist material for negative tone development process
Resist material for negative tone development process FUJIFILM Corporation Electronic Materials Research Laboratories P-1 Outline 1. Advantages of negative tone imaging for DP 2. Process maturity of negative
More informationMonte Carlo simulation and experimental study of stopping power of lithography resist and its application in development of a CMOS/EE process
Monte Carlo simulation and experimental study of stopping power of lithography resist and its application in development of a CMOS/EE process Predrag Habaš, Roman Stapor, Alexandre Acovic and Maurice Lobet
More informationFigure 1: Graphene release, transfer and stacking processes. The graphene stacking began with CVD
Supplementary figure 1 Graphene Growth and Transfer Graphene PMMA FeCl 3 DI water Copper foil CVD growth Back side etch PMMA coating Copper etch in 0.25M FeCl 3 DI water rinse 1 st transfer DI water 1:10
More informationThe Monte Carlo Simulation of Secondary Electrons Excitation in the Resist PMMA
Applied Physics Research; Vol. 6, No. 3; 204 ISSN 96-9639 E-ISSN 96-9647 Published by Canadian Center of Science and Education The Monte Carlo Simulation of Secondary Electrons Excitation in the Resist
More informationExploration of non-chemically amplified resists based on chain-scission mechanism for 193 nm lithography
Rochester Institute of Technology RIT Scholar Works Theses Thesis/Dissertation Collections 2010 Exploration of non-chemically amplified resists based on chain-scission mechanism for 193 nm lithography
More informationPolymeric microelement on the top of the fiber formation and optical loss in this element analysis
Vol.2, No.8, 868-872 (2010) http://dx.doi.org/10.4236/ns.2010.28109 Natural Science Polymeric microelement on the top of the fiber formation and optical loss in this element analysis Maria I. Fokina, Nina
More informationThe Solubility is the Solution
The Solubility is the Solution The Company BellandTechnology AG is a polymer technology company, originally founded in Switzerland 1983. BellandTechnology developed a proprietary selectively soluble polymer
More informationSelf-study problems and questions Processing and Device Technology, FFF110/FYSD13
Self-study problems and questions Processing and Device Technology, FFF110/FYSD13 Version 2016_01 In addition to the problems discussed at the seminars and at the lectures, you can use this set of problems
More informationEFFECT OF NANOSCALE CONFINEMENT ON THE PHYSICAL PROPERTIES OF POLYMER THIN FILMS
EFFECT OF NANOSCALE CONFINEMENT ON THE PHYSICAL PROPERTIES OF POLYMER THIN FILMS A Thesis Presented to The Academic Faculty by Lovejeet Singh In Partial Fulfillment of the Requirements for the Degree Doctor
More informationLithography and Etching
Lithography and Etching Victor Ovchinnikov Chapters 8.1, 8.4, 9, 11 Previous lecture Microdevices Main processes: Thin film deposition Patterning (lithography) Doping Materials: Single crystal (monocrystal)
More informationEtching Issues - Anisotropy. Dry Etching. Dry Etching Overview. Etching Issues - Selectivity
Etching Issues - Anisotropy Dry Etching Dr. Bruce K. Gale Fundamentals of Micromachining BIOEN 6421 EL EN 5221 and 6221 ME EN 5960 and 6960 Isotropic etchants etch at the same rate in every direction mask
More informationSimulation and characterization of surface and line edge roughness in photoresists before and after etching
Simulation and characterization of surface and line edge roughness in photoresists before and after etching Motivation of this work : Sub 100nm lithographic features often suffer from roughness. Need to
More information(c) Dr. Payal B. Joshi
Polymer (Greek: poly=many; mer=part) Made up of large molecules characterized by repeating units called monomers held together by covalent bonds Functionality To act as monomer, it must have at least two
More informationDUV ( nm ) Characterization of Materials: A new instrument, the Purged UV Spectroscopic Ellipsometer,
WISE 2000, International Workshop on Spectroscopic Ellipsometry, 8 9 May 2000 DUV (150 350nm ) Characterization of Materials: A new instrument, the Purged UV Spectroscopic Ellipsometer, Pierre BOHER,,
More informationEncapsulation. Battelle Technology. Introduction
Encapsulation Introduction The encapsulation methods reported in the literature 1-7 for the production of microcapsules are generally achieved using one of the following techniques: 1. Phase separation
More informationEE-612: Lecture 22: CMOS Process Steps
EE-612: Lecture 22: CMOS Process Steps Mark Lundstrom Electrical and Computer Engineering Purdue University West Lafayette, IN USA Fall 2006 NCN www.nanohub.org Lundstrom EE-612 F06 1 outline 1) Unit Process
More informationEE115C Winter 2017 Digital Electronic Circuits. Lecture 3: MOS RC Model, CMOS Manufacturing
EE115C Winter 2017 Digital Electronic Circuits Lecture 3: MOS RC Model, CMOS Manufacturing Agenda MOS Transistor: RC Model (pp. 104-113) S R on D CMOS Manufacturing Process (pp. 36-46) S S C GS G G C GD
More informationTitel van de presentatie :41
, TNO, Senior Scientist Sensor Materials Photonic Crystals as Gas and Liquid Sensors 1 Competence matrix Sector R&D Technology Application Market Photonics for green energy & environment Lighting for well
More informationEE 434 Lecture 7. Process Technology
EE 434 Lecture 7 Process Technology Quiz 4 How many wafers can be obtained from a 2m pull? Neglect the material wasted in the kerf used to separate the wafers. 2m And the number is. 1 8 3 5 6 4 9 7 2 1
More informationAdvanced Texturing of Si Nanostructures on Low Lifetime Si Wafer
Advanced Texturing of Si Nanostructures on Low Lifetime Si Wafer SUHAILA SEPEAI, A.W.AZHARI, SALEEM H.ZAIDI, K.SOPIAN Solar Energy Research Institute (SERI), Universiti Kebangsaan Malaysia (UKM), 43600
More informationSupplementary Information. High-Performance, Transparent and Stretchable Electrodes using. Graphene-Metal Nanowire Hybrid Structures
Supplementary Information High-Performance, Transparent and Stretchable Electrodes using Graphene-Metal Nanowire Hybrid Structures Mi-Sun Lee, Kyongsoo Lee, So-Yun Kim, Heejoo Lee, Jihun Park, Kwang-Hyuk
More informationDeveloper-soluble Gap fill materials for patterning metal trenches in Via-first Dual Damascene process
Developer-soluble Gap fill materials for patterning metal trenches in Via-first Dual Damascene process Mandar Bhave, Kevin Edwards, Carlton Washburn Brewer Science, Inc., 2401 Brewer Dr., Rolla, MO 65401,
More information