Evaluation of in-plane orthotropic elastic constants of paper and paperboard
|
|
- Jonas Gilbert
- 5 years ago
- Views:
Transcription
1 Evaluation of in-plane orthotropic elastic constants of paper and paperboard T. Yokoyama and K. Nakai Department of Mechanical Engineering, Okayama University of Science - Ridai-cho, Okayama 7-5, Japan ABSTRACT The in-plane orthotropic elastic constants of machine-made paper and paperboard were determined in a compact testing machine equipped with an optical extensometer and using a high-speed digital image sensor. Commercial copy paper, sack paper and paperboard were tested in a standard atmosphere of 23 ±2 C and 5 ±2% relative humidity. A dumbbell-type specimen specified in the JIS Z 22for sheet materials was used in the tension tests. Tensile specimens were cut in three different orientations from each type of paper and paperboard. Their thicknesses were carefully measured with a high-precision digital micrometer under a constant pressure. The in-plane elastic (Young's) moduli, shear modulus and Poisson's ratios as an orthotropic material were determined. It was shown that the in-plane elastic constants of commercial paper and paperboard roughly obey the theory of orthotropic linear elasticity.. INTRODUCTION Paper and paperboard are two of the most commonly used materials in pulp and paper, and packing industries. They generally exhibit anisotropic and non-linear mechanical behavior, strongly affected by moisture and temperature. A sufficient understanding of their mechanical behavior is very important in most converting operations and in end-use applications. However, determination of the mechanical properties is limited to those few properties, which can easily be measured, such as the elastic (Young's) moduli and the ultimate tensile strength in the machine direction (MD) and cross-machine direction (CD). The shear moduli, Poisson's ratios and virtually all of the out-of-plane elastic parameters are not readily measured by normal mechanical methods [], and hence their relationships to the ultimate end-use requirements of paper and paperboard are not known. Measurements of the in-plane orthotropic elastic constants (E MD, E CD, G, ν xy ) of paper and paperboard have been usually conducted using ultrasonic techniques [2-4]. Ultrasonic measurements involve the determination of wave velocities which relate directly to the elastic constants of the paper materials. The primary objective of the present work is to determine the in-plane orthotropic elastic constants of commercial paper and paperboard in a compact testing machine equipped with an optical extensometer and using a high-speed digital image sensor. Tension tests were conducted using dumbbell-type specimens in three different orientations in a standard atmosphere of 23 ±2 C and 5 ±2% relative humidity. The in-plane Young's moduli, shear modulus and Poisson's ratios for each paper and paperboard were determined. The values of the in-plane shear modulus were compared with theoretical values.
2 2. PAPER MATERIALS AND SPECIMEN PREPARATION Commercial paper and paperboard were chosen for testing: copy paper, sack paper made from unbleached kraft pulp (or UKP-sack paper), and uncoated paperboard. They are made from cellulose fibers. During the manufacturing process, the axes of the fibers tend to be aligned parallel to the paper flow through the paper machine. This phenomenon leads to anisotropy in the mechanical properties of paper. Basically, there are three principal directions which coincide with the directions of the paper machine (see Fig. ). JIS Z 22 dumbbell-type specimens (see Fig. 2) were cut in three different orientations from each type of paper and paperboard on a paper cutter, following a -mm thickness steel template as shown in Fig. 3. The specimen's ends were over-wrapped with chipboard doublers to prevent localized end failure. Their basic properties in both MD and CD in the standard atmosphere are given in Table. It is very difficult to determine the real thickness of paper because of its surface roughness and compressibility. Conforming to the ASTM D645/D645M-97 [5], the thickness of ten sheets of paper was carefully measured with a digital micrometer (Mitutoyo: GMA-25 DM) having a flat ground circular movable face with a 2 mm diameter under a constant pressure of 3 kpa with an accuracy of ±4mm. The surface roughness R a (center-lined average roughness) was non-contactly measured with a confocal laser scanning microscope (Keyence: VK-95). The measured surface roughness R a is almost the same in both MD and CD for any paper and paperboard. The paper tensile strength (S) given in Table was determined on the constant-width strip specimens of 25 mm in width by 25 mm in length specified in the ASTM D [6]. Note that the paper tensile strength (S) provides only an apparent tensile strength, which is given by the maximum load per unit width (kn/m). ZD (3) MD () 2 SPECIMEN (DIMENSIONS IN MM) direction of paper flow through paper machine Fig. Definitions of three principal material axes in paper or paperboard where MD is the machine direction, CD the cross-machine direction and ZD the thickness direction. The notations, 2 and 3 are also used Fig. 2 Geometry of JIS Z 22 tensile specimen for commercial paper and paperboard Table Basic properties of commercial paper and paperboard tested at 23 and 5% RH Basis weight (g/m 2 ) Thickness t (µm) Apparent density ρ (kg/m 3 ) Roughness R a (µm) MD CD Tensile strength S (kn/m) MD CD Copy paper (65)* 85 (87) 753 (754) UKP-sack paper Paperboard (85) 25 (9) 68 (74) (43) 7 (69) 64 (623) * Note: values in parentheses are provided by paper manufacturers Fig. 3 Three orientations in which tensile specimens were cut. The longitudinal direction in paper commonly corresponds to the machine direction
3 3. TESTING APPARATUS AND PROCEDURE It is virtually impossible to mechanically measure the deformation of a paper specimen in a conventional universal testing machine with a strain-gage extensometer, and hence we used the compact testing machine (JT Tohsi: Little Senstar LSC-/3) equipped with a non-contacting optical extensometer using a CCD camera (see Fig. 4). Tension tests were conducted using dumbbell-type paper specimens at a crosshead velocity of 3mm/min. Before testing, a small pretension load of N was applied to remove slack from the paper specimens. The applied load was measured with a load cell of kn capacity, and the longitudinal elongation over a 5-mm gage length stamped in black on a reduced section of the paper specimen was determined with the optical extensometer. The resulting tensile load-elongation relation was then converted to the nominal tensile stress-strain curve. In the measurement of Poisson's ratios, the transverse strain during tensile loading was simultaneously determined by recording the transverse contraction along the width of the paper specimen using the high-speed digital image sensor at a sampling rate of 5Hz (see Fig. 5). Note that the accuracy of transverse strain measurement was gradually degraded, because the paper specimen tended to curl about a loading axis as the tensile stress increased. CCD CAMERA TESTING MACHINE PERSONAL COMPUTER Fig. 4 Overall view of compact testing machine equipped with optical extensometer and personal computer Fig. 5 Picture of high-speed digital image sensor used for measurement of longitudinal and transverse strains in paper specimen 4. RESULTS AND DISCUSSION 4. In-Plane Tensile Stress-Strain Behavior Typical in-plane tensile stress-strain curves for copy paper in the three different orientations (or MD, 45 and CD) are shown in Fig. 6. It is seen that these stress-strain curves clearly depict the anisotropic elastic, initial yielding and strain hardening behavior. Young's modulus and the tensile strength decrease, and the strain-to-fracture and absorbed energy up to fracture increase with increasing angle from MD. This is due to the fact that machine-made paper and paperboard have more fibers aligned in MD. The tensile data are summarized in Table 2, where the coefficient of variation of both Young's modulus and the strain-to-fracture is lager than that of the tensile strength in any test orientation. The degree of elastic anisotropy is usually defined as the ratio of R = E MD / E CD [2, 4], where E MD and E CD are Young's moduli in MD and CD. The paperboard is found to have the highest anisotropy and the lowest tensile strength in each test orientation. This is because the macrostructure of the paperboard is quite different from that of other two types of paper, i.e., the paperboard has a structure built up of 7 layers of paper. Figure 7 displays fracture appearance of the paper and paperboard specimens, indicating that fractures occurred inside the extensometer gage length. None of the specimens exhibited a necking behavior just before
4 sudden fracture. Note that fractures in the 45 off-axis specimens took place at planes aligned at about 45 to 8 to the loading axis, which do not correspond to a shearing fracture. Each fracture propagated only along a zigzag path in a direction along the fibers preferentially aligned % RH (MD) 45 9 (CD) : FRACTURE. -3 ε= /s (V CH= 3mm/min).2. MD LOADING ε ε ε ε TENSILE STRAIN ε (%) Fig. 6 Typical in-plane tensile stress-strain curves for copy paper in three test orientations 5 TIME t (sec) Fig. 8 Time histories of longitudinal strain and transverse strain in copy paper specimen 5 UKP-SACK PAPER PAPERBOARD MD 45 CD MD 45 CD MD 45 CD Fig. 7 Fracture appearance of dumbbell-type specimen in three test orientations Table 2 Summary of in-plane tensile properties of commercial paper and paperboard tested at a strain rate of -3 /s in three test orientations Copy paper UKP-sack paper Paperboard MD() MD() MD() Young's modulus (GPa) Tensile strength σ (MPa) Strain-to-fracture ε (%) f Anisotoropy ratio R (=E MD /E CD ) MeanS.D. (Standard deviation). No. of specimens tested = 5.
5 4.2 In-Plane Poisson's Ratios and Shear Modulus Figure 8 shows typical time histories of longitudinal strain (ε ) and transverse strain (ε 2 ) in the copy paper specimen under MD loading. Both strains increase discontinuously with time due to the non-homogeneous deformation in copy paper. Eliminating time t yields the ε 2 vs ε and ε vs ε 2 relations as given in Fig.9 where the latter relation is obtained from another tension test under the CD loading. In-plane two Poisson's ratios ν 2 and ν 2 are defined as ν 2 = ε 2 / ε : ratio of transverse contraction ε 2 to longitudinal extension ε under -direction loading ν 2 = ε / ε 2 : ratio of transverse contraction ε to longitudinal extension ε 2 under 2-direction loading and determined from the initial slopes of the two relations depicted in Fig. 9. Both Poisson's ratios increase with increasing longitudinal strain. According to the test procedure specified in the ASTM D [7], the tension test on a 45 off-axis specimen gives the shear stress (τ = σ /2) and shear strain (γ = ε ε 2 ) where ε and ε 2 are, respectively, the longitudinal and transverse strains, which are simultaneously measured with the high-speed digital image sensor. From this relation, we can determine a shear stress-strain curve as depicted in Fig.. The in-plane shear modulus G 2 is determined from the initial slope of the shear stress-strain curve. Typical in-plane orthotropic constants (E,, ν 2, ν 2, and G 2 ) of paper and paperboard are summarized in Table 3. It is observed that Poisson's ratio ν 2 is about.6 to 2.7 times larger than Poisson's ratio ν 2, suggesting the high anisotropy of paper and paperboard. It is also found that the measured G 2 agrees reasonably well with the theoretical values obtained by Eqs. (3) and (4) % RH. -3 ε= /s (MD) LOADING 9(CD) LOADING (V CH = 3mm/min) SPECIMEN τ = σ 2 γ = ε ε 2. 2 G 2 ν 2 ν LONGITUDINAL STRAIN ε or ε (%) Fig. 9 Transverse strain vs longitudinal strain for copy paper SHEAR STRAIN γ (%) Fig. Shear stress-strain curve for copy paper from tension test on 45 off-axis specimen Table 3 Summary of typical in-plane elastic constants of paper and paperboard Young's modulus or (GPa) 2 Poisson's ratio ν or ν 2 2 Shear modulus G 2 (GPa) Measured Theoretical (3) Campbell (4) MD () MD () MD ()
6 Following classical laminate theory [8], Young's modulus and Poisson's ratio in the x-y plane can be expressed in terms of an angle θ from MD (see the inset in Fig. ) as = m2 m 2 n 2 ν 2 E x E ( ) + n2 n 2 m 2 ν 2 ( ) + m2 n 2 () G 2 ν xy = m2 m 2 ν 2 n 2 E x E ( ) + n2 n 2 ν 2 m 2 ( ) + m2 n 2 (2) G 2 where m = cosθ ; n = sinθ ; the subscripts and 2 denote MD and CD, respectively. When θ = 45 is substituted into Eq. (), we obtain the following relation: = ν 2 + ν 2 + (3) E x 4E θ=45 o 4 4G 2 Since the left hand side of Eq. (3) is known from Young's modulus measured in the 45 orientation, the shear modulus G 2 can be then determined from the measured four elastic constants E,, ν 2 and ν 2. Campbell [9] proposed a simple expression similar to Eq. (3) for a variety of paper as G 2 = + ν 2 E + + ν 2 under the assumption that the following expression given in [] is satisfied: E x = m2 E + n2 Figure indicates the variation of Young's modulus with fiber (or test) orientation. Young's modulus decreases monotonically from its maximum value E at θ = to its minimum value at θ = 9. Measured Young's moduli are in excellent agreement with the theoretical values calculated from Eq. (). Similarly, Fig. 2 presents the variation of Poisson's ratio with fiber (or test) orientation. Poisson's ratio varies monotonically from its maximum value ν 2 at θ = to its minimum value ν 2 at θ = 9. Measured Poisson's ratios also agree well with the theoretical values derived from Eq. (2). (4) (5) 8 6 E UKP-SACK PAPER PAPERBOARD EXPERIMENT THEORY.3.2 ν 2 UKP-SACK PAPER PAPERBOARD EXPERIMENT THEORY 4 y 2 MD() θ x. y MD() θ x ν 2 (MD) ANGLE θ FROM MD (degree) Fig. Young's modulus as a function of fiber (or test) orientation 8 9 (CD) (MD) ANGLE θ FROM MD (degree) Fig. 2 Poisson's ratio as a function of fiber (or test) orientation 8 9 (CD) 5. CONCLUSIONS The in-plane orthotropic elastic constants of machine-made copy paper, UKP-sack paper and uncoated paperboard were determined in the compact testing machine equipped with the optical extensometer and using the high-speed digital image sensor. From the present experimental results, the following conclusions can be drawn:
7 () The in-plane elastic constants of machine-made paper and paperboard roughly obey the theory of orthotropic linear elasticity. (2) Machine-made paper and paperboard may be regarded as a kind of composite material, although pulp (or wood) fibers do not have matrix structure. Acknowledgement The authors wish to thank Mr. Takafumi Odamura, formerly Graduate Student, Okayama University of Science, for his assistance in the experimental work. References [] Jones, A.R.: An experimental investigation of the in-plane elastic moduli of paper, Tappi J., Vol. 5, No. 5, (968). [2] Baum, G.A. and Bornhoeft, L.R.: Estimating Poisson ratios in paper using ultrasonic techniques, Tappi J., Vol. 62, No. 5, 87-9 (979). [3] Mann, R.W., Baum, G.A. and Habeger, C.C.: Determination of all nine orthotropic elastic constants for machine-made paper, Tappi J., Vol. 63, No. 2, (98). [4] Baum, G.A., Brennan, D.C. and Habeger, C.C.: Orthotropic elastic constants of paper, Tappi J., Vol. 64, No. 8, 97- (98). [5] ASTM D645/D645M-97: Annual Book of ASTM Standards 25, Vol. 5.9, 374, ASTM International (25). [6] ASTM D828-97: Annual Book of ASTM Standards 25, Vol. 5.9, 2, ASTM International (25). [7] ASTM D358-76: ASTM Standards and Literature References for Composite Materials, 5, ASTM (99). [8] Daniel, I.M. and Ishai, O.: Engineering Mechanics of Composite Materials, 64, Oxford University Press, Oxford (994). [9] Campbell, J.G.: The in-plane elastic constants of paper, J. Australian Appl. Sci., Vol. 2, No. 3, (96). [] Horio, M. and Onogi, S.: Dynamic measurements of physical properties of pulp and paper by audiofrequency sound, J. Appl. Phys., Vol. 22, (95).
Samantha Ramirez, MSE. Stress. The intensity of the internal force acting on a specific plane (area) passing through a point. F 2
Samantha Ramirez, MSE Stress The intensity of the internal force acting on a specific plane (area) passing through a point. Δ ΔA Δ z Δ 1 2 ΔA Δ x Δ y ΔA is an infinitesimal size area with a uniform force
More informationNORMAL STRESS. The simplest form of stress is normal stress/direct stress, which is the stress perpendicular to the surface on which it acts.
NORMAL STRESS The simplest form of stress is normal stress/direct stress, which is the stress perpendicular to the surface on which it acts. σ = force/area = P/A where σ = the normal stress P = the centric
More informationRELATIONSHIP BETWEEN RADIAL COMPRESSIVE MODULUS OF ELASTICITY AND SHEAR MODULUS OF WOOD Jen Y. Liu Research Engineer
RELATIONSHIP BETWEEN RADIAL COMPRESSIVE MODULUS OF ELASTICITY AND SHEAR MODULUS OF WOOD Jen Y. Liu Research Engineer and Robert J. Ross Supervisory Research Engineer USDA Forest Service Forest Products
More informationModule III - Macro-mechanics of Lamina. Lecture 23. Macro-Mechanics of Lamina
Module III - Macro-mechanics of Lamina Lecture 23 Macro-Mechanics of Lamina For better understanding of the macromechanics of lamina, the knowledge of the material properties in essential. Therefore, the
More informationMECE 3321 MECHANICS OF SOLIDS CHAPTER 3
MECE 3321 MECHANICS OF SOLIDS CHAPTER 3 Samantha Ramirez TENSION AND COMPRESSION TESTS Tension and compression tests are used primarily to determine the relationship between σ avg and ε avg in any material.
More informationSTANDARD SAMPLE. Reduced section " Diameter. Diameter. 2" Gauge length. Radius
MATERIAL PROPERTIES TENSILE MEASUREMENT F l l 0 A 0 F STANDARD SAMPLE Reduced section 2 " 1 4 0.505" Diameter 3 4 " Diameter 2" Gauge length 3 8 " Radius TYPICAL APPARATUS Load cell Extensometer Specimen
More informationME 2570 MECHANICS OF MATERIALS
ME 2570 MECHANICS OF MATERIALS Chapter III. Mechanical Properties of Materials 1 Tension and Compression Test The strength of a material depends on its ability to sustain a load without undue deformation
More informationThe science of elasticity
The science of elasticity In 1676 Hooke realized that 1.Every kind of solid changes shape when a mechanical force acts on it. 2.It is this change of shape which enables the solid to supply the reaction
More informationStress-Strain Behavior
Stress-Strain Behavior 6.3 A specimen of aluminum having a rectangular cross section 10 mm 1.7 mm (0.4 in. 0.5 in.) is pulled in tension with 35,500 N (8000 lb f ) force, producing only elastic deformation.
More informationOutline. Tensile-Test Specimen and Machine. Stress-Strain Curve. Review of Mechanical Properties. Mechanical Behaviour
Tensile-Test Specimen and Machine Review of Mechanical Properties Outline Tensile test True stress - true strain (flow curve) mechanical properties: - Resilience - Ductility - Toughness - Hardness A standard
More informationNANOINDENTATION STUDIES OF PAPER
Progress in Paper Physics Seminar 2008 - June 2-5, Otaniemi Finland NANOINDENTATION STUDIES OF PAPER B. F. West 1, B. T. Hotle 2, J. E. Jakes 3,4, J. M. Considine 3, R. E. Rowlands 1 and K. T. Turner 1,4
More informationMechanical Properties of Materials
Mechanical Properties of Materials Strains Material Model Stresses Learning objectives Understand the qualitative and quantitative description of mechanical properties of materials. Learn the logic of
More informationCHAPTER 6 MECHANICAL PROPERTIES OF METALS PROBLEM SOLUTIONS
CHAPTER 6 MECHANICAL PROPERTIES OF METALS PROBLEM SOLUTIONS Concepts of Stress and Strain 6.1 Using mechanics of materials principles (i.e., equations of mechanical equilibrium applied to a free-body diagram),
More information6.4 A cylindrical specimen of a titanium alloy having an elastic modulus of 107 GPa ( psi) and
6.4 A cylindrical specimen of a titanium alloy having an elastic modulus of 107 GPa (15.5 10 6 psi) and an original diameter of 3.8 mm (0.15 in.) will experience only elastic deformation when a tensile
More informationIPC TECHNICAL PAPER SERIES NUMBER 116
THE INSTITUTE OF PAPER CHEMISTRY, APPLETON, WISCONSIN IPC TECHNICAL PAPER SERIES NUMBER 116 AN INVESTIGATION OF THE ELASTIC AND DIELECTRIC ANISOTROPY OF PAPER E. H. FLEISCHMAN, G. A. BAUM, AND C. C. HABEGER
More informationChapter 7. Highlights:
Chapter 7 Highlights: 1. Understand the basic concepts of engineering stress and strain, yield strength, tensile strength, Young's(elastic) modulus, ductility, toughness, resilience, true stress and true
More informationMaterial Characterization of Carbon Fiber Reinforced Polymer Laminate Using Virtual Fields Method
Proceedings of ICTACEM 014 International Conference on Theoretical, Applied, Computational and Experimental Mechanics December 9-31, 014, IIT Kharagpur, India ICTACEM-014/39 Material Characterization of
More informationFailure analysis of serial pinned joints in composite materials
Indian Journal of Engineering & Materials Sciences Vol. 18, April 2011, pp. 102-110 Failure analysis of serial pinned joints in composite materials Alaattin Aktaş* Department of Mechanical Engineering,
More information4.MECHANICAL PROPERTIES OF MATERIALS
4.MECHANICAL PROPERTIES OF MATERIALS The diagram representing the relation between stress and strain in a given material is an important characteristic of the material. To obtain the stress-strain diagram
More informationTask 1 - Material Testing of Bionax Pipe and Joints
Task 1 - Material Testing of Bionax Pipe and Joints Submitted to: Jeff Phillips Western Regional Engineer IPEX Management, Inc. 20460 Duncan Way Langley, BC, Canada V3A 7A3 Ph: 604-534-8631 Fax: 604-534-7616
More informationIntroduction to Engineering Materials ENGR2000. Dr. Coates
Introduction to Engineering Materials ENGR2 Chapter 6: Mechanical Properties of Metals Dr. Coates 6.2 Concepts of Stress and Strain tension compression shear torsion Tension Tests The specimen is deformed
More informationME 243. Mechanics of Solids
ME 243 Mechanics of Solids Lecture 2: Stress and Strain Ahmad Shahedi Shakil Lecturer, Dept. of Mechanical Engg, BUET E-mail: sshakil@me.buet.ac.bd, shakil6791@gmail.com Website: teacher.buet.ac.bd/sshakil
More informationEMA 3702 Mechanics & Materials Science (Mechanics of Materials) Chapter 2 Stress & Strain - Axial Loading
MA 3702 Mechanics & Materials Science (Mechanics of Materials) Chapter 2 Stress & Strain - Axial Loading MA 3702 Mechanics & Materials Science Zhe Cheng (2018) 2 Stress & Strain - Axial Loading Statics
More informationBIAXIAL STRENGTH INVESTIGATION OF CFRP COMPOSITE LAMINATES BY USING CRUCIFORM SPECIMENS
BIAXIAL STRENGTH INVESTIGATION OF CFRP COMPOSITE LAMINATES BY USING CRUCIFORM SPECIMENS H. Kumazawa and T. Takatoya Airframes and Structures Group, Japan Aerospace Exploration Agency 6-13-1, Ohsawa, Mitaka,
More information1.103 CIVIL ENGINEERING MATERIALS LABORATORY (1-2-3) Dr. J.T. Germaine Spring 2004 LABORATORY ASSIGNMENT NUMBER 6
1.103 CIVIL ENGINEERING MATERIALS LABORATORY (1-2-3) Dr. J.T. Germaine MIT Spring 2004 LABORATORY ASSIGNMENT NUMBER 6 COMPRESSION TESTING AND ANISOTROPY OF WOOD Purpose: Reading: During this laboratory
More informationMINE ROOF SUPPORT DESIGN AND ANALYSIS. Document no : Revision no : 1.0
MINE ROOF SUPPORT DESIGN AND ANALYSIS Document no : 1806-2697-23 Revision no : 1.0 DOCUMENT TITLE : MINE ROOF SUPPORT DESIGN AND ANALYSIS DOCUMENT NUMBER : 1806-2697-23 ISSUE : Issue 1.0 DATE : 7 October
More informationGB/T / ISO 527-1:1993
Translated English of Chinese Standard: GB/T1040.1-2006 www.chinesestandard.net Sales@ChineseStandard.net GB NATIONAL STANDARD OF THE PEOPLE S REPUBLIC OF CHINA ICS 83.080.01 G 31 GB/T 1040.1-2006 / ISO
More informationThe objective of this experiment is to investigate the behavior of steel specimen under a tensile test and to determine it's properties.
Objective: The objective of this experiment is to investigate the behavior of steel specimen under a tensile test and to determine it's properties. Introduction: Mechanical testing plays an important role
More informationUNIT I SIMPLE STRESSES AND STRAINS
Subject with Code : SM-1(15A01303) Year & Sem: II-B.Tech & I-Sem SIDDHARTH GROUP OF INSTITUTIONS :: PUTTUR Siddharth Nagar, Narayanavanam Road 517583 QUESTION BANK (DESCRIPTIVE) UNIT I SIMPLE STRESSES
More informationPREDICTION OF OUT-OF-PLANE FAILURE MODES IN CFRP
PREDICTION OF OUT-OF-PLANE FAILURE MODES IN CFRP R. R. Pinto 1, P. P. Camanho 2 1 INEGI - Instituto de Engenharia Mecanica e Gestao Industrial, Rua Dr. Roberto Frias, 4200-465, Porto, Portugal 2 DEMec,
More informationPlane Strain Test for Metal Sheet Characterization
Plane Strain Test for Metal Sheet Characterization Paulo Flores 1, Felix Bonnet 2 and Anne-Marie Habraken 3 1 DIM, University of Concepción, Edmundo Larenas 270, Concepción, Chile 2 ENS - Cachan, Avenue
More informationLab Exercise #5: Tension and Bending with Strain Gages
Lab Exercise #5: Tension and Bending with Strain Gages Pre-lab assignment: Yes No Goals: 1. To evaluate tension and bending stress models and Hooke s Law. a. σ = Mc/I and σ = P/A 2. To determine material
More informationSupplementary Uniaxial Compressive Strength Testing of DGR-3 and DGR-4 Core
Technical Report Title: Document ID: Authors: Supplementary Uniaxial Compressive Strength Testing of DGR-3 and DGR-4 Core TR-08-39 B. Gorski, T. Anderson and D. Rodgers CANMET Mining and Mineral Sciences
More informationELASTICITY (MDM 10203)
ELASTICITY () Lecture Module 3: Fundamental Stress and Strain University Tun Hussein Onn Malaysia Normal Stress inconstant stress distribution σ= dp da P = da A dimensional Area of σ and A σ A 3 dimensional
More informationINTRODUCTION TO STRAIN
SIMPLE STRAIN INTRODUCTION TO STRAIN In general terms, Strain is a geometric quantity that measures the deformation of a body. There are two types of strain: normal strain: characterizes dimensional changes,
More informationUNIVERSITY OF SASKATCHEWAN ME MECHANICS OF MATERIALS I FINAL EXAM DECEMBER 13, 2008 Professor A. Dolovich
UNIVERSITY OF SASKATCHEWAN ME 313.3 MECHANICS OF MATERIALS I FINAL EXAM DECEMBER 13, 2008 Professor A. Dolovich A CLOSED BOOK EXAMINATION TIME: 3 HOURS For Marker s Use Only LAST NAME (printed): FIRST
More informationDEVELOPMENT OF MEASURING SYSTEM FOR STRESS BY MEANS OF IMAGE PLATE FOR LABORATORY X-RAY EXPERIMENT
Copyright JCPDS - International Centre for Diffraction Data 003, Advances in X-ray Analysis, Volume 46. 6 DEVELOPMENT OF MEASURING SYSTEM FOR STRESS BY MEANS OF IMAGE PLATE FOR LABORATORY X-RAY EXPERIMENT
More informationMaterials and Structures. Indian Institute of Technology Kanpur
Introduction to Composite Materials and Structures Nachiketa Tiwari Indian Institute of Technology Kanpur Lecture 16 Behavior of Unidirectional Composites Lecture Overview Mt Material ilaxes in unidirectional
More informationAdvanced Structural Analysis EGF Section Properties and Bending
Advanced Structural Analysis EGF316 3. Section Properties and Bending 3.1 Loads in beams When we analyse beams, we need to consider various types of loads acting on them, for example, axial forces, shear
More informationFig. 1. Circular fiber and interphase between the fiber and the matrix.
Finite element unit cell model based on ABAQUS for fiber reinforced composites Tian Tang Composites Manufacturing & Simulation Center, Purdue University West Lafayette, IN 47906 1. Problem Statement In
More informationAmerican Society for Testing and Materials (ASTM) Standards. Mechanical Testing of Composites and their Constituents
Mechanical Testing of Composites and their Constituents American Society for Testing and Materials (ASTM) Standards Tests done to determine intrinsic material properties such as modulus and strength for
More information2. Rigid bar ABC supports a weight of W = 50 kn. Bar ABC is pinned at A and supported at B by rod (1). What is the axial force in rod (1)?
IDE 110 S08 Test 1 Name: 1. Determine the internal axial forces in segments (1), (2) and (3). (a) N 1 = kn (b) N 2 = kn (c) N 3 = kn 2. Rigid bar ABC supports a weight of W = 50 kn. Bar ABC is pinned at
More informationPost Graduate Diploma in Mechanical Engineering Computational mechanics using finite element method
9210-220 Post Graduate Diploma in Mechanical Engineering Computational mechanics using finite element method You should have the following for this examination one answer book scientific calculator No
More informationME Final Exam. PROBLEM NO. 4 Part A (2 points max.) M (x) y. z (neutral axis) beam cross-sec+on. 20 kip ft. 0.2 ft. 10 ft. 0.1 ft.
ME 323 - Final Exam Name December 15, 2015 Instructor (circle) PROEM NO. 4 Part A (2 points max.) Krousgrill 11:30AM-12:20PM Ghosh 2:30-3:20PM Gonzalez 12:30-1:20PM Zhao 4:30-5:20PM M (x) y 20 kip ft 0.2
More informationChapter 2 - Macromechanical Analysis of a Lamina. Exercise Set. 2.1 The number of independent elastic constants in three dimensions are: 2.
Chapter - Macromechanical Analysis of a Lamina Exercise Set. The number of independent elastic constants in three dimensions are: Anisotropic Monoclinic 3 Orthotropic 9 Transversely Orthotropic 5 Isotropic.
More informationCTC 460 kcmil ACCC Conductor Stress Strain Tests
CTC 46 kcmil ACCC Conductor Stress Strain Tests NEETRAC Project Number: 8-45 March, 28 Requested by: Doug Pilling CTC Principal Investigator: Paul Springer, PE Reviewed by: Graham Price CTC 46 kcmil Conductor
More informationN = Shear stress / Shear strain
UNIT - I 1. What is meant by factor of safety? [A/M-15] It is the ratio between ultimate stress to the working stress. Factor of safety = Ultimate stress Permissible stress 2. Define Resilience. [A/M-15]
More informationMATERIAL ELASTIC ANISOTROPIC command
MATERIAL ELASTIC ANISOTROPIC command.. Synopsis The MATERIAL ELASTIC ANISOTROPIC command is used to specify the parameters associated with an anisotropic linear elastic material idealization. Syntax The
More informationTHE TRANSVERSE OFF-AXIS STIFFNESS AND STRENGTH OF SOFTWOODS. Abstract
THE TRANSVERSE OFF-AXIS STIFFNESS AND STRENGTH OF SOFTWOODS Carl S. Moden 1, Jessica Polycarpe 1 and Lars A. Berglund 2 1 Dept. of Aeronautical and Vehicle Engineering The Royal Institute of Technology
More informationDetermination of Dynamic Fracture Toughness Using Strain Measurement
Key Engineering Materials Vols. 61-63 (4) pp. 313-318 online at http://www.scientific.net (4) Trans Tech Publications, Switzerland Online available since 4/4/15 Determination of Dynamic Fracture Toughness
More informationCOMPLEX STRESS TUTORIAL 4 THEORIES OF FAILURE. You should judge your progress by completing the self assessment exercises.
COMPLEX STRESS TUTORIAL 4 THEORIES OF FAILURE This short tutorial covers no known elements of the E.C. or Edexcel Exams but should be studied as part of complex stress, structures and materials. You should
More informationOutline. Organization. Stresses in Beams
Stresses in Beams B the end of this lesson, ou should be able to: Calculate the maimum stress in a beam undergoing a bending moment 1 Outline Curvature Normal Strain Normal Stress Neutral is Moment of
More informationTheory at a Glance (for IES, GATE, PSU)
1. Stress and Strain Theory at a Glance (for IES, GATE, PSU) 1.1 Stress () When a material is subjected to an external force, a resisting force is set up within the component. The internal resistance force
More informationTuesday, February 11, Chapter 3. Load and Stress Analysis. Dr. Mohammad Suliman Abuhaiba, PE
1 Chapter 3 Load and Stress Analysis 2 Chapter Outline Equilibrium & Free-Body Diagrams Shear Force and Bending Moments in Beams Singularity Functions Stress Cartesian Stress Components Mohr s Circle for
More informationME 582 Advanced Materials Science. Chapter 2 Macromechanical Analysis of a Lamina (Part 2)
ME 582 Advanced Materials Science Chapter 2 Macromechanical Analysis of a Lamina (Part 2) Laboratory for Composite Materials Research Department of Mechanical Engineering University of South Alabama, Mobile,
More informationHardened Concrete. Lecture No. 16
Hardened Concrete Lecture No. 16 Fatigue strength of concrete Modulus of elasticity, Creep Shrinkage of concrete Stress-Strain Plot of Concrete At stress below 30% of ultimate strength, the transition
More informationLaboratory 4 Bending Test of Materials
Department of Materials and Metallurgical Engineering Bangladesh University of Engineering Technology, Dhaka MME 222 Materials Testing Sessional.50 Credits Laboratory 4 Bending Test of Materials. Objective
More informationTABLE OF CONTENTS. Mechanics of Composite Materials, Second Edition Autar K Kaw University of South Florida, Tampa, USA
Mechanics of Composite Materials, Second Edition Autar K Kaw University of South Florida, Tampa, USA TABLE OF CONTENTS 1. INTRODUCTION TO COMPOSITE MATERIALS 1.1 Introduction... 1.2 Classification... 1.2.1
More informationNONLINEAR ELASTIC CONSTITUTIVE RELATIONS FOR CELLULOSIC MATERIALS
In: Perkins, R.W., ed. Mechanics of cellulosic and polymeric materials: Proceedings, 3d Joint ASCE/ASME Mechanics conference; 1989 July 9-12; San Diego, New York: The American Society of Mechanical Engineers;
More informationStress intensity factors for an inclined and/or eccentric crack in a finite orthotropic lamina
1886 Stress intensity factors for an inclined and/or eccentric crack in a finite orthotropic lamina Abstract Stress intensity factors (SIF) are determined for an inclined and / or eccentric crack in a
More informationCharacterizations of Aluminum Alloy Sheet Materials Numisheet 2005
Characterizations of Aluminum Alloy Sheet Materials Numisheet 25 John C. Brem, Frederic Barlat, Robert E. Dick, and Jeong-Whan Yoon Alcoa Technical Center, PA, 1569-1, USA Abstract. This report reproduces
More informationINFLUENCE KINDS OF MATERIALS ON THE POISSON S RATIO OF WOVEN FABRICS
ISSN 1846-6168 (Print), ISSN 1848-5588 (Online) ID: TG-217816142553 Original scientific paper INFLUENCE KINDS OF MATERIALS ON THE POISSON S RATIO OF WOVEN FABRICS Željko PENAVA, Diana ŠIMIĆ PENAVA, Željko
More informationDesign of a fastener based on negative Poisson's ratio foam adapted from
1 Design of a fastener based on negative Poisson's ratio foam adapted from Choi, J. B. and Lakes, R. S., "Design of a fastener based on negative Poisson's ratio foam", Cellular Polymers, 10, 205-212 (1991).
More informationINCREASING RUPTURE PREDICTABILITY FOR ALUMINUM
1 INCREASING RUPTURE PREDICTABILITY FOR ALUMINUM Influence of anisotropy Daniel Riemensperger, Adam Opel AG Paul Du Bois, PDB 2 www.opel.com CONTENT Introduction/motivation Isotropic & anisotropic material
More informationTensile Properties of Thermoplastic-Laminated Composites Based on a Polypropylene Matrix Reinforced with Continuous Twaron Fibers
Tensile Properties of Thermoplastic-Laminated Composites Based on a Polypropylene Matrix Reinforced with Continuous Twaron Fibers J. L. MENA-TUN, P. I. GONZALEZ-CHI Centro de Investigación Científica de
More informationDAMAGE MECHANICS MODEL FOR OFF-AXIS FATIGUE BEHAVIOR OF UNIDIRECTIONAL CARBON FIBER-REINFORCED COMPOSITES AT ROOM AND HIGH TEMPERATURES
DAMAGE MECHANICS MODEL FOR OFF-AXIS FATIGUE BEHAVIOR OF UNIDIRECTIONAL CARBON FIBER-REINFORCED COMPOSITES AT ROOM AND HIGH TEMPERATURES M. Kawai Institute of Engineering Mechanics University of Tsukuba,
More informationSolid Mechanics Chapter 1: Tension, Compression and Shear
Solid Mechanics Chapter 1: Tension, Compression and Shear Dr. Imran Latif Department of Civil and Environmental Engineering College of Engineering University of Nizwa (UoN) 1 Why do we study Mechanics
More informationMECHANICS OF MATERIALS
CHATR Stress MCHANICS OF MATRIALS and Strain Axial Loading Stress & Strain: Axial Loading Suitability of a structure or machine may depend on the deformations in the structure as well as the stresses induced
More informationMechanical Engineering Ph.D. Preliminary Qualifying Examination Solid Mechanics February 25, 2002
student personal identification (ID) number on each sheet. Do not write your name on any sheet. #1. A homogeneous, isotropic, linear elastic bar has rectangular cross sectional area A, modulus of elasticity
More information[5] Stress and Strain
[5] Stress and Strain Page 1 of 34 [5] Stress and Strain [5.1] Internal Stress of Solids [5.2] Design of Simple Connections (will not be covered in class) [5.3] Deformation and Strain [5.4] Hooke s Law
More informationStrength of Material. Shear Strain. Dr. Attaullah Shah
Strength of Material Shear Strain Dr. Attaullah Shah Shear Strain TRIAXIAL DEFORMATION Poisson's Ratio Relationship Between E, G, and ν BIAXIAL DEFORMATION Bulk Modulus of Elasticity or Modulus of Volume
More informationEFFECT OF ELLIPTIC OR CIRCULAR HOLES ON THE STRESS DISTRIBUTION IN PLATES
EFFECT OF ELLIPTIC OR CIRCULAR HOLES ON THE STRESS DISTRIBUTION IN PLATES OF WOOD OR PLYWOOD CONSIDERED AS ORTHOTROPIC MATERIALS Information Revied and Reaffirmed March 1956 No. 1510 EFFECT OF ELLIPTIC
More informationChapter 2: Elasticity
OHP 1 Mechanical Properties of Materials Chapter 2: lasticity Prof. Wenjea J. Tseng ( 曾文甲 ) Department of Materials ngineering National Chung Hsing University wenjea@dragon.nchu.edu.tw Reference: W.F.
More informationEffect of Specimen Dimensions on Flexural Modulus in a 3-Point Bending Test
Effect of Specimen Dimensions on Flexural Modulus in a 3-Point Bending Test M. Praveen Kumar 1 and V. Balakrishna Murthy 2* 1 Mechanical Engineering Department, P.V.P. Siddhartha Institute of Technology,
More informationBioen MIDTERM. Covers: Weeks 1-4, FBD, stress/strain, stress analysis, rods and beams (not deflections).
Name Bioen 326 Midterm 2013 Page 1 Bioen 326 2013 MIDTERM Covers: Weeks 1-4, FBD, stress/strain, stress analysis, rods and beams (not deflections). Rules: Closed Book Exam: Please put away all notes and
More information20. Rheology & Linear Elasticity
I Main Topics A Rheology: Macroscopic deformation behavior B Linear elasticity for homogeneous isotropic materials 10/29/18 GG303 1 Viscous (fluid) Behavior http://manoa.hawaii.edu/graduate/content/slide-lava
More informationFinite Element and Plate Theory Modeling of Acoustic Emission Waveforms. NASA Langley Research Center. Hampton, VA *University of Denver
Finite Element and Plate Theory Modeling of Acoustic Emission Waveforms W. H. Prosser, M. A. Hamstad + *, J. Gary +, and A. O Gallagher + NASA Langley Research Center Hampton, VA 23681-1 *University of
More informationEffect of intermediate principal stresses on compressive strength of Phra Wihan sandstone
Rock Mechanics, Fuenkajorn & Phien-wej (eds) 211. ISBN 978 974 533 636 Effect of intermediate principal stresses on compressive strength of Phra Wihan sandstone T. Pobwandee & K. Fuenkajorn Geomechanics
More informationExperimental study of mechanical and thermal damage in crystalline hard rock
Experimental study of mechanical and thermal damage in crystalline hard rock Mohammad Keshavarz Réunion Technique du CFMR - Thèses en Mécanique des Roches December, 3 nd 2009 1 Overview Introduction Characterization
More informationFlexural properties of polymers
A2 _EN BUDAPEST UNIVERSITY OF TECHNOLOGY AND ECONOMICS FACULTY OF MECHANICAL ENGINEERING DEPARTMENT OF POLYMER ENGINEERING Flexural properties of polymers BENDING TEST OF CHECK THE VALIDITY OF NOTE ON
More informationPOST-PEAK BEHAVIOR OF FRP-JACKETED REINFORCED CONCRETE COLUMNS
POST-PEAK BEHAVIOR OF FRP-JACKETED REINFORCED CONCRETE COLUMNS - Technical Paper - Tidarut JIRAWATTANASOMKUL *1, Dawei ZHANG *2 and Tamon UEDA *3 ABSTRACT The objective of this study is to propose a new
More informationUSE OF DIGITAL IMAGE CORRELATION TO OBTAIN MATERIAL MODEL PARAMETERS FOR COMPOSITES
USE OF DIGITAL IMAGE CORRELATION TO OBTAIN MATERIAL MODEL PARAMETERS FOR COMPOSITES Brian Croop, Hubert Lobo (DatapointLabs, USA). Presenter: Hubert Lobo, President SUMMARY The development of material
More informationLAMINATION THEORY FOR THE STRENGTH OF FIBER COMPOSITE MATERIALS
XXII. LAMINATION THEORY FOR THE STRENGTH OF FIBER COMPOSITE MATERIALS Introduction The lamination theory for the elastic stiffness of fiber composite materials is the backbone of the entire field, it holds
More informationMECHANICS OF MATERIALS
Third E CHAPTER 2 Stress MECHANICS OF MATERIALS Ferdinand P. Beer E. Russell Johnston, Jr. John T. DeWolf Lecture Notes: J. Walt Oler Texas Tech University and Strain Axial Loading Contents Stress & Strain:
More information8 Properties of Lamina
8 Properties of Lamina 8- ORTHOTROPIC LAMINA An orthotropic lamina is a sheet with unique and predictable properties and consists of an assemblage of fibers ling in the plane of the sheet and held in place
More informationBending Load & Calibration Module
Bending Load & Calibration Module Objectives After completing this module, students shall be able to: 1) Conduct laboratory work to validate beam bending stress equations. 2) Develop an understanding of
More informationPURE BENDING. If a simply supported beam carries two point loads of 10 kn as shown in the following figure, pure bending occurs at segment BC.
BENDING STRESS The effect of a bending moment applied to a cross-section of a beam is to induce a state of stress across that section. These stresses are known as bending stresses and they act normally
More information2 Experiment of GFRP bolt
16 TH INTERNATIONAL CONFERENCE ON COMPOSITE MATERIALS FATIGUE LIFE EVALUATION OF BOLT MADE OF WOVEN FABRIC FRP Takeshi INOUE*, Hiroaki NAKAI**, Tetsusei KURASHIKI**, Masaru ZAKO**, Yuji KOMETANI*** *Graduate
More informationINTERFACIAL STRENGTH EVALUATION IN A GLASS FIBER REINFORCED COMPOSITE USING CRUCIFORM SPECIMEN METHOD
INTERFACIAL STRENGTH EVALUATION IN A GLASS FIBER REINFORCED COMPOSITE USING CRUCIFORM SPECIMEN METHOD Shinji Ogihara, oriaki Sakamoto 2, Hajime Kato 2, Satoshi Kobayashi 3 and Ichiro Ueno Dept. of Mechanical
More informationAn integrated approach to the design of high performance carbon fibre reinforced risers - from micro to macro - scale
An integrated approach to the design of high performance carbon fibre reinforced risers - from micro to macro - scale Angelos Mintzas 1, Steve Hatton 1, Sarinova Simandjuntak 2, Andrew Little 2, Zhongyi
More informationIPC TECHNICAL PAPER SERIES NUMBER 145 THE ELASTIC PROPERTIES OF PAPER: A REVIEW GARY A. BAUM
THE INSTITUTE OF PAPER CHEMISTRY, APPLETON, WISCONSIN IPC TECHNICAL PAPER SERIES NUMBER 145 THE ELASTIC PROPERTIES OF PAPER: A REVIEW GARY A. BAUM AUGUST, 1984 The Elastic Properties of Paper: A Review
More informationComposite Structures. Indian Institute of Technology Kanpur
Mechanics of Laminated Composite Structures Nachiketa Tiwari Indian Institute of Technology Kanpur Lecture 23 Analysis of an Orthotropic Ply Lecture Overview Introduction Engineering constants for an 2
More informationA rate-dependent Hosford-Coulomb model for predicting ductile fracture at high strain rates
EPJ Web of Conferences 94, 01080 (2015) DOI: 10.1051/epjconf/20159401080 c Owned by the authors, published by EDP Sciences, 2015 A rate-dependent Hosford-Coulomb model for predicting ductile fracture at
More informationCoupling of plasticity and damage in glass fibre reinforced polymer composites
EPJ Web of Conferences 6, 48 1) DOI: 1.151/epjconf/1648 c Owned by the authors, published by EDP Sciences, 1 Coupling of plasticity and damage in glass fibre reinforced polymer composites R. Kvale Joki
More informationMechanical properties 1 Elastic behaviour of materials
MME131: Lecture 13 Mechanical properties 1 Elastic behaviour of materials A. K. M. B. Rashid Professor, Department of MME BUET, Dhaka Today s Topics Deformation of material under the action of a mechanical
More informationHigh Tech High Top Hat Technicians. An Introduction to Solid Mechanics. Is that supposed to bend there?
High Tech High Top Hat Technicians An Introduction to Solid Mechanics Or Is that supposed to bend there? Why don't we fall through the floor? The power of any Spring is in the same proportion with the
More informationSolid Mechanics Homework Answers
Name: Date: Solid Mechanics Homework nswers Please show all of your work, including which equations you are using, and circle your final answer. Be sure to include the units in your answers. 1. The yield
More informationThe Relationship between the Applied Torque and Stresses in Post-Tension Structures
ECNDT 6 - Poster 218 The Relationship between the Applied Torque and Stresses in Post-Tension Structures Fui Kiew LIEW, Sinin HAMDAN * and Mohd. Shahril OSMAN, Faculty of Engineering, Universiti Malaysia
More informationME 207 Material Science I
ME 207 Material Science I Chapter 3 Properties in Tension and Compression Dr. İbrahim H. Yılmaz http://web.adanabtu.edu.tr/iyilmaz Automotive Engineering Adana Science and Technology University Introduction
More informationFig. 1. Different locus of failure and crack trajectories observed in mode I testing of adhesively bonded double cantilever beam (DCB) specimens.
a). Cohesive Failure b). Interfacial Failure c). Oscillatory Failure d). Alternating Failure Fig. 1. Different locus of failure and crack trajectories observed in mode I testing of adhesively bonded double
More information