INCREASING RUPTURE PREDICTABILITY FOR ALUMINUM

Size: px
Start display at page:

Download "INCREASING RUPTURE PREDICTABILITY FOR ALUMINUM"

Transcription

1 1

2 INCREASING RUPTURE PREDICTABILITY FOR ALUMINUM Influence of anisotropy Daniel Riemensperger, Adam Opel AG Paul Du Bois, PDB 2

3 CONTENT Introduction/motivation Isotropic & anisotropic material models Rupture criterion Conducted tests for characterization Validation Comparison Conclusion 3

4 INTRODUCTION / MOTIVATION Reducing weight + growing safety standards More ultra high strength materials Ductility and hardening as a safety buffer is diminished Rupture prediction essential for CAE driven product development Rupture prediction is limited by physical noises like material or geometry deviations by the applied numerical material and rupture model. Will the introduction of Anisotropy push this limitation? 4

5 Anisotropy DIRECTION DEPENDENCY Young's modulus A 90 A Yield strength 45 Hardening 0 Rolling direction Flow, necking and rupture Lankford coefficient R R = ε yy ε zz = ε yy ν ε xx = ε yy (ε xx + ε yy ) Ratio of lateral vs. thickness strain z x y z A - A 5

6 Force [N] Anisotropy TESTED ALUMINUM SHEET Young's modulus uniaxial tests Yield strength Hardening Flow, necking and rupture Lankford coefficient R 0 ~R 45 ~R 90 ~0.5 displacement [mm] Transversely isotropic Model handling same as isotropic 6

7 force force Comparison Von Mises vs Barlat YIELD CRITERION Von Mises (*MAT_024): σ 1 Hosford(isotropic) / Barlat(anisotropic) (*MAT_036): test sim σ 2 7 displacement Von Mises displacement Hosford σ 1 = 2 σ 2 (η = 1 3 )

8 true stress [MPa] Comparison Von Mises vs Barlat NECKING BEHAVIOR Von Mises curve is reverse engineered yield curves necking point σ = σ Barlat curve is purely test based pt of rupture Barlat Von Mises plastic strain [-] 8 test simulation ( 0.5 mm)

9 Rupture criterion TRIAXIALITY Capture stress state in one value (The Lode angle parameter is not needed for elements following plane stress ) For plane stress(s ZZ =0, t XZ =0, t YZ =0) follows : Definition : h = hydrostatic stress deviatoric stress compression shear tension -2/3-1/3 0 1/3 2/3 9

10 Damage accumulation GISSMO ε eq.pl. D = ΔD D = 1 IP deleted D 0 =1E-12 ε f (η) LCSDG rupture starts D crit = D(ε crit η ) Δε p ECRIT localization starts η 10 D = D crit σ = σ D = 1 σ = 0 Eq. plastic strain at rupture is not equal to ε f (η) Coupling reduces the strength of the element prior to element deletion ductile fracture

11 l = 50mm r = 80mm r = 5mm Triaxality tests TEST GEOMETRIES Shear specimen Tensile ratio Notched specimen Principles : Plane stress as long as possible (b/t>4) Scalability of element size r = 80mm l = 8mm η = Homogenous triaxiality in deformed area No local thickness reduction η~0 η~0.15 η~0.3 η =

12 Triaxality tests TEST GEOMETRIES - SHEAR Optimized radii and offsets to focus the load onto the center Symmetrical specimen : lateral deformation does not effect the test equipment Asymmetrical specimen : lateral deformation is test equipment 8 8 dependent Different rupture modes can be triggered for the same material 12

13 l = 50mm r = 80mm r = 5mm Triaxality tests TEST GEOMETRIES Shear specimen Tensile ratio Notched specimen Principles : Plane stress as long as possible (b/t>4) Scalability of element size r = 80mm l = 8mm η = Homogenous triaxiality in deformed area No local thickness reduction Internal moment dissipation η~0 η~0.15 η~0.3 η =

14 Barlat with GISSMO smooth l=50mm double shear 0 double shear 35 double shear tensile eq. plastic strain [-] lcsdg ecrit 1st eroded element 2nd eroded element notched r=80mm, l=8mm notched r=80mm notched r=5mm /3 2/3 Triaxiality [-] Test

15 Von Mises with GISSMO smooth l=50mm double shear 0 double shear 35 double shear tensile eq. plastic strain [-] lcsdg ecrit 1st eroded element 2nd eroded element notched r=80mm, l=8mm notched r=5mm /3 2/3 Triaxiality [-] Test

16 true stress Comparison VON MISES VS BARLAT Yield curves Damage curves eq. plastic strain [-] lcsdg Barlat lcsdg Von Mises ecrit Barlat ecrit Von Mises true plastic strain Lankford coefficient R (1) /3 2/3 Triaxiality [-]

17 16.5 Three point bending test SETUP, TEST Small roll formed beam with continuous laser welds 250 mm Rotational free cylindrical rests Cylindrical impactor 17

18 Three point bending test SETUP, SIMULATION Beam : Discretization [mm]: 0.5 (also 1.0, 1.5, 2.25, 4.5 not part of this presentation) Fully integrated shell elements (type 16) Laser weld as solid w/ constrained contact Rests : Rotational free 18 Double precision

19 Three point bending test TEST RESULTS Force [kn] mm/min 20 mm/min tests / 2 velocities Good reproducibility Only little strain rate dependency Variation in rupture deflection Displacement [mm]

20 Three point bending test TEST RESULTS VS SIMULATION Force [kn] 8 Von Mises Barlat Yielding is too soft Rupture too late Barlat and Von Mises similar Displacement [mm]

21 Three point bending test ADDITIONAL TEST EVALUATION HV hardness Uniform, but for weld line Inner and outer radius Smaller than intended (1.5 mm < 2.3 mm) Overall geometry Angles and lengths deviate Geometry has to be adjusted 21

22 Three point bending test ADDITIONAL TEST EVALUATION HV hardness Uniform, but for weld line Inner and outer radius Smaller than intended (1.5 mm < 2.3 mm) Overall geometry Angles and lengths deviate Geometry has to be adjusted 22

23 Three point bending test ADDITIONAL TEST EVALUATION HV hardness Uniform, but for weld line Inner and outer radius nominal adjusted 10 mm Smaller than intended (1.5 mm < 2.3 mm) Overall geometry Angles and lengths deviate Geometry has to be adjusted 23

24 Three point bending test TEST RESULTS VS SIMULATION 8 6 von Mises Barlat Model geometry adjusted to test Process simulation mapped Friction set to µ=0.1 from 0.2 Force [kn] 4 2 Best rupture prediction Von Mises Too optimistic Barlat Still optimistic but close to test Displacement [mm]

25 Three point bending test TEST RESULTS VS SIMULATION Von Mises Test Barlat 25

26 Three point bending test TEST RESULTS VS SIMULATION Bottom view Triaxiality Plastic strain Rupture imminent Barlat Von Mises 26

27 CONCLUSION An accurate yield criterion and flow law are fundamental, Von Mises law is not sufficient in this study Introduction of out of plain anisotropy has improved results significantly without increasing the model complexity Geometrical detail and process data have an immense impact on validation We need every piece of the puzzle 27

28 Daniel Riemensperger THANK YOU. 28

Anisotropic plasticity, anisotropic failure and their application to the simulation of aluminium extrusions under crash loads

Anisotropic plasticity, anisotropic failure and their application to the simulation of aluminium extrusions under crash loads Anisotropic plasticity, anisotropic failure and their application to the simulation of aluminium extrusions under crash loads Paul Du Bois, Consulting engineer Oasys LS-DYNA Users Meeting 28th January

More information

Lecture #7: Basic Notions of Fracture Mechanics Ductile Fracture

Lecture #7: Basic Notions of Fracture Mechanics Ductile Fracture Lecture #7: Basic Notions of Fracture Mechanics Ductile Fracture by Dirk Mohr ETH Zurich, Department of Mechanical and Process Engineering, Chair of Computational Modeling of Materials in Manufacturing

More information

Bone Tissue Mechanics

Bone Tissue Mechanics Bone Tissue Mechanics João Folgado Paulo R. Fernandes Instituto Superior Técnico, 2016 PART 1 and 2 Introduction The objective of this course is to study basic concepts on hard tissue mechanics. Hard tissue

More information

Lecture #8: Ductile Fracture (Theory & Experiments)

Lecture #8: Ductile Fracture (Theory & Experiments) Lecture #8: Ductile Fracture (Theory & Experiments) by Dirk Mohr ETH Zurich, Department of Mechanical and Process Engineering, Chair of Computational Modeling of Materials in Manufacturing 2015 1 1 1 Ductile

More information

Lecture 8. Stress Strain in Multi-dimension

Lecture 8. Stress Strain in Multi-dimension Lecture 8. Stress Strain in Multi-dimension Module. General Field Equations General Field Equations [] Equilibrium Equations in Elastic bodies xx x y z yx zx f x 0, etc [2] Kinematics xx u x x,etc. [3]

More information

Mechanical Properties of Materials

Mechanical Properties of Materials Mechanical Properties of Materials Strains Material Model Stresses Learning objectives Understand the qualitative and quantitative description of mechanical properties of materials. Learn the logic of

More information

UNIVERSITY OF SASKATCHEWAN ME MECHANICS OF MATERIALS I FINAL EXAM DECEMBER 13, 2008 Professor A. Dolovich

UNIVERSITY OF SASKATCHEWAN ME MECHANICS OF MATERIALS I FINAL EXAM DECEMBER 13, 2008 Professor A. Dolovich UNIVERSITY OF SASKATCHEWAN ME 313.3 MECHANICS OF MATERIALS I FINAL EXAM DECEMBER 13, 2008 Professor A. Dolovich A CLOSED BOOK EXAMINATION TIME: 3 HOURS For Marker s Use Only LAST NAME (printed): FIRST

More information

SEMM Mechanics PhD Preliminary Exam Spring Consider a two-dimensional rigid motion, whose displacement field is given by

SEMM Mechanics PhD Preliminary Exam Spring Consider a two-dimensional rigid motion, whose displacement field is given by SEMM Mechanics PhD Preliminary Exam Spring 2014 1. Consider a two-dimensional rigid motion, whose displacement field is given by u(x) = [cos(β)x 1 + sin(β)x 2 X 1 ]e 1 + [ sin(β)x 1 + cos(β)x 2 X 2 ]e

More information

Plasticity R. Chandramouli Associate Dean-Research SASTRA University, Thanjavur

Plasticity R. Chandramouli Associate Dean-Research SASTRA University, Thanjavur Plasticity R. Chandramouli Associate Dean-Research SASTRA University, Thanjavur-613 401 Joint Initiative of IITs and IISc Funded by MHRD Page 1 of 9 Table of Contents 1. Plasticity:... 3 1.1 Plastic Deformation,

More information

GISSMO Material Modeling with a sophisticated Failure Criteria

GISSMO Material Modeling with a sophisticated Failure Criteria GISSMO Material Modeling with a sophisticated Failure Criteria André Haufe, Paul DuBois, Frieder Neukamm, Markus Feucht Dynamore GmbH Industriestraße 2 70565 Stuttgart http://www.dynamore.de Motivation

More information

NORMAL STRESS. The simplest form of stress is normal stress/direct stress, which is the stress perpendicular to the surface on which it acts.

NORMAL STRESS. The simplest form of stress is normal stress/direct stress, which is the stress perpendicular to the surface on which it acts. NORMAL STRESS The simplest form of stress is normal stress/direct stress, which is the stress perpendicular to the surface on which it acts. σ = force/area = P/A where σ = the normal stress P = the centric

More information

Chapter 3. Load and Stress Analysis

Chapter 3. Load and Stress Analysis Chapter 3 Load and Stress Analysis 2 Shear Force and Bending Moments in Beams Internal shear force V & bending moment M must ensure equilibrium Fig. 3 2 Sign Conventions for Bending and Shear Fig. 3 3

More information

WORKSHOP Introduction to material characterization

WORKSHOP Introduction to material characterization WORKSHOP Introduction to material characterization Martin Helbig, David Koch DYNAmore GmbH, Germany 15 th German LS-DYNA Forum 2018 Bamberg, October 15, 2018 1 Motivation Example of material usage in a

More information

Development, implementation and Validation of 3-D Failure Model for Aluminium 2024 for High Speed Impact Applications

Development, implementation and Validation of 3-D Failure Model for Aluminium 2024 for High Speed Impact Applications Development, implementation and Validation of -D Failure Model for Aluminium 2024 for High Speed Impact Applications Paul Du Bois, Murat Buyuk, Jeanne He, Steve Kan NCAC-GWU th International LS-DYNA Users

More information

Recent Developments in Damage and Failure Modeling with LS-DYNA

Recent Developments in Damage and Failure Modeling with LS-DYNA Recent evelopments in amage and Failure Modeling with LS-YNA r. André Haufe ynamore GmbH Frieder Neukamm, r. Markus Feucht aimler AG Paul ubois Consultant r. Thomas Borvall ERAB 1 Technological challenges

More information

EMA 3702 Mechanics & Materials Science (Mechanics of Materials) Chapter 2 Stress & Strain - Axial Loading

EMA 3702 Mechanics & Materials Science (Mechanics of Materials) Chapter 2 Stress & Strain - Axial Loading MA 3702 Mechanics & Materials Science (Mechanics of Materials) Chapter 2 Stress & Strain - Axial Loading MA 3702 Mechanics & Materials Science Zhe Cheng (2018) 2 Stress & Strain - Axial Loading Statics

More information

4.MECHANICAL PROPERTIES OF MATERIALS

4.MECHANICAL PROPERTIES OF MATERIALS 4.MECHANICAL PROPERTIES OF MATERIALS The diagram representing the relation between stress and strain in a given material is an important characteristic of the material. To obtain the stress-strain diagram

More information

A rate-dependent Hosford-Coulomb model for predicting ductile fracture at high strain rates

A rate-dependent Hosford-Coulomb model for predicting ductile fracture at high strain rates EPJ Web of Conferences 94, 01080 (2015) DOI: 10.1051/epjconf/20159401080 c Owned by the authors, published by EDP Sciences, 2015 A rate-dependent Hosford-Coulomb model for predicting ductile fracture at

More information

Inverse identification of plastic material behavior using. multi-scale virtual experiments

Inverse identification of plastic material behavior using. multi-scale virtual experiments Inverse identification of plastic material behavior using multi-scale virtual experiments Debruyne 1 D., Coppieters 1 S., Wang 1 Y., Eyckens 2 P., Kuwabara 3 T., Van Bael 2 A. and Van Houtte 2 P. 1 Department

More information

Mechanical Engineering Ph.D. Preliminary Qualifying Examination Solid Mechanics February 25, 2002

Mechanical Engineering Ph.D. Preliminary Qualifying Examination Solid Mechanics February 25, 2002 student personal identification (ID) number on each sheet. Do not write your name on any sheet. #1. A homogeneous, isotropic, linear elastic bar has rectangular cross sectional area A, modulus of elasticity

More information

Chapter 7. Highlights:

Chapter 7. Highlights: Chapter 7 Highlights: 1. Understand the basic concepts of engineering stress and strain, yield strength, tensile strength, Young's(elastic) modulus, ductility, toughness, resilience, true stress and true

More information

Failure from static loading

Failure from static loading Failure from static loading Topics Quiz /1/07 Failures from static loading Reading Chapter 5 Homework HW 3 due /1 HW 4 due /8 What is Failure? Failure any change in a machine part which makes it unable

More information

If you take CT5143 instead of CT4143 then write this at the first of your answer sheets and skip problem 4 and 6.

If you take CT5143 instead of CT4143 then write this at the first of your answer sheets and skip problem 4 and 6. Delft University of Technology Faculty of Civil Engineering and Geosciences Structural Mechanics Section Write your name and study number at the top right-hand of your work. Exam CT4143 Shell Analysis

More information

Stress-Strain Behavior

Stress-Strain Behavior Stress-Strain Behavior 6.3 A specimen of aluminum having a rectangular cross section 10 mm 1.7 mm (0.4 in. 0.5 in.) is pulled in tension with 35,500 N (8000 lb f ) force, producing only elastic deformation.

More information

Experiments and Numerical Simulations on Stress-State-Dependence of Ductile Damage Criteria

Experiments and Numerical Simulations on Stress-State-Dependence of Ductile Damage Criteria Experiments and Numerical Simulations on Stress-State-Dependence of Ductile Damage Criteria Michael Brünig, Steffen Gerke and Daniel Brenner Abstract The paper deals with a series of new experiments and

More information

MECE 3321 MECHANICS OF SOLIDS CHAPTER 3

MECE 3321 MECHANICS OF SOLIDS CHAPTER 3 MECE 3321 MECHANICS OF SOLIDS CHAPTER 3 Samantha Ramirez TENSION AND COMPRESSION TESTS Tension and compression tests are used primarily to determine the relationship between σ avg and ε avg in any material.

More information

Material parameter identification for the numerical simulation of deep-drawing drawing of aluminium alloys

Material parameter identification for the numerical simulation of deep-drawing drawing of aluminium alloys Material parameter identification for the numerical simulation of deep-drawing drawing of aluminium alloys B.M. Chaparro, J.M. Antunes, A.J. Baptista, D.M. Rodrigues,, J.V. Fernandes, L.F. Menezes M2D'26

More information

Homework No. 1 MAE/CE 459/559 John A. Gilbert, Ph.D. Fall 2004

Homework No. 1 MAE/CE 459/559 John A. Gilbert, Ph.D. Fall 2004 Homework No. 1 MAE/CE 459/559 John A. Gilbert, Ph.D. 1. A beam is loaded as shown. The dimensions of the cross section appear in the insert. the figure. Draw a complete free body diagram showing an equivalent

More information

A Simple and Accurate Elastoplastic Model Dependent on the Third Invariant and Applied to a Wide Range of Stress Triaxiality

A Simple and Accurate Elastoplastic Model Dependent on the Third Invariant and Applied to a Wide Range of Stress Triaxiality A Simple and Accurate Elastoplastic Model Dependent on the Third Invariant and Applied to a Wide Range of Stress Triaxiality Lucival Malcher Department of Mechanical Engineering Faculty of Tecnology, University

More information

Samantha Ramirez, MSE. Stress. The intensity of the internal force acting on a specific plane (area) passing through a point. F 2

Samantha Ramirez, MSE. Stress. The intensity of the internal force acting on a specific plane (area) passing through a point. F 2 Samantha Ramirez, MSE Stress The intensity of the internal force acting on a specific plane (area) passing through a point. Δ ΔA Δ z Δ 1 2 ΔA Δ x Δ y ΔA is an infinitesimal size area with a uniform force

More information

This guide is made for non-experienced FEA users. It provides basic knowledge needed to start your fatigue calculations quickly.

This guide is made for non-experienced FEA users. It provides basic knowledge needed to start your fatigue calculations quickly. Quick Fatigue Analysis Guide This guide is made for non-experienced FEA users. It provides basic knowledge needed to start your fatigue calculations quickly. Experienced FEA analysts can also use this

More information

Bending Load & Calibration Module

Bending Load & Calibration Module Bending Load & Calibration Module Objectives After completing this module, students shall be able to: 1) Conduct laboratory work to validate beam bending stress equations. 2) Develop an understanding of

More information

Mechanics of Biomaterials

Mechanics of Biomaterials Mechanics of Biomaterials Lecture 7 Presented by Andrian Sue AMME498/998 Semester, 206 The University of Sydney Slide Mechanics Models The University of Sydney Slide 2 Last Week Using motion to find forces

More information

Evaluation of Material Models to Predict Material Failure in LS-DYNA

Evaluation of Material Models to Predict Material Failure in LS-DYNA Department of Construction Sciences Solid Mechanics ISRN LUTFD2/TFHF-16/5209-SE(1-55) Evaluation of Material Models to Predict Material Failure in LS-DYNA Master s Dissertation by Hjalmar Sandberg Oscar

More information

Card Variable MID RO E PR ECC QH0 FT FC. Type A8 F F F F F F F. Default none none none 0.2 AUTO 0.3 none none

Card Variable MID RO E PR ECC QH0 FT FC. Type A8 F F F F F F F. Default none none none 0.2 AUTO 0.3 none none Note: This is an extended description of MAT_273 input provided by Peter Grassl It contains additional guidance on the choice of input parameters beyond the description in the official LS-DYNA manual Last

More information

STRESS UPDATE ALGORITHM FOR NON-ASSOCIATED FLOW METAL PLASTICITY

STRESS UPDATE ALGORITHM FOR NON-ASSOCIATED FLOW METAL PLASTICITY STRESS UPDATE ALGORITHM FOR NON-ASSOCIATED FLOW METAL PLASTICITY Mohsen Safaei 1, a, Wim De Waele 1,b 1 Laboratorium Soete, Department of Mechanical Construction and Production, Ghent University, Technologiepark

More information

Structural Metals Lab 1.2. Torsion Testing of Structural Metals. Standards ASTM E143: Shear Modulus at Room Temperature

Structural Metals Lab 1.2. Torsion Testing of Structural Metals. Standards ASTM E143: Shear Modulus at Room Temperature Torsion Testing of Structural Metals Standards ASTM E143: Shear Modulus at Room Temperature Purpose To determine the shear modulus of structural metals Equipment Tinius-Olsen Lo-Torq Torsion Machine (figure

More information

Chapter 6: Plastic Theory

Chapter 6: Plastic Theory OHP Mechanical Properties of Materials Chapter 6: Plastic Theory Prof. Wenjea J. Tseng 曾文甲 Department of Materials Engineering National Chung Hsing University wenjea@dragon.nchu.edu.tw Reference: W. F.

More information

Module-4. Mechanical Properties of Metals

Module-4. Mechanical Properties of Metals Module-4 Mechanical Properties of Metals Contents ) Elastic deformation and Plastic deformation ) Interpretation of tensile stress-strain curves 3) Yielding under multi-axial stress, Yield criteria, Macroscopic

More information

Constitutive model for quasi-static deformation of metallic sandwich cores

Constitutive model for quasi-static deformation of metallic sandwich cores INTERNATIONAL JOURNAL FOR NUMERICAL METHODS IN ENGINEERING Int. J. Numer. Meth. Engng 2004; 61:2205 2238 Published online 18 October 2004 in Wiley InterScience (www.interscience.wiley.com). DOI: 10.1002/nme.1142

More information

Modelling the behaviour of plastics for design under impact

Modelling the behaviour of plastics for design under impact Modelling the behaviour of plastics for design under impact G. Dean and L. Crocker MPP IAG Meeting 6 October 24 Land Rover door trim Loading stages and selected regions Project MPP7.9 Main tasks Tests

More information

Use Hooke s Law (as it applies in the uniaxial direction),

Use Hooke s Law (as it applies in the uniaxial direction), 0.6 STRSS-STRAIN RLATIONSHIP Use the principle of superposition Use Poisson s ratio, v lateral longitudinal Use Hooke s Law (as it applies in the uniaxial direction), x x v y z, y y vx z, z z vx y Copyright

More information

Mechanics of Materials Primer

Mechanics of Materials Primer Mechanics of Materials rimer Notation: A = area (net = with holes, bearing = in contact, etc...) b = total width of material at a horizontal section d = diameter of a hole D = symbol for diameter E = modulus

More information

Tensile stress strain curves for different materials. Shows in figure below

Tensile stress strain curves for different materials. Shows in figure below Tensile stress strain curves for different materials. Shows in figure below Furthermore, the modulus of elasticity of several materials effected by increasing temperature, as is shown in Figure Asst. Lecturer

More information

Characterizations of Aluminum Alloy Sheet Materials Numisheet 2005

Characterizations of Aluminum Alloy Sheet Materials Numisheet 2005 Characterizations of Aluminum Alloy Sheet Materials Numisheet 25 John C. Brem, Frederic Barlat, Robert E. Dick, and Jeong-Whan Yoon Alcoa Technical Center, PA, 1569-1, USA Abstract. This report reproduces

More information

ANSYS Mechanical Basic Structural Nonlinearities

ANSYS Mechanical Basic Structural Nonlinearities Lecture 4 Rate Independent Plasticity ANSYS Mechanical Basic Structural Nonlinearities 1 Chapter Overview The following will be covered in this Chapter: A. Background Elasticity/Plasticity B. Yield Criteria

More information

Multiaxial Fatigue. Professor Darrell F. Socie. Department of Mechanical Science and Engineering University of Illinois at Urbana-Champaign

Multiaxial Fatigue. Professor Darrell F. Socie. Department of Mechanical Science and Engineering University of Illinois at Urbana-Champaign Multiaxial Fatigue Professor Darrell F. Socie Department of Mechanical Science and Engineering University of Illinois at Urbana-Champaign 2001-2011 Darrell Socie, All Rights Reserved Contact Information

More information

FCP Short Course. Ductile and Brittle Fracture. Stephen D. Downing. Mechanical Science and Engineering

FCP Short Course. Ductile and Brittle Fracture. Stephen D. Downing. Mechanical Science and Engineering FCP Short Course Ductile and Brittle Fracture Stephen D. Downing Mechanical Science and Engineering 001-015 University of Illinois Board of Trustees, All Rights Reserved Agenda Limit theorems Plane Stress

More information

Laboratory 4 Bending Test of Materials

Laboratory 4 Bending Test of Materials Department of Materials and Metallurgical Engineering Bangladesh University of Engineering Technology, Dhaka MME 222 Materials Testing Sessional.50 Credits Laboratory 4 Bending Test of Materials. Objective

More information

Crack Tip Plastic Zone under Mode I Loading and the Non-singular T zz -stress

Crack Tip Plastic Zone under Mode I Loading and the Non-singular T zz -stress Crack Tip Plastic Zone under Mode Loading and the Non-singular T -stress Yu.G. Matvienko Mechanical Engineering Research nstitute of the Russian Academy of Sciences Email: ygmatvienko@gmail.com Abstract:

More information

20. Rheology & Linear Elasticity

20. Rheology & Linear Elasticity I Main Topics A Rheology: Macroscopic deformation behavior B Linear elasticity for homogeneous isotropic materials 10/29/18 GG303 1 Viscous (fluid) Behavior http://manoa.hawaii.edu/graduate/content/slide-lava

More information

Introduction to Engineering Materials ENGR2000. Dr. Coates

Introduction to Engineering Materials ENGR2000. Dr. Coates Introduction to Engineering Materials ENGR2 Chapter 6: Mechanical Properties of Metals Dr. Coates 6.2 Concepts of Stress and Strain tension compression shear torsion Tension Tests The specimen is deformed

More information

Practice Final Examination. Please initial the statement below to show that you have read it

Practice Final Examination. Please initial the statement below to show that you have read it EN175: Advanced Mechanics of Solids Practice Final Examination School of Engineering Brown University NAME: General Instructions No collaboration of any kind is permitted on this examination. You may use

More information

1 332 Laboratories 1. 2 Computational Exercises 1 FEA of a Cantilever Beam... 1 Experimental Laboratory: Tensile Testing of Materials...

1 332 Laboratories 1. 2 Computational Exercises 1 FEA of a Cantilever Beam... 1 Experimental Laboratory: Tensile Testing of Materials... 1 332 Laboratories Contents 1 332 Laboratories 1 2 Computational Exercises 1 FEA of a Cantilever Beam.......................................... 1 Experimental Laboratory: Tensile Testing of Materials..........................

More information

The objective of this experiment is to investigate the behavior of steel specimen under a tensile test and to determine it's properties.

The objective of this experiment is to investigate the behavior of steel specimen under a tensile test and to determine it's properties. Objective: The objective of this experiment is to investigate the behavior of steel specimen under a tensile test and to determine it's properties. Introduction: Mechanical testing plays an important role

More information

MECHANICS OF MATERIALS

MECHANICS OF MATERIALS Third E CHAPTER 2 Stress MECHANICS OF MATERIALS Ferdinand P. Beer E. Russell Johnston, Jr. John T. DeWolf Lecture Notes: J. Walt Oler Texas Tech University and Strain Axial Loading Contents Stress & Strain:

More information

3D Elasticity Theory

3D Elasticity Theory 3D lasticity Theory Many structural analysis problems are analysed using the theory of elasticity in which Hooke s law is used to enforce proportionality between stress and strain at any deformation level.

More information

* Many components have multiaxial loads, and some of those have multiaxial loading in critical locations

* Many components have multiaxial loads, and some of those have multiaxial loading in critical locations Why do Multiaxial Fatigue Calculations? * Fatigue analysis is an increasingly important part of the design and development process * Many components have multiaxial loads, and some of those have multiaxial

More information

NUMERICAL AND EXPERIMENTAL STUDY OF FAILURE IN STEEL BEAMS UNDER IMPACT CONDITIONS

NUMERICAL AND EXPERIMENTAL STUDY OF FAILURE IN STEEL BEAMS UNDER IMPACT CONDITIONS Blucher Mechanical Engineering Proceedings May 2014, vol. 1, num. 1 www.proceedings.blucher.com.br/evento/10wccm NUMERICAL AND EXPERIMENTAL STUDY OF FAILURE IN STEEL BEAMS UNDER IMPACT CONDITIONS E. D.

More information

Anisotropic modeling of short fibers reinforced thermoplastics materials with LS-DYNA

Anisotropic modeling of short fibers reinforced thermoplastics materials with LS-DYNA Anisotropic modeling of short fibers reinforced thermoplastics materials with LS-DYNA Alexandre Hatt 1 1 Faurecia Automotive Seating, Simplified Limited Liability Company 1 Abstract / Summary Polymer thermoplastics

More information

STANDARD SAMPLE. Reduced section " Diameter. Diameter. 2" Gauge length. Radius

STANDARD SAMPLE. Reduced section  Diameter. Diameter. 2 Gauge length. Radius MATERIAL PROPERTIES TENSILE MEASUREMENT F l l 0 A 0 F STANDARD SAMPLE Reduced section 2 " 1 4 0.505" Diameter 3 4 " Diameter 2" Gauge length 3 8 " Radius TYPICAL APPARATUS Load cell Extensometer Specimen

More information

AERO 214. Lab II. Measurement of elastic moduli using bending of beams and torsion of bars

AERO 214. Lab II. Measurement of elastic moduli using bending of beams and torsion of bars AERO 214 Lab II. Measurement of elastic moduli using bending of beams and torsion of bars BENDING EXPERIMENT Introduction Flexural properties of materials are of interest to engineers in many different

More information

five Mechanics of Materials 1 ARCHITECTURAL STRUCTURES: FORM, BEHAVIOR, AND DESIGN DR. ANNE NICHOLS SUMMER 2017 lecture

five Mechanics of Materials 1 ARCHITECTURAL STRUCTURES: FORM, BEHAVIOR, AND DESIGN DR. ANNE NICHOLS SUMMER 2017 lecture ARCHITECTURAL STRUCTURES: FORM, BEHAVIOR, AND DESIGN DR. ANNE NICHOLS SUMMER 2017 lecture five mechanics www.carttalk.com of materials Mechanics of Materials 1 Mechanics of Materials MECHANICS MATERIALS

More information

Cracks Jacques Besson

Cracks Jacques Besson Jacques Besson Centre des Matériaux UMR 7633 Mines ParisTech PSL Research University Institut Mines Télécom Aγνωστ oς Θεoς Outline 1 Some definitions 2 in a linear elastic material 3 in a plastic material

More information

Fatigue and Fracture

Fatigue and Fracture Fatigue and Fracture Multiaxial Fatigue Professor Darrell F. Socie Mechanical Science and Engineering University of Illinois 2004-2013 Darrell Socie, All Rights Reserved When is Multiaxial Fatigue Important?

More information

Mechanics PhD Preliminary Spring 2017

Mechanics PhD Preliminary Spring 2017 Mechanics PhD Preliminary Spring 2017 1. (10 points) Consider a body Ω that is assembled by gluing together two separate bodies along a flat interface. The normal vector to the interface is given by n

More information

Discrete Element Modelling of a Reinforced Concrete Structure

Discrete Element Modelling of a Reinforced Concrete Structure Discrete Element Modelling of a Reinforced Concrete Structure S. Hentz, L. Daudeville, F.-V. Donzé Laboratoire Sols, Solides, Structures, Domaine Universitaire, BP 38041 Grenoble Cedex 9 France sebastian.hentz@inpg.fr

More information

PURE BENDING. If a simply supported beam carries two point loads of 10 kn as shown in the following figure, pure bending occurs at segment BC.

PURE BENDING. If a simply supported beam carries two point loads of 10 kn as shown in the following figure, pure bending occurs at segment BC. BENDING STRESS The effect of a bending moment applied to a cross-section of a beam is to induce a state of stress across that section. These stresses are known as bending stresses and they act normally

More information

Lecture 15 Strain and stress in beams

Lecture 15 Strain and stress in beams Spring, 2019 ME 323 Mechanics of Materials Lecture 15 Strain and stress in beams Reading assignment: 6.1 6.2 News: Instructor: Prof. Marcial Gonzalez Last modified: 1/6/19 9:42:38 PM Beam theory (@ ME

More information

MATERIALS. Why do things break? Why are some materials stronger than others? Why is steel tough? Why is glass brittle?

MATERIALS. Why do things break? Why are some materials stronger than others? Why is steel tough? Why is glass brittle? MATERIALS Why do things break? Why are some materials stronger than others? Why is steel tough? Why is glass brittle? What is toughness? strength? brittleness? Elemental material atoms: A. Composition

More information

Engineering Solid Mechanics

Engineering Solid Mechanics }} Engineering Solid Mechanics 1 (2013) 1-8 Contents lists available at GrowingScience Engineering Solid Mechanics homepage: www.growingscience.com/esm Impact damage simulation in elastic and viscoelastic

More information

MATERIAL MECHANICS, SE2126 COMPUTER LAB 2 PLASTICITY

MATERIAL MECHANICS, SE2126 COMPUTER LAB 2 PLASTICITY MATERIAL MECHANICS, SE2126 COMPUTER LAB 2 PLASTICITY PART A INTEGRATED CIRCUIT An integrated circuit can be thought of as a very complex maze of electronic components and metallic connectors. These connectors

More information

Mechanics of Materials MENG 270 Fall 2003 Exam 3 Time allowed: 90min. Q.1(a) Q.1 (b) Q.2 Q.3 Q.4 Total

Mechanics of Materials MENG 270 Fall 2003 Exam 3 Time allowed: 90min. Q.1(a) Q.1 (b) Q.2 Q.3 Q.4 Total Mechanics of Materials MENG 70 Fall 00 Eam Time allowed: 90min Name. Computer No. Q.(a) Q. (b) Q. Q. Q.4 Total Problem No. (a) [5Points] An air vessel is 500 mm average diameter and 0 mm thickness, the

More information

MATERIAL MODELS FOR THE

MATERIAL MODELS FOR THE Project work report MATERIAL MODELS FOR THE DEFORMATION AND FAILURE OF HIGH STRENGTH STEEL Katia BONI August 2008 to January 2009 Supervisor: Larsgunnar NILSSON 2 Contents 1 Introduction 6 1.1 Background.........................................

More information

Lecture #10: Anisotropic plasticity Crashworthiness Basics of shell elements

Lecture #10: Anisotropic plasticity Crashworthiness Basics of shell elements Lecture #10: 151-0735: Dynamic behavior of materials and structures Anisotropic plasticity Crashworthiness Basics of shell elements by Dirk Mohr ETH Zurich, Department of Mechanical and Process Engineering,

More information

Johns Hopkins University What is Engineering? M. Karweit MATERIALS

Johns Hopkins University What is Engineering? M. Karweit MATERIALS Why do things break? Why are some materials stronger than others? Why is steel tough? Why is glass brittle? What is toughness? strength? brittleness? Elemental material atoms: MATERIALS A. Composition

More information

GATE SOLUTIONS E N G I N E E R I N G

GATE SOLUTIONS E N G I N E E R I N G GATE SOLUTIONS C I V I L E N G I N E E R I N G From (1987-018) Office : F-16, (Lower Basement), Katwaria Sarai, New Delhi-110016 Phone : 011-65064 Mobile : 81309090, 9711853908 E-mail: info@iesmasterpublications.com,

More information

Modelling of ductile failure in metal forming

Modelling of ductile failure in metal forming Modelling of ductile failure in metal forming H.H. Wisselink, J. Huetink Materials Innovation Institute (M2i) / University of Twente, Enschede, The Netherlands Summary: Damage and fracture are important

More information

ME Final Exam. PROBLEM NO. 4 Part A (2 points max.) M (x) y. z (neutral axis) beam cross-sec+on. 20 kip ft. 0.2 ft. 10 ft. 0.1 ft.

ME Final Exam. PROBLEM NO. 4 Part A (2 points max.) M (x) y. z (neutral axis) beam cross-sec+on. 20 kip ft. 0.2 ft. 10 ft. 0.1 ft. ME 323 - Final Exam Name December 15, 2015 Instructor (circle) PROEM NO. 4 Part A (2 points max.) Krousgrill 11:30AM-12:20PM Ghosh 2:30-3:20PM Gonzalez 12:30-1:20PM Zhao 4:30-5:20PM M (x) y 20 kip ft 0.2

More information

D : SOLID MECHANICS. Q. 1 Q. 9 carry one mark each. Q.1 Find the force (in kn) in the member BH of the truss shown.

D : SOLID MECHANICS. Q. 1 Q. 9 carry one mark each. Q.1 Find the force (in kn) in the member BH of the truss shown. D : SOLID MECHANICS Q. 1 Q. 9 carry one mark each. Q.1 Find the force (in kn) in the member BH of the truss shown. Q.2 Consider the forces of magnitude F acting on the sides of the regular hexagon having

More information

A Semianalytical Model for the Simulation of Polymers

A Semianalytical Model for the Simulation of Polymers A Semianalytical Model for the Simulation of Polymers Paul Du Bois 3, Stefan Kolling 1, Markus Feucht 1 & André Haufe 2 1 DaimlerChrysler AG, Sindelfingen, Germany 2 Dynamore GmbH, Stuttgart, Germany 3

More information

ME 2570 MECHANICS OF MATERIALS

ME 2570 MECHANICS OF MATERIALS ME 2570 MECHANICS OF MATERIALS Chapter III. Mechanical Properties of Materials 1 Tension and Compression Test The strength of a material depends on its ability to sustain a load without undue deformation

More information

University of Sheffield The development of finite elements for 3D structural analysis in fire

University of Sheffield The development of finite elements for 3D structural analysis in fire The development of finite elements for 3D structural analysis in fire Chaoming Yu, I. W. Burgess, Z. Huang, R. J. Plank Department of Civil and Structural Engineering StiFF 05/09/2006 3D composite structures

More information

Lecture 8 Viscoelasticity and Deformation

Lecture 8 Viscoelasticity and Deformation Read: pg 130 168 (rest of Chpt. 4) 1 Poisson s Ratio, µ (pg. 115) Ratio of the strain in the direction perpendicular to the applied force to the strain in the direction of the applied force. For uniaxial

More information

EQUIVALENT FRACTURE ENERGY CONCEPT FOR DYNAMIC RESPONSE ANALYSIS OF PROTOTYPE RC GIRDERS

EQUIVALENT FRACTURE ENERGY CONCEPT FOR DYNAMIC RESPONSE ANALYSIS OF PROTOTYPE RC GIRDERS EQUIVALENT FRACTURE ENERGY CONCEPT FOR DYNAMIC RESPONSE ANALYSIS OF PROTOTYPE RC GIRDERS Abdul Qadir Bhatti 1, Norimitsu Kishi 2 and Khaliq U Rehman Shad 3 1 Assistant Professor, Dept. of Structural Engineering,

More information

BioMechanics and BioMaterials Lab (BME 541) Experiment #5 Mechanical Prosperities of Biomaterials Tensile Test

BioMechanics and BioMaterials Lab (BME 541) Experiment #5 Mechanical Prosperities of Biomaterials Tensile Test BioMechanics and BioMaterials Lab (BME 541) Experiment #5 Mechanical Prosperities of Biomaterials Tensile Test Objectives 1. To be familiar with the material testing machine(810le4) and provide a practical

More information

Theory at a Glance (for IES, GATE, PSU)

Theory at a Glance (for IES, GATE, PSU) 1. Stress and Strain Theory at a Glance (for IES, GATE, PSU) 1.1 Stress () When a material is subjected to an external force, a resisting force is set up within the component. The internal resistance force

More information

MMJ1133 FATIGUE AND FRACTURE MECHANICS A - INTRODUCTION INTRODUCTION

MMJ1133 FATIGUE AND FRACTURE MECHANICS A - INTRODUCTION INTRODUCTION A - INTRODUCTION INTRODUCTION M.N.Tamin, CSMLab, UTM Course Content: A - INTRODUCTION Mechanical failure modes; Review of load and stress analysis equilibrium equations, complex stresses, stress transformation,

More information

Volume 2 Fatigue Theory Reference Manual

Volume 2 Fatigue Theory Reference Manual Volume Fatigue Theory Reference Manual Contents 1 Introduction to fatigue 1.1 Introduction... 1-1 1. Description of the applied loading... 1-1.3 Endurance curves... 1-3 1.4 Generalising fatigue data...

More information

Finite Element Simulation of Bar-Plate Friction Welded Joints Steel Product Subjected to Impact Loading

Finite Element Simulation of Bar-Plate Friction Welded Joints Steel Product Subjected to Impact Loading Finite Element Simulation of Bar-Plate Friction Welded Joints Steel Product Subjected to Impact Loading Yohanes, a,* Muftil Badri, a Panji Adino, a Dodi Sofyan Arief, a and Musthafa Akbar, a a) Department

More information

Mechanics of Earthquakes and Faulting

Mechanics of Earthquakes and Faulting Mechanics of Earthquakes and Faulting www.geosc.psu.edu/courses/geosc508 Surface and body forces Tensors, Mohr circles. Theoretical strength of materials Defects Stress concentrations Griffith failure

More information

Aim of the study Experimental determination of mechanical parameters Local buckling (wrinkling) Failure maps Optimization of sandwich panels

Aim of the study Experimental determination of mechanical parameters Local buckling (wrinkling) Failure maps Optimization of sandwich panels METNET Workshop October 11-12, 2009, Poznań, Poland Experimental and numerical analysis of sandwich metal panels Zbigniew Pozorski, Monika Chuda-Kowalska, Robert Studziński, Andrzej Garstecki Poznan University

More information

Mechanics of Earthquakes and Faulting

Mechanics of Earthquakes and Faulting Mechanics of Earthquakes and Faulting www.geosc.psu.edu/courses/geosc508 Overview Milestones in continuum mechanics Concepts of modulus and stiffness. Stress-strain relations Elasticity Surface and body

More information

UNIT I SIMPLE STRESSES AND STRAINS

UNIT I SIMPLE STRESSES AND STRAINS Subject with Code : SM-1(15A01303) Year & Sem: II-B.Tech & I-Sem SIDDHARTH GROUP OF INSTITUTIONS :: PUTTUR Siddharth Nagar, Narayanavanam Road 517583 QUESTION BANK (DESCRIPTIVE) UNIT I SIMPLE STRESSES

More information

Reference material Reference books: Y.C. Fung, "Foundations of Solid Mechanics", Prentice Hall R. Hill, "The mathematical theory of plasticity",

Reference material Reference books: Y.C. Fung, Foundations of Solid Mechanics, Prentice Hall R. Hill, The mathematical theory of plasticity, Reference material Reference books: Y.C. Fung, "Foundations of Solid Mechanics", Prentice Hall R. Hill, "The mathematical theory of plasticity", Oxford University Press, Oxford. J. Lubliner, "Plasticity

More information

Fracture mechanics fundamentals. Stress at a notch Stress at a crack Stress intensity factors Fracture mechanics based design

Fracture mechanics fundamentals. Stress at a notch Stress at a crack Stress intensity factors Fracture mechanics based design Fracture mechanics fundamentals Stress at a notch Stress at a crack Stress intensity factors Fracture mechanics based design Failure modes Failure can occur in a number of modes: - plastic deformation

More information

STRENGTH OF MATERIALS-I. Unit-1. Simple stresses and strains

STRENGTH OF MATERIALS-I. Unit-1. Simple stresses and strains STRENGTH OF MATERIALS-I Unit-1 Simple stresses and strains 1. What is the Principle of surveying 2. Define Magnetic, True & Arbitrary Meridians. 3. Mention different types of chains 4. Differentiate between

More information

Module 5: Failure Criteria of Rock and Rock masses. Contents Hydrostatic compression Deviatoric compression

Module 5: Failure Criteria of Rock and Rock masses. Contents Hydrostatic compression Deviatoric compression FAILURE CRITERIA OF ROCK AND ROCK MASSES Contents 5.1 Failure in rocks 5.1.1 Hydrostatic compression 5.1.2 Deviatoric compression 5.1.3 Effect of confining pressure 5.2 Failure modes in rocks 5.3 Complete

More information

7.6 Stress in symmetrical elastic beam transmitting both shear force and bending moment

7.6 Stress in symmetrical elastic beam transmitting both shear force and bending moment 7.6 Stress in symmetrical elastic beam transmitting both shear force and bending moment à It is more difficult to obtain an exact solution to this problem since the presence of the shear force means that

More information

6.4 A cylindrical specimen of a titanium alloy having an elastic modulus of 107 GPa ( psi) and

6.4 A cylindrical specimen of a titanium alloy having an elastic modulus of 107 GPa ( psi) and 6.4 A cylindrical specimen of a titanium alloy having an elastic modulus of 107 GPa (15.5 10 6 psi) and an original diameter of 3.8 mm (0.15 in.) will experience only elastic deformation when a tensile

More information