1 INECTOBLEND FABS007 General Purpose ABS FABS007 is available in black color only. Further information and details are available upon request Melt Flow 230C / 3.8kg, nominal D Tensile Yield. 73 (23 ) Tensile Break. 73 (23 ) 6, Flexural Strength. 73 (23 ) Flexural Modulus. 73 (23 ) 9, , ,277 Shear Modulus. 73 (23 ) D 4065 Izod Impact, notched. 73 (23 ), (3.2mm) Izod Impact, notched. 22 (30 ), (3.2mm) Izod Impact, notched. 73 (23 ), 4 mm ftlb/in ftlb/in Instrumented Impact Total Energy. 73 (23 ), (3.2mm) ftlb 264 (1.82 ), Load 66 (0.45 ), Load CLTE ( ) 5.3 E5 9.5 E5 UL 94 Flame Class (1.47mm) UL 94 Rev. 1.02
2 INECTOBLEND FABSPC003 ABS/PC Blend FABSPC003 is available with internal and external lubricants, UV stabilized and other modifications. Further information and details are available upon request Tensile Yield. 73 (23 ) Tensile Break. 73 (23 ) 7, Flexural Strength. 73 (23 ) Flexural Modulus. 73 (23 ) 11, , ,898 Izod Impact, notched. 73 (23 ), (3.2mm) Izod Impact, notched. 22 (30 ), (3.2mm) Izod Impact, notched. 73 (23 ), 4 mm ftlb/in ftlb/in Instrumented Impact Total Energy. 73 (23 ), (3.2mm) Instrumented Impact Total Energy. 22 (30 ), (3.2mm), ftlb ftlb (1.82 ), Load 66 (0.45 ), Load CLTE ( ) 4.0 E5 7.2 E5 Vicat Softening Temperature, 50N ISO UL 94 Flame Class (1.47mm) UL 94 Rev. 1.02
3 INECTOBLEND FPA66233 Nylon 6 6, 33 Glass Fiber Reinforced, Heat Stabilized reported DAM. Further information is available upon request Reported 50 RH are available upon request Mold Shrinkage, flow, (3.2mm) Mold Shrinkage, crossflow, (3.2mm) Water Absorption, saturation, 73F (23C) Fiberglass Content D Tensile Modulus. 73 (23 ) Tensile Break. 73 (23 ) Tensile Break. 73 (23 ) ISO 5271/2 ISO 5271/2 Psi 25, , Flexural Strength. 73 (23 ) Flexural Modulus. 73 (23 ) ISO 178 ISO ,500 Izod Impact Strength, notched. 73 (23 ), (3.2mm) Izod Impact, Strength, notched. 23, 4 mm Izod Impact Strength, notched. 30, 4 mm Charpy Impact Strength. 23, 4 mm 1/A 1/A ISO 179/1eU ftlb/in (1.82 ), Load 66 (0.45 ), Load 1.82 Load, flatwise ISO 751/ CLTE ( ) 1.38 E E5 Melting Point ISO UL 94 Flame Class (1.47mm) 2.00mm +/ 0.2 mm UL 94 ISO 3795 <100 provided without any warranty or guarantee. Each user of the material should make his own test to determine the suitability of the material for his use. Therefore, it is understood and agreed that the customer assumes and hereby releases AGS Technology, Inc. from all liabilities, incurred in connection with the use of AGS products, technical assistance and information. Rev
4 INECTOBLEND FPC1 Impact Modified Grade Polycarbonate FPC1 is available with internal and external lubricants, UV stabilized and other modifications. Further information and details are available upon request Melt Flow 300C / 1.2kg, nominal D Tensile Yield. 73 (23 ) Tensile Break. 73 (23 ) 8, Flexural Strength. 73 (23 ) Flexural Modulus. 73 (23 ) 12, , ,277 Shear Modulus. 73 (23 ) D , Izod Impact, notched. 73 (23 ), (3.2mm) Izod Impact, notched. 22 (30 ), (3.2mm) Izod Impact, notched. 73 (23 ), 4 mm ftlb/in ftlb/in Charpy Impact, notched. 73 (23 ), 4 mm ISO Instrumented Impact Total Energy. 73 (23 ), (3.2mm) Instrumented Impact Total Energy. 22 (30 ), (3.2mm), ftlb ftlb (1.82 ), Load 66 (0.45 ), Load CLTE ( ) 4.31 E E5 Vicat Softening Temperature, 50N ISO UL 94 Flame Class (1.47mm) UL 94 Rev. 1.02
5 INECTOBLEND FPOM110 Medium Viscosity Acetal Copolymer FPOM110 is available in black color, UV stabilized and with other modifications. Further information and details are available upon request Water Absorption. Saturation 73F (23C) Melt Flow Rate D Tensile Yield. 73 (23 ) Tensile Break. 73 (23 ) 9, Flexural Strength. 73 (23 ) Flexural Modulus. 73 (23 ) 13, , ,691 Izod Impact, notched. 73 (23 ), (3.2mm) Izod Impact, notched. 73 (23 ), 4 mm ftlb/in (1.82 ), Load 66 (0.45 ), Load Melting Point D CLTE. 40 to +35 (40 to +95 ) in/in/ in/in/ UL 94 Flame Class (1.47mm) UL 94 Rev.1.02
6 INECTOBLEND FPP135 Polypropylene Copolymer FPP135 is available in a variety of viscosities and other modifications. Further information and details are available upon request Tensile Yield. 73 (23 ) Tensile Yield. 73 (23 ) 3, Flexural Strength. 73 (23 ) Flexural Modulus. 73 (23 ) 4, , ,000 Izod Impact, notched. 73 (23 ), (3.2mm) ftlb/in Dart Impact. 22 (30 ), (3.2mm) GM9300P ftlb (1.82 ), Load 66 (0.45 ), Load CLTE. +75 ( ) 5.5 E5 9.9 E5 Thermal Oxidative Stability. 150 D 3012 hours 350 hours 350 UL 94 Flame Class (1.47mm) GM UL 94 ISO 3795 < 100 < 100 Rev. 1.02
7 INECTOBLEND FPP330 Polypropylene Homopolymer, 30 Glass Fiber Reinforced, Heat Stabilized / Reported DAM Fiberglass Content D Tensile Break. 73 (23 ) Tensile Break. 73 (23 ) Tensile Modulus. 73 (23 ) 11, , ,800 Flexural Strength. 73 (23 ) Flexural Modulus. 73 (23 ) , ,100 Izod Impact Strength, notched. 73 (23 ), (3.2mm) Izod Impact Strength, notched. 73 (23 ), 4 mm Izod Impact Strength, notched. 22 (30 ), 4 mm D 256 ftlb/in Charpy Impact Strength, notched. 73 (23 ), 4 mm Charpy Impact Strength, notched. 22 (30 ), 4 mm ISO 179 ISO (1.82 ), Load 66 (0.45 ), Load CLTE ( ) Flow CLTE ( ) Cross Flow 4.4 E5 4.0 E UL 94 Flame Class (1.47mm) UL 94 ISO 3795 < 100 Rev.4.0
DuPont Zenite LCP. liquid crystal polymer resin PRODUCT AND PROPERTY GUIDE
DuPont Zenite LCP liquid crystal polymer resin PRODUCT AND PROPERTY GUIDE DuPont Zenite LCP liquid crystal polymer resin Description Zenite is the DuPont trademark for its liquid crystal polymer (LCP)
More informationChimei ABS POLYLAC. Properties Guide.
www.wahsin.com Chimei ABS POLYLAC Guide Wah Sin Industrial Pte Ltd 519 Balestier Road #02-02 Le Shantier Singapore 329852 Tel : +65 6252 5647 No. 24, Jalan Canggih 7, Taman Perindustrian Cemerlang, 81800
More informationCOMPATIBILIZERS VISCOSITY CHAIN EXTENDERS MODIFIERS XIBOND BLEND OPTIMIZERS COUPLING AGENTS SURFACE MODIFIERS
COMPATIBILIZERS CHAIN EXTENDERS VISCOSITY MODIFIERS XIBOND BLEND OPTIMIZERS SURFACE MODIFIERS COUPLING AGENTS XIBOND Blend Optimizers At Polyscope, we offer a wide range of polymer additives for the compounding
More informationMolded/Machined Both Both Machined Machined Both Dielectric Strength V/mil D ,000
Material Properties Properties Units ASTM Test Method ABS Acetal CPVC G10-FR4 Halar (ECTFE) Molded/Machined Both Both Machined Machined Both Dielectric Strength V/mil D-149 812.8 500 1250 400 2,000 Elongation
More informationAppendix. A 1 Properties of areas.* *Symbols used are: A = area I = moment of inertia S = Section modulus
Appendix A 1 Properties of areas.* *Symbols used are: A = area I = moment of inertia S = Section modulus r = radius of gyration = I/A J = polar moment of inertia Z p = polar section modulus Circle R D
More informationMarkForged's Onyx is a material that is ideal for customer-facing parts that need to look good while standing up to industrial requirements.
ONYX MarkForged's Onyx is a material that is ideal for customer-facing parts that need to look good while standing up to industrial requirements. Onyx is based on a remarkably tough nylon, but also provides
More informationELECTRICAL SOLUTIONS
Ties Panduct Type FL Flexible Material: Flexible Polypropylene UL Recognized continuous use temperature: 9 F (5 C) H W UL 94 flaability rating of V-2 Factory applied adhesive tape provided for easy mounting
More informationGENERAL PROPERTIES OF FLOMAT SHEET MOULDING COMPOUND
PAGE: 1 OF 5 PROPERTY TEST METHOD UNITS 512/20 513/15 514/15 515/15 516/25 DENSITY BS-2782-PART 5-509A-1970 gm/cc 1.70-1.90 1.70-1.90 1.70-1.90 1.70-1.90 1.70-1.90 MOULD SHRINKAGE BS-2782-PART 6-640A-1979
More informationPeriodic table with the elements associated with commercial polymers in color.
Polymers 1. What are polymers 2. Polymerization 3. Structure features of polymers 4. Thermoplastic polymers and thermosetting polymers 5. Additives 6. Polymer crystals 7. Mechanical properties of polymers
More informationOverview of Maleic-Anhydride-Grafted Polyolefin Coupling Agents
Overview of Maleic-Anhydride-Grafted Polyolefin Coupling Agents A guide to understanding their uses, benefits, functions, selection, and developments Louis W. Martin, Addcomp North America Inc. Fundamentals
More informationResponse Surface Models for Optimization of Wheat Straw- Polypropylene Composite Formulations
Proceedings of the 014 International Conference on Industrial Engineering and Operations Management Bali, Indonesia, January 7 9, 014 Response Surface Models for Optimization of Wheat Straw- Polypropylene
More informationSizes 48" x 96" (1.22m x 2.44m) Custom sheet sizes available upon request
Applications Decorative paneling Partitions Water features Signage Furniture Displays and more... Attributes Excellent UV properties High impact resistance - 17x greater than glass and 4x greater than
More informationMoldflow Report Beaumont Logo. Performed by: Beaumont Technologies Requested by: Customer
Moldflow Report Beaumont Logo Performed by: Beaumont Technologies Requested by: Customer Objective To analyze the BTI Logo part in order to determine an optimal gate location. To thoroughly evaluate the
More informationAbstract Process Economics Program Report 51C POLYMER NANOCOMPOSITES (June 2002)
Abstract Process Economics Program Report 51C POLYMER NANOCOMPOSITES (June 2002) With the rush of interest in all things related to nanotechnology, polymer nanocomposites represent one of the emerging
More informationMathematics and Science in Schools in Sub-Saharan Africa
Mathematics and Science in Schools in Sub-Saharan Africa MATERIAL SCIENCE Introduction to Material Properties What Material Scientists Do Physical Properties Melting & Boiling Points Magnetism Color Physical
More informationMATERIALS SCIENCE POLYMERS
POLYMERS 1) Types of Polymer (a) Plastic Possibly the largest number of different polymeric materials come under the plastic classification. Polyethylene, polypropylene, polyvinyl chloride, polystyrene,
More informationStress Analysis Report
Stress Analysis Report Analyzed File: Majakkarunko.iam Autodesk Inventor Version: 2013 SP2 (Build 170200200, 200) Creation Date: 29.5.2013, 7:01 Simulation Author: NJu Summary: Project Info (iproperties)
More informationPANDUCT Type E Slotted Wall Wiring Duct
PANDUCT Type E Slotted Wall Wiring Duct Type E Wiring Duct Standard Colors : LG DG WH Light Gray Dark Gray White BL Black IB IntrinsicBlue Colors shown are approximate. Ordering Information: Order number
More informationMaterial Characterization of Natural Fiber Acrylic Thermoset Composites
Material Characterization of Natural Fiber Acrylic Thermoset Composites Andre Bendo Jeremy Funk, John Norton, Dr. Gero Nordmann & Dr. Michael Kalbe BASF Corporation 08/01/2011 1 Presentation verview Key
More informationStandard Test Methods for Flexural Properties of Unreinforced and Reinforced Plastics and Electrical Insulating Materials 1
NOTICE: This standard has either been superseded and replaced by a new version or discontinued. Contact ASTM International (www.astm.org) for the latest information. Designation: D 790 00 An American National
More information135WRx-2 Direct Thermal Film
Specifications may change without notice Last update: Aug. 2016 Ref: PS-1531 (Rev. 3) S P E C I F I C A T I O N 135WRx-2 S H E E T This product specification sheet provides the detail to aid you in identifying
More informationEXPERIMENTAL STUDY ON YOUNG S MODULUS E OF A POLYMER COMPOSITE REINFORCED BY NANO TITANIUM DIOXIDE PARTICLES
Vietnam Journal of Mechanics, VAST, Vol. 34, No. (202), pp. 9 25 EXPERIMENTAL STUDY ON YOUNG S MODULUS E OF A POLYMER COMPOSITE REINFORCED BY NANO TITANIUM DIOXIDE PARTICLES Nguyen Dinh Duc, Dinh Khac
More informationLV-MV INSULATORS INSULATORS
LV-MV INSULATORS LV-MV INSULATORS CONTENTS LOW VOLTAGE & MEDIUM VOLTAGE INSULATORS 0 0 0 0 0 0 0 0 /0 LV Insulators type SK LV Insulators type SR LV Insulators type RD LV Insulators type DS LV Insulators
More informationColor Availability Clear Standard colors stocked (thin gauge only) Custom colors available by special order.
Applications Aquariums Displays Fountains Projection screens Furniture Optical lenses Port hole windows Sight glass Scientific applications Point of purchase Vacuum chambers Bio-safety chambers and more...
More informationPolymer engineering syllabus (BSc)
Polymer engineering syllabus (BSc) First semester Math 1 Physics 1 Physics 1 lab General chemistry General chemistry lab workshop Second semester Math 2 Physics 2 Organic chemistry 1 Organic chemistry
More informationMICROMECHANICAL DEFORMATIONS IN PARTICULATE FILLED POLYMERS: THE EFFECT OF ADHESION
MICROMECHANICAL DEFORMATIONS IN PARTICULATE FILLED POLYMERS: THE EFFECT OF ADHESION K. Renner, J. Móczó, B. Pukánszky Laboratory of Plastics and Rubber Technology, Department of Physical Chemistry and
More informationPD626 Polypro Replacement Material Evaluation and Selection
PD626 Polypro Replacement Material Evaluation and Selection This test data provided is based on representative testing done in the lab and is provided to show the similarities between PD626 and 11R12A
More informationHexPly F655 Resin Systems for Advanced Composites
HexPly F655 Resin Systems for Advanced Composites Product Data Description HexPly F655 is a bismaleimide resin that cures via an addition reaction in a toughened two-phase thermoset matrix with no condensation
More informationLecture No. (1) Introduction of Polymers
Lecture No. (1) Introduction of Polymers Polymer Structure Polymers are found in nature as proteins, cellulose, silk or synthesized like polyethylene, polystyrene and nylon. Some natural polymers can also
More informationR CHEM ADD PYN - TS. Technical Data Sheet. Physical Properties: Advantages: Applications: Use Level: SR NO. PROPERTIES UNITS ANALYSIS
R CHEM ADD PYN - TS R CHEM ADD PYN is a speciality additive developed fo antifibrillation masterbatches/compounds to reduce water carry over problem on high speed tape line at high speed operation. 1 Appearnce
More informationThe rate of oxygen consumption from a cone calorimeter as an original criterion of evaluation of the fire risk for the Resin Kit polymers
European Journal of Environmental and Safety Sciences 2014 2(2): 23-27 ISSN 1339-472X European Science and Research Institute (Original Research Paper) The rate of oxygen consumption from a cone calorimeter
More informationF ( C) Cure Epoxy Resin System. Out life 30 days at 70 F (21 C)
301 250-300 F (120-150 C) Cure Epoxy Resin System Typical applications Sporting goods Marine Medical Industrial manufacturing Out life 30 days at 70 F (21 C) Shelf life 6 months at 40 F (4 C) 12 months
More informationCoupling agent to improve adhesion of organic resins to inorganic surfaces DESCRIPTION
XIAMETER OFS-6032 Coupling agent to improve adhesion of organic resins to inorganic surfaces FEATURES Improved adhesion Good resin wet-out Increased wet and dry composite tensile strength BENEFITS Organic
More informationAPPLICATIONS OF NANOMER IN NANOCOMPOSITES: FROM CONCEPT TO REALITY
APPLICATIONS OF NANOMER IN NANOCOMPOSITES: FROM CONCEPT TO REALITY Tie Lan, Jaewhan Cho, Ying Liang, Jerry Qian, and Peter Maul Nanocor, Inc. 1500 West Shure Drive Arlington Heights, IL 60004 ABSTRACT
More informationCHAPTER 4 MODELING OF MECHANICAL PROPERTIES OF POLYMER COMPOSITES
CHAPTER 4 MODELING OF MECHANICAL PROPERTIES OF POLYMER COMPOSITES 4. Introduction Fillers added to polymer matrices as additives are generally intended for decreasing the cost (by increase in bulk) of
More informationThermal Conductivity, Electrical Conductivity and Mechanical Properties of Polypropylene/Graphene and Polystyrene/ Graphene Nanocomposites
Thermal Conductivity, Electrical Conductivity and Mechanical Properties of Polypropylene/Graphene and Polystyrene/ Graphene Nanocomposites Peter Ryzyk 1, Thomas Hurson 1, Joo Yong Yi 1, Joshua Weinstein
More informationAnisotropic modeling of short fibers reinforced thermoplastics materials with LS-DYNA
Anisotropic modeling of short fibers reinforced thermoplastics materials with LS-DYNA Alexandre Hatt 1 1 Faurecia Automotive Seating, Simplified Limited Liability Company 1 Abstract / Summary Polymer thermoplastics
More informationFlexural properties of polymers
A2 _EN BUDAPEST UNIVERSITY OF TECHNOLOGY AND ECONOMICS FACULTY OF MECHANICAL ENGINEERING DEPARTMENT OF POLYMER ENGINEERING Flexural properties of polymers BENDING TEST OF CHECK THE VALIDITY OF NOTE ON
More informationPolymers in Modified Asphalt Robert Q. Kluttz KRATON Polymers
Polymers in Modified Asphalt Robert Q. Kluttz KRATON Polymers Polymers in Modified Asphalt Types of Polymers Compatibility of Polymers Effects of Polymers Analysis of polymers Recovery of PMA What Is a
More informationSECTION 23 - METRIC DESIGN INFORMATION. Table of Contents
SECTION 23 - METRIC DESIGN INFORMATION Table of Contents Metric System Conversions and Abbreviations... 23-3 EXTREN Availability List... 23-4 EXTREN vs. Traditional Materials... 23-6 SECTION 23 METRIC
More information1. Demonstrate that the minimum cation-to-anion radius ratio for a coordination number of 8 is
1. Demonstrate that the minimum cation-to-anion radius ratio for a coordination number of 8 is 0.732. This problem asks us to show that the minimum cation-to-anion radius ratio for a coordination number
More information2. Amorphous or Crystalline Structurally, polymers in the solid state may be amorphous or crystalline. When polymers are cooled from the molten state
2. Amorphous or Crystalline Structurally, polymers in the solid state may be amorphous or crystalline. When polymers are cooled from the molten state or concentrated from the solution, molecules are often
More informationAdvances in the Reactive Processing of Polymer Composites Based on Magnesium Hydroxide*
Advances in the Reactive Processing of Polymer Composites Based on Magnesium Hydroxide* a a b V. KHUNOVÁ and b C. M. LIAUW Department of Plastics and Rubber, Faculty of Chemical Technology, Slovak University
More informationEffect of Rubber Content of ABS on the Mechanical Properties of ABS/Clay Nanocomposites
Composite Interfaces 16 (2009) 337 346 www.brill.nl/ci Effect of Rubber Content of ABS on the Mechanical Properties of ABS/Clay Nanocomposites Hyun-Kyo Kim a, Gue-Hyun Kim b,, Byung-Mook Cho b and Chang-Sik
More informationPERFORMANCE TEST REPORT. Rendered to: VELUX AMERICA, INC. PRODUCT: SUN TUNNEL Domes TYPES: Acrylic and Polycarbonate
PERFORMANCE TEST REPORT Rendered to: VELUX AMERICA, INC. PRODUCT: SUN TUNNEL Domes TYPES: Acrylic and Polycarbonate Report No.: E3490.01-106-31 Report Date: 07/13/15 Test Record Retention Date: 06/18/19
More informationPalm Frond Calculations
Palm Frond Calculations 250 E. Broad Street Suite 500 Columbus, Ohio 43215 Paul J. Ford and Company Job # 33201-0014 Reference PJF Drawing # 33201-0014 Sheet S-3, Dated 02/06/2001 PAGE 1 OF 6 FORMULAS
More informationInnovative Products February 2016
Bison Pedestals & Accessories Material Testing Test Description Bison Results ASTM D792 ASTM D638 ASTM G155 ASTM G26 ASTM D790 ASTM D256 0 ASTM D5420 50.0 ASTM D2240 ASTM D648 231 ASTM D648 231 ASTM D635
More informationTensile stress strain curves for different materials. Shows in figure below
Tensile stress strain curves for different materials. Shows in figure below Furthermore, the modulus of elasticity of several materials effected by increasing temperature, as is shown in Figure Asst. Lecturer
More informationEngineering Composite Reinforcements
Facing up to the Challenges of Natural Fibres as Potential Engineering Composite Reinforcements Jim Thomason Composites Week @Leuven September 16-20 th 2013 Leuven, Belgium Jim why are you so down on Natural
More informationASPECTS CONCERNING TO THE MECHANICAL PROPERTIES OF THE GLASS / FLAX / EPOXY COMPOSITE MATERIAL
5 th International Conference Advanced Composite Materials Engineering COMAT 2014 16-17 October 2014, Braşov, Romania ASPECTS CONCERNING TO THE MECHANICAL PROPERTIES OF THE GLASS / FLAX / EPOXY COMPOSITE
More informationMATERIALES PARA EL DESARROLLO SUSTENTABLE
MATERIALES PARA EL DESARROLLO SUSTENTABLE Dra. Patricia Eisenberg Coordinadora de la Unidad Técnica Tecnología a de Materiales INTI-Pl Plásticos patsy@inti.gov.ar Bio Polymers or Biobased Polymers Renewable
More informationA tribute to Eero Saarinen and the North Chirstian Church
orphosis A tribute to Eero Saarinen and the North Chirstian Church ero mit chapel inspiration I have always remembered one night on my travels as a student when I sat in a mountain village in Sparta.
More informationIMPACT PROPERTIES OF POLYMERIC NANOCOMPOSITES WITH DIFFERENT SHAPE OF NANOPARTICLES. Robert VALEK a, Jaroslav HELL a
IMPACT PROPERTIES OF POLYMERIC NANOCOMPOSITES WITH DIFFERENT SHAPE OF NANOPARTICLES Robert VALEK a, Jaroslav HELL a a SVUM, a. s., Podnikatelska 565, 19 11 Prague, Czech Republic, valek@svum.cz Abstract
More informationA Project on Wear and its Relation to Ball Valves. A project for MANE 6960 By Robert Sayre Submitted 12/9/2013
A Project on Wear and its Relation to Ball Valves A project for MANE 6960 By Robert Sayre Submitted 12/9/2013 Introduction Ball valves have many possible applications; they typically have low pressure
More informationUSA Mexico
1.800.231.6074 USA 001.800.426.1447 Mexico 1.800.231.6074 USA 001.800.426.1447 Mexico 1.800.231.6074 USA 001.800.426.1447 Mexico 1.800.231.6074 USA 001.800.426.1447 Mexico 1.800.231.6074 USA 001.800.426.1447
More informationInstrumented Impact Testing
Prüfen mit Verstand Instrumented Impact Testing Helmut Fahrenholz Agenda Why impact testing? Typical DWT standards Impact methods Energy, speed and mass in DWT Results evaluation acc. standards 2 Why impact
More informationF ( C) Cure Epoxy Resin System. Out life 30 days at 70 F (21 C)
301 250-300 F (121-149 C) Cure Epoxy Resin System Typical applications Sporting goods Marine Medical Industrial manufacturing Benefits/features Excellent mechanical properties Moderate tack Good toughness
More informationPERFORMANCE OF PP/CLAY NANOCOMPOSITES WITH EDGE FUNCTIONALIZED CLAY
PERFORMANCE OF PP/CLAY NANOCOMPOSITES WITH EDGE FUNCTIONALIZED CLAY Sharad Kumar and K. Jayaraman Department of Chemical Engineering and Materials Science Michigan State University, East Lansing, MI 48824
More informationINFLUENCE OF FLOWABILITY AND MAH-CONTENT OF MALEATED POLYOLEFINES ON RHEOLOGICAL AND MECHANICAL INTERACTION EFFECTS OF WOOD FILLERS IN POLYOLEFINES
59 th ILMENAU SCIENTIFIC COLLOQUIUM Technische Universität Ilmenau, 11 15 September 2017 URN: urn:nbn:de:gbv:ilm1-2017iwk-093:2 INFLUENCE OF FLOWABILITY AND MAH-CONTENT OF MALEATED POLYOLEFINES ON RHEOLOGICAL
More informationHELOXY Epoxy Functional Modifiers
Product Selector HELXY Epoxy Functional Modifiers Momentive's epoxy functional product line of HELXY Modifiers offers formulators the ability to choose between monofunctional and polyfunctional glycidyl
More informationIn Situ Ultrasonic NDT of Fracture and Fatigue in Composites
ECNDT 26 - Mo.2.6.5 In Situ Ultrasonic NDT of Fracture and Fatigue in Composites I. SOLODOV, K. PFLEIDERER, and G. BUSSE Institute for Polymer Testing and Polymer Science (IKP), Non-destructive Testing
More informationEffect of crystallinity on properties. Melting temperature. Melting temperature. Melting temperature. Why?
Effect of crystallinity on properties The morphology of most polymers is semi-crystalline. That is, they form mixtures of small crystals and amorphous material and melt over a range of temperature instead
More informationReliable Test Results
Intelligent testing Johannes J.Bührle - Agenda Reliable test results are a fundamental and highly topical aspect of materials testing. Using suitable examples we would like to show you how we view this
More informationOne Corporate Drive, Suite 106, Bedford, PA USA
DESIGN GUIDE Revised: 4/2012 One Corporate Drive, Suite 106, Bedford, PA 15522-7401 USA Phone: 814-623-8125 Sales Fax: 814-623-6032 Website: www.bedfordreinforced.com E-mail: frpsales@bedfordreinforced.com
More informationThermal and mechanical properties of several phthalonitrile resin system
Thermal and mechanical properties of several phthalonitrile resin system Heng Zhou, Feng Liu, Yuehai Li, Tong Zhao* Institute of Chemistry, Chinese Academy of Sciences, Beijing, 100190, China Abstract:An
More informationIMPACT BEHAVIOUR OF POLYMERS
1 APPLICATION OF FRACTURE MECHANICS TO THE IMPACT BEHAVIOUR OF POLYMERS by EVANGELIA PLATI B.Sc.(Eng.), M.Sc., D.I.C. A thesis submitted for the degree of Doctor of Philosophy. of the University of London
More information2008 International ANSYS Conference
2008 International ANSYS Conference Plastic Injection Molding Using ANSYS Sarah Luo Ph.D. Senior. Mechanical Engineer Aurora Optical Inc. Daniel Robinson Senior Consulting Engineer PADT Inc. 2008 ANSYS,
More informationDATA SHEET FOR COMPOUND TEV
TEFLON/FEP ENCAPSULATED VITON DATA SHEET FOR COMPOUND TEV Compound Features: Virtually chemically inert encapsulation material. Better elasticity and sealing ability than a solid PTFE O Ring. FDA compliant
More informationMethod for Determining Flexural Property Changes of Polymeric Materials Upon Accelerated Aging in Refrigerant/Lubricant Mixtures
Purdue University Purdue e-pubs International Refrigeration and Air Conditioning Conference School of Mechanical Engineering 199 Method for Determining Flexural Property Changes of Polymeric Materials
More informationAC Line Rated Ceramic Disc Capacitors Class X1, 760 V AC, Class Y1, 500 V AC
AC Line Rated Ceramic Disc Capacitors Class X1, 760 V AC, Class Y1, 500 V AC FEATURES Complying with IEC 60384-14 4 th edition Can pass 10 kv pulses (10 per polarity) Withstands 85 / 85 / 1000 h test Reduced
More information6.37 Determine the modulus of resilience for each of the following alloys:
6.37 Determine the modulus of resilience for each of the following alloys: Yield Strength Material MPa psi Steel alloy 550 80,000 Brass alloy 350 50,750 Aluminum alloy 50 36,50 Titanium alloy 800 116,000
More informationLong term ageing of polypropylene foam. The results of testing performed after 18 years of exposure in a subsea environment
Long term ageing of polypropylene foam. The results of testing performed after 18 years of exposure in a subsea environment A. Jackson, E. Simonsen Bredero Shaw AS T. Stark R. Nixon Borealis Group AG B.
More informationPolyethylene Chemical Resistance. ARM Fall Conference 2015, Denver CO. Carmine D Agostino, Technical Service and Application Development
Polyethylene Chemical Resistance Workshop ARM Fall Conference 2015, Denver CO Carmine D Agostino, Technical Service and Application Development 1 Contents Introduction Definition Chemical Effects on Polyethylene
More informationri [11111 IlL DIRECTIONAL PROPERTIES Of GLASS-FABRIC-BASE PLASTIC LAMINATE PANELS Of SIZES THAT DO NOT IBUCICLE (P-Q1lAtVjr) No.
Supplement to DIRECTIONAL PROPERTIES Of GLASS-FABRIC-BASE PLASTIC LAMINATE PANELS Of SIZES THAT DO NOT IBUCICLE (P-Q1lAtVjr) No. 1803-13 November 1955 This Report is One of a Series issued hi Cooperation
More informationEpoxy resins for electrotechnical applications
Epoxy resins for electrotechnical applications Epoxy resins for electrotechnical applications ELANTAS Europa offers a complete range of of products that can be used in in electrical engineering for the
More informationDeformation of Polymers. Version 2.1. Boban Tanovic, MATTER David Dunning, University of North London
Deformation of Polymers Version 2.1 Boban Tanovic, MATTER David Dunning, University of North London Assumed Pre-knowledge It is assumed that the user is familiar with the terms elasticity, stress, strain,
More informationSynthetic Fused Silica Optical and technical grades
SCHOTT LITHOTEC FUSED SILICA Synthetic Fused Silica Optical and technical grades Schott Lithotec Fused Silica LithosilTMQ is available in six different quality grades: LithosilTMQT is not specified concerning
More informationCompany Businness Units
Rev.no. 23M, 23.1.2019 Company Businness Units FUNCTIONAL POWDERS FUNCTIONAL MODIFIERS MASTERBATCHES POLYMER ALLOYS R & D COMPATIBILIZERS & COUPLING AGENTS Products Pipeline 2018 Compatibilizers are used
More informationSee https://pubs.acs.org/sharingguidelines for options on how to legitimately share published articles.
INDEX Downloaded via 148.251.232.83 on June 15, 2018 at 06:15:49 (UTC). See https://pubs.acs.org/sharingguidelines for options on how to legitimately share published articles. A Absorption spectra of cellulose
More informationRosalite 9148 UV D 9148
Rosalite 9148 UV Colour: Application: dark rose light tinted sunglare filter with contrast intensification red / yellow and high UV - absorption filter category 1 acc. to DIN EN 1836 The subsequent properties
More informationmy!wind Ltd 5 kw wind turbine Static Stability Specification
my!wind Ltd 5 kw wind turbine Static Stability Specification 1 P a g e 0 3 / 0 4 / 2 0 1 4 Contents Contents... 2 List of Changes... 2 Appendixes... 2 General remarks... 3 1. Introduction... 4 2. Geometry...
More informationInstrumented Pendulum Impact Testing for Plastics
Prüfen mit Verstand Instrumented Pendulum Impact Testing for Plastics testxpo 2015 Instrumented Impact Testing Agenda Pendulum Impact Testing - Basics Instrumented Impact Testing Tests and Curves Summary
More informationIII. Molecular Structure Chapter Molecular Size Size & Shape
III. Molecular Structure Chapter 3. 3. Molecular Size Size & Shape Molecular Structure (1)Molecular Size & Shape Size : molecular weight molecular weight distribution Shape : branching (2) Molecular Flexibility
More informationEFFECTS OF TEMPERATURE AND ENVIRONMENT ON MECHANICAL PROPERTIES OF TWO CONTINUOUS CARBON- FIBER AUTOMOTIVE STRUCTURAL COMPOSITES. M. B.
ORNL/TM-2003/117 EFFECTS OF TEMPERATURE AND ENVIRONMENT ON MECHANICAL PROPERTIES OF TWO CONTINUOUS CARBON- FIBER AUTOMOTIVE STRUCTURAL COMPOSITES M. B. Ruggles-Wrenn DOCUMENT AVAILABILITY Reports produced
More informationCharpy Impact Response of Glass Fiber Reinforced Composite with Nano Graphene Enhanced Epoxy
Periodicals of Engineering and Natural Scinces ISSN 2303-4521 Vol.5, No.3, November 2017, pp. 341~346 Available online at: http://pen.ius.edu.ba Charpy Impact Response of Glass Fiber Reinforced Composite
More informationGLASS POLYVINYL CHLORIDE/ MONTMORILLONITE NANOCOMPOSITES Transition temperature and mechanical properties
6458 Journal of Thermal Analysis and Calorimetry, Vol. 78 (2004) GLASS POLYVINYL CHLORIDE/ MONTMORILLONITE NANOCOMPOSITES Transition temperature and mechanical properties W. Xu 1,2 *,M.Ge 1 and W.-P. Pan
More informationThe TSM-DS. TSM-DS Family of Dimensionally Stable Low Loss Laminates. Benefits & Applications:
The TSM-DS family is comprised of thermally stable, industry leading low loss cores (Df = 0.0010 / 0.0011 [DS/DS3] at 10 GHz) that can be manufactured with the predictability and consistency of the best
More informationChapter. Materials. 1.1 Notations Used in This Chapter
Chapter 1 Materials 1.1 Notations Used in This Chapter A Area of concrete cross-section C s Constant depending on the type of curing C t Creep coefficient (C t = ε sp /ε i ) C u Ultimate creep coefficient
More informationThe Development Of A High Temperature And Acid Resistant Fire Retardant Resin
The Development Of A High Temperature And Acid Resistant Fire Retardant Resin Bruce Curry October 3-6, 2001 ABSTRACT Composites made with polyester and vinyl ester res- ins are resistant to acidic environments.
More informationNonlinear Modeling of Fiber-Reinforced Elastomers and the Response of a Rubber Muscle Actuator
Nonlinear Modeling of Fiber-Reinforced Elastomers and the Response of a Rubber Muscle Actuator Larry D. Peel, Ph.D.* Department of Mechanical & Industrial Engineering Texas A&M Univ. - Kingsville David
More informationSolid Tantalum Surface Mount Chip Capacitors TANTAMOUNT, Molded Case, for Medical Instruments
Solid Tantalum Surface Mount Chip Capacitors TANTAMOUNT, Molded Case, for Medical Instruments FEATURES For non-life support medical applications High reliability Weibull grading options DC leakage at 0.005
More informationMECHANICS OF MATERIALS
CHATR Stress MCHANICS OF MATRIALS and Strain Axial Loading Stress & Strain: Axial Loading Suitability of a structure or machine may depend on the deformations in the structure as well as the stresses induced
More informationStructure-Property Investigation of Functional Resins for UV-Curable Gaskets
Structure-Property Investigation of Functional Resins for UV-Curable Gaskets Joel D. Schall and Eric Edo-Hernandez Henkel Corporation Rocky Hill, CT USA Introduction The main purpose of this work was to
More informationSmall Signal Zener Diodes, Dual
DZ-V-G Series Small Signal Zener Diodes, Dual PRIMERY CHARACTERISTICS PARAMETER VALUE UNIT range nom.. to V Test current T specification Pulse current FEATURES Dual silicon planar Zener diodes, common
More informationD Y N A M I C M E C H A N I C A L A N A L Y S I S A N D I T S A D V A N T A G E S O V E R D E F L E C T I O N T E M P E R A T U R E U N D E R L O A D
D Y N A M I C M E C H A N I C A L A N A L Y S I S A N D I T S A D V A N T A G E S O V E R D E F L E C T I O N T E M P E R A T U R E U N D E R L O A D Sujan E. Bin Wadud TA Instruments 9 Lukens Drive, New
More informationMELT FLOW INDEX (MFI)
MELT FLOW INDEX (MFI) The melt flow index (MFI) is a measure of the ease of flow of the melt of a thermoplastic polymer. It is defined as the mass of polymer, in grams, flowing in ten minutes through a
More informationPOLYMER SCIENCE : lecture 1. Dr. Hanaa J. Alshimary Second class Poly. Eng. Dep. Introduction of Polymers Polymer poly mer Monomer Polymerization
Introduction of Polymers Polymer - The word polymer is the Greek word : poly means many and mer means unit or parts, A Polymer is a large molecule that comprises repeating structural units joined by the
More information3D Compression Molding
Autodesk Simulation Moldflow Insight 2014 3D Compression Molding Executive summary In this work, the simulation results from a program developed for the three-dimensional analysis of compression molding
More informationShree Tirupati Polypack
POLYPROPYLENE CHEMICAL RESISTANCE TABLE POLYPROPYLENE INTRODUCTION: The table in this documents summarizes the data given in a number of Polypropylene Chemical resistance tables at present in use in various
More informationSusterra Propanediol A Renewable Resource for Unsaturated Polyester Resins
TECHNICAL BULLETIN Susterra Propanediol A Renewable Resource for Unsaturated Polyester Resins WILMINGTON, Del., July 9, 2008 Opportunities for Susterra Propanediol (1,3- propanediol) in unsaturated polyester
More information