AO291 Issue date: Product Data FASSON Transfer Polyimide Matt White TC11 / S8088 / BG50 Wh

Transcription

1 FASSON Transfer Polyimide Matt White TC11 / S8088 / BG50 Wh Facestock A matt white topcoated polyimide film with very high dimensional stability, heat and chemical. The high opacity white topcoat is specifically designed for thermal transfer printing and offers good scratch, scuff, high temperature and solvent. Basis weight: 55 g/m² ISO 536 Caliper: 0,045 mm ISO 534 Adhesive S8088 is a high performance acrylic adhesive with excellent heat and chemical. Type: Solvent acrylic Coat weight: 27 g/m² Initial Tack: 220 N/m FTM 9 glass Peel Adhesion: 330 N/m FTM 2 steel 24 hrs. Min. application temperature: +10 C Min. service temperature: -40 C Max. peak temperature: +260 C Liner BG50 Wh: siliconized, bleached, super-calendered liner. Good die-cutting and matrix stripping. Suitable for roll-to-roll conversion. Basis weight: 80 g/m² ISO 536 Caliper: 0,073 mm ISO 534 Transparency: 47 % DIN This liner is not recommended for sheeting. Total construction caliper 0,145 mm Applications and use This product is ideal for labeling printed circuit boards. It is able to withstand surface mount circuit board processes on either the top or bottom side of the board. This product can also be used on the top side of the board in mixed processes and suitable for use on the bottom side when directly exposed to wave solder environment. Application tests are recommended. Printing and conversion The high opacity matte white top coat was specifically designed for thermal transfer printing. The choice of thermal transfer printer and ribbon influences the overall print quality and environmental. We recommend the use of resin ribbons, for example DNP300, DNP510 or Ricoh B110CR. Testing is recommended to ensure satisfactory print results and chemical. For printing high density barcodes an increased temperature setting of the thermal transfer printer might be required. Due to the low caliper of the facestock, automatic dispensing and application should be thoroughly tested prior to committing to production. UL Recognition This product meets the requirements as stated in UL 969 for indoor use, including thermal transfer printing with DNP R300, R510, TR4070, Iimak SP300, Ricoh B110C and B110CR. The UL file number is MH For specific information on approved conditions, see appendix 2. RoHS / Regulation 2002/95/EU and 2011/65/EC The substances listed in article 4 lid 1 of 2002/95/EC and 2011/65/EC (RoHS) are not intentionally used in this product. The concentration limits of these substances will not exceed the set maximum concentration limits as provided in the proposed amendment for 2002/95/EU and 2011/65/EC. Shelf life One year when stored at 22 C and 50 %rh. 1/5

2 FASSON Transfer Polyimide Matt White TC11 / S8088 / BG50 Wh Appendix 1: Performance Data Note: the following technical data should be considered representative or typical only and should not be used for specification purposes. Peel Adhesion: FTM1: 180, 300 mm/min in N/25mm. Surface dwell time 20 min dwell time 24 hrs Epoxy Printed Circuit Board 4,5 7 Stainless steel 4,5 6,5 Short term high temperature The label material has been tested on Epoxy Printed Circuit Board. A typical reflow solder profile with a maximum temperature peak of 260 C has been processed. No visible changes could be noticed. Print is still legible. Chemical Resistance The performance results are based on simulation of a typical PCB cleaning process including a simulation of a solder process. Cleaning agent Cleaner agent base Process Wash time Temperature ( C) Rinse time Hot air drying 80 ( C) Visual appearance Vigon US (25%) 1 Water based Ultrasonic 5 min 50 5 min 10 min No change Vigon A200 (30%) 1 Water based Ultrasonic 5 min 50 5 min 10 min No change Vigon A300 (33%) 1 Water based Ultrasonic 5 min 50 5 min 10 min No change Zestron FA+ 1 Semi-aqueous Ultrasonic 5 min 50 5 min 10 min No change Atron AC205 (15%) 1 Water based Ultrasonic 5 min 50 5 min 10 min No change 1 Dr. O.K. Wack-Chemie GmbH 2/5

3 Thermal Transfer Printing: Printability Physical Resistance Flat head printers: Ribbon Settings speed energy Print Quality 1 ANSI Grade 2 Scratch Tape Armor AXR A ++ + Dai Nippon R A ++ + Dai Nippon R A ++ + Iimak SP A Ricoh B110 A A o o Ricoh B110 CR A The print tests were performed with the printer Zebra Stripe S-500. Near edge printers: Ribbon Settings Print Quality 1 ANSI Grade 2 Scratch Tape Ricoh B120 Ec 6 /s o A - - Sony TR /s + A o + The print tests were performed with the printer Avery TTX 450 Near Edge. 1 Print Quality: ++: excellent +: good o: acceptable -: poor 2 ANSI (American National Standards Institute) Grade,information about barcode quality: A: excellent B: good C: acceptable D: readable with difficulty Chemical Resistance The printed samples passed a simulation of a typical PCB cleaning processes (including solder process simulation) as described beforehand. Afterwards the evaluation took place. R300 R510 B110 CR Vigon US (25%) Vigon A200 (30%) Vigon A300 (33%) Zestron FA Atron AC205 (15%) : good (no change) o: acceptable (minor change, still readable) -: poor 2 Dr. O.K. Wack-Chemie GmbH 3/5

4 Appendix 2: Compliance Data UL Underwriters Laboratories File Number: MH17205 This material is UL recognized for indoor use for exposure to high humidity or occasional exposure to water. Substrate Minimum Temperature ( C) Maximum Temperature ( C) Aluminum Galvanized steel Stainless steel Alkyd paint Epoxy The UL certification includes the printing with one or more of the following thermal transfer ribbons: DNP R300, DNP R510, DNP TR4070, Iimak SP330, Ricoh B110C, Ricoh B110CR. 4/5

5 Warranty All statements, technical information and recommendations about AVERY DENNISON products are based upon tests believed to be reliable but do not constitute a guarantee or warranty. All AVERY DENNISON products are sold with the understanding that PURCHASER has independently determined the suitability of such products for its purposes. AVERY DENNISON products are warranted to be free of defects in material or workmanship for a period of one year from the date of shipment. Any product shown to the satisfaction of AVERY DENNISON within the time provided to be so defective shall be replaced without charge or AVERY DENNISON may issue credit in such amount as it deems reasonable however, in no event shall AVERY DENNISON be responsible for claims beyond the replacement value of the defective product or in any way liable or responsible for consequential or incidental damages. NO EXPRESS WARRANTIES AND NO IMPLIED WARRANTIES, WHETHER OF MERCHANTIBILITY OR FITNESS FOR ANY PARTICULAR USE, OR OTHERWISE, EXCEPT AS SET FORTH ABOVE (WHICH IS MADE EXPRESSLY IN LIEU OF ALL OTHER WARRANTIES) SHALL APPLY TO PRODUCTS SOLD BY AVERY DENNISON. AVERY DENNISON SPECIFICALLY DISCLAIMS AND EXCLUDES ALL OTHER SUCH WARRANTIES. NO WAIVER, ALTERATION, ADDITION OR MODIFICATION OF THE FOREGOING CONDITIONS SHALL BE VALID UNLESS MADE IN WRITING AND SIGNED BY AN EXECUTIVE OFFICER OF AVERY DENNISON. No salesman, representative, or agent of AVERY DENNISON is authorized to give any guarantee, warranty or make any representation contrary to the above. 5/5