HØGSKOLEN I NARVIK - SIVILINGENIØRUTDANNINGEN EKSAMEN OG LØSNINGSFORSLAG I KURSET STE 6289 MODERNE MATERIALER OG BEREG- NINGER
|
|
- Hannah Armstrong
- 6 years ago
- Views:
Transcription
1 HØGSKOLEN I NARVIK - SIVILINGENIØRUTDANNINGEN EKSAMEN OG LØSNINGSFORSLAG I KURSET STE 689 MODERNE MATERIALER OG BEREG- NINGER KLASSE: 5ID, DATO:. Desember 9 TID: 9.-., 3 timer EMNESTØRRELSE: 7.5 stp. ANTALL SIDER: (inklusiv Appendix: tabell og formler) TILLATTE HJELPEMIDLER: Bestemt, enkel kalkulator tillatt, noe som betyr at kalkulatoren kun skal inneha enkle numeriske og trigonometriske funksjoner. Kalkulatoren skal ikke ha grafisk display, og ved kontroll skal den være enkelt identifiserbar. Ingen trykte eller håndskrevne hjelpemidler tillatt. KONTAKTPERSONER UNDER EKSAMEN: professor Annette Meidell tlf eller professor Dag Lukkassen tlf Eksamensbesvarelsen kan gis på norsk, skandinavisk eller engelsk. Totalt antall deloppgaver er 9, og de teller like mye. I Task Project er det de 3 prosjektene i kurset som skal legges ved.
2 Task a) What is a biopolymer? Answer: According to the American Society for Testing and Materials (ASTM), biopolymers are degradable polymers in which degradation results from the action of naturally occurring micro-organisms such as bacteria, fungi and algae. Biopolymers are an alternative to petroleum-based polymers (traditional plastics) produced by living organisms. The term biopolymers is often used for all polymers that are made from natural renewable resources and/or are completely biodegradable. Biopolymers can be produced by biological systems like microorganisms, plants and animals, or chemically synthesized from biological starting materials (e.g. sugars, starch, natural fats or oils, etc.). Most of the biopolymers are biodegradable, compostable or will biodegrade in landfill (time can vary from a couple of days to even years, but they will eventually degrade). Additional answer: Biopolymers can be used in all kinds of applications, and with all kinds of production techniques, like injection moulding, thermoforming and blow moulding! Some biopolymers can directly replace synthetic plastics in traditional applications, while others possess unique properties that may open new applications. b) Explain how a structure with negative Poissons ratio will behave in contrast to a material or structure with positive Poissons ratio. Answer: Instead of contracting in the direction perpendicular to the loading plane if the structure is exposed to tension, it will expand (the opposite reaction compared to a rubber band which gets thinner in the middle when stretching it). In an isotropic material structure (a material which does not have a preferred orientation) the allowable range of Poisson s ratio is from. to +.5. Normally, materials have a Poissons ratio <ν<.5. Metals have a Poissons numer of about.3. Hierarchical structures and foams have also been made with negative Poissons ratio (also called auxetic materials, anti-rubber, ) ν <, and Poisson s ratio >, which give exciting respond to loads. In stead of contracting in the direction perpenidcular to the loading plane if it is exposed to tension, it will expand (the opposite reaction compared to a rubber band which gets thinner in the middle when stretching it), see an example of a structure with negative Poissons number
3 Figure.: An example of a structure with negative Poissons ratio. in Figure.. c) What is the main ideas with reiterated homogenization? Answer: For a reiterated structure (hierarchical structure), see an example in Figure.. we can use the homogenization theory to obtain for instance the effective thermal conductivity (for instance if the structure is a reiterated chessboard structure) for each level of the structure, beginning at the inner level of hierarchy. By using the homogenized (effective moduli) as the next input value for the next level, we can continue in this way until there are no more levels. The final value is the effective conductivity for the structure. This technique is a very efficient method for finding the effective moduli in complicated structures which is difficult to analyze by using ordinary finite elemet programs due to the different size in the areas. This makes the solution difficult to obtain due to the large number of elements required to obtain the solution. Task a) Find the deflection of the sandwich beam with ends built in and that has a midpoint load P N, see Figure.3 by using the approximation D E fbt f d. The length of the sandwich L 5mm, thickness of the facings t f is mm and t c is 4mm, b mm. The facings are aluminium plates with Youngs 3
4 Figure.: A hierarchical structure. modulus of E f MPa (GRP), strength σ f,cr MPa. The core material is a PVC material with shear modulus G c 4MPa (8kg/m 3 PVC foam), (E c MPa), shear strength τ c,cr.5mpa. Answer: The total deflection is described as PL 3 δ δ b + δ s + PL, 9 4(AG) eq where the bending contribution is δ b PL 3 P L 3 P (5) 3 ³ ³ 9 (EI) Ef bt eq 9 f d 9 (4+) (P ) (mm/n) () mm, and the shear contribution is δ s PL PL P 5 ³ ³ (P ) (mm/n) 4(AG) eq bd 4 G c t c 4 (4+) () (mm/n) 7.436mm. 4
5 Figure.3: A sandwich beam with ends built in and a midpoint load. The total deflection is δ δ b + δ s mm. b) Is the approximation for valid? If not find the correct deflection. Answer: Therequirementsduetotheapproximationsisvalidif µ d 3 3 t f (or d t f 4 µ > 4> 5.77) then the first term of.3 is less than % of the second, and can therefore be neglected, and since 6E f t f d E c t 3 c 6 (4) (4) , which is less than,hence, the third term of.3 is not less than % of the second, and can therefore not be neglected. The assumption D E fbt f d 5
6 is not valid! We have to use D E fbt f d + E cbt 3 c Ã! (4 + ) µ which gives that the bending contribution δ b PL 3 9 P L 3 9 ³ P (5) 3 9 ( ) (P ) (mm/n) () mm, and the shear contribution δ s PL PL P 5 ³ ³ (P ) (mm/n) 4(AG) eq bd 4 G c t c 4 (4+) () (mm/n) 7.436mm. The total correct deflection is δ δ b + δ s mm. c) Calculate the face thickness, t f, for maximum allowable stress. Is the thickness given in a) satisfactory? Answer:The stress in the facings σ f M x maxt c E PL f tc E 8 f ³ (EI) Ef bt eq f d ³ 56.5, () tf 4 t f ³ 8 () tf 4
7 here d t c, thus the face thickness for maximum allowable stress (Or: t f mm. σ f σ f M x maxt c E f M x maxt c E 5 f σ f µ µ Ef bt f d () tf (.5 9 ) t f () ). Thethicknessgivenina)isnotsatisfactory. Itshouldbeatleast.565mm in order to avoid that the allowable face stress is exceeded. d) Calculate the maximum shear stress in the core. Is it satisfactory? Answer: The maximum shear stress in the core τ c T x max db P db P db.9 5MPa 4 () which is satisfactory since τ c,cr.5 MPa.. e) What is the wrinkling stress? Will it wrinkle? Answer: The wrinkling stress (can be found from (.)) σ cr.5 3p E f E c G c MPa. The face will not wrinkle since σ cr >σ f MPa. 7
8 Task 3 Assume that you have a periodic square symmetric unidirectional structure with a periodic cell Y [, ] [, ]. The periodic material structure consists of two isotropic materials with Young s modulus E o GPa and E I GPa, Poisson s ratio ν o and ν I.4 and volume fractions p I p o / (where index o and I refer to the white and black material, respectively). Describe as detailed as possible how you proceed in order to compute the value of the effective bulk modulus K. Answer: For the computation we can solve the two-dimensional cell problem by using plane strain. The effective stress/strain-relation is hσ i hσ i hσ 33 i hσ i hσ 3 i hσ 3 i K + G T K G T l K G T K + G T l l l n G T,45 G L G L he i he i he 33 i hγ i hγ 3 i hγ 3 i (see the compendium). In order to compute the effective in-plane moduli K we solve the cell problem for hei [,,,,,, ] T and compute the corresponding values K hσ i /. Alternatively we can compute the strain energy W and compute K from the identity W hei C hei Y (.) Since Y 4, we obtain from (.) that the strain energy W corresponding to the average strain vector hei [,,,,,, ] T is K + G T K G T l W K G T K + G T l l l n G T,45 4 G L G L 8
9 (K + G T )+(K G T ) (K G T )+(K + G T ) 4 K K 4 W (K +K )4 (4K )4K 8 which gives us that K W/8. We can use uniform boundary conditions on each face of the square structure. More precisely, for hei [,,,,,, ] T the boundary conditions are: u (,x ), u (,x ), u (x, ), u (x, ). Projects Attach the copies of the three projects in this course (legg ved kopiene av de tre prosjektene dere har gjort i dette kurset). 9
10 Appendix: Tables and formulae Mode of loading, (all beams of length L) Cantilever, end load, P Cantilever, Uniformly distributed load, q P/L Three-point bend, central load, P Three-point bend, Uniformly distributed load, q P/L Ends built in, Central load, P Ends built in, Uniformly distributed load, q P/L δ b B B B 3 B 4 PL3 B δ (EI) s PL eq B (AG) eq M x PL B 3 T x P B Deflection: Maximum face stress: δ δ b + δ s PL3 PL +. B B (AG) eq Wrinkling stress: σ f M x max t c E f. σ cr.5 3p E f E c G c (.)
11 Flexural rigidity: (we can use if E fbt 3 f 6 + E fbt f d E fbt f d + E cbt 3 c (.3) and The shear stiffness is given by µ d 3 > or t f 6E f t f d E c t 3 c > ). d t f > 5.77 and the shear stress (AG) eq bd G c t c τ c T x max. db.. Isotropic materials For an isotropic material the shear modulus G and bulk modulus K in plane elasticity (plane strain) are related to the well known Young s modulus E and Poisson s ratio ν as follows: K E (+ν)( ν), G E (+ν)... Square symmetric unidirectional two-phase structure: Stress/strain-relation:
12 hσ i hσ i hσ 33 i hσ i hσ 3 i hσ 3 i K + G T K G T l K G T K + G T l l l n G T,45 G L G L he i he i he 33 i hγ i hγ 3 i hγ 3 i. Effectivecompliancematrix: Relations: E T ν T E T ν L E L ν T ET E T ν L E L ν L E L ν L EL E L G T,45 G L G L. 4 E T G T G T E T (+ν T ), + K + 4(ν L ), EL l ν LK,n EL +4(ν L) K, EL p o E o + p I E I + 4(ν o ν I ) ³ (p o + p I ), (.4) K o K o K I K K I ν L p o ν o + p I ν I ν o ν I K o (p o + p I ), (.5) K I K o K I K K i E i (+ν i )( ν i ) and G i E i (+ν i ) ).
COURSE STE6289 Modern Materials and Computations (Moderne materialer og beregninger 7.5 stp.)
Narvik University College (Høgskolen i Narvik) EXAMINATION TASK COURSE STE6289 Modern Materials and Computations (Moderne materialer og beregninger 7.5 stp.) CLASS: Master students in Engineering Design
More informationPost Graduate Diploma in Mechanical Engineering Computational mechanics using finite element method
9210-220 Post Graduate Diploma in Mechanical Engineering Computational mechanics using finite element method You should have the following for this examination one answer book scientific calculator No
More informationEMA 3702 Mechanics & Materials Science (Mechanics of Materials) Chapter 2 Stress & Strain - Axial Loading
MA 3702 Mechanics & Materials Science (Mechanics of Materials) Chapter 2 Stress & Strain - Axial Loading MA 3702 Mechanics & Materials Science Zhe Cheng (2018) 2 Stress & Strain - Axial Loading Statics
More informationNORMAL STRESS. The simplest form of stress is normal stress/direct stress, which is the stress perpendicular to the surface on which it acts.
NORMAL STRESS The simplest form of stress is normal stress/direct stress, which is the stress perpendicular to the surface on which it acts. σ = force/area = P/A where σ = the normal stress P = the centric
More informationPURE BENDING. If a simply supported beam carries two point loads of 10 kn as shown in the following figure, pure bending occurs at segment BC.
BENDING STRESS The effect of a bending moment applied to a cross-section of a beam is to induce a state of stress across that section. These stresses are known as bending stresses and they act normally
More informationSTRENGTH OF MATERIALS-I. Unit-1. Simple stresses and strains
STRENGTH OF MATERIALS-I Unit-1 Simple stresses and strains 1. What is the Principle of surveying 2. Define Magnetic, True & Arbitrary Meridians. 3. Mention different types of chains 4. Differentiate between
More informationNomenclature. Length of the panel between the supports. Width of the panel between the supports/ width of the beam
omenclature a b c f h Length of the panel between the supports Width of the panel between the supports/ width of the beam Sandwich beam/ panel core thickness Thickness of the panel face sheet Sandwich
More informationClass XI Chapter 9 Mechanical Properties of Solids Physics
Book Name: NCERT Solutions Question : A steel wire of length 4.7 m and cross-sectional area 5 3.0 0 m stretches by the same 5 amount as a copper wire of length 3.5 m and cross-sectional area of 4.0 0 m
More informationUNIVERSITY OF SASKATCHEWAN ME MECHANICS OF MATERIALS I FINAL EXAM DECEMBER 13, 2008 Professor A. Dolovich
UNIVERSITY OF SASKATCHEWAN ME 313.3 MECHANICS OF MATERIALS I FINAL EXAM DECEMBER 13, 2008 Professor A. Dolovich A CLOSED BOOK EXAMINATION TIME: 3 HOURS For Marker s Use Only LAST NAME (printed): FIRST
More informationLevel 7 Postgraduate Diploma in Engineering Computational mechanics using finite element method
9210-203 Level 7 Postgraduate Diploma in Engineering Computational mechanics using finite element method You should have the following for this examination one answer book No additional data is attached
More informationChapter 7. Highlights:
Chapter 7 Highlights: 1. Understand the basic concepts of engineering stress and strain, yield strength, tensile strength, Young's(elastic) modulus, ductility, toughness, resilience, true stress and true
More informationCHAPTER THREE SYMMETRIC BENDING OF CIRCLE PLATES
CHAPTER THREE SYMMETRIC BENDING OF CIRCLE PLATES * Governing equations in beam and plate bending ** Solution by superposition 1.1 From Beam Bending to Plate Bending 1.2 Governing Equations For Symmetric
More informationMechanics of Solids. Mechanics Of Solids. Suraj kr. Ray Department of Civil Engineering
Mechanics Of Solids Suraj kr. Ray (surajjj2445@gmail.com) Department of Civil Engineering 1 Mechanics of Solids is a branch of applied mechanics that deals with the behaviour of solid bodies subjected
More informationLecture 4 Honeycombs Notes, 3.054
Honeycombs-In-plane behavior Lecture 4 Honeycombs Notes, 3.054 Prismatic cells Polymer, metal, ceramic honeycombs widely available Used for sandwich structure cores, energy absorption, carriers for catalysts
More informationUNIT III DEFLECTION OF BEAMS 1. What are the methods for finding out the slope and deflection at a section? The important methods used for finding out the slope and deflection at a section in a loaded
More informationMAAE 2202 A. Come to the PASS workshop with your mock exam complete. During the workshop you can work with other students to review your work.
It is most beneficial to you to write this mock final exam UNDER EXAM CONDITIONS. This means: Complete the exam in 3 hours. Work on your own. Keep your textbook closed. Attempt every question. After the
More informationAN EFFECTIVE SOLUTION OF THE COMPOSITE (FGM S) BEAM STRUCTURES
Engineering MECHANICS, Vol. 15, 2008, No. 2, p. 115 132 115 AN EFFECTIVE SOLUTION OF THE COMPOSITE (FGM S) BEAM STRUCTURES Justín Murín, Vladimír Kutiš* The additive mixture rules have been extended for
More informationINTRODUCTION TO STRAIN
SIMPLE STRAIN INTRODUCTION TO STRAIN In general terms, Strain is a geometric quantity that measures the deformation of a body. There are two types of strain: normal strain: characterizes dimensional changes,
More informationMechanical Engineering Ph.D. Preliminary Qualifying Examination Solid Mechanics February 25, 2002
student personal identification (ID) number on each sheet. Do not write your name on any sheet. #1. A homogeneous, isotropic, linear elastic bar has rectangular cross sectional area A, modulus of elasticity
More informationStresses and Strains in flexible Pavements
Stresses and Strains in flexible Pavements Multi Layered Elastic System Assumptions in Multi Layered Elastic Systems The material properties of each layer are homogeneous property at point A i is the same
More information= 50 ksi. The maximum beam deflection Δ max is not = R B. = 30 kips. Notes for Strength of Materials, ET 200
Notes for Strength of Materials, ET 00 Steel Six Easy Steps Steel beam design is about selecting the lightest steel beam that will support the load without exceeding the bending strength or shear strength
More informationTensile stress strain curves for different materials. Shows in figure below
Tensile stress strain curves for different materials. Shows in figure below Furthermore, the modulus of elasticity of several materials effected by increasing temperature, as is shown in Figure Asst. Lecturer
More informationChapter 2: Elasticity
OHP 1 Mechanical Properties of Materials Chapter 2: lasticity Prof. Wenjea J. Tseng ( 曾文甲 ) Department of Materials ngineering National Chung Hsing University wenjea@dragon.nchu.edu.tw Reference: W.F.
More information2. Determine the deflection at C of the beam given in fig below. Use principal of virtual work. W L/2 B A L C
CE-1259, Strength of Materials UNIT I STRESS, STRAIN DEFORMATION OF SOLIDS Part -A 1. Define strain energy density. 2. State Maxwell s reciprocal theorem. 3. Define proof resilience. 4. State Castigliano
More informationDESIGN OF BEAMS AND SHAFTS
DESIGN OF EAMS AND SHAFTS! asis for eam Design! Stress Variations Throughout a Prismatic eam! Design of pristmatic beams! Steel beams! Wooden beams! Design of Shaft! ombined bending! Torsion 1 asis for
More informationFlexural properties of polymers
A2 _EN BUDAPEST UNIVERSITY OF TECHNOLOGY AND ECONOMICS FACULTY OF MECHANICAL ENGINEERING DEPARTMENT OF POLYMER ENGINEERING Flexural properties of polymers BENDING TEST OF CHECK THE VALIDITY OF NOTE ON
More informationChapter 5 Elastic Strain, Deflection, and Stability 1. Elastic Stress-Strain Relationship
Chapter 5 Elastic Strain, Deflection, and Stability Elastic Stress-Strain Relationship A stress in the x-direction causes a strain in the x-direction by σ x also causes a strain in the y-direction & z-direction
More informationAdvanced Structural Analysis EGF Section Properties and Bending
Advanced Structural Analysis EGF316 3. Section Properties and Bending 3.1 Loads in beams When we analyse beams, we need to consider various types of loads acting on them, for example, axial forces, shear
More information[5] Stress and Strain
[5] Stress and Strain Page 1 of 34 [5] Stress and Strain [5.1] Internal Stress of Solids [5.2] Design of Simple Connections (will not be covered in class) [5.3] Deformation and Strain [5.4] Hooke s Law
More informationHigh Tech High Top Hat Technicians. An Introduction to Solid Mechanics. Is that supposed to bend there?
High Tech High Top Hat Technicians An Introduction to Solid Mechanics Or Is that supposed to bend there? Why don't we fall through the floor? The power of any Spring is in the same proportion with the
More informationIndentation Energy in Bending of Sandwich Beams with Composite Laminated Faces and Foam Core
Indentation Energy in Bending of Sandwich Beams with Composite Laminated Faces and Foam Core M. SADIGHI, H. POURIAYEVALI, and M. SAADATI Dept. of Mechanical Engineering, Amirkabir University of Tech, Tehran,
More informationUse Hooke s Law (as it applies in the uniaxial direction),
0.6 STRSS-STRAIN RLATIONSHIP Use the principle of superposition Use Poisson s ratio, v lateral longitudinal Use Hooke s Law (as it applies in the uniaxial direction), x x v y z, y y vx z, z z vx y Copyright
More informationStrength of Material. Shear Strain. Dr. Attaullah Shah
Strength of Material Shear Strain Dr. Attaullah Shah Shear Strain TRIAXIAL DEFORMATION Poisson's Ratio Relationship Between E, G, and ν BIAXIAL DEFORMATION Bulk Modulus of Elasticity or Modulus of Volume
More informationMECHANICS OF MATERIALS
Third E CHAPTER 2 Stress MECHANICS OF MATERIALS Ferdinand P. Beer E. Russell Johnston, Jr. John T. DeWolf Lecture Notes: J. Walt Oler Texas Tech University and Strain Axial Loading Contents Stress & Strain:
More informationMECE 3321 MECHANICS OF SOLIDS CHAPTER 3
MECE 3321 MECHANICS OF SOLIDS CHAPTER 3 Samantha Ramirez TENSION AND COMPRESSION TESTS Tension and compression tests are used primarily to determine the relationship between σ avg and ε avg in any material.
More informationModule III - Macro-mechanics of Lamina. Lecture 23. Macro-Mechanics of Lamina
Module III - Macro-mechanics of Lamina Lecture 23 Macro-Mechanics of Lamina For better understanding of the macromechanics of lamina, the knowledge of the material properties in essential. Therefore, the
More informationQuestion 9.1: A steel wire of length 4.7 m and cross-sectional area 3.0 10 5 m 2 stretches by the same amount as a copper wire of length 3.5 m and cross-sectional area of 4.0 10 5 m 2 under a given load.
More informationME 2570 MECHANICS OF MATERIALS
ME 2570 MECHANICS OF MATERIALS Chapter III. Mechanical Properties of Materials 1 Tension and Compression Test The strength of a material depends on its ability to sustain a load without undue deformation
More informationTheory at a Glance (for IES, GATE, PSU)
1. Stress and Strain Theory at a Glance (for IES, GATE, PSU) 1.1 Stress () When a material is subjected to an external force, a resisting force is set up within the component. The internal resistance force
More informationLecture 16-17, Sandwich Panel Notes, 3.054
Sandwich Panels Two stiff strong skins separated by a lightweight core Separation of skins by core increases moment of inertia, with little increase in weight Efficient for resisting bending and buckling
More informationSamantha Ramirez, MSE. Stress. The intensity of the internal force acting on a specific plane (area) passing through a point. F 2
Samantha Ramirez, MSE Stress The intensity of the internal force acting on a specific plane (area) passing through a point. Δ ΔA Δ z Δ 1 2 ΔA Δ x Δ y ΔA is an infinitesimal size area with a uniform force
More informationChapter Two: Mechanical Properties of materials
Chapter Two: Mechanical Properties of materials Time : 16 Hours An important consideration in the choice of a material is the way it behave when subjected to force. The mechanical properties of a material
More informationISHIK UNIVERSITY DEPARTMENT OF MECHATRONICS ENGINEERING
ISHIK UNIVERSITY DEPARTMENT OF MECHATRONICS ENGINEERING QUESTION BANK FOR THE MECHANICS OF MATERIALS-I 1. A rod 150 cm long and of diameter 2.0 cm is subjected to an axial pull of 20 kn. If the modulus
More informationDOWN-HOLE SEISMIC SURVEY AND VERTICAL ELECTRIC SOUNDINGS RABASKA PROJECT, LÉVIS, QUÉBEC. Presented to :
DOWN-HOLE SEISMIC SURVEY AND VERTICAL ELECTRIC SOUNDINGS RABASKA PROJECT, LÉVIS, QUÉBEC Presented to : TERRATECH 455, René-Lévesque Blvd. West Montreal, Québec HZ 1Z3 Presented by : GEOPHYSICS GPR INTERNATIONAL
More informationQUESTION BANK ENGINEERS ACADEMY. PL 4Ed d. Ed d. 4PL Ed d. 4Ed d. 42 Axially Loaded Members Junior Engineer
NGINRS CDMY xially oaded Members Junior ngineer QUSTION BNK 1. The stretch in a steel rod of circular section, having a length subjected to a tensile load P and tapering uniformly from a diameter d 1 at
More informationLecture 7, Foams, 3.054
Lecture 7, Foams, 3.054 Open-cell foams Stress-Strain curve: deformation and failure mechanisms Compression - 3 regimes - linear elastic - bending - stress plateau - cell collapse by buckling yielding
More informationSTRESS STRAIN AND DEFORMATION OF SOLIDS, STATES OF STRESS
1 UNIT I STRESS STRAIN AND DEFORMATION OF SOLIDS, STATES OF STRESS 1. Define: Stress When an external force acts on a body, it undergoes deformation. At the same time the body resists deformation. The
More informationIDE 110 Mechanics of Materials Spring 2006 Final Examination FOR GRADING ONLY
Spring 2006 Final Examination STUDENT S NAME (please print) STUDENT S SIGNATURE STUDENT NUMBER IDE 110 CLASS SECTION INSTRUCTOR S NAME Do not turn this page until instructed to start. Write your name on
More information1. A pure shear deformation is shown. The volume is unchanged. What is the strain tensor.
Elasticity Homework Problems 2014 Section 1. The Strain Tensor. 1. A pure shear deformation is shown. The volume is unchanged. What is the strain tensor. 2. Given a steel bar compressed with a deformation
More information2012 MECHANICS OF SOLIDS
R10 SET - 1 II B.Tech II Semester, Regular Examinations, April 2012 MECHANICS OF SOLIDS (Com. to ME, AME, MM) Time: 3 hours Max. Marks: 75 Answer any FIVE Questions All Questions carry Equal Marks ~~~~~~~~~~~~~~~~~~~~~~
More informationComb resonator design (2)
Lecture 6: Comb resonator design () -Intro Intro. to Mechanics of Materials School of Electrical l Engineering i and Computer Science, Seoul National University Nano/Micro Systems & Controls Laboratory
More informationName :. Roll No. :... Invigilator s Signature :.. CS/B.TECH (CE-NEW)/SEM-3/CE-301/ SOLID MECHANICS
Name :. Roll No. :..... Invigilator s Signature :.. 2011 SOLID MECHANICS Time Allotted : 3 Hours Full Marks : 70 The figures in the margin indicate full marks. Candidates are required to give their answers
More informationDEPARTMENT OF MECHANICAL ENIGINEERING, UNIVERSITY OF ENGINEERING & TECHNOLOGY LAHORE (KSK CAMPUS).
DEPARTMENT OF MECHANICAL ENIGINEERING, UNIVERSITY OF ENGINEERING & TECHNOLOGY LAHORE (KSK CAMPUS). Lab Director: Coordinating Staff: Mr. Muhammad Farooq (Lecturer) Mr. Liaquat Qureshi (Lab Supervisor)
More informationPES Institute of Technology
PES Institute of Technology Bangalore south campus, Bangalore-5460100 Department of Mechanical Engineering Faculty name : Madhu M Date: 29/06/2012 SEM : 3 rd A SEC Subject : MECHANICS OF MATERIALS Subject
More information20. Rheology & Linear Elasticity
I Main Topics A Rheology: Macroscopic deformation behavior B Linear elasticity for homogeneous isotropic materials 10/29/18 GG303 1 Viscous (fluid) Behavior http://manoa.hawaii.edu/graduate/content/slide-lava
More informationCIVIL DEPARTMENT MECHANICS OF STRUCTURES- ASSIGNMENT NO 1. Brach: CE YEAR:
MECHANICS OF STRUCTURES- ASSIGNMENT NO 1 SEMESTER: V 1) Find the least moment of Inertia about the centroidal axes X-X and Y-Y of an unequal angle section 125 mm 75 mm 10 mm as shown in figure 2) Determine
More informationQUESTION BANK SEMESTER: III SUBJECT NAME: MECHANICS OF SOLIDS
QUESTION BANK SEMESTER: III SUBJECT NAME: MECHANICS OF SOLIDS UNIT 1- STRESS AND STRAIN PART A (2 Marks) 1. Define longitudinal strain and lateral strain. 2. State Hooke s law. 3. Define modular ratio,
More informationQuestion Figure shows the strain-stress curve for a given material. What are (a) Young s modulus and (b) approximate yield strength for this material?
Question. A steel wire of length 4.7 m and cross-sectional area 3.0 x 10-5 m 2 stretches by the same amount as a copper wire of length 3.5 m and cross-sectional area of 4.0 x 10-5 m 2 under a given load.
More informationSample Question Paper
Scheme I Sample Question Paper Program Name : Mechanical Engineering Program Group Program Code : AE/ME/PG/PT/FG Semester : Third Course Title : Strength of Materials Marks : 70 Time: 3 Hrs. Instructions:
More informationQUESTION BANK DEPARTMENT: CIVIL SEMESTER: III SUBJECT CODE: CE2201 SUBJECT NAME: MECHANICS OF SOLIDS UNIT 1- STRESS AND STRAIN PART A
DEPARTMENT: CIVIL SUBJECT CODE: CE2201 QUESTION BANK SEMESTER: III SUBJECT NAME: MECHANICS OF SOLIDS UNIT 1- STRESS AND STRAIN PART A (2 Marks) 1. Define longitudinal strain and lateral strain. 2. State
More information**********************************************************************
Department of Civil and Environmental Engineering School of Mining and Petroleum Engineering 3-33 Markin/CNRL Natural Resources Engineering Facility www.engineering.ualberta.ca/civil Tel: 780.492.4235
More informationLecture 15 Strain and stress in beams
Spring, 2019 ME 323 Mechanics of Materials Lecture 15 Strain and stress in beams Reading assignment: 6.1 6.2 News: Instructor: Prof. Marcial Gonzalez Last modified: 1/6/19 9:42:38 PM Beam theory (@ ME
More informationRESEARCH PROJECT NO. 26
RESEARCH PROJECT NO. 26 DETERMINATION OF POISSON'S RATIO IN AD1 TESTING BY UNIVERSITY OF MICHIGAN REPORT PREPARED BY BELA V. KOVACS and JOHN R. KEOUGH \ MEMBER / / DUCTILE IRON \ SOCIETY Issued by the
More informationANALYSIS OF YARN BENDING BEHAVIOUR
ANALYSIS OF YARN BENDING BEHAVIOUR B. Cornelissen, R. Akkerman Faculty of Engineering Technology, University of Twente Drienerlolaan 5, P.O. Box 217; 7500 AE Enschede, the Netherlands b.cornelissen@utwente.nl
More informationComb Resonator Design (2)
Lecture 6: Comb Resonator Design () -Intro. to Mechanics of Materials Sh School of felectrical ti lengineering i and dcomputer Science, Si Seoul National University Nano/Micro Systems & Controls Laboratory
More informationCHAPTER 3 THE EFFECTS OF FORCES ON MATERIALS
CHAPTER THE EFFECTS OF FORCES ON MATERIALS EXERCISE 1, Page 50 1. A rectangular bar having a cross-sectional area of 80 mm has a tensile force of 0 kn applied to it. Determine the stress in the bar. Stress
More informationOutline. Tensile-Test Specimen and Machine. Stress-Strain Curve. Review of Mechanical Properties. Mechanical Behaviour
Tensile-Test Specimen and Machine Review of Mechanical Properties Outline Tensile test True stress - true strain (flow curve) mechanical properties: - Resilience - Ductility - Toughness - Hardness A standard
More informationHomework No. 1 MAE/CE 459/559 John A. Gilbert, Ph.D. Fall 2004
Homework No. 1 MAE/CE 459/559 John A. Gilbert, Ph.D. 1. A beam is loaded as shown. The dimensions of the cross section appear in the insert. the figure. Draw a complete free body diagram showing an equivalent
More information3. BEAMS: STRAIN, STRESS, DEFLECTIONS
3. BEAMS: STRAIN, STRESS, DEFLECTIONS The beam, or flexural member, is frequently encountered in structures and machines, and its elementary stress analysis constitutes one of the more interesting facets
More informationComposite Structures. Indian Institute of Technology Kanpur
Mechanics of Laminated Composite Structures Nachiketa Tiwari Indian Institute of Technology Kanpur Lecture 23 Analysis of an Orthotropic Ply Lecture Overview Introduction Engineering constants for an 2
More informationEffect of Specimen Dimensions on Flexural Modulus in a 3-Point Bending Test
Effect of Specimen Dimensions on Flexural Modulus in a 3-Point Bending Test M. Praveen Kumar 1 and V. Balakrishna Murthy 2* 1 Mechanical Engineering Department, P.V.P. Siddhartha Institute of Technology,
More informationStress-Strain Behavior
Stress-Strain Behavior 6.3 A specimen of aluminum having a rectangular cross section 10 mm 1.7 mm (0.4 in. 0.5 in.) is pulled in tension with 35,500 N (8000 lb f ) force, producing only elastic deformation.
More informationUNIT 1 STRESS STRAIN AND DEFORMATION OF SOLIDS, STATES OF STRESS 1. Define stress. When an external force acts on a body, it undergoes deformation.
UNIT 1 STRESS STRAIN AND DEFORMATION OF SOLIDS, STATES OF STRESS 1. Define stress. When an external force acts on a body, it undergoes deformation. At the same time the body resists deformation. The magnitude
More informationChapter 3. Load and Stress Analysis. Lecture Slides
Lecture Slides Chapter 3 Load and Stress Analysis 2015 by McGraw Hill Education. This is proprietary material solely for authorized instructor use. Not authorized for sale or distribution in any manner.
More informationTABLE OF CONTENTS. Mechanics of Composite Materials, Second Edition Autar K Kaw University of South Florida, Tampa, USA
Mechanics of Composite Materials, Second Edition Autar K Kaw University of South Florida, Tampa, USA TABLE OF CONTENTS 1. INTRODUCTION TO COMPOSITE MATERIALS 1.1 Introduction... 1.2 Classification... 1.2.1
More informationModelling the behaviour of plastics for design under impact
Modelling the behaviour of plastics for design under impact G. Dean and L. Crocker MPP IAG Meeting 6 October 24 Land Rover door trim Loading stages and selected regions Project MPP7.9 Main tasks Tests
More informationTHE present paper is concerned with the problem of wrinkling
AIAA JOURNAL Vol. 4, No. 7, July 4 Thermomechanical Wrinkling in Composite Sandwich Structures Victor Birman University of Missouri Rolla, St. Louis, Missouri 6311 A new approach to the solution of the
More informationUnit I Stress and Strain
Unit I Stress and Strain Stress and strain at a point Tension, Compression, Shear Stress Hooke s Law Relationship among elastic constants Stress Strain Diagram for Mild Steel, TOR steel, Concrete Ultimate
More informationFinite Element Analysis of Piezoelectric Cantilever
Finite Element Analysis of Piezoelectric Cantilever Nitin N More Department of Mechanical Engineering K.L.E S College of Engineering and Technology, Belgaum, Karnataka, India. Abstract- Energy (or power)
More informationClass XI Physics. Ch. 9: Mechanical Properties of solids. NCERT Solutions
Downloaded from Class XI Physics Ch. 9: Mechanical Properties of solids NCERT Solutions Page 242 Question 9.1: A steel wire of length 4.7 m and cross-sectional area 3.0 10 5 m 2 stretches by the same amount
More information: APPLIED MECHANICS & STRENGTH OF MATERIALS COURSE CODE : 4021 COURSE CATEGORY : A PERIODS/ WEEK : 5 PERIODS/ SEMESTER : 75 CREDIT : 5 TIME SCHEDULE
COURSE TITLE : APPLIED MECHANICS & STRENGTH OF MATERIALS COURSE CODE : 4021 COURSE CATEGORY : A PERIODS/ WEEK : 5 PERIODS/ SEMESTER : 75 CREDIT : 5 TIME SCHEDULE MODULE TOPIC PERIODS 1 Simple stresses
More informationThe University of Melbourne Engineering Mechanics
The University of Melbourne 436-291 Engineering Mechanics Tutorial Four Poisson s Ratio and Axial Loading Part A (Introductory) 1. (Problem 9-22 from Hibbeler - Statics and Mechanics of Materials) A short
More informationLab Exercise #5: Tension and Bending with Strain Gages
Lab Exercise #5: Tension and Bending with Strain Gages Pre-lab assignment: Yes No Goals: 1. To evaluate tension and bending stress models and Hooke s Law. a. σ = Mc/I and σ = P/A 2. To determine material
More informationBack Calculation of Rock Mass Modulus using Finite Element Code (COMSOL)
Back Calculation of Rock Mass Modulus using Finite Element Code (COMSOL) Amirreza Ghasemi 1. Introduction Deformability is recognized as one of the most important parameters governing the behavior of rock
More informationPresented By: EAS 6939 Aerospace Structural Composites
A Beam Theory for Laminated Composites and Application to Torsion Problems Dr. BhavaniV. Sankar Presented By: Sameer Luthra EAS 6939 Aerospace Structural Composites 1 Introduction Composite beams have
More information(48) CHAPTER 3: TORSION
(48) CHAPTER 3: TORSION Introduction: In this chapter structural members and machine parts that are in torsion will be considered. More specifically, you will analyze the stresses and strains in members
More informationME 323 Examination #2 April 11, 2018
ME 2 Eamination #2 April, 2 PROBLEM NO. 25 points ma. A thin-walled pressure vessel is fabricated b welding together two, open-ended stainless-steel vessels along a 6 weld line. The welded vessel has an
More informationRevealing bending and force in a soft body through a plant root inspired. approach. Lucia Beccai 1* Piaggio 34, Pontedera (Italy)
Revealing bending and force in a soft body through a plant root inspired approach Chiara Lucarotti 1,2, Massimo Totaro 1, Ali Sadeghi 1, Barbara Mazzolai 1, Lucia Beccai 1* 1 Center for Micro-BioRobotics
More information1 Force Sensing. Lecture Notes. 1.1 Load Cell. 1.2 Stress and Strain
Lecture Notes 1 Force Sensing 1.1 Load Cell A Load Cell is a structure which supports the load and deflects a known amount in response to applied forces and torques. The deflections are measured to characterize
More informationOpen Access Prediction on Deflection of V-core Sandwich Panels in Weak Direction
Send Orders for Reprints to reprints@benthamscience.net The Open Ocean Engineering Journal, 2013, 6, Suppl-1, M5) 73-81 73 Open Access Prediction on Deflection of V-core Sandwich Panels in Weak Direction
More informationfive Mechanics of Materials 1 ARCHITECTURAL STRUCTURES: FORM, BEHAVIOR, AND DESIGN DR. ANNE NICHOLS SUMMER 2017 lecture
ARCHITECTURAL STRUCTURES: FORM, BEHAVIOR, AND DESIGN DR. ANNE NICHOLS SUMMER 2017 lecture five mechanics www.carttalk.com of materials Mechanics of Materials 1 Mechanics of Materials MECHANICS MATERIALS
More informationMechanical Properties of Polymers. Scope. MSE 383, Unit 3-1. Joshua U. Otaigbe Iowa State University Materials Science & Engineering Dept.
Mechanical Properties of Polymers Scope MSE 383, Unit 3-1 Joshua U. Otaigbe Iowa State University Materials Science & Engineering Dept. Structure - mechanical properties relations Time-dependent mechanical
More informationBending of Simply Supported Isotropic and Composite Laminate Plates
Bending of Simply Supported Isotropic and Composite Laminate Plates Ernesto Gutierrez-Miravete 1 Isotropic Plates Consider simply a supported rectangular plate of isotropic material (length a, width b,
More information1.050: Beam Elasticity (HW#9)
1050: Beam Elasticity (HW#9) MIT 1050 (Engineering Mechanics I) Fall 2007 Instructor: Markus J BUEHER Due: November 14, 2007 Team Building and Team Work: We strongly encourage you to form Homework teams
More information9 MECHANICAL PROPERTIES OF SOLIDS
9 MECHANICAL PROPERTIES OF SOLIDS Deforming force Deforming force is the force which changes the shape or size of a body. Restoring force Restoring force is the internal force developed inside the body
More informationQuestion 9.1: Answer. Length of the steel wire, L 1 = 4.7 m. Area of cross-section of the steel wire, A 1 = m 2
Question 9.1: A steel wire of length 4.7 m and cross-sectional area 3.0 10 5 m 2 stretches by the same amount as a copper wire of length 3.5 m and cross-sectional area of 4.0 10 5 m 2 under a given load.
More informationProblem " Â F y = 0. ) R A + 2R B + R C = 200 kn ) 2R A + 2R B = 200 kn [using symmetry R A = R C ] ) R A + R B = 100 kn
Problem 0. Three cables are attached as shown. Determine the reactions in the supports. Assume R B as redundant. Also, L AD L CD cos 60 m m. uation of uilibrium: + " Â F y 0 ) R A cos 60 + R B + R C cos
More informationXI. NANOMECHANICS OF GRAPHENE
XI. NANOMECHANICS OF GRAPHENE Carbon is an element of extraordinary properties. The carbon-carbon bond possesses large magnitude cohesive strength through its covalent bonds. Elemental carbon appears in
More informationThe science of elasticity
The science of elasticity In 1676 Hooke realized that 1.Every kind of solid changes shape when a mechanical force acts on it. 2.It is this change of shape which enables the solid to supply the reaction
More informationChapter Objectives. Design a beam to resist both bendingand shear loads
Chapter Objectives Design a beam to resist both bendingand shear loads A Bridge Deck under Bending Action Castellated Beams Post-tensioned Concrete Beam Lateral Distortion of a Beam Due to Lateral Load
More information