Supporting information
|
|
- Mercy Doyle
- 5 years ago
- Views:
Transcription
1 Supporting information In Situ Hydrothermal Grown of TiO Core-Shell Nanowire Coating for High Sensitive Solid Phase Microextraction of Polycyclic Aromatic Hydrocarbons Fuxin Wang, Juan Zheng, Junlang Qiu, Shuqin Liu, Guosheng Chen, Yexiang Tong, Fang Zhu* and Gangfeng Ouyang* MOE Key Laboratory of Aquatic Product Safety/KLGHEI of Environment and Energy Chemistry, School of Chemistry and Chemical Engineering, Sun Yat-sen University, Guangzhou , P. R. China * Corresponding author. Tel. & Fax: ceszhuf@mail.sysu.edu.cn; cesoygf@mail.sysu.edu.cn. S-1
2 Figure S1. Low-magnification SEM image of the section of the TiO 2 fiber S-2
3 Figure S2. EDS line scan of the TiO sample Figure S3. EDS spectra of the TiO2@C sample S-3
4 Figure S4. N 2 adsorption-deposition isotherm of the amorphous carbon Figure S5. The O 1s core level XPS spectrum of TiO sample S-4
5 Figure S6. The chromatogram of TiO 2 and TiO fiber at the same condition (Sample volume, 10ml; 2 μg L -1 PAHs solution, extraction time, 60 min; extraction temperature, 45 C; salt concentration, 24% (w/v); deposition temperature 250 C, deposition time 300 s.). S-5
6 Optimization of SPME parameters. In order to obtain the best extraction performance, SPME parameters, including extraction time, extraction temperature, desorption temperature and NaCl concentration, were optimized. The experiments were conducted at the concentration of 200 μg L -1 for PAHs. According to the result, the optimal conditions were as follows: extraction time 60 min, extraction temperature 45 C, desorption temperature 250 C, NaCl concentration 24 g / 100 ml. Figure S7. Effects of SPME conditions on the extraction efficiencies of TiO fiber. (a) Desorption temperature; (b) extraction time; (c) extraction temperature; (d) salt concentration. S-6
7 Table S1. The Comparison of LODs Between the Novel Core-Shell TiO Fiber and the Other Works compounds LOD a (ng L -1 ) TiO fiber naphthalene acenaphthylene acenaphthene fluorene anthracene phenathrene References: (1) Zheng, J.; Liang, Y.; Liu, S.; Ding, Y.; Shen, Y.; Luan, T.; Zhu, F.; Jiang, R.; Wu, D.; Ouyang, G., Ordered Mesoporous Polymers in situ Coated on a Stainless Steel Wire for a Highly Sensitive Solid Phase Microextraction Fibre. Nanoscale 2015, 7, (2) Zhang, S.; Du, Z.; Li, G., Layer-by-layer Fabrication of Chemical-bonded Graphene Coating for Solid-phase Microextraction. Anal. Chem. 2011, 83, (3) Abolghasemi, M. M.; Karimi, B.; Yousefi, V., Periodic Mesoporous Organosilica with Ionic Liquid Framework as a Novel Fiber Coating for Headspace Solid-phase Microextraction of Polycyclic Aromatic Hydrocarbons. Anal. Chim. Acta 2013, 804, (4) Es-haghi, A.; Hosseininasab, V.; Bagheri, H., Preparation, Characterization, and S-7
8 Applications of a Novel Solid-phase Microextraction Fiber by sol-gel Technology on the Surface of Stainless Steel Wire for Determination of Poly Cyclic Aromatic Hydrocarbons in Aquatic Environmental Samples. Anal. Chim. Acta 2014, 813, (5) Guo, M.; Song, W.; Wang, T.; Li, Y.; Wang, X.; Du, X., Phenyl-functionalization of Titanium Dioxide-nanosheets Coating Fabricated on a Titanium Wire for Selective Solid-phase Microextraction of Polycyclic Aromatic Hydrocarbons from Environment Water Samples. Talanta 2015, 144, (6) Sun, M.; Feng, J.; Qiu, H.; Fan, L.; Li, X.; Luo, C., CNT-TiO 2 Coating Bonded onto Stainless Steel Wire as a Novel Solid-phase Microextraction Fiber. Talanta 2013, 114, S-8
The Sensitive and Selective Adsorption of Aromatic. Compounds with Highly Crosslinked Polymer Nanoparticles
Electronic Supplementary Material (ESI) for Nanoscale. This journal is The Royal Society of Chemistry 2015 Supplementary Information The Sensitive and Selective Adsorption of Aromatic Compounds with Highly
More informationSupporting information
Supporting information MOF-derived hollow carbon nanocubes for fast solid-phase microextraction of polycyclic aromatic hydrocarbons Xingru Hu, Chaohai Wang, Jiansheng Li,* Rui Luo, Chao Liu, Xiuyun Sun,
More informationSolid Phase Microextraction
Solid Phase Microextraction Gangfeng Ouyang Ruifen Jiang Editors Solid Phase Microextraction Recent Developments and Applications 123 Editors Gangfeng Ouyang School of Chemistry Sun Yat-sen University
More informationOxygen Vacancy Induced Bismuth Oxyiodide with Remarkably. Increased Visible-light Absorption and Superior Photocatalytic.
Oxygen Vacancy Induced Bismuth Oxyiodide with Remarkably Increased Visible-light Absorption and Superior Photocatalytic Performance Yongchao Huang, Haibo Li, Muhammad-Sadeeq Balogun, Wenyue Liu, Yexiang
More informationSupporting Information. Facile design of phase separation for microfluidic. droplet-based liquid phase microextraction as a front end to
Supporting Information Facile design of phase separation for microfluidic droplet-based liquid phase microextraction as a front end to electrothermal vaporization-icpms for the analysis of trace metals
More informationMetal Organic Framework-Derived Metal Oxide Embedded in Nitrogen-Doped Graphene Network for High-Performance Lithium-Ion Batteries
Supporting Information for Metal Organic Framework-Derived Metal Oxide Embedded in Nitrogen-Doped Graphene Network for High-Performance Lithium-Ion Batteries Zhu-Yin Sui, Pei-Ying Zhang,, Meng-Ying Xu,
More informationSupporting Information
Supporting Information A Robust Versatile Hybrid Electrocatalyst for the Oxygen Reduction Reaction Kun Wang, Yi Wang*, Yexiang Tong, Zhangweihao Pan, Shuqin Song* a The Key Lab of Low- Chemistry & Energy
More informationHierarchical MoO 2 /Mo 2 C/C Hybrid Nanowires for High-Rate and. Long-Life Anodes for Lithium-Ion Batteries. Supporting Information
Supporting Information Hierarchical MoO 2 /Mo 2 C/C Hybrid Nanowires for High-Rate and Long-Life Anodes for Lithium-Ion Batteries Lichun Yang, a Xiang Li, a Yunpeng Ouyang, a Qingsheng Gao, b Liuzhang
More informationHydrothermally Activated Graphene Fiber Fabrics for Textile. Electrodes of Supercapacitors
Supporting Information for Hydrothermally Activated Graphene Fiber Fabrics for Textile Electrodes of Supercapacitors Zheng Li, Tieqi Huang, Weiwei Gao*, Zhen Xu, Dan Chang, Chunxiao Zhang, and Chao Gao*
More informationIn-Situ Fabrication of CoS and NiS Nanomaterials Anchored on. Reduced Graphene Oxide for Reversible Lithium Storage
Supporting Information In-Situ Fabrication of CoS and NiS Nanomaterials Anchored on Reduced Graphene Oxide for Reversible Lithium Storage Yingbin Tan, [a] Ming Liang, [b, c] Peili Lou, [a] Zhonghui Cui,
More informationTailorable and Wearable Textile Devices for Solar Energy Harvesting and Simultaneous Storage
Supporting Information Tailorable and Wearable Textile Devices for Solar Energy Harvesting and Simultaneous Storage Zhisheng Chai,, Nannan Zhang,, Peng Sun, Yi Huang, Chuanxi Zhao, Hong Jin Fan, Xing Fan,*,
More informationCo-vacancy-rich Co 1 x S nanosheets anchored on rgo for high-efficiency oxygen evolution
Electronic Supplementary Material Co-vacancy-rich Co 1 x S nanosheets anchored on rgo for high-efficiency oxygen evolution Jiaqing Zhu 1, Zhiyu Ren 1 ( ), Shichao Du 1, Ying Xie 1, Jun Wu 1,2, Huiyuan
More informationFacile synthesis of a ZnO BiOI p n nano-heterojunction with excellent visible-light photocatalytic activity
Supporting Information for Facile synthesis of a ZnO BiOI p n nano-heterojunction with excellent visible-light photocatalytic activity Mengyuan Zhang 1, Jiaqian Qin 2,3 *, Pengfei Yu 1, Bing Zhang 1, Mingzhen
More informationHighly doped and exposed Cu(I)-N active sites within graphene towards. efficient oxygen reduction for zinc-air battery
Electronic Supplementary Material (ESI) for Energy & Environmental Science. This journal is The Royal Society of Chemistry 2016 Electronic Supplementary Information (ESI) for Energy & Environmental Science.
More informationPyrolytic Temperature Dependent and Ash Catalyzed Formation of Sludge Char. Xiao-Qing Liu, Hong-Sheng Ding, Yuan-Ying Wang, Wu-Jun Liu, Hong Jiang*
Pyrolytic Temperature Dependent and Ash Catalyzed Formation of Sludge Char with Ultra-High Adsorption to 1-Naphthol Xiao-Qing Liu, Hong-Sheng Ding, Yuan-Ying Wang, Wu-Jun Liu, Hong Jiang* CAS Key Laboratory
More informationElectronic Supplementary Information (ESI) Three dimensional dendrite Cu-Co/rGO architectures on disposable
Electronic Supplementary Information (ESI) Three dimensional dendrite Cu-Co/rGO architectures on disposable pencil graphite electrode as an electrochemical sensor for non-enzymatic glucose detection K.
More informationSupporting Information
Supporting Information Nest-like NiCoP for Highly Efficient Overall Water Splitting Cheng Du, a Lan Yang, a Fulin Yang, a Gongzhen Cheng a and Wei Luo a,b* a College of Chemistry and Molecular Sciences,
More informationSelf-Supported Three-Dimensional Mesoporous Semimetallic WP 2. Nanowire Arrays on Carbon Cloth as a Flexible Cathode for
Electronic Supplementary Material (ESI) for Nanoscale. This journal is The Royal Society of Chemistry 2016 Electronic supplementary information Self-Supported Three-Dimensional Mesoporous Semimetallic
More informationElectronic Supplementary Information
Electronic Supplementary Material (ESI) for Journal of Materials Chemistry A. This journal is The Royal Society of Chemistry 2016 Electronic Supplementary Information Mesoporous C-coated SnO x nanosheets
More informationanthracene Figure 1: Structures of Selected Polyaromatic Hydrocarbons (PAHs)
Stir Bar Sorptive Extraction Analysis of PAHs in Aqueous Solution: Using a polymer based technique to pre-concentrate polyaromatic hydrocarbons for analysis by GC-MS. Background: Polyaromatic hydrocarbons
More informationSupporting Information. Co 4 N Nanosheets Assembled Mesoporous Sphere as a Matrix for Ultrahigh Sulfur Content Lithium Sulfur Batteries
Supporting Information Co 4 N Nanosheets Assembled Mesoporous Sphere as a Matrix for Ultrahigh Sulfur Content Lithium Sulfur Batteries Ding-Rong Deng, Fei Xue, Yue-Ju Jia, Jian-Chuan Ye, Cheng-Dong Bai,
More informationSupporting Information
Electronic Supplementary Material (ESI) for Journal of Materials Chemistry A. This journal is The Royal Society of Chemistry 2018 Supporting Information Si/SiO x Hollow Nanospheres/Nitrogen-Doped Carbon
More informationSupporting information. One-step facile synthesis of novel β-amino alcohol functionalized
Electronic Supplementary Material (ESI) for RSC Advances. This journal is The Royal Society of Chemistry 2016 Supporting information One-step facile synthesis of novel β-amino alcohol functionalized carbon
More informationAppNote 2/2000. Stir Bar Sorptive Extraction (SBSE) applied to Environmental Aqueous Samples
AppNote 2/2 Stir Bar Sorptive Extraction (SBSE) applied to Environmental Aqueous Samples Pat Sandra Department of Organic Chemistry, University of Gent, Krijgslaan 281 S4, B-9 Gent, Belgium Erik Baltussen
More informationDominating Role of Aligned MoS 2 /Ni 3 S 2. Nanoarrays Supported on 3D Ni Foam with. Hydrophilic Interface for Highly Enhanced
Supporting Information Dominating Role of Aligned MoS 2 /Ni 3 S 2 Nanoarrays Supported on 3D Ni Foam with Hydrophilic Interface for Highly Enhanced Hydrogen Evolution Reaction Jiamu Cao a, Jing Zhou a,
More informationSupporting Information
Supporting Information Fe 3 O 4 @Carbon Nanosheets for All-Solid-State Supercapacitor Electrodes Huailin Fan, Ruiting Niu, & Jiaqi Duan, Wei Liu and Wenzhong Shen * State Key Laboratory of Coal Conversion,
More informationFlexible Asymmetrical Solid-state Supercapacitors Based on Laboratory Filter Paper
SUPPORTING INFORMATION Flexible Asymmetrical Solid-state Supercapacitors Based on Laboratory Filter Paper Leicong Zhang,,,# Pengli Zhu,,,#, * Fengrui Zhou, Wenjin Zeng, Haibo Su, Gang Li, Jihua Gao, Rong
More informationSupporting Information
Supporting Information Ultrasensitive Label-Free Resonance Rayleigh Scattering Aptasensor for Hg 2+ Using Hg 2+ -Triggered Exonuclease III-Assisted Target Recycling and Growth of G-Wires for Signal Amplification
More informationHexagonal-Phase Cobalt Monophosphosulfide for. Highly Efficient Overall Water Splitting
Supporting Information for Hexagonal-Phase Cobalt Monophosphosulfide for Highly Efficient Overall Water Splitting Zhengfei Dai,,, Hongbo Geng,,, Jiong Wang, Yubo Luo, Bing Li, ǁ Yun Zong, ǁ Jun Yang, Yuanyuan
More informationSupporting Information
Supporting Information N,P-co-doped Meso-/microporous Carbon Derived from Biomass Materials via a Dual-activation Strategy as High-performance Electrodes for Deionization Capacitors Dong Xu,, Ying Tong,,
More informationSupplementary Information
Electronic Supplementary Material (ESI) for RSC Advances. This journal is The Royal Society of Chemistry 2017 Supplementary Information Supramolecular interactions via hydrogen bonding contributing to
More informationRational One-Step Synthesis of Porous PtPdRu Nanodendrites for Ethanol Oxidation Reaction with a Superior Tolerance for COpoisoning
Electronic Supplementary Material (ESI) for Nanoscale. This journal is The Royal Society of Chemistry 2017 Supporting information for Rational One-Step Synthesis of PtPdRu Nanodendrites for Ethanol Oxidation
More informationPt-like Hydrogen Evolution Electrocatalysis on PANI/CoP Hybrid Nanowires. by Weakening the Shackles of Hydrogen Ions on the Surfaces of Catalysts
Pt-like Hydrogen Evolution Electrocatalysis on PANI/CoP Hybrid Nanowires by Weakening the Shackles of Hydrogen Ions on the Surfaces of Catalysts Jin-Xian Feng, Si-Yao Tong, Ye-Xiang Tong, and Gao-Ren Li
More informationSupporting Information
Electronic Supplementary Material (ESI) for Nanoscale. This journal is The Royal Society of Chemistry 2015 Supporting Information Synthesis and electrochemical properties of spherical and hollow-structured
More informationHigh Salt Removal Capacity of Metal-Organic Gel Derived. Porous Carbon for Capacitive Deionization
Supporting Information High Salt Removal Capacity of Metal-Organic Gel Derived Porous Carbon for Capacitive Deionization Zhuo Wang, Tingting Yan, Guorong Chen, Liyi Shi and Dengsong Zhang* Research Center
More informationGeneral Synthesis of Graphene-Supported. Bicomponent Metal Monoxides as Alternative High- Performance Li-Ion Anodes to Binary Spinel Oxides
Electronic Supplementary Material (ESI) for Journal of Materials Chemistry A. This journal is The Royal Society of Chemistry 2016 Electronic Supplementary Information (ESI) General Synthesis of Graphene-Supported
More informationFull-Color Light-Emitting Carbon Dots with a Surface-State
Supporting information Full-Color Light-Emitting Carbon Dots with a Surface-State -Controlled Luminescence Mechanism Hui Ding, Shang-Bo Yu, Ji-Shi Wei and Huan-Ming Xiong* Department of Chemistry, Fudan
More informationPhoto of the mass manufacture of the Fe-rich nanofiber film by free-surface electrospinning technique
Supporting Information Design 3D hierarchical architectures of carbon and highly active transition-metals (Fe, Co, Ni) as bifunctional oxygen catalysts for hybrid lithiumair batteries Dongxiao Ji, Shengjie
More informationSupporting Information
Supporting Information A General Strategy for the Synthesis of Transition-Metal Phosphide/N-doped Carbon Frameworks for Hydrogen and Oxygen Evolution Zonghua Pu, Chengtian Zhang, Ibrahim Saana Amiinu,
More informationfor highly efficient and stable corrosive-water evaporation
Electronic Supplementary Material (ESI) for Journal of Materials Chemistry A. This journal is The Royal Society of Chemistry 2018 Electronic Supplementary Information Synthesis of mesoporous Fe 3 Si aerogel
More informationSupporting Information. Metal-Organic Frameworks Mediated Synthesis of One-Dimensional Molybdenum-Based/Carbon Composites for Enhanced Lithium Storage
Supporting Information Metal-Organic Frameworks Mediated Synthesis of One-Dimensional Molybdenum-Based/Carbon Composites for Enhanced Lithium Storage Wei Tian a, Han Hu b, Yixian Wang a, Peng Li c, Jingyan
More informationSupporting Information for
Supporting Information for Multilayer CuO@NiO Hollow Spheres: Microwave-Assisted Metal-Organic-Framework Derivation and Highly Reversible Structure-Matched Stepwise Lithium Storage Wenxiang Guo, Weiwei
More informationEfficient removal of typical dye and Cr(VI) reduction using N-doped
Electronic Supplementary Material (ESI) for RSC Advances. This journal is The Royal Society of Chemistry 2014 Efficient removal of typical dye and Cr(VI) reduction using N-doped magnetic porous carbon
More informationSupporting Infromation
Supporting Infromation Transparent and Flexible Self-Charging Power Film and Its Application in Sliding-Unlock System in Touchpad Technology Jianjun Luo 1,#, Wei Tang 1,#, Feng Ru Fan 1, Chaofeng Liu 1,
More informationHoneycomb-like Interconnected Network of Nickel Phosphide Hetero-nanoparticles
Supporting Information Honeycomb-like Interconnected Network of Nickel Phosphide Hetero-nanoparticles with Superior Electrochemical Performance for Supercapacitors Shude Liu a, Kalimuthu Vijaya Sankar
More informationConversion and Storage, School of Chemistry and Chemical Engineering, Harbin Institute of Technology, Harbin , PR China
Supporting information for Assembly of flexible CoMoO 4 @NiMoO 4 xh 2 O and Fe 2 O 3 electrodes for solid-state asymmetric supercapacitors Jing Wang a, Leipeng Zhang b, Xusong Liu a, Xiang Zhang b, Yanlong
More informationgraphene oxide as robust platform for highly sensitive uric acid detection
Electronic Supplementary Material (ESI) for Nanoscale. This journal is The Royal Society of Chemistry 2017 Supporting Information CeO 2-x /C/rGO nanocomposites derived from Ce-MOF and graphene oxide as
More informationSupporting Information
Supporting Information Hierarchical Mesoporous Zinc-Nickel-Cobalt Ternary Oxide Nanowire Arrays on Nickel Foam as High Performance Electrodes for Supercapacitors Chun Wu a, Junjie Cai a, Qiaobao Zhang
More informationOne-pot synthesis of bi-metallic PdRu tripods as an efficient catalyst for. electrocatalytic nitrogen reduction to ammonia
Electronic Supplementary Material (ESI) for Journal of Materials Chemistry A. This journal is The Royal Society of Chemistry 2018 Supporting Information for One-pot synthesis of bi-metallic PdRu tripods
More informationSupporting Information for
Electronic Supplementary Material (ESI) for Journal of Materials Chemistry A. This journal is The Royal Society of Chemistry 2019 Supporting Information for Enhanced cycling stability of boron-doped lithium-rich
More informationSupporting Information
Supporting Information Heterostructured Bi 2 S 3 -Bi 2 O 3 Nanosheets with a Built-In Electric Field for Improved Sodium Storage Wen Luo, a,b Feng Li, a Qidong Li, a Xuanpeng Wang, a Wei Yang, a Liang
More informationCarbon-encapsulated heazlewoodite nanoparticles as highly efficient and durable electrocatalysts for oxygen evolution reactions
Electronic Supplementary Material Carbon-encapsulated heazlewoodite nanoparticles as highly efficient and durable electrocatalysts for oxygen evolution reactions Mohammad Al-Mamun 1, Huajie Yin 1, Porun
More informationSupporting Information
Supporting Information Transparent and Self-supporting Graphene Films with Wrinkled- Graphene-Wall-assembled Opening Polyhedron Building Blocks for High Performance Flexible/Transparent Supercapacitors
More informationScalable Preparation of Hierarchical Porous Activated Carbon/graphene composite for High-Performance Supercapacitors
Electronic Supplementary Material (ESI) for Journal of Materials Chemistry A. This journal is The Royal Society of Chemistry 2019 Supplementary Information Scalable Preparation of Hierarchical Porous Activated
More informationSupporting information
Electronic Supplementary Material (ESI) for Journal of Materials Chemistry A. This journal is The Royal Society of Chemistry 2018 Supporting information Effect of cation substitution on pseudocapacitive
More informationSupporting Information. sulfurization of a bi-metal-organic framework for highperformance. supercapacitor and its photocurrent
Electronic Supplementary Material (ESI) for Dalton Transactions. This journal is The Royal Society of Chemistry 2018 Supporting Information One-step synthesis of MnS/MoS 2 /C through calcination and sulfurization
More informationFacile synthesis of accordion-like Ni-MOF superstructure for highperformance
Electronic Supplementary Material (ESI) for Journal of Materials Chemistry A. This journal is The Royal Society of Chemistry 2016 Supplementary Information Facile synthesis of accordion-like Ni-MOF superstructure
More informationSupplementary Information for
Supplementary Information for Highly Self-healable 3D Microsupercapacitor with MXene-Graphene Composite Aerogel Yang Yue, Nishuang Liu, * Yanan Ma, Siliang Wang, Weijie Liu, Cheng Luo Hang Zhang, Feng
More informationTuning the Shell Number of Multi-Shelled Metal Oxide. Hollow Fibers for Optimized Lithium Ion Storage
Supporting Information Tuning the Shell Number of Multi-Shelled Metal Oxide Hollow Fibers for Optimized Lithium Ion Storage Jin Sun, Chunxiao Lv, Fan Lv, ǁ Shuai Chen, Daohao Li, Ziqi Guo, Wei Han, Dongjiang
More informationPhytic Acid-Assisted Formation of Hierarchical Porous CoP/C Nanoboxes for Enhanced Lithium Storage and Hydrogen Generation
Phytic Acid-Assisted Formation of Hierarchical Porous CoP/C Nanoboxes for Enhanced Lithium Storage and Hydrogen Generation Xuxu Wang, ab Zhaolin Na, a Dongming Yin, a Chunli Wang, ab Yaoming Wu, a Gang
More informationEffective Adsorption of Pd(II), Pt(IV) and Au(III) by Zr- Cluster-Based Metal-Organic Frameworks from Strongly Acidic Solution
Electronic Supplementary Material (ESI) for Journal of Materials Chemistry A. This journal is The Royal Society of Chemistry 2017 Supporting Information Effective Adsorption of Pd(II), Pt(IV) and Au(III)
More informationSupporting Information for:
Electronic Supplementary Material (ESI) for Journal of Materials Chemistry A. This journal is The Royal Society of Chemistry 2017 Supporting Information for: A Highly Efficient Electrocatalyst Based on
More informationMulticomponent (Mo, Ni) metal sulfide and selenide microspheres with empty nanovoids as anode materials for Na-ion batteries
Electronic Supplementary Material (ESI) for Journal of Materials Chemistry A. This journal is The Royal Society of Chemistry 2017 Multicomponent (Mo, Ni) metal sulfide and selenide microspheres with empty
More informationJournal of Materials Chemistry A ELECTRONIC SUPPLEMENTARY INFORMATION (ESI )
Electronic Supplementary Material (ESI) for Journal of Materials Chemistry A. This journal is The Royal Society of Chemistry 218 Journal of Materials Chemistry A ELECTRONIC SUPPLEMENTARY INFORMATION (ESI
More informationSupporting Information
Electronic Supplementary Material (ESI) for Journal of Materials Chemistry A. This journal is The Royal Society of Chemistry 2015 Supporting Information 1. Synthesis of perovskite materials CH 3 NH 3 I
More informationCHEM. RES. CHINESE UNIVERSITIES 2011, 27(2),
CHEM. RES. CHINESE UNIVERSITIES 2011, 27(2), 198 202 Solid-phase Microextraction with Benzoxy-calix[6]arene Fiber Coupled to Gas Chromatography for the Analysis of Polycyclic Aromatic Hydrocarbons in Water
More informationGraphene Aerogel Composites Derived From Recycled. Cigarette Filter for Electromagnetic Wave Absorption
Electronic Supplementary Material (ESI) for Journal of Materials Chemistry C. This journal is The Royal Society of Chemistry 2015 Graphene Aerogel Composites Derived From Recycled Cigarette Filter for
More informationMetal-Organic Framework Derived Iron Sulfide-Carbon Core-Shell Nanorods as a Conversion-Type Battery Material
Supporting Information Metal-Organic Framework Derived Iron Sulfide-Carbon Core-Shell Nanorods as a Conversion-Type Battery Material Wei Huang,, Shuo Li, Xianyi Cao, Chengyi Hou, Zhen Zhang, Jinkui Feng,
More informationCloth for High-Efficient Electrocatalytic Urea Oxidation
Electronic Supplementary Material (ESI) for Journal of Materials Chemistry A. This journal is The Royal Society of Chemistry 2018 Supporting Information In-situ Growth of Single-Layered α-ni(oh) 2 Nanosheets
More informationSupporting Information
Supporting Information MoSe2 embedded CNT-Reduced Graphene Oxide (rgo) Composite Microsphere with Superior Sodium Ion Storage and Electrocatalytic Hydrogen Evolution Performances Gi Dae Park, Jung Hyun
More informationNickel Cobalt Thiospinel Nanoparticles as Hydrodesulfurization Catalysts: Importance of Cation Position, Structural Stability and Sulfur Vacancy
Nickel Cobalt Thiospinel Nanoparticles as Hydrodesulfurization Catalysts: Importance of Cation Position, Structural Stability and Sulfur Vacancy Kun Guo a,b, Yi Ding c, Jun Luo c, and Zhixin Yu a,b * a
More informationSupporting Information
Supporting Information Hierarchical Porous N-doped Graphene Monoliths for Flexible Solid-State Supercapacitors with Excellent Cycle Stability Xiaoqian Wang, Yujia Ding, Fang Chen, Han Lu, Ning Zhang*,
More informationLotus root-like porous carbon nanofiber anchored with CoP nanoparticles as all-ph hydrogen evolution electrocatalysts
Electronic Supplementary Material Lotus root-like porous carbon nanofiber anchored with CoP nanoparticles as all-ph hydrogen evolution electrocatalysts Hengyi Lu 1, Wei Fan 2 ( ), Yunpeng Huang 1, and
More informationSupporting Information (SI) Headspace Solid-Phase Microextraction Coupled to. Miniaturized Microplasma Optical Emission Spectrometry
Supporting Information (SI) Headspace Solid-Phase Microextraction Coupled to Miniaturized Microplasma Optical Emission Spectrometry for Detection of Mercury and Lead Chengbin Zheng,, Ligang Hu, Xiandeng
More informationMultifunctional bi-continuous composite foams with ultralow percolation thresholds
Supporting Information for Multifunctional bi-continuous composite foams with ultralow percolation thresholds Jiabin Xi 1,, Yingjun Liu 1,, Ying Wu 1,4, Jiahan Hu 1, Weiwei Gao 1, Erzhen Zhou 1,3, Honghui
More informationSupporting Information
Supporting Information Zeolite-Templated Mesoporous Silicon Particles for Advanced Lithium-Ion Battery Anodes Nahyeon Kim, Hyejung Park, Naeun Yoon, and Jung Kyoo Lee * Department of Chemical Engineering,
More informationSupporting material. Figures
Electronic Supplementary Material (ESI) for New Journal of Chemistry. This journal is The Royal Society of Chemistry and the Centre National de la Recherche Scientifique 2018 Supporting material Figures
More informationSupporting Information
Electronic Supplementary Material (ESI) for Journal of Materials Chemistry A. This journal is The Royal Society of Chemistry 2018 Supporting Information Na3V2(PO4)2F3-SWCNT: A High Voltage Cathode for
More informationFabrication of Metallic Nickel-Cobalt Phosphide Hollow Microspheres for. High-Rate Supercapacitors
Supporting Information Fabrication of Metallic Nickel-Cobalt Phosphide Hollow Microspheres for High-Rate Supercapacitors Miao Gao, Wei-Kang Wang, Xing Zhang, Jun Jiang, Han-Qing Yu CAS Key Laboratory of
More informationSupplementary Information
Electronic Supplementary Material (ESI) for Nanoscale. This journal is The Royal Society of Chemistry 2014 Supplementary Information Highly efficient and recyclable triple-shelled Ag@Fe 3 O 4 @SiO 2 @TiO
More informationSupporting Information
Supporting Information Modulation of PEDOT:PSS ph for Efficient Inverted Perovskite Solar Cells with Reduced Potential Loss and Enhanced Stability Qin Wang 1,2, Chu-Chen Chueh 1, Morteza Eslamian 2 * and
More informationMorphology-controllable ZnO rings: ionic liquid-assisted hydrothermal synthesis, growth mechanism and photoluminescence properties
Morphology-controllable ZnO rings: ionic liquid-assisted hydrothermal synthesis, growth mechanism and photoluminescence properties (Supporting information) Kezhen Qi, a Jiaqin Yang, a Jiaqi Fu, a Guichang
More informationLarge-Scale Multifunctional Electrochromic-Energy Storage Device Based on Tungsten Trioxide Monohydrate Nanosheets and Prussian White
Supporting Information Large-Scale Multifunctional Electrochromic-Energy Storage Device Based on Tungsten Trioxide Monohydrate Nanosheets and Prussian White Zhijie Bi, a,b Xiaomin Li,* a Yongbo Chen, a,b
More informationHierarchical Nanocomposite by Integrating Reduced Graphene Oxide and Amorphous Carbon with Ultrafine MgO Nanocrystallites for Enhanced CO 2 Capture
Supporting Information Hierarchical Nanocomposite by Integrating Reduced Graphene Oxide and Amorphous Carbon with Ultrafine MgO Nanocrystallites for Enhanced CO 2 Capture Ping Li, and Hua Chun Zeng* Department
More informationEngineering of Hollow Core-Shell Interlinked Carbon Spheres for Highly Stable Lithium-Sulfur Batteries
SUPPLEMENTARY INFORMATION Engineering of Hollow Core-Shell Interlinked Carbon Spheres for Highly Stable Lithium-Sulfur Batteries Qiang Sun, Bin He, Xiang-Qian Zhang, and An-Hui Lu* State Key Laboratory
More informationSupporting Information. for Water Splitting. Guangxing Zhang, Jie Yang, Han Wang, Haibiao Chen, Jinlong Yang, and Feng Pan
Supporting Information Co 3 O 4-δ Quantum Dots as a Highly Efficient Oxygen Evolution Reaction Catalyst for Water Splitting Guangxing Zhang, Jie Yang, Han Wang, Haibiao Chen, Jinlong Yang, and Feng Pan
More informationDegradation of Bisphenol A by Peroxymonosulfate Catalytically Activated with. Gui-Xiang Huang, Chu-Ya Wang, Chuan-Wang Yang, Pu-Can Guo, Han-Qing Yu*
Supporting Information for Degradation of Bisphenol A by Peroxymonosulfate Catalytically Activated with Mn 1.8 Fe 1.2 O 4 Nanospheres: Synergism between Mn and Fe Gui-Xiang Huang, Chu-Ya Wang, Chuan-Wang
More informationSupporting Information. Unique Core-Shell Concave Octahedron with Enhanced Methanol Oxidation Activity
Supporting Information Unique Cu@CuPt Core-Shell Concave Octahedron with Enhanced Methanol Oxidation Activity Qi Wang a, Zhiliang Zhao c, Yanlin Jia* b, Mingpu Wang a, Weihong Qi a, Yong Pang a, Jiang
More informationSupporting Information. Electronic Modulation of Electrocatalytically Active. Highly Efficient Oxygen Evolution Reaction
Supporting Information Electronic Modulation of Electrocatalytically Active Center of Cu 7 S 4 Nanodisks by Cobalt-Doping for Highly Efficient Oxygen Evolution Reaction Qun Li, Xianfu Wang*, Kai Tang,
More informationSupplementary Information for. Immobilizing photogenerated electrons from graphitic carbon nitride for
Supplementary Information for Immobilizing photogenerated electrons from graphitic carbon nitride for an improved visible-light photocatalytic activity Han Sun, Yue Cao, Leiyu Feng *, Yinguang Chen * State
More informationElectronic Supplementary Information
Electronic Supplementary Material (ESI) for ChemComm. This journal is The Royal Society of Chemistry 2018 Electronic Supplementary Information One-Dimensional MoO2-Co2Mo3O8@C Nanorods: A Novel and High
More informationGraphene Size-dependent Modulation of Graphene Framework Contributing to Superior. Thermal Conductivity of Epoxy Composite
Electronic Supplementary Material (ESI) for Journal of Materials Chemistry A. This journal is The Royal Society of Chemistry 2018 Graphene Size-dependent Modulation of Graphene Framework Contributing to
More informationElectronic Supplementary Information
Electronic Supplementary Material (ESI) for Dalton Transactions. This journal is The Royal Society of Chemistry 2018 Electronic Supplementary Information In situ growth of heterostructured Sn/SnO nanospheres
More informationSupporting Information
Supporting Information Enhanced Photocatalytic Activity of Titanium Dioxide: Modification with Graphene Oxide and Reduced Graphene Oxide Xuandong Li,* Meirong Kang, Xijiang Han, Jingyu Wang, and Ping Xu
More informationSupplementary Information for
Supplementary Information for Facile transformation of low cost thiourea into nitrogen-rich graphitic carbon nitride nanocatalyst with high visible light photocatalytic performance Fan Dong *a, Yanjuan
More informationA label-free colorimetric strategy for facile and low-cost sensing of
Electronic Supplementary Material (ESI) for Analytical Methods. This journal is The Royal Society of Chemistry 2019 Supporting Information A label-free colorimetric strategy for facile and low-cost sensing
More informationElectronic Supplementary Information
Electronic Supplementary Material (ESI) for Journal of Materials Chemistry A. This journal is The Royal Society of Chemistry 2017 Electronic Supplementary Information A coaxial triboelectric nanogenerator
More informationElectronic Supplementary Information
Electronic Supplementary Material (ESI) for Journal of Materials Chemistry A. This journal is The Royal Society of Chemistry 2017 Electronic Supplementary Information Cation exchange MOF-derived nitrogen-doped
More informationSupporting Information. Ze-Min Zhang, Lu-Yi Pan, Wei-Quan Lin, Ji-Dong Leng, Fu-Sheng Guo, Yan-Cong Chen, Jun-Liang Liu, and Ming-Liang Tong*
Supporting Information Wheel-shaped nanoscale 3d-4f {Co II 16Ln III 24} clusters (Ln = Dy and Gd) Ze-Min Zhang, Lu-Yi Pan, Wei-Quan Lin, Ji-Dong Leng, Fu-Sheng Guo, Yan-Cong Chen, Jun-Liang Liu, and Ming-Liang
More informationApplication of Nano-ZnO on Antistatic Finishing to the Polyester Fabric
Modern Applied Science January, 2009 Application of Nano-ZnO on Antistatic Finishing to the Polyester Fabric Fan Zhang & Junling Yang School of Material Science and Chemical Engineer Tianjin Polytechnic
More information