Supporting Information. Unique Core-Shell Concave Octahedron with Enhanced Methanol Oxidation Activity
|
|
- Barbra Watts
- 5 years ago
- Views:
Transcription
1 Supporting Information Unique Core-Shell Concave Octahedron with Enhanced Methanol Oxidation Activity Qi Wang a, Zhiliang Zhao c, Yanlin Jia* b, Mingpu Wang a, Weihong Qi a, Yong Pang a, Jiang Yi a, Yufang Zhang a, Zhou Li a, Zhuo Zhang d a. School of Materials Science and Engineering, Central South University, Changsha, , P. R. China b. School of Materials Science and Engineering, Beijing University of Technology, Beijing, , P.R. China c. Institute for Clean Energy & Advanced Materials, Faculty of Materials and Energy, Southwest University, Chongqing , P. R. China. d. Advanced Research Center, Central South University, Changsha, , P. R. China * Corresponding authors: jiayanlin@126.com (Yanlin Jia) KEYWORDS: Core-shell, High-index, CuPt, Concave octahedron, Methanol oxidation reaction S-1
2 Table of contents: Synthesis of CuPt octahedron Figure S1: Magnified SEM and TEM images. Figure S2: Atomic model of high index surfaces. Figure S3: HRTEM images of core and shell and corresponding FFT. Figure S4: Color change overall the reaction process. Figure S5: Geometry model of rhombic dodecahedron. Figure S6: TEM images of T21/2-25/2 and T25/4. Figure S7: TEM images of T21/2 and T25/2, and corresponding EDS results. Figure S8: TEM images of T15.5/2-25/2 and corresponding CV curves. Figure S9: XRD, XPS comparison of T17/2-25/2, T21/2-25/2 and T25/4. Table S1: Composition of samples determined by ICP-AES, EDS and XPS Figure S10: HADDF-STEM image of catalyst. Figure S11: CV profiles of catalyst dealloying process. Figure S12: TEM images and XRD pattern of octahedral CuPt nanocrystals Figure S13: CV profiles of and commercial before and after 1000 cycles. Figure S14: Morphology observation of catalyst and commercial Pt/C before and after cycling. Table S2: Summary of typical reported CuPt catalysis for MOR Reference S-2
3 Additional experimental procedure Synthesis of CuPt nanooctahedron In a typical procedure, 14 mg of Cu(acac) 2, 20 mg of Pt(acac) 2 and 1 ml OAm were added in 9 ml N,N-Dimethylformamide (DMF) solution. The mixture was magnetically stirred at 40 for 30 min. After that, the resulting solution was heated in a Teflon-lined stainless steel autoclave at 180 for 12 h and then cooled down to room temperature. The obtained sample was then loaded on Vulcan XC-72 carbon. S-3
4 Figure S1 Magnified SEM (A) and TEM (B) image illustrates the uniformity of as-prepared concave octahedron particles S-4
5 Figure S3 (A) HRTEM including core and leg of a concave octahedron particle. (B) lattice fringe and (D) corresponding FFT of core, the d-spacing was measured to be 2.10 Å. (C) lattice fringe and (E) corresponding FFT of core, the d-spacing was measured to be 2.19 Å. It is obvious that the core and shell have the same orientation. The overlap of (D) and (E) show the indistinguishable nature of core and shell through SEAD. Figure S4 color of different reaction stages reflecting the revolution of products. From brilliant yellow to orange, green and finally dark. S-5
6 Figure S5 Geometry model of rhombic dodecahedron. It is encapsulated by twelve (110) surface, any preferable deposition of shell in the preferential deposit site may lead to higher index S-6
7 Figure S6 TEM images of the nanoparticles synthesized by different initial temperature. (A) and (B) images of sample T21/2-25/2. (C) and (D) images of sample T25/4. As seen in (A-B), no obvious morphology change was spotted in T21/2-25/2 except for decreased size compared to T17/2-25/2. However, when initial temperature raised to 250, some sphere particles were found (C-D). S-7
8 Figure S7 (A) TEM image of sample collected at 2 hours after reacted at an initial 210 (T21/2). (B) TEM-EDS of T21/2 and T21/2-25/2, revealing majority of Pt atoms have deposit after 2 hours at 210. (C) TEM image of sample collected at 2 hours after reacted at an initial 250. (D) TEM-EDS of T25/2 and T25/4. S-8
9 Figure S8 (A) TEM images of samples obtained under an initial temperature of 155. (B) corresponding distribution histogram of nanoparticles. (C) CV profiles of the catalysts recorded in N 2 -saturated 0.5 M H 2 SO 4 solution at a sweep rate of 50 mv s -1 and (D) CV profiles of mass activities of T15.5/2-25/2 catalysts for MOR in 0.5 M H 2 SO M CH 3 OH solutions. These particles still present concave octahedron morphology, but the size ranges from nm in this initial temperature. The reason can be attributed to uneven Cu seeds. The ECSAs (12.2 m 2 g -1 ) and mass activity (277 A g -1 Pt) are also poor due to the large size. S-9
10 Figure S9 (A) XRD patterns of T17/2-25/2, T21/2-25/2 and T25/4. (B) magnification of black box in (A), revealing up-shift of (111) peak of CuPt alloy. (C) XPS spectra of T17/2-25/2, T21/2-25/2 and T25/4, demonstrating surface Cu/Pt molar ratio of these samples. (D) High-resolution XPS patterns of the Pt 4f. Table S1 Compositions (Cu/Pt molar ratios) of different samples determined by EDS, ICP and XPS. Cu/Pt ICP-AES EDS XPS sample before after T17/2-25/2 71.9/ / / :39.9 T21/2-25/2 75.1/ / / :42.3 T25/4 70.1/ / / :44.9 S-10
11 Figure S10 HAADF STEM image of after loaded on Vulcant-72 carbon. Figure S11 CV profiles of catalyst during electrochemical dealloying process. The broad hydrogen-adsorption/desorption regime and redox-peak couple of Pt oxide become clear by gradual removal of Cu atom. Stable CV curve was obtained after 3 cycles, facilitating the identification of low Cu content surface. S-11
12 S-12
13 Figure S13 Voltammetry curves for (A) commercial Pt/C catalyst and (C) T17/2-25/2 catalyst before and after the accelerated stability tests. sweep rate, 100 mv s -1. And electrocatalytic stability test of (B) commercial Pt/C catalyst and (D) T17/2-25/2 Cu@CuPt/C catalyst before and after 1000 cycles of accelerated stability tests. sweep rate, 50 mv s -1. Normalized to the loading amount of Pt. S-13
14 Figure S14 TEM images of commercial Pt/C catalyst (A-B) and catalyst (C-F) before (C) and after 1000 cycles (D-F). No obvious aggregation was spotted in catalyst. In contrast, commercial Pt/C catalyst suffer serious aggregation after 1000 cycles. (E) magnified TEM images disclosing gradual miss of Cu-rich core. (F) HRTEM of legs revealing the invariability of CuPt shell. S-14
15 Table S2: Summary of typical reported CuPt catalysis for MOR Catalyst Electrolyte Mass activity/a mg-1 Specific activity/ma cm-2 Ref Pt Cu alloy concave nanocubes 0.1 M HClO PtCu hexapod 0.5 M H2SO hollow-ptcu 0.5 M H2SO Nanoporous Pt Cu Microwires rhombic dodecahedral PtCu nanoframes 0.5 M H2SO M HClO Pt Cu hollow 0.5 M H2SO Pt-Cu nanoparticles 0.5 M H2SO porous PtCu 0.1 M HClO PtCu Nanowire 0.5 M H2SO Hierarchical Branched Pt-Cu 0.5 M H2SO concave octahedron Cu@CuPt 0.5 M H2SO this work S-15
16 Reference 1.Qi, Y.; Bian, T.; Choi, S.-I.; Jiang, Y.; Jin, C.; Fu, M.; Zhang, H.; Yang, D., Kinetically Controlled Synthesis of Pt Cu Alloy Concave Nanocubes with High-Index Facets for Methanol Electro-oxidation. Chem. Commun. 2014, 50 (5), Wang, K.; Sriphathoorat, R.; Luo, S.; Tang, M.; Du, H.; Shen, P. K., Ultrathin PtCu Hexapod Nanocrystals with Enhanced Catalytic Performance for Electro-oxidation Reactions. J. Mater. Chem. A 2016, 4 (35), Huang, X.; Chen, Y.; Zhu, E.; Xu, Y.; Duan, X.; Huang, Y., Monodisperse Cu@ PtCu Nanocrystals and Their Conversion into Hollow-PtCu Nanostructures for Methanol Oxidation. J. Mater. Chem. A 2013, 1 (46), Qiu, H.-J.; Shen, X.; Wang, J.; Hirata, A.; Fujita, T.; Wang, Y.; Chen, M., Aligned Nanoporous Pt Cu Bimetallic Microwires with High Catalytic Activity toward Methanol Electrooxidation. ACS Catal. 2015, 5 (6), Ding, J.; Zhu, X.; Bu, L.; Yao, J.; Guo, J.; Guo, S.; Huang, X., Highly Open Rhombic Dodecahedral PtCu Nanoframes. Chem. Commun. 2015, 51 (47), Yu, X.; Wang, D.; Peng, Q.; Li, Y., High Performance Electrocatalyst Pt Cu Hollow Nanocrystals. Chem. Commun. 2011, 47 (28), Du, X.; Luo, S.; Du, H.; Tang, M.; Huang, X.; Shen, P. K., Monodisperse and Self-Assembled Pt-Cu Nanoparticles as An Efficient Electrocatalyst for The Methanol Oxidation Reaction. J. Mater. Chem. A 2016, 4 (5), Eid, K.; Wang, H.; He, P.; Wang, K.; Ahamad, T.; Alshehri, S. M.; Yamauchi, Y.; Wang, L., One-Step Synthesis of Porous Bimetallic PtCu Nanocrystals with High Electrocatalytic Activity for Methanol Oxidation Reaction. Nanoscale 2015, 7 (40), Xiao, M.; Li, S.; Zhao, X.; Zhu, J.; Yin, M.; Liu, C.; Xing, W., Enhanced Catalytic Performance of Composition Tunable PtCu Nanowire Networks for Methanol Electrooxidation. Chemcatchem 2014, 6 (10), Cao, Y.; Yang, Y.; Shan, Y.; Huang, Z., One-Pot and Facile Fabrication of Hierarchical Branched Pt Cu Nanoparticles as Excellent Electrocatalysts for Direct Methanol Fuel Cells. ACS Appl. Mater. Interfaces 2016, 8 (9), S-16
Highly Open Rhombic Dodecahedral PtCu Nanoframes
Electronic Supplementary Material (ESI) for ChemComm. This journal is The Royal Society of Chemistry 2015 Supporting information for Highly Open Rhombic Dodecahedral PtCu Nanoframes Jiabao Ding, a Xing
More informationSupporting Information
Supporting Information High Performance Electrocatalyst: Pt-Cu Hollow Nanocrystals Xiaofei Yu, a Dingsheng, a Qing Peng a and Yadong Li* a a Department of Chemistry, Tsinghua University, Beijing, 100084
More informationShape-selective Synthesis and Facet-dependent Enhanced Electrocatalytic Activity and Durability of Monodisperse Sub-10 nm Pt-Pd Tetrahedrons and Cubes
Supporting Information Shape-selective Synthesis and Facet-dependent Enhanced Electrocatalytic Activity and Durability of Monodisperse Sub-10 nm Pt-Pd Tetrahedrons and Cubes An-Xiang Yin, Xiao-Quan Min,
More informationSupporting Information
Electronic Supplementary Material (ESI) for Journal of Materials Chemistry A. This journal is The Royal Society of Chemistry 2018 Supporting Information Adding refractory 5d transition metal W into PtCo
More informationElectronic Supplementary Material. Methods. Synthesis of reference samples in Figure 1(b) Nano Res.
Electronic Supplementary Material Shaped Pt Ni nanocrystals with an ultrathin Pt-enriched shell derived from one-pot hydrothermal synthesis as active electrocatalysts for oxygen reduction Jun Gu 1,, Guangxu
More informationMultiply twinned Pt Pd nanoicosahedrons as highly active electrocatalyst for methanol oxidation
Supporting Information for Multiply twinned Pt Pd nanoicosahedrons as highly active electrocatalyst for methanol oxidation An-Xiang Yin, Xiao-Quan Min, Wei Zhu, Hao-Shuai Wu, Ya-Wen Zhang* and Chun-Hua
More informationSupporting Information
Supporting Information A General Strategy for the Synthesis of Transition-Metal Phosphide/N-doped Carbon Frameworks for Hydrogen and Oxygen Evolution Zonghua Pu, Chengtian Zhang, Ibrahim Saana Amiinu,
More informationSupporting Information for Active Pt 3 Ni (111) Surface of Pt 3 Ni Icosahedron for Oxygen Reduction
Supporting Information for Active Pt 3 Ni (111) Surface of Pt 3 Ni Icosahedron for Oxygen Reduction Jianbing Zhu,, Meiling Xiao,, Kui Li,, Changpeng Liu, Xiao Zhao*,& and Wei Xing*,, State Key Laboratory
More informationPomegranate-Like N, P-Doped Nanospheres as Highly Active Electrocatalysts for Alkaline Hydrogen Evolution
Supporting Information Pomegranate-Like N, P-Doped Mo2C@C Nanospheres as Highly Active Electrocatalysts for Alkaline Hydrogen Evolution Yu-Yun Chen,,,# Yun Zhang,,# Wen-Jie Jiang,, Xing Zhang,, Zhihui
More informationGeneral Synthesis of Graphene-Supported. Bicomponent Metal Monoxides as Alternative High- Performance Li-Ion Anodes to Binary Spinel Oxides
Electronic Supplementary Material (ESI) for Journal of Materials Chemistry A. This journal is The Royal Society of Chemistry 2016 Electronic Supplementary Information (ESI) General Synthesis of Graphene-Supported
More informationSupporting Information. Electronic Modulation of Electrocatalytically Active. Highly Efficient Oxygen Evolution Reaction
Supporting Information Electronic Modulation of Electrocatalytically Active Center of Cu 7 S 4 Nanodisks by Cobalt-Doping for Highly Efficient Oxygen Evolution Reaction Qun Li, Xianfu Wang*, Kai Tang,
More informationSupporting Information. Bi-functional Catalyst with Enhanced Activity and Cycle Stability for. Rechargeable Lithium Oxygen Batteries
Supporting Information Hierarchical Mesoporous/Macroporous Perovskite La 0.5 Sr 0.5 CoO 3-x Nanotubes: a Bi-functional Catalyst with Enhanced Activity and Cycle Stability for Rechargeable Lithium Oxygen
More informationMetal Organic Framework-Derived Metal Oxide Embedded in Nitrogen-Doped Graphene Network for High-Performance Lithium-Ion Batteries
Supporting Information for Metal Organic Framework-Derived Metal Oxide Embedded in Nitrogen-Doped Graphene Network for High-Performance Lithium-Ion Batteries Zhu-Yin Sui, Pei-Ying Zhang,, Meng-Ying Xu,
More informationSupporting Information
Supporting Information MoSe2 embedded CNT-Reduced Graphene Oxide (rgo) Composite Microsphere with Superior Sodium Ion Storage and Electrocatalytic Hydrogen Evolution Performances Gi Dae Park, Jung Hyun
More informationSupporting information
a Supporting information Core-Shell Nanocomposites Based on Gold Nanoparticle@Zinc-Iron- Embedded Porous Carbons Derived from Metal Organic Frameworks as Efficient Dual Catalysts for Oxygen Reduction and
More informationCo-vacancy-rich Co 1 x S nanosheets anchored on rgo for high-efficiency oxygen evolution
Electronic Supplementary Material Co-vacancy-rich Co 1 x S nanosheets anchored on rgo for high-efficiency oxygen evolution Jiaqing Zhu 1, Zhiyu Ren 1 ( ), Shichao Du 1, Ying Xie 1, Jun Wu 1,2, Huiyuan
More informationRevelation of the Excellent Intrinsic Activity. Evolution Reaction in Alkaline Medium
Supporting Information Revelation of the Excellent Intrinsic Activity of MoS2 NiS MoO3 Nanowires for Hydrogen Evolution Reaction in Alkaline Medium Chuanqin Wang a,b, Bin Tian b, Mei Wu b, Jiahai Wang
More informationSupplementary Information for
Supplementary Information for One-Nanometer-Thick PtNiRh Trimetallic Nanowires with Enhanced Oxygen Reduction Electrocatalysis in Acid Media: Integrating Multiple Advantages into One Catalyst Kan Li,,
More informationSupporting information:
Supporting information: The Role of Anisotropic Structure and Its Aspect Ratio: High-Loading Carbon Nanospheres Supported Pt Nanowires and Their High Performance Toward Methanol Electrooxidation Feng-Zhan
More informationSupporting Information for:
Electronic Supplementary Material (ESI) for Journal of Materials Chemistry A. This journal is The Royal Society of Chemistry 2017 Supporting Information for: A Highly Efficient Electrocatalyst Based on
More informationSupporting information
Supporting information imetallic AuRh nanodendrites consisting of Au icosahedron cores and atomically ultrathin Rh nanoplate shells: synthesis and light-enhanced catalytic activity Yongqiang Kang 1,2,
More informationSupplementary Figure 1. (a-b) EDX of Mo 2 and Mo 2
Supplementary Figure 1. (a-b) EDX of Mo 2 C@NPC/NPRGO and Mo 2 C@NPC. Supplementary Figure 2. (a) SEM image of PMo 12 2-PPy, (b) TEM, (c) HRTEM, (d) STEM image and EDX elemental mapping of C, N, P, and
More informationSelf-assembled pancake-like hexagonal tungsten oxide with ordered mesopores for supercapacitors
Electronic Supplementary Material (ESI) for Journal of Materials Chemistry A. This journal is The Royal Society of Chemistry 2018 Electronic Supporting Information Self-assembled pancake-like hexagonal
More informationSupplementary Information (ESI) Synthesis of Ultrathin Platinum Nanoplates for Enhanced Oxygen Reduction Activity
Electronic Supplementary Material (ESI) for Chemical Science. This journal is The Royal Society of Chemistry 2017 Supplementary Information (ESI) Synthesis of Ultrathin Platinum Nanoplates for Enhanced
More informationRational One-Step Synthesis of Porous PtPdRu Nanodendrites for Ethanol Oxidation Reaction with a Superior Tolerance for COpoisoning
Electronic Supplementary Material (ESI) for Nanoscale. This journal is The Royal Society of Chemistry 2017 Supporting information for Rational One-Step Synthesis of PtPdRu Nanodendrites for Ethanol Oxidation
More informationSupported 3-D Pt nanostructures: the straightforward synthesis and enhanced electrochemical performance for methanol oxidation in an acidic medium
Li, Z. et al. (2013). Supported 3-D Pt nanostructures: the straightforward synthesis and enhanced electrochemical performance for methanol oxidation in an acidic medium. Journal of Nanoparticle Research,
More informationSupporting Information
Supporting Information Facet-Selective Deposition of FeO x on α-moo 3 Nanobelts for Lithium Storage Yao Yao, 1 Nuo Xu, 2 Doudou Guan, 1 Jiantao Li, 1 Zechao Zhuang, 1 Liang Zhou,*,1 Changwei Shi 1, Xue
More informationSupporting Information
Electronic Supplementary Material (ESI) for Journal of Materials Chemistry A. This journal is The Royal Society of Chemistry 2017 Supporting Information Experimental section Synthesis of Ni-Co Prussian
More informationAn Advanced Anode Material for Sodium Ion. Batteries
Layered-Structure SbPO 4 /Reduced Graphene Oxide: An Advanced Anode Material for Sodium Ion Batteries Jun Pan, Shulin Chen, # Qiang Fu, Yuanwei Sun, # Yuchen Zhang, Na Lin, Peng Gao,* # Jian Yang,* and
More informationSupporting Information
Supporting Information Fe 3 O 4 @Carbon Nanosheets for All-Solid-State Supercapacitor Electrodes Huailin Fan, Ruiting Niu, & Jiaqi Duan, Wei Liu and Wenzhong Shen * State Key Laboratory of Coal Conversion,
More informationEngineering NiS/Ni 2 P Heterostructures for Efficient Electrocatalytic Water Splitting
Supporting Information Engineering NiS/Ni 2 P Heterostructures for Efficient Electrocatalytic Water Splitting Xin Xiao, Dekang Huang, Yongqing Fu, Ming Wen, Xingxing Jiang, Xiaowei Lv, Man Li, Lin Gao,
More informationFabrication of Metallic Nickel-Cobalt Phosphide Hollow Microspheres for. High-Rate Supercapacitors
Supporting Information Fabrication of Metallic Nickel-Cobalt Phosphide Hollow Microspheres for High-Rate Supercapacitors Miao Gao, Wei-Kang Wang, Xing Zhang, Jun Jiang, Han-Qing Yu CAS Key Laboratory of
More informationSupporting Information
Electronic Supplementary Material (ESI) for Nanoscale. This journal is The Royal Society of Chemistry 2014 Supporting Information Hydrothermal synthesis of - alloy nanooctahedra and their enhanced electrocatalytic
More informationHierarchical MoO 2 /Mo 2 C/C Hybrid Nanowires for High-Rate and. Long-Life Anodes for Lithium-Ion Batteries. Supporting Information
Supporting Information Hierarchical MoO 2 /Mo 2 C/C Hybrid Nanowires for High-Rate and Long-Life Anodes for Lithium-Ion Batteries Lichun Yang, a Xiang Li, a Yunpeng Ouyang, a Qingsheng Gao, b Liuzhang
More informationShaping Single-crystalline Trimetallic Pt Pd Rh Nanocrystals toward. High-efficiency C C Splitting of Ethanol in Conversion to CO 2
Supporting Information Shaping Single-crystalline Trimetallic Pt Pd Rh Nanocrystals toward High-efficiency C C Splitting of Ethanol in Conversion to CO 2 Wei Zhu,, Jun Ke,, Si-Bo Wang, Jie Ren, Hong-Hui
More informationSupporting Information
Electronic Supplementary Material (ESI) for CrystEngComm. This journal is The Royal Society of Chemistry 217 Supporting Information Catalyst preparation A certain of aqueous NiCl 2 6H 2 O (2 mm), H 2 PtCl
More informationSupporting Information for
Supporting Information for Iridium-tungsten Alloy Nanodendrites as ph-universal Water Splitting Electrocatalysts Fan Lv, Jianrui Feng, Kai Wang, Zhipeng Dou, Weiyu Zhang, Jinhui Zhou, Chao Yang, Mingchuan
More informationFacile Synthesis of Porous Pt-Cu Alloy with Enhanced Catalytic Activity
Facile Synthesis of Porous Pt-Cu Alloy with Enhanced Catalytic Activity Xiang Li, Jiao-Jiao Su, Ying-Xin Li, Shi-zhang Qiao, Hui Liu, Xi-Wen Du Institute of New-Energy Materials, School of Materials and
More informationSupplementary Figure 2. (a) XRD patterns of the MOF and the simulated Ni-MOF-74
Supplementary Figure 1. Low-magnification TEM image of Pt-Ni frame @ MOF. The scale bar is 200 nm. Supplementary Figure 2. (a) XRD patterns of the Pt-Ni @ MOF and the simulated Ni-MOF-74 pattern. (b) XRD
More informationDegradation of Bisphenol A by Peroxymonosulfate Catalytically Activated with. Gui-Xiang Huang, Chu-Ya Wang, Chuan-Wang Yang, Pu-Can Guo, Han-Qing Yu*
Supporting Information for Degradation of Bisphenol A by Peroxymonosulfate Catalytically Activated with Mn 1.8 Fe 1.2 O 4 Nanospheres: Synergism between Mn and Fe Gui-Xiang Huang, Chu-Ya Wang, Chuan-Wang
More informationJournal of Materials Chemistry A ELECTRONIC SUPPLEMENTARY INFORMATION (ESI )
Electronic Supplementary Material (ESI) for Journal of Materials Chemistry A. This journal is The Royal Society of Chemistry 218 Journal of Materials Chemistry A ELECTRONIC SUPPLEMENTARY INFORMATION (ESI
More informationState Key Laboratory of Chemical Resource Engineering, Beijing University of Chemical Technology, Beijing , China
Electronic Supplementary Material A Co-N/C hollow-sphere electrocatalyst derived from a metanilic CoAl layered double hydroxide for the oxygen reduction reaction, and its active sites in various ph media
More informationHigh Salt Removal Capacity of Metal-Organic Gel Derived. Porous Carbon for Capacitive Deionization
Supporting Information High Salt Removal Capacity of Metal-Organic Gel Derived Porous Carbon for Capacitive Deionization Zhuo Wang, Tingting Yan, Guorong Chen, Liyi Shi and Dengsong Zhang* Research Center
More informationHighly doped and exposed Cu(I)-N active sites within graphene towards. efficient oxygen reduction for zinc-air battery
Electronic Supplementary Material (ESI) for Energy & Environmental Science. This journal is The Royal Society of Chemistry 2016 Electronic Supplementary Information (ESI) for Energy & Environmental Science.
More informationAtomic H-Induced Mo 2 C Hybrid as an Active and Stable Bifunctional Electrocatalyst Supporting Information
Atomic H-Induced Mo 2 C Hybrid as an Active and Stable Bifunctional Electrocatalyst Supporting Information Xiujun Fan, * Yuanyue Liu, ς Zhiwei Peng, Zhenhua Zhang, # Haiqing Zhou, Xianming Zhang, Boris
More informationPt-Ni alloyed nanocrystals with controlled archtectures for enhanced. methanol oxidation
Supplementary Information Pt-Ni alloyed nanocrystals with controlled archtectures for enhanced methanol oxidation Xiao-Jing Liu, Chun-Hua Cui, Ming Gong, Hui-Hui Li, Yun Xue, Feng-Jia Fan and Shu-Hong
More informationThe design and construction of 3D rose petal-shape MoS 2. hierarchical nanostructures with structure-sensitive. properties
Electronic Supplementary Material (ESI) for Journal of Materials Chemistry A. This journal is The Royal Society of Chemistry 2014 The design and construction of 3D rose petal-shape MoS 2 hierarchical nanostructures
More informationElectronic Supplementary Information (ESI)
Electronic Supplementary Material (ESI) for Journal of Materials Chemistry A. This journal is The Royal Society of Chemistry 2016 Electronic Supplementary Information (ESI) Synthesis of 1T-MoSe 2 ultrathin
More informationSUPPLEMENTARY INFORMATION
Anisotropic phase segregation and migration of Pt in nanocrystals en route to nanoframe catalysts Zhiqiang Niu 1, Nigel Becknell 1, Yi Yu 1,2, Dohyung Kim 3, Chen Chen 1,4, Nikolay Kornienko 1, Gabor A.
More informationFormation of Hierarchical Structure Composed of (Co/Ni)Mn-LDH Nanosheets on MWCNT Backbones for Efficient Electrocatalytic Water Oxidation
Supporting Information Formation of Hierarchical Structure Composed of (Co/Ni)Mn-LDH Nanosheets on MWCNT Backbones for Efficient Electrocatalytic Water Oxidation Gan Jia, Yingfei Hu, Qinfeng Qian, Yingfang
More informationN-doped Carbon-Coated Cobalt Nanorod Arrays Supported on a Titanium. Mesh as Highly Active Electrocatalysts for Hydrogen Evolution Reaction
Electronic Supplementary Material (ESI) for Journal of Materials Chemistry A. This journal is The Royal Society of Chemistry 2014 Electronic Supplementary Information N-doped Carbon-Coated Cobalt Nanorod
More informationSupporting Information. MOF Templated Nitrogen Doped Carbon Stabilized Pt-Co Bimetallic
Supporting Information MOF Templated Nitrogen Doped Carbon Stabilized Pt-Co Bimetallic Nanoparticles: Low Pt Contents and Robust Activity towards Electrocatalytic Oxygen Reduction Reaction Li-Li Ling,
More informationPt-Cu Hierarchical Quasi Great Dodecahedrons with Abundant
Electronic Supplementary Material Material (ESI) for (ESI) Chemical for ChemComm. Science. This journal is is The The Royal Royal Society Society of Chemistry of Chemistry 2017 2017 Supporting Information
More informationSupporting Information for
Supporting Information for Multilayer CuO@NiO Hollow Spheres: Microwave-Assisted Metal-Organic-Framework Derivation and Highly Reversible Structure-Matched Stepwise Lithium Storage Wenxiang Guo, Weiwei
More information[Supplementary Information] One-Pot Synthesis and Electrocatalytic Activity of Octapodal Au-Pd Nanoparticles
[Supplementary Information] One-Pot Synthesis and Electrocatalytic Activity of Octapodal Au-Pd Nanoparticles Jong Wook Hong, Young Wook Lee, Minjung Kim, Shin Wook Kang, and Sang Woo Han * Department of
More informationSupporting Information
Electronic Supplementary Material (ESI) for Chemical Communications. This journal is The Royal Society of Chemistry 2016 Supporting Information Single-crystalline Pd square nanoplates enclosed by {100}
More informationSize-dependent catalytic activity of monodispersed nickel nanoparticles for the hydrolytic dehydrogenation of ammonia borane
Size-dependent catalytic activity of monodispersed nickel nanoparticles for the hydrolytic dehydrogenation of ammonia borane Kun Guo a,b, Hailong Li c and Zhixin Yu a,b * a Department of Petroleum Engineering,
More informationElectronic Supplementary Information:
Electronic Supplementary Material (ESI) for Journal of Materials Chemistry A. This journal is The Royal Society of Chemistry 2017 Electronic Supplementary Information: Platinum-Nickel Nanowire Catalysts
More informationHoneycomb-like Interconnected Network of Nickel Phosphide Hetero-nanoparticles
Supporting Information Honeycomb-like Interconnected Network of Nickel Phosphide Hetero-nanoparticles with Superior Electrochemical Performance for Supercapacitors Shude Liu a, Kalimuthu Vijaya Sankar
More informationDominating Role of Aligned MoS 2 /Ni 3 S 2. Nanoarrays Supported on 3D Ni Foam with. Hydrophilic Interface for Highly Enhanced
Supporting Information Dominating Role of Aligned MoS 2 /Ni 3 S 2 Nanoarrays Supported on 3D Ni Foam with Hydrophilic Interface for Highly Enhanced Hydrogen Evolution Reaction Jiamu Cao a, Jing Zhou a,
More informationElectronic Supplementary Information
Electronic Supplementary Material (ESI) for ChemComm. This journal is The Royal Society of Chemistry 2018 Electronic Supplementary Information One-Dimensional MoO2-Co2Mo3O8@C Nanorods: A Novel and High
More informationLotus root-like porous carbon nanofiber anchored with CoP nanoparticles as all-ph hydrogen evolution electrocatalysts
Electronic Supplementary Material Lotus root-like porous carbon nanofiber anchored with CoP nanoparticles as all-ph hydrogen evolution electrocatalysts Hengyi Lu 1, Wei Fan 2 ( ), Yunpeng Huang 1, and
More informationSupporting Information. Surface-Engineered PtNi-O Nanostructure with Record-High Performance for Electrocatalytic Hydrogen Evolution Reaction
Supporting Information Surface-Engineered PtNi-O Nanostructure with Record-High Performance for Electrocatalytic Hydrogen Evolution Reaction Zipeng Zhao, # Haotian Liu, # Wenpei Gao, Wang Xue, Zeyan Liu,
More informationSUPPLEMENTARY INFORMATION
DOI: 1.138/NMAT3668 Compositional segregation in shaped Pt alloy nanoparticles and their structural behavior during electrocatalysis Chunhua Cui 1, Lin Gan 1, Marc Heggen 2, Stefan Rudi 1 and Peter Strasser
More informationSupporting Information
Supporting Information Simultaneous Reduction-Etching Route to Pt/ZnSnO 3 Hollow Polyhedral Architectures for Methanol Electrooxidation in Alkaline Media with Superior Performance Han Jiang, Baoyou Geng
More informationElectronic Supplementary Information
Electronic Supplementary Material (ESI) for Journal of Materials Chemistry A. This journal is The Royal Society of Chemistry 2014 Electronic Supplementary Information MoS 2 nanosheet/mo 2 C-embedded N-doped
More informationElectronic supplementary information for Chemical Communications
Electronic Supplementary Material (ESI) for ChemComm. This journal is The Royal Society of Chemistry 2018 Electronic supplementary information for Chemical Communications Synthesis of hierarchical Pd 4
More informationSupplementary Information:
Supplementary Information: One-Step and Rapid Synthesis of Clean and Monodisperse Dendritic Pt Nanoparticles and Their High Performance Toward Methanol Oxidation and p-nitrophenol Reduction Jun Wang, Xin-Bo
More informationEngineering of Hollow Core-Shell Interlinked Carbon Spheres for Highly Stable Lithium-Sulfur Batteries
SUPPLEMENTARY INFORMATION Engineering of Hollow Core-Shell Interlinked Carbon Spheres for Highly Stable Lithium-Sulfur Batteries Qiang Sun, Bin He, Xiang-Qian Zhang, and An-Hui Lu* State Key Laboratory
More informationThickness-tunable Core-shell Nanoparticles Encapsulated in Sandwich-like Carbon
Electronic Supplementary Material (ESI) for Journal of Materials Chemistry A. This journal is The Royal Society of Chemistry 2018 Supporting Information: Thickness-tunable Core-shell Co@Pt Nanoparticles
More informationSUPPLEMENTARY INFORMATION
Structurally ordered intermetallic platinum cobalt core shell nanoparticles with enhanced activity and stability as oxygen reduction electrocatalysts Deli Wang, Huolin L. Xin, Robert Hovden, Hongsen Wang,
More informationBoosting the hydrogen evolution performance of ruthenium clusters. through synergistic coupling with cobalt phosphide
Electronic Supplementary Material (ESI) for Energy & Environmental Science. This journal is The Royal Society of Chemistry 2018 Electronic Supplementary Information for Boosting the hydrogen evolution
More informationNi-Mo Nanocatalysts on N-Doped Graphite Nanotubes for Highly Efficient Electrochemical Hydrogen Evolution in Acid
Supporting Information Ni-Mo Nanocatalysts on N-Doped Graphite Nanotubes for Highly Efficient Electrochemical Hydrogen Evolution in Acid Teng Wang, Yanru Guo, Zhenxing Zhou, Xinghua Chang, Jie Zheng *,
More informationSupporting Information
Electronic Supplementary Material (ESI) for Journal of Materials Chemistry A. This journal is The Royal Society of Chemistry 2018 Supporting Information Si/SiO x Hollow Nanospheres/Nitrogen-Doped Carbon
More informationHydrogenated CoO x Ni(OH) 2 nanosheet core shell nanostructures for high-performance asymmetric supercapacitors
. Electronic Supplementary Material (ESI) for Nanoscale Electronic Supplementary Information (ESI) Hydrogenated CoO x nanowire @ Ni(OH) 2 nanosheet core shell nanostructures for high-performance asymmetric
More informationSupplementary Figure 1. HRTEM images of PtNi / Ni-B composite exposed to electron beam. The. scale bars are 5 nm.
Supplementary Figure 1. HRTEM images of PtNi / Ni-B composite exposed to electron beam. The scale bars are 5 nm. S1 Supplementary Figure 2. TEM image of PtNi/Ni-B composite obtained under N 2 protection.
More informationunique electronic structure for efficient hydrogen evolution
Electronic Supplementary Material (ESI) for Journal of Materials Chemistry A. This journal is The Royal Society of Chemistry 2017 Supplementary Information Atom-scale dispersed palladium in conductive
More informationSupporting Information. Cobalt Molybdenum Oxide Derived High-Performance Electrocatalyst
Supporting Information Cobalt Molybdenum Oxide Derived High-Performance Electrocatalyst for the Hydrogen Evolution Reaction Mingjie Zang, [a] Ning Xu, [a] Guoxuan Cao, [a] Zhengjun Chen, [a] Jie Cui, [b]
More informationUrchin-like Ni-P microstructures: A facile synthesis, properties. and application in the fast removal of heavy-metal ions
SUPPORTING INFORMATION Urchin-like Ni-P microstructures: A facile synthesis, properties and application in the fast removal of heavy-metal ions Yonghong Ni *a, Kai Mi a, Chao Cheng a, Jun Xia a, Xiang
More informationSupporting Information. Phenolic/resin assisted MOFs derived hierarchical Co/N-doping carbon
Electronic Supplementary Material (ESI) for Journal of Materials Chemistry A. This journal is The Royal Society of Chemistry 2018 Electronic Supplementary Material (ESI) for Journal of Materials Chemistry
More informationOxygen Vacancy Induced Bismuth Oxyiodide with Remarkably. Increased Visible-light Absorption and Superior Photocatalytic.
Oxygen Vacancy Induced Bismuth Oxyiodide with Remarkably Increased Visible-light Absorption and Superior Photocatalytic Performance Yongchao Huang, Haibo Li, Muhammad-Sadeeq Balogun, Wenyue Liu, Yexiang
More informationCarbon-encapsulated heazlewoodite nanoparticles as highly efficient and durable electrocatalysts for oxygen evolution reactions
Electronic Supplementary Material Carbon-encapsulated heazlewoodite nanoparticles as highly efficient and durable electrocatalysts for oxygen evolution reactions Mohammad Al-Mamun 1, Huajie Yin 1, Porun
More informationOne-Step Facile Synthesis of Cobalt Phosphides for Hydrogen Evolution Reaction Catalyst in Acidic and Alkaline Medium
Supporting Information One-Step Facile Synthesis of Cobalt Phosphides for Hydrogen Evolution Reaction Catalyst in Acidic and Alkaline Medium Afriyanti Sumboja, a Tao An, a Hai Yang Goh, b Mechthild Lübke,
More informationElectronic Supplementary Information
Electronic Supplementary Material (ESI) for Nanoscale. This journal is The Royal Society of Chemistry 2014 Electronic Supplementary Information One-pot synthesis of ultralong coaxial Au@Pt nanocables with
More informationElectronic Supplementary Information
Electronic Supplementary Material (ESI) for Journal of Materials Chemistry A. This journal is The Royal Society of Chemistry 2016 Electronic Supplementary Information Mesoporous C-coated SnO x nanosheets
More informationElectronic Supplementary Information
Electronic Supplementary Material (ESI) for Journal of Materials Chemistry A. This journal is The Royal Society of Chemistry 2017 Electronic Supplementary Information Two-dimensional CoNi nanoparticles@s,n-doped
More informationSupporting information. Stability Issues in Pd-based Catalysts: The Role of Surface Pt in Improving the Stability
Supporting information Stability Issues in Pd-based Catalysts: The Role of Surface Pt in Improving the Stability and Oxygen Reduction Reaction (ORR) Activity R. K. Singh, R. Rahul, M. Neergat 1 Department
More informationBimetallic Thin Film NiCo-NiCoO as Superior Bifunctional Electro- catalyst for Overall Water Splitting in Alkaline Media
Electronic Supplementary Material (ESI) for Journal of Materials Chemistry A. This journal is The Royal Society of Chemistry 2017 Supportting Information for Bimetallic Thin Film NiCo-NiCoO 2 @NC as Superior
More informationDepartment of Bioengineering, 815C Benedum Hall, 3700 O Hara Street, Pittsburgh, PA
1 Supplementary information 2 3 Noble metal-free bifunctional oxygen evolution and oxygen reduction acidic media electro- catalysts 4 5 6 Prasad Prakash Patel 1, Moni Kanchan Datta 2,3, Oleg I. Velikokhatnyi
More informationSimple synthesis of urchin-like Pt-Ni bimetallic nanostructures as enhanced electrocatalysts for oxygen reduction reaction
Electronic Supplementary Material (ESI) for ChemComm. This journal is The Royal Society of Chemistry 2015 Electronic Supplementary Information Simple synthesis of urchin-like Pt- bimetallic nanostructures
More informationSupplementary Figure S1: Particle size distributions of the Pt ML /Pd 9 Au 1 /C
a 2 15 before cycle test mean particle size: 3.8 ± 1.2 nm b 2 15 after.6v - 1.V 1k cycle test mean particle size: 4.1 ± 1.5 nm Number 1 total number: 558 Number 1 total number: 554 5 5 1 2 3 4 5 6 7 8
More informationSupporting information
Supporting information Manipulating the Concavity of Rhodium Nanocubes Enclosed with High-index Facets via Site-selective Etching Yumin Chen, Qing-Song Chen, Si-Yan Peng, Zhi-Qiao Wang, Gang Lu, and Guo-Cong
More informationElectronic Supplementary Information. Three-Dimensional Carbon Foam/N-doped 2. Hybrid Nanostructures as Effective Electrocatalysts for
Electronic Supplementary Material (ESI) for Journal of Materials Chemistry A. This journal is The Royal Society of Chemistry 2016 Electronic Supplementary Information Three-Dimensional Carbon Foam/N-doped
More informationSupporting information Synthesis of ultrathin wrinkle-free PdCu alloy. nanosheets for d-band electrons modulating
Electronic Supplementary Material (ESI) for Journal of Materials Chemistry A. This journal is The Royal Society of Chemistry 2018 Supporting information Synthesis of ultrathin wrinkle-free PdCu alloy nanosheets
More informationSupporting Information
Supporting Information Heterostructured arrays of Ni x P/S/Se nanosheets on Co x P/S/Se nanowires for efficient hydrogen evolution Weiqiang Tang, 1 Jianying Wang, 1 Lixia Guo, 1 Xue Teng, 1 Thomas J. Meyer,
More informationbifunctional electrocatalyst for overall water splitting
Electronic Supplementary Material (ESI) for Journal of Materials Chemistry A. This journal is The Royal Society of Chemistry 2017 Hierarchical Ni/NiTiO 3 derived from NiTi LDHs: a bifunctional electrocatalyst
More informationSupporting Information. Engineering Two-Dimensional Mass-Transport Channels
Supporting Information Engineering Two-Dimensional Mass-Transport Channels of MoS 2 Nanocatalyst towards Improved Hydrogen Evolution Performance Ge Wang a, Jingying Tao a, Yijie Zhang a, Shengping Wang
More informationCloth for High-Efficient Electrocatalytic Urea Oxidation
Electronic Supplementary Material (ESI) for Journal of Materials Chemistry A. This journal is The Royal Society of Chemistry 2018 Supporting Information In-situ Growth of Single-Layered α-ni(oh) 2 Nanosheets
More informationNanoporous metals by dealloying multicomponent metallic glasses. Chen * Institute for Materials Research, Tohoku University, Sendai , Japan
Supporting information for: Nanoporous metals by dealloying multicomponent metallic glasses Jinshan Yu, Yi Ding, Caixia Xu, Akihisa Inoue, Toshio Sakurai and Mingwei Chen * Institute for Materials Research,
More informationSupporting Information
Supporting Information Surfactant-Free Assembly of Mesoporous Carbon Hollow Spheres with Large Tunable Pore Sizes Hongwei Zhang, Owen Noonan, Xiaodan Huang, Yannan Yang, Chun Xu, Liang Zhou, and Chengzhong
More information