Exchange Coupled Composite Media for Perpendicular Magnetic Recording
|
|
- Denis Nelson
- 6 years ago
- Views:
Transcription
1 BB-01 1 Exchange Coupled Composite Media for Perpendicular Magnetic Recording R. H. Victora, Fellow, IEEE, X. Shen Abstract Exchange coupled composite (ECC) media has been shown to possess several major advantages relative to conventional perpendicular media, including a reduction in the switching field of approximately a factor two for the same thermal stability and greater insensitivity to easy axis distribution. In this paper, full magnetostatic interactions are included: this allows comparison between the behavior of multigrain thin films and that of isolated grains as presented earlier. Significant results include hysteresis loops for thin films under various conditions including inadequate and excessive intra granular exchange between the hard and soft materials. An important distinction is made between the coercivity and remnant coercivity as a function of angle between applied field and easy axis. A perpendicular magnetic recording head is used to compare the shape of effective fields for ECC and conventional perpendicular media. Written transitions in the ECC media appear to be similar to those written in perpendicular media at comparable densities. Index Terms Exchange coupled composite media, Perpendicular magnetic recording, Thermal fluctuations. P I. INTRODUCTION ERPENDICULAR magnetic recording has multiple advantages [1] for high-density magnetic recording and was proposed more than 20 years ago as the successor to longitudinal magnetic recording for the next generation of hard disk [2]. Recently, perpendicular recording products with densities over 130 Gbits/in 2 have been announced [3]. However, to greatly increase this recording density is difficult, mostly owing to limitations of the perpendicular recording media itself. One important factor that limits the recording density of perpendicular media is the low writability that reflects the paradox between its thermal stability and switching capability. To increase recording density, grain volumes are reduced and the anisotropy of the media must be increased to maintain thermal stability. This increases the anisotropy field. Thus, extremely high density leads to a very high switching field that cannot be reached by current perpendicular writing heads. To address this problem, we must either increase the head field or decrease the switching field of Manuscript received February 7, This work was supported in part by the National Science Foundation under Grant ECS and in part by the INSIC EHDR program. The authors are with the Center of Micromagnetics and Information Technology (MINT), Electrical and Computer Engineering Department, University of Minnesota, Minneapolis, MN 55455, USA ( victora@ece.umn.edu). the media. Since head field increases are limited by the highest saturation magnetization of head material that can be realized, the other way, decreasing switching field while maintaining the thermal stability of the media seems more applicable. There is a ratio between the thermal barrier of the media and its switching field, which can be defined as! = 2 " E /( H # M # V ) [4]. Here ΔE is the thermal barrier and s s H s, M s, V are switching field, saturation magnetization and volume, respectively. Increasing this ratio can effectively solve the paradox between thermal stability and writability. For example, perpendicular media has a ratio of one and 45 tilted media [5][6] has a ratio of two, which means that at the same thermal stability, 45 tilted media will have half the switching field of perpendicular media. Previously, we have introduced [4] the idea of exchange coupled composite (ECC) media. This media consists of magnetically isolated grains each consisting of two parts: a magnetically hard part with perpendicular anisotropy and a magnetically soft part where the anisotropy can point in any direction provided it is small. For this ECC media, this ratio ξ can also approach two. Taking into account that the fabrication of ECC media is much easier than tilted media [7], it is quite promising for ultra high-density recording. In this paper, ECC media is studied by means of simulating its hysteresis loop and writing behavior under a special perpendicular magnetic recording head [1]. Effects of inter granular magnetostatic interaction and intra- and inter granular exchange coupling are illustrated by hysteresis loops. Angular dependence of coercivity and remnant coercivity are shown. Transition shapes are studied by applying a perpendicular magnetic recording head with a 50 nm thick soft under layer (SUL). II. SIMULATION MODEL We generate a piece of media with 500 composite grains. Voroni cells are used to represent grains within our micromagnetic model. This introduces difficulty in doing surface integrals for calculating the magnetostatic interaction energy, but may give results closer to reality than widely used rectangular grain models. The calculation tricks for Voroni cells arranged in a single layer can be found in [8][9]. For the present calculation, the grain model contains two parts referring to magnetically hard and soft regions of ECC media. The top part sits exactly on the bottom one with the same Voroni shape, but different thickness. Although there is an
2 BB-01 2 inter-layer (for example PdSi) between the two parts that controls the exchange coupling strength, in our micromagnetic simulation model, the two parts are adjacent to each other: this slightly exaggerates the magnetostatic interaction. The dimension of the media is 125 nm 100 nm. The mean diameter of the media is set to 5 nm to meet the requirement for 1 Tbits/in 2 recording density. The distribution of the diameter is approximately log normal with a 20% standard deviation. The thickness of the top region (magnetically hard region), t hard is 5 nm and that of the bottom region (magnetically soft region), t soft is 10 nm. The saturation magnetization of the top region, M hard is 150 emu/cm 3 and that of the soft region, M soft is 750 emu/cm 3. Thus, the volume and magnetization ratio of the two regions are ½ and 1/5, respectively, which may be the optimal choice [4]. The anisotropy of the hard region, Ku hard equals erg/cm 3 and for soft region, Ku soft equals 100 erg/cm 3. The easy axes are both in the perpendicular direction. The variation of anisotropy field is not included in our simulation. The exchange coupling constant between the hard and soft region Jex/V is erg/cm 3 [4]. The strength of inter granular exchange coupling is defined in (1) and varied from 0 to erg/cm 3. E exch V!! lij = " Jex( M i# M j ) (1) l norm Here l ij is the length of the neighboring edge of grain i and j and l norm is the average length. III. EFFECT OF MAGNETOSTATIC INTERACTION The effect of the magnetostatic interaction of ECC media can be studied by comparing the hysteresis loops of a single grain and the 500 grain media. The magnetostatic fields are calculated using the definition of H=-Interaction Energy/(Element Volume Saturation Magnetization). In the calculation, the magnetically hard and soft regions of one grain can be considered as two different grains to give the magnetostatic field between the hard and soft layers. To calculate the interaction energy between grains, integration of surface charges is implemented as shown in (2). Here, E(I,J) denotes the interaction energy between grain I and grain J. The various surfaces of the two grains are denoted m and n. The integration is implemented over all the surfaces that are then summed to give the total interaction energy. The charge densities of surface i and j are σ i and σ j. The integration variables u, u, v, v are local coordinates on surface i and j. While calculating the distance between magnetic charges, these coordinates must be transformed to global coordinates, x, x, y, y and z, z. E( I, J ) = n m ' '! i! jdudu dvdv ##$$$$ (2) ' 2 ' 2 ' 2 i= 1 j= 1 i j ( x " x ) + ( y " y ) + ( z " z ) The difficulty here is that the top and bottom surfaces of grains have voroni shapes, as shown in Figure 2. How to integrate these irregular shapes becomes the greatest problem that needs to be addressed in the calculation. The solution we use is first dividing these irregular shapes into several quadrilaterals or triangles and then mapping the quadrilaterals and triangles to squares [8][9]. Fig. 1. Schematic view of the perpendicular magnetic recording head The perpendicular recording head contains a tip, 150 nm in length, 50 nm in width and 250 nm in height and a collar surrounding the top part of the tip. Figure 1 gives a schematic view of the head. Detailed parameters of the head and head field distribution can be found in [1]. The SUL consists of two layers of 25 nm cubic soft cell arrays with saturation magnetization the same as that of the head. The dimension of the SUL is 500 nm 500 nm. When simulating hysteresis loops, no SUL is used. Fig. 2. Illustration of the surface integration between two voroni shaped grains A trick is used when calculating the magnetostatic interaction energy between the top and bottom regions of the same grain. Since these two regions are adjacent to each other, a singularity problem may occur. In other words, since the distance between the bottom surface of the top region and the top surface of the bottom region vanishes, the magnetostatic interaction energy relative to this pair of surfaces, according to (2), must be infinity.
3 BB-01 3 This singularity problem is addressed by defining the magnetostatic interaction energy between the top and soft regions of one grain in the way depicted in (3). Here, I and J denotes the top and bottom regions. E(I,J) is the interaction energy between them. E(I,I) and E(J,J) are self magnetostatic energies of region I and J, respectively. If we consider the grain that contains these two regions, I and J, as a single grain and denote it as grain K, then the difference between E(K,K) and the sum of E(I,I) and E(J,J) is just the interaction energy between I and J. E( I, J ) = E( K, K)! E( I, I)! E( J, J ) (3) After the magnetostatic interaction energy is calculated successfully and divided by the element volume and saturation magnetization, the magnetostatic field is given. We then use standard rotation matrices to transform it from the local (grain) coordinates to the common film axes. in Figure 3. During this step, the magnetizations of hard regions also rotate, but to a small angle compared with that of the soft regions. It is also worthwhile to notice that, during this step, all the soft regions and the hard regions rotate coherently. No grain switches in this step. This coherent rotation can be seen in Figure 4 that shows the standard deviation of normalized magnetizations of all the soft and hard regions of the 500 grains. In the range of 0 to 12 koe, the standard deviation is very small revealing that all the magnetizations are almost in the same direction. The benefit of this step is that, owing to the rotation of the magnetizations of the soft region, the effective field at the hard region of the media, comprising both the applied field and the exchange field generated by the soft region and others such as magnetostatic fields, is at an angle to the magnetization of the hard region, making it much easier to switch compared to a perfectly aligned field. After this coherent rotation step, the applied field continues to increase and grains start to switch, which corresponds to the second step of the hysteresis loop. Fig. 3. Comparison of hysteresis loops of single grain and 500 grain media. The dashed loop is loop for single grain and the solid one is for 500 grain media. The hysteresis loop of the 500 grain media is shown in figure 3 with a comparison to that of a single grain. There is a good agreement between the coercivities of the two hysteresis loops. However, the loop for 500 grains is tilted owing to the effect of magnetostatic interactions. For conventional perpendicular media, the idealized tangent of the tilted loop, α, should be approximately one, indicating that the maximum magnetostatic field is 4π M s. However, for the ECC media, the loop has two regions that are tilted at different angles. However, if we draw a line to connect the nucleation point and the closure point, the tangent of that line can be seen as the effective α of ECC media, which is approximately one. The switching of the grains complies with a two-step process that is described in [4]. This can successfully explain the two different regions of the hysteresis loop. While the applied field is increasing from 0 to about 12 koe in the negative direction, the magnetizations of the soft regions rotate leading to the deduction of the average magnetization from 550 emu/cm 3 to approximately 200 emu/cm 3, as shown Fig. 4. Standard deviation of the granular magnetization evaluated over a 500 grain specimen. The solid and dotted curves are for the soft and hard regions, respectively. IV. EFFECT OF INTRA GRANULAR EXCHANGE COUPLING The switching field of ECC media depends on the exchange coupling strength between the soft and hard regions. With zero exchange coupling, the soft region has no effect on the hard region, and the switching field will be as high as that of the hard material. While increasing the exchange coupling strength, because of the effect of the soft region, the switching field of the media decreases to a minimum. Further increasing the exchange coupling will reduce the benefit of ECC media because the magnetization of the soft region is tightly bound to that of the hard region, thus losing its freedom to rotate before switching. The switching field of the media will increase. Figure 5 shows the hysteresis loops of ECC media when exchange coupling strength between the soft and hard regions, Jex/V, equals 0, and erg/cm 3. For the zero exchange coupling case, the loop shows clearly the separated switching of the hard and soft regions. The
4 BB-01 4 coercivity of the soft and hard regions are at 100 Oe and Oe, respectively, just being equal to the anisotropy fields of the two regions. When the exchange coupling strength is erg/cm 3 which is the proper coupling case, the coercivity is reduced from Oe to 12.8 koe. Although the proper coupling case and the zero coupling case both have two-step hysteresis loops, the switching processes are totally different in that the switching of the hard and soft regions for the zero coupling case are separated but for the proper coupling case, these two regions switch together. When the exchange coupling strength is increased to erg/cm 3, the coercivity is increased. the inter granular exchange coupling constant equals 0, 0.5, 1.0 and 1.5 times (M 1 M 2 ) where M 1 and M 2 are saturation magnetizations of the soft and hard region, respectively. From the figure, we can see that inter granular exchange coupling of ECC media does increase the steepness of the loop of the second step of switching but has little effect on the first step which is dominated by the rotation of magnetizations of the soft region. VI. ANGULAR DEPENDENCE OF COERCIVITY One of the most serious problems of conventional perpendicular media is its sensitivity to easy axis distribution. According to the Stoner-Wolfarth model, when the applied field is almost aligned with the easy axis of the media, a small variation of the angle between the easy axis and the field will cause a great change in switching field of the media, which contributes greatly to recording noise. However, if the applied field is at about a 45 angle to the easy axis of the media, the switching field is quite independent to variation of that angle. This is one reason why 45 tilted media is considered advantageous to conventional perpendicular media in highdensity recording. Fig. 5. Comparison of hysteresis loops at different intra granular exchange coupling strength. In the top figure, solid line and dashed line represent loops for exchange coupling strength at and erg/cm 3, respectively. The bottom figure gives loop for the zero exchange coupling case Fig. 6. Comparison of hysteresis loops with different inter granular exchange coupling of ECC media V. EFFECT OF INTER GRANULAR EXCHANGE COUPLING Exchange coupling between neighboring grains can affect the nucleation field and the steepness of the hysteresis loop for conventional perpendicular media. The effects of inter granular exchange coupling on ECC media is also studied. Figure 6 shows several hysteresis loops of ECC media when Fig. 7. Hysteresis loops of ECC media when applied field is tilted at 0, 30, 45 and 85. In the case of ECC media, the angular dependence of switching field is also insensitive to the variation of angle between the easy axis of the hard region and the applied field. The switching field versus applied field angle is studied in [4] showing that when the angle between applied field and easy axis is less than 10, the switching field of ECC media is almost constant. This insensitivity can be explained by the mechanism that switches ECC media when it is properly coupled. Although the applied perpendicular field is almost aligned with the easy axis of the hard region of ECC media, the effective field that switches the media is not the applied field, but a combination of the applied field and the exchange field from the soft region. This effective field is tilted at an angle, near 45, to the easy axis. Thus, ECC media has a similar angular dependence to tilted media.
5 BB-01 5 Fig. 8. Comparison of switching fields, coercivity and remnant coercivity of single grain and 500 grains media at tilted field angles. Figure 7 shows hysteresis loops of ECC media when the angle between applied field and easy axis of hard region is 0, 30, 45 and 85. Along with the increase of tilted angle of the field, the coercivity of the media reduces and the remnant coercivity increases. Figure 8 shows a comparison of coercivity and remnant coercivity of ECC media at different tilted field angles. The dashed and dotted curves are switching fields and coercivity of a single grain, respectively. The filled and open circles are remnant coercivity and coercivity, respectively, of 500 grain media at several tilted field angles. The difficulty in switching of ECC media at a large field angle is quite promising for addressing the problem of adjacent track erasure. For conventional perpendicular media, although the head field at the center is larger than that at the edge, grains right under the center of the head usually resist switching and grains at the edge of neighboring tracks are likely to switch unintentionally. This is because the switching of grains not only depends on the amplitude of the field, but also the angle at which the field tilts. To consider the effect of field angle, we can define the effective field, which is generated by normalizing those real head fields as if they are perpendicular to the media so that the amplitude of the effective field is the only index to evaluate the switching of the grain. Figure 9 and 10 show a comparison of effective field (normalized to its maximum value) for conventional perpendicular media and ECC media based on the perpendicular recording head described in section two. It can be seen that, at the edge of the adjacent track (40nm in cross track direction), the effective field for conventional perpendicular media is about 0.68 while for ECC media, it is reduced to The field available to write a 40 nm track is 0.88 and 0.89 in the two cases. This means that the effective write field has only declined by 22% (=1-0.68/0.88) for conventional perpendicular recording, but 40% for recording on an ECC media. This should translate into a significant reduction in adjacent track erasure that is known to be a major problem for terabit/inch 2 recording. [10] Fig. 9. Effective field of conventional perpendicular media Fig. 10. Effective field of ECC media Fig. 11. Transition shapes of ECC media VII. TRANSITION Several transitions are written on the 500 grain media using the head mentioned above. For conventional perpendicular media, transitions have curved shapes. The transitions written on ECC media appear to be similar to those written on
6 BB-01 6 conventional perpendicular media. Figure 11 shows an example of 5 transitions written on DC erased media. VIII. CONCLUSION Exchange coupled composite media has been studied using a newly developed simulation code that allows for two layers of granular media based on Voronoi cells. Three important points are made. First, the apparently small nucleation field caused by the magnetostatic interaction between grains (film demagnetization) is immaterial because it only represents the magnetically soft elements of each grain rotating in unison with the soft elements of other grains. Actual switching does not occur until much larger fields comparable to the isolated grain case. Second, it was shown that, as the angle between the applied field and the perpendicular axis increases, there is an increased divergence between the remnant coercivity (indicative of switching) and the coercivity. This is important for experimentally assessing the properties of proposed media. Finally, the write field profile associated with ECC media is narrower in the cross track direction than that associated with conventional perpendicular media. This may have important implications for adjacent track erasure, a problem of great current importance [5][10] ACKNOWLEDGMENT The authors would like to thank the Minnesota Super Computing Institute for computing time. REFERENCES [1] R. H. Victora, J. Xue, and M. Patwari, Areal density limits for perpendicular magnetic recording, IEEE. Trans. Magn., vol. 38, pp , [2] S. Iwasaki, Perpendicular magnetic recording evolution and future, IEEE. Trans. Magn., vol. 20, pp , 1984 [3] Dec. 14, 2004, Toshiba leads industry in bringing perpendicular data recording to HDD sets new record for storage capacity with tow new HDDs, Available: downloads/pressrelease/hdd_pressrelease_v4final.pdf [4] R. H. Victora, X. Shen, Composite media for perpendicular magnetic recording, will be published on IEEE. Trans. Magn., vol. 41, 2005 [5] H. N. Bertram and K. Z. Gao, Magnetic recording configuration for densities beyond 1 Tb/in 2 and data rates beyond 1 Gb/s, IEEE Trans. Magn., vol. 38, no. 5, pp , 2002 [6] J. P. Wang, Y. Y. Zou, C. H. Hee, T. C. Chong, and Y. F. Zheng, Approaches to tilted magnetic recording for extremely high areal density, IEEE Trans. Magn., vol. 39, no. 4, pp , 2003 [7] W. Shen, J. Bai, R. H. Victora, J. H. Judy and J. Wang, Composite media for perpendicular magnetic recording using [Co/PdSi]n hard layer and Fe-Si-O soft layer, accepted by J. Appl. Phys., vol. 97, 2005 [8] J. Xue, Micromagnetic simulation of hysteresis characteristics for thin magnetic films, Ph.D. thesis, Dept. Elect. Eng., University of Minnesota, Minneapolis, MN, 2004 [9] R. H. Victora and Mujahid Khan, Micromagnetic model of perpendicular head and double-layer media for 100 Gb/in 2, IEEE Trans. Magn., vol. 38, pp , 2002 [10] J. A. Bain, M. L. Williams and R. H. Victora, Analysis of transition shape and adjacent track aging for 1 Tb/in 2 write head designs, IEEE. Trans. Magn., vol. 40, pp , 2004 TMAG
7 BB-01 7
ECC Media Technology. 1. Introduction. 2. ECC Media. Shunji Takenoiri TuQiang Li Yoshiyuki Kuboki
ECC Media Technology Shunji Takenoiri TuQiang Li Yoshiyuki Kuboki 1. Introduction Two years have already elapsed since Fuji Electric began mass-producing perpendicular magnetic recording media, and now
More informationMicromagnetic Modeling of Soft Underlayer Magnetization Processes and Fields in Perpendicular Magnetic Recording
1670 IEEE TRANSACTIONS ON MAGNETICS, VOL. 38, NO. 4, JULY 2002 Micromagnetic Modeling of Soft Underlayer Magnetization Processes and Fields in Perpendicular Magnetic Recording Manfred E. Schabes, Byron
More informationAnisotropy Distributions in Patterned Magnetic Media
MINT Review & Workshop 24-25 Oct. 2006 Anisotropy Distributions in Patterned Magnetic Media Tom Thomson Hitachi San Jose Research Center Page 1 Acknowledgements Manfred Albrecht (Post-doc) Tom Albrecht
More informationThis is a repository copy of Parametric optimization for terabit perpendicular recording.
This is a repository copy of Parametric optimization for terabit perpendicular recording. White Rose Research Online URL for this paper: http://eprints.whiterose.ac.uk/1836/ Article: Miles, J.J., McKirdy,
More informationTHE continuous increase in areal density and data rate in
IEEE TRANSACTIONS ON MAGNETICS, VOL. 41, NO. 10, OCTOBER 2005 2839 Micromagnetic Simulation of Head-Field and Write Bubble Dynamics in Perpendicular Recording Werner Scholz, Member, IEEE, and Sharat Batra,
More informationSimulation of Hysteresis In Permalloy Films
GQ-02 1 Simulation of Hysteresis In Permalloy Films Andrew Kunz and Chuck Campbell Magnetic Microscopy Center University of Minnesota Minneapolis, MN Introduction 2 Looking for the classical behavior of
More information01 Development of Hard Disk Drives
01 Development of Hard Disk Drives Design Write / read operation MR / GMR heads Longitudinal / perpendicular recording Recording media Bit size Areal density Tri-lemma 11:00 10/February/2016 Wednesday
More informationMICROMAGNETICS OF EXCHANGE SPRING MEDIA: OPTIMIZATION AND LIMITS
1/49 MICROMAGNETICS OF EXCHANGE SPRING MEDIA: OPTIMIZATION AND LIMITS Dieter Suess dieter.suess@tuwien.ac.at Institut of Solid State Physics, Vienna University of Technology, Austria (submitted to Journal
More informationAMETHOD of reconstructing the in-plane component of
2324 IEEE TRANSACTIONS ON MAGNETICS, VOL. 34, NO. 4, JULY 1998 Magnetization Reconstruction from Differential Phase Contrast Lorentz Microscopy and Magnetic Force Microscopy M. Wdowin, J. J. Miles, B.
More informationAntiferromagnetically coupled capped bit patterned media: Writability, switching field distributions, and readback regulation
Antiferromagnetically coupled capped bit patterned media: Writability, switching field distributions, and readback regulation Marko V. Lubarda, 1 Shaojing Li, 1 Boris Livshitz, 2 Eric E. Fullerton, 1 Vitaliy
More informationMicrowave Assisted Magnetic Recording
Microwave Assisted Magnetic Recording, Xiaochun Zhu, and Yuhui Tang Data Storage Systems Center Dept. of Electrical and Computer Engineering Carnegie Mellon University IDEMA Dec. 6, 27 Outline Microwave
More informationMagnetic properties of spherical fcc clusters with radial surface anisotropy
Magnetic properties of spherical fcc clusters with radial surface anisotropy D. A. Dimitrov and G. M. Wysin Department of Physics Kansas State University Manhattan, KS 66506-2601 (December 6, 1994) We
More informationAdouble-layered (DL) perpendicular anisotropy system
1200 IEEE TRANSACTIONS ON MAGNETICS, VOL. 41, NO. 3, MARCH 2005 Methodology for Investigating the Magnetization Process of the Storage Layer in Double-Layered Perpendicular Magnetic Recording Media Using
More informationAn investigation of magnetic reversal in submicron-scale Co dots using first order reversal curve diagrams
JOURNAL OF APPLIED PHYSICS VOLUME 85, NUMBER 9 1 MAY 1999 An investigation of magnetic reversal in submicron-scale Co dots using first order reversal curve diagrams Chris Pike a) Department of Geology,
More informationJ 12 J 23 J 34. Driving forces in the nano-magnetism world. Intra-atomic exchange, electron correlation effects: Inter-atomic exchange: MAGNETIC ORDER
Driving forces in the nano-magnetism world Intra-atomic exchange, electron correlation effects: LOCAL (ATOMIC) MAGNETIC MOMENTS m d or f electrons Inter-atomic exchange: MAGNETIC ORDER H exc J S S i j
More informationSpin-transfer-torque efficiency enhanced by edge-damage. of perpendicular magnetic random access memories
Spin-transfer-torque efficiency enhanced by edge-damage of perpendicular magnetic random access memories Kyungmi Song 1 and Kyung-Jin Lee 1,2,* 1 KU-KIST Graduate School of Converging Science and Technology,
More informationPerpendicular Magnetic Recording. Dmitri Litvinov and Sakhrat Khizroev Seagate Research
Perpendicular Magnetic Recording Dmitri Litvinov and Sakhrat Khizroev Seagate Research Acknowledgments Leon Abelmann (U Twente) James Bain (CMU) Chunghee Chang Roy Chantrell Roy Gustafson Kent Howard Earl
More informationCharacterization of Heat-Assisted Magnetic Recording Channels
DIMACS Series in Discrete Mathematics and Theoretical Computer Science Volume 73, 2007 Characterization of Heat-Assisted Magnetic Recording Channels Rathnakumar Radhakrishnan, Bane Vasić, Fatih Erden,
More informationFuture Magnetic Recording Technologies
Future Magnetic Recording Technologies Seagate Research Areal Density Perspective Max. Areal Density (Gbit/in 2 ) 10000 1000 100 10 1 0.1 1 Tbit/in 2 LABORATORY DEMOS Products Historical 60% CGR line 1990
More informationInfluence of Size on the Properties of Materials
Influence of Size on the Properties of Materials M. J. O Shea Kansas State University mjoshea@phys.ksu.edu If you cannot get the papers connected to this work, please e-mail me for a copy 1. General Introduction
More informationHysteretic properties of a two dimensional array of small magnetic particles: a test-bed for the Preisach model
Preisach Memorial Book A. Iványi (Ed.) Akadémiai Kiadó, Budapest, 2005 Hysteretic properties of a two dimensional array of small magnetic particles: a test-bed for the Preisach model Gábor VÉRTESY Research
More informationChapter 8. Conclusions and Further Work Overview of Findings
8.1. Overview of Findings The aim of this thesis was to analyse, theoretically and experimentally, the signal and noise aspects of digital magnetic recording on longitudinal thin-film disk media. This
More informationA Monte Carlo Approach to Modelling Thermal Decay in Perpendicular Recording. Media
A Monte Carlo Approach to Modelling Thermal Decay in Perpendicular Recording Media T. J. Fal, 1 J. I. Mercer, 2 M. D. Leblanc, 1 J. P. Whitehead, 1 M. L. Plumer, 1 and J. van Ek 3 1 Department of Physics
More informationMagnetic force microscopy of signature erasure in magnetic recording media
Magnetic force microscopy of signature erasure in magnetic recording media Hsia-Po V. Kuo and E.D. Dahlberg Department of Physics, University of Minnesota Minneapolis, MN 55455 Magnetic force microscope
More informationJ 12 J 23 J 34. Driving forces in the nano-magnetism world. Intra-atomic exchange, electron correlation effects: Inter-atomic exchange: MAGNETIC ORDER
Driving forces in the nano-magnetism world Intra-atomic exchange, electron correlation effects: LOCAL (ATOMIC) MAGNETIC MOMENTS m d or f electrons Inter-atomic exchange: MAGNETIC ORDER H exc J S S i j
More informationThermal Effects in Magnetic Recording Media
Thermal Effects in Magnetic Recording Media J.W. Harrell MINT Center and Dept. of Physics & Astronomy University of Alabama Work supported by NSF-MRSEC MINT Fall Review, Nov. 21 Stability Problem in Granular
More informationInfluence of magnetic field and mechanical scratch on the recorded magnetization stability of longitudinal and perpendicular recording media
Available online at www.sciencedirect.com Physics Procedia 16 (2011) 53 57 The 9th Perpendicular Magnetic Recording Conference Influence of magnetic field and mechanical scratch on the recorded magnetization
More informationarxiv:cond-mat/ v1 18 Mar 2003
Hysteresis loop of a nanoscopic magnetic array A. Kaczanowski, K. Malarz and K. Ku lakowski arxiv:cond-mat/3333v1 18 Mar 23 Department of Applied Computer Science, Faculty of Physics and Nuclear Techniques,
More informationMicromagnetic Modeling
Micromagnetic Modeling P. B. Visscher Xuebing Feng, D. M. Apalkov, and Arkajyoti Misra Department of Physics and Astronomy Supported by NSF grants # ECS-008534 and DMR-0213985, and DOE grant # DE-FG02-98ER45714
More informationDynamics of a magnetic nanoparticle with cubic anisotropy in a viscous liquid
Dynamics of a magnetic nanoparticle with cubic anisotropy in a viscous liquid N. A. Usov 1,2,4, M. L. Fdez-Gubieda 2, A. Muela 3 and J. M. Barandiarán 2 1 IKERBASQUE, The Basque Foundation for Science,
More informationTransition from single-domain to vortex state in soft magnetic cylindrical nanodots
Transition from single-domain to vortex state in soft magnetic cylindrical nanodots W. Scholz 1,2, K. Yu. Guslienko 2, V. Novosad 3, D. Suess 1, T. Schrefl 1, R. W. Chantrell 2 and J. Fidler 1 1 Vienna
More informationImprinting domain/spin configurations in antiferromagnets. A way to tailor hysteresis loops in ferromagnetic-antiferromagnetic systems
Imprinting domain/spin configurations in antiferromagnets A way to tailor hysteresis loops in ferromagnetic-antiferromagnetic systems Dr. J. Sort Institució Catalana de Recerca i Estudis Avançats (ICREA)
More informationMICRO-SCALE NUMERICAL SIMULATION OF THE MAGNETIC RECORDING
Électrotechnique et électroénergétique MICRO-SCALE NUMERICAL SIMULATION OF THE MAGNETIC RECORDING ADELINA BORDIANU, VALENTIN IONIŢĂ, LUCIAN PETRESCU 1 Key words: Nanoparticles, Micro-scale magnetic characterization,
More informationFinite element /boundary element simulation of future hard disk recording
Finite element /boundary element simulation of future hard disk recording T. SCHREFL, G. HRKAC, A. GONCHAROV, J. DEAN, S. BANCE, M. A. BASHIR Department of Engineering Materials University of Shef Mappin
More informationMagnetic Force Microscopy practical
European School on Magnetism 2015 From basic magnetic concepts to spin currents Magnetic Force Microscopy practical Organized by: Yann Perrin, Michal Staňo and Olivier Fruchart Institut NEEL (CNRS & Univ.
More informationSimulation Of Spin Wave Switching In Perpendicular Media
Simulation Of Spin Wave Switching In Perpendicular Media P. B.Visscher Department of Physics and Astronomy The University of Alabama Abstract We propose to build on our understanding of spin wave switching
More informationMicromagnetic simulation of magnetization reversal in rotational magnetic fields
Physica B 306 (2001) 112 116 Micromagnetic simulation of magnetization reversal in rotational magnetic fields J. Fidler*, T. Schrefl, W. Scholz, D. Suess, V.D. Tsiantos Institute of Applied and Technical
More informationMagnetic States and Hysteresis Properties of Small Magnetite Particles
The Physics of Metals and Metallography, Vol. 86, No. 3, 998, pp. 269 275. Original Russian Text Copyright 998 by Fizika Metallov i Metallovedenie, Afremov, Panov. English Translation Copyright 998 by
More informationExchange Splitting of Backward Volume Spin Wave Configuration Dispersion Curves in a Permalloy Nano-stripe
760 PIERS Proceedings, Kuala Lumpur, MALAYSIA, March 27 30, 2012 Exchange Splitting of Backward Volume Spin Wave Configuration Dispersion Curves in a Permalloy Nano-stripe G. Venkat 1, A. Prabhakar 1,
More informationTHERE are many possibilities by which the hysteresis loop
1968 IEEE TRANSACTIONS ON MAGNETICS, VOL. 44, NO. 7, JULY 2008 Exchange-Biased Magnetic Vortices Axel Hoffmann 1;2, Jordi Sort 3, Kristen S. Buchanan 2, and Josep Nogués 4 Materials Science Division, Argonne
More informationS. Mangin 1, Y. Henry 2, D. Ravelosona 3, J.A. Katine 4, and S. Moyerman 5, I. Tudosa 5, E. E. Fullerton 5
Spin transfer torques in high anisotropy magnetic nanostructures S. Mangin 1, Y. enry 2, D. Ravelosona 3, J.A. Katine 4, and S. Moyerman 5, I. Tudosa 5, E. E. Fullerton 5 1) Laboratoire de Physique des
More informationBreaking the thermally induced write error in heat assisted recording by using low and high Tc materials
Breaking the thermally induced write error in heat assisted recording by using low and high Tc materials D. Suess, Vienna University of Technology, Wiedner Hauptstrasse 8-10, 1040 Vienna, Austria. T. Schrefl
More informationMicromagnetic simulation of dynamic and thermal effects
Micromagnetic simulation of dynamic and thermal effects T. Schrefl, J. Fidler, D. Suess, W. Scholz, V. Tsiantos Institute of Applied and Technical Physics Vienna University of Technology Wiedner Haupstr.
More informationIntroduction to magnetic recording + recording materials
Introduction to magnetic recording + recording materials Laurent Ranno Institut Néel, Nanoscience Dept, CNRS-UJF, Grenoble, France I will give two lectures about magnetic recording. In the first one, I
More informationMicromagnetics: Basic Principles
A small class of materials exhibit the important property of long range magnetic order Fundamentally, this arises because of the so-called exchange energy which can, under certain circumstances, lead to
More informationELECTRON HOLOGRAPHY OF NANOSTRUCTURED MAGNETIC MATERIALS. Now at: Department of Materials, University of Oxford, Parks Road, Oxford OX1 3PH, UK
ELECTRON HOLOGRAPHY OF NANOSTRUCTURED MAGNETIC MATERIALS R. E. DUNIN-BORKOWSKI a,b, B. KARDYNAL c,d, M. R. MCCARTNEY a, M. R. SCHEINFEIN e,f, DAVID J. SMITH a,e a Center for Solid State Science, Arizona
More informationANGULAR DEPENDENCE OF MAGNETIC PROPERTIES IN Co/Pt MULTILAYERS WITH PERPENDICULAR MAGNETIC ANISOTROPY
International Journal of Modern Physics B Vol. 19, Nos. 15, 16 & 17 (2005) 2562-2567 World Scientific Publishing Company World Scientific V www.worldscientific.com ANGULAR DEPENDENCE OF MAGNETIC PROPERTIES
More informationMatSci 224 Magnetism and Magnetic. November 5, 2003
MatSci 224 Magnetism and Magnetic Materials November 5, 2003 How small is small? What determines whether a magnetic structure is made of up a single domain or many domains? d Single domain d~l d d >> l
More informationExchange bias of polycrystalline antiferromagnets with perfectly compensated interface
Exchange bias of polycrystalline antiferromagnets with perfectly compensated interface D. Suess, M. Kirschner, T. Schrefl, J. Fidler 1 Institute of Solid State Physics, Vienna University of Technology,
More informationMAGNETO-RESISTANCE AND INDUCED DOMAIN STRUCTURE IN TUNNEL JUNCTIONS
Mat. Res. Soc. Symp. Proc. Vol. 674 001 Materials Research Society MAGNETO-RESISTANCE AND INDUCED DOMAIN STRUCTURE IN TUNNEL JUNCTIONS M. Hehn, O. Lenoble, D. Lacour and A. Schuhl Laboratoire de Physique
More informationMagnetic recording technology
Magnetic recording technology The grain (particle) can be described as a single macrospin μ = Σ i μ i 1 0 1 0 1 W~500nm 1 bit = 300 grains All spins in the grain are ferromagnetically aligned B~50nm Exchange
More informationTheory of magnetoelastic dissipation due to domain wall width oscillation
JOURNAL OF APPLIED PHYSICS VOLUME 83, NUMBER 11 1 JUNE 1998 Theory of magnetoelastic dissipation due to domain wall width oscillation Y. Liu and P. Grütter a) Centre for the Physics of Materials, Department
More informationOptimization of Bias Magnetic Tape in a Remote Readable Data-Carrier using Amorphous Magnetostrictive Strip
Optimization of Bias Magnetic Tape in a Remote Readable Data-Carrier using Amorphous Magnetostrictive Strip SUENAGA Wataru The magnetic characteristics of a magnetic tag device composed of a magnetostrictive
More informationScanning Probe Microscopy. L. J. Heyderman
1 Scanning Probe Microscopy 2 Scanning Probe Microscopy If an atom was as large as a ping-pong ball......the tip would have the size of the Matterhorn! 3 Magnetic Force Microscopy Stray field interaction
More informationNeutron Reflectometry of Ferromagnetic Arrays
Neutron Reflectometry of Ferromagnetic Arrays Z.Y. Zhao a, P. Mani a, V.V.Krishnamurthy a, W.-T. Lee b, F. Klose b, and G.J. Mankey a a Center for Materials for Information Technology and Department of
More informationTHE INFLUENCE OF A SURFACE ON HYSTERESIS LOOPS FOR SINGLE-DOMAIN FERROMAGNETIC NANOPARTICLES
THE INFLUENCE OF A SURFACE ON HYSTERESIS LOOPS FOR SINGLE-DOMAIN FERROMAGNETIC NANOPARTICLES A thesis submitted in partial fulfillment of the requirements for the degree of Master of Science By Saad Alsari
More informationMAGNETIC BEHAVIOUR OF CORE/SHELL NANOPARTICLE ASSEMBLIES: INTERPARTICLE INTERACTIONS EFFECTS
IMS MAGNETIC BEHAVIOUR OF CORE/SHELL NANOPARTICLE ASSEMBLIES: INTERPARTICLE INTERACTIONS EFFECTS Kalliopi Trohidou Computational Materials Science Group Institute of Materials Science, NCSR Demokritos,
More informationCurrent-driven Magnetization Reversal in a Ferromagnetic Semiconductor. (Ga,Mn)As/GaAs/(Ga,Mn)As Tunnel Junction
Current-driven Magnetization Reversal in a Ferromagnetic Semiconductor (Ga,Mn)As/GaAs/(Ga,Mn)As Tunnel Junction D. Chiba 1, 2*, Y. Sato 1, T. Kita 2, 1, F. Matsukura 1, 2, and H. Ohno 1, 2 1 Laboratory
More informationCHAPTER 2 MAGNETISM. 2.1 Magnetic materials
CHAPTER 2 MAGNETISM Magnetism plays a crucial role in the development of memories for mass storage, and in sensors to name a few. Spintronics is an integration of the magnetic material with semiconductor
More informationMagneto Optical Kerr Effect Microscopy Investigation on Permalloy Nanostructures
Magneto Optical Kerr Effect Microscopy Investigation on Permalloy Nanostructures Zulzawawi Bin Haji Hujan A thesis submitted for the degree of MSc by research University of York Department of Physics January
More informationIntroduction to magnetism of confined systems
Introduction to magnetism of confined systems P. Vavassori CIC nanogune Consolider, San Sebastian, Spain; nano@nanogune.eu Basics: diamagnetism and paramagnetism Every material which is put in a magnetic
More informationMagnetic Recording. by Gaspare Varvaro. Istituto di Struttura della Materia CNR Nanostructured Magnetic Materials Group
Magnetic Recording by Gaspare Varvaro Istituto di Struttura della Materia CNR Nanostructured Magnetic Materials Group Outline Brief History of Magnetic Recording Hard Disk Drives General Aspects (Longitudinal
More informationAnisotropy properties of magnetic colloidal materials
INSTITUTE OF PHYSICS PUBLISHING JOURNAL OF PHYSICS D: APPLIED PHYSICS J. Phys. D: Appl. Phys. 36 (2003) L10 L14 PII: S0022-3727(03)53088-1 RAPID COMMUNICATION Anisotropy properties of magnetic colloidal
More informationHALL EFFECT AND MAGNETORESISTANCE MEASUREMENTS ON PERMALLOY Py THIN FILMS AND Py/Cu/Py MULTILAYERS
Journal of Optoelectronics and Advanced Materials, Vol. 4, No. 1, March 2002, p. 79-84 HALL EFFECT AND MAGNETORESISTANCE MEASUREMENTS ON PERMALLOY Py THIN FILMS AND Py/Cu/Py MULTILAYERS M. Volmer, J. Neamtu
More informationMagnetic domain theory in dynamics
Chapter 3 Magnetic domain theory in dynamics Microscale magnetization reversal dynamics is one of the hot issues, because of a great demand for fast response and high density data storage devices, for
More informationDIRECTIVITY AND SENSITIVITY OF HIGH FREQUENCY CARRIER TYPE THIN-FILM MAGNETIC FIELD SENSOR
DIRECTIVITY AND SENSITIVITY OF HIGH FREQUENCY CARRIER TYPE THIN-FILM MAGNETIC FIELD SENSOR M. Yamaguchi a, M. Takezawa a, H. Ohdaira b, K. I. Arai a, and A. Haga b a Research Institute of Electrical Communication,
More informationEnhanced Magnetic Properties of Bit Patterned Magnetic Recording Media by Trench-Filled Nanostructure
CMRR Report Number 32, Summer 2009 Enhanced Magnetic Properties of Bit Patterned Magnetic Recording Media by Trench-Filled Nanostructure Edward Chulmin Choi, Daehoon Hong, Young Oh, Leon Chen, Sy-Hwang
More informationThermal Effects in High Coercivity Perpendicular Media
Thermal Effects in High Coercivity Perpendicular Media J.W. Harrell Scott Brown MINT Center University of Alabama Introduction Thermal stability of perpendicular media will be a limiting factor in future
More information0.002 ( ) R xy
a b z 0.002 x H y R xy () 0.000-0.002 0 90 180 270 360 (degree) Supplementary Figure 1. Planar Hall effect resistance as a function of the angle of an in-plane field. a, Schematic of the planar Hall resistance
More informationDirect study of domain and domain wall structure in magnetic films and nanostructures
Direct study of domain and domain wall structure in magnetic films and nanostructures John Chapman, University of Glasgow Synopsis Why use Lorentz microscopy? Magnetisation reversal in soft magnetic films
More informationHigh-frequency measurements of spin-valve films and devices invited
JOURNAL OF APPLIED PHYSICS VOLUME 93, NUMBER 10 15 MAY 003 High-frequency measurements of spin-valve films and devices invited Shehzaad Kaka, John P. Nibarger, and Stephen E. Russek a) National Institute
More informationAdvanced Lab Course. Tunneling Magneto Resistance
Advanced Lab Course Tunneling Magneto Resistance M06 As of: 015-04-01 Aim: Measurement of tunneling magnetoresistance for different sample sizes and recording the TMR in dependency on the voltage. Content
More informationFerromagnetic Domain Distribution in Thin Films During Magnetization Reversal. and E. D. Dahlberg 3. Abstract
Ferromagnetic Domain Distribution in Thin Films During Magnetization Reversal W.-T. Lee 1, S. G. E. te Velthuis 2, G. P. Felcher 2, F. Klose 1, T. Gredig 3, and E. D. Dahlberg 3. 1 Spallation Neutron Source,
More informationSWITCHED reluctance motor (SRM) drives have been
IEEE TRANSACTIONS ON INDUSTRIAL ELECTRONICS, VOL. 45, NO. 5, OCTOBER 1998 815 A Novel Power Converter with Voltage-Boosting Capacitors for a Four-Phase SRM Drive Yasser G. Dessouky, Barry W. Williams,
More informationSUPPLEMENTARY INFORMATION
SUPPLEMENTARY INFORMATION doi:10.1038/nature11733 1 Ising-Macrospin model The Ising-Macrospin (IM) model simulates the configuration of the superlattice (SL) by assuming every layer is a single spin (macrospin)
More informationResolution of Patterned Magnetic Media
Resolution of Patterned Magnetic Media by Ki Seog Song Bachelor of Science in Engineering Mechanical Design and Production Engineering Seoul National University, 1989 Submitted to the Department of Mechanical
More informationOgnjan Tzarnoretchki. Introduction
BULGARIAN ACADEMY OF SCIENCES CYBERNETICS AND INFORMATION TECHNOLOGIES Volume 6, No 1 Sofia 2006 Coefficients of the Evolution Potentials of the Informative Features Linear, Track and Areal Density of
More informationMagnetoresistance due to Domain Walls in Micron Scale Fe Wires. with Stripe Domains arxiv:cond-mat/ v1 [cond-mat.mes-hall] 9 Mar 1998.
Magnetoresistance due to Domain Walls in Micron Scale Fe Wires with Stripe Domains arxiv:cond-mat/9803101v1 [cond-mat.mes-hall] 9 Mar 1998 A. D. Kent a, U. Ruediger a, J. Yu a, S. Zhang a, P. M. Levy a
More informationMagnetic properties of Co nanocolumns fabricated by oblique-angle deposition
JOURNAL OF APPLIED PHYSICS VOLUME 93, NUMBER 7 1 APRIL 2003 Magnetic properties of Co nanocolumns fabricated by oblique-angle deposition F. Tang, a) D.-L. Liu, D.-X. Ye, Y.-P. Zhao, T.-M. Lu, and G.-C.
More informationINFLUENCE OF MAGNETIC ANISOTROPY ON THE ROTATIONAL MAGNETIZATION IN TYPICAL DYNAMO STEEL SHEETS
Zeszyty Problemowe Maszyny Elektryczne Nr 3/014 (103) 173 Witold Mazgaj, Zbigniew Szular, Adam Warzecha Cracow University of Technology INFLUENCE OF MAGNETIC ANISOTROPY ON THE ROTATIONAL MAGNETIZATION
More information2.9 DEMAGNETIZING FACTORS
52 EXPERIMENTAL METHODS Fig. 2.25 Magnetic shielding. 2.9 DEMAGNETIZING FACTORS Returning to the bar magnets of Fig. 2.24, we might ascribe the nonuniformity of the induction inside the magnet to the fact
More informationTechniques for inferring M at small scales
Magnetism and small scales We ve seen that ferromagnetic materials can be very complicated even in bulk specimens (e.g. crystallographic anisotropies, shape anisotropies, local field effects, domains).
More informationInjecting, Controlling, and Storing Magnetic Domain Walls in Ferromagnetic Nanowires
Marquette University e-publications@marquette Physics Faculty Research and Publications Physics, Department of 8-1-2010 Injecting, Controlling, and Storing Magnetic Domain Walls in Ferromagnetic Nanowires
More informationExchange bias in core/shell magnetic nanoparticles: experimental results and numerical simulations
Exchange bias in core/shell magnetic nanoparticles: experimental results and numerical simulations Xavier Batlle, A. Labarta, Ò. Iglesias, M. García del Muro and M. Kovylina Goup of Magnetic Nanomaterials
More informationFundamental of HDD Technology (1)
Course Information Fundamental of HDD Technology (1) Data Storage Technology Research Unit Nakhon Pathom Rajabhat University Assistant Prof. Piya Kovintavewat, Ph.D. E-mail: piya@npru.ac.th URL: http://home.npru.ac.th/piya
More informationChapter 3. Magnetic Model. 3.1 Magnetic interactions
Chapter 3 Magnetic Model In this chapter, the micromagnetic model for the description of the magnetic properties of a laterally nanostructured film during growth is presented. The main physical idea of
More informationMagnetoresistance behavior of nanoscale antidot arrays
Magnetoresistance behavior of nanoscale antidot arrays C. C. Wang and A. O. Adeyeye* Information Storage Materials Laboratory, Department of Electrical and Computer Engineering, National University of
More informationSUPPLEMENTARY INFORMATION
SUPPLEMENTARY INFORMATION doi:.38/nphys436 Non-adiabatic spin-torques in narrow magnetic domain walls C. Burrowes,2, A. P. Mihai 3,4, D. Ravelosona,2, J.-V. Kim,2, C. Chappert,2, L. Vila 3,4, A. Marty
More informationProceedings of SPIE, Micro- and Nanoelectronics -2003, Vol. 5401, pp (2003).
Proceedings of SPIE, Micro- and Nanoelectronics -2003, Vol. 5401, pp 555-560 (2003). Magnetic force microscopy of magnetization reversal of microstructures in situ in the external field of up to 2000Oe
More informationGiant Magnetoresistance
Giant Magnetoresistance This is a phenomenon that produces a large change in the resistance of certain materials as a magnetic field is applied. It is described as Giant because the observed effect is
More informationUnidirectional spin-wave heat conveyer
Unidirectional spin-wave heat conveyer Figure S1: Calculation of spin-wave modes and their dispersion relations excited in a 0.4 mm-thick and 4 mm-diameter Y 3 Fe 5 O 12 disk. a, Experimentally obtained
More informationField homogeneity improvement of maglev NdFeB magnetic rails from joints
DOI 10.1186/s40064-016-1965-3 RESEARCH Open Access Field homogeneity improvement of maglev NdFeB magnetic rails from joints Y. J. Li 1,2, Q. Dai 2, C. Y. Deng 2, R. X. Sun 1, J. Zheng 1, Z. Chen 3, Y.
More informationMAGNETIC HEADS FOR HIGH COERCIVITY RECORDING MEDIA
Journal of ptoelectronics and Advanced Materials Vol. 6, No. 3, September 4, p. 9-96 MAGNETIC HEADS FR HIGH CERCIVITY RECRDING MEDIA V. N. Samofalov *, E. I. Il ashenko a, A. Ramstad b, L.Z. Lub anu, T.H.
More informationSUPPLEMENTARY INFORMATION
Magneto-ionic Control of Interfacial Magnetism Uwe Bauer, Lide Yao, Aik Jun Tan, Parnika Agrawal, Satoru Emori, Harry L. Tuller, Sebastiaan van Dijken and Geoffrey S. D. Beach - Supplementary Information
More informationPreparation, Structural Characterization, and Dynamic Properties Investigation of Permalloy Antidot Arrays
University of Montana ScholarWorks at University of Montana Chemistry and Biochemistry Faculty Publications Chemistry and Biochemistry 5-12-2005 Preparation, Structural Characterization, and Dynamic Properties
More informationAPPLICATION OF THE NONLINEAR HARMONICS METHOD TO CONTINUOUS
APPLICATION OF THE NONLINEAR HARMONICS METHOD TO CONTINUOUS MEASUREMENT OF STRESS IN RAILROAD RAIL G.L. Burkhardt and H. Kwun Southwest Research Institute 6220 Culebra Road San Antonio, Texas 78284 INTRODUCTION
More informationCharacteristics of soft magnetic composite material under rotating magnetic fluxes
Characteristics of soft magnetic composite material under rotating magnetic fluxes J.J. Zhong, Y.G. Guo*, J.G. Zhu, and Z.W. Lin Faculty of Engineering, University of Technology, Sydney, P.O. Box 123,
More informationLarge-amplitude coherent spin waves excited by spin-polarized current in nanoscale spin valves
Large-amplitude coherent spin waves excited by spin-polarized current in nanoscale spin valves I. N. Krivorotov Department of Physics and Astronomy, University of California, Irvine, California 92697-4575,
More informationMagnetic nanoparticles containing soft-hard diblock
Electronic Supplementary Material (ESI) for Nanoscale. This journal is The Royal Society of Chemistry 2018 Electronic Supplementary Information Magnetic nanoparticles containing soft-hard diblock copolymer
More informationEFFECTS OF SKEW ANGLE AND TRANSITION CURVATURE IN HAMR HARD DISK DRIVES A THESIS SUBMITTED TO THE FACULTY OF THE UNIVERSITY OF MINNESOTA BY
EFFECTS OF SKEW ANGLE AND TRANSITION CURVATURE IN HAMR HARD DISK DRIVES A THESIS SUBMITTED TO THE FACULTY OF THE UNIVERSITY OF MINNESOTA BY MICHAEL CORDLE IN PARTIAL FULFILLMENT OF THE REQUIREMENTS FOR
More information