Delamination Modeling for Power Packages and Modules. Rainer Dudek, R. Döring, S. Rzepka Fraunhofer ENAS, Micro Materials Center Chemnitz
|
|
- Paula Bond
- 5 years ago
- Views:
Transcription
1 Delamination Modeling for Power Packages and Modules Rainer Dudek, R. Döring, S. Rzepka Fraunhofer ENAS, Micro Materials Center Chemnitz
2 The Micro Materials Virtual Prototyping Finite Element Analysis Optimization Deformation/Stress Measurement MicroDAC e.g. FIB- resolution: 3 nm Diagnostics/Failure Analysis Tomography, SEM, LSM, Testing Temperature, Moisture, Vibration
3 Outline Introduction: Delamination failure and Finite Element Modelling Delamination failure in a plastic power package Stress analyses on a power module with Transient Liquid Phase interconnects Evaluation of interface delamination risk by the Cohesive Zone Method delamination analyses on a sintered power module Summary
4 Important Mechanical Reliability Issues in Electronics Addressed by Finite Element Analysis temperature voltage (Coupled) mechanical analysis mechanical loading fracture fatigue high cycle low cycle overload cracking delamination vibration noise environmental T/moist.-cycle power on-off
5 Examples: Interface Delamination in Electronics SAM Thermo-mechanically driven interface delamination is a major reliability concern SAM X- ray die Glob Top FR-4 Board UF SAM FCoB 20µm
6 Modeling of Interface Delamination Failure by Finite Element Analysis Fracture mechanics based approaches consider the real or fictious presence of initial defects singular crack or delamination tip stress field Cohesive zone based approaches fracture zone of finite size describe interface debonding as the gradual degradation between two materials (avoids crack tip singularity) do not describe a fully brittle fracture, but cohesive parameters were chosen such to describe quasi-brittle fracture fracture criterion: G C cohesive energy, critical fracture energy release rate to cause failure failure criterion has to be chosen in dependence on mode mixity, as delamination toughness in shear loading is much higher than in tension
7 Delamination Analysis of Power IC Package - Cohesive FE Model P-DSO 8 Interface Si (SiO 2 ) to MC (top) Interface heat slug to MC Interface Si (SiO 2 ) to MC (edge) Interface die attach to MC, CZM analysis used to predict interface delamination onset and propagation Scalar stiffness degradation (D) used as damage metric 0.99 D 1 = delaminated
8 Delamination Onset for Package - P-DSO 8 Subjected to Thermal Loading T = C T = C Delamination onset Si-die/MC = Cu-heatsink/MC T = C during a very small temp. decrease, i.e. between -47 C and -48 C maximum degradation shifts to lower leadframe-mc edge Delamination shift
9 Delamination Evolution for Si-Die/ Molding Compound and Heatsink/ MC Delamination occurs by unstable crack growth at one certain temperature Delaminated area in red T = C
10 Delaminated Package P-DSO C out of plane displacement u-y (mm) D deformation 10x delamination complete opening of the delaminated area package undergoes a warpage towards the outer edges
11 Reliability Studies on Power Modules Characteristic control unit for high power (IGBTs on DCB) (PCB) Power Terminals Case Auxilliary Terminals Temperature load Substrate 1 2 Solder Casting Base Plate Soft Casting Characteristic failure mechanism: USM: after 2000 cycles Soft (high lead) solder undergoes cyclic plastic (creep) deformation Solder fails from the outer pheriphery of the joint areas
12 New Interconnects by Transient Liquid Phase (TLP) Soldering Soft (high lead) IGBT die attach is replaced by new TLP solder layer. TLP layer (IMC dominated) is less ductile. Solder fatigue is no longer the dominating failure mechanism. New reliability issues, e.g. delamination of metallizations, due to stiff interconnect! Transient liquid phase soldering layer (Project HotPowCon)
13 Simulations on Failure Risk of IGBTs, TLP-Soldered Symmetry IGBT (10 x 10 x 0.365mm³) Cohesive-Interface DCB Chipmetallis ation solder, optional TLP solder Thermo-mechanical Loading (Temperature loading) Active: P = 440 W, t= 45 ms Cyclic passive 100 Temperatur [ C] Zeit [s]
14 Critical Stresses for SAC vs. TLP Die Attach Risk of brittle fracture/delamination due to stress at IGBT Fatigue failure risk due to plastic strain in solder Stress concentration at chip edge Passive loading Creep strain concentration at solder edge Cooling to - 65 C SAC IMC SAC IMC SAC New interconnection technologies cause shift in failure risk!
15 Evaluation of Delamination Die- Interface for SAC vs. TLP Solder D SAC die attach D IMC die attach No delamination (D = 0) Delamination initiates for adhesion parameters assumed T = - 65 C bad interface adhesion between metallization and die assumed for SAC the damage parameter D is equal to 0 everywhere, i.e. at the entire interface absolutely no risk of delamination for the IMC layer a delamination risk is given in the peripheral region
16 Simulations on Failure Risk of IGBTs, Ag-Sintered On heatsink Die (10.23 x 9.73 x 0.07mm³) Var 1 DCB Copper Cohesive zone interfaces prone to delamin. Sinter Ag (20µm thick)
17 IGBT Loading: Active T-Cycle 3s on /3s off, 700 W T ( K)
18 Delamination Failure Risk of Ag-Sinter Layer Dependent on Adhesion D Good interface adhesion D equally bad interface adhesion D = 1 D = 0 everywhere D = 0 for characteristic good metal-metal adhesion no delamination risk delamiantion starts from periphery, is stable for bad but equal adhesion, upper interface Ag to die metallization is critical D very bad adhesion delaminated zone D = 0
19 Summary More rigid multi-material assemblies in power electronics makes them prone to interface delamination failure. Characteristic low cycle fatigue solder failures become unlikely and are replaced by kinds of brittle failure. Multiple failure modes must be considered in FEA based virtual prototyping. Cohesive Zone Modeling based investigations show great potential to evaluate interface delamination failure.
TABLE OF CONTENTS CHAPTER TITLE PAGE DECLARATION DEDICATION ACKNOWLEDGEMENT ABSTRACT ABSTRAK
vii TABLE OF CONTENTS CHAPTER TITLE PAGE DECLARATION DEDICATION ACKNOWLEDGEMENT ABSTRACT ABSTRAK TABLE OF CONTENTS LIST OF TABLES LIST OF FIGURES LIST OF ABBREVIATIONS LIST OF SYMBOLS ii iii iv v vi vii
More informationExperimentally Calibrating Cohesive Zone Models for Structural Automotive Adhesives
Experimentally Calibrating Cohesive Zone Models for Structural Automotive Adhesives Mark Oliver October 19, 2016 Adhesives and Sealants Council Fall Convention contact@veryst.com www.veryst.com Outline
More information1 INTRODUCTION 2 SAMPLE PREPARATIONS
Chikage NORITAKE This study seeks to analyze the reliability of three-dimensional (3D) chip stacked packages under cyclic thermal loading. The critical areas of 3D chip stacked packages are defined using
More informationPowerful Modelling Techniques in Abaqus to Simulate
Powerful Modelling Techniques in Abaqus to Simulate Necking and Delamination of Laminated Composites D. F. Zhang, K.M. Mao, Md. S. Islam, E. Andreasson, Nasir Mehmood, S. Kao-Walter Email: sharon.kao-walter@bth.se
More informationMechanical Simulations for Chip Package Interaction: Failure Mechanisms, Material Characterization, and Failure Data
Mechanical Simulations for Chip Package Interaction: Failure Mechanisms, Material Characterization, and Failure Data Ahmer Syed Amkor Technology Enabling a Microelectronic World Outline Effect of Chip
More informationFracture mechanics fundamentals. Stress at a notch Stress at a crack Stress intensity factors Fracture mechanics based design
Fracture mechanics fundamentals Stress at a notch Stress at a crack Stress intensity factors Fracture mechanics based design Failure modes Failure can occur in a number of modes: - plastic deformation
More informationReliability analysis of different structure parameters of PCBA under drop impact
Journal of Physics: Conference Series PAPER OPEN ACCESS Reliability analysis of different structure parameters of PCBA under drop impact To cite this article: P S Liu et al 2018 J. Phys.: Conf. Ser. 986
More informationFig. 1. Different locus of failure and crack trajectories observed in mode I testing of adhesively bonded double cantilever beam (DCB) specimens.
a). Cohesive Failure b). Interfacial Failure c). Oscillatory Failure d). Alternating Failure Fig. 1. Different locus of failure and crack trajectories observed in mode I testing of adhesively bonded double
More informationPrediction of Encapsulant Performance Toward Fatigue Properties of Flip Chip Ball Grid Array (FC-BGA) using Accelerated Thermal Cycling (ATC)
Prediction of Encapsulant Performance Toward Fatigue Properties of Flip Chip Ball Grid Array (FC-BGA) using Accelerated Thermal Cycling (ATC) ZAINUDIN KORNAIN 1, AZMAN JALAR 2,3, SHAHRUM ABDULLAH 3, NOWSHAD
More informationTRENDS IN LEVENSDUURTESTEN VOOR MICRO-ELEKTRONICA PLOT CONFERENTIE
TRENDS IN LEVENSDUURTESTEN VOOR MICRO-ELEKTRONICA PLOT CONFERENTIE JEROEN JALINK 8 JUNI 2016 MICROELECTRONICS RELIABILITY 54 (2014) 1988 1994 Contents Introduction NXP Package form factor Failure mechanism
More informationTHERMOMECHANICAL ANALYSIS OF ELECTRONIC PACKAGE USING FINITE ELEMENT METHOD
THERMOMECHANICAL ANALYSIS OF ELECTRONIC PACKAGE USING FINITE ELEMENT METHOD N.BhargavaRamudu 1, V. Nithin Kumar Varma 2, P.Ravi kiran 3, T.Venkata Avinash 4, Ch. Mohan Sumanth 5, P.Prasanthi 6 1,2,3,4,5,6
More informationFour-point bending cycling as alternative for Thermal cycling solder fatigue testing
Four-point bending as alternative for Thermal solder fatigue testing Bart Vandevelde a, Filip Vanhee b, Davy Pissoort b, Lieven Degrendele c, Johan De Baets c, Bart Allaert d, Ralph Lauwaert e, Riet Labie
More informationIn Situ Ultrasonic NDT of Fracture and Fatigue in Composites
ECNDT 26 - Mo.2.6.5 In Situ Ultrasonic NDT of Fracture and Fatigue in Composites I. SOLODOV, K. PFLEIDERER, and G. BUSSE Institute for Polymer Testing and Polymer Science (IKP), Non-destructive Testing
More informationDesign of Power Electronics Reliability: A New, Interdisciplinary Approach. M.C. Shaw. September 5, 2002
Design of Power Electronics Reliability: A New, Interdisciplinary Approach M.C. Shaw September 5, 2002 Physics Department California Lutheran University 60 W. Olsen Rd, #3750 Thousand Oaks, CA 91360 (805)
More informationDurability of bonded aircraft structure. AMTAS Fall 2016 meeting October 27 th 2016 Seattle, WA
Durability of bonded aircraft structure AMTAS Fall 216 meeting October 27 th 216 Seattle, WA Durability of Bonded Aircraft Structure Motivation and Key Issues: Adhesive bonding is a key path towards reduced
More informationADVANCED BOARD LEVEL MODELING FOR WAFER LEVEL PACKAGES
As originally published in the SMTA Proceedings ADVANCED BOARD LEVEL MODELING FOR WAFER LEVEL PACKAGES Tiao Zhou, Ph.D. Southern Methodist University Dallas, TX, USA tiaoz@smu.edu Zhenxue Han, Ph.D. University
More informationFatigue Life Prediction for Solder Interconnects in IGBT Modules for Hybrid Vehicle Application
International Journal of Engineering and Technical Research (IJETR) ISSN: 2321-0869 (O) 2454-4698 (P), Volume-4, Issue-1, January 2016 Fatigue Life Prediction for Solder Interconnects in IGBT Modules for
More informationCLCC Solder Joint Life Prediction under Complex Temperature Cycling Loading
CLCC Solder Joint Life Prediction under Complex Temperature Cycling Loading, Michael Osterman, and Michael Pecht Center for Advanced Life Cycle Engineering (CALCE) University of Maryland College Park,
More informationThe Increasing Importance of the Thermal Management for Modern Electronic Packages B. Psota 1, I. Szendiuch 1
Ročník 2012 Číslo VI The Increasing Importance of the Thermal Management for Modern Electronic Packages B. Psota 1, I. Szendiuch 1 1 Department of Microelectronics, Faculty of Electrical Engineering and
More informationOn characterising fracture resistance in mode-i delamination
9 th International Congress of Croatian Society of Mechanics 18-22 September 2018 Split, Croatia On characterising fracture resistance in mode-i delamination Leo ŠKEC *, Giulio ALFANO +, Gordan JELENIĆ
More informationFinite element model for evaluation of low-cycle-fatigue life of solder joints in surface mounting power devices
Finite element model for evaluation of low-cycle-fatigue life of solder joints in surface mounting power devices N. Delmonte *1, F. Giuliani 1, M. Bernardoni 2, and P. Cova 1 1 Dipartimento di Ingegneria
More informationCHARACTERIZATION, ANALYSIS AND PREDICTION OF DELAMINATION IN COMPOSITES USING FRACTURE MECHANICS
Oral Reference Number: ICF100942OR CHARACTERIZATION, ANALYSIS AND PREDICTION OF DELAMINATION IN COMPOSITES USING FRACTURE MECHANICS T. Kevin O Brien U.S. Army Research Laboratory Vehicle Technology Directorate
More informationSOLDER JOINT RELIABILITY IN ELECTRONICS UNDER SHOCK AND VIBRATION USING EXPLICIT FINITE-ELEMENT SUB-MODELING. Sameep Gupte
SOLDER JOINT RELIABILITY IN ELECTRONICS UNDER SHOCK AND VIBRATION USING EXPLICIT FINITE-ELEMENT SUB-MODELING Except where reference is made to the work of others, the work described in this thesis is my
More informationWoon-Seong Kwon Myung-Jin Yim Kyung-Wook Paik
Woon-Seong Kwon e-mail: wskwon@kaist.ac.kr Myung-Jin Yim Kyung-Wook Paik Department of Materials Science and Engineering Korea Advanced Institute of Science and Technology Daejon 305-701, Korea Suk-Jin
More informationChapter 5: Ball Grid Array (BGA)
Chapter 5: Ball Grid Array (BGA) 5.1 Development of the Models The following sequence of pictures explains schematically how the FE-model of the Ball Grid Array (BGA) was developed. Initially a single
More informationEffects of underfill material on solder deformation and damage in 3D packages
University of New Mexico UNM Digital Repository Mechanical Engineering ETDs Engineering ETDs 9-3-2013 Effects of underfill material on solder deformation and damage in 3D packages Geno Flores Follow this
More informationImpact of Uneven Solder Thickness on IGBT Substrate Reliability
Impact of Uneven Solder Thickness on IGBT Substrate Reliability Hua Lu a, Chris Bailey a, Liam Mills b a Department of Mathematical Sciences, University of Greenwich 30 Park Row, London, SE10 9LS, UK b
More informationFlip Chip Reliability
Flip Chip Reliability P e t e r B o r g e s e n, P h. D., S u r face Mount Laboratory, Corporation, Binghamton, New York 13902-0825 Daniel Blass, Sur f a c e M o u n t L a b o r a t o r y, U n i v e r
More informationCyclic Bend Fatigue Reliability Investigation for Sn-Ag-Cu Solder Joints
Cyclic Bend Fatigue Reliability Investigation for Sn-Ag-Cu Solder Joints F.X. Che* 1, H.L.J. Pang 2, W.H. Zhu 1 and Anthony Y. S. Sun 1 1 United Test & Assembly Center Ltd. (UTAC) Packaging Analysis &
More informationDesign Guidelines for Preventing Flex Cracking Failures in Ceramic Capacitors
CARTS 2003: 23 rd Capacitor And Resistor Technology Symposium, March 31 April 3, 2003 Design Guidelines for Preventing Flex Cracking Failures in Ceramic Capacitors N. Blattau, D. Barker, and C. Hillman
More informationComparison between a Cohesive Zone Model and a Continuum Damage Model in Predicting Mode-I Fracture Behavior of Adhesively Bonded Joints
Copyright 2012 Tech Science Press CMES, vol.83, no.2, pp.169-181, 2012 Comparison between a Cohesive Zone Model and a Continuum Damage Model in Predicting Mode-I Fracture Behavior of Adhesively Bonded
More informationRatcheting deformation in thin film structures
Ratcheting deformation in thin film structures Z. SUO Princeton University Work with MIN HUANG, Rui Huang, Jim Liang, Jean Prevost Princeton University Q. MA, H. Fujimoto, J. He Intel Corporation Interconnect
More informationAssessment of the SMT assemblies and Improvements through Accelerated testing methods. SMTA Chapter Meeting 18 th Jan 2014, India
Assessment of the SMT assemblies and Improvements through Accelerated testing methods SMTA Chapter Meeting 18 th Jan 2014, India 1 Contents SMT solder defects due Thermo-Mechanical stress- what and how!
More informationThermal-Mechanical Analysis of a Different Leadframe Thickness of Semiconductor Package under the Reflow Process
American Journal of Applied Sciences 6 (4): 616-625, 2009 ISSN 1546-9239 2009 Science Publications Thermal-Mechanical Analysis of a Different Leadframe Thickness of Semiconductor Package under the Reflow
More informationLow Inductance Ceramic Capacitor (LICC)
Low Inductance Ceramic Capacitor (LICC) LICC(Low Inductance Ceramic Capacitor) is a kind of MLCC that is used for decoupling in High Speed IC. The termination shape of LICC is different from that of MLCC.
More informationMicrosemi Power Modules. Reliability tests for Automotive application
Microsemi Power Modules Reliability tests for Automotive application on basis of AEC-Q101 SP module line 1/ 10 Introduction With reference to standard AEC-Q101, designed by Automotive Electronics Council
More informationDynamic behaviour of electronics package and impact reliability of BGA solder joints
Dynamic behaviour of electronics package and impact reliability of BGA solder joints Q YU1, H Kikuchil, S Ikedal, M Shiratoril, M Kakino2, N Fujiwara2 Department of Mechanical Engineering and Material
More informationSSRG International Journal of Mechanical Engineering (SSRG-IJME) volume1 issue5 September 2014
Finite Element Modeling for Delamination Analysis of Double Cantilever Beam Specimen Mohammed Waseem H.S. 1, Kiran Kumar N. 2 1 Post Graduate Student, 2 Asst. Professor Dept. of Mechanical Engineering,
More informationFRACTURE MECHANICS IN ANSYS R16. Session 04 Fracture Mechanics using Cohesive Zone Material (CZM) Model
FRACTURE MECHANICS IN ANSYS R16 Session 04 Fracture Mechanics using Cohesive Zone Material (CZM) Model COHESIVE ZONE MATERIAL MODEL (CZM) Fracture or delamination along an interface between phases plays
More informationSimulation of the Influence of Manufacturing Quality on Thermomechanical Stress of Microvias
As originally published in the IPC APEX EXPO Conference Proceedings. Simulation of the Influence of Manufacturing Quality on Thermomechanical Stress of Microvias Yan Ning, Michael H. Azarian, and Michael
More informationAdvanced Strength of Materials Prof S. K. Maiti Mechanical Engineering Indian Institute of Technology, Bombay. Lecture 27
Advanced Strength of Materials Prof S. K. Maiti Mechanical Engineering Indian Institute of Technology, Bombay Lecture 27 Last time we considered Griffith theory of brittle fracture, where in it was considered
More informationCHAPTER 8 FATIGUE LIFE ESTIMATION OF ELECTRONIC PACKAGES SUBJECTED TO DYNAMIC LOADS
80 CHAPTER 8 FATIGUE LIFE ESTIMATIO OF ELECTROIC PACKAGES SUBJECTED TO DYAMIC LOADS 8. ITRODUCTIO Vibration environments can often involve millions of stress cycles because natural frequencies in electronics
More informationAutodesk Helius PFA. Guidelines for Determining Finite Element Cohesive Material Parameters
Autodesk Helius PFA Guidelines for Determining Finite Element Cohesive Material Parameters Contents Introduction...1 Determining Cohesive Parameters for Finite Element Analysis...2 What Test Specimens
More informationStress in Flip-Chip Solder Bumps due to Package Warpage -- Matt Pharr
Stress in Flip-Chip Bumps due to Package Warpage -- Matt Pharr Introduction As the size of microelectronic devices continues to decrease, interconnects in the devices are scaling down correspondingly.
More informationModeling of Interfacial Debonding Induced by IC Crack for Concrete Beam-bonded with CFRP
Proceedings of the World Congress on Engineering 21 Vol II WCE 21, June 2 - July 1, 21, London, U.K. Modeling of Interfacial Debonding Induced by IC Crack for Concrete Beam-bonded with CFRP Lihua Huang,
More informationReliability assessment for Cu/Low-k structure based on bump shear modeling and simulation method
Reliability assessment for Cu/Low-k structure based on bump shear modeling and simulation method Abstract Bump shear is widely used to characterize interface strength of Cu/low-k structure. In this work,
More informationMulti Disciplinary Delamination Studies In Frp Composites Using 3d Finite Element Analysis Mohan Rentala
Multi Disciplinary Delamination Studies In Frp Composites Using 3d Finite Element Analysis Mohan Rentala Abstract: FRP laminated composites have been extensively used in Aerospace and allied industries
More informationAdhesive Joints Theory (and use of innovative joints) ERIK SERRANO STRUCTURAL MECHANICS, LUND UNIVERSITY
Adhesive Joints Theory (and use of innovative joints) ERIK SERRANO STRUCTURAL MECHANICS, LUND UNIVERSITY Wood and Timber Why I m intrigued From this to this! via this Fibre deviation close to knots and
More informationStudy of Reliability Test Methods for Die-attach Joints on Power Semiconductors
Technology Report Study of Reliability Test Methods for Die-attach Joints on Power Semiconductors Kazunobu Arii, Yuichi Aoki and Kuniaki Takahashi Test Consulting Service Headquarters, ESPEC CORP. Abstract
More informationShorter Field Life in Power Cycling for Organic Packages
Shorter Field Life in Power Cycling for Organic Packages S. B. Park e-mail: sbpark@binghamton.edu Izhar Z. Ahmed Department of Mechanical Engineering, State University of New York at Binghamton, Binghamton,
More informationCopyright 2008 Year IEEE. Reprinted from IEEE TRANSACTIONS ON COMPONENTS AND PACKAGING TECHNOLOGIES, VOL. 31, NO. 1, MARCH Such permission of
Copyright 2008 Year IEEE. Reprinted from IEEE TRANSACTIONS ON COMPONENTS AND PACKAGING TECHNOLOGIES, VOL. 31, NO. 1, MARCH 2008. Such permission of the IEEE does not in any way imply IEEE endorsement of
More informationAn Engelmaier Model for Leadless Ceramic Chip Devices with Pb-free Solder
An Engelmaier Model for Leadless Ceramic Chip Devices with Pb-free Solder Nathan Blattau and Craig Hillman DfR Solutions 5110 Roanoke Place, Suite 101 College Park, MD 20740 nblattau@dfrsolutions.com ABSTRACT
More informationDrop Impact Reliability Test and Failure Analysis for Large Size High Density FOWLP Package on Package
2017 IEEE 67th Electronic Components and Technology Conference Drop Impact Reliability Test and Failure Analysis for Large Size High Density FOWLP Package on Package Zhaohui Chen, Faxing Che, Mian Zhi
More informationModeling Fracture and Failure with Abaqus
Modeling Fracture and Failure with Abaqus Day 1 Lecture 1 Lecture 2 Lecture 3 Workshop 1 Workshop 2 Basic Concepts of Fracture Mechanics Modeling Cracks Fracture Analysis Crack in a Three-point Bend Specimen
More informationThermal experimental & simulation investigations on new lead frame based LED packages.
Thermal experimental & simulation investigations on new lead frame based LED packages. B. Pardo, A. Piveteau, J. Routin, S, A. Gasse, T. van Weelden* CEA-Leti, MINATEC Campus, 17 rue des Martyrs, 38054
More informationEmergent properties in interface mechanical problems:
IMT Institute for Advanced Studies March 5, 2013, Lucca, Italy Emergent properties in interface mechanical problems: A paradigm of organized complexity Dr. Ing. Marco Paggi Politecnico di Torino Centre
More information314 IEEE TRANSACTIONS ON ADVANCED PACKAGING, VOL. 33, NO. 2, MAY Wei Tan, I. Charles Ume, Ying Hung, and C. F. Jeff Wu
314 IEEE TRANSACTIONS ON ADVANCED PACKAGING, VOL. 33, NO. 2, MAY 2010 Effects of Warpage on Fatigue Reliability of Solder Bumps: Experimental and Analytical Studies Wei Tan, I. Charles Ume, Ying Hung,
More informationStatic and Time Dependent Failure of Fibre Reinforced Elastomeric Components. Salim Mirza Element Materials Technology Hitchin, UK
Static and Time Dependent Failure of Fibre Reinforced Elastomeric Components Salim Mirza Element Materials Technology Hitchin, UK Introduction Fibre reinforced elastomers are used in many applications,
More informationThermo-structural Model of Stacked Field-programmable Gate Arrays (FPGAs) with Through-silicon Vias (TSVs)
Manuscript for Review Thermo-structural Model of Stacked Field-programmable Gate Arrays (FPGAs) with Through-silicon Vias (TSVs) Journal: Electronics Letters Manuscript ID: draft Manuscript Type: Letter
More informationFlexible Termination Reliability in Stringent Environments
Flexible Termination Reliability in Stringent Environments John Prymak, Corey Antoniades, Peter Blais, Allen Hill, Ken Lai, Mark Laps, Kevin Lynn, Reggie Phillips, Cory Riedl, Axel Schmidt, Bill Sloka,
More informationNUMERICAL INVESTIGATION OF DELAMINATION IN L-SHAPED CROSS-PLY COMPOSITE BRACKET
NUMERICAL INVESTIGATION OF DELAMINATION IN L-SHAPED CROSS-PLY COMPOSITE BRACKET M.Gümüş a*, B.Gözlüklü a, D.Çöker a a Department of Aerospace Eng., METU, Ankara, Turkey *mert.gumus@metu.edu.tr Keywords:
More informationInternational Power, Electronics and Materials Engineering Conference (IPEMEC 2015)
International Power, Electronics and Materials Engineering Conference (IPEMEC 015) Research Based on Cohesive Zone Model for Interface Delamination of Waste Plastic Chip Xueping Liu 1, a, Zufu Pang 1,,b,
More informationReliability of 3D IC with Via-Middle TSV: Characterization and Modeling
Reliability of 3D IC with Via-Middle TSV: Characterization and Modeling Victor Moroz *, Munkang Choi *, Geert Van der Plas, Paul Marchal, Kristof Croes, and Eric Beyne * Motivation: Build Reliable 3D IC
More informationReliability Study of Subsea Electronic Systems Subjected to Accelerated Thermal Cycle Ageing
, July 2-4, 2014, London, U.K. Reliability Study of Subsea Electronic Systems Subjected to Accelerated Thermal Cycle Ageing Sabuj Mallik and Franziska Kaiser Abstract Reliability is of increasing importance
More informationA 3D Discrete Damage Modeling Methodology for Abaqus for Fatigue Damage Evaluation in Bolted Composite Joints
A 3D Discrete Damage Modeling Methodology for Abaqus for Fatigue Damage Evaluation in Bolted Composite Joints Eugene Fang 1, Ling Liu 1, Michael Stuebner 1, Jim Lua 1 1 Global Engineering and Materials,
More informationBoundary Condition Dependency
Boundary Condition Dependency of Junction to Case Thermal Resistance Introduction The junction to case ( ) thermal resistance of a semiconductor package is a useful and frequently utilized metric in thermal
More informationImpact of BGA Warpage on Quality. Mike Varnau
Impact of BGA Warpage on Quality Mike Varnau 5-11-06 Contents What is a Ball in Cup Failure Case Study Background Problem Identification Solution Results Assembly Related Factors Causing Ball in Cup Component
More informationInfluence of Plating Quality on Reliability of Microvias
As originally published in the IPC APEX EXPO Conference Proceedings. Influence of Plating Quality on Reliability of Microvias Yan Ning, Michael H. Azarian, and Michael Pecht Center for Advanced Life Cycle
More informationChapter 7 Mechanical Characterization of the Electronic Packages
Chapter 7 Mechanical Characterization of the Electronic Packages 1 3 Thermal Mismatch Si (CTE=~3 ppm/c) Underfill (CTE=7 ppm/c) EU solder (CTE=5 ppm/c) Substrate (CTE=15~0 ppm/c) Thermal mismatch in electronic
More informationKey words Lead-free solder, Microelectronic packaging, RF packaging, RoHS compliant, Solder joint reliability, Weibull failure distribution
Solder Joint Reliability Assessment for a High Performance RF Ceramic Package Paul Charbonneau, Hans Ohman, Marc Fortin Sanmina Corporation 500 Palladium Dr. Ottawa, Ontario K2V 1C2 Canada Ph: 613-886-6000;
More informationMLCC with FLEXITERM. General Specifications GENERAL DESCRIPTION APPLICATIONS PRODUCT ADVANTAGES HOW TO ORDER
General Specifications GENERAL DESCRIPTION With increased requirements from the automotive industry for additional component robustness, AVX recognized the need to produce a MLCC with enhanced mechanical
More informationComputational Analysis for Composites
Computational Analysis for Composites Professor Johann Sienz and Dr. Tony Murmu Swansea University July, 011 The topics covered include: OUTLINE Overview of composites and their applications Micromechanics
More informationF. G. Marín, D Whalley, H Kristiansen and Z. L. Zhang, Mechanical Performance of Polymer Cored BGA Interconnects, Proceedings of the 10th Electronics
F. G. Marín, D Whalley, H Kristiansen and Z. L. Zhang, Mechanical Performance of Polymer Cored BGA Interconnects, Proceedings of the 1th Electronics Packaging Technology Conference, 28. Mechanical Performance
More informationInterlaminar fracture characterization in composite materials by using acoustic emission
5th International Symposium on NDT in Aerospace, 13-15th November 2013, Singapore Interlaminar fracture characterization in composite materials by using acoustic emission Ian SILVERSIDES 1, Ahmed MASLOUHI
More informationTHE demand for plastic packages has increased due to
294 IEEE TRANSACTIONS ON COMPONENTS AND PACKAGING TECHNOLOGIES, VOL. 30, NO. 2, JUNE 2007 Predictive Model for Optimized Design Parameters in Flip-Chip Packages and Assemblies Seungbae Park, H. C. Lee,
More informationTracker Tower 01 Prototype Test & Analysis Overview
Tracker Tower 01 Prototype Test & Analysis Overview Erik Swensen June 19, 2002 HPS-102070-0002 Test Background Design Philosophy: Tracker Tower 01 Prototype was used as an engineering evaluation model
More informationFracture Behavior. Section
Section 6 Fracture Behavior In January 1943 the one-day old Liberty Ship, SS Schenectady, had just completed successful sea trials and returned to harbor in calm cool weather when... "Without warning and
More informationThermal Characterization of Packaged RFIC, Modeled vs. Measured Junction to Ambient Thermal Resistance
Thermal Characterization of Packaged RFIC, Modeled vs. Measured Junction to Ambient Thermal Resistance Steven Brinser IBM Microelectronics Abstract Thermal characterization of a semiconductor device is
More informationMMJ1133 FATIGUE AND FRACTURE MECHANICS A - INTRODUCTION INTRODUCTION
A - INTRODUCTION INTRODUCTION M.N.Tamin, CSMLab, UTM Course Content: A - INTRODUCTION Mechanical failure modes; Review of load and stress analysis equilibrium equations, complex stresses, stress transformation,
More informationTutorial - Basic Operation of FLO/STRESS
of FLO/STRESS Introduction FLO/STRESS is intended to provide a fast, accurate stress prediction within the product design cycle. It is intended to provide the thermal designer with a greater understanding
More informationSKIN-STRINGER DEBONDING AND DELAMINATION ANALYSIS IN COMPOSITE STIFFENED SHELLS
SKIN-STRINER DEBONDIN AND DELAMINATION ANALYSIS IN COMPOSITE STIFFENED SHELLS R. Rikards, K. Kalnins & O. Ozolinsh Institute of Materials and Structures, Riga Technical University, Riga 1658, Latvia ABSTRACT
More informationISSN: ISO 9001:2008 Certified International Journal of Engineering Science and Innovative Technology (IJESIT) Volume 2, Issue 4, July 2013
Delamination Studies in Fibre-Reinforced Polymer Composites K.Kantha Rao, Dr P. Shailesh, K. Vijay Kumar 1 Associate Professor, Narasimha Reddy Engineering College Hyderabad. 2 Professor, St. Peter s Engineering
More informationThis guide is made for non-experienced FEA users. It provides basic knowledge needed to start your fatigue calculations quickly.
Quick Fatigue Analysis Guide This guide is made for non-experienced FEA users. It provides basic knowledge needed to start your fatigue calculations quickly. Experienced FEA analysts can also use this
More informationRELIABILITY STUDY OF POWER MODULE BY STOCHASTIC UNCERTAINTY METHOD FOR AN AERONAUTICAL APPLICATION
26 TH INTERNATIONAL CONGRESS OF THE AERONAUTICAL SCIENCES RELIABILITY STUDY OF POWER MODULE BY STOCHASTIC UNCERTAINTY METHOD FOR AN A. Micol a, T. Lhommeau b, R. Meuret c, C. Martin a, M. Mermet-Guyennet
More informationLecture #7: Basic Notions of Fracture Mechanics Ductile Fracture
Lecture #7: Basic Notions of Fracture Mechanics Ductile Fracture by Dirk Mohr ETH Zurich, Department of Mechanical and Process Engineering, Chair of Computational Modeling of Materials in Manufacturing
More informationMLCC with FLEXITERM. General Specifications GENERAL DESCRIPTION APPLICATIONS PRODUCT ADVANTAGES HOW TO ORDER C 104 K A Z 2 A
General Specifications GENERAL DESCRIPTION With increased requirements from the automotive industry for additional component robustness, AVX recognized the need to produce a MLCC with enhanced mechanical
More informationNumerical simulation of delamination onset and growth in laminated composites
Numerical simulation of delamination onset and growth in laminated composites G. Wimmer, C. Schuecker, H.E. Pettermann Austrian Aeronautics Research (AAR) / Network for Materials and Engineering at the
More informationFCP Short Course. Ductile and Brittle Fracture. Stephen D. Downing. Mechanical Science and Engineering
FCP Short Course Ductile and Brittle Fracture Stephen D. Downing Mechanical Science and Engineering 001-015 University of Illinois Board of Trustees, All Rights Reserved Agenda Limit theorems Plane Stress
More informationA generalised damage model for constant amplitude fatigue loading
A generalised damage model for constant amplitude fatigue loading of adhesively bonded joints H. Khoramishad a, A.D. Crocombe a,1, K.B. Katnam a and I.A. Ashcroft b a Mechanical, Medical and Aerospace
More informationMODELLING MIXED-MODE RATE-DEPENDENT DELAMINATION IN LAYERED STRUCTURES USING GEOMETRICALLY NONLINEAR BEAM FINITE ELEMENTS
PROCEEDINGS Proceedings of the 25 th UKACM Conference on Computational Mechanics 12-13 April 217, University of Birmingham Birmingham, United Kingdom MODELLING MIXED-MODE RATE-DEPENDENT DELAMINATION IN
More informationCohesive Band Model: a triaxiality-dependent cohesive model inside an implicit non-local damage to crack transition framework
University of Liège Aerospace & Mechanical Engineering MS3: Abstract 131573 - CFRAC2017 Cohesive Band Model: a triaxiality-dependent cohesive model inside an implicit non-local damage to crack transition
More informationFatigue Life Evaluation of Lead-free Solder under Thermal and Mechanical Loads
Fatigue Life Evaluation of Lead-free Solder under Thermal and Mechanical Loads Ilho Kim and Soon-Bok Lee* Department of Mechanical Engineering, Korea Advanced Institute of Science and Technology 373-,
More informationEffects of Stresses in Highly Accelerated Limit Test (HALT)
Technical Report Effects of Stresses in Highly Accelerated Limit Test (HALT) Takuya Hirata, Raphael Pihet and Yuichi Aoki, Development Headquarters, ESPEC CORP. Abstract The effects of vibration stress
More informationTCAD Modeling of Stress Impact on Performance and Reliability
TCAD Modeling of Stress Impact on Performance and Reliability Xiaopeng Xu TCAD R&D, Synopsys March 16, 2010 SEMATECH Workshop on Stress Management for 3D ICs using Through Silicon Vias 1 Outline Introduction
More informationFriction and Elongation of Al Electrodes due to Micro-Sliding between the Inner Mo Electrode and the Al Electrodes in High-Power Devices
Materials Transactions, Vol. 43, No. 9 (2002) pp. 2326 to 2330 c 2002 The Japan Institute of Metals EXPRESS REGULAR ARTICLE Friction and Elongation of Al Electrodes due to Micro-Sliding between the Inner
More informationSuper Bright LEDs, Inc.
Package Dimensions Notes: 1.All dimensions are in millimeters 2.Tolerances unless dimensions ±0.25mm Absolute Maximum Ratings (Ta=25 ) Parameter Symbol Rating Unit Forward Current I F 700 ma Reverse Voltage
More informationThermal Management of SMT LED Application Note
hermal Management of SM LED Application Note Introduction o achieve reliability and optimal performance of LED Light sources a proper thermal management design is necessary. Like all electronic components,
More informationVariational phase field model for dynamic brittle fracture
Variational phase field model for dynamic brittle fracture Bleyer J., Roux-Langlois C., Molinari J-F. EMMC 15, September 8th, 2016 1 / 18 Outline Mechanisms of dynamic fracture Variational phase-field
More informationCohesive band model: a triaxiality-dependent cohesive model for damage to crack transition in a non-local implicit discontinuous Galerkin framework
University of Liège Aerospace & Mechanical Engineering Cohesive band model: a triaxiality-dependent cohesive model for damage to crack transition in a non-local implicit discontinuous Galerkin framework
More informationNumerical Simulation of the Mode I Fracture of Angle-ply Composites Using the Exponential Cohesive Zone Model
Numerical Simulation of the Mode I Fracture of Angle-ply Composites Using the Exponential Cohesive Zone Model Numerical Simulation of the Mode I Fracture of Angle-ply Composites Using the Exponential Cohesive
More information