CONSTRUCTION MATERIALS T E C H N O L O G I E S LABORATORY TEST REPORT Report for: 6 Cherry Ave Penticton, BC VA L7 Canada Product(s): Deksmart Ultra 68mil Decking Membrane Manufacturer: O Sullivan Films, Inc. Date Received: Aug. 7, 07 Sampling: Client provided samples PRI-CMT Project No.: DKSM-00-0-0 Dates: Aug. 9, 07 Apr., 08 Purpose: Evaluate the physical properties for compliance with 7.-9 Polyvinyl Chloride Roofing and Waterproofing Membrane Type III, Class B. Type III products are defined as with a non-embedded fabric backing. Class B is defined as exposed roofing. s: ing was completed in compliance with 7.-9 Polyvinyl Chloride Roofing and Waterproofing Membrane. methods assigned or referenced include 70: Standard for Water Absorption of Plastics; 7: Standard for Coated Fabrics; 790: Standard for Brittleness Temperature of Plastic Sheeting by Impact; 6: Standard for Coated Fabrics Low Temperature Bend ; 6: Standard Practice for Xenon-Arc Exposure of Plastics Intended for Outdoor Applications; ASTM E 96/E 96M: Standard s for Water Vapor Transmission of Materials; and Waterproofing Materials; and ASTM G : Standard Practice for Operating Light- and Water-Exposure Apparatus (Fluorescent UV-Condensate Type) for Exposure of Nonmetallic Materials. Sampling: A roll of PVC decking membrane was provided in the color Silver Maple Plank for testing by the O Sullivan Films, Inc. from Winchester, VA on August 7, 07. DKSM-00-0-0 The test results, opinions, or interpretations are based on the material supplied by the client. This report is for the exclusive use of stated client. No reproduction or facsimile in any form can be made without the client's permission. This report shall not be reproduced except in full without the written approval of this laboratory. PRI Construction Materials Technologies LLC assumes no responsibility nor makes a performance or warranty statement for this material or products and processes containing this material in connection with this report. PRI Construction Materials Technologies LLC 6 Badger Drive Tampa, FL 60 Tel: 8-6-777 Fax: 8-6-80 e-mail: materialstesting@pricmt.com WebSite: http://www.pricmt.com
7.-9 Page of 8 : Thickness, (mm) Overall; 7.0...0.0.0 0.0. Thickness, (mm) Over scrim 7.-9 No individual measurement less than 0. N/A N/A N/A N/A N/A N/A N/A 0. Breaking Strength, (kn/m) specimens each direction; 0 x mm @ ± C & 0±%RH; Rate = ± mm/s 7 MD 9 CMD 7 0 Elongation at Break, (%) specimens each direction; 0 x mm @ ± C & 0±%RH; Rate = ± mm/s 7 PVC matrix intact at break MD 9 7 9 7 CMD 9 DKSM-00-0-0 PRI Construction Materials Technologies LLC 6 Badger Drive Tampa, FL 60 Tel: 8-6-777 Fax: 8-6-80 e-mail: materialstesting@pricmt.com WebSite: http://www.pricmt.com
6 7 8 9 0 7.-9 Page of 8 Lap Joint Strength, (% of Breaking Strength) specimens; 0 x mm; @ ± C & 0±%RH; Rate = ± mm/s 7 Initial with no shearing of lap joint 06 09 0 09 7 After 7 days in boiling water with no delamination 96 0 98 96 98 98 70 Low Temperature Impact, (# of passing specimens) 0 specimens; Cond. 90 min @ -0± C; @ -0± C; 790 8 of 0 specimens shall pass Low Temperature Flexibility, (/Fail) specimens; Cond. h @ -0± C; @ -0± C; Bend 80 over. mm Ø steel rod 6 Water Vapor Transmission, (g/m in h) specimens; @ ± C & 0±% RH ASTM E 96 Procedure A 0.7 0.7 0.6 0.7 0.0.0 DKSM-00-0-0 PRI Construction Materials Technologies LLC 6 Badger Drive Tampa, FL 60 Tel: 8-6-777 Fax: 8-6-80 e-mail: materialstesting@pricmt.com WebSite: http://www.pricmt.com
7.-9 Page of 8 Retention of Properties after Heat Aging, After 60 days at 80± C; 8h recovery 7.-9 Breaking Strength MD, (% of original) specimens each direction; 0 x mm @ ± C & 0±%RH; Rate = ± mm/s 7 MD 0 9 08 7 9 0 90 CMD 6 7 7 08 6 6 90 Elongation at Break, (% of original) specimens each direction; 0 x mm @ ± C & 0±%RH; Rate = ± mm/s 7 PVC matrix intact at break MD 8 7 97 9 97 90 CMD 99 0 90 Low Temperature Flexibility, (/Fail) specimens; Cond. h @ -0± C; @ -0± C; Bend 80 over. mm Ø steel rod 6 DKSM-00-0-0 PRI Construction Materials Technologies LLC 6 Badger Drive Tampa, FL 60 Tel: 8-6-777 Fax: 8-6-80 e-mail: materialstesting@pricmt.com WebSite: http://www.pricmt.com
6 7 8 9 0 7.-9 Page of 8 Retention of Properties after Accelerated Weathering, UVA-0 bulbs; 8h light; h condensate; Black panel temp. 6± C; Condensate temp. 0± C; ASTM G Visual Inspection 7.-9 No cracking, blistering, or appreciable color change Elongation at Break, (% of original) specimens CMD direction; 0 x mm @ ± C & 0±%RH; Rate = ± mm/s 7 PVC matrix intact at break 9 97 87 9 9 9 90 Low Temperature Impact, (# of passing specimens) 0 specimens; Cond. 90 min @ -0± C; @ -0± C; 790 8 of 0 specimens shall pass Low Temperature Flexibility, (/Fail) specimens; Cond. h @ -0± C; @ -0± C; Bend 80 over 6. mm Ø steel rod 6 DKSM-00-0-0 PRI Construction Materials Technologies LLC 6 Badger Drive Tampa, FL 60 Tel: 8-6-777 Fax: 8-6-80 e-mail: materialstesting@pricmt.com WebSite: http://www.pricmt.com
7.-9 Page 6 of 8 Effect of Water Absorption After immersion for 7 days at 70± C Mass Increase, (% of original) 70 -. -. -.6 -. 0..0 Breaking Strength MD, (% of original) specimens each direction; 0 x mm @ ± C & 0±%RH; Rate = ± mm/s 7 MD 06 0 00 96 9 00 90 CMD 87 09 8 0 08 90 Elongation at Break, (% of original) specimens each direction; 0 x mm @ ± C & 0±%RH; Rate = ± mm/s 7 PVC matrix intact at break MD 06 98 87 09 6 90 CMD 88 8 0 0 90 DKSM-00-0-0 PRI Construction Materials Technologies LLC 6 Badger Drive Tampa, FL 60 Tel: 8-6-777 Fax: 8-6-80 e-mail: materialstesting@pricmt.com WebSite: http://www.pricmt.com
Left Center Right 7.-9 Page 7 of 8 Dimensional Change, (%) After 6 h at 80± C; Without Loading; 7.-9 MD -0. -0. -0. -0. -0. -0. 0.0 0. CMD 0. 0. 0.0 0.0 0. 0. 0. 0. Dimensional Change, (%) After 6 h at 80± C; With Loading; 7.-9 MD -0. 0.0-0. -0. 0.0 0. CMD 0.0 0.0 0. 0.0 0.0 0. Cone Penetration, (N) specimens; 0 x 0 mm; @ ± C & 0±%RH; Rate =.7 mm/min 7.-9 89 80 8 90 99 88 7 0 DKSM-00-0-0 PRI Construction Materials Technologies LLC 6 Badger Drive Tampa, FL 60 Tel: 8-6-777 Fax: 8-6-80 e-mail: materialstesting@pricmt.com WebSite: http://www.pricmt.com
7.-9 Page 8 of 8 Statement of Compliance: The product tested has demonstrated compliance with the physical property requirements of 7.-9 Polyvinyl Chloride Roofing and Waterproofing Membrane Type III, Class B. The laboratory test results presented in this report are representative of the material supplied. Signed: Zachary Priest, P.E. Director Report Issue History: Issue # Date Pages Revision Description (if applicable) Original 0/0/08 8 NA END OF REPORT DKSM-00-0-0 PRI Construction Materials Technologies LLC 6 Badger Drive Tampa, FL 60 Tel: 8-6-777 Fax: 8-6-80 e-mail: materialstesting@pricmt.com WebSite: http://www.pricmt.com