1 arxiv: v1 [cond-mat.supr-con] 21 Sep 2015 Two-gap superconducting properties of alkaline-earth intercalated A x (A = Ba or Sr) Yung-Yuan Hsu yungyuan.hsu@gmail.com Yu-Bo Li njvulfu761218@yahoo.com.tw Shou-Ting Jian drizzle @hotmail.com Gu-Kuei Li tracephysics@hotmail.com Ming-Cheng Yang hulumiow@gmail.com Abstract. Superconducting properties were studied on high quality superconductors Ba x (T c = 39 K) and Sr x (T c = 44 K) prepared by intercalating Ba/Sr atoms into tetragonal β-fese by liquid ammonia. The elongated c-axis and almost unchanged a-axis of Ba x, comparing with β-fese, suggested an unchanged intra-fe 2 -layer structure and the T c enhancement is due to a 3D to 2D-like Fermi surface transformation. The superconducting coherent lengths ξ(0), Ginzburg-Landau parameters κ and penetration depths λ(0) obtained from the extrapolated lower and upper critical fields B c1 (0) and B c2 (0) indicates that both compounds are typical type-ii superconductors. The temperature dependence of 1/λ 2 (T) of Ba x deduced from the low field magnetic susceptibility
2 Two-gap superconducting properties of intercalated iron-selenides 2 shows a two-gap s-wave behaviour with superconducting gaps of 1 = 6.47 mev and 2 = 1.06 mev. Keywords: iron chacogenide, two-gap s-wave superconductor, alkaline-earth intercalated FeSe, penetration depth, Ginzburg-Landau parameter 1. Introduction Since the discovery of iron-based superconductors in 2008 [1], the T c 8 K superconducting β-fese[2] has attracted much interest duo to its simple lattice structure and sharing a common electronic origin for superconducting mechanism with the much complicated iron-arsenide systems [3, 4]. The T c of iron-selenide can be raised upto 14.5 K by tellurium partial substitution on selenium site [5]. A break through of the iron-selenides system was achieved by the discovery of superconductors A 1 x Fe 2 y (A = K, Rb, Cs or Tl, FeSe-122) [6, 7] for their high T c 32 K and being a direct comparison system in electronic structure with iron-arsenide 122 systems(feas-122) and relative pnictide systems [8, 9, 10]. However, the unavoidable nano-scaled coexistence of antiferromagnetic insulated 245-phases (T N = K) inside the superconducting FeSe-122 phase interferes the discussions of fundamental superconducting and electronic properties [8, 9, 10, 11, 12, 13]. Recently, an exciting development about pure superconductors with T c up to 46 K were reported for metal intercalated iron-selenides by ammonothermal reaction [14, 15]. The neutron diffraction studies indicated that ammonia molecules were inserted together with lithium atoms in-between the Fe 2 -layers in the T c = 43 K Li x superconductor [15]. It has been found that T c of the iron-selenides systems increases with an increasing adjacent Fe 2 -layers distance [16]. On the other hand, structural variations of intra-fe 2 -layer and electron doping as the origin of T c enhancement after the Li and NH 3 intercalation is also reported. [15, 17]. In this report, structural and superconducting properties of A x (A = Ba or Sr) were studied. The structural analysis suggested that the intra-fe 2 -layer structure of Ba x remains the same as the parent superconducting FeSe compound. The enhancement of T c could be attributed to the more 2D-like electronic structure by shortened Brillouin zone z-axis due to inter-fe 2 -layer intercalation. Superconducting parameters, coherence length ξ(0), penetration depth λ(0), and Ginzburg-Landau parameter κ extracted from magnetic measurements indicates both systems are typical type-ii superconductors. Furthermore, superfluid density n s λ 2 (T) of Ba x is found to be well described by a two-gap s-wave model similar to that of the parent compound [18].
3 Two-gap superconducting properties of intercalated iron-selenides 3 2. Experimental High quality powder samples of A x (A = Ba, Sr) were synthesized by intercalating Ba (or Sr) atoms into tetragonal β-fese using liquid ammonia (LA) [14, 15]. First, high-purity superconducting β-fese was prepared by high temperature reactions [2]. Iron granules (99.98%) and selenium shots (99.999%) with 1.008:1 molar ratio were placed in an alumina crucible and sealed in a quartz tube. The tube was slowly heated to 750 C and held 1 day for complete reaction, then melted by heating to 1080 C followed by quenching to 420 C and held for 2 days for pure β phase. The intercalating reaction was carried out by placing β-fese powder with Ba (99.7%) or Sr (99%) metal in a 4:1 molar ratio in an evacuated autoclave cooled in a liquid nitrogen bath [14]. Gaseous ammonia was slowly condensed into liquid until a Ba/Sr in LA concentration of at% was reached. The vessel was kept at room temperature and magnetically stirred for 3 days. The obtained fine sample powders were then pressed into pellets and encapsulated by epoxy to prevent sample degradation due to ammonia escape. The lattice structure analysis was carried out by X- ray diffraction with a PHILIPS X PERT diffractometer for 2θ range of 5-60 degree. The magnetic measurements were carried out by a QUANTUM DESIGN MPMS2 SQUID magnetometer with temperature down to 5 K and applied magnetic field up to 1 T. 3. Results and discussions Intensity (arb. unit) (0 0 2) v (0 0 2) (0 0 4) (1 0 1) (1 0 3) v Ba x (1 1 0) H Fe 2 O 3 (1 1 4) v H (1 0 7) Sr x (1 1 6) (2 0 0) (2 0 2) a = Å c = Å (2 1 1) (2 1 3) a = Å c = Å (0 0 4) (1 0 1) (1 0 3) (2 0 0) * * * (degree) Figure 1. Powder X-ray diffraction patterns of Ba x (upper panel) and Sr x (lower panel). The small peaks corresponding to hexagonal δ-fese are labeled by H, iron oxide by Fe 2 O 3 and unknown phases by asteroids. Thepowder X-raydiffractionpatternsofA x (A=BaorSr), asshown in Figure 1, can be well indexed by body-centered-tetragonal (bct) Li type structure (space group: I4/mmm) [15]. Minor phases of impurities were barely observedforhexagonalfese(markedby H andironoxide(by Fe 2 O 3 ), andunknown phases (by asteroids). No trace of superconducting precursor β-fese was observed. The derived lattice parameters for A = Ba are a = nm and c = nm, and for A = Sr are a = nm and c = nm. The greatly elongated c-axes
4 Two-gap superconducting properties of intercalated iron-selenides 4 observed are consistent with the literatures and can be attributed to NH 3 molecules co-intercalation [14, 15, 19, 20]. Lager lattice parameters and unit cell volume observed for Sr-compound (V = nm 3 ) than Ba-compound (V = nm 3 ) suggests a higher content of intercalated metal atoms in the former, which is consistent with the preliminary refinement results that the stoichiometric parameter x of 0.25 and 0.4 for A = Ba and Sr, respectively. However, due to the signal to noise ratio of the XRD data is not conclusive enough, we left the Ba/Sr content as undetermined in the following discussion. g (10-3 emu/g G) FC FC A x T c = 44 K -3 ZFC A = Ba 0 B a = 1 T 39 K kg 38.5 K T -5 c = 37 K ZFC A = Sr G -6 A = Ba B a = 10 G T g ( 10-3 ) Temperature (K) T c = 39 K Figure 2. Low apply field (B a = 10 G) diamagnetic mass susceptibility χ g (T) of superconducting Ba x and Sr x in zero-field-cooled (ZFC, solid symbols) and field-cooled (FC, open symbols) modes. An enhancement of diamagnetism below 14 K is attributed to the opening of smaller superconducting gap in the two-gapscenario. (Inset) Higher field (ZFC) χ g T curves of Ba x were used for B c2 (T) determination. The observed superconducting transition temperature T c for Ba x is 39 K and for Sr x is 44 K, as shown in Figure 2. A relatively large paramagnetic background was observed in the normal state, which could be attributed to the minor magnetic phases observed in XRD patterns. An enhancement of diamagnetism below14kcanbeclearlyobservedinba x. Thisphenomenonisattributed to the opening of second superconducting gap in the weak-coupling two-gap scenario. Similar behaviour was barely seen for Sr-compound due to its much larger particle sizes of the powder. Among all intercalated iron-selenides superconductors, the enhancement of T c to around 40 K is believed due to the c-axis expansion and carrier density tuning by atoms/molecules intercalation [2, 15, 19]. However, the almost unchanged a-axis length and very low content of inserted Ba in Ba x suggests that one can consider the Ba x as directly separating Fe 2 layers in β FeSe by the inserted atoms/molecules without changing its intra-layer structure. This insertion elongates the c-axis length which weakens the inter-fe 2 -layer coupling. Consequently, it shortens the corresponding Brillouin zone c*-axis length in the reciprocal space, which makes the Fermi surfaces more cylindrical and more two-dimensional-like assuming the band structure is mainly determined by the almost unchanged intra-fe 2 -layer
5 Two-gap superconducting properties of intercalated iron-selenides 5 structure [17]. Inset of figure 2 shows the higher-field χ g for Ba x which were measured right after the 10-G measurement to avoid any sample degradation problems. The observed T c determined by the deviation point from the normal state decreases slightly to 37 K for B a = 1 T. The magnitude of diamagnetic signal decreases rapidly with increasing applied field. The ZFC χ g (1 T) curve even did not change sign down to 5 K due to fine powder grand size of the sample powder and the strong paramagnetic background. magnetization M g (emu/g) B c1 (35 K) = 6 G Ba x T = 35 K T = 30 K 25 K 20 K B c1 (5 K) = 28 G 10 K 15 K applied field B a (G) Figure 3. Low field initial magnetization curves of superconducting Ba x at various temperature below T c = 39 K. The curves deviate from liner at B c1 as marked by arrows. The initial mass magnetization curves, M g (T), of Ba x was shown in figure 3. The lower critical field B c1 (T) determined by the deviation point from the low-field linear Meissner response. The obtained B c1 (T) decreases monotonically with increasing temperature from 28 G for T = 5 K, to 22 G for 20 K, and then to 6 G for 35 K. Measurements on Sr x also revealed a similar behavior of B c1 (T) decreased from B c1 (10 K) = 23 G, to B c1 (20 K) = 18 G, then to B c1 (30 K) = 12 G. The observed low B c1 values are comparable to those observed for B a c-axis in β-fese [21], despite their much higher T c s in these intercalated superconductors. The superconducting critical fields, B c1 (T) and B c2 (T), of Ba x obtained from magnetic measurements are summarized in a B a T phase diagram as shown in figure 4. The irreversible line, B irr, determined from the deviation points of ZFC and FC curves is also shown as a boundary between vortex glass and liquid states. The zero temperature lower critical field B c1 (0) 30 G was easily obtained by extrapolation. An empirical value of B c2 (0) = 13.4 T was obtained by using the Werthamer-Helfand-Hohenberg formula with a linear slope db c2 (T c )/dt = T/K. The Ginzburg-Landau parameter κ Ba = 102 was derived from these extrapolated B c2 (0) and B c1 (0) values by solving B c2 /B c1 = 2κ 2 /lnκ, which indicates that Ba x is a typical type-ii superconductor as expected. Since the superconducting coherent length ξ Ba (0) = 4.96 nm can be easily derived by using the formula B c2 = Φ 0 /2πξ 2, it is straight forward to calculate the magnetic field penetration depth λ Ba (0) = κξ(0) = 508
6 Two-gap superconducting properties of intercalated iron-selenides 6 applied field B a (G) 10 4 Ba x B c vortex glass B c1 vortex liquid 10 1 Meissner state T c (Ba) Temperature (K) B irr normal state Figure 4. The superconducting B a -T phase diagram of Ba x derived frommagneticmeasurements. TheB c1 (0) 30Gwasobtainedbysimple extrapolation and the linear fitting of B c2 (T) was shown by solid curves. The dashed line with B irr is only a guide to the eyes. nm. Similar analysis was performed onsr x and theobtained critical fields were B c2 (0) = 61.4 T and B c1 (0) = 24 G, by which the superconducting parameters κ Sr = 266, ξ Sr (0) = 2.33 nm, and λ Sr (0) = 620 nm were derived. -2 ( m -2 ) Ba x experimental data BCS gap two-gap model 1 = 6.47(12) mev = 1.06(9) mev T (K) Figure 5. The temperature dependence of 1/λ 2, proportional to superfluid density, of Ba x estimated from low-field magnetic susceptibility. The data can be well described by a two-gap s-wave model (solid brown curve) with a larger gap 1 = 6.47 mev and a smaller gap 2 = 1.06 mev. The dashed curves are the individual contributions of each gap. The single-gap BCS behavior is shown in green for comparison. To further investigate superconductivity of the system, temperature dependence of superfluid density, proportional and presented by 1/λ 2, of Ba x was estimated and plotted in figure 5. The London penetration depth λ(t) was derived by solving the equation χ(t) (1 3 λ r χ 0 = cot( r λ )+3λ2 r 2)r3 g(r)dr r 3 g(r)dr where χ 0 is the susceptibility of perfect diamagnetic spheres and g(r) is the grand size distribution function, which was obtained by counting sample powder grands under an optical microscope as g(r) = 95exp( ((logr + 0.5)/0.382) 2 ). A constant
7 Two-gap superconducting properties of intercalated iron-selenides 7 paramagnetic background was subtracted from the susceptibility for completely counting the diamagnetic signal. Since the 10-G applied field became larger than B c1 for temperature higher than 32 K, the penetration depth λ values obtained at those temperature were contaminated by vortex formation, thus 1/λ 2 data for T > 32 K were excluded for further discussion. At the low temperature side, 1/λ 2 for temperature below 15 K apparently deviated from the saturation behaviour of conventional BCS single-gap model. Referring to similar systems, [18, 22] two-gap model was used for analysis and consistent results were obtained. The temperature dependence of the penetration depth of Ba x was fitted by a weakly coupled two-gap s-wave model [21, 22, 23] λ 2 (T) = (T, 1 ) (T, 2 ) λ 2 (0) ωλ 2 λ (0, 1 ) +(1 ω)λ 2 λ 2 (0, 2 ) whereλ(0)isthezerotemperaturepenetrationdepth, i istheithsuperconducting gap at T = 0 K and ω is the weighting factor of the first gap [22]. Each component can be expressed within the local London approximation as λ 2 (T) = λ 2 (0) i ()( f ) EdE E E 2 i (T) 2 where f = 1/(1+exp(E/k B T)) is the Fermi function, and the temperature dependence of the gap is approximated as i (T) = i tanh1.82[1.018(t c /T 1)] [18] The two-gap s-wave model, the brown curve in figure 5, describes the temperature dependence of penetration depth very well. The zero temperature gaps values obtained for Ba x are 1 = 6.47 mev and 2 = 1.06 mev with ω = The derived gap to T c ratios of 2 1 /k B T c = 3.85 and 2 2 /k B T c = 0.63 are consistent with those in Li(C 2 H 5 N) 0.2 Fe 2 (T c = 40 K) [22] and Li 0.6 (T c = 43 K) [15]. The slightly bigger value for the 2 1 /k B T c, comparing with the BCS value of 2 0 /k B T c = 3.35, suggests that the weak-coupling assumption in the two-gap s-wave model used is a good approximation. Since our samples were randomly orientated powder, the influence of temperature variation of λ c (T) should be observed in diamagnetic susceptibility. However, by taking typical anisotropy of iron-selenide systems andtheobtainedλ(0), theestimated valueofλ c (0)isabout2µmwhich islarger thanmost ( 80%)grainsize of thepowder. When thec-axes of thesingle crystal grains have large angles to the applied magnetic field, magnetic field penetrates into the grains completely even at low temperature which makes the effects of temperature dependence are not observed. Thus the estimated λ(0) value of 506 nm could be regarded as the upper bound of λ ab (0) and the temperature dependence of 1/λ 2 represents the supercurrent behaviour in the Fe 2 -layer. In conclusion, superconducting properties of A x (A = Ba or Sr) were studied by magnetic measurements. The high T c after alkali-metal and ammonia molecule intercalation is due to a 3D-like to 2D-like Fermi surface change. Temperature dependence of the London penetration depth was derived from diamagnetic susceptibility for Ba x which is well described by a two-gap s-wave model with gap values 1 = 6.47 mev and 2 = 1.06 mev and λ(0) 506 nm.
8 Two-gap superconducting properties of intercalated iron-selenides 8 Acknowledgments This work was supported by the National Science Council of Taiwan under NSC M References [1] Y. Kamihara, T. Watanabe, M. Hirano, and H. Hosono, Iron-based layered superconductor La[O 1 x F x ]FeAs (x = ) with T c = 26 K, J. Am. Chem. Soc. 130 (2008) 3296 [2] T. M. McQueen, Q. Huang, V. Ksenofontov, C. Felser, Q. Xu, H. Zandbergen, Y. S. Hor, J. Allred, A. J. Williams, D. Qu, J. Checkelsky, N. P. Ong, and R. J. Cava, Extreme sensitivity of superconductivity to stoichiometry in Fe 1+δ Se, Phys. Rev. B 79 (2009) [3] J. Paglione and R. L. Greene, High-temperature superconductivity in iron-based materials, Nature Phys. 6 (2010) 645 [4] A. A. Kordyuk, Iron-based superconductors: Magnetism, superconductivity, and electronic structure, Low Temp. Phys. 38 (2012) 888 [5] K. W. Yeh, T. W. Huang, Y. L. Huang, T. K. Chen, F. C. Hsu, P. M. Wu, Y. C. Lee, Y. Y. Chu, C. L.Chen, J. Y. Luo, D. C. Yan, andm. K.Wu, Telluriumsubstitution effect on superconductivity of the α-phase iron selenide, Europhys. Lett. 84 (2008) [6] J. Guo, S. Jin, G. Wang, S. Wang, K. Zhu, T. Zhou, M. He. and X. Chen, Superconductivity in the iron selenide K x Fe 2 (0 x 1.0), Phys. Rev. B 82 (2010) [7] F. Ye, S. Chi, W. Bao, X. F. Wang, J. J. Ying, X. H. Chen, H. D. Wang, C. H. Dong, and M. H. Fang, Common crystalline and magnetic structure of superconducting A 2 Fe 4 Se 5 (A = K, Rb, Cs, Tl) single crystals measured using neutron diffraction, Phys. Rev. Lett. 107 (2011) [8] Z. W. Wang, Z. Wang, Y. J. Song, C. Ma, Y. Cai, Z. Chen, H. F. Tian, H. X. Yang, G. F. Chen, and J. Q. Li, Structural phase separation in K 0.8 Fe 1.6+x superconductors, J. Phys. Chem. C 116 (2012) [9] D. P. Shoemaker, D. Y. Chung, H. Claus, M. C. Francisco, S. Avci, A. Llobet, and M. G. Kanatzidis, Phase relations in K x Fe 2 y and the structure of superconducting K x Fe 2 via high-resolution synchrotron diffraction, Phys. Rev. B 86 (2012) [10] W. Li, H. Ding, P. Deng, K. Chang, C. Song, K. He, L. Wang, X. Ma, J. P. Hu, X. Chen, and Q. K. Xue, Phase separation and magnetic order in K-doped iron selenide superconductor, Nat. Phys. 8 (2012) 126 [11] F. Chen, M. Xu, Q. Q. Ge, Y. Zhang, Z. R. Ye, L. X. Yang, J. Jiang, B. P. Xie, R. C. Che, M. Zhang, A. F. Wang, X. H. Chen, D. W. Shen, J. P. Hu, and D. L. Feng, Electronic identification of the parental phases and mesoscopic phase separation of K x Fe 2 y superconductors Phys. Rev. X 1 (2011) [12] V. Ksenofontov, G. Wortmann, S. A. Medvedev, V. Tsurkan, J. Deisenhofer, A. Loidl, and C. Felser, Phase separation in superconducting and antiferromagnetic Rb 0.8 Fe 1.6 probed by Mössbauer spectroscopy, Phys. Rev. B 84 (2011) [13] R. H. Yuan, T. Dong, Y. J. Song, P. Zheng, G. F. Chen, J. P. Hu, J. Q. Li, and N. L. Wang, Nanoscalephase separationofantiferromagneticorderand superconductivity in K 0.75 Fe 1.75, Sci. Rep. 2 (2012) 221 [14] T. P. Ying, X. L. Chen, G. Wang, S. F. Jin, T. T. Zhou, X. F. Lai, H. Zhang, and W. Y. Wang, Observation of superconductivity at K in A x Fe 2 (A = Li, Na, Ba, Sr, Ca, Yb, and Eu), Sci. Rep. 2 (2012) 426 [15] M. Burrard-Lucas, D. G. Free, S. J. Sedlmaier, J. D. Wright, S. J. Cassidy, Y. Hara, A. J. Corkett, T. Lancaster, P. J. Baker, S. J. Blundell, and S. J. Clarke, Enhancement of the superconducting transition temperature of FeSe by intercalation of a molecular spacer layer, Nature Mater. 12 (2013) 15
9 Two-gap superconducting properties of intercalated iron-selenides 9 [16] A. M. Zhang, T. L. Xia, K. Liu, W. Tong, Z. R. Yang, and Q. M. Zhang, Superconductivity at 44 K in K intercalated FeSe system with excess Fe, Sci. Rep. 3 (2013) 1216 [17] A. Subedi, L. Zhang, D. J. Singh, and M. H. Du, Density functional study of FeS, FeSe, and FeTe: Electronic structure, magnetism, phonons, and superconductivity, Phys. Rev. B 78 (2008) [18] R. Khasanov, K. Conder, E. Pomjakushina, A. Amato, C. Baines, Z. Bukowski, J. Karpinski, S. Katrych, H.-H. Klauss, H. Luetkens, A. Shengelaya, and N. D. Zhigadlo, Evidence of nodelesssuperconductivityinfese 0.85 fromamuon-spin-rotationstudyofthein-planemagnetic penetration depth, Phys. Rev. B 78 (2008) [19] T. P. Ying, X. L. Chen, G. Wang, S. F. Jin, X. F. Lai, T. T. Zhou, H. Zhang, S. J. Shen, and W. Y. Wang, Superconducting phases in potassium-intercalated iron selenides, J. Am. Chem. Soc. 135 (2013) 2951 [20] S. Shibasaki, K. Ashida, Y. Takahei, K. Tomita, R. Kumai, and T. Kambe, Co-intercalation of Ammonia molecules between FeSe layers in Ba-doped FeSe superconductor arxiv:condmat/ (2008) [21] M. Abdel-Hafiez, J. Ge, A. N. Vasiliev, D. A. Chareev, J. Van de Vondel, V. V. Moshchalkov, and A. V. Silhanek, Temperature dependence of lower critical field H c1 (T) shows nodeless superconductivity in FeSe, Phys. Rev. B 88 (2013) [22] P. K. Biswas, A. Krzton-Maziopa, R. Khasanov, H. Luetkens, E. Pomjakushina, K. Conder, and A. Amato, Two-dimensional superfluid density in an alkali metal-organic solvent intercalated iron selenide superconductor Li(C 5 H 5 N) 0.2 Fe 2, Phys. Rev. Lett. 110 (2013) [23] A. Carrington, and F. Manzano, Magnetic penetration depth of MgB 2, Physica C 385 (2003) 205
New Li-Ethylenediamine-Intercalated Superconductor Li x (C 2 H 8 N 2 ) y Fe 2-z Se 2 with T c = 45 K
New Li-Ethylenediamine-Intercalated Superconductor Li x (C 2 H 8 N 2 ) y Fe 2-z Se 2 with T c = 45 K Takehiro Hatakeda, Takashi Noji, Takayuki Kawamata, Masatsune Kato, and Yoji Koike Department of Applied
More informationalkaline-metal-ethylenediamine-intercalated superconductors A x (C 2 H 8 N 2 ) y Fe 2-z Se 2 (A = Li, Na) with T c = 45 K
Synthesis and post-annealing effects of alkaline-metal-ethylenediamine-intercalated superconductors A x (C N Fe -z Se (A = Li, Na) with T c = K Takashi Noji, Takehiro Hatakeda, Shohei Hosono, Takayuki
More informationT. Hatakeda, T. Noji, S. Hosono, T. Kawamata, M. Kato, and Y. Koike
Resistive superconducting transition and effects of atmospheric exposure in the intercalation superconductor A x (A = Li, Na) T. Hatakeda, T. Noji, S. Hosono, T. Kawamata, M. Kato, and Y. Koike Department
More informationWe have investigated the effect of atomic substitutions in the FeSe system, which
Substitution Effects on FeSe Superconductor Yoshikazu Mizuguchi 1,2,3, Fumiaki Tomioka 1,3, Shunsuke Tsuda 1,3, Takahide Yamaguchi 1,3 and Yoshihiko Takano 1,2,3 1 National Institute for Materials Science,
More informationSuperconductivity at 41.0 K in the F-doped LaFeAsO 1-x F x
Superconductivity at 41.0 K in the F-doped LaFeAsO 1-x F x Wei Lu, Xiao-Li Shen, Jie Yang, Zheng-Cai Li, Wei Yi, Zhi-An Ren*, Xiao-Li Dong, Guang-Can Che, Li-Ling Sun, Fang Zhou, Zhong-Xian Zhao* National
More informationShohei Hosono, Takashi Noji, Takehiro Hatakeda, Takayuki Kawamata, Masatsune Kato, and Yoji Koike
New Superconducting Phase of Li x (C 6 H 16 N 2 ) y Fe 2-z Se 2 with T c = 41 K Obtained through the Post-Annealing Shohei Hosono, Takashi Noji, Takehiro Hatakeda, Takayuki Kawamata, Masatsune Kato, and
More informationHigh pressure synthesis of late rare earth RFeAs(O,F) superconductors; R = Tb and Dy.
High pressure synthesis of late rare earth RFeAs(O,F) superconductors; R = Tb and Dy. Jan-Willem G. Bos, a,b George B. S. Penny, a,b Jennifer A. Rodgers, a,b Dmitry A. Sokolov, a,c Andrew D. Huxley a,c
More informationT he discovery of superconductivity (SC) at about 30 K in 1 2,3
SUBJECT AREAS: CONDENSED MATTER PHYSICS SUPERCONDUCTIVITY SUPERCONDUCTING MATERIALS MATERIALS PHYSICS Received 19 April 2012 Accepted 10 May 2012 Published 28 May 2012 Correspondence and requests for materials
More informationKeywords: superconductivity, Fe-based superconductivity, FeTe, alcohol, wine
Superconductivity in FeTe1-xSx induced by alcohol Keita Deguchi 1,2,3, Yoshikazu Mizuguchi 1,2,3, Toshinori Ozaki 1,3, Shunsuke Tsuda 1,3, Takahide Yamaguchi 1,3 and Yoshihiko Takano 1,2,3 1. National
More informationSuperconductivity in oxygen-annealed FeTe 1-x S x single crystal
Superconductivity in oxygen-annealed FeTe 1-x S x single crystal Yoshikazu Mizuguchi 1,2,3, Keita Deguchi 1,2,3, Yasuna Kawasaki 1,2,3, Toshinori Ozaki 1,2, Masanori Nagao 4, Shunsuke Tsuda 1,2, Takahide
More informationSuperconductivity close to magnetic instability in Fe(Se 1 x Te x ) 0.82
Superconductivity close to magnetic instability in Fe(Se x M. H. Fang, H. M. Pham, 2 B. Qian, T. J. Liu, E. K. Vehstedt, Y. Liu, 3 L. Spinu, 2 and Z. Q. Mao Department of Physics, Tulane University, New
More informationAnnealing Effect on Microstructure and Superconductivity of K x Fe y Se 2 Synthesized by an Easy One-step Method. Abstract
Annealing Effect on Microstructure and Superconductivity of K x Fe y Se 2 Synthesized by an Easy One-step Method W. Zhou, X. Li, X. Zhou, F. F. Yuan, Y. Ding, J. C. Zhuang, Y. Sun, H. L. Zhou, Z. X. Shi
More informationBulk superconductivity at 14 K in single crystals of Fe 1+y Te x Se 1 x
Bulk superconductivity at 14 K in single crystals of Fe 1+y Te x Se 1 x B. C. Sales, A. S. Sefat, M. A. McGuire, R. Y. Jin, and D. Mandrus Oak Ridge National Laboratory, Oak Ridge, Tennessee 37831, USA
More informationStudies of Iron-Based Superconductor Thin Films
MBE Growth and STM Studies of Iron-Based Superconductor Thin Films Wei Li 1, Canli Song 1,2, Xucun Ma 2, Xi Chen 1*, Qi-Kun Xu 1 State Key Laboratory of Low-Dimensional Quantum Physics, Department of Physics,
More informationSuperconductivity in nickel-based compound GdONiBi and hole doped Gd 0.9 Sr 0.1 ONiBi
Superconductivity in nickel-based compound GdONiBi and hole doped Gd 0.9 Sr 0.1 ONiBi Junyi Ge, Shixun Cao, Jincang Zhang Department of Physics,Shanghai University,Shanghai 200444, China We successfully
More informationMössbauer studies on FeSe and FeTe
Mössbauer studies on FeSe and FeTe Yoshikazu Mizuguchi a,b,c, Takao Furubayashi a, Keita Deguchi a,b,c, Shunsuke Tsuda a,b, Takahide Yamaguchi a,b and Yoshihiko Takano a,b,c a Superconducting Materials
More informationMagnetic Order versus superconductivity in the Iron-based
Magnetic Order versus superconductivity in the Iron-based layered La(O 1-x F x )FeAs systems Clarina de la Cruz 1,2, Q. Huang 3, J. W. Lynn 3, Jiying Li 3,4, W. Ratcliff II 3, J. L. Zarestky 5, H. A. Mook
More informationA new 111 type iron pnictide superconductor LiFeP. Abstract
epl 87, 3704(2009) A new 111 type iron pnictide superconductor LiFeP Z. Deng, X. C. Wang, Q.Q. Liu, S. J. Zhang, Y. X. Lv, J. L. Zhu, R.C. Yu, C.Q. Jin Institute of Physics, Chinese Academy of Sciences,
More informationBiS 2 - based superconductivity in F-substituted NdOBiS 2
BiS 2 - based superconductivity in F-substituted NdOBiS 2 Satoshi Demura, 1,2 Yoshikazu Mizuguchi, 1,3 Keita Deguchi, 1,2 Hiroyuki Okazaki, 1 Hiroshi Hara, 1,2 Tohru Watanabe, 1,2 Saleem James Denholme,
More informationSpecific Heat and Electrical Transport Properties of Sn 0.8 Ag 0.2 Te Superconductor
Specific Heat and Electrical Transport Properties of Sn 0.8 Ag 0.2 Te Superconductor Yoshikazu Mizuguchi 1 *, Akira Yamada 2, Ryuji Higashinaka 2, Tatsuma D. Matsuda 2, Yuji Aoki 2, Osuke Miura 1, and
More informationJie Yang, Xiao-Li Shen, Wei Lu, Wei Yi, Zheng-Cai Li, Zhi-An Ren*, Guang-Can Che, Xiao-Li Dong, Li-Ling Sun, Fang Zhou, Zhong-Xian Zhao*
High-T c Superconductivity in some Heavy Rare-earth Iron-arsenide REFeAsO 1- (RE = Ho, Y, Dy and Tb) Compounds Jie Yang, Xiao-Li Shen, Wei Lu, Wei Yi, Zheng-Cai Li, Zhi-An Ren*, Guang-Can Che, Xiao-Li
More informationConnection between ambient-pressure and pressure-induced. superconducting phases in alkaline iron selenide superconductors
Connection between ambient-pressure and pressure-induced superconducting phases in alkaline iron selenide superconductors Dachun Gu 1, Liling Sun 1,2, Qi Wu 1, Peiwen Gao 1, Jing Guo 1,Chao Zhang 1, Shan
More informationSuperconducting properties of FeSe 0.5 Te 0.5
Superconducting properties of FeSe 0.5 Te 0.5 C.V. Tomy G. Balakrishnan and M.R. Lees Dept. of Physics, University of Warwick, UK Pradip Das and A.K. Grover Department of CMP&MS, TIFR Ravi P. Singh, Anil
More informationChemical pressure effect on superconductivity of BiS 2 -based Ce 1-x Nd x O 1-y F y BiS 2 and Nd 1-z Sm z O 1-y F y BiS 2
Chemical pressure effect on superconductivity of BiS 2 -based Ce 1-x Nd x O 1-y F y BiS 2 and Nd 1-z Sm z O 1-y F y BiS 2 Joe Kajitani*, Takafumi Hiroi, Atsushi Omachi, Osuke Miura, and Yoshikazu Mizuguchi
More informationEvolution of superconductivity in LaO 1-x F x BiS 2 prepared by high pressure technique
Evolution of superconductivity in LaO 1-x F x BiS 2 prepared by high pressure technique K. Deguchi 1,2,3, Y. Mizuguchi 1,2,4, S. Demura 1,2,3, H. Hara 1,2,3, T. Watanabe 1,2,3, S. J. Denholme 1,2, M. Fujioka
More informationSuperconductivity in the PbO-type Structure α FeSe
1 Superconductivity in the PbO-type Structure α FeSe Fong-Chi Hsu 1,2, Jiu-Yong Luo 2, Kuo-Wei Yeh 2, Ta-Kun Chen 2, Tzu-Wen Huang 2, Phillip M. Wu 3, Yong-Chi Lee 2, Yi-Lin Huang 2, Yan-Yi Chu 1,2, Der-Chung
More informationIntercalation effect on hyperfine parameters of Fe in FeSe superconductor with T c = 42 K
Intercalation effect on hyperfine parameters of Fe in FeSe superconductor with T c = 42 K Sergii I. Shylin 1,2, Vadim Ksenofontov 1, Stefan J. Sedlmaier 3, Simon J. Clarke 3, Simon J. Cassidy, 3 Gerhard
More informationPhases of Na x CoO 2
Phases of Na x CoO 2 by Aakash Pushp (pushp@uiuc.edu) Abstract This paper deals with the various phases of Na x CoO 2 ranging from charge ordered insulator to Curie-Weiss metal to superconductor as the
More informationCrystal Structure and Superconductivity at about 30 K in ACa 2 Fe 4 As 4 F 2 (A = Rb, Cs)
Crystal Structure and Superconductivity at about K in ACa 2 (A = Rb, Cs) Zhi-Cheng Wang 1, Chao-Yang He 1, Zhang-Tu Tang 1, Si-Qi Wu 1 and Guang-Han Cao 1,2 * Abstract We have synthesized two iron fluo-arsenides
More informationSynthesis and superconductivity of CeNi 0.8 Bi 2 : New entrant in superconductivity kitchen?
Letter to Editor J. Sup. Nov. Mag. (2012) Synthesis and superconductivity of CeNi 0.8 Bi 2 : New entrant in superconductivity kitchen? Anuj Kumar, Shiva Kumar, Rajveer Jha and V.P.S. Awana * Quatum Phenomena
More informationPhase Separation and Magnetic Order in K-doped Iron Selenide Superconductor
Phase Separation and Magnetic Order in K-doped Iron Selenide Superconductor Wei Li 1, Hao Ding 1, Peng Deng 1, Kai Chang 1, Canli Song 1, Ke He 2, Lili Wang 2, Xucun Ma 2, Jiang-Ping Hu 3, Xi Chen 1, *,
More informationSmall anisotropy, weak thermal fluctuations, and high field superconductivity in Co-doped iron pnictide Ba(Fe 1-x Co x ) 2 As 2
Small anisotropy, weak thermal fluctuations, and high field superconductivity in Co-doped iron pnictide Ba(Fe 1-x Co x ) 2 As 2 A. Yamamoto, J. Jaroszynski, C. Tarantini, L. Balicas, J. Jiang, A. Gurevich,
More information*Corresponding author: Yoshikazu Mizuguchi
Stabilization of high-tc phase of BiS2-based superconductor LaO0.5F0.5BiS2 using high-pressure synthesis Yoshikazu Mizuguchi 1*, Takafumi Hiroi 1, Joe Kajitani 1, Hiroshi Takatsu 2, Hiroaki Kadowaki 2
More informationarxiv: v1 [cond-mat.supr-con] 30 Sep 2009
Superconductivity at 15.6 K in Calcium-doped Tb 1 x Ca x : the structure requirement for achieving superconductivity in the hole-doped 1111 phase Gang Mu, Bin Zeng, Peng Cheng, Xiyu Zhu, Fei Han, Bing
More informationarxiv: v1 [cond-mat.supr-con] 4 Jan 2014
Conventional Superconductivity properties of the ternary boron-nitride Nb 2 BN O. V. Cigarroa 1, S. T. Renosto 1, A. J. S. Machado 1 1 Escola de Engenharia de Lorena, Universidade de São Paulo, P.O. Box
More informationGrowth, Annealing Effects on Superconducting and Magnetic Properties and
Growth, Annealing Effects on Superconducting and Magnetic Properties and Anisotropy of FeSe 1-x Te x (.5 x 1) Single Crystals Takashi Noji, Takumi Suzuki, Haruki Abe, Tadashi Adachi, Masatsune Kato, and
More informationSuperconductivity in Fe-Chalcogenide
Superconductivity in Fe-Chalcogenide Yao Li May 12, 2018 Submitted as term paper of PHYS 569: Emergent States of Matter taught by Professor Nigel Goldenfeld at University of Illinois at Urbana Champaign
More informationA new 111 type iron pnictide superconductor LiFeP
OFFPRINT A new 111 type iron pnictide superconductor LiFeP Z. Deng, X. C. Wang, Q. Q. Liu, S. J. Zhang, Y. X. Lv, J. L. Zhu, R. C. Yu and C. Q. Jin EPL, 87 (2009) 37004 Please visit the new website TAKE
More informationStrong interplay between stripe spin fluctuations, nematicity and superconductivity in FeSe
Strong interplay between stripe spin fluctuations, nematicity and superconductivity in FeSe Qisi Wang 1, Yao Shen 1, Bingying Pan 1, Yiqing ao 1, Mingwei Ma 2, Fang Zhou 2, P. Steens 3,. Schmalzl 4, T.
More informationImprovement of superconducting properties of FeSe 0.5 Te 0.5 single crystals by Mn substitution
Improvement of superconducting properties of FeSe 0.5 Te 0.5 single crystals by Mn substitution 1 A. Günther 1, J. Deisenhofer 1, Ch. Kant 1, H.-A. Krug von Nidda 1, V. Tsurkan 1,2*, and A. Loidl 1 1 Experimental
More informationInverse Iron Isotope Effect on the transition temperature of the
Inverse Iron Isotope Effect on the transition temperature of the (Ba,K)Fe 2 As 2 superconductor Parasharam M. Shirage 1, Kunihiro Kihou 1, Kiichi Miyazawa 1,2, Chul-Ho Lee 1,3, Hijiri Kito 1,3, Hiroshi
More informationFrom ( 0) magnetic order to superconductivity with ( ) magnetic resonance in Fe 1.02 (Te 1-x Se x )
From ( 0) magnetic order to superconductivity with ( ) magnetic resonance in Fe 1.02 (Te 1-x Se x ) T.J. Liu 1, J. Hu 1, B. Qian 1, D. Fobes 1, Z.Q. Mao 1*, W. Bao 2, M. Reehuis 3, S.A.J. Kimber 3, K.
More informationFile name: Supplementary Information Description: Supplementary Figures, Supplementary Notes, Supplementary Tables, Supplementary References
File name: Supplementary Information Description: Supplementary Figures, Supplementary Notes, Supplementary Tables, Supplementary References Supplementary Figure 1 Illustration of the reaction chamber
More informationSpacer Layers. Q. Huang 2,3, X. H. Chen Hefei National Laboratory for Physical Sciences at Microscale and
Superconductivity in LiFeO 2 Fe 2 Se 2 with anti-pbo-type Spacer Layers X. F. Lu 1, N. Z. Wang 1, G. H. Zhang 2,3, X. G. Luo 1, Z. M. Ma 3, B. Lei 1, F. Q. Huang 2,3, X. H. Chen 1 1. Hefei National Laboratory
More informationShigeki Yonezawa*, Yuji Muraoka and Zenji Hiroi Institute for Solid State Physics, University of Tokyo, Kashiwa, Chiba
New β-pyrochlore Oxide Superconductor CsOs 2 O 6 Shigeki Yonezawa*, Yuji Muraoka and Zenji Hiroi Institute for Solid State Physics, University of Tokyo, Kashiwa, Chiba 277-8581 Abstract The discovery of
More informationPressure-Induced Effects on the Structure of the FeSe Superconductor
Pressure-Induced Effects on the Structure of the FeSe Superconductor Jasmine N. Millican 1*, Daniel Phelan 1, Evan L. Thomas 2, Juscelino B. Leão 1, and Elisabeth Carpenter 1 1 NIST Center for Neutron
More informationThe Meissner and Mesoscopic Superconducting States in 1-4 Unit- Cell FeSe- Films up to 80 K
The Meissner and Mesoscopic Superconducting States in 1-4 Unit- Cell FeSe- Films up to 80 K L. Z. Deng 1, B. Lv 1, Z. Wu 1, Y. Y. Xue 1, W. H. Zhang 2, F. H. Li 2, L. L. Wang 3, X. C. Ma 3, Q. K. Xue 2
More informationSuperconducting Fe-based compounds (A 1 x Sr x )Fe 2 As 2 with A = K and Cs with transition temperatures up to 37 K
Superconducting Fe-based compounds (A 1 x Sr x ) with A = K and Cs with transition temperatures up to 37 K Kalyan Sasmal 1, Bing Lv, Bernd Lorenz 1, Arnold Guloy, Feng Chen 1, Yu-Yi Xue 1, and Ching-Wu
More informationFeSe a simple superconductor?
FeSe a simple superconductor? Claudia Felser Vadim Ksenofontov, Fred Casper, Shahab Naghavi T. M. McQueen, A. J. Williams, R. J. Cava S. Medvedev, I. Trojan, T. Palasyuk, Mikhail I. Eremets, G. Wortmann
More informationDao-Xin Yao and Chun Loong
Magnetism and multi-orbital l models in the iron-based superconductors Dao-Xin Yao and Chun Loong Sun Yat-sen University Guangzhou China City of Guangzhou Indiana Guangzhou Hong Kong Sun Yat-sen University
More informationHigh temperature superconductivity
High temperature superconductivity Applications to the maglev industry Elsa Abreu April 30, 2009 Outline Historical overview of superconductivity Copper oxide high temperature superconductors Angle Resolved
More informationSuperconductivity and thermal properties of sulphur doped FeTe with effect of oxygen post annealing
Superconductivity and thermal properties of sulphur doped FeTe with effect of oxygen post annealing V. P. S. Awana *, Anand Pal, Arpita Vajpayee, Bhasker Gahtori and H. Kishan National Physical Laboratory,
More informationSuperconductivity and Magnetism in (Tl,K,Rb)Fe x Se 2. Minghu Fang ( 方明虎 ) Zhejiang University, Hangzhou , China
Superconductivity and Magnetism in (Tl,K,Rb)Fe x Se 2 Minghu Fang ( 方明虎 ) Zhejiang University, Hangzhou 310027, China Email: mhfang@zju.edu.cn Thanks to my Collaborators Zhejiang University, China Hangdong
More informationarxiv: v2 [cond-mat.supr-con] 19 Feb 2016
Multi-band superconductivity and large anisotropy in FeS crystals Hai Lin, Yufeng Li, Qiang Deng, Jie Xing, Jianzhong Liu, Xiyu Zhu, Huan Yang and Hai-Hu Wen Center for Superconducting Physics and Materials,
More informationPairing symmetry in iron based superconductors
Pairing symmetry in iron based superconductors Caizhi Xu Department of Physics University of Illinois Urbana Champaign Abstract: Iron-based superconductor is a new type of unconventional superconductors.
More informationMg coating induced superconductivity in the FeSe ultrathin film
Mg coating induced superconductivity in the FeSe ultrathin film Wenbin Qiu 2, Zongqing Ma 1, 2, Yongchang Liu 1, Xiaolin Wang 2, Shi Xue Dou 2 1 Tianjin Key Laboratory of Composite and Functional Materials,
More informationA combined method for synthesis of superconducting Cu doped Bi 2 Se 3
A combined method for synthesis of superconducting Cu doped Bi 2 Se 3 Meng Wang 1, Yanru Song 2, Lixing You 1, Zhuojun Li 1, Bo Gao 1, Xiaoming Xie 1, Mianheng Jiang 2 1 Shanghai Institute of Microsystem
More informationarxiv: v1 [cond-mat.supr-con] 6 Feb 2014
Dichotomy of Electronic Structure and Superconductivity between Single-Layer and Double-Layer FeSe/SrTiO 3 Films Xu Liu 1,, Defa Liu 1,, Wenhao Zhang 3,4,, Junfeng He 1,, Lin Zhao 1, Shaolong He 1, Daixiang
More informationTunable Dirac Fermion Dynamics in Topological Insulators
Supplementary information for Tunable Dirac Fermion Dynamics in Topological Insulators Chaoyu Chen 1, Zhuojin Xie 1, Ya Feng 1, Hemian Yi 1, Aiji Liang 1, Shaolong He 1, Daixiang Mou 1, Junfeng He 1, Yingying
More informationWhat's so unusual about high temperature superconductors? UBC 2005
What's so unusual about high temperature superconductors? UBC 2005 Everything... 1. Normal State - doped Mott insulator 2. Pairing Symmetry - d-wave 2. Short Coherence Length - superconducting fluctuations
More informationSimultaneous emergence of superconductivity, inter-pocket scattering and. nematic fluctuation in potassium-coated FeSe superconductor., and Y.
Simultaneous emergence of superconductivity, inter-pocket scattering and nematic fluctuation in potassium-coated FeSe superconductor Z. R. Ye 1,, C. F. Zhang 2, 3,, H. L. Ning 1, W. Li 2, 3, L. Chen 1,
More informationAngular-dependent magnetic torque in iron-pnictide BaFe 2 x Ni x As 2
International Journal of Modern Physics B Vol. 31, No. 3 (2017) 1750005 (9 pages) c World Scientific Publishing Company DOI: 10.1142/S0217979217500059 Angular-dependent magnetic torque in iron-pnictide
More informationCrystal growth and annealing study of the hightemperature superconductor HgBa 2 CuO 4+δ
Nagarajan 1 Crystal growth and annealing study of the hightemperature superconductor HgBa 2 CuO 4+δ Vikram Nagarajan University of Minnesota, Twin Cities Greven Lab Supervisor: Martin Greven The flux crystal-growth
More informationCaloric Determination of the Upper Critical Fields and Anisotropy of NdFeAsO 1-x F x. Single Crystals. U. Welp, R. Xie, A. E. Koshelev and W. K.
Caloric Determination of the Upper Critical Fields and Anisotropy of NdFeAsO 1-x F x Single Crystals U. Welp, R. Xie, A. E. Koshelev and W. K. Kwok Materials Science Division, Argonne National Laboratory,
More informationSuperconductivity dichotomy in K coated single and double unit cell FeSe films
Superconductivity dichotomy in K coated single and double unit cell FeSe films on SrTiO 3 Chenjia Tang, 1 Ding Zhang, 1 Yunyi Zang, 1 Chong Liu, 1 Guanyu Zhou, 1 Zheng Li, 1 Cheng Zheng, 1 Xiaopeng Hu,
More informationMore a progress report than a talk
Superconductivity and Magnetism in novel Fe-based superconductors Ilya Eremin 1,2 and Maxim Korshunov 1 1 - Max-Planck Institut für Physik komplexer Systeme, Dresden, 2- Institut für Theoretische Physik,
More informationedited by Nan-Lin Wang Hideo Hosono Pengcheng Dai MATERIALS, PROPERTIES, AND MECHANISMS IRON-BASED SUPERCONDUCTORS
edited by " Nan-Lin Wang Hideo Hosono Pengcheng Dai MATERIALS, PROPERTIES, AND MECHANISMS IRON-BASED SUPERCONDUCTORS Pan Stanford Publishing Contents Preface xiii 1 Iron-Based Superconductors: Discovery
More informationarxiv: v1 [cond-mat.str-el] 8 Apr 2012
Metamagnetic transition in Ca x Sr x (x = and.) single crystals J. J. Ying, Y. J. Yan, A. F. Wang, Z. J. Xiang, P. Cheng, G. J. Ye and X. H. Chen Hefei National Laboratory for Physical Science at Microscale
More informationMagnetization reversal and ferrimagnetism in Pr 1 x Nd x MnO 3
Bull. Mater. Sci., Vol. 37, No. 4, June 2014, pp. 809 813. Indian Academy of Sciences. Magnetization reversal and ferrimagnetism in Pr 1 x Nd x MnO 3 SANJAY BISWAS, MOMIN HOSSAIN KHAN and SUDIPTA PAL*
More informationSuperconductivity and non-metallicity induced by doping the. topological insulators Bi 2 Se 3 and Bi 2 Te 3
Superconductivity and non-metallicity induced by doping the topological insulators Bi 2 Se 3 and Bi 2 Te 3 Y. S. Hor 1, J. G. Checkelsky 2, D. Qu 2, N. P. Ong 2, and R. J. Cava 1 1 Department of Chemistry,
More informationMagnetic Properties and Scaling Behavior in Perovskite like La 0.7 (Ba 1-x Pb x ) 0.3 CoO 3 System
Mat. Res. Soc. Symp. Proc. Vol. 674 21 Materials Research Society Magnetic Properties and Scaling Behavior in Perovskite like La.7 (Ba 1-x Pb x ).3 CoO 3 System Chiung-Hsiung Chen, Ting-Sheng Huang and
More informationMolecular Beam Epitaxy Growth of Tetragonal FeS Film on
Molecular Beam Epitaxy Growth of Tetragonal FeS Film on SrTiO3(001) Substrate Kun Zhao( 赵琨 ) 1, Haicheng Lin( 林海城 ) 1, Wantong Huang( 黄万通 ) 1, Xiaopeng Hu( 胡小鹏 ) 1,2, Xi Chen( 陈曦 ) 1,2, Qi-Kun Xue( 薛其坤
More informationSuperconductivity at 4.4K in PdTe 2 -chains of a Ta Based Compound
Superconductivity at 4.4K in PdTe 2 -chains of a Ta Based Compound Reena Goyal, Brajesh Tiwari, Rajveer Jha, and V. P. S Awana* CSIR-National Physical Laboratory, Dr. K. S. Krishnan Marg, New Delhi-110012,
More informationSynchrotron powder X-ray diffraction and structural analysis of Eu0.5La0.5FBiS2-xSex
Synchrotron powder X-ray diffraction and structural analysis of Eu0.5La0.5FBiS2-xSex K. Nagasaka 1, G. Jinno 1, O. Miura 1, A. Miura 2, C. Moriyoshi 3, Y. Kuroiwa 3, Y. Mizuguchi 1 * 1. Department of Electrical
More informationSuperconductivity in the Mn 5 Si 3 -type Zr 5 Sb 3 system
Superconductivity in the Mn 5 Si 3 -type Zr 5 Sb 3 system B. Lv, 1 * X. Y. Zhu, 1 B. Lorenz, 1 F. Y. Wei, 1 Y. Y. Xue, 1 Z. P. Yin, 2 G. Kotliar 2 and C. W. Chu 1,3 * 1 Department of Physics and Texas
More informationSite Selectivity on Chalcogen Atoms in Superconducting La(O,F)BiSSe
Site Selectivity on Chalcogen Atoms in Superconducting La(O,F)BiSSe Masashi TANAKA 1,a), Takuma YAMAKI 1,2, Yoshitaka MATSUSHITA 1, Masaya FUJIOKA 1, Saleem J. DENHOLME 1, Takahide YAMAGUCHI 1, Hiroyuki
More informationStructural and magnetic characterization of the new GdMn 1-x. O 3 perovskite material
Journal of Physics: Conference Series PAPER OPEN ACCESS Structural and magnetic characterization of the new GdMn 1-x Fe x O 3 perovskite material To cite this article: J A Cardona Vasquez et al 2016 J.
More informationSuperconductivity - Overview
Superconductivity - Overview Last week (20-21.11.2017) This week (27-28.11.2017) Classification of Superconductors - Theory Summary - Josephson Effect - Paraconductivity Reading tasks Kittel: Chapter:
More informationEnhancement of Tc in BiS 2 based superconductors NdO 0.7 F 0.3 BiS 2 by substitution. of Pb for Bi
Enhancement of Tc in BiS 2 based superconductors NdO 0.7 F 0.3 BiS 2 by substitution of Pb for Bi S. Demura 1,2, Y. Fujisawa 1, S. Otsuki 1, R. Ishio 1, Y. Takano 2 and H. Sakata 1 1 Tokyo University of
More informationSchematic for resistivity measurement
Module 9 : Experimental probes of Superconductivity Lecture 1 : Experimental probes of Superconductivity - I Among the various experimental methods used to probe the properties of superconductors, there
More informationSuperconducting (Li, Fe)OHFeSe film of high quality and high critical parameters
Superconducting (Li, Fe)OHFeSe film of high quality and high critical parameters Yulong Huang 1,2,+, Zhongpei Feng 1,2,+, Shunli Ni 1,2,+, Jun Li 4, Wei Hu 1,2, Shaobo Liu 1,2, Yiyuan Mao 1,2, Huaxue Zhou
More informationarxiv: v2 [cond-mat.supr-con] 13 Jan 2010
The crystal structure of FeSe 0. Te 0.56 M. Tegel, C. Löhnert, D. Johrendt arxiv:092.3706v2 [cond-mat.supr-con] 3 Jan 200 Abstract Department Chemie, Ludwig-Maximilians-Universität München, Butenandtstr.
More informationAnisotropic Magnetic Structures in Iron-Based Superconductors
Anisotropic Magnetic Structures in Iron-Based Superconductors Chi-Cheng Lee, Weiguo Yin & Wei Ku CM-Theory, CMPMSD, Brookhaven National Lab Department of Physics, SUNY Stony Brook Another example of SC
More informationRare double spin canting antiferromagnetic behaviours in a. [Co 24 ] cluster
Electronic Supplementary Material (ESI) for ChemComm. This journal is The Royal Society of Chemistry 2016 Rare double spin canting antiferromagnetic behaviours in a [Co 24 ] cluster Guang-Ming Liang, Qing-Ling
More informationOnset of the Meissner effect at 65 K in FeSe thin film grown on Nb doped SrTiO 3 substrate
Onset of the Meissner effect at 65 K in FeSe thin film grown on Nb doped SrTiO 3 substrate Zuocheng Zhang 1,4*, Yihua Wang 2,3*, Qi Song 2,5*, Chang Liu 1,4, Rui Peng 2,5, K.A. Moler 3, Donglai Feng 2,5
More informationStripes developed at the strong limit of nematicity in FeSe film
Stripes developed at the strong limit of nematicity in FeSe film Wei Li ( ) Department of Physics, Tsinghua University IASTU Seminar, Sep. 19, 2017 Acknowledgements Tsinghua University Prof. Qi-Kun Xue,
More informationThe Chemical Control of Superconductivity in Bi 2 Sr 2 (Ca 1 x Y x )Cu 2 O 8+±
CHINESE JOURNAL OF PHYSICS VOL. 38, NO. 2-II APRIL 2000 The Chemical Control of Superconductivity in Bi 2 Sr 2 (Ca 1 x Y x )Cu 2 O 8+± R. S. Liu 1, I. J. Hsu 1, J. M. Chen 2, and R. G. Liu 2 1 Department
More informationc-axis Dimer Inducing Dome-like Superconductivity in Weakly Correlated RE 2 Cu 5 As 3 O 2 (RE=La, Pr)
c-axis Dimer Inducing Dome-like Superconductivity in Weakly Correlated RE 2 Cu 5 As 3 O 2 (RE=La, Pr) Xu Chen 1,2,, Jiangang Guo 1,,*, Chunsheng Gong 1, Erjian Cheng 3, Congcong Le 4,1, Ning Liu 1,2, Tianping
More informationHyper-expanded interlayer separation in superconducting barium intercalated FeSe
Electronic Supplementary Material (ESI) for ChemComm. This journal is The Royal Society of Chemistry 2015 SUPPLEMENTARY INFORMATION Hyper-expanded interlayer separation in superconducting barium intercalated
More informationMagnetic properties of fullerene superconductors
Supercond. Sci. Technol. 9 (1996) 599 615. Printed in the UK TOPICAL REVIEW Magnetic properties of fullerene superconductors V Buntar and H W Weber Atominstitut der Österreichischen Universitäten, Schüttelstrasse
More informationarxiv: v2 [cond-mat.supr-con] 11 Apr 2009
Raman phonons in α-fete and Fe 1.03 Se 0.3 Te 0.7 single crystals arxiv:0811.2350v2 [cond-mat.supr-con] 11 Apr 2009 T.-L. Xia, 1 D. Hou, 2,1 S. C. Zhao, 1 A. M. Zhang, 1 G. F. Chen, 3 J. L. Luo, 3 N. L.
More informationSulfur annealing effect for superconductivity in iron chalcogenide
Sulfur annealing effect for superconductivity in iron chalcogenide compounds K. Deguchi 1,2, A. Yamashita 1, T. Yamaki 1,2, H. Hara 1,2, S. Demura 1,2, S. J. Denholme 1, M. Fujioka 1, H. Okazaki 1, H.
More informationElectrical Resistivity Measurements under High Pressure for Nd3.5Sm0.5Ni3O8
Proc. 17th Int. Conf. on High Pressure in Semiconductor Physics & Workshop on High-pressure Study on Superconducting JJAP Conf. Proc. 6, https://doi.org/10.7567/jjapcp.6.011106 Electrical Resistivity Measurements
More informationMössbauer spectroscopy of spin dynamics in Mn x Fe 1 x Se 0.85 superconductors: Evidence for an incommensurate-spin-density-wave state
March 2010 EPL, 89 (2010) 67009 doi: 10.1209/0295-5075/89/67009 www.epljournal.org Mössbauer spectroscopy of spin dynamics in Mn x Fe 1 x superconductors: Evidence for an incommensurate-spin-density-wave
More informationRoom-temperature Protonation Induced High-Tc Phase in. Iron-based Superconductors Evidenced by NMR and. Magnetization Measurements
Room-temperature Protonation Induced High-Tc Phase in Iron-based Superconductors Evidenced by NMR and Magnetization Measurements Yi Cui 1, G. Zhang 1, H. B. Li 2, H. Lin 3, X. Zhu 3, H. H. Wen 3, G. Q.
More informationInfluence of tetragonal distortion on the topological electronic structure. of the half-heusler compound LaPtBi from first principles
Influence of tetragonal distortion on the topological electronic structure of the half-heusler compound LaPtBi from first principles X. M. Zhang, 1,3 W. H. Wang, 1, a) E. K. Liu, 1 G. D. Liu, 3 Z. Y. Liu,
More informationStrongly Correlated Systems:
M.N.Kiselev Strongly Correlated Systems: High Temperature Superconductors Heavy Fermion Compounds Organic materials 1 Strongly Correlated Systems: High Temperature Superconductors 2 Superconductivity:
More informationStructural, and Magnetic properties of flux free large FeTe Single crystal
Structural, and Magnetic properties of flux free large FeTe Single crystal P. K Maheshwari 1,2, Rajveer Jha 1, Bhasker Gahtori and V.P.S. Awana 1* 1 CSIR-National Physical Laboratory, Dr. K. S. Krishnan
More informationChemical doping and high pressure studies of layered β-pdbi 2 single crystals
Chemical doping and high pressure studies of layered β-pdbi 2 single crystals Kui Zhao 1, Bing Lv 1, Yu-Yi Xue 1, Xi-Yu Zhu 1,2, Liangzi Deng 1, Zheng Wu 1 and C. W. Chu 1,3 1 Texas Center for Superconductivity
More informationSuperconductivity and Spin Density Wave (SDW) in NaFe 1-x Co x As
Superconductivity Spin Density Wave SDW) in NaFe 1-x Co x As Haftu Brhane Department of Physics, College of Natural Computational Sciences, Haramaya University, Dire- Dawa, Ethiopia Amarendra Rajput Department
More information