2K water-borne PU for furniture coatings
|
|
- Harold Powell
- 5 years ago
- Views:
Transcription
1 2K water-borne PU for furniture coatings Water-borne 2K polyurethane systems are a new technology which is already successfully used in many applications also for wood coatings and more specifically furniture finishes, without having to sacrifice quality. Some properties like the ease of introduction by hand of the hardener and the determination of the pot-life through the viscosity increase can be optimised by choosing the right solvent to dilute the polyisocyanate. C. Varron, V. Granier, C. Kwee The application of a lacquer or paint is the ultimate protection of wood. Sustrate preparation, like in any paint application, is essential to ensure good adhesion and durability of the final coating. Polyurethane-based coatings have an established place in the coating industry because of their very high level of quality. Polyurethanes come from the reaction between a hydroxylated polymer and an aliphatic or aromatic isocyanates, the latter being used when yellowing due to UV exposure is not a drawback. 2K water-borne PU As furniture coatings are applied indoors, the main requirements include low emission of solvents during application and drying for health and safety reasons. Good resistance to chemicals and durability are also important. In addition to these film performances, the user requires an easy homogenisation of the hardener and binder (in case of a two-component system), and a good balance between pot-life and drying time. In the case of light-coloured wood, low yellowing of the film is also required to preserve the natural beauty of the substrate. Water-borne coatings offer new challenges to formulate properly, as: - they are complex fluids, due to the fact that entities are often dispersed into water in order to optimise water dispersibility and water sensitivity, and not any longer simple solutions - system compatibility is more difficult to optimise, when compared to solvent-borne coatings - side reactions may occur, due to the fact that the solvent (water) may react with polyisocyanates - they raise new issues and require new working habits, like every technological change does. But as always, everything is just a matter of time and training and in recent years, the market share of waterborne systems has grown very fast due to their favourable properties such as mild odour, ease of application and fast drying for example. Chemical reactions of polyisocyanates The reaction between the hydroxyl groups of the polyol and the isocyanate (reaction 1 in Figure 1) is predominant to form the polyurethane network. But secondary reactions also occur in the system, especially the reaction between isocyanate and water (reaction 2a in Figure 1). The reaction with water plays an important role, as it affects film properties because of carbon dioxide release and urea bond formation (reaction 2b). NCO/OH ratio between 1.2 and 1.8 gives good properties The reaction of organic acid groups with isocyanates (reaction 1 in Figure 2) needs to be mentioned because it destroys the hydrophilic nature of the polyol (if it contains acid stabilising groups) and contributes to carbon dioxide formation. Other side reactions (Figure 2) are less important as they play a far less significant role in the crosslinking and properties of the coating. The relative reaction rates of functional groups with aliphatic isocyanates are: Amine (primary/secondary)>hydroxyl>water>urea>urethane>>carbo xylic [1] This reactivity scale explains why it is possible to use aliphatic polyisocyanates to formulate water-borne coatings with an acceptable pot-life. In order to compensate for these side reactions, the NCO to OH ratio of water-borne formulations has to be higher than 1, as it is normally not the case for solvent-borne coatings. If the NCO/OH ratio is too low, then the polyol may not be fully crosslinked, thus resulting in poor properties. Overall ratio varies between 1.2 and 3, depending on the polyol and polyisocyanate used. Normal ratios stay between 1.2 and 1.8. View of hydrophobic polyisocyanates Aromatic polyisocyanates must be avoided because of their high reactivity with water, therefore it will be focus on aliphatic polyisocyanates, and more specifically HDI-trimer derivatives. There are two types of polyisocyanates which can be used in water-borne formulations. The first approach is to use conventional poly- isocyanates which were developed for solvent-borne systems, and so in theory are not suitable for use in aqueous systems. These products are hydrophobic in nature, but in some cases, depending on the polyol, good performances can be achieved. Isocyanurate trimers of hexamethylene di-isocyanate such as "Tolonate HDT-LV" or "HDT-LV2" are normally used, due to their lower intrinsic viscosity compared to biurets. In such a case, water-soluble polyols and some dispersions are hydrophilic enough to act as dispersing agent for the hydrophobic polyisocyanate. In order to achieve a good introduction of the polyisocyanate into such a system, a low viscosity of the polyisocyanate is highly recommended. Water-compatible solvent can be used to reduce the polyisocyanate viscosity [2]. It is also possible to use high shear equipment to introduce these hydrophobic polyisocyanates into the aqueous phase. View of hydrophilic polyisocyanates The second approach is to modify the polyisocyanate in a way that it becomes hydrophilic and thus water-dispersible under low shear mixing conditions or self-emulsifying. The most common way to increase the hydrophilicity of a polyisocyanate is to graft hydrophilic polyether groups [3, 4], and thus to lower the functionality of the polyisocyanate. Such hydrophilic groups can either be non-ionic or ionic if terminated by a specific group which can be dissociated above a specific ph [5]. Another way to produce hydrophilic polyisocyanates is to formulate them with NCO-non reactive component able to render them water-dispersible. "Rhodocoat WT2104" is a water-dispersible isocyanate based on HDI-trimer with 19% NCO, at 100% solids. Hardener easy to use
2 The hardener has to be easily dispersible in the binder. This can be obtained by using self water-dispersible polyisocyanate crosslinkers. The major advantage of these new products is clearly their ease to use, as they will not request high shear mixing. Figure 3 illustrates the difference in dispersibility between hydrophobic and hydrophilic polyisocyanates. The left-hand picture shows a hydrophilic isocyanate which has been incorporated into an aqueous medium containing a polyacrylic polyol. The dispersion of the polyisocyanate has been done by simple shaking. The droplets have a diameter lower than half a micron and the particle size is evenly distributed. The right hand side shows the distribution of droplets of a low viscosity hydrophobic polyisocyanate, mechanically introduced into the same polyol. In this case the particle diameter is about 2-3 microns. Solvents assit gloss, chemical resistance and hardness In order to satisfy wood coatings requirements, polyols can be polyacrylic dispersions, emulsions,polyacrylate-grafted polyurethane dispersions or polyurethane dispersions or combinations of these. The choice of one polyol or of a mixture of polyols is in fact imposed by the balance between the level of performance of the film and the cost of the formulation. Why using a solvent in the water-borne formulation? The use of a solvent to pre-dilute a hydrophilic isocyanate is not necessary, however is recommended to reduce the hardener's viscosity so that it is closer to the polyol's, and is therefore dispersed easily into the polyol. Other advantages have been noticed, such as higher gloss, better chemical resistance and hardness. The choice of dilution solvent is important as the solvent much be free of hydroxylic or carboxylic groups, suceptible of reacting with isocyanate, allowing good storage stability. The selection of the dilution solvent is made by measuring the particle size of the pre-diluted isocyanate in water; one particle size is necessary and the smaller the particle, the better the dispersion in a water-borne formulation. Table 1 shows a large choice of solvents and that a wide range of dilution ratios can be used, provided the solvents are urethane grades. NMP is not suitable as it causes swelling of the particles in water. The dilution solvent can also influence the coating's properties, as our experiments showed. Choice of suitable solvent Table 2 shows a typical matt furniture clear-coat formulation based on "Worleecryl 7816" (from Worlée Chemie); this resin is a hydroxylated acrylic dispersion, which was obtained from a solvent-borne resin, dispersed into water using emulsifiers. In this case, several solvents are suitable to pre-dilute the isocyanate; the choice was made by stirring the prediluted isocyanate into the water-based clear-coat with a spatula (hand mixing). The clear-coat is then applied onto glass panels and gloss is measured once the coating is dry. Results are displayed in Table 3. In this clear-ocat formulation, Persoz hardness is influenced by the type of solvent used to dilute the hardener; here, EEP and MPA give suitable results for furniture coatings requirements. Figure 4 shows that once the clear-coat is touch dry (a few hours), it takes several days for the polyurethane coating to be fully cured at room temperature (23 C, 55%RH). Chemical resistance a key point of wood finishes performance The nature of the solvent used to dilute the hydrophilic isocyanate has no effect on the level of chemical resistance of the clearcoat, which gives more flexibility to adjust the formulation to some specific needs. Various chemicals which can be found for example in a kitchen, are left on the clear-coat following DIN All the samples show a excellent chemical resistance, except with coffee. More tests were conducted on a 2K water-borne polyurethane based on "Neocryl XK101" (from Avecia NeoResins); this time, the polyol is a hydroxylated acrylic emulsion, which can be cross-linked with "Rhodocoat WT2104" prediluted in MPA. Refer to Table 4 for starting formulation. The hardener is easily dispersed into the polyol phase, giving excellent levelling and high gloss. Then the formulation can be used for several hours and its viscosity may vary or not. In this case, the water-borne system behaves like a solvent-borne one, as the pot-life can be measured as doubling of the initial viscosity. Table 5 shows the various charateristics of the clear-coat applied on glass. The clear-coat was then applied onto maple wood panels. Two coats were applied and dried at room temperature, chemical resistance tests were perfomed as described previously. Figure 5 shows the results of the chemical resistance test performed according to the DIN standard. Rating is : 0 (excellent) to 5 (very poor). The resistance to most chemicals is excellent, except for some solvents. References [1] C. R. Hegedus, D. C. Lawson and D. L. Lindenmuth, Two-component waterborne polyurethane coatings: chemistry and application, Proc. Of the International Waterborne, High-Solids and Powder Coatings Symposium, New Orleans, Feb [2] E. Brinkman, M. Van Wingerde, Two-component PU paints: a comparison between solvent and waterborne, Proc. 3rd Nürnberg Congress, 1995, Paper 37 [3] L. Kahl, M. Bock, Waterborne two-component PU clear coats for automotive coatings: development of raw materials and mixing technology, Proc. 3rd Nürnberg Congress, 1995, Paper 7 [4] US patent , Oct [5] US Patent , Dec Result at a glance Two examples of formulations show that aqueous 2K PU coatings can be used for wood coatings, without having to sacrifice quality. By choosing the right polyol, a requested balance between cost and performance can be reached. Some properties like the ease of introduction by hand of the hardener and the determination of the pot-life through the viscosity increase can be optimised by choosing the right solvent to dilute the polyisocyanate. The authors: -> Corinne Varron, Rhodia, graduated from the E.N.S.S.S.P.I.C.A.M. in organic chemistry in In 1995 she joined Rhodia in Manchester. She moved to Rhodia's research center in Lyon/France dealing with application & development on aliphatic isocyanates, position she is currently occupying. -> Vincent Granier, Rhodia, graduated from the Ecole Normale Supérieure de St Cloud (France) in chemistry in He passed his PhD at Bordeaux University in physico-chemistry in He joined Rhodia in Aubervilliers/France in1990. Since 2001 he is also World Wide Technical Manager for aliphatic isocyanates.
3 Figure 1: Reaction of isocyanate groups with hydroxy-functions.
4 Figure 2: Further possible reaction of isocyanate groups in water-borne systems.
5 Quelle/Publication: European Coatings Journal 06/2003 Ausgabe/Issue: 36 Seite/Page: Figure 3: Comparison under an optical microscope (x 400).
6 Figure 4: Persoz hardness developement.
7 Figure 5: Chemical resistance of the clearcoats.
8 .
9 .
10 .
11 .
12 .
Tolonate X FLO 100. Bio-based & low viscosity aliphatic isocyanate polymer
Tolonate X FLO 100 Bio-based & low viscosity aliphatic isocyanate polymer Discover the of Tolonate TM X FLO 100 Tolonate X FLO 100 is a new, partially bio-based, solvent-free and low viscosity aliphatic
More informationCREATING TOMORROW S SOLUTIONS HEAT-SEALABLE COATINGS I PRINTING INKS I INDUSTRIAL COATINGS VINNOL SURFACE COATING RESINS PRODUCT OVERVIEW
CREATING TOMORROW S SOLUTIONS HEAT-SEALABLE COATINGS I PRINTING INKS I INDUSTRIAL COATINGS VINNOL SURFACE COATING RESINS PRODUCT OVERVIEW 1 Viscosity Flexibility Thermal-activation temperature Solubility
More informationA Glossary of Terms Used in the Adhesives, Coatings and Elastomers (ACE) Sector
A Glossary of Terms Used in the Adhesives, Coatings and Elastomers (ACE) Sector Abrasion resistance The ability of the coating membrane to resist mechanical action such as foot traffic and particles, which
More informationACRYSOL RM-5000 Rheology Modifier
Technical Data Sheet ACRYSOL RM-5000 Rheology Modifier For water based paint applications Regional Product Availability Description Performance Features EMEA ACRYSOL RM-5000 Rheology Modifier is a non-ionic
More informationMolecular defoamers. Seite/Page: 132
Molecular defoamers Resolving stability and compatibility problems. Wim Stout, Christine Louis. Though surfactants allow waterborne coatings to wet low surface energy substrates even in high-speed applications,
More informationProduct Data Sheet. NeoRez R Delivery form: 32 % solids in water.
is an aliphatic waterborne urethane dispersion offering a unique combination of "soft feel" and a very low gloss. Good chemical resistances can be obtained when crosslinked with a suitable hardener. Delivery
More informationPolymer Systems and Film Formation Mechanisms in High Solids, Powder, and UV Cure Systems
Polymer Systems and Film Formation Mechanisms in High Solids, Powder, and UV Cure Systems J. Baghdachi, Ph.D. Coatings Research Institute Eastern Michigan University (734) 487-3192 Freshpaint@aol.com jamil.baghdachi@emich.edu
More informationCOMPARATIVE PROPERTIES OF SILYLATED POLYURETHANE, SILICONE AND NON-SILICONE PRESSURE SENSITIVE ADHESIVES
COMPARATIVE PROPERTIES OF SILYLATED POLYURETHANE, SILICONE AND NON-SILICONE PRESSURE SENSITIVE ADHESIVES Roy M. Griswold and Robert L. Frye, Momentive Performance Materials, Wilton, CT Introduction SPUR
More informationKeeping the weight up
Keeping the weight up Acrylic polymer dispersions give novel approach to waterborne coatings. Dirk Mestach, Derrick R. Twene. Waterborne UV-curing binders based on acrylic polymer dispersions have been
More informationLiquid Polybutadienes and Derivatives
Liquid Polybutadienes and Derivatives Coatings & Colorants Product Range Our polyoils and derivatives are stereospecific, lowviscosity and unsaponifiable liquid polybutadienes having a high 1.4-cis double
More informationInnovative. Technologies. Chemie des Klebens Chemistry of Adhesives. Dr. Jochen Stock, Laboratory Manager CRL Germany: Neuss, November 27 th, 2013
Chemie des Klebens Chemistry of Adhesives Dr. Jochen Stock, Laboratory Manager CRL Germany: Neuss, November 27 th, 2013 Innovative Technologies 1 Overview Chemie des Klebens Chemistry of Adhesives Introduction
More informationFlexible Packaging Adhesives The Basics. Larry Jopko Rohm and Haas Company. Abstract
Flexible Packaging Adhesives The Basics Larry Jopko Rohm and Haas Company Abstract Flexible packaging adhesives are predominately based on urethane and acrylic chemistry. Backbone options create unique
More informationAlkoxylates Promoting superior performance
Our range of versatile liquid polyols Promote superior end-product performance in radiation curing Enhance properties of polyurethane elastomers and foams Tailor ideal additives for a wide variety of applications
More informationDESIGN OF POLYMERIC DISPERSANTS FOR LOW AND NO VOC APPLICATIONS
DESIGN OF POLYMERIC DISPERSANTS FOR LOW AND NO VOC APPLICATIONS Jeff Norris, Tom Annable, Matt Dunn, Antonio Lopez Lubrizol Advanced Materials, Inc. USA PIGMENT DISPERSION AND STABILIZATION Polymeric dispersants
More informationFundamentals of Rheology Science of Deformation and Flow Homer Jamasbi, Ph.D. Elementis Specialties
Fundamentals of Rheology Science of Deformation and Flow Homer Jamasbi, Ph.D. Elementis Specialties Introduction Rheology is the study of how materials deform and flow under the influence of external forces.
More informationMaking chemistry work for you. ISCATHIX Rheological Additives
Making chemistry work for you Rheological Additives ISCA was established in 1998 with the aim of supplying high quality speciality chemicals across a broad spectrum of industry. Our commitment to provide
More informationFORMULATING THE RAINBOW
4 TINTING SYSTEMS Source: Marco2811 - Fotolia.com FORMULATING THE RAINBOW Label-free universal colourants created with matched set of dispersants. By Steffen Onclin, Heinz-Günther Schulte and Paula Gomez-Perea,
More informationADDITIVES. HIGH SOLIDS AND WATER- BORNE COATINGS Werner J. Blank Rudy Berndlmaier & Dan Miller King Industries Inc.
You are now at www.wernerblank.com HOME NEWS PUBLICATIONS LECTURES PATENTS DOWNLOADS ADDITIVES FOR HIGH SOLIDS AND WATER- BORNE COATINGS Werner J. Blank Rudy Berndlmaier & Dan Miller King Industries Inc.
More informationBorchi Gel Associative HEUR thickener for water-borne coating systems with NEWtonian rheology profile. Borchi Gel page 1 of 14
Associative HEUR thickener for water-borne coating systems with NEWtonian rheology profile - page 1 of 14 For decades, OMG Borchers' Borchi Gel associative thickeners have been synonymous with quality
More informationSPECIALTY MONOMERS FOR ENHANCED FUNCTIONALITY IN EMULSION POLYMERIZATION
SPECIALTY MONOMERS FOR ENHANCED FUNCTIONALITY IN EMULSION POLYMERIZATION Pierre Hennaux, Nemesio Martinez-Castro, Jose P. Ruiz, Zhihua Zhang and Michael D. Rhodes Solvay Inc. Centre for Research & Technology-
More informationVINNOL SURFACE COATING RESINS PRODUCT OVERVIEW
SURFACE COATING RESINS PRODUCT OVERVIEW WACKER markets vinyl chloride copolymers and terpolymers under the trade name surface coating resins. The product range currently contains surface coating resins
More informationDynasylan SIVO 110. Description. Product Information. SIVO SOL Technology for coating systems
Dynasylan SIVO 110 +49-69-218-5656 SIVO SOL Technology for coating systems Description Dynasylan SIVO 110 resembles a multifunctional, basically VOC-free, water-borne sol-gel system. It is composed of
More informationTEPZZ 8 _446A_T EP A1 (19) (11) EP A1 (12) EUROPEAN PATENT APPLICATION. (51) Int Cl.: C09D 5/00 ( )
(19) TEPZZ 8 _446A_T (11) EP 2 821 446 A1 (12) EUROPEAN PATENT APPLICATION (43) Date of publication: 07.01.1 Bulletin 1/02 (1) Int Cl.: C09D /00 (06.01) (21) Application number: 141773.6 (22) Date of filing:
More informationADDITIVES FOR PAINTS, INKS & COATINGS. Innovative Silicone Specialties
ADDITIVE FOR PAINT, INK & COATING Innovative ilicone pecialties ILICONE ADDITIVE FOR PAINT, INK AND COATING ilicone additives have long been recognized for providing special properties to inks and coatings,
More informationDefoamer. Mark Heekeren, Lab Manager Technical Service Automotive Coatings Wesel, 12. August 2015
Defoamer Mark Heekeren, Lab Manager Technical Service Automotive Coatings Wesel, 12. August 2015 Content Whatis foam foamstabilization Mode ofaction ofdefoamers Defoamer classes Defoamer test methods 7/20/2015,
More informationVINYL ACETATE-ETHYLENE (VAE) DISPERSIONS PROVIDE HIGH PERFORMANCE VERSATILE BINDERS FOR A VARIETY OF COATINGS APPLICATIONS
VINYL ACETATE-ETYLENE (VAE) DISPERSIONS PROVIDE IG PERFORMANCE VERSATILE BINDERS FOR A VARIETY OF COATINGS APPLICATIONS Authors: Kevin Merlo, Ricardo Gouvea, Angelita Saul, and Markus Busold Wacker Chemical
More informationCationic UV Curing Speeding up reactivity 15x with Curalite
Cationic UV Curing Speeding up reactivity 15x with Curalite European Coatings Show, April 5 th 2017 Presented by David Engberg Introduction Background MSc. In Chemical Engineering at the Faculty of Engineering
More informationThe Role of Thickeners in Optimising Coatings Formulation
The Role of Thickeners in Optimising Coatings Formulation Clemens Auschra, Immanuel Willerich, Iván García Romero, Hunter He, Robert Reichardt, Cindy Muenzenberg, Elena Martinez ChinaCoat, December 2014
More informationPositive property enhancement of waterborne coatings using nanoparticle based performance additives
Positive property enhancement of waterborne coatings using nanoparticle based performance additives IPEK Presentation, 22.04.2009 Samuel Schär Bühler AG Head of Business Unit PARTEC Bühler AG IPEK Presentation
More informationOptical & Spectroscopic Insight into Rheology. SR Kim
Optical & Spectroscopic Insight into Rheology SR Kim 14.11.2014 Contents Rheology and Microscopy Rheology and Simultaneous FT-IR Analysis 2 3 RHEOLOGY AND MICROSCOPY What does Rheology Do? Put a defined
More informationrace to the Second Edition Preface to the First Edition 'kno\t'ledgements Contents
Contents race to the Second Edition Preface to the First Edition 'kno\t'ledgements Chemistry and Basic Intermediates. Introduction. Basic Chemistry Basic Structure of a Polyurethane Elastomer. Synthesis
More informationFigure 1. Principle of crosslinking emulsion copolymers by using hexaallylamino-cyclo-triphosphazene
COATING BINDERS BASED ON STRUCTURED SELF-CROSSLINKING LATEXES Rückerová A., Machotová J., Kalendová A., Puková K. University of Pardubice, Institute of Chemistry and Technology of Macromolecular Materials,
More informationProgress in Organic Coatings
Progress in Organic Coatings 65 (2009) 125 130 Contents lists available at ScienceDirect Progress in Organic Coatings journal homepage: www.elsevier.com/locate/porgcoat The influence of surface chemistry
More informationPolySurF Functional Monomers Radiation Curing Additives
Chemicals BV for tomorrow s Technology CH = C - C - - - - P - H 2 CH 3 R PolySurF Functional Monomers Radiation Curing Additives for tomorrow s World Contents 1. Introduction 2 2. Properties 3 2.1 ADDAPT
More informationASSOCIATIVE POLYURETHANE THICKENERS FOR WATER- BORNE COATINGS Rheological behavior precisely adjusted application!
In a more and more competitive environment coating materials must be able to be optimally used. The desired layer thickness should be applied in an optimum way in a single work step with simple processing
More informationACRYSOL TM RM-8W Rheology Modifier
Technical Data Sheet ACRYSOL TM RM-8W Rheology Modifier For Water Based Coatings Regional Product Availability EMEAI Summary ACRYSOL RM-8W Rheology Modifier is a non ionic urethane type polymer, designed
More informationRadiation Curable Additives Enabling Excellent Paint Surfaces
Radiation Curable Additives Enabling Excellent Paint Surfaces RADTECH North America April 2013 Paulo Roberto Vieira Jr, PhD 1 When and why do we need additives? Introduction Leveling and Flow Foam Rheology
More informationStandard Glossary of Packaging Inks and Coatings Terms
Standard Glossary of Packaging Inks and Coatings Terms 1 Acrylic binder Additive Basecoat Binder/ Vehicle Non-reactive Styrene-acrylate-copolymers or pure acrylate polymers as a resin solution in water
More informationPOLYURETHANE - DISPERSIONS
PLYURETHAE - DISPERSIS Johnny Zhang Asia Pacific TS&D Manager for Liquid Coating Resins Cytec Surface Specialties Pioneering Sustainable Change 章志源液体涂料树脂亚太地区技术服务与发展经理氰特表面技术 2009 Cytec Industries Inc. All
More informationCompliant yet excellent
Compliant yet excellent NMP- and critical-additive-free polyurethane dispersions for high performance parquet flooring applications. Waterborne polyurethane dispersions (PUDs) can produce coatings with
More informationPreparation and Properties of Two-Component and Double-Crosslinking Waterborne Polyurethane-Acrylic Dispersions
Open Journal of Organic Polymer Materials, 213, 3, 27-33 http://dx.doi.org/1.4236/ojopm.213.325 Published Online April 213 (http://www.scirp.org/journal/ojopm) Preparation and Properties of Two-Component
More informationIntroduction: Green Technology
Product categories Surfactant classification Introduction: Green Technology One of the newer technologies is using renewable resources as basis for surfactant formulating Surfactant: hydrophilic / hydrophobic
More informationUV curing is one of the fastest growing technologies UTOPIA OR REALITY?
Highest Agent Loading with Outstanding Viscosity Reduction in %-UV Coatings UTOPIA OR REALITY? UV curing is one of the fastest growing technologies worldwide, with a predicted growth of 6-7% yearly. of
More informationPREPARATION OF CARBON FIBER SIZING AGENT AND CHARACTERIZATION OF ITS PROPERTIES Kunming Yang 1, Peng Li 2, Xiaoping Yang
21 st International onference on omposite Materials Xi an, 20-25 th August 2017 PREPARATIN F ARBN FIBER SIZING AGENT AND HARATERIZATIN F ITS PRPERTIES State Key Laboratory of rganic-inorganic omposites,
More informationCREATING TOMORROW S SOLUTIONS REPRINT I PPCJ I MARCH 2016 VAE DISPERSIONS FOR A VARIETY OF COATINGS APPLICATIONS
CREATING TMRRW S SLUTINS REPRINT I PPCJ I MARCH 2016 VAE DISPERSINS FR A VARIETY F CATINGS APPLICATINS ARCHITECTURAL CATINGS Ethylene-based dispersions have grown in popularity as high performance versatile
More informationWaterborne UV Curable Polyurethane Dispersions
Waterborne Curable Polyurethane Dispersions Bo Lv, Zhongqun Xue Jiangsu Sanmu Group, Yixing 214258, Jiangsu, China Abstract Two high molecular weight polyurethane dispersions (PUDs) were synthesized by
More informationRheological Additives TEGO ViscoPlus
88 Rheological Additives TEGO ViscoPlus 89 Panta Rhei Greek for everything flows certainly applies to paints and coatings. From manufacture through storage and processing to drying or curing after application,
More informationSELF-CROSSLINKING WATER BORNE CHEMISTRY FOR EXCELLENT SHELF STABILITY AND ROOM TEMPERATURE CURE
SELF-CROSSLINKING WATER BORNE CHEMISTRY FOR EXCELLENT SHELF STABILITY AND ROOM TEMPERATURE CURE Presenter Author: Dr. Brian Hanrahan KH Neochem Americas, Inc. INTRODUCTION In recent years, the usage of
More informationBorchers Rheological Additives for waterborne coating systems. Borchi Gel
Borchers Rheological Additives for waterborne coating systems Borchi Gel Additives with a thickening effect have a significant influence on the shelf life and application properties of liquid coating systems
More informationSafety of the UV/EB Curing Process
Safety of the UV/EB Curing Process 2 Abstract The coatings and paint industries strive to provide high technology coatings while reducing volatile organic compounds (V.O.C.s) and energy consumption to
More informationDMPA Dimethylolpropionic Acid in Fast Drying Water Soluble Enamels
DMPA Dimethylolpropionic Acid in Fast Drying Water Soluble Enamels DMPA Dimethylolpropionic Acid TECHNICAL BULLETIN #4 North America 300 Brookside Avenue Building #23, Suite 100 Ambler, PA 19002 USA +1
More informationACRYSOL TT-935 Rheology Modifier
Technical Data Sheet ACRYSOL TT-935 Rheology Modifier Description ACRYSOL TT-935 Rheology Modifier offers a low cost/high performance alternative to cellulosic thickeners in interior flat to semigloss
More informationNew routes to sol-gel systems
New routes to sol-gel systems Polymer-based process extends scope of organic-inorganic coatings. Uwe Wienhold, Ulrich Westerwelle. Hybrid organic-inorganic coatings can be readily prepared by the sol-gel
More informationADVANCES IN WATERBORNE RHEOLOGY MODIFIERS: IMPROVING THICKENING EFFICIENCY IN LOW TO ZERO VOC ARCHITECTURAL PAINT FORMULATIONS
ADVANCES IN WATERBORNE RHEOLOGY MODIFIERS: IMPROVING THICKENING EFFICIENCY IN LOW TO ZERO VOC ARCHITECTURAL PAINT FORMULATIONS By Dr. Mihai Polverejan, Group Leader, Construction and Yaw Aidoo, Group Leader,
More informationACRYSOL TM RM-8WE Rheology Modifier
Technical Data Sheet ACRYSOL TM RM-8WE Rheology Modifier For Water Based Coatings Regional Product Availability EMEAI Summary ACRYSOL RM-8WE Rheology Modifier is a non-ionic urethane type polymer, designed
More informationStandard Glossary of Food Contact Material Inks and Coatings Terms
1 Standard Glossary of Food Contact Material Inks and Coatings Terms Acrylic binder Additive Basecoat Binder/ Vehicle Non-reactive Styrene-acrylate-copolymers or pure acrylate polymers as a resin solution
More informationFomrez catalyst UL-50
Technical Data Sheet Fomrez catalyst UL-50 Description Momentive Performance Materials offers the Fomrez line of tin catalysts. This line of world-class organometallic tin(iv) catalysts is one of the broadest
More informationImproving the Performance of UV Curable Coatings with Carbon Nanomaterials
Improving the Performance of UV Curable Coatings with Carbon Nanomaterials Yun JIANG 1, Andy ZHANG 2, 3, Steven YU 3, Nick YIN 3, Willy DU 3, Tao ZHANG 1,* 1. College of Engineering and Applied Sciences,
More informationNanoparticles for coatings. Why is reality so much less than the promise? Professor Steven Abbott R&T Director MacDermid Autotype Ltd
Nanoparticles for coatings. Why is reality so much less than the promise? Professor Steven Abbott R&T Director MacDermid Autotype Ltd Background to the problem MacDermid Autotype make high quality coated
More informationLevasil and Bindzil colloidal silica dispersions. for the adhesive industry uses and benefits
and Bindzil colloidal silica dispersions for the adhesive industry uses and benefits Colloidal silicas from Eka at a glance and Bindzil are aqueous colloidal dispersions of amorphous silica. They can be
More informationCatalisi e stabilizzazione di schiume PIR: recenti sviluppi
Catalisi e stabilizzazione di schiume PIR: recenti sviluppi Milano, 25 Maggio 2017 Jobst Grimminger Andrea Stefani Introduction With high energy costs, increasing importance is being placed on insulation
More informationApplications of Neuburg Siliceous Earth in Coatings and Related Systems. We supply material for good ideas
Applications of Neuburg Siliceous Earth in Coatings and Related Systems We supply material for good ideas Contents related 1. Coatings 2. Coatings related 3. New Applications 2 Electro Deposition Paints
More informationIn this place, the following terms or expressions are used with the meaning indicated:
B05D PROCESSES FOR APPLYING LIQUIDS OR OTHER FLUENT MATERIALS TO SURFACES, IN GENERAL (apparatus for applying liquids or other fluent materials to surfaces B05B, B05C; {coating of foodstuffs A23P 20/17,
More informationPAINT COATINGS WITH HIGHER HYDROPHOBICITY FOR PROTECTION AGAINST ICE ACCRETION
17th International Symposium on Ice Saint Petersburg, Russia, 21-25 June 2004 International Association of Hydraulic Engineering and Research Session A PAINT COATINGS WITH HIGHER HYDROPHOBICITY FOR PROTECTION
More informationStudy on Military Polyurethane Adhesive
Research Paper Study on Military Polyurethane Adhesive Changming Zhang 1 *, Zhanggen Huang 1, Jun Ping Li 2 and Xiao Juan Lu 2 1 State Key Lab. of Coal Conversion, Institute of Coal Chemistry, Chinese
More informationCharacterization of Polymerization of Isocyanate Resin and Phenolic Resins of Different Molecular weights. Part I: morphology and structure analysis
SWST 2015 International Convention Characterization of Polymerization of Isocyanate Resin and Phenolic Resins of Different Molecular weights. Part I: morphology and structure analysis Xiaomei Liu Department
More informationChapter 4 Acrylic Polyurethane Emulsion Polymers
Chapter 4 Acrylic Polyurethane Emulsion Polymers In this chapter, isophorone diisocyanate (IPDI), a cycloaliphatic diisocyanate, has been selected to react with the different types of hydroxyl acrylic
More informationRHEOLOGY AG.02/2005 AG0905
RHEOLOGY Rheology Basics TYPES OF RHEOLOGICAL BEHAVIOUR NEWTONIAN FLOW PSEUDOPLASTICITY SHEAR THINNING FLOW (case with Yield Value) THIXOTROPY Yield Value Viscosity Viscosity Viscosity Shear Rate. Shear
More informationThe present chapter deals with synthesis of Polyurethane acrylate Oligomers.
The present chapter deals with synthesis of Polyurethane acrylate Oligomers. 2.1 Principle reactions in preparation of UV-curable polyurethane acrylates oligomers If polymer chain carries -NCO group as
More informationIntroduction. Photoresist : Type: Structure:
Photoresist SEM images of the morphologies of meso structures and nanopatterns on (a) a positively nanopatterned silicon mold, and (b) a negatively nanopatterned silicon mold. Introduction Photoresist
More informationImproving Adhesion: Examining the Electrochemistry of Organic Inhibitors
Improving Adhesion: Examining the Electrochemistry of rganic Inhibitors Benefits of rganics Chemisorb onto metallic substrates Complex with metal ions at substrate Neutralize & absorb the corrodents Decrease
More informationCarboset CR-717 Acrylic Copolymer Emulsion TECHNICAL DATA SHEET
Acrylic Copolymer Emulsion TECHNICAL DATA SHEET General Description Carboset CR-717 resin is a non-yellowing, water white hydroxy-functional acrylic copolymer emulsion designed to be crosslinked for optimal
More informationNovel UV Curable Polyurethanes from Glycidyl Carbamate (GC) Resins
ovel UV Curable Polyurethanes from Glycidyl Carbamate (GC) Resins Umesh D. arka 1, Dusty Pfundhelle 1, Andrew J. Muehlber 1 and Dean C. Webste 1* Department of Coatings and Polymeric Materials orth Dakota
More informationNovel Isocyanate-Reactive Adhesives for Structural Wood Based Composites (LVL) ITP Forest Products Peer Review April 5-6, 2006
Novel Isocyanate-Reactive Adhesives for Structural Wood Based Composites (LVL) ITP Forest Products Peer Review April 5-6, 2006 Outline I. General Project Information II. Delamination Tests III. Mechanical
More informationNew types of silicone resin open up wider fields of application. By Marco Heuer, Evonik Resource Efficiency GmbH.
50 SILICONE RESINS Source: by-studio - Fotolia.com TAKING THE HEAT New types of silicone resin open up wider fields of application. By Marco Heuer, Evonik Resource Efficiency GmbH. The properties of the
More informationAssoc. Prof. Dr. Ruta MINIOTAITE
KAUNAS UNIVERSITY OF TECHNOLOGY, LITHUANIA VAPOUR PERMEABILITY AND WATER ABSORPTION OF DIFFERENT EXTERIOR PAINT SYSTEMS Assoc. Prof. Dr. Ruta MINIOTAITE Increasing focus on the durability aspects of buildings
More informationStudies on Furan Polymer Concrete
Studies on Furan Polymer Concrete Rajesh Katiyar 1, Shobhit Shukla 2 1Associate Professor, Department of Chemical engineering, H.B.T.U., Kanpur-208002, India 2Research Scholar, Department of Chemical engineering
More informationACRIFIX. Adhesives and Auxiliaries
ACRIFIX Adhesives and Auxiliaries For a perfect union PLEXIGLAS, the world s first acrylic, manufactured by our company, can be joined by a variety of methods. A distinction is made between permanent and
More informationRosin resin dispersions for the package printing industry
Rosin resin dispersions for the package printing industry Dr. M. Eva Ramos 1 Masami Aihara 1, Tony Dallavia 2, Wietze Bakker 3, John Hazen 3, Anton de Krom 1, David Bainbridge 2 1 Lawter BVBA, Kallo, Belgium
More informationNEW OLIGOMERS DESIGNED TO ENHANCE FORMULATING UV/EB PRESSURE SENSITIVE ADHESIVES
NEW OLIGOMERS DESIGNED TO ENHANCE FORMULATING UV/EB PRESSURE SENSITIVE ADHESIVES Deborah A. Smith, Sr. Application Chemist, UV/EB Adhesives, Sartomer Company, Exton, PA Introduction Pressure sensitive
More informationHELOXY Epoxy Functional Modifiers
Product Selector HELXY Epoxy Functional Modifiers Momentive's epoxy functional product line of HELXY Modifiers offers formulators the ability to choose between monofunctional and polyfunctional glycidyl
More informationYou are now at HOME NEWS PUBLICATIONS LECTURES PATENTS DOWNLOADS
You are now at www.wernerblank.com HOME NEWS PUBLICATIONS LECTURES PATENTS DOWNLOADS ADDITIVES FOR HIGH SOLIDS AND WATER-BORNE COATINGS Werner J. Blank, Rudy Berndlmaier and Dan Miller King Industries
More informationFilm Formation from Industrial Waterborne Latices
Film Formation from Industrial Waterborne Latices I. Ludwig*, W. Schabel*, J.-C. Castaing**, P. Ferlin**, M. Kind* *Universität Karlsruhe (TH), Germany **Rhodia Recherches, Aubervilliers, France Abstract
More informationHyperbranched urethane-acrylates
Hyperbranched urethane-acrylates Hyperbranched urethane-acrylates based on alkoxylated hydroxy acrylates combine high molecular weight, excellent reactivity and good coating properties, such as hardness,
More informationProduct Guide L-G 6. Additives for Aqueous Coatings
Additives for Aqueous Coatings Additives for Aqueous Coatings Content Wetting and Dispersing Additives Page 3 Defoamers Page 4 Rheology Additives Page 5 Surface Additives: Silicones, Waxes and Others Page
More informationChemicals BV CH = C - C - O - - O - P - OH. Technology. PolySurF. Functional Monomers Radiation Curing Additives. for tomorrow s
Chemicals BV for tomorrow s Technology CH = C - C - - - - P - H 2 CH 3 R PolySurF Functional Monomers Radiation Curing Additives for tomorrow s World 2 Contents 1. Introduction 4 2. Properties 5 2.1 ADDAPT
More informationAcetals, more than solvents. Expanding Chemistry 8-9 November 2017
Acetals, more than solvents Expanding Chemistry 8-9 November 2017 Acetals RANGE 2 Acetals Name Methylal Formula CH3-O-CH2-O-CH3 Ethylal CH3-CH2-O-CH2-O-CH2-CH3 Propylal CH3-CH2-CH2-O-CH2-O-CH2-CH2-CH3
More informationTEPZZ A T EP A2 (19) (11) EP A2. (12) EUROPEAN PATENT APPLICATION published in accordance with Art.
(19) TEPZZ 644668A T (11) EP 2 644 668 A2 (12) EUROPEAN PATENT APPLICATION published in accordance with Art. 13(4) EPC (43) Date of publication: 02..13 Bulletin 13/ (21) Application number: 1274694.2 (22)
More informationBio-compatible polymer coatings using low temperature, atmospheric pressure plasma
High Performance and Optimum Design of Structures and Materials 579 Bio-compatible polymer coatings using low temperature, atmospheric pressure plasma S. Farhat, M. Gilliam, A. Zand & M. Rabago-Smith Department
More informationMetal Containing Acrylic Oligomers. Gary W. Ceska, Catherine Leroy, Bill Schaeffer, Sartomer, USA
Metal Containing Acrylic Oligomers Gary W. Ceska, Catherine Leroy, Bill Schaeffer, Sartomer, USA Introduction Many papers have been written describing metal containing oligomers. (1, 2, 3) Little has been
More informationPVOH with Special Performance
PVOH with Special Performance Shuki OGAWA Manager The Nippon Synthetic Chemical Industry Co., Ltd. (Nippon Gohsei) PVOH with Special Performance The Nippon Synthetic Chemical Industry Co., Ltd. China Office
More informationASC Fall Conference October 18, 2016
ASC Fall Conference October 18, 2016 NonMigratory Surfactants in Emulsion Polymerization By : Dr. Steven Y. Chan Agenda Introduction Surfactants in Emulsion Polymerization NonMigratory Surfactants (NMS)
More informationOperating Characteristics of Diene-Urethane Elastomers on the base of NISSOG 3000 Oligodienediol
ORIENTAL JOURNAL OF CHEMISTRY An International Open Free Access, Peer Reviewed Research Journal www.orientjchem.org ISSN: 0970-020 X CODEN: OJCHEG 2016, Vol. 32, No. (5): Pg. 2363-2370 Operating Characteristics
More informationADHESION MECHANISMS FOR AUTOMOTIVE PLASTIC PARTS
ADHESION MECHANISMS FOR AUTOMOTIVE PLASTIC PARTS Dr. Marcos Fernandes de Oliveira 1 1 DuPont do Brasil S.A. - São Paulo Brazil Contacting the author: marcos-fernandes.oliveira@bra.dupont.com marcosfernandes1@yahoo.com.br
More informationSynthesis and properties of aqueous polyurethane dispersions: Influence of molecular weight of polyethylene glycol
Korean J. Chem. Eng., 30(12), 2259-2263 (2013) DOI: 10.1007/s11814-013-0166-9 INVITED REVIEW PAPER pissn: 0256-1115 eissn: 1975-7220 Synthesis and properties of aqueous polyurethane dispersions: Influence
More informationPreparation of Water-borne Polyurethane-acrylate (PUA) and Application to UV-curing Coatings on the Package of Paper
Preparation of Water-borne Polyurethane-acrylate (PUA) and Application to UV-curing Coatings on the Package of Paper Liu Xiaoxuan *, Hong Peng, Duan Lunyong and Li Yuanpei Department of Polymeric Materials
More informationPOLYTONE P Series/Rosin Modified Phenolic Resin MPE Series/Modified Rosin Esters
POLYTONE P Series/Rosin Modified Phenolic Resin MPE Series/Modified Rosin Esters POLYOLS & POLYMERS PVT. LTD. REGD. OFFICE & WORKS -1 (VAPI): C-1/58-59, G.I.D.C. VAPI 396 195 GUJARAT STATE INDIA info@polyolsandpolymers.net
More informationEvaluation of Bonding Performance and Interface of Birch with API Adhesive
The Open Materials Science Journal, 2011, 5, 21-27 21 Open Access Evaluation of Bonding Performance and Interface of Birch with API Adhesive Yanhua Zhang 1,2, Jiyou Gu *,1, Haiyan Tan 1, and Wengxiangli
More informationIntroduction to the Basics of UV/EB Chemistry and Formulations
Introduction to the Basics of UV/EB Chemistry and Formulations SUNY ESF Radiation Curing Program RadTech NA Dr. Mike J. Idacavage Colorado Photopolymer Solutions September 9, 2015 Agenda Introduction to
More informationA New Dielectrophoretic Coating Process for Depositing Thin Uniform Coatings on Films and Fibrous Surfaces
A New Dielectrophoretic Coating Process for Depositing Thin Uniform Coatings on Films and Fibrous Surfaces by Angelo Yializis Ph.D., Xin Dai Ph.D. Sigma Technologies International Tucson, AZ USA SIGMA
More information