Interfacial Defects. Grain Size Determination

Similar documents
CHAPTER 3 THE STRUCTURE OF CRYSTALLINE SOLIDS PROBLEM SOLUTIONS

Introduction To Materials Science FOR ENGINEERS, Ch. 5. Diffusion. MSE 201 Callister Chapter 5

HW #3. Concentration of nitrogen within the surface (at the location in question), C B = 2 kg/m3

DIFFUSION IN SOLIDS. IE-114 Materials Science and General Chemistry Lecture-5

Diffusion. Diffusion. Diffusion in Solid Materials

N = N A Pb A Pb. = ln N Q v kt. = kt ln v N

CHAPTER 6 MECHANICAL PROPERTIES OF METALS PROBLEM SOLUTIONS

Practice Problems Set II

water adding dye partial mixing homogenization time

CHAPTER 4 IMPERFECTIONS IN SOLIDS PROBLEM SOLUTIONS

For this activity, all of the file labels will begin with a Roman numeral IV.

Activity 8b - Electric Field Exploration

Module 16. Diffusion in solids II. Lecture 16. Diffusion in solids II

Steady-state diffusion is diffusion in which the concentration of the diffusing atoms at

ME 254 MATERIALS ENGINEERING 1 st Semester 1430/ st Med-Term Exam (1.5 hrs)

Materials for Civil and Construction Engineers CHAPTER 2. Nature of Materials

Logarithms Dr. Laura J. Pyzdrowski

Computer simulation of radioactive decay

Mass Transfer Operations I Prof. Bishnupada Mandal Department of Chemical Engineering Indian Institute of Technology, Guwahati

n i exp E g 2kT lnn i E g 2kT

3.022 Microstructural Evolution in Materials

ECE 474: Principles of Electronic Devices. Prof. Virginia Ayres Electrical & Computer Engineering Michigan State University

THE STRUCTURE OF CRYSTALLINE SOLIDS PROBLEM SOLUTIONS

SAT RELEASED TEST ADMINISTERED ON APRIL 10, 2018 CLASSROOM SAT SESSION #6

Optimization. f 0, relative maximum

Chapter 5: Diffusion (2)

States of Matter; Liquids and Solids. Condensation - change of a gas to either the solid or liquid state

2nd. The TI-30XIIS Calculator and Fractions, Mixed Numbers and Decimals These are the buttons we will be using to calculate fractions.

Report Form for Experiment 6: Solid State Structures

MSE 360 Exam 1 Spring Points Total

Lab 1 Uniform Motion - Graphing and Analyzing Motion

2. As gas P increases and/or T is lowered, intermolecular forces become significant, and deviations from ideal gas laws occur (van der Waal equation).

X-ray fluorescence analysis - calibration of the X-ray energy detector

Electric Field PHYS 296

Electrochemistry. Part I: Electrochemical Activity from Chemical Reactions. Part II. Electrochemical activity from cell potentials.

EGN 3365 Review on Bonding & Crystal Structures by Zhe Cheng

EMA5001 Lecture 2 Interstitial Diffusion & Fick s 1 st Law. Prof. Zhe Cheng Mechanical & Materials Engineering Florida International University

RedOx Chemistry. with. Dr. Nick

Diffusion in Solid State

CHEM1902/ N-2 November 2014

Atomic Arrangement. Primer in Materials Spring

Dr. White Chem 1B Saddleback College 1. Experiment 15 Thermodynamics of the Solution Process

α m ! m or v T v T v T α m mass

Chapter 3. The structure of crystalline solids 3.1. Crystal structures

Chapter 12: Structures & Properties of Ceramics

Introduction to Quantitative Metallography

CHAPTER 12 STRUCTURES AND PROPERTIES OF CERAMICS PROBLEM SOLUTIONS

Experiment 2a Models of the Solid State*

Uniformly Accelerated Motion

Experiment Flow Analysis

Physics 103 Newton s 2 nd Law On Atwood s Machine with Computer Based Data Collection

Metal Structure. Chromium, Iron, Molybdenum, Tungsten Face-centered cubic (FCC)

CHAPTER 12 ELECTRICAL PROPERTIES PROBLEM SOLUTIONS

Chapter 10 Liquids, Solids and Phase Changes

Activity 5&6: Metals and Hexagonal Close-Packing

Honors Chemistry Dr. Kevin D. Moore

Cart on a Ramp. Evaluation Copy. Figure 1. Vernier Dynamics Track. Motion Detector Bracket

Computer Aided Process Plant Design

Liquids, Solids and Phase Changes

FIRST MIDTERM EXAM Chemistry March 2011 Professor Buhro

KINETICS II - THE IODINATION OF ACETONE Determining the Activation Energy for a Chemical Reaction

CHAPTER 7 MECHANICAL PROPERTIES PROBLEM SOLUTIONS

Appendix. Using Your Calculator. Squares, Square Roots, Reciprocals, and Logs. Addition, Subtraction, Multiplication, and Division

Final Examination 201-NYA-05 May 18, 2018

What determines the phase of a substance? Temperature Pressure Interparticle Forces of Attraction

ENGR 151: Materials of Engineering MIDTERM 1 REVIEW MATERIAL

Intermolecular Forces and States of Matter AP Chemistry Lecture Outline

3D - Structure Graphics Capabilities with PDF-4 Database Products

Name (Print) Section # or TA. 1. You may use a crib sheet which you prepared in your own handwriting. This may be

Math 114 Spring 2013 Final Exam

3.091 Introduction to Solid State Chemistry. Lecture Notes No. 9a BONDING AND SOLUTIONS

Multiphysics Modeling

CHAPTER 6 Modern Theory Principles LECTURER SAHEB M. MAHDI

Chemical Kinetics I: The Dry Lab. Up until this point in our study of physical chemistry we have been interested in

More Differentiation Page 1

Chapter 13 - Chemical Kinetics II. Integrated Rate Laws Reaction Rates and Temperature

ElectroChemistry * Section I: Reactivity of Metals and Metal Ions PRELAB

Chem 112 Dr. Kevin Moore

PY2N20 Material Properties and Phase Diagrams

Materials Engineering 272-C Fall 2001, Lecture 7 & 8 Fundamentals of Diffusion

Contents. 13. Graphs of Trigonometric Functions 2 Example Example

Hg2 2+ (aq) + H2(g) 2 Hg(l) + 2H + (aq)

UNIVERSITY OF SOUTHAMPTON VERY IMPORTANT NOTE. Section A answers MUST BE in a separate blue answer book. If any blue

Lecture 1: Atomic Diffusion

Finite Element Modules for Enhancing Undergraduate Transport Courses: Application to Fuel Cell Fundamentals

2. As gas P increases and/or T is lowered, intermolecular forces become significant, and deviations from ideal gas laws occur (van der Waal equation).

RADIOACTIVITY MATERIALS: PURPOSE: LEARNING OBJECTIVES: DISCUSSION:

UNIT-1 SOLID STATE. Ans. Gallium (Ga) is a silvery white metal, liquid at room temp. It expands by 3.1% on solidifica-tion.

3-D Crystal Lattice Images

Exam Thermodynamics 12 April 2018

Grade 11 Mathematics Practice Test

Chem. 112 spring 2012 Exam 1 7:30am/Odago Wednesday March 7, 2012

7. A capacitor has been charged by a D C source. What are the magnitude of conduction and displacement current, when it is fully charged?

1 8 =1 8 8 =1 6 =3. Unit cell Atoms at corner Atoms at faces Atoms at centre. Total no. of atoms per unit cell. bcc. fcc

Exsolution and Ordering in Solid Solutions

Atomic Arrangement. Primer Materials For Science Teaching Spring

Data Mining with the PDF-4 Databases. FeO Non-stoichiometric Oxides

a. Follow the Start-Up Procedure in the laboratory manual. Note the safety rules.

M61 1 M61.1 PC COMPUTER ASSISTED DETERMINATION OF ANGULAR ACCELERATION USING TORQUE AND MOMENT OF INERTIA

Mathematical Modeling of Electrodeposition

Transcription:

Interfacial Defects 4.27 For an FCC single crystal, would you expect the surface energy for a (00) plane to be greater or less than that for a () plane? Why? (Note: You may want to consult the solution to Problem 3.54 at the end of Chapter 3.) The surface energy for a crystallographic plane will depend on its packing density [i.e., the planar density (Section 3.)] that is, the higher the packing density, the greater the number of nearest-neighbor atoms, and the more atomic bonds in that plane that are satisfied, and, consequently, the lower the surface energy. From the solution to Problem 3.54, planar densities for FCC (00) and () planes are 4R 2 and 2R 2 3, respectively that is 0.25 0.29 and R2 R 2 (where R is the atomic radius). Thus, since the planar density for () is greater, it will have the lower surface energy. Grain Size Determination 4.32 (a) Using the intercept method, determine the average grain size, in millimeters, of the specimen whose microstructure is shown in Figure 4.4(b); use at least seven straight-line segments. (b) Estimate the ASTM grain size number for this material. (a) Below is shown the photomicrograph of Figure 4.4(b), on which seven straight line segments, each of which is 60 mm long has been constructed; these lines are labeled through 7.

In order to determine the average grain diameter, it is necessary to count the number of grains intersected by each of these line segments. These data are tabulated below. Line Number No. Grains Intersected 2 0 3 9 4 8.5 5 7 6 0 7 8 The average number of grain boundary intersections for these lines was 9.. Therefore, the average line length intersected is just 60 mm 9. = 6.59 mm Hence, the average grain diameter, d, is d = ave. line length intersected magnification = 6.59 mm 00 = 6.59 0 2 mm

(b) This portion of the problem calls for us to estimate the ASTM grain size number for this same material. The average grain size number, n, is related to the number of grains per square inch, N, at a magnification of 00 according to Equation 4.6. Inasmuch as the magnification is 00, the value of N is measured directly from the micrograph. The photomicrograph on which has been constructed a square in. on a side is shown below. The total number of complete grains within this square is approximately 0 (taking into account grain fractions). Now, in order to solve for n in Equation 4.6, it is first necessary to take logarithms as log N = (n ) log 2 From which n equals n = log N log 2 + = log 0 log 2 + = 4.3 4.35 Determine the ASTM grain size number if 25 grains per square inch are measured at a magnification of 600. This problem asks that we determine the ASTM grain size number if 8 grains per square inch are measured at a magnification of 600. In order to solve this problem we make use of Equation 4.7:

2 M N M 00 = 2 n where N M = the number of grains per square inch at magnification M, and n is the ASTM grain size number. Solving the above equation for n, and realizing that N M = 8, while M = 600, we have n = M log N M + 2 log 00 + log 2 = log 8 + 2 log 600 00 log 2 + = 9.2 CHAPTER 5 5. Briefly explain the difference between self-diffusion and interdiffusion. Self-diffusion is atomic migration in pure metals--i.e., when all atoms exchanging positions are of the same type. Interdiffusion is diffusion of atoms of one metal into another metal. 5.4 Briefly explain the concept of steady state as it applies to diffusion. Steady-state diffusion is the situation wherein the rate of diffusion into a given system is just equal to the rate of diffusion out, such that there is no net accumulation or depletion of diffusing species--i.e., the diffusion flux is independent of time. 5.6 The purification of hydrogen gas by diffusion through a palladium sheet was discussed in Section 5.3. Compute the number of kilograms of hydrogen that pass per hour through a 5-mm-thick sheet of palladium having an area of 0.20 m 2 at 500 C. Assume a diffusion coefficient of.0 0-8 m 2 /s, that the concentrations at the high- and lowpressure sides of the plate are 2.4 and 0.6 kg of hydrogen per cubic meter of palladium, and that steady-state conditions have been attained.

This problem calls for the mass of hydrogen, per hour, that diffuses through a Pd sheet. It first becomes necessary to employ both Equations 5.a and 5.3. Combining these expressions and solving for the mass yields M = JAt = DAt C x = (.0 0-8 m 2 /s)(0.20 m 2 0.6 2.4 kg / m3 ) (3600 s/h) 5 0 3 m = 2.6 0-3 kg/h 5.7 Using the data in Table 5.2, compute the value of D for the diffusion of zinc in copper at 650ºC. Incorporating the appropriate data from Table 5.2 into Equation 5.8 leads to D = (2.4 0-5 m 2 89, 000 J/mol /s) exp (8.3 J/mol- K)(650 + 273 K) = 4.8 0-6 m 2 /s Note: this problem may also be solved using the Diffusion module in the VMSE software. Open the Diffusion module, click on the D vs /T Plot submodule, and then do the following:. In the left-hand window that appears, click on the Zn-Cu pair under the Diffusing Species - Host Metal headings. 2. Next, at the bottom of this window, click the Add Curve button. 3. A log D versus /T plot then appears, with a line for the temperature dependence of the diffusion coefficient for Zn in Cu. Now under Temp Range in the boxes appearing below T Max change the temperature to either 650 C or 923 K. At the top of this curve is a diamond-shaped cursor. Click-and-drag this cursor down the line to the point at which the entry under the Temperature (T): label reads 923 K (inasmuch as this is the Kelvin equivalent of 650ºC). Finally, the diffusion coefficient value at this temperature is given under the label Diff Coeff (D):. For this problem, the value is 4.7 0-6 m 2 /s.

5.2 The diffusion coefficients for iron in nickel are given at two temperatures: T (K) D (m 2 /s) 273 9.4 0 6 473 2.4 0 4 (a) Determine the values of D 0 and the activation energy Q d. (b) What is the magnitude of D at 00ºC (373 K)? (a) Using Equation 5.9a, we set up two simultaneous equations with Q d and D 0 as unknowns as follows: ln D = lnd 0 Q d R T ln D 2 = lnd 0 Q d R T 2 Now, solving for Q d in terms of temperatures T and T 2 (273 K and 473 K) and D and D 2 (9.4 0-6 and 2.4 0-4 m 2 /s), we get Q d = R ln D ln D 2 T T 2 = (8.3 J/mol - K) [ ln (9.4 0-6 ) ln (2.4 0-4 )] 273 K 473 K = 252,400 J/mol Now, solving for D 0 from Equation 5.8 (and using the 273 K value of D) D 0 = D exp Q d RT = (9.4 0-6 m 2 252, 400 J/mol /s)exp (8.3 J/mol- K)(273 K)

= 2.2 0-5 m 2 /s (b) Using these values of D 0 and Q d, D at 373 K is just D = (2.2 0-5 m 2 252, 400 J/mol /s)exp (8.3 J/mol- K)(373 K) = 5.4 0-5 m 2 /s Note: this problem may also be solved using the Diffusion module in the VMSE software. Open the Diffusion module, click on the D0 and Qd from Experimental Data submodule, and then do the following:. In the left-hand window that appears, enter the two temperatures from the table in the book (viz. 273 and 473, in the first two boxes under the column labeled T (K). Next, enter the corresponding diffusion coefficient values (viz. 9.4e-6 and 2.4e-4 ). 3. Next, at the bottom of this window, click the Plot data button. 4. A log D versus /T plot then appears, with a line for the temperature dependence for this diffusion system. At the top of this window are give values for D 0 and Q d ; for this specific problem these values are 2.7 0-5 m 2 /s and 252 kj/mol, respectively 5. To solve the (b) part of the problem we utilize the diamond-shaped cursor that is located at the top of the line on this plot. Click-and-drag this cursor down the line to the point at which the entry under the Temperature (T): label reads 373. The value of the diffusion coefficient at this temperature is given under the label Diff Coeff (D):. For our problem, this value is 5.4 0-5 m 2 /s.