Asymmetric block copolymer membranes with ultrahigh porosity and hierarchical pore structure by plain solvent evaporation

Similar documents
Supplementary Information

SUPPORTING INFORMATION

Interaction of Gold Nanoparticle with Proteins

Supplementary Information

Infused Porous Polyelectrolyte Multilayers

The SAXS Guide. Getting acquainted with the principles. New Edition with special contributions

Hierarchically Structured Nanoporous Poly(Ionic Liquid) Membranes: Facile Preparation and Application in Fiber-optic ph Sensing

Supporting Information

Micro- and Nano-Fabrication of Stimuli-Responsive Polymers

Supporting Information

Supplementary Information

Encapsulation of enzyme in metal ion-surfactant nanocomposites for

Dumpling-Like Nanocomplex of Foldable Janus Polymer Sheet and Sphere

Digitized single scattering nanoparticles for probing molecular binding

Supplementary Information

Self-Assembled Asymmetric Block Copolymer Membranes: Bridging the Gap from Ultra- to Nanofiltration

SUPPORTING INFORMATION

Supporting Information

Single-walled carbon nanotubes as nano-electrode and nanoreactor to control the pathways of a redox reaction

Electronic Supplementary Information. Molecular Antenna Tailored Organic Thin-film Transistor for. Sensing Application

Self-assembly of PEGylated Gold Nanoparticles. with Satellite Structures as Seeds

Salt-induced Hydrogelation of Functionalised-Dipeptides at high ph

Supracolloidal Polymer Chains of Diblock Copolymer Micelles

Supporting Information

Supporting Information

Electronic Supplementary Information

Nanoporous Organosilica Membrane for Water Desalination

Supplementary materials for Gels and Threads: Mussel-inspired One-pot Route to Advanced Responsive Materials

Transformation of Pd PdH 0.7 nanoparticles inside the mesoporous Zr-modified SiO 2 films in ambient conditions

Visualizing the bi-directional electron transfer in a Schottky junction consisted of single CdS nanoparticles and a planar gold film

Supplementary Material (ESI) for Chemical Communications This journal is (c) The Royal Society of Chemistry 2009

Fabrication and characterization of poly (ethylene oxide) templated nickel oxide nanofibers for dye degradation

Supporting Information. Oleic Acid-Induced Atomic Alignment of ZnS Polyhedral Nanocrystals

Colloidal Particles with Complex Microstructures via Phase Separation in Swelled Polymer Microspheres

Electronic Supplementary Information

High-Purity Separation of Gold Nanoparticle Dimers and Trimers

Electronic Supplementary Information

SUPPLEMENTARY INFORMATION

Electronic Supplementary Information (ESI) From metal-organic framework to hierarchical high surface-area hollow octahedral carbon cages

Supplementary Information

Supporting Information

High-Performance Semiconducting Polythiophenes for Organic Thin Film. Transistors by Beng S. Ong,* Yiliang Wu, Ping Liu and Sandra Gardner

Shape Assisted Fabrication of Fluorescent Cages of Squarate based Metal-Organic Coordination Frameworks

One-pot polymer brush synthesis via simultaneous isocyanate coupling chemistry and grafting from RAFT polymerization

Facile Synthesis of Gold Wavy Nanowires and Investigation of

The ph-responsive behaviour of aqueous solutions of poly(acrylic acid) is dependent on molar mass

Constructed from Amino Carrier Containing Nanorods and. Macromolecules**

Electronic Supplementary Information. Tubulation of Liposomes via the Interaction of Supramolecular Nanofibers

Supporting Information

Scanning Electron Microscopy (SEM) with Energy Dispersive Spectroscopy (EDS) Analysis The samples were also characterized by scanning electron

Supporting Information for: Emulsion-assisted synthesis of monodisperse binary metal nanoparticles

Electronic Supplementary Information (ESI)

The morphology of PVDF/1Gra and PVDF/1IL/1Gra was investigated by field emission scanning

Supporting Materials Ultra-small Sub-10 nm Near Infrared Fluorescent Mesoporous Silica Nanoparticles

Supplementary Information

Direct measurements of exciton diffusion length limitations on organic solar cell performance

Fabrication of COF-MOF Composite Membranes and Their Highly. Selective Separation of H 2 /CO 2

Supplementary Information. Self-assembly of PS-PNaSS-PS triblock copolymers from solution to solid state

Electronic Supplementary Information

Novel Tri-Block Copolymer of Poly (acrylic acid)-b-poly (2,2,3,3,4,4,4- hexafluorobutyl acrylate)-b-poly (acrylic acid) Prepared via Two-Step

Supporting Information

Carbon nanotube coated snowman-like particles and their electro-responsive characteristics. Ke Zhang, Ying Dan Liu and Hyoung Jin Choi

Turn-On Detection of Pesticides via Reversible Fluorescence Enhancement of Conjugated Polymer Nanoparticles and Thin Films

Biomimetic material - poly(n-vinylimidazole)-zinc complex for CO 2 separation

Supporting Information

Facile Assembly Enhanced Spontaneous Fluorescence Response of Ag + Ion Containing Polyelectrolyte Multilayer Films

Supporting Information for. Long-Distance Charge Carrier Funneling in Perovskite Nanowires Enable by Built-in Halide Gradient

Supramolecular electrospun nanofibers with high conductivity at. ultra-low carbon nanotube content

A facile procedure to fabricate nano. calcium carbonate/polymer-based. superhydrophobic surfaces

Covalent-Organic Frameworks: Potential Host Materials for Sulfur Impregnation in Lithium-Sulfur Batteries

Three-dimensional Multi-recognition Flexible Wearable

A General Synthesis of Discrete Mesoporous Carbon Microspheres through a Confined Self- Assembly Process in Inverse Opals

Fluorescent Labeling and Tracking of Nanoclay

A Research Agenda for a New Era in Separations Science: Understanding Synthesis for Separations. Benny Freeman

Petroleum Thermodynamic Research Group

Supporting information

1. Experimental section

Supporting Information

Supporting Information:

Biodegradable Hollow Silica Nanospheres Containing Gold Nanoparticle Arrays

Membrane Performance Forecast

Study on the Selective Hydrogenation of Nitroaromatics to N-aryl hydroxylamines using a Supported Pt nanoparticle Catalyst

Supplementary Material for. Zinc Oxide-Black Phosphorus Composites for Ultrasensitive Nitrogen

Supporting Information

Permeable Silica Shell through Surface-Protected Etching

A Conjugated Polyelectrolyte-Based New Strategy. for In Situ Detection of Carbon Dioxide

Structure and properties of polyurethane nanocomposites modified by dibutyl phosphate boehmite

Supplementary Information

Supporting Information

- Supporting Information - Controlled Assembly of Eccentrically Encapsulated Gold Nanoparticles

Supporting Information

Controlling Multicompartment Morphologies Using Solvent Conditions and Chemical Modification

Supplemental Information. Lewis-Acid-Catalyzed. Interfacial Polymerization. of Covalent Organic Framework Films

Supplementary Information

Electronic Supplementary Information (ESI) Synthesis of gold nanoparticles in a biocompatible fluid from sputtering deposition onto castor oil

Dual-Wavelength Lasing from Organic Dye Encapsulated Metal-Organic Framework Microcrystals

A Smart Core-sheath Nanofiber that Captures and Releases Red

Bright CuInS 2 /CdS Nanocrystal Phosphors for High-Gain Full-Spectrum Luminescent Solar Concentrators

Supporting information

Supporting Information for

Transcription:

Electronic Supplementary Material (ESI) for ChemComm. This journal is The Royal Society of Chemistry 2016 Electronic Supplementary Information Asymmetric block copolymer membranes with ultrahigh porosity and hierarchical pore structure by plain solvent evaporation Haizhou Yu, Xiaoyan Qiu, Ali Reza Behzad, Valentina Musteata, Detlef-M. Smilgies, Suzana P. Nunes and Klaus-Viktor Peinemann* 1.Hansen solubility parameter The following Hansen solubility parameters [1] are reported for dioxane and the polymer blocks under consideration here: Table S1. Hansen solubility parameters δ d (MPa 1/2 ) δ p (MPa 1/2 ) δ h (MPa 1/2 ) Polystyrene (PS) 21.3 5.8 4.3 Styrene (S) 18.6 1.0 4.1 Acrylic acid (AA) 17.7 6.4 14.9 1,4-Dioxane 19.0 1.8 7.4 d, p and h: dispersive, polar and h-bond contributions to solubility parameters (δ) 1

2. Grazing Incidence Small-Angle X-Ray Scattering (GISAXS) and Small-Angle X-Ray Scattering (SAXS) a) 10 6 q/q* 1; 1.42; 2.5 0/1 1.9/1 0.8/1 2.7/1 1.5/1 3/1 b) d=46.2 nm 0/1 2.7/1 1; 1.44; 2.5 10 7 Intensity (shifted) 10 4 10 2 1; 1.41; 2.55 1; 1.43; 2.56 1; 1.53; 2.65 d = 35.9 nm d = 34.8 nm d = 32.8 nm d = 33.8 nm Intensity (shifted) 10 6 d=40.5 nm 1; 1.5 d = 34 nm d = 33.8 nm 10 0 0.01 0.1 q (A -1 ) 10 5 0.01 0.1 q (A -1 ) Figure S1. (a) In plane GISAXS data for casted membranes with different PS 144 -b-paa 22 / PS 678 -b-paa 180 ratio after 5 min solvent evaporation time. (b) SAXS data for solution pure PS 678 -b-paa 180 and PS 144 -b-paa 22 / PS 678 -b-paa 180 blend with a 2.7 /1 molar ratio. 3. Experimental Details 3.1. Membrane Preparation Polystyrene-b-poly(acrylic acid) block copolymers (PS 144 -b-paa 22, M n = 16,600 g mol -1 and PS 678 -b-paa 180, M n = 83,500 g mol -1 ) were purchased from Polymer Source, Inc., Canada. The subscripts indicate the number of repeat units of the blocks. Dioxane was supplied by Aldrich. The BCP membranes with two mixed molecular weights were cast from a polymer solution mixture of PS 144 -b-paa 22 and PS 678 -b-paa 180 /dioxane on a Hirose TH100 polyester support, using casting blades with 200 μm air gap. The PS 678 -b-paa 180 /dioxane composition was kept constant, i.e., 18.7 wt % copolymer, 81.3 wt % dioxane, while the molar ratio of PS 144 -b-paa 22 to PS 678 -b-paa 180 varied from 0.8:1 to 3:1 in the preparation of different 2

membranes. The solvent was allowed to evaporate completely at room temperature in the fume hood. To study the kinetics of membrane surface phase transition the membranes were dried for different time at room temperature and then immersed in a non-solvent bath (Milli-Q water, 18.2 MΩ). 3.2. Electron Microscopy and Zeta Potential Measurement Field emission scanning electron microscopy (FESEM) images were obtained using a FEI Quanta 600 series microscope at 5kV with a working distance of 10 mm. Cryo-field emission scanning electron microscopy (Cryo-FESEM) experiments were carried out using a Quorum PP2000T cryo-transfer system (Quorum Technologies, Newhaven, U.K.) that was fitted to an FEI Nova Nano630 FESEM with a field-emission electron source and throughlens electron detectors. A small amount of block copolymer blends was dropped on the specimen holder. The sample holder, attached to a transfer rod, was rapidly plunged into liquid-nitrogen slush, transferred under vacuum to the preparation chamber precooled to -180 C, and allowed to equilibrate for 10 min. The sample temperature was raised to -160 C. To avoid charging, the sample temperature was then reduced to -135 C and the sample was sputter coated with gold-palladium for 90 s at a 5 ma current in an argon atmosphere. Then the sample was transferred to a FESEM cryo stage, which was held at -140 C. The membrane surface zeta potential was tested using SurPASS electrokinetic analyzer (Anton Paar, Austria) with background of 10 mm NaCl solution around neutral ph. 3.3. Flux and Rejection Measurements The membranes (diameter 2.2 cm) were tested in a stirred Amicon cell at a pressure of 1.38 bar until 3 ml of a 6 ml starting sample passed through the membranes. The rejection of the proteins was monitored by a NanoDrop 2000/2000c spectrophotometer (Thermo Fisher Scientific). Globulin-γ (IgG, 150 kda), Bovine serum albumin (BSA, 66 kda), Ovalbumin (OVA, 45 kda), Myoglobin (MB, 17 kda), protoporphyrin IX (PpIX, 562 g/mol) and vitamin B12 (VB12, 1355 g/mol) are from Sigma Co., and no further purification was carried out. 3

Transport of VB12 was carried out using a diffusion cell (PermGear, Inc) with two compartments (left and right chambers). The membrane was placed between the two chambers with the ordered top layer toward left side containing the VB12 The effective permeation area of the membrane was 1.77 cm 2. All permeate samples were collected from the right chamber and the concentration was determined by a NanoDrop 2000/2000c spectrophotometer. 3.4. SAXS and GISAXS Measurements In-situ Grazing Incidence Small Angle X-Ray Scattering (GISAXS) experiments were performed at D1 beamline of the Cornell High Energy Synchrotron Source (CHESS). The operating parameters were: a wavelength of the X-ray beam of 0.1162 nm, a sample-todetector distance of 1.82 m and a corresponding beam energy of 10.67 kev. Membranes were casted on a microscope glass slide as support using in-situ doctor blading system existent at the beam-line. A gap of 200 μm was used to cast the membranes. The data were taken immediately after casting at every 3.3 s. The time interval corresponds to 0.3 s exposure and 3 s detector readout time. A pre-alignment of height and incident angle of the beam with the substrate was performed. An incidence angle of 0.13 degrees was used, which is below the critical angle of the substrate and above the critical angle of the polymer film. 2D GISAXS pattern were recorded with a MedOptics CCD camera with a pixel size of (46.9 μm) 2 and 1024 2 pixels. The GISAXS images were analyzed using Igor Pro 6.3 software by taking a horizontal cut that contains details of the size distribution parallel to the sample surface. Using the same software, the position of the peaks was determined by fitting the obtained data with two or three Lorentz functions. Small angle X-ray scattering (SAXS) measurements were performed at the SAXS1 beamline of the Brazilian Synchrotron facility (LNLS), which works at fixed energy of 8.0 kev. The solution was injected with syringe in a vacuum cell with mica windows The X-ray wavelength was 1.764 Å and the sample to detector distance was 1 m. The detector used was 4

PILATUS with a pixel size of (172 μm) 2. The beam area on the sample was 1 mm 2 and a number of 20 frames each with 30 s exposure time were performed. Data was obtained as the average of the integrated 2D patterns, after normalization to the intensity of incident beam and subtraction of background. 4. Permeance and Rejection Results Figure S2a and S2c show both the zeta potential and the water flux of the membrane decreased as the ph increased. The effect of ph on the water flux is mainly due to the change in the swelling and electrostatic repulsion generated by ionization of the PAA blocks. PAA is a weak polyelectrolyte and the amount of charged groups is a function of ph. The carboxylic acid groups were deprotonated at high ph and the PAA segments stretched to minimize the charge repulsion, transforming the pore into a ph-sensitive gate without affecting the overall ordered structure of the membrane. The effect is opposite to that observed in stimuliresponsive PS-b-P4VP isoporous membranes prepared by combining self-assembly with nonsolvent-induced phase separation. Figure S2b shows the cut-off curve of the membrane at different ph, evaluated by filtering biomolecules with sizes ranging from ca. 1.5 to 14 nm in diameter. The effective pore radius of the membrane evaluated from the rejection experiment is ca. 10 nm at ph 3.0 and ca. 2 nm at ph 7.4. The water permeation of the membranes was measured for one day before and after immersion in water, which showed no big difference indicating the stability of the membrane. The ph responsive membrane with tunable nanopores can be used as a sensitive gate controlled by ph without any modification. To evaluate the controlled transport behavior of the membrane, vitamin B12 (VB12) was selected as a model substance. The transport rate of VB12 could be controlled by changing ph values at 37 ºC. At a ph of 7.4 in phosphate-buffered saline (PBS) solution, VB12 was released in a very slow fashion in one day (Figure S2d). When the environmental ph was changed from ph 5

7.4 to ph 3.0, the pores of the membrane change from closed to open, due to the conformational change of the PAA chains. Therefore, the diffusion channels for the VB12 solutes become wider leading to an abrupt release. Figure S2. Performance of the blended membrane of PS 144 -b-paa 22 / PS 678 -b-paa 180 with a molar ratio 2.7/1: (a) zeta potential of this membrane as a function of ph; (b) filtration of biomolecules with sizes of 1.5-14 nm through this membrane; (c) water flux of this membrane as a function of the ph, measured at 1.38 bar feed pressure; (d) release of VB 12 at ph 3.0 and ph 7.4 using this membrane, respectively. 5. Supporting Reference [1] C. M. Hansen, Hansen Solubility Parameters, a User s Handbook, CRC Press, Boca Raton, USA, 2000. 6