Permeable Silica Shell through Surface-Protected Etching
|
|
- Andrea Higgins
- 5 years ago
- Views:
Transcription
1 Permeable Silica Shell through Surface-Protected Etching Qiao Zhang, Tierui Zhang, Jianping Ge, Yadong Yin* University of California, Department of Chemistry, Riverside, California Experimental Chemicals: Tetraethylorthosilicate (TEOS), poly(vinyl pyrrolidone) (PVP, Mw ~ 10,000), sodium hydroxide (NaOH), HAuCl 4, sodium citrate, and ammonium hydroxide (NH 3 H 2 O, 28% by weight in water) were purchased from Sigma-Aldrich. Ethanol and isopropanol were of analytical grade and obtained from Fisher. All chemicals were directly used as received without further purification. Synthesis of SiO 2 solid spheres: In a typical synthesis, 1 ml TEOS was injected into a mixture of 4 ml of deionized H 2 O, 1 ml of NH 3 H 2 O and 20 ml 2-propanol at room temperature under magnetic stirring. After reacting for 2 hours, the colloidal spheres were collected by centrifugation, re-dispersed in 30 ml deionized water. Synthesis of Au@SiO 2 core-shell structures: A gold sol (30 ml) is prepared according to the standard sodium citrate reduction method. Briefly, a solution of hydrogen tetrachloroaurate trihydrate was prepared in water and heated to reflux with magnetic stirring, followed immediately by addition of 1 ml of 3 wt% freshly prepared trisodium citrate-water solution, which initiated the reduction of the hydrogen tetrachloroaurate trihydrate. The aurate-citrate solution was allowed to reflux for approximately 30 min. or until completion of the redox reaction as indicated by a change in solution color from faint yellow to dark red. This method produces a stable, deep-red dispersion of gold particles with an average diameter of around 15 nm and 10% polydispersity. An aqueous solution
2 of PVP (0.235 ml, 12.8 mg/ml) was added to the sol. The mixture was allowed to stand at room temperature for 24 hours under magnetic stirring, allowing PVP molecules to attach to Au nanoparticles, which were then separated from solution by centrifuging at 11,000 rpm for 45 min and re-dispersed in 92 ml ethanol. The as-prepared solution was then mixed with 13.2 ml of deionized H 2 O and 2.48 ml of NH 3 H 2 O. TEOS (3.45 ml) was injected into the mixture at room temperature under stirring. After reacting for 4 hours, the spheres were collected by centrifugation, and finally re-dispersed in 24 ml of deionized water. Etching SiO 2 spheres: PVP K15 (Mw ~ 10,000) was added to the as-prepared solid SiO 2 solution (molar ratio of PVP/SiO 2 is 10). The mixture was heated up to 100 C for 3 hours to load PVP, and then cooled to room temperature. Under magnetic stirring, 1 ml of 0.1 g/ml sodium hydroxide (NaOH) dissolved in water was added to 4 ml of the as-prepared solution at room temperature. As more material is etched away from the silica particles, the solution becomes less and less opaque. Therefore, we were able to monitor the progress of the etching process by measuring transmission through the solution using UV-Vis spectrometry. For the etching completion times reported in Fig 1b, the criterion was 75% transmittance at the wavelength of 700 nm. The solution was cleaned with repeated actions of water dilution and centrifugation. The colloidal spheres were finally dispersed in polar solvents such as deionized water or ethanol. Au@SiO 2 core-shell particles can be etched using a similar procedure. Catalytic reduction of 4-nitrophenol: The reduction of 4-NP by NaBH 4 was chosen as a model reaction to test the catalytic activity and stability of the Au@SiO 2 nanocatalysts. Aqueous solutions of 4-NP (0.03 ml, 0.01M) and NaBH 4 (0.20 ml, 0.1M) were added to deionized water (2.5 ml) in a quartz cuvette under magnetic stirring. After adding yolk-shell Au@SiO 2 catalyst particles (0.02 ml), the bright yellow solution gradually faded as the reaction proceeded. UV-Vis spectra were recorded at regular interval to monitor the progress of the reaction. Characterization: Morphology of the products was characterized by using a Tecnai T12 transmission electron microscope (TEM). The hollow spheres dispersed in water were cast onto a carbon-coated copper grid, followed by evaporation under vacuum at
3 room temperature. Fourier transform infrared (FT-IR) spectra were collected with a Bruker Equinox 55 spectrophotometer scanning from cm -1 with a resolution of 4 cm -1 for 64 scans. Measurements were performed with pressed pellets, which were made by using KBr powder as diluents. Thermo-gravimetric analyses (TGA) were carried out on a Mettler Toledo TGA/SDTA 851e under N 2 atmosphere in the temperature range of C at a rate of 10 C/min. A probe-type Ocean Optics HR2000CG-UV-NIR spectrometer was used to measure the UV-Vis spectra of the solution to monitor the real-time variation of concentration of 4-NP. The integration time was set to be 3 msec. Figure S1. Fourier transform infrared (FTIR) spectra of pure silica (blue line); silica with PVP refluxed at 100 C for 3 hours (red line); the PVP-coated silica spheres after etching (green line); and pure PVP (black line). For as-synthesized solid silica colloids, weak absorption bands between 1350 and 1650 cm -1 are attributed to C-H bending vibration in unhydrolyzed -OEt groups. Both the PVP treated and the etched sample clearly show additional bands centered at about 2968 and 2950 cm -1 which can be assigned to the CH 2 stretching modes of PVP: ν as (CH 2 ) for the pyrrolidone ring, ν as (CH 2 ) for the polymer backbone, respectively. In consistent to previous observations [Saegusa, T., Pure and Applied Chemistry 1995, 67, ], the C=O stretching band of PVP originally at ~1678 cm -1 shifts to a lower frequency to ~1653 cm -1 upon forming a hydrogen bond with silica surface.
4 Figure S2. TEM images showing the structure evolution of 2 core-shell particles: (a) the original samples; and (b-f) the samples after etching by NaOH for (b) 1 hr 30 min, (c) 2 hrs, (d) 2 hr 30 min, (e) 2hr 45min, and (f) 3hrs. All scale bars are 200 nm. Figure S3. UV-vis spectra of Au@SiO 2 yolk-shell structures before (red) and after (blue) twelve successive cycles of reduction/separation.
5 Figure S4. (a) Digital photo showing 4-NP and NaBH 4 solution before adding catalyst (left) and after completing catalytic reaction (right). (b) TEM image of Au@SiO 2 yolk-shell catalyst particles after twelve successive cycles of reduction/separation.
Sacrifical Template-Free Strategy
Supporting Information Core/Shell to Yolk/Shell Nanostructures by a Novel Sacrifical Template-Free Strategy Jie Han, Rong Chen and Rong Guo* School of Chemistry and Chemical Engineering, Yangzhou University,
More informationA Systematic Study of the Synthesis of Silver Nanoplates: Is Citrate a. "Magic" Reagent?
SUPPORTING INFORMATION A Systematic Study of the Synthesis of Silver Nanoplates: Is Citrate a "Magic" Reagent? Qiao Zhang, Na Li,, James Goebl, Zhenda Lu, Yadong Yin*, Department of Chemistry, University
More informationOne-step seeded growth of Au nanoparticles with widely tunable sizes
Electronic Supplementary Information (ESI) One-step seeded growth of Au nanoparticles with widely tunable sizes Chuanbo Gao, John Vuong, Qiao Zhang, Yiding Liu and Yadong Yin* Department of Chemistry,
More informationTetraethyl orthosilicate (TEOS, 99 %), resorcinol, formalin solution (37 wt. %),
Supporting Information A Versatile Cooperative Template-Directed Coating Method to Construct Uniform Microporous Carbon Shell for Multifunctional Core-shell Nanocomposites Buyuan Guan, Xue Wang, Yu Xiao,
More informationSupporting Information. Sol gel Coating of Inorganic Nanostructures with Resorcinol Formaldehyde Resin
Supporting Information Sol gel Coating of Inorganic Nanostructures with Resorcinol Formaldehyde Resin Na Li, a,b Qiao Zhang, b Jian Liu, c Jibong Joo, b Austin Lee, b Yang Gan,* a Yadong Yin *b a School
More informationSupplementary Information. Core-Shell Silver/Polymeric Nanoparticles-Based Combinatorial Therapy against Breast Cancer In-vitro
Supplementary Information Core-Shell Silver/Polymeric Nanoparticles-Based Combinatorial Therapy against Breast Cancer In-vitro Nancy M. El-Baz 1,2, Laila Ziko 1,3, Rania Siam 1,3, Wael Mamdouh 1,2 * 1
More informationNovel fluorescent matrix embedded carbon quantum dots enrouting stable gold and silver hydrosols
Novel fluorescent matrix embedded carbon quantum dots enrouting stable gold and silver hydrosols Shouvik Mitra a, Sourov Chandra b, Prasun Patra a, Panchanan Pramanik b *, Arunava Goswami a * a AERU, Biological
More informationDivision of Fuel Cells, Dalian National Laboratory for Clean Energy, Dalian Institute of Chemical Physics, Chinese
Electronic Supplementary Material (ESI) for RSC Advances. This journal is The Royal Society of Chemistry 2016 Supporting information Tuned Depositing Ag clusters on ZrO 2 Nanocrystals from Silver Mirror
More informationSynthesis of Colloidal Au-Cu 2 S Heterodimers via Chemically Triggered Phase Segregation of AuCu Nanoparticles
SUPPORTING INFORMATION Synthesis of Colloidal Au-Cu 2 S Heterodimers via Chemically Triggered Phase Segregation of AuCu Nanoparticles Nathan E. Motl, James F. Bondi, and Raymond E. Schaak* Department of
More informationSupporting Information
Supporting Information Fabrication of Cubic Nanocages and Nanoframes by Dealloying Au/Ag Alloy Nanoboxes with an Aqueous Etchant Based on Fe(NO 3 ) 3 or NH 4 OH Xianmao Lu, 1,2 Leslie Au, 1 Joseph McLellan,
More informationSupporting Information
Electronic Supplementary Material (ESI) for RSC Advances. This journal is The Royal Society of Chemistry 2014 Supporting Information Au nanoparticles supported on magnetically separable Fe 2 O 3 - graphene
More informationA single Au nanoparticle anchored inside the porous shell of periodic mesoporous organosilica hollow spheres
Electronic Supplementary Material A single Au nanoparticle anchored inside the porous shell of periodic mesoporous organosilica hollow spheres Ying Yang 1 ( ), Wen Zhang 1, Ying Zhang 1, Anmin Zheng 2,
More informationSupporting Information
Electronic Supplementary Material (ESI) for Chemical Communications. This journal is The Royal Society of Chemistry 2016 Supporting Information Single-crystalline Pd square nanoplates enclosed by {100}
More informationStudying the Chemical, Optical and Catalytic Properties of Noble Metal (Pt, Pd, Ag, Au)/Cu 2 O Core-Shell Nanostructures Grown via General Approach
Studying the Chemical, Optical and Catalytic Properties of Noble Metal (Pt, Pd, Ag, Au)/Cu 2 O Core-Shell Nanostructures Grown via General Approach Noga Meir, Ilan Jen-La Plante, Kobi Flomin, Elina Chockler,
More informationMagnetically-driven selective synthesis of Au clusters on Fe 3 O 4 Nanoparticles
Electronic Supplementary Material (ESI) for Chemical Communications Magnetically-driven selective synthesis of Au clusters on Fe 3 O 4 Nanoparticles Víctor Sebastian, M. Pilar Calatayud, Gerardo F. Goya
More informationenzymatic cascade system
Electronic Supplementary Information Fe 3 O 4 -Au@mesoporous SiO 2 microsphere: an ideal artificial enzymatic cascade system Xiaolong He, a,c Longfei Tan, a Dong Chen,* b Xiaoli Wu, a,c Xiangling Ren,
More informationSupplementary Information:
Supplementary Information: One-Step and Rapid Synthesis of Clean and Monodisperse Dendritic Pt Nanoparticles and Their High Performance Toward Methanol Oxidation and p-nitrophenol Reduction Jun Wang, Xin-Bo
More informationSUPPORTING INFORMATION
Electronic Supplementary Material (ESI) for Chemical Communications. This journal is The Royal Society of Chemistry 2017 SUPPORTING INFORMATION Synthesis of Circular and Triangular Gold Nanorings with
More informationGrowth of silver nanocrystals on graphene by simultaneous reduction of graphene oxide and silver ions with a rapid and efficient one-step approach
Growth of silver nanocrystals on graphene by simultaneous reduction of graphene oxide and silver ions with a rapid and efficient one-step approach Xiu-Zhi Tang, a Zongwei Cao, b Hao-Bin Zhang, a Jing Liu
More informationSupporting Information
Electronic Supplementary Material (ESI) for ChemComm. This journal is The Royal Society of Chemistry 2019 Supporting Information for Halide-assisted activation of atomic hydrogen for photoreduction on
More informationCore-shell 2 mesoporous nanocarriers for metal-enhanced fluorescence
Core-shell Ag@SiO 2 @msio 2 mesoporous nanocarriers for metal-enhanced fluorescence Jianping Yang a, Fan Zhang a *, Yiran Chen a, Sheng Qian a, Pan Hu a, Wei Li a, Yonghui Deng a, Yin Fang a, Lu Han a,
More informationHybrid Gold Superstructures: Synthesis and. Specific Cell Surface Protein Imaging Applications
Supporting Information Hybrid Gold Nanocube@Silica@Graphene-Quantum-Dot Superstructures: Synthesis and Specific Cell Surface Protein Imaging Applications Liu Deng, Ling Liu, Chengzhou Zhu, Dan Li and Shaojun
More informationProbing the Kinetics of Ligand Exchange on Colloidal Gold. Nanoparticles by Surface-Enhanced Raman Scattering
-Supporting Information- Probing the Kinetics of Ligand Exchange on Colloidal Gold Nanoparticles by Surface-Enhanced Raman Scattering Yuhua Feng, Shuangxi Xing, Jun Xu, Hong Wang, Jun Wei Lim, and Hongyu
More informationBiodegradable Hollow Silica Nanospheres Containing Gold Nanoparticle Arrays
Electronic Supplementary Material (ESI) for ChemComm. This journal is The Royal Society of Chemistry 2015 Biodegradable Hollow Silica Nanospheres Containing Gold Nanoparticle Arrays Domenico Cassano a,b,
More informationSupplementary Figure 1. SEM and TEM images of the metal nanoparticles (MNPs) and metal oxide templates.
Supplementary Figure 1. SEM and TEM images of the metal nanoparticles (MNPs) and metal oxide templates. (a) 13 nm Au, (b) 60 nm Au, (c) 3.3 nm Pt, (d) ZnO spheres, (e) Al 2O 3 spheres and (f) Cu 2O cubes.
More informationSelf-assembly of PEGylated Gold Nanoparticles. with Satellite Structures as Seeds
Electronic Supplementary Material (ESI) for ChemComm. This journal is The Royal Society of Chemistry 216 Electronic Supplementary Information for Self-assembly of PEGylated Gold Nanoparticles with Satellite
More informationSupporting Information
Supporting Information High Performance Electrocatalyst: Pt-Cu Hollow Nanocrystals Xiaofei Yu, a Dingsheng, a Qing Peng a and Yadong Li* a a Department of Chemistry, Tsinghua University, Beijing, 100084
More informationA soft-templated method to synthesize sintering-resistant Au/mesoporous-silica core-shell nanocatalysts with sub-5 nm single-core
A soft-templated method to synthesize sintering-resistant Au/mesoporous-silica core-shell nanocatalysts with sub-5 nm single-core Chunzheng Wu, ab Zi-Yian Lim, a Chen Zhou, a Wei Guo Wang, a Shenghu Zhou,
More informationSupporting Information
Supporting Information Au-HKUST-1 Composite Nanocapsules: Synthesis with a Coordination Replication Strategy and Catalysis on CO Oxidation Yongxin Liu, 1 Jiali Zhang, 1 Lingxiao Song, 1 Wenyuan Xu, 1 Zanru
More informationElectronic Supplementary Information
Electronic Supplementary Material (ESI) for Journal of Materials Chemistry A. This journal is The Royal Society of Chemistry 2019 Salt-Templated Growth of Monodisperse Hollow Nanostructures Chaoran Li,
More informationDumpling-Like Nanocomplex of Foldable Janus Polymer Sheet and Sphere
Dumpling-Like Nanocomplex of Foldable Janus Polymer Sheet and Sphere Lei Gao, Ke Zhang, and Yongming Chen* Supporting Information Experimental Section Materials The triblock terpolymer, P2VP 310 -b-ptepm
More informationSynthesis of nano-sized anatase TiO 2 with reactive {001} facets using lamellar protonated titanate as precursor
Supporting Information Synthesis of nano-sized anatase TiO 2 with reactive {001} facets using lamellar protonated titanate as precursor Liuan Gu, Jingyu Wang *, Hao Cheng, Yunchen Du and Xijiang Han* Department
More informationSupporting Information
Supporting Information A Low-Temperature Solid-Phase Method to Synthesize Highly Fluorescent Carbon Nitride Dots with Tunable Emission Juan Zhou, Yong Yang, and Chun-yang Zhang* Single-Molecule Detection
More informationSupporting Information:
Supporting Information: In Situ Synthesis of Magnetically Recyclable Graphene Supported Pd@Co Core-Shell Nanoparticles as Efficient Catalysts for Hydrolytic Dehydrogenation of Ammonia Borane Jun Wang,
More informationO-Allylation of phenols with allylic acetates in aqueous medium using a magnetically separable catalytic system
Supporting information for -Allylation of phenols with allylic acetates in aqueous medium using a magnetically separable catalytic system Amit Saha, John Leazer* and Rajender S. Varma* Sustainable Technology
More informationSupporting Information
Supporting Information Phenyl-Modified Carbon Nitride Quantum Dots with Distinct Photoluminescence Behavior Qianling Cui, Jingsan Xu,* Xiaoyu Wang, Lidong Li,* Markus Antonietti, and Menny Shalom anie_201511217_sm_miscellaneous_information.pdf
More informationSupporting Information
Supporting Information Precisely Controllable Core-Shell Ag@Carbon Dots Nanoparticles: Application to in Situ Super-Sensitive Monitoring of Catalytic Reactions Jing Jin, Shoujun Zhu, Yubin Song, Hongyue
More informationSupplementary Information
Electronic Supplementary Material (ESI) for Materials Chemistry Frontiers. This journal is the Partner Organisations 2018 Supplementary Information Facile one-pot synthesis of MOF supported gold pseudo-single-atom
More informationSupporting Information. Self-assembled nanofibers from Leucine Derived Amphiphiles as Nanoreactors for Growth of ZnO Nanoparticles
Supporting Information Self-assembled nanofibers from Leucine Derived Amphiphiles as Nanoreactors for Growth of ZnO Nanoparticles Karen T. Johnson, Theodore E. Gribb, Evan M. Smoak, and Ipsita A. Banerjee*
More informationBeads-On-String-Shaped Poly(azomethine) Applicable for Solution Processing of Bilayer. Devices using a Same Solvent
Supporting information Beads-n-String-Shaped Poly(azomethine) Applicable for Solution Processing of Bilayer Devices using a Same Solvent Shunichi Fujii, Saori Minami, Kenji Urayama, Yu Suenaga, Hiroyoshi
More informationA Novel Detection Technique of Hydrazine Hydrate: Modality Change of Hydrogen-Bonding Induced Rapid and Ultrasensitive Colorimetric Assay
A Novel Detection Technique of Hydrazine Hydrate: Modality Change of Hydrogen-Bonding Induced Rapid and Ultrasensitive Colorimetric Assay Zhenlu Zhao, a Kelong Ai, b Guo Zhang, b Ying Gao, a Xiuyun Yang,*
More informationoften display a deep green color due to where the SPR occurs (i.e., the wavelength of light that interacts with this specific morphology).
Synthesis-Dependent Catalytic Properties of Gold Nanoparticles Nanoscience is the study of materials that have dimensions, intuitively, on the nanoscale, typically between 1 100 nm. This field has received
More informationSynthesis of 2 ) Structures by Small Molecule-Assisted Nucleation for Plasmon-Enhanced Photocatalytic Activity
Electronic Supplementary Material (ESI) for ChemComm. This journal is The Royal Society of Chemistry 2015 Electronic Supplementary Information Synthesis of Au@UiO-66(NH 2 ) Structures by Small Molecule-Assisted
More informationNd 3+ -Sensitized Multicolor Upconversion Luminescence from A Sandwiched Core/Shell/Shell Nanostructure
Electronic Supplementary Material (ESI) for Nanoscale. This journal is The Royal Society of Chemistry 2017 Supporting Information Nd 3+ -Sensitized Multicolor Upconversion Luminescence from A Sandwiched
More informationElectronic Supplementary Material. Methods. Synthesis of reference samples in Figure 1(b) Nano Res.
Electronic Supplementary Material Shaped Pt Ni nanocrystals with an ultrathin Pt-enriched shell derived from one-pot hydrothermal synthesis as active electrocatalysts for oxygen reduction Jun Gu 1,, Guangxu
More informationElectronic Supporting Information (ESI): Silver nitrate (99.9%), hydrogen peroxide (30-32 wt. % solution in water (ca M),
Experimental section: Electronic Supporting Information (ESI): Reagents Silver nitrate (99.9%), hydrogen peroxide (30-32 wt. % solution in water (ca.. 10.4 M), semiconductor grade, 99.99), L-arginine (TLC,
More informationSupporting Information s for
Supporting Information s for # Self-assembling of DNA-templated Au Nanoparticles into Nanowires and their enhanced SERS and Catalytic Applications Subrata Kundu* and M. Jayachandran Electrochemical Materials
More informationOne-pot Solvent-free Synthesis of Sodium Benzoate from the Oxidation of Benzyl Alcohol over Novel Efficient AuAg/TiO 2 Catalysts
Electronic Supplementary Information One-pot Solvent-free Synthesis of Sodium Benzoate from the Oxidation of Benzyl Alcohol over Novel Efficient AuAg/TiO 2 Catalysts Ying Wang, Jia-Min Zheng, Kangnian
More informationSpecifically colorimetric recognition of calcium, strontium, barium. ions using 2-mercaptosuccinic acid-functionalized gold nanoparticles
Electronic Supporting Information (ESI) for Specifically colorimetric recognition of calcium, strontium, barium ions using 2-mercaptosuccinic acid-functionalized gold nanoparticles and its use in reliable
More informationSupporting Information for. Selectivity and Activity in Catalytic Methanol Oxidation in the Gas Phase
1 / 5 Supporting Information for The Influence of Size-Induced Oxidation State of Platinum Nanoparticles on Selectivity and Activity in Catalytic Methanol Oxidation in the Gas Phase Hailiang Wang, Yihai
More informationSupporting Information
Supporting Information Activating Room Temperature Long Afterglow of Carbon Dots via Covalent Fixation Kai Jiang,, Yuhui Wang, Congzhong Cai, and Hengwei Lin*, Key Laboratory of Graphene Technologies and
More informationHierarchical Host-Guest Assemblies Formed on Dodecaborate-Coated Gold Nanoparticles
Electronic Supplementary Material (ESI) for Chemical Communications. This journal is The Royal Society of Chemistry 17 Hierarchical Host-Guest Assemblies Formed on Dodecaborate-Coated Gold Nanoparticles
More informationCHAPTER 3. FABRICATION TECHNOLOGIES OF CdSe/ZnS / Au NANOPARTICLES AND NANODEVICES. 3.1 THE SYNTHESIS OF Citrate-Capped Au NANOPARTICLES
CHAPTER 3 FABRICATION TECHNOLOGIES OF CdSe/ZnS / Au NANOPARTICLES AND NANODEVICES 3.1 THE SYNTHESIS OF Citrate-Capped Au NANOPARTICLES Au NPs with ~ 15 nm were prepared by citrate reduction of HAuCl 4
More informationSupporting Information
Supporting Information Efficient Temperature Sensing Platform Based on Fluorescent Block Copolymer Functionalized Graphene Oxide Hyunseung Yang, Kwanyeol Paek, and Bumjoon J. Kim * : These authors contributed
More informationRoom Temperature Hydrogen Generation from Hydrous Hydrazine for Chemical Hydrogen Storage
(Supporting Information) Room Temperature Hydrogen Generation from Hydrous Hydrazine for Chemical Hydrogen Storage Sanjay Kumar Singh, Xin-Bo Zhang, and Qiang Xu* National Institute of Advanced Industrial
More informationSupporting Information
Supporting Information Interconversion between Superatomic 6-Electron and 8-Electron Configurations of M@Au 24 (SR) 18 Clusters (M = Pd, Pt) Kyuju Kwak, Qing Tang, Minseok Kim, De-en Jiang, and Dongil
More informationFacile synthesis of yolk-shell structured Si-C nanocomposites as anode for lithium-ion battery 1. Experimental 1.1 Chemicals
Electronic Supplementary Material (ESI) for ChemComm. This journal is The Royal Society of Chemistry 2014 Facile synthesis of yolk-shell structured Si-C nanocomposites as anode for lithium-ion battery
More informationElectronic supplementary information
Electronic Supplementary Material (ESI) for ChemComm. This journal is The Royal Society of Chemistry 2018 Electronic supplementary information Heterogeneous nucleation and growth of highly crystalline
More informationEncapsulation of enzyme in metal ion-surfactant nanocomposites for
Electronic Supplementary Material (ESI) for ChemComm. This journal is The Royal Society of Chemistry 2017 Supporting information for Encapsulation of enzyme in metal ion-surfactant nanocomposites for catalysis
More informationSupplementary Information
Supplementary Information Direct Synthesis of a Macroscopic Array of Naked Ag Nanoparticles Omar Ayyad,* a,b,c David Muñoz-Rojas, a Pedro Gómez-Romero* a,c Experimental details Polyvinylpyrrolidone (PVP40T-500G,
More informationFacile Synthesis and Catalytic Properties of CeO 2 with Tunable Morphologies from Thermal Transformation of Cerium Benzendicarboxylate Complexes
Electronic Supplementary Information Facile Synthesis and Catalytic Properties of CeO 2 with Tunable Morphologies from Thermal Transformation of Cerium Benzendicarboxylate Complexes Yuhua Zheng, Kai Liu,
More informationSupporting Information
Supporting Information Polyoxometalate-based crystalline tubular microreactor: redox-active inorganic-organic hybrid materials producing gold nanoparticles and catalytic properties Dong-Ying Du, Jun-Sheng
More informationFast ph-assisted functionalization of silver nanoparticles with monothiolated DNA
Supporting Information for Fast ph-assisted functionalization of silver nanoparticles with monothiolated DNA Xu Zhang ab, Mark R. Servos b, and Juewen Liu* a a Department of Chemistry and Waterloo Institute
More informationSupporting Information
Electronic Supplementary Material (ESI) for Dalton Transactions. This journal is The Royal Society of Chemistry 2016 Supporting Information Polystyrene Sulfonate Threaded in MIL-101Cr(III) as Stable and
More informationTransformation of Pd PdH 0.7 nanoparticles inside the mesoporous Zr-modified SiO 2 films in ambient conditions
Transformation of Pd PdH 0.7 nanoparticles inside the mesoporous Zr-modified SiO 2 films in ambient conditions Jony Saha, Anirban Dandapat and Goutam De* Nano-Structured Materials Division, Central Glass
More informationSUPPORTING INFORMATION. A New Approach for the Surface Enhanced Resonance Raman Scattering (SERRS)
SUPPORTING INFORMATION A New Approach for the Surface Enhanced Resonance Raman Scattering (SERRS) Detection of Dopamine at Picomolar (pm) Levels in the Presence of Ascorbic Acid Murat Kaya, Mürvet Volkan
More informationHigh-yield halide-free synthesis of biocompatible Au nanoplates
Electronic Supplementary Material (ESI) for Chemical Communications. This journal is The Royal Society of Chemistry 2016 Supporting information High-yield halide-free synthesis of biocompatible Au nanoplates
More informationDown-conversion monochrome light-emitting diodeswith the color determined
Electronic Supplementary Material (ESI) for Journal of Materials Chemistry C. This journal is The Royal Society of Chemistry 2015 Electronic supplementary information (ESI) for Down-conversion monochrome
More informationElectronic supplementary information
Electronic supplementary information Surface plasmon resonance enhanced upconversion luminescence in aqueous media for TNT selective detection Nina Tu and Leyu Wang* State Key Laboratory of Chemical Resource
More informationMultifunctional silica nanoparticles modified via silylateddecaborate
Supporting information Multifunctional silica nanoparticles modified via silylateddecaborate precursors Fatima Abi-Ghaida, [a,b,c] Sébastien Clément, [a] Ali Safa, [b] Daoud Naoufal* [b,c] and Ahmad Mehdi*
More informationElectronic Supplementary Information. Facile synthesis of polypyrrole coated copper nanowire: new concept to engineered core-shell structures
Electronic Supplementary Information Facile synthesis of polypyrrole coated copper nanowire: new concept to engineered core-shell structures Yang Liu, a Zhen Liu, a Ning Lu, b Elisabeth Preiss, a Selcuk
More informationShape Effect of Ag-Ni Binary Nanoparticles on Catalytic Hydrogenation Aided by Surface Plasmon
Electronic Supplementary Material (ESI) for ChemComm. This journal is The Royal Society of Chemistry 2015 Supplementary Information Shape Effect of Ag-Ni Binary Nanoparticles on Catalytic Hydrogenation
More informationSynthesis of uniform hollow silica spheres with ordered mesoporous shells in a CO 2 induced nanoemulsion. Supporting Information
Synthesis of uniform hollow silica spheres with ordered mesoporous shells in a CO 2 induced nanoemulsion Yueju Zhao, Jianling Zhang, Wei Li, Chaoxing Zhang, Buxing Han* Beijing National Laboratory for
More informationSupporting Information
Electronic Supplementary Material (ESI) for ChemComm. This journal is The Royal Society of Chemistry 2014 Supporting Information Synthesis of Poly(dihydroxystyrene-block-styrene) (PDHSt-b-PSt) by the RAFT
More informationElectronic Supplementary Information (ESI) Green synthesis of shape-defined anatase TiO 2 nanocrystals wholly exposed with {001} and {100} facets
Electronic Supplementary Information (ESI) Green synthesis of shape-defined anatase TiO 2 nanocrystals wholly exposed with {001} and {100} facets Lan Wang, a Ling Zang, b Jincai Zhao c and Chuanyi Wang*
More informationEfficient charge storage in photoexcited TiO 2 nanorod-noble metal nanoparticle composite systems
Electronic Supplementary Information Efficient charge storage in photoexcited TiO 2 nanorod-noble metal nanoparticle composite systems P. D. Cozzoli, M. L. Curri, and A. Agostiano 1. Synthesis of TiO 2
More informationSupporting Information. Near infrared light-powered Janus mesoporous silica nanoparticle motors
Supporting Information Near infrared light-powered Janus mesoporous silica nanoparticle motors Mingjun Xuan,, Zhiguang Wu,, Jingxin Shao, Luru Dai, Tieyan Si,, * and Qiang He, * State Key Laboratory of
More informationAdsorption of Methylene Blue on Mesoporous SBA 15 in Ethanol water Solution with Different Proportions
2015 2 nd International Conference on Material Engineering and Application (ICMEA 2015) ISBN: 978-1-60595-323-6 Adsorption of Methylene Blue on Mesoporous SBA 15 in Ethanol water Solution with Different
More informationThe sacrificial role of graphene oxide in stabilising Fenton-like catalyst GO Fe 3 O 4
Electronic Supplementary Material (ESI) for ChemComm. This journal is The Royal Society of Chemistry 2015 The sacrificial role of graphene oxide in stabilising Fenton-like catalyst GO Fe 3 O 4 Nor Aida
More informationMagnetic Janus Nanorods for Efficient Capture, Separation. and Elimination of Bacteria
Electronic Supplementary Material (ESI) for RSC Advances. This journal is The Royal Society of Chemistry 2016 Magnetic Janus Nanorods for Efficient Capture, Separation and Elimination of Bacteria Zhi-min
More informationSupporting Information. Single Particle Detection by Area Amplification Single Wall Carbon Nanotube Attachment to a Nanoelectrode
Supporting Information Single Particle Detection by Area Amplification Single Wall Carbon Nanotube Attachment to a Nanoelectrode Jun Hui Park, Scott N. Thorgaard, Bo Zhang, Allen J. Bard * Center for Electrochemistry,
More informationHigh-Performance Semiconducting Polythiophenes for Organic Thin Film. Transistors by Beng S. Ong,* Yiliang Wu, Ping Liu and Sandra Gardner
Supplementary Materials for: High-Performance Semiconducting Polythiophenes for Organic Thin Film Transistors by Beng S. Ong,* Yiliang Wu, Ping Liu and Sandra Gardner 1. Materials and Instruments. All
More informationSupporting Information
Supporting Information Wiley-VCH 2011 69451 Weinheim, Germany Silver Nanocrystals with Concave Surfaces and Their Optical and Surface-Enhanced Raman Scattering Properties** Xiaohu Xia, Jie Zeng, Brenden
More informationSupporting Information for: Emulsion-assisted synthesis of monodisperse binary metal nanoparticles
Supporting Information for: Emulsion-assisted synthesis of monodisperse binary metal nanoparticles Zhen Yin, Ding Ma* and Xinhe Bao* Synthesis of the PdCu nanoparticles: All synthesis was carried out under
More informationMicrowave-Assisted Synthesis of BSA-Protected Small Gold. Nanoclusters and Their Fluorescence-Enhanced Sensing of Silver(Ι) Ions
Microwave-Assisted Synthesis of BSA-Protected Small Gold Nanoclusters and Their Fluorescence-Enhanced Sensing of Silver(Ι) Ions (Supporting Information) Yuan Yue, a,b Tian-Ying Liu, a Hong-Wei Li,* a Zhongying
More informationRole of Surface Charge of Inhibitors on Amyloid Beta Fibrillation
Supporting Information Role of Surface Charge of Inhibitors on Amyloid Beta Fibrillation SWATHI SUDHAKAR, PANDURANGAN KALIPILLAI, POORNIMA BUDIME SANTHOSH, ETHAYARAJA MANI* POLYMER ENGINEERING AND COLLOID
More informationSupporting Information
Supporting Information Decorating Graphene Sheets with Gold Nanoparticles Ryan Muszynski, Brian Seeger and, Prashant V. Kamat* Radiation Laboratory, Departments of Chemistry & Biochemistry and Chemical
More informationElectronic supplementary information. A longwave optical ph sensor based on red upconversion
Electronic Supplementary Material (ESI) for RSC Advances. This journal is The Royal Society of Chemistry 2014 Electronic supplementary information A longwave optical ph sensor based on red upconversion
More informationElectronic supplementary information for:
Electronic supplementary information for: Charge-transfer-induced suppression of galvanic replacement and synthesis of (Au@Ag)@Au double shell nanoparticles for highly uniform, robust and sensitive bioprobes
More informationAn Optimal Substrate Design for SERS: Dual-Scale Diamond-Shaped Gold Nano-Structures Fabricated via Interference Lithography
Supporting Information An Optimal Substrate Design for SERS: Dual-Scale Diamond-Shaped Gold Nano-Structures Fabricated via Interference Lithography Hyo-Jin Ahn a, Pradheep Thiyagarajan a, Lin Jia b, Sun-I
More information- Supporting Information - Controlled Assembly of Eccentrically Encapsulated Gold Nanoparticles
- Supporting Information - S1 Controlled Assembly of Eccentrically Encapsulated Gold Nanoparticles Tao Chen, Miaoxin Yang, Xinjiao Wang, Li Huey Tan, Hongyu Chen* Division of Chemistry and Biological Chemistry,
More informationSupporting Information
Supporting Information Lattice Contracted AgPt Nanoparticles Hongjun You, ab Zhenmeng Peng, a Jianbo Wu a and Hong Yang,* a a Department of Chemical Engineering, University of Rochester, Rochester, NY
More informationSupporting Information
Supporting Information Collapsed (Kippah) Hollow Silica Nanoparticles Kun-Che Kao, Chieh-Jui Tsou and Chung-Yuan Mou* Experimental Section Materials: Reagents: Cetyltrimethylammonium bromide (CTAB, 99%+),
More informationVery low temperature CO oxidation over colloidally deposited gold nanoparticles on Mg(OH) 2 and MgO
Supporing Information Very low temperature CO oxidation over colloidally deposited gold nanoparticles on Mg(OH) 2 and MgO Chun-Jiang Jia, Yong Liu, Hans Bongard, Ferdi Schüth* Max-Planck-Institut für Kohlenforschung,
More informationFabrication and characterization of poly (ethylene oxide) templated nickel oxide nanofibers for dye degradation
Electronic Supplementary Material (ESI) for Environmental Science: Nano. This journal is The Royal Society of Chemistry 2014 Supplementary Information Fabrication and characterization of poly (ethylene
More informationSupplementary Material
Supplementary Material Title: Optical Characterization of Non-Covalent Interaction between Non-Conjugated Polymers and Chemically Converted Graphene Author: Yufei Wang A, Xueliang Hou A, Chi Cheng A, Ling
More informationDigitized single scattering nanoparticles for probing molecular binding
Electronic Supplementary Information (ESI) Digitized single scattering nanoparticles for probing molecular binding Yue Liu a, Cheng Zhi Huang a,b* a Education Ministry Key Laboratory on Luminescence and
More informationSupporting Information
Supporting Information Dynamic Interaction between Methylammonium Lead Iodide and TiO 2 Nanocrystals Leads to Enhanced Photocatalytic H 2 Evolution from HI Splitting Xiaomei Wang,, Hong Wang,, Hefeng Zhang,,
More informationSupporting Information
Electronic Supplementary Material (ESI) for Journal of Materials Chemistry C. This journal is The Royal Society of Chemistry 2015 Supporting Information Plasmonics-enhanced metal-organic frameworks nanofilms
More informationSupporting Information
Supporting Information Electrochemical Synthesis of Ammonia from N 2 and H 2 O under Ambient Conditions Using Pore-Size Controlled Hollow Gold Nanocatalysts with Tunable Plasmonic Properties Mohammadreza
More information