TOUGHNESS OF PLASTICALLY-DEFORMING ASYMMETRIC JOINTS. Ford Research Laboratory, Ford Motor Company, Dearborn, MI 48121, U.S.A. 1.
|
|
- Ralf Snow
- 5 years ago
- Views:
Transcription
1 TOUGHNESS OF PLASTICALLY-DEFORMING ASYMMETRIC JOINTS M. D. Thouless, M. S. Kafkalidis, S. M. Ward and Y. Bankowski Department of Mechanical Engineering and Applied Mechanics, University of Michigan, Ann Arbor, MI 4809 U.S.A. Ford Research Laboratory, Ford Motor Company, Dearborn, MI 48, U.S.A.. Introduction Owing to current trends towards light-weight energy-efficient vehicles, the use of adhesives as a replacement for traditional joining techniques has many advantages for the automotive industry. For example, spot-welding is difficult in light-weight materials such as aluminum and impossible in composites and polymers. These materials can be effectively joined with adhesives. Furthermore, adhesively-bonded joints can exhibit substantially greater stiffnesses than spot-welded joints (). The use of Linear Elastic Fracture Mechanics (LEFM) to describe the failure of adhesive joints is now wellestablished (-4). These techniques are, of course, only appropriate when plasticity is limited to a zone that is small in comparison with the specimen geometry. However, an important design consideration for the use of adhesive joints in the automotive industry is how they fail during gross plastic deformation of the structural members. Energy absorption during a crash is provided by this plastic deformation. Design for crash-worthiness with adhesive joints requires that the properties of an adhesive be optimized so that the energy absorption can be maximized by controlled failure of the interfaces. Techniques to assess adhesive failure in the presence of plasticity is therefore required for design purposes. In a previous paper, a testing geometry for adhesive joints in which steady-state crack propagation occurred in the presence of gross plastic deformation was described (5). An analysis based on a steady-state energy balance was presented that described the conditions required for crack propagation. This analysis was used to compute the toughness of symmetrical adhesive joints; and it was shown that the resulting value of toughness was independent of the thickness of the plastically-deforming substrate material. In the present paper, it is demonstrated that the previous result can also be derived from Hutchinson s I-integral [6,7]. The results of additional experiments are presented to show that the geometry-independence of the technique applies also for asymmetrical joints.. Analysis The general problem considered here is illustrated in Figure. An adhesively-bonded double-cantilever beam has a width b and arms of thickness h and h, respectively. A moment M is applied to each arm. For this geometry, crack propagation occurs under steady-state conditions, and the path-independent I-integral introduced by Hutchinson can then be used. The I-integral is defined by $ I = & u Wn σ ij n i % j ) dl () C x ( where W is the history-dependent work density of the material at any point relative to its initial state of zero strain, n is the unit outward normal to the contour C, σ is the stress, and u is the displacement [7]. Hutchinson has shown that this is a path-independent integral that can be used as a crack-driving force even in the presence of non-proportional loading, providing steady-state conditions apply [7]. In the particular geometry considered here, the only contribution to the I-integral is from the segments parallel to the x -axis and for which x is negative. The I-integral then simplifies to
2 h [ ] I = W +σ ε h dx () If the material on both sides of the joint are assumed to be identical and to follow a power-law constitutive equation so that σ = Aε n, (3) W is given by ( ) = σ dε W x ε ( x ) = 0 A ( n + ) ε n + ( x ). (4) For pure bending in the arms, ε (x ) is given by # ε ( x ) = % x + h & ( $ R R x 0 + (5a) " ε ( x ) = $ x + h % # R R & x 0 (5b) where R is the radius of curvature along the neutral axis for the arm above the x -axis, and R is the radius of curvature along the neutral axis for the arm below the x -axis. In addition, from simple-beam theory, it can be shown that the radius of curvature, R, of a plastically-deforming beam is related to the thickness of the beam, h, and the applied moment, M, by /n! bah n+ $ R =. (6) "# n+ ( n + )M %& Therefore, substituting Eqns. (3-6) into Eqn. (), and integrating, results in an expression for the I-integral, I = Mn /n! ( n + )M $! b( n + ) " # Ab % & ( +n)/ n h + $ (+ n)/n (7) " # h % & which is identical to the expression derived for the crack-driving force using a steady-state energy-balance argument in Ref. (5). In this reference, it was further demonstrated that, by using Eqn. (6), it is possible to deduce the critical moment required to fracture the joint by measuring the radius of curvature of the two arms, R and R, after failure. The toughness of the joint is given by n+ An h Γ = n + ( n + ) ( n + ) R + h n+ " % n + n + (8) # $ R &. Experiments The details of the sample preparation and of the experiments are provided in Ref. (5). Rectangular, flat coupons were cut from sheets of different thicknesses of a 5754 aluminum alloy. All the coupons were 0.0 mm wide and 90.0 mm long. These coupons were bonded together to form test samples with different ratios of arm thicknesses, h and h. The samples were bonded over a distance of 30.0 mm from one end of the coupons by a 0.5 mm layer of a commercial structural adhesive. Three different adhesives were used, and six different ratios of h/h were examined. After curing, the sample was placed over a wedge, and a drop weight was released onto the bonded end of the sample (Fig. ). The impact of the weight forced the wedge through the sample, causing the arms to bend and the adhesive to fracture at a constant rate of m/s. It was observed that, after failure, the aluminum substrates were deformed into arcs of circles in the region of the adhesive (Fig. 3). The radii of curvature of these arcs were measured using a ruler on the magnified shadows of the specimens projected on a screen. The values for the power-law hardening exponents, A and n, were obtained by fitting power laws to tensile tests performed on the aluminum substrates. The best-fit values for A and n depended slightly on the particular thickness of the aluminum used (see Ref. (5)). The exponent n varied between 0.3 and 0.7, while A varied between 350 MPa and 40 MPa. As noted in Ref. (5), the possibility that the power-law fits may have introduced errors into the calculation of Γ has been eliminated by comparing the results to those obtained by numerically integrating the stress-strain data directly. Furthermore, it was observed that Γ is not very sensitive to particular choices of A and n provided the area under the moment-curvature curve is well-described by the choice in the appropriate range. The
3 appropriate values of A and n for each arm were used with the measured values of the radii of curvature to compute the toughness of the bonded joints. 3. Discussion The mean values of the measured curvatures (κ), the corresponding values of the moments deduced to have acted on each arm, and the toughness of the joints are shown in Table. Typically, for large aspect ratios, one arm did not deform plastically, and no radius of curvature could be determined. In these cases, the moment was measured from the deformed arm, and it was assumed that this same moment acted on the undeformed arm. As expected, it was found that in these cases, the deduced moment was of a magnitude that would not cause plastic deformation of the thicker arm. When the toughness was calculated, it was seen that the contribution from the strain energy in the elastic arm to the crack-driving force was very small. No reliable results could be obtained for the joints with the two most extreme aspect ratios formed with the toughest adhesive. This was because the deformation was so extreme that the arms formed a tight enough arc of a circle to interfere with the hammer as it descended (Fig. 3). This illustrates a limitation of this technique if the bonded region is too long compared with the radius of curvature. The results of Table show that, for a particular adhesive, Γ is independent of the aspect ratio of the two arms. Furthermore, the present results are in excellent agreement with those obtained in Ref. (5) for the same adhesives. It should be noted that, although the measured curvatures could be quite different for the two arms, the corresponding moments that were calculated from these radii were, to a very close approximation, the same. Any difference in the moments is attributed to the fact that the samples may not have been placed perfectly symmetrically on the wedge, so that rotation of the samples occurred during the test. The difference in moments acting on the two arms implies that an additional counter-balancing moment must have been exerted on the bonded portion of the sample. However, a close examination of the results shows that, even for the largest imbalance, the additional moment makes a negligible contribution to the calculation of the overall value of toughness. From Eqn. (6), it can be seen that, if both arms of the wedge-impact specimen are made of the same material and an equal moment is applied to each, the ratio of the resulting radii of the arms is given by R = h ( +n )/n! # $ &. (9) R " h % In other words, for the aluminum sample, the ratio of the radii increases approximately as the ninth power of the thickness ratio. This demonstrates why the deformation occurs predominately in the thinner arm, even for relatively symmetrical samples. Furthermore, from Eqn. (6) it can be seen that the relative contributions to the crack driving force has the same dependence on the thickness ratio. It is also of interest to compare the results obtained in these experiments with interfacial fracture studies made under linear-elastic conditions. A dependence of the toughness on the symmetry of loading ( mixedmode effects) is often found (8-). However, the loading geometry that most closely mimics the situation described here is where an asymmetrical double cantilever beam is opened by means of a wedge (3, 4). The extent of the mode-mixedness is limited in this case, and loading effects on toughness do not appear to be substantial. However, it was observed in this geometry that, owing to the asymmetry of the loading, the crack path always ran near the interface between the adhesive and the thinner arm (3, 4). Similar effects of the mode-mixedness on crack path have been observed and explained in other adhesive systems (8,, 5, 6). In the present experiments it was also observed that the crack inevitably ran close to, or at, the interface of the thinnest arm. 4. Conclusions A wedge-impact technique has been used to determine the toughness of asymmetric joints made of aluminum bonded with three different commercial adhesives. It was found that the toughness did not vary The adhesives tested here were from a different batch and of a different age from those tested in Ref. (5). They therefore exhibited a small difference in the toughness.
4 with the aspect ratio of the two arms for the range of thicknesses used. The values of toughness obtained were consistent with previous work in which it was shown that the toughness did not depend on the thickness of the adherends. These results indicate that, with this particular type of loading, a geometricallyindependent value for the toughness can be found, despite the presence of a significant amount of plastic deformation. Although no mixed-mode effects were observed in these experiments, the issue of whether they are important for geometries that introduce even more severe shear loading needs to be addressed in future work. Acknowledgments This work was supported by Ford Motor Company, a Rackham Faculty Grant from the University of Michigan, and NSF Grant No. CMS References. D. A. Wagner, C. M. Cunningham and M. A. Debolt, Proc. International Body Engineering Conference, 3-8 (993).. A. N. Gent and A. J. Kinloch, J. Polymer Sci. A, (97). 3. A. Gledhill, A. J. Kinloch, S. Yamani and R. J. Young, Polymer, 9, (978). 4. M. D. Chang, K. L. DeVries and M. L. Williams, J. Adhesion 4, -3 (97). 5. M. D. Thouless, J. L. Adams, M. S. Kafkalidis, S. M. Ward, R. A. Dickie and G. L. Westerbeek, submitted to J. Mater. Sci.. 6. J. W. Hutchinson, Harvard University Report DEAAP S-8 (AFSOR-TR ) (974). 7. Y. Wei and J. W. Hutchinson, submitted to Acta Mater.. 8. J. W. Hutchinson and Z. Suo, Adv. Appl. Mechs., 9, 63-9 (99) 9. H. C. Cao and A. G. Evans, Mechs. Mater., 7, (989). 0. K. M. Liechti and Y. S. Chai, J. Appl. Mechs., 4, (99).. J. S. Wang and Z. Suo, Acta Metall. Mater., 38, (990).. M. D. Thouless, J. W. Hutchinson and E. G. Liniger, Acta Metall. Mater., 40, (99). 3. M. D. Thouless, Acta Metall. Mater., 38, (990). 4. M. D. Thouless, Scripta Meter. Mater., 6, (99). 5. N. A. Fleck, J. W. Hutchinson and Z. Suo, Int. J. Solids Structs., 7, (99). 6 A. R. Akisanya and N. A. Fleck, Int. J. Fract., 58, 93-4 (99).
5 Table (Aluminum substrates) LMD-4 Adhesive h (mm) h (mm) κ (m ) - κ (m ) - M M (Nm/m) (Nm/m) Γ (kj/m ) N.A. < N.A. N.A. N.A..0.3 N.A. < N.A. N.A. N.A ± ± 04.4 ± ± 6 0 ± 5 ± 09 ± 5.5 ± ± 3 8± 60 ± 68 ± 5. ± ± 6 66 ± 8 7 ± 67 ±.0 ± 0.3 Average.3 ± 0.3 XD-4600 Adhesive h (mm) h (mm) κ (m ) - κ (m ) M - M (Nm/m) (Nm/m) Γ (kj/m ) ± 6 < 43.5 ± 0.5 (43). ± ± 6 < 44.7 ± 0.5 (45).3 ± ± ±.6 99 ± 6 ± 6. ± ± ±.6 98 ± 05 ± 5. ± ± 3 ± 4 ± 55 ± 6. ± ± 8 46 ± 7 66 ± 6 ±.3 ± 0. Average. ± 0. Essex-7330 Adhesive h (mm) h (mm) κ (m ) - κ (m ) - M M (Nm/m) (Nm/m) Γ (kj/m ) ± 6 < 43.7 ± 0.5 (44). ± ±6 < 43.0 ± 0.5 (43). ± ± 3 < 99 ± (99). ± ± ±.0 98 ± 85 ± 7. ± ± 5 5. ±.7 4 ± 5 6 ±.0 ± ± 5 40 ± 7 39 ± 3 ±.0 ± 0. Average. ± 0.
6 M x h x M C h Figure. The general problem of an asymmetric double-cantilever beam analyzed in this paper. A contour C is shown along which the I-integral is taken. Hammer Sample Wedge Figure. The test geometry in which a asymmetric double-cantilever beam is fractured by means of a wedge being forced along the interface under the impact of a hammer. Figure 3. Three aluminum samples bonded by the XD-4600 adhesive after failure.
Fig. 1. Different locus of failure and crack trajectories observed in mode I testing of adhesively bonded double cantilever beam (DCB) specimens.
a). Cohesive Failure b). Interfacial Failure c). Oscillatory Failure d). Alternating Failure Fig. 1. Different locus of failure and crack trajectories observed in mode I testing of adhesively bonded double
More informationThe Effects of Transverse Shear on the Delamination of Edge-Notch Flexure and 3-Point Bend Geometries
The Effects of Transverse Shear on the Delamination of Edge-Notch Flexure and 3-Point Bend Geometries M. D. Thouless Department of Mechanical Engineering Department of Materials Science & Engineering University
More informationINFLUENCE OF TEMPERATURE ON BEHAVIOR OF THE INTERFACIAL CRACK BETWEEN THE TWO LAYERS
Djoković, J. M., et.al.: Influence of Temperature on Behavior of the Interfacial THERMAL SCIENCE: Year 010, Vol. 14, Suppl., pp. S59-S68 S59 INFLUENCE OF TEMPERATURE ON BEHAVIOR OF THE INTERFACIAL CRACK
More informationMechanics of wafer bonding: Effect of clamping
JOURNAL OF APPLIED PHYSICS VOLUME 95, NUMBER 1 1 JANUARY 2004 Mechanics of wafer bonding: Effect of clamping K. T. Turner a) Massachusetts Institute of Technology, Cambridge, Massachusetts 0219 M. D. Thouless
More informationNON-LINEAR FRACTURE BEHAVIOR OF DOUBLE CANTILEVER BEAM
Engineering MECHANICS, Vol., 015, No., p. 95 10 95 NON-LINEAR FRACTURE BEHAVIOR OF DOUBLE CANTILEVER BEAM Viktor Rizov* This article describes a theoretical study of non-linear fracture behavior of the
More informationExperimentally Calibrating Cohesive Zone Models for Structural Automotive Adhesives
Experimentally Calibrating Cohesive Zone Models for Structural Automotive Adhesives Mark Oliver October 19, 2016 Adhesives and Sealants Council Fall Convention contact@veryst.com www.veryst.com Outline
More informationCHARACTERIZING ADHESION OF PSA TAPES USING THE SHAFT LOADED BLISTER TEST
.. CHARACTERIZING ADHESION OF PSA TAPES USING THE SHAFT LOADED BLISTER TEST Emmett O'Brien Graduate Student Dept. of Chemical Engineering Virginia Tech Blacksburg, VA Shu Guo Graduate Student Dept. of
More informationPrinceton University. Adhsion and Interfacial Failure in Drug Eluting Stents
Princeton University Adhsion and Interfacial Failure in Drug Eluting Stents Princeton University Background and Introduction Cardiovascular disease is the leading cause of death across the world It represents
More informationA PROTOCOL FOR DETERMINATION OF THE ADHESIVE FRACTURE TOUGHNESS OF FLEXIBLE LAMINATES BY PEEL TESTING: FIXED ARM AND T-PEEL METHODS
1 A PROTOCOL FOR DETERMINATION OF THE ADHESIVE FRACTURE TOUGHNESS OF FLEXIBLE LAMINATES BY PEEL TESTING: FIXED ARM AND T-PEEL METHODS An ESIS Protocol Revised June 2007, Nov 2010 D R Moore, J G Williams
More informationFRACTURE MECHANICS OF COMPOSITES WITH RESIDUAL STRESSES, TRACTION-LOADED CRACKS, AND IMPERFECT INTERFACES
Proc. 2 nd ESIS TC4 Conference on Polymers and Composites, in press, 1999 Author prepared reprint FRACTURE MECHANICS OF COMPOSITES WITH RESIDUAL STRESSES, TRACTION-LOADED CRACKS, AND IMPERFECT INTERFACES
More informationSupplementary Figures
Fracture Strength (GPa) Supplementary Figures a b 10 R=0.88 mm 1 0.1 Gordon et al Zhu et al Tang et al im et al 5 7 6 4 This work 5 50 500 Si Nanowire Diameter (nm) Supplementary Figure 1: (a) TEM image
More informationThe Effect of Cohesive-Law Parameters on Mixed-Mode Fracture
The Effect of Cohesive-Law Parameters on Mixed-Mode Fracture R. B. Sills * and M. D. Thouless * Abstract * Department of Mechanical Engineering Department of Materials Science & Engineering University
More informationThe Effects of Cohesive Strength and Toughness on Mixed-Mode Delamination of Beam-Like Geometries
The Effects of Cohesive Strength and Toughness on Mixed-Mode Delamination of Beam-Like Geometries J. P. Parmigiani and M. D. Thouless,2 Department of Mechanical Engineering 2 Department of Materials Science
More informationLecture 15 Strain and stress in beams
Spring, 2019 ME 323 Mechanics of Materials Lecture 15 Strain and stress in beams Reading assignment: 6.1 6.2 News: Instructor: Prof. Marcial Gonzalez Last modified: 1/6/19 9:42:38 PM Beam theory (@ ME
More informationNumerical analysis of the energy contributions in peel tests: a steady-state multilevel finite element approach
Int. J. Adhesion and Adhesives, vol 28, 2008, 222-236 Numerical analysis of the energy contributions in peel tests: a steady-state multilevel finite element approach Ph. Martiny a, *, F. Lani a, A.J. Kinloch
More informationConstraint effects in adhesive joint fracture
Journal of the Mechanics and Physics of Solids 53 (25) 1951 1983 www.elsevier.com/locate/jmps Constraint effects in adhesive joint fracture T. Pardoen a,, T. Ferracin a, C.M. Landis b, F. Delannay a a
More informationOutline. Tensile-Test Specimen and Machine. Stress-Strain Curve. Review of Mechanical Properties. Mechanical Behaviour
Tensile-Test Specimen and Machine Review of Mechanical Properties Outline Tensile test True stress - true strain (flow curve) mechanical properties: - Resilience - Ductility - Toughness - Hardness A standard
More informationME 176 Final Exam, Fall 1995
ME 176 Final Exam, Fall 1995 Saturday, December 16, 12:30 3:30 PM, 1995. Answer all questions. Please write all answers in the space provided. If you need additional space, write on the back sides. Indicate
More informationCritical applied stresses for a crack initiation from a sharp V-notch
Focussed on: Fracture and Structural Integrity related Issues Critical applied stresses for a crack initiation from a sharp V-notch L. Náhlík, P. Hutař Institute of Physics of Materials, Academy of Sciences
More informationMaterials and Structures
Journal of Mechanics of Materials and Structures BRITTLE FRACTURE BEYOND THE STRESS INTENSITY FACTOR C. T. Sun and Haiyang Qian Volume 4, Nº 4 April 2009 mathematical sciences publishers JOURNAL OF MECHANICS
More informationMechanical Behavior of Circular Composite Springs with Extended Flat Contact Surfaces
Mechanical Behavior of Circular Composite Springs with Extended Flat Contact Surfaces Ping-Cheung Tse epartment of Mechanical Engineering, The Hong Kong Polytechnic University, Hunghom, Kowloon, Hong Kong
More informationMechanical Engineering Ph.D. Preliminary Qualifying Examination Solid Mechanics February 25, 2002
student personal identification (ID) number on each sheet. Do not write your name on any sheet. #1. A homogeneous, isotropic, linear elastic bar has rectangular cross sectional area A, modulus of elasticity
More informationProceedings of the 28th Risø international symposium on materials science, 3-6 Sept 2007.
Proceedings of the 28th Risø international symposium on materials science, 3-6 Sept 27. INFLUENCE OF TEMPERATURE ON COHESIVE PARAMETERS FOR ADHESIVES Anders Biel 1 and Thomas Carlberger 2 1 University
More informationEnergy release rate analysis for adhesive and laminate double cantilever beam specimens emphasizing the effect of residual stresses
International Journal of Adhesion & Adhesives 20 (1999) 59 70 International Journal of Adhesion & Adhesives Energy release rate analysis for adhesive and laminate double cantilever beam specimens emphasizing
More informationInt. J. Fracture, vol. 173, 2012, A multiscale parametric study of mode I fracture in metal-to-metal low-toughness adhesive joints
Int. J. Fracture, vol. 173, 2012, 105-133 A multiscale parametric study of mode I fracture in metal-to-metal low-toughness adhesive joints Ph. Martiny a, F. Lani a,c, A.J. Kinloch b, T. Pardoen c* a Cenaero,
More informationCalculation of Energy Release Rate in Mode I Delamination of Angle Ply Laminated Composites
Copyright c 2007 ICCES ICCES, vol.1, no.2, pp.61-67, 2007 Calculation of Energy Release Rate in Mode I Delamination of Angle Ply Laminated Composites K. Gordnian 1, H. Hadavinia 1, G. Simpson 1 and A.
More informationFrontiers of Fracture Mechanics. Adhesion and Interfacial Fracture Contact Damage
Frontiers of Fracture Mechanics Adhesion and Interfacial Fracture Contact Damage Biology, Medicine & Dentistry The Next Frontiers For Mechanics One of the current challenges in materials & mechanics is
More informationDamage and plasticity in adhesive layer: an experimental study
Int J Fract () 16:93 3 DOI.7/s74--98-3 ORIGINAL PAPER Damage and plasticity in adhesive layer: an experimental study Anders Biel Ulf Stigh Received: January / Accepted: 18 May / Published online: 9 June
More informationICM11. Simulation of debonding in Al/epoxy T-peel joints using a potential-based cohesive zone model
Available online at www.sciencedirect.com Procedia Engineering 10 (2011) 1760 1765 ICM11 Simulation of debonding in Al/epoxy T-peel joints using a potential-based cohesive zone model Marco Alfano a,, Franco
More informationMATERIALS. Why do things break? Why are some materials stronger than others? Why is steel tough? Why is glass brittle?
MATERIALS Why do things break? Why are some materials stronger than others? Why is steel tough? Why is glass brittle? What is toughness? strength? brittleness? Elemental material atoms: A. Composition
More informationInt. J. Fracture, 119, 2003, 25-46
Int. J. Fracture, 119, 003, 5-46 THE USE OF A COHESIVE ZONE MODEL TO STUDY THE FRACTURE OF FIBRE COMPOSITES AND ADHESIVELY-BONDED JOINTS Blackman, B.R.K., Hadavinia, H., Kinloch, A.J. and Williams, J.G.
More informationJohns Hopkins University What is Engineering? M. Karweit MATERIALS
Why do things break? Why are some materials stronger than others? Why is steel tough? Why is glass brittle? What is toughness? strength? brittleness? Elemental material atoms: MATERIALS A. Composition
More informationTHE DETERMINATION OF FRACTURE STRENGTH FROM ULTIMATE TENSILE AND TRANSVERSE RUPTURE STRESSES
Powder Metallurgy Progress, Vol.3 (003), No 3 119 THE DETERMINATION OF FRACTURE STRENGTH FROM ULTIMATE TENSILE AND TRANSVERSE RUPTURE STRESSES A.S. Wronski, A.Cias Abstract It is well-recognized that the
More informationFor an imposed stress history consisting of a rapidly applied step-function jump in
Problem 2 (20 points) MASSACHUSETTS INSTITUTE OF TECHNOLOGY DEPARTMENT OF MECHANICAL ENGINEERING CAMBRIDGE, MASSACHUSETTS 0239 2.002 MECHANICS AND MATERIALS II SOLUTION for QUIZ NO. October 5, 2003 For
More informationINDENTATION RESISTANCE OF AN ALUMINIUM FOAM
Scripta mater. 43 (2000) 983 989 www.elsevier.com/locate/scriptamat INDENTATION RESISTANCE OF AN ALUMINIUM FOAM O.B. Olurin, N.A. Fleck and M.F. Ashby Cambridge University Engineering Department, Cambridge,
More informationMechanical Properties of Materials
Mechanical Properties of Materials Strains Material Model Stresses Learning objectives Understand the qualitative and quantitative description of mechanical properties of materials. Learn the logic of
More informationBending Load & Calibration Module
Bending Load & Calibration Module Objectives After completing this module, students shall be able to: 1) Conduct laboratory work to validate beam bending stress equations. 2) Develop an understanding of
More informationElastic-Plastic Fracture Mechanics. Professor S. Suresh
Elastic-Plastic Fracture Mechanics Professor S. Suresh Elastic Plastic Fracture Previously, we have analyzed problems in which the plastic zone was small compared to the specimen dimensions (small scale
More informationMECHANICS OF 2D MATERIALS
MECHANICS OF 2D MATERIALS Nicola Pugno Cambridge February 23 rd, 2015 2 Outline Stretching Stress Strain Stress-Strain curve Mechanical Properties Young s modulus Strength Ultimate strain Toughness modulus
More informationLaboratory 4 Bending Test of Materials
Department of Materials and Metallurgical Engineering Bangladesh University of Engineering Technology, Dhaka MME 222 Materials Testing Sessional.50 Credits Laboratory 4 Bending Test of Materials. Objective
More informationAdhesive Joints Theory (and use of innovative joints) ERIK SERRANO STRUCTURAL MECHANICS, LUND UNIVERSITY
Adhesive Joints Theory (and use of innovative joints) ERIK SERRANO STRUCTURAL MECHANICS, LUND UNIVERSITY Wood and Timber Why I m intrigued From this to this! via this Fibre deviation close to knots and
More information3.032 Problem Set 2 Solutions Fall 2007 Due: Start of Lecture,
3.032 Problem Set 2 Solutions Fall 2007 Due: Start of Lecture, 09.21.07 1. In the beam considered in PS1, steel beams carried the distributed weight of the rooms above. To reduce stress on the beam, it
More informationExamination in Damage Mechanics and Life Analysis (TMHL61) LiTH Part 1
Part 1 1. (1p) Define the Kronecker delta and explain its use. The Kronecker delta δ ij is defined as δ ij = 0 if i j 1 if i = j and it is used in tensor equations to include (δ ij = 1) or "sort out" (δ
More informationMembers Subjected to Torsional Loads
Members Subjected to Torsional Loads Torsion of circular shafts Definition of Torsion: Consider a shaft rigidly clamped at one end and twisted at the other end by a torque T = F.d applied in a plane perpendicular
More informationMixed-Mode Fracture Toughness Determination USING NON-CONVENTIONAL TECHNIQUES
Mixed-Mode Fracture Toughness Determination USING NON-CONVENTIONAL TECHNIQUES IDMEC- Pólo FEUP DEMec - FEUP ESM Virginia Tech motivation fracture modes conventional tests [mode I] conventional tests [mode
More informationFRACTURE MECHANICS APPROACHES STRENGTHENING USING FRP MATERIALS
Fracture Mechanics of Concrete Structures Proceedings FRAMCOS-3 AEDIFICATIO Publishers, D-79104 Freiburg, Germany FRACTURE MECHANICS APPROACHES STRENGTHENING USING FRP MATERIALS Triantafillou Department
More informationLecture #7: Basic Notions of Fracture Mechanics Ductile Fracture
Lecture #7: Basic Notions of Fracture Mechanics Ductile Fracture by Dirk Mohr ETH Zurich, Department of Mechanical and Process Engineering, Chair of Computational Modeling of Materials in Manufacturing
More informationCHAPTER 6: Shearing Stresses in Beams
(130) CHAPTER 6: Shearing Stresses in Beams When a beam is in pure bending, the only stress resultants are the bending moments and the only stresses are the normal stresses acting on the cross sections.
More informationChapter 7. Highlights:
Chapter 7 Highlights: 1. Understand the basic concepts of engineering stress and strain, yield strength, tensile strength, Young's(elastic) modulus, ductility, toughness, resilience, true stress and true
More informationPURE BENDING. If a simply supported beam carries two point loads of 10 kn as shown in the following figure, pure bending occurs at segment BC.
BENDING STRESS The effect of a bending moment applied to a cross-section of a beam is to induce a state of stress across that section. These stresses are known as bending stresses and they act normally
More informationME Final Exam. PROBLEM NO. 4 Part A (2 points max.) M (x) y. z (neutral axis) beam cross-sec+on. 20 kip ft. 0.2 ft. 10 ft. 0.1 ft.
ME 323 - Final Exam Name December 15, 2015 Instructor (circle) PROEM NO. 4 Part A (2 points max.) Krousgrill 11:30AM-12:20PM Ghosh 2:30-3:20PM Gonzalez 12:30-1:20PM Zhao 4:30-5:20PM M (x) y 20 kip ft 0.2
More informationA study of forming pressure in the tube-hydroforming process
Journal of Materials Processing Technology 192 19 (2007) 404 409 A study of forming pressure in the tube-hydroforming process Fuh-Kuo Chen, Shao-Jun Wang, Ray-Hau Lin Department of Mechanical Engineering,
More informationInfluence of impact velocity on transition time for V-notched Charpy specimen*
[ 溶接学会論文集第 35 巻第 2 号 p. 80s-84s (2017)] Influence of impact velocity on transition time for V-notched Charpy specimen* by Yasuhito Takashima** and Fumiyoshi Minami** This study investigated the influence
More informationME 2570 MECHANICS OF MATERIALS
ME 2570 MECHANICS OF MATERIALS Chapter III. Mechanical Properties of Materials 1 Tension and Compression Test The strength of a material depends on its ability to sustain a load without undue deformation
More informationThe Roles of Cohesive Strength and Toughness for Crack Growth in Visco-elastic and Creeping Materials
The Roles of Cohesive Strength and Toughness for Crack Growth in Visco-elastic and Creeping Materials H. Wang, W. Lu, J. R. Barber and M. D. Thouless, Department of Mechanical Engineering Department of
More informationMECHANICS OF MATERIALS Sample Problem 4.2
Sample Problem 4. SOLUTON: Based on the cross section geometry, calculate the location of the section centroid and moment of inertia. ya ( + Y Ad ) A A cast-iron machine part is acted upon by a kn-m couple.
More informationMassachusetts Institute of Technology Department of Aeronautics and Astronautics Cambridge, MA Problem Set 14
Massachusetts Institute of Technology Department of Aeronautics and Astronautics Cambridge, MA 02139 16.01/16.02 Unified Engineering I, II Fall 2003 Problem Set 14 Name: Due Date: 12/9/03 F18 F19 F20 M19
More informationModule-4. Mechanical Properties of Metals
Module-4 Mechanical Properties of Metals Contents ) Elastic deformation and Plastic deformation ) Interpretation of tensile stress-strain curves 3) Yielding under multi-axial stress, Yield criteria, Macroscopic
More informationINCREASING RUPTURE PREDICTABILITY FOR ALUMINUM
1 INCREASING RUPTURE PREDICTABILITY FOR ALUMINUM Influence of anisotropy Daniel Riemensperger, Adam Opel AG Paul Du Bois, PDB 2 www.opel.com CONTENT Introduction/motivation Isotropic & anisotropic material
More informationHomework Problems. ( σ 11 + σ 22 ) 2. cos (θ /2), ( σ θθ σ rr ) 2. ( σ 22 σ 11 ) 2
Engineering Sciences 47: Fracture Mechanics J. R. Rice, 1991 Homework Problems 1) Assuming that the stress field near a crack tip in a linear elastic solid is singular in the form σ ij = rλ Σ ij (θ), it
More informationAERO 214. Lab II. Measurement of elastic moduli using bending of beams and torsion of bars
AERO 214 Lab II. Measurement of elastic moduli using bending of beams and torsion of bars BENDING EXPERIMENT Introduction Flexural properties of materials are of interest to engineers in many different
More informationOn characterising fracture resistance in mode-i delamination
9 th International Congress of Croatian Society of Mechanics 18-22 September 2018 Split, Croatia On characterising fracture resistance in mode-i delamination Leo ŠKEC *, Giulio ALFANO +, Gordan JELENIĆ
More informationCOMELD TM JOINTS: A NOVEL TECHNIQUE FOR BONDING COMPOSITES AND METAL
COMELD TM JOINTS: A NOVEL TECHNIQUE FOR BONDING COMPOSITES AND METAL F.J. Guild *, P.J. Hogg + and W. Tu School of Engineering and Materials Science, Queen Mary, University of London, London E1 4NS, UK
More informationCompressive splitting failure of composites using modified shear lag theory
International Journal of Fracture 115: 27 40, 2002. 2002 Kluwer Academic Publishers. Printed in the Netherlands. Compressive splitting failure of composites using modified shear lag theory CHANDRA S. YERRAMALLI
More informationA Note on Suhir s Solution of Thermal Stresses for a Die-Substrate Assembly
M. Y. Tsai e-mail: mytsai@mail.cgu.edu.tw C. H. Hsu C. N. Han Department of Mechanical Engineering, Chang Gung University, Kwei-Shan, Tao-Yuan, Taiwan 333, ROC A Note on Suhir s Solution of Thermal Stresses
More informationSSRG International Journal of Mechanical Engineering (SSRG-IJME) volume1 issue5 September 2014
Finite Element Modeling for Delamination Analysis of Double Cantilever Beam Specimen Mohammed Waseem H.S. 1, Kiran Kumar N. 2 1 Post Graduate Student, 2 Asst. Professor Dept. of Mechanical Engineering,
More informationSTRENGTH OF MATERIALS-I. Unit-1. Simple stresses and strains
STRENGTH OF MATERIALS-I Unit-1 Simple stresses and strains 1. What is the Principle of surveying 2. Define Magnetic, True & Arbitrary Meridians. 3. Mention different types of chains 4. Differentiate between
More informationPES Institute of Technology
PES Institute of Technology Bangalore south campus, Bangalore-5460100 Department of Mechanical Engineering Faculty name : Madhu M Date: 29/06/2012 SEM : 3 rd A SEC Subject : MECHANICS OF MATERIALS Subject
More informationStress Analysis Lecture 3 ME 276 Spring Dr./ Ahmed Mohamed Nagib Elmekawy
Stress Analysis Lecture 3 ME 276 Spring 2017-2018 Dr./ Ahmed Mohamed Nagib Elmekawy Axial Stress 2 Beam under the action of two tensile forces 3 Beam under the action of two tensile forces 4 Shear Stress
More informationReview Lecture. AE1108-II: Aerospace Mechanics of Materials. Dr. Calvin Rans Dr. Sofia Teixeira De Freitas
Review Lecture AE1108-II: Aerospace Mechanics of Materials Dr. Calvin Rans Dr. Sofia Teixeira De Freitas Aerospace Structures & Materials Faculty of Aerospace Engineering Analysis of an Engineering System
More information[8] Bending and Shear Loading of Beams
[8] Bending and Shear Loading of Beams Page 1 of 28 [8] Bending and Shear Loading of Beams [8.1] Bending of Beams (will not be covered in class) [8.2] Bending Strain and Stress [8.3] Shear in Straight
More informationGeometric and Material Property Effects on the Strength of Rubber-Toughened Adhesive Joints
Geometric and Material Property Effects on the Strength of Rubber-Toughened Adhesive Joints Altering the geometry of a bonded joint will invariably cause changes to occur in the stress and strain distribution
More informationLecture 8 Viscoelasticity and Deformation
Read: pg 130 168 (rest of Chpt. 4) 1 Poisson s Ratio, µ (pg. 115) Ratio of the strain in the direction perpendicular to the applied force to the strain in the direction of the applied force. For uniaxial
More informationComparison between a Cohesive Zone Model and a Continuum Damage Model in Predicting Mode-I Fracture Behavior of Adhesively Bonded Joints
Copyright 2012 Tech Science Press CMES, vol.83, no.2, pp.169-181, 2012 Comparison between a Cohesive Zone Model and a Continuum Damage Model in Predicting Mode-I Fracture Behavior of Adhesively Bonded
More informationAn Analytical Model for Long Tube Hydroforming in a Square Cross-Section Die Considering Anisotropic Effects of the Material
Journal of Stress Analysis Vol. 1, No. 2, Autumn Winter 2016-17 An Analytical Model for Long Tube Hydroforming in a Square Cross-Section Die Considering Anisotropic Effects of the Material H. Haghighat,
More informationMechanics PhD Preliminary Spring 2017
Mechanics PhD Preliminary Spring 2017 1. (10 points) Consider a body Ω that is assembled by gluing together two separate bodies along a flat interface. The normal vector to the interface is given by n
More informationDurability of bonded aircraft structure. AMTAS Fall 2016 meeting October 27 th 2016 Seattle, WA
Durability of bonded aircraft structure AMTAS Fall 216 meeting October 27 th 216 Seattle, WA Durability of Bonded Aircraft Structure Motivation and Key Issues: Adhesive bonding is a key path towards reduced
More information1 Static Plastic Behaviour of Beams
1 Static Plastic Behaviour of Beams 1.1 Introduction Many ductile materials which are used in engineering practice have a considerable reserve capacity beyond the initial yield condition. The uniaxial
More informationSIZE EFFECTS IN THE COMPRESSIVE CRUSHING OF HONEYCOMBS
43rd AIAA/ASME/ASCE/AHS/ASC Structures, Structural Dynamics, and Materials Con 22-25 April 2002, Denver, Colorado SIZE EFFECTS IN THE COMPRESSIVE CRUSHING OF HONEYCOMBS Erik C. Mellquistand Anthony M.
More informationThermal load-induced notch stress intensity factors derived from averaged strain energy density
Available online at www.sciencedirect.com Draft ScienceDirect Draft Draft Structural Integrity Procedia 00 (2016) 000 000 www.elsevier.com/locate/procedia 21st European Conference on Fracture, ECF21, 20-24
More informationEfficient 2-parameter fracture assessments of cracked shell structures
Efficient 2-parameter fracture assessments of cracked shell structures B. Skallerud, K.R. Jayadevan, C. Thaulow, E. Berg*, K. Holthe Faculty of Engineering Science The Norwegian University of Science and
More informationBurst pressure estimation of reworked nozzle weld on spherical domes
Indian Journal of Engineering & Materials Science Vol. 21, February 2014, pp. 88-92 Burst pressure estimation of reworked nozzle weld on spherical domes G Jegan Lal a, Jayesh P a & K Thyagarajan b a Cryo
More informationProblem d d d B C E D. 0.8d. Additional lecturebook examples 29 ME 323
Problem 9.1 Two beam segments, AC and CD, are connected together at C by a frictionless pin. Segment CD is cantilevered from a rigid support at D, and segment AC has a roller support at A. a) Determine
More informationEffect of Strain Hardening on Unloading of a Deformable Sphere Loaded against a Rigid Flat A Finite Element Study
Effect of Strain Hardening on Unloading of a Deformable Sphere Loaded against a Rigid Flat A Finite Element Study Biplab Chatterjee, Prasanta Sahoo 1 Department of Mechanical Engineering, Jadavpur University
More information1 Force Sensing. Lecture Notes. 1.1 Load Cell. 1.2 Stress and Strain
Lecture Notes 1 Force Sensing 1.1 Load Cell A Load Cell is a structure which supports the load and deflects a known amount in response to applied forces and torques. The deflections are measured to characterize
More informationCracks Jacques Besson
Jacques Besson Centre des Matériaux UMR 7633 Mines ParisTech PSL Research University Institut Mines Télécom Aγνωστ oς Θεoς Outline 1 Some definitions 2 in a linear elastic material 3 in a plastic material
More informationComputational Analysis for Composites
Computational Analysis for Composites Professor Johann Sienz and Dr. Tony Murmu Swansea University July, 011 The topics covered include: OUTLINE Overview of composites and their applications Micromechanics
More information7.6 Stress in symmetrical elastic beam transmitting both shear force and bending moment
7.6 Stress in symmetrical elastic beam transmitting both shear force and bending moment à It is more difficult to obtain an exact solution to this problem since the presence of the shear force means that
More informationNUMERICAL INVESTIGATION OF DELAMINATION IN L-SHAPED CROSS-PLY COMPOSITE BRACKET
NUMERICAL INVESTIGATION OF DELAMINATION IN L-SHAPED CROSS-PLY COMPOSITE BRACKET M.Gümüş a*, B.Gözlüklü a, D.Çöker a a Department of Aerospace Eng., METU, Ankara, Turkey *mert.gumus@metu.edu.tr Keywords:
More informationCohesive Fracture Study of a Bonded Coarse Silica Sand Aggregate Bond Interface Subjected to Mixed-Mode Bending Conditions
Polymers 04, 6, -8; doi:0.90/polym6000 Article OPEN ACCESS polymers ISSN 07-460 www.mdpi.com/journal/polymers Cohesive Fracture Study of a Bonded Coarse Silica Sand Aggregate Bond Interface Subjected to
More informationStress Analysis Lecture 4 ME 276 Spring Dr./ Ahmed Mohamed Nagib Elmekawy
Stress Analysis Lecture 4 ME 76 Spring 017-018 Dr./ Ahmed Mohamed Nagib Elmekawy Shear and Moment Diagrams Beam Sign Convention The positive directions are as follows: The internal shear force causes a
More informationIntroduction to Engineering Materials ENGR2000. Dr. Coates
Introduction to Engineering Materials ENGR2 Chapter 6: Mechanical Properties of Metals Dr. Coates 6.2 Concepts of Stress and Strain tension compression shear torsion Tension Tests The specimen is deformed
More informationFME461 Engineering Design II
FME461 Engineering Design II Dr.Hussein Jama Hussein.jama@uobi.ac.ke Office 414 Lecture: Mon 8am -10am Tutorial Tue 3pm - 5pm 10/1/2013 1 Semester outline Date Week Topics Reference Reading 9 th Sept 1
More informationPROPAGATION OF CURVED CRACKS IN HOMOGENEOUS AND GRADED MATERIALS
PROPAGATION OF CURVED CRACKS IN HOMOGENEOUS AND GRADED MATERIALS Abstract Matthew T. Tilbrook, Robert J. Moon and Mark Hoffman School of Materials Science and Engineering University of New South Wales,
More informationMECE 3321 MECHANICS OF SOLIDS CHAPTER 3
MECE 3321 MECHANICS OF SOLIDS CHAPTER 3 Samantha Ramirez TENSION AND COMPRESSION TESTS Tension and compression tests are used primarily to determine the relationship between σ avg and ε avg in any material.
More informationEFFECT OF STRAIN HARDENING ON ELASTIC-PLASTIC CONTACT BEHAVIOUR OF A SPHERE AGAINST A RIGID FLAT A FINITE ELEMENT STUDY
Proceedings of the International Conference on Mechanical Engineering 2009 (ICME2009) 26-28 December 2009, Dhaka, Bangladesh ICME09- EFFECT OF STRAIN HARDENING ON ELASTIC-PLASTIC CONTACT BEHAVIOUR OF A
More informationExperimental investigation on monotonic performance of steel curved knee braces for weld-free beam-to-column connections
Experimental investigation on monotonic performance of steel curved knee braces for weld-free beam-to-column connections *Zeyu Zhou 1) Bo Ye 2) and Yiyi Chen 3) 1), 2), 3) State Key Laboratory of Disaster
More informationToughness of Ni/Al 2 O 3 interfaces as dependent on micron-scale plasticity and atomistic-scale separation
Philosophical Magazine Vol. 88, Nos. 30 32, 21 October 11 November 2008, 3841 3859 Toughness of Ni/Al 2 O 3 interfaces as dependent on micron-scale plasticity and atomistic-scale separation Y. Wei a and
More informationA FINITE ELEMENT STUDY OF ELASTIC-PLASTIC HEMISPHERICAL CONTACT BEHAVIOR AGAINST A RIGID FLAT UNDER VARYING MODULUS OF ELASTICITY AND SPHERE RADIUS
Proceedings of the International Conference on Mechanical Engineering 2009 (ICME2009) 26-28 December 2009, Dhaka, Bangladesh ICME09- A FINITE ELEMENT STUDY OF ELASTIC-PLASTIC HEMISPHERICAL CONTACT BEHAVIOR
More informationCHAPTER 4: BENDING OF BEAMS
(74) CHAPTER 4: BENDING OF BEAMS This chapter will be devoted to the analysis of prismatic members subjected to equal and opposite couples M and M' acting in the same longitudinal plane. Such members are
More information