Plasmonic properties and sizing of core-shell Cu-Cu 2 O nanoparticles fabricated by femtosecond laser ablation in liquids ABSTRACT
|
|
- Sophie Bruce
- 6 years ago
- Views:
Transcription
1 Plasmonic properties and sizing of core-shell Cu-Cu O nanoparticles fabricated by femtosecond laser ablation in liquids J. M. J. Santillán 1, F. A. Videla 1,, D. C. Schinca 1, and L. B. Scaffardi 1, 1 Centro de Investigaciones Ópticas (CIOp), (CONICET La Plata - CIC), Argentina Departamento de Ciencias Básicas, Facultad de Ingeniería, UNLP, Argentina ABSTRACT The synthesis and study of optical properties of copper nanoparticles are of great interest since they are applicable to different areas such as catalysis, lubrication, conductive thin films and nanofluids. Their optical properties are governed by the characteristics of the dielectric function of the metal, its size and environment. The study of the dielectric function with radius is carried out through the contribution of free and bound electrons. The first one is corrected for size using the modification of the damping constant. The second one takes into consideration the contribution of the interband transitions from the d-band to the conduction band, considering the larger spacing between electronic energy levels as the particle decreases in size below nm. Taking into account these specific modifications, it was possible to fit the complex dielectric function, and consequently, determine optical parameters and band energy values such as the coefficient for bound electron contribution Q = x 1, gap energy E g = 1.95 ev, Fermi energy E F =.15 ev and damping constant for bound electrons γ b = 1.15 x 1 1 Hz. The fit of the experimental extinction spectra of the colloidal suspensions obtained by 5 µj ultrashort pulse laser ablation of solid target in water and acetone, reveals that the nanometric and subnanometric particles have a Cu- Cu O structure due to an oxidation reaction during the fabrication. The results were compared with those obtained by AFM, observing a very good agreement between the two techniques, showing that Optical Extinction Spectroscopy (OES) is a good complementary technique to standard electron microscopy. Keywords: Cu-Cu O nanoparticles, copper dielectric function, subnanometric size, optical extinction spectroscopy, ultrashort pulse laser ablation. 1. THEORETICAL BACKGROUND In general, the complex dielectric function for metals can be decomposed in two terms, a free-electron term and an interband (or bound-electron) term as: ε size ( ω, = ε ( ω, ε ( ω, (1) bound electrons + free electrons For bound electrons, the complex dielectric function arising due to transitions from the copper d-band to the conduction sp-band, can be calculated using the expression given by Scaffardi et al. [1]: ε bound ( ( )) [ ] ( ) x ωg x ω + γ b + i ωγ b 1 R R 1 F( x, T) ( x ω + γ ) b electrons( ω, = Q exp dx () ωg x + ω γ where ħω g is the copper gap energy (E g ), F (x, T) is the Fermi energy distribution function of conduction electrons of energy ħx at the temperature T with Fermi energy E F ; γ b represents the damping constant of the interband transition, ( ( R )) Q = Q 1 exp R size is a radius dependent proportionality factor [1], R is the particle radius, R =.35 nm is a scale factor and Q is the coefficient for bound electron contribution. For free electrons, the complex dielectric function can be written as: b Plasmonics: Metallic Nanostructures and Their Optical Properties X, edited by Mark I. Stockman, Proc. of SPIE Vol. 857, 857U 1 SPIE CCC code: /1/$18 doi: / Proc. of SPIE Vol U-1
2 ε free electrons ω p ( ω, = 1 (3) vf ω + i γ + C ω R where ω p = 13. x 1 15 Hz [] is the plasma frequency and the term in parenthesis in the denominator is the size modification of the free-electron damping constant. The value of γ = 1.5 x 1 1 Hz, was taken from Johnson and Christy [3] and v F = nm/s is the Fermi velocity for copper []. C =.8 is a constant that depends on the electron scattering processes inside the nanoparticle. The Q, E g, E F and γ b parameters that appear in eq. () influence independent features in the experimental dielectric function, especially in the imaginary part. For example, theoretical calculation of the imaginary part of the full dielectric function for different E g values changes the curve in the wavelength region between 35 and 53 nm while small variations in E F values influence the imaginary part in the region between 53 and 7 nm. When eq. (), (3) are introduced in eq. (1) to fit the dielectric function considering R = 1 nm (R>>R ), it is possible to determine the following parameters for copper: Q = x 1, E g = 1.95 ev, E F =.15 ev and γ b = 1.15 x 1 1 Hz. Figure 1 (a) and (b) shows the real and imaginary components of bound (eq. ) and free electron (eq. 3) contributions calculated separately, while its sum (full line) is the best fit to experimental values derived from complex refractive index data taken from Johnson and Christy [3], represented by full triangles. 1 (a) bound electrons 1 8 calculated values (b) ε' -1 - experimental values calculated values ε'' 6 experimental values -3 - free electrons free electrons bound electrons Figure 1. Comparison between experimental values (full triangles) and theoretical calculation for the real and imaginary part of copper dielectric function. Experimental values were derived from Johnson and Christy [3] while theoretical free and bound electron contributions to the complex dielectric function were carried out using eq. (1) to (3). (a) Real component ε and (b) imaginary component ε. Figure shows the behaviour of the real and the imaginary parts of the total dielectric function (eq. 1) as a function of wavelength for different nanometric and subnanometric particles radii, using the optimum parameters obtained after fitting the experimental dielectric function. It can be seen that the real part of the dielectric function (fig. (a)) is very sensitive to size for R < nm. However, this sensitivity decreases for the range - 1 nm and it is almost coincident with the curve for R = 1 nm. On the other hand, the imaginary part (fig. (b)) shows a similar limit behaviour for R > 15 nm, but there seems to be also a limiting behaviour for R =.6 nm. Proc. of SPIE Vol U-
3 ε' ( nm.8 nm 1 nm 1. nm nm 1 nm (a) ε'' (.6 nm.8 nm 1 nm 1. nm 16 nm 1 nm 1 8 (b) Figure. Real (a) and imaginary (b) parts of the copper complex dielectric function considering free and bound electron contributions for different values of nanometric and subnanometric particles radii. To study the influence of the subnanometric correction ( ( R )) 1 exp R in eq., the real and the imaginary part were calculated without it. Figure 3 (a) and (b) shows these calculations for the same radii as in fig. (a) and (b). It can be seen that the influence of this correction affects particles under nm radii approximately, especially in the wavelength region under 6 nm. The curves for ε (fig. 3 (a)) without the ( ( R )) splitting for radii under nm, while for radii over this value, the correction is negligible. 1 exp R correction show a larger ε' nm.8 nm 1 nm 1. nm nm 1 nm (a) ε''.6 nm.8 nm 1 nm 1. nm nm 16 1 nm 1 8 (b) Figure 3: theoretical calculation for full dielectric function using eq. () without the ( exp ( R )) 1 R subnanometric correction. (a) Real part and (b) imaginary part. Lack of inclusion of the subnanometric correction overestimates the dielectric function below 6 nm wavelength. A similar behaviour is observed in fig. 3 (b) for the imaginary part. These results show that the dielectric function for small particles is overestimated if the correction for the larger spacing between energy levels for small radii is not taken into account in eq. (). The apparently small influence of the subnanometric correction on the dielectric function is more noticeable when the optical extinction spectrum is calculated. Since the size of the copper particles considered in this paper is very small compared with the incident wavelength, the response to optical extinction can be described using the electrostatic approximation. In this approach, the expression for the extinction cross section is Proc. of SPIE Vol U-3
4 ( α) C = k Im () ext where α is the polarizability, π nm k' = is the wavenumber in the medium surrounding the particle, n m is the refractive λ index of the medium and λ is the wavelength of the incident light in vacuum. Since during ablation there are conditions of high temperature and high pressure in the plasma plume, oxidation processes proceed very fast over the formed copper particles and there is a large probability that copper-copper oxide particles may be generated. In view of this, it is important to take into account the expression of the polarizability for capped particles. So, for spherical particles with core-shell structure, the polarizability can be written as [5]: 3 α = π ( ε εm )( ε1 + ε ) + f ( ε1 ε )( ε m + ε ) ( ε + ε )( ε + ε ) + f ( ε ε )( ε ε ) 3 R (5) m 1 where R ' f = is the ratio between inner and outer radius volumes, R = r core is the metal central core (copper), R R = r (core + coating) is the outer radius (copper core + copper- oxide coat thickness), ε 1 = ε 1 (λ,, ε = ε (λ) and ε m = ε m (λ) are the dielectric functions of the core, coating (shell) and surrounding medium, respectively. Another parameter related with the extinction cross section is the extinction coefficient defined as Q m 1 ext = C π R'. Figure shows the extinction coefficient for a subnanometric copper bare core particle with and without correction. The differences between the spectra are more evident for wavelengths shorter than 6 nm. This difference in the shape of the spectra in the short wavelength region is readily measurable with a moderate resolution spectrophotometer. In turn, this behaviour is important when the composition of copper colloidal solution has to be determined by optical extinction spectroscopy. ext.6.5 Bare core Cu particles R =.7 nm Extinction..3. with bound electron size correction without bound electron size correction Figure. Extinction coefficient for subnanometric bare core Cu particle, with and without bound electron size correction. The difference in the spectra is more noticeable for wavelengths smaller that the plasmon peak, where the influence of the bound electron is more important. If a particle is surrounded by a shell of oxide (due, for example, to the fabrication process), the extinction spectrum is modified. Figure 5 shows the spectrum for a bare core (zero shell thickness) subnanometric particle of.7 nm radius compared with that corresponding to the same subnanometric particle capped with.35 nm (5% of core radius) thickness of Cu O. It can be seen that there is a considerable redshift of the peak position (about 7 nm in this Proc. of SPIE Vol U-
5 case) and an increase of the slope for wavelengths below 6 nm in the extinction spectrum when an oxide shell thickness is considered. The inset shows the complex dielectric function corresponding to the Cu O shell according to the data given by [6] used in the calculations ε' ε'' ε 6 Extinction R =.7 nm R =.7 nm; shell 5% R Figure 5. Theoretical optical extinction spectra of subnanometric copper bare core particle compared with a subnanometric Cu-Cu O particle with the same core and 5% of shell thickness for a.7 nm particle radius. The shell produces a measurable redshift of the plasmon peak. Inset shows the dielectric function of Cu O taken from Johnson and Christy [3].. EXPERIMENTAL Subnanometric and nanometric copper particles were fabricated by ultrafast pulse laser ablation in liquids. A high purity grade 1 mm thick copper circular disk was used to carry out these experiments. Laser ablation was performed using a Ti:Sapphire chirped pulsed amplification (CPA) system from Spectra Physics, emitting pulses of 1 fs width at 1 khz repetition rate centered at 8 nm wavelength. The maximum output energy was 1 mj per pulse. A 5 cm focal length was used to focus the laser beam on the target disk surface, which was immersed in water or acetone. The energy per pulse used in this experiment was 5 µj. The fabrication process was done during minutes, after which the solution shows a typical greenish colour in water or reddish in acetone, which is attributed to the presence of a large number of subnanometric and nanometric particles in the solution. Optical extinction spectroscopy was conducted by means of a Shimadzu spectrophotometer from 3 to 1 nm. Measurements were performed on highly diluted and sonicated colloidal suspensions immediately after laser ablation. Since many other authors work with laser ablation in pure liquids, no surfactants were added to the sample to make the analysis in pure water or acetone without extra additives. To compare our results with standard sizing technique, samples were also analyzed using AFM imaging. 3. RESULTS We have applied the above calculations to fit the experimental extinction spectra of the obtained suspension. Figure 6 shows the best fit of the experimental extinction spectrum corresponding to a colloidal suspension fabricated by fs laser ablation in water. The fit was attained considering a linear combination of two types of subnanometric core-shell particles: one with.9 nm core radius and shell thickness of % R and the other of the same core radius and a 15% R shell thickness. The coefficients of this combination,.5 and.55 respectively, give the optimum relative abundance of the specie. No combination of bare core particles could fit the whole spectrum. Proc. of SPIE Vol U-5
6 7 Extinction Relative abundance Experimental Theorical fit R [nm] % R 15 % R Figure 6. Experimental spectra and theoretical fit of colloidal suspension in water with pulse energy E = 5 µj. The fit is based on a combination of Cu-Cu O structures with the same core size and different shell thicknesses. Figure 7 shows the experimental curves (red full line) and the theoretical fit (hollow diamond and dashed line) corresponding to subnanometric and nanometric copper particles in acetone fabricated with 5 µj. The optimum size distribution has a dominant size of Cu bare core nm radius and includes a 7% abundance of nm radius and a 1% abundance of 1 nm radius of Cu-Cu O nanoparticles. There is also an important subnanometric contribution of.8 nm core radius of the same configuration whose abundance is 3%. It is important to remark the fact that core radii and shell thicknesses that appear in the histogram depicted in the inset indicate a bimodal distribution composed by small radii in the range 1 to nm and a larger one centered at 1 nm. Extinction Relative abundance R [nm] Experimental Theorical fit % R 5 % R 1 % R 15 % R % R Figure 7. Experimental spectra and theoretical fit of colloidal suspension in acetone with pulse energy E = 5 µj. The fit is based on a combination of Cu bare core and Cu-Cu O structures. Figure 8 (a) shows an AFM picture of the colloidal sample generated in water using 5 µj pulse energy laser ablation. Individual particles are clearly resolved by AFM imaging of the scanned 1. µm x 1. µm area under the low Proc. of SPIE Vol U-6
7 concentration condition used. The height profiles of line 1 and line in figure 8 (a) are shown in figure 8 (b). The scan of the first line in the range.9 µm < x < 1.1µm includes a single nanoparticle of.5 nm height (diameter). This size agrees with the results obtained by extinction spectroscopy of the same sample considering a core-shell Cu-Cu O particle with a core radius of.9 nm and a shell thickness of 1.35 nm. On the other hand, line scans over a. nm height nanoparticle, which agrees with the other size present in the core-shell Cu-Cu O colloidal suspension. 1, 1. 1, 1. (a),8.8 line 1 Y [µm],6.6 line,.,., X [µm] h [nm] 6 (b) (b) line line X [µm] X m ] Figure 8. (a) AFM image of the diluted colloidal suspension in water obtained by laser ablation with 5 µj pulse energy; (b) height (diameter) of the nanoparticles vs X position for line 1 and line marked on AFM image. Notice the single peak in line 1 and two single nanoparticle peaks in line.. CONCLUSIONS This work was focused on two aspects of subnanometric and nanometric copper particles characterization. The first one dealt with the analysis of the behaviour of free and bound electron contribution to the wavelength dependent dielectric function of copper. The free electron contribution was modified as usual including a term inversely proportional to the particle radius in the expression of the damping constant. With this modification, both real and imaginary parts of the free electron dielectric function show a noticeable dependence with size from 1 nm to 1 nm, with a limiting behaviour to for a radius R 1 nm. The bound electron contribution of transitions from the d-band to the conduction band was modelled using an expression that takes into account all the possible interband transitions. The parameters involved in the expression for the bound electron dielectric function, such as Q, E g, γ b and E F, were adjusted to fit simultaneously the real and imaginary experimental values for copper complex dielectric function. For subnanometric particles, a size dependence factor that accounts for the larger energy level spacing was included in the former expression for the bound electron dielectric function. This correction is important from subnanometric size to a radius of about nm, above which the correction is negligible. The second part of the work was devoted to the application of this technique to retrieve the size distribution of colloidal copper suspensions generated by fs laser ablation in water and acetone, as well as the possible appearance of Proc. of SPIE Vol U-7
8 core-shell copper-copper oxide structure. The expressions of the obtained dielectric function were used in the calculation of the polarizability of subnanometric and nanometric particles within Mie s theory, showing particularly the influence of bound electron size correction on the shape of the extinction spectrum of subnanometric particles. We have successfully fitted the experimental optical extinction spectra of subnanometric and nanometric coreshell Cu-Cu O particles fabricated by ultrashort pulse laser ablation of solid target in water and acetone with 5 µj pulse energy. In the former, the optimum fitting using Mie s theory yielded a dominant core radius R =.9 nm with a shell thickness distribution of % R and 15% R, while in the latter there is a larger size dispersion with a dominant size of Cu bare core nm radius together with a small abundance of Cu-Cu O 1 nm particles as well as an important subnanometric contribution of.8 nm core radius of the same configuration. We also showed that the method of spectral fitting is extremely sensitive to small variations in core radius (±.1 nm) or shell thickness (± %. These small changes modify the shape of the curves and depart from the experimental spectrum. For comparison purposes the colloidal suspensions generated by fs laser ablation were analyzed with standard microscopy technique such as AFM. The results show very good agreement with those obtained from the fitting of the experimental extinction spectra using the Drude-interband model. ACKNOWLEDGMENTS The authors wish to thank Dr Marcela Fernández van Raap from the Instituto de Físca La Plata (IFLP) for the AFM pictures. This work was performed by grants PIP (CONICET) 39, PME 6-18 (ANPCyT), 11/I151 (Facultad de Ingeniería, Universidad Nacional de La Plata) and funds from IFLP-CONICET, Argentina. Daniel C. Schinca and Fabián A. Videla are members of CIC, Comisión de Investigaciones Científicas de la Provincia de Buenos Aires. L. B. Scaffardi and Marcela B. Fernández van Raap are researchers of CONICET and Jesica M. J. Santillán is fellow of CONICET, Argentina. REFERENCES [1] Scaffardi, L. B. and Tocho J. O., Size dependence of refractive index of gold nanoparticles, Nanotechnology 17(5), (6). [] Cai, W. and Shalaev, V., Optical metamaterials. Fundamentals and Applications, Springer. Berlin, (1). [3] Johnson, P. B. and Christy, R. W., Optical constants of the noble metals, Phys. Rev. B 6(1), (197). [] Kaye, G. W. C. and Laby, T. H., Tables of Physical and Chemical Constants and Some Mathematical Functions, Longman Scientific and Technical, London, (1995). [5] Bohren, C. F. and Huffman, D. R., Absorption and Scattering of Light by Small Particles, Wiley, New York, (1998). [6] Palik, E. D., Handbook of Optical Constants of Solids vol 1, Academic, New York, (1998). Proc. of SPIE Vol U-8
are the eigenvalues of the permittivity tensor in Cartesian coordinates, written as, 3 " xx + i" xy ( , which gives
Supplemental Material for Faraday rotation enhancement of gold coated Fe2O3 nanoparticles: Comparison of experiment and theory Raj Kumar Dani, Hongwang Wang, Stefan H. Bossmann, Gary Wysin and Viktor Chikan,
More informationSupporting Information
Supporting Information Improved Working Model for Interpreting the Excitation Wavelength- and Fluence-Dependent Response in Pulsed aser-induced Size Reduction of Aqueous Gold Nanoparticles Daniel Werner
More informationSimulated Study of Plasmonic Coupling in Noble Bimetallic Alloy Nanosphere Arrays
CHAPTER 4 Simulated Study of Plasmonic Coupling in Noble Bimetallic Alloy Nanosphere Arrays 4.1 Introduction In Chapter 3, the noble bimetallic alloy nanosphere (BANS) of Ag 1-x Cu x at a particular composition
More informationSupplementary Figure S1 SEM and optical images of Si 0.6 H 0.4 colloids. a, SEM image of Si 0.6 H 0.4 colloids. b, The size distribution of Si 0.
Supplementary Figure S1 SEM and optical images of Si 0.6 H 0.4 colloids. a, SEM image of Si 0.6 H 0.4 colloids. b, The size distribution of Si 0.6 H 0.4 colloids. The standard derivation is 4.4 %. Supplementary
More informationOptical properties of TiO2:Ag composites
Optical properties of TiO:Ag composites Krzysztof Skorupski a a Wroclaw University of Technology, Chair of Electronics and Photonics Metrology, Boleslawa Prusa 53/55, 50-31 Wroclaw, Poland ABSTRACT The
More informationSUPPORTING INFORMATION. Influence of plasmonic Au nanoparticles on the photoactivity of
SUPPORTING INFORMATION Influence of plasmonic Au nanoparticles on the photoactivity of Fe 2 O 3 electrodes for water splitting Elijah Thimsen, Florian Le Formal, Michael Grätzel and Scott C. Warren* Interband
More informationDetermination of plasma frequency, damping constant, and size distribution from the complex dielectric function of noble metal nanoparticles
Determination of plasma frequency, damping constant, and size distribution from the comple dielectric function of noble metal nanoparticles Luis J. Mendoza Herrera, David Muñetón Arboleda, Daniel C. Schinca,
More informationOptical properties of spherical and anisotropic gold shell colloids
8 Optical properties of spherical and anisotropic gold shell colloids Core/shell colloids consisting of a metal shell and a dielectric core are known for their special optical properties. The surface plasmon
More informationTaking cascaded plasmonic field enhancement to the ultimate limit in silver nanoparticle dimers S. Toroghi* a, P. G. Kik a,b
Taking cascaded plasmonic field enhancement to the ultimate limit in silver nanoparticle dimers S. Toroghi* a, P. G. Kik a,b a CREOL, The College of Optics and Photonics, University of Central Florida,
More informationEnergy transport in metal nanoparticle plasmon waveguides
Energy transport in metal nanoparticle plasmon waveguides Stefan A. Maier, Pieter G. Kik, and Harry A. Atwater California Institute of Technology Thomas J. Watson Laboratory of Applied Physics, Pasadena,
More informationConnecting metallic nanoparticles by optical
Supplementary Information for Connecting metallic nanoparticles by optical printing Julián Gargiulo 1, Santiago Cerrota 1, Emiliano Cortés 1, Ianina L. Violi 1, Fernando D. Stefani* 1,2 1 Centro de Investigaciones
More informationInternational Journal of Pure and Applied Sciences and Technology
Int. J. Pure Appl. Sci. Technol., 9(1) (2012), pp. 1-8 International Journal of Pure and Applied Sciences and Technology ISSN 2229-6107 Available online at www.ijopaasat.in Research Paper Preparation,
More informationSUPPLEMENTARY INFORMATION
DETECTION LIMITS IN PHOTOTHERMAL MICROSCOPY Alexander Gaiduk, Paul V. Ruijgrok, Mustafa Yorulmaz, Michel Orrit Institute of Physics, Leiden University, P.O. Box 9504, 300 RA Leiden, The Netherlands SUPPLEMENTARY
More informationOptical and Photonic Glasses. Lecture 39. Non-Linear Optical Glasses III Metal Doped Nano-Glasses. Professor Rui Almeida
Optical and Photonic Glasses : Non-Linear Optical Glasses III Metal Doped Nano-Glasses Professor Rui Almeida International Materials Institute For New Functionality in Glass Lehigh University Metal-doped
More informationSupporting Information
Supporting Information Remarkable Photothermal Effect of Interband Excitation on Nanosecond Laser-induced Reshaping and Size Reduction of Pseudo-spherical Gold Nanoparticles in Aqueous Solution Daniel
More informationNano Optics Based on Coupled Metal Nanoparticles
Nano Optics Based on Coupled Metal Nanoparticles Shangjr Gwo ( 果尚志 ) Department of Physics National Tsing-Hua University, Hsinchu 30013, Taiwan E-mail: gwo@phys.nthu.edu.tw NDHU-Phys (2010/03/01) Background
More informationHYPER-RAYLEIGH SCATTERING AND SURFACE-ENHANCED RAMAN SCATTERING STUDIES OF PLATINUM NANOPARTICLE SUSPENSIONS
www.arpapress.com/volumes/vol19issue1/ijrras_19_1_06.pdf HYPER-RAYLEIGH SCATTERING AND SURFACE-ENHANCED RAMAN SCATTERING STUDIES OF PLATINUM NANOPARTICLE SUSPENSIONS M. Eslamifar Physics Department, BehbahanKhatamAl-Anbia
More informationOptical properties of morphology-controlled gold nanoparticles
Optical properties of morphology-controlled gold nanoparticles Qiguang Yang, 1* Jaetae Seo, 1* Wan-Joong Kim, SungSoo Jung, 3 Bagher Tabibi, 1 Justin Vazquez, 1 Jasmine Austin, 1 and Doyle Temple 1 1 Department
More informationSimulation of Surface Plasmon Resonance on Different Size of a Single Gold Nanoparticle
Journal of Physics: Conference Series PAPER OPEN ACCESS Simulation of Surface Plasmon Resonance on Different Size of a Single Gold Nanoparticle To cite this article: Norsyahidah Md Saleh and A. Abdul Aziz
More information7. Localized surface plasmons (Particle plasmons)
7. Localized surface plasmons (Particle plasmons) ( Plasmons in metal nanostructures, Dissertation, University of Munich by Carsten Sonnichsen, 2001) Lycurgus cup, 4th century (now at the British Museum,
More informationOptical cavity modes in gold shell particles
9 Optical cavity modes in gold shell particles Gold (Au) shell particles with dimensions comparable to the wavelength of light exhibit a special resonance, with a tenfold field enhancement over almost
More informationSynthesis of Cu 2 O, CuCl, and Cu 2 OCl 2 nanoparticles by ultrafast laser ablation of copper in liquid media
PRAMANA c Indian Academy of Sciences Vol. xx, No. x journal of Month 2014 physics pp. 1 7 Synthesis of Cu 2 O, CuCl, and Cu 2 OCl 2 nanoparticles by ultrafast laser ablation of copper in liquid media SYED
More informationSurface-enhanced raman scattering from a layer of gold nanoparticles
VNU Journal of Science, Mathematics - Physics 26 (2010) 187-192 Surface-enhanced raman scattering from a layer of gold nanoparticles Nguyen The Binh *, Nguyen Thanh Dinh, Nguyen Quang Dong, Vu Thi Khanh
More informationSpring 2009 EE 710: Nanoscience and Engineering
Spring 009 EE 710: Nanoscience and Engineering Part 10: Surface Plasmons in Metals Images and figures supplied from Hornyak, Dutta, Tibbals, and Rao, Introduction to Nanoscience, CRC Press Boca Raton,
More informationInvited Paper ABSTRACT 1. INTRODUCTION
Invited Paper Numerical Prediction of the Effect of Nanoscale Surface Roughness on Film-coupled Nanoparticle Plasmon Resonances Chatdanai Lumdee and Pieter G. Kik *,, CREOL, the College of Optics and Photonics;
More informationLecture 3: Optical Properties of Insulators, Semiconductors, and Metals. 5 nm
Metals Lecture 3: Optical Properties of Insulators, Semiconductors, and Metals 5 nm Course Info Next Week (Sept. 5 and 7) no classes First H/W is due Sept. 1 The Previous Lecture Origin frequency dependence
More informationLocalized surface plasmons (Particle plasmons)
Localized surface plasmons (Particle plasmons) ( Plasmons in metal nanostructures, Dissertation, University of Munich by Carsten Sonnichsen, 2001) Lycurgus cup, 4th century (now at the British Museum,
More informationObservation of coupled plasmon-polariton modes of plasmon waveguides for electromagnetic energy transport below the diffraction limit
Mat. Res. Soc. Symp. Proc. Vol. 722 2002 Materials Research Society Observation of coupled plasmon-polariton modes of plasmon waveguides for electromagnetic energy transport below the diffraction limit
More informationSupplementary Figure 1 Simulations of the lm thickness dependence of plasmon modes on lms or disks on a 30 nm thick Si 3 N 4 substrate.
Supplementary Figure 1 Simulations of the lm thickness dependence of plasmon modes on lms or disks on a 30 nm thick Si 3 N 4 substrate. (a) Simulated plasmon energy at k=30 µm 1 for the surface plasmon
More informationECE280: Nano-Plasmonics and Its Applications. Week8
ECE280: Nano-Plasmonics and Its Applications Week8 Surface Enhanced Raman Scattering (SERS) and Surface Plasmon Amplification by Stimulated Emission of Radiation (SPASER) Raman Scattering Chandrasekhara
More informationPlan of the lectures
Plan of the lectures 1. Introductory remarks on metallic nanostructures Relevant quantities and typical physical parameters Applications. Linear electron response: Mie theory and generalizations 3. Nonlinear
More informationElectronic Supplementary Information
Electronic Supplementary Material (ESI) for Physical Chemistry Chemical Physics. This journal is the Owner Societies 2014 Electronic Supplementary Information CW-Laser-Induced Morphological Changes of
More informationSupplementary information for. plasmonic nanorods interacting with J-aggregates.
Supplementary information for Approaching the strong coupling limit in single plasmonic nanorods interacting with J-aggregates. by Gülis Zengin, Göran Johansson, Peter Johansson, Tomasz J. Antosiewicz,
More informationSupporting Online Material. Highly Sensitive Plasmonic Silver Nanorods
Supporting Online Material Highly Sensitive Plasmonic Silver Nanorods Arpad Jakab, Christina Rosman, Yuriy Khalavka, Jan Becker, Andreas Trügler+, Ulrich Hohenester+, and Carsten Sönnichsen * MAINZ graduate
More informationSupporting information for Metal-semiconductor. nanoparticle hybrids formed by self-organization: a platform to address exciton-plasmon coupling
Supporting information for Metal-semiconductor nanoparticle hybrids formed by self-organization: a platform to address exciton-plasmon coupling Christian Strelow, T. Sverre Theuerholz, Christian Schmidtke,
More informationEELS, Surface Plasmon and Adsorbate Vibrations
EELS, Surface Plasmon and Adsorbate Vibrations Ao Teng 2010.10.11 Outline I. Electron Energy Loss Spectroscopy(EELS) and High Resolution EELS (HREELS) II. Surface Plasmon III. Adsorbate Vibrations Surface
More informationABSTRACT 1. INTRODUCTION
Cascaded plasmon resonances multi-material nanoparticle trimers for extreme field enhancement S. Toroghi a, Chatdanai Lumdee a, and P. G. Kik* a CREOL, The College of Optics and Photonics, University of
More informationNonlinear optics spectroscopy in glasses doped with nanoparticles
Nonlinear optics spectroscopy in glasses doped with nanoparticles Juliana Mara Pinto de Almeida 1, Luciana R. P. Kassab, Cleber R. Mendonça 1 and Leonardo De Boni 1 1 Instituto de Física de São Carlos,
More informationFluorescent silver nanoparticles via exploding wire technique
PRAMANA c Indian Academy of Sciences Vol. 65, No. 5 journal of November 2005 physics pp. 815 819 Fluorescent silver nanoparticles via exploding wire technique ALQUDAMI ABDULLAH and S ANNAPOORNI Department
More informationSCATTERING CROSS SECTION OF A META-SPHERE
Progress In Electromagnetics Research Letters, Vol. 9, 85 91, 009 SCATTERING CROSS SECTION OF A META-SPHERE A. Alexopoulos Electronic Warfare and Radar Division Defence Science and Technology Organisation
More informationInvestigating functionalized active coated nanoparticles for use in nano-sensing applications
Investigating functionalized active coated nanoparticles for use in nano-sensing applications Joshua A. Gordon 1*, Richard W. Ziolkowski 2, 1 1 College of Optical Sciences, University of Arizona, Tucson,
More informationCarrier dynamics of rubrene single-crystals revealed by transient broadband terahertz
Supplemental Material Carrier dynamics of rubrene single-crystals revealed by transient broadband terahertz spectroscopy H. Yada 1, R. Uchida 1, H. Sekine 1, T. Terashige 1, S. Tao 1, Y. Matsui 1, N. Kida
More informationarxiv:cond-mat/ v1 [cond-mat.mtrl-sci] 26 Aug 2003
Circular dichroism simulated spectra of chiral gold nanoclusters: A dipole approximation arxiv:cond-mat/0308552v1 [cond-mat.mtrl-sci] 26 Aug 2003 Carlos E. Román-Velázquez, 1 Cecilia Noguez, 2, and Ignacio
More informationThe effect of surface plasmon resonance on optical response in dielectric (core) metal (shell) nanoparticles
PRAMANA c Indian Academy of Sciences Vol. 85, No. 6 journal of December 2015 physics pp. 1245 1255 The effect of surface plasmon resonance on optical response in dielectric (core) metal (shell) nanoparticles
More informationSupporting Information. Optical Scattering Spectral Thermometry and Refractometry of a Single Gold Nanoparticle under CW laser excitation
Supporting Information Optical Scattering Spectral Thermometry and Refractometry of a Single Gold Nanoparticle under CW laser excitation Kenji Setoura, Daniel Werner, and Shuichi Hashimoto* Department
More informationSize dependence of multipolar plasmon resonance frequencies and damping rates in simple metal spherical nanoparticles
The original publication is available at www.eurphysj.org: http://www.epjst-journal.org/index.php?option=article&access=standard&itemid=9&url= /articles/epjst/pdf/7/5/st44.pdf EPJ manuscript No. (will
More informationDetermination of size and concentration of gold and silica nanoparticles from absorption and turbidity spectra. Nikolai Khlebtsov
Determination of size and concentration of gold and silica nanoparticles from absorption and turbidity spectra Nikolai Khlebtsov Institute of Biochemistry and Physiology of Plants and Microorganisms (IBPPM),
More informationEnhancing the Rate of Spontaneous Emission in Active Core-Shell Nanowire Resonators
Chapter 6 Enhancing the Rate of Spontaneous Emission in Active Core-Shell Nanowire Resonators 6.1 Introduction Researchers have devoted considerable effort to enhancing light emission from semiconductors
More informationSupplementary Information
Electrochemical Charging of Single Gold Nanorods Carolina Novo, Alison M. Funston, Ann K. Gooding, Paul Mulvaney* School of Chemistry & Bio21 Institute, University of Melbourne, Parkville, VIC, 3010, Australia
More informationPlasmonics. The long wavelength of light ( μm) creates a problem for extending optoelectronics into the nanometer regime.
Plasmonics The long wavelength of light ( μm) creates a problem for extending optoelectronics into the nanometer regime. A possible way out is the conversion of light into plasmons. They have much shorter
More informationPrediction and Optimization of Surface-Enhanced Raman Scattering Geometries using COMSOL Multiphysics
Excerpt from the Proceedings of the COMSOL Conference 2008 Hannover Prediction and Optimization of Surface-Enhanced Raman Scattering Geometries using COMSOL Multiphysics I. Knorr 1, K. Christou,2, J. Meinertz
More informationA General Kinetic-Optical Model for Solid-State Reactions Involving the Nano Kirkendall Effect. The Case of Copper Nanoparticle Oxidation
Supporting Information A General Kinetic-Optical Model for Solid-State Reactions Involving the Nano Kirkall Effect. The Case of Copper Nanoparticle Oxidation Mariano D. Susman, Alexander Vaskevich, * Israel
More informationDiffusion of silver in silicate glass and clustering in hydrogen atmosphere
Defect and Diffusion Forum Vols. 7-4 (5) pp. 689-694 online at http://www.scientific.net 5 Trans Tech Publications, Switzerland Diffusion of silver in silicate glass and clustering in hydrogen atmosphere
More informationBlueshift of the silver plasmon band using controlled nanoparticle dissolution in aqueous solution
Downloaded from orbit.dtu.dk on: Oct 23, 2018 Blueshift of the silver plasmon band using controlled nanoparticle dissolution in aqueous solution Mogensen, Klaus Bo; Kneipp, Katrin Published in: Proceedings
More informationNanophotonics: principle and application. Khai Q. Le Lecture 4 Light scattering by small particles
Nanophotonics: principle and application Khai Q. Le Lecture 4 Light scattering by small particles Previous lecture Drude model, Drude-Sommerfeld model and Drude-Lorentz model for conducting media (metal):
More informationSupplementary Information for. Vibrational Spectroscopy at Electrolyte Electrode Interfaces with Graphene Gratings
Supplementary Information for Vibrational Spectroscopy at Electrolyte Electrode Interfaces with Graphene Gratings Supplementary Figure 1. Simulated from pristine graphene gratings at different Fermi energy
More informationSupporting Information. Metallic Adhesion Layer Induced Plasmon Damping and Molecular Linker as a Non-Damping Alternative
Supporting Information Metallic Adhesion Layer Induced Plasmon Damping and Molecular Linker as a Non-Damping Alternative Terefe G. Habteyes, Scott Dhuey, Erin Wood, Daniel Gargas, Stefano Cabrini, P. James
More informationSCATTERING OF ELECTROMAGNETIC WAVES ON METAL NANOPARTICLES. Tomáš Váry, Juraj Chlpík, Peter Markoš
SCATTERING OF ELECTROMAGNETIC WAVES ON METAL NANOPARTICLES Tomáš Váry, Juraj Chlpík, Peter Markoš ÚJFI, FEI STU, Bratislava E-mail: tomas.vary@stuba.sk Received xx April 2012; accepted xx May 2012. 1.
More informationOne-step Solution Processing of Ag, Au and Hybrids for SERS
1 2 3 Supplementary Information One-step Solution Processing of Ag, Au and Pd@MXene Hybrids for SERS 4 5 6 Elumalai Satheeshkumar 1, Taron Makaryan 2, Armen Melikyan 3, Hayk Minassian 4, Yury Gogotsi 2*
More informationSUPPLEMENTARY INFORMATION
SUPPLEMENTARY INFORMATION Coupling of Plasmonic Nanopore Pairs: Facing Dipoles Attract Each Other Takumi Sannomiya 1, Hikaru Saito 2, Juliane Junesch 3, Naoki Yamamoto 1. 1 Department of Innovative and
More informationNanoscale optical circuits: controlling light using localized surface plasmon resonances
Nanoscale optical circuits: controlling light using localized surface plasmon resonances T. J. Davis, D. E. Gómez and K. C. Vernon CSIRO Materials Science and Engineering Localized surface plasmon (LSP)
More informationThe Dielectric Function of a Metal ( Jellium )
The Dielectric Function of a Metal ( Jellium ) Total reflection Plasma frequency p (10 15 Hz range) Why are Metals Shiny? An electric field cannot exist inside a metal, because metal electrons follow the
More informationTemperature ( o C)
Viscosity (Pa sec) Supplementary Information 10 8 10 6 10 4 10 2 150 200 250 300 Temperature ( o C) Supplementary Figure 1 Viscosity of fibre components (PC cladding blue; As 2 Se 5 red; CPE black) as
More informationUltrafast spectroscopy of a single metal nanoparticle. Fabrice Vallée FemtoNanoOptics group
CENTRE NATIONAL DE LA RECHERCHE SCIENTIFIQUE Ultrafast spectroscopy of a single metal nanoparticle Fabrice Vallée FemtoNanoOptics group LASIM, CNRS - Université Lyon 1, France Metal Nanoparticles: from
More information6. Plasmon coupling between a flat gold interface and gold nanoparticles.
6. Plasmon coupling between a flat gold interface and gold nanoparticles. 6.1. Introduction In this outlook oriented chapter the applicability of the multilayered system used in chapter 4.1., for the study
More informationChapter 2 Optical Properties of Nanocomposites Containing Metal Nanoparticles
Chapter 2 Optical Properties of Nanocomposites Containing Metal Nanoparticles Interaction of light with nanocomposites reveals novel optical phenomena indicating unrivalled optical properties of these
More informationNegative Index of Refraction in Optical Metamaterials
1 Negative Index of Refraction in Optical Metamaterials V. M. Shalaev, W. Cai, U. Chettiar, H.-K. Yuan, A. K. Sarychev, V. P. Drachev, and A. V. Kildishev School of Electrical and Computer Engineering,
More informationPreparation of Gold Nanoparticles by Pulsed Laser Ablation in NaOH solution
Preparation of Gold Nanoparticles by Pulsed Laser Ablation in NaOH solution Raheem Gaayied Kadhim Maryam falah noori Babylon university /colloge of the scince Abdulrahman Khalaf Ali School of Applied Sciences
More informationSet-up for ultrafast time-resolved x-ray diffraction using a femtosecond laser-plasma kev x-ray-source
Set-up for ultrafast time-resolved x-ray diffraction using a femtosecond laser-plasma kev x-ray-source C. Blome, K. Sokolowski-Tinten *, C. Dietrich, A. Tarasevitch, D. von der Linde Inst. for Laser- and
More informationFREE-ELECTRON ANALYSIS OF OPTICAL PROPERTIES OF THERMALLY EVAPORATED GOLD FILMS N. EL-KA DRY
Vol. 86 (1994) ACTA PHYSICA POLONICΛ Α No. 3 FREE-ELECTRON ANALYSIS OF OPTICAL PROPERTIES OF THERMALLY EVAPORATED GOLD FILMS N. EL-KA DRY Physics Department, Μinia University, El-Minia, Egypt (Received
More informationSupplementary Figure 1 Reflection and transmission measurement. Supplementary Figure 2 Wavelength dependence of χ
Supplementary Figure 1 Reflection and transmission measurement. (a) and (b) show the reflection and transmission curves with 45 incident angle and S-polarization for the 3 nm metal quantum well sample.
More informationTunable plasmon resonance of a touching gold cylinder arrays
J. At. Mol. Sci. doi: 10.4208/jams.091511.101811a Vol. 3, No. 3, pp. 252-261 August 2012 Tunable plasmon resonance of a touching gold cylinder arrays Geng-Hua Yan a, Yan-Ying Xiao a, Su-Xia Xie b, and
More information1 Mathematical description of ultrashort laser pulses
1 Mathematical description of ultrashort laser pulses 1.1 We first perform the Fourier transform directly on the Gaussian electric field: E(ω) = F[E(t)] = A 0 e 4 ln ( t T FWHM ) e i(ω 0t+ϕ CE ) e iωt
More informationEffect of Addition Au Nanoparticles on Emission Spectra of Laser Dye
International Journal of Applied Engineering Research ISSN 973-462 Volume 2, Number 24 (27) pp. 4833-484 Effect of Addition Au Nanoparticles on Emission Spectra of Laser Dye Sara Ali Razzak, Lazem Hassan
More informationNanocomposite photonic crystal devices
Nanocomposite photonic crystal devices Xiaoyong Hu, Cuicui Lu, Yulan Fu, Yu Zhu, Yingbo Zhang, Hong Yang, Qihuang Gong Department of Physics, Peking University, Beijing, P. R. China Contents Motivation
More informationAluminum for nonlinear plasmonics: Methods Section
Aluminum for nonlinear plasmonics: Methods Section Marta Castro-Lopez, Daan Brinks, Riccardo Sapienza, and Niek F. van Hulst, ICFO - Institut de Ciencies Fotoniques, and ICREA - Institució Catalana de
More informationSupplementary Figure 1. Schematics of light transmission and reflection from a slab confined between
Supplementary Figures: Supplementary Figure. Schematics of light transmission and reflection from a slab confined between two infinite media. Supplementary Figure. Reflectivity of a magneto-electric slab
More informationEnhanced Nonlinear Optical Response from Nano-Scale Composite Materials
Enhanced Nonlinear Optical Response from Nano-Scale Composite Materials Robert W. Boyd The Institute of Optics, University of Rochester, Rochester, NY 14627, USA with special thanks to: Nick Lepeshkin,
More informationSUPPORTING INFORMATION. Plasmon Spectroscopy and Chemical Structure of Small Bimetallic Cu (1-x) Ag x clusters.
SUPPORTING INFORMATION Plasmon Spectroscopy and Chemical Structure of Small Bimetallic (1-x) x clusters. Michel Pellarin a*, Inas Issa a, Cyril Langlois b, Marie-Ange Lebeault a, Julien Ramade a, Jean
More informationOptical Characteristics of ZnO Based Photodetectors Doped with Au Nanoparticles
nd International Conference on Mechanical and Electronics Engineering (ICMEE ) Optical Characteristics of ZnO Based Photodetectors Doped with Au Nanoparticles S. Mohammadnejad, S. G. Samani, and E. Rahimi
More informationInitiation of nuclear reactions under laser irradiation of Au nanoparticles in the aqueous solution of Uranium salt. A.V. Simakin and G.A.
Initiation of nuclear reactions under laser irradiation of Au nanoparticles in the aqueous solution of Uranium salt A.V. Simakin and G.A. Shafeev Wave Research Center of A.M. Prokhorov General Physics
More informationComputational Study on the Effect of the Pulse Length on Laser Ablation Processes
Lasers in Manufacturing Conference 015 Computational Study on the Effect of the Pulse Length on Laser Ablation Processes "Stefan Tatra *, Rodrigo Gómez Vázquez, Andreas Otto" "Vienna University of Technology,
More informationUV-vis Analysis of the Effect of Sodium Citrate on the Size and the Surface Plasmon Resonance of Au NPs. Eman Mousa Alhajji
UV-vis Analysis of the Effect of Sodium Citrate on the Size and the Surface Plasmon Resonance of Au NPs Eman Mousa Alhajji North Carolina State University Department of Materials Science and Engineering
More informationNanofabrication and characterization of gold metal by Pulsed Laser. Ablation in SDS solution
Nanofabrication and characterization of gold metal by Pulsed Laser Ablation in SDS solution Raheem Gaayied Kadhim (Corresponding author) College of the Science - University of Babylon Tel:0964-7801305881
More informationMANIPAL INSTITUTE OF TECHNOLOGY
SCHEME OF EVAUATION MANIPA INSTITUTE OF TECHNOOGY MANIPA UNIVERSITY, MANIPA SECOND SEMESTER B.Tech. END-SEMESTER EXAMINATION - MAY SUBJECT: ENGINEERING PHYSICS (PHY/) Time: 3 Hrs. Max. Marks: 5 Note: Answer
More informationUV femtosecond laser inscribes a 300-nm-period nanostructure. in a pure fused silica
UV femtosecond laser inscribes a 300-nm-period nanostructure in a pure fused silica Mykhaylo Dubov, Vladimir Mezentsev, Ian Bennion Photonics Research Group, Aston University, Birmingham B4 7ET, UK David
More informationOptical Properties of Solid from DFT
Optical Properties of Solid from DFT 1 Prof.P. Ravindran, Department of Physics, Central University of Tamil Nadu, India & Center for Materials Science and Nanotechnology, University of Oslo, Norway http://folk.uio.no/ravi/cmt15
More informationSurface Plasmon Amplification by Stimulated Emission of Radiation. By: Jonathan Massey-Allard Graham Zell Justin Lau
Surface Plasmon Amplification by Stimulated Emission of Radiation By: Jonathan Massey-Allard Graham Zell Justin Lau Surface Plasmons (SPs) Quanta of electron oscillations in a plasma. o Electron gas in
More information386 Brazilian Journal of Physics, vol. 30, no. 2, June, 2000 Atomic Transitions for the Doubly Ionized Argon Spectrum, Ar III 1 F. R. T. Luna, 2 F. Br
386 Brazilian Journal of Physics, vol. 30, no. 2, June, 2000 Atomic Transitions for the Doubly Ionized Argon Spectrum, Ar III 1 F. R. T. Luna, 2 F. Bredice, 3 G. H. Cavalcanti, and 1;4 A. G. Trigueiros,
More informationII Theory Of Surface Plasmon Resonance (SPR)
II Theory Of Surface Plasmon Resonance (SPR) II.1 Maxwell equations and dielectric constant of metals Surface Plasmons Polaritons (SPP) exist at the interface of a dielectric and a metal whose electrons
More informationWhat is spectroscopy?
Absorption Spectrum What is spectroscopy? Studying the properties of matter through its interaction with different frequency components of the electromagnetic spectrum. With light, you aren t looking directly
More informationPIC simulations of laser interactions with solid targets
PIC simulations of laser interactions with solid targets J. Limpouch, O. Klimo Czech Technical University in Prague, Faculty of Nuclear Sciences and Physical Engineering, Břehová 7, Praha 1, Czech Republic
More informationUltrafast synthesis and switching of light polarization in nonlinear anisotropic metamaterials
SUPPLEMENTARY INFORMATION Letters DOI: 10.1038/s41566-017-0002-6 In the format provided by the authors and unedited. Ultrafast synthesis and switching of light polarization in nonlinear anisotropic metamaterials
More informationNonlocal effects on optical and molecular interactions with metallic nanoshells
PHYSICAL REVIEW B 73, 125438 2006 Nonlocal effects on optical and molecular interactions with metallic nanoshells Railing Chang 1 and P. T. Leung 2 1 Institute of Optoelectronic Sciences, National Taiwan
More informationTitle. Author(s)Nagasaki, Akira; Saitoh, Kunimasa; Koshiba, Masanori. CitationOptics Express, 19(4): Issue Date Doc URL.
Title Polarization characteristics of photonic crystal fib Author(s)Nagasaki, Akira; Saitoh, Kunimasa; Koshiba, Masanori CitationOptics Express, 19(4): 3799-3808 Issue Date 2011-02-14 Doc URL http://hdl.handle.net/2115/45257
More informationSpatial Coherence Properties of Organic Molecules Coupled to Plasmonic Surface Lattice Resonances in the Weak and Strong Coupling Regimes
Spatial Coherence Properties of Organic Molecules Coupled to Plasmonic Surface Lattice Resonances in the Weak and Strong Coupling Regimes Supplemental Material L. Shi, T. K. Hakala, H. T. Rekola, J. -P.
More informationModification of Solar Energy Harvesting in Photovoltaic Materials by Plasmonic Nanospheres: New Absorption Bands in Perovskite Composite Film
Article Subscriber access provided by INSTYTUT FIZYKI PAN Modification of Solar Energy Harvesting in Photovoltaic Materials by Plasmonic Nanospheres: New Absorption Bands in Perovskite Composite Film Krystyna
More informationLight Interaction with Small Structures
Light Interaction with Small Structures Molecules Light scattering due to harmonically driven dipole oscillator Nanoparticles Insulators Rayleigh Scattering (blue sky) Semiconductors...Resonance absorption
More informationLecture 20 Optical Characterization 2
Lecture 20 Optical Characterization 2 Schroder: Chapters 2, 7, 10 1/68 Announcements Homework 5/6: Is online now. Due Wednesday May 30th at 10:00am. I will return it the following Wednesday (6 th June).
More information