DEFORMATION PATTERN AND FAILURE CRITERIA OF WOVEN COMPOSITE PREFORM IN GENERAL BIAS EXTENSION
|
|
- Jasper Simpson
- 5 years ago
- Views:
Transcription
1 DEFORMATION PATTERN AND FAILURE CRITERIA OF WOVEN COMPOSITE PREFORM IN GENERAL BIAS EXTENSION B. Zhu 1,2*, T.X. Yu 1, X.M. Tao 2 1 Department of Mechanical Engineering, Hong Kong University of Science and Technology, Clear Water Bay, Kowloon, Hong Kong. 2 Institute of Textiles and Clothing, Hong Kong Polytechnic University, Hung Hom, Kowloon, Hong Kong. * Corresponding author, tczb@polyu.edu.hk SUMMARY A series of bias extension tests was carried out on balanced plain woven composite preforms with various aspect ratios, revealing that different aspect ratios may result in different first failures. By competition of the corresponding required energies, the failure of wrinkling or inter-yarn slippage is approximately predicted. Keywords: Woven composite preform, Bias extension, Wrinkling, Slippage, Energy method INTRODUCTION Textile composite materials have demonstrated their superiorities to be structural components due to the physical and mechanical advantages such as high specific stiffness and strength, low weight, nice integral performance, good spatial properties, and so on. In particular, textile composites possess better flexibility than conventional metals so that they can be shaped more easily into many complicated contours. In industry, the most efficient way to form textile composites is through stamping operation [1, 2], in which a flat sheet of material is stamped into a specific shape with a pair of punch and die. However, a crucial and challenging problem that restricts the stamping operation is the material s formability. Taking a woven fabric textile composite as an example, it is recognized that its primary deformation mode during forming is in-plane large shear deformation between two groups of yarns. In the presence of complex boundary conditions, there are mainly two types of failures: wrinkling [3, 4] and slippage [5, 6]. Inter-yarn slippage, i.e., pulling out of yarns from each other, may occur during shear process, especially when yarns are under tension with free ends. This inter-yarn slippage can be characterized by widely adopted bias extension test [7]. One of the most important and attractive characters of bias extension is that both wrinkling and slippage may possibly take place during the test process. In this connection, a bias extension test involves more complicated factors and information, which is closer to practical deformation cases as occurred in real stamping operations.
2 Our previous paper [8] has reported an experimental and theoretical study, which includes the analysis of the large deformation behaviour, the determination of the onset of slippage, and the simulation of the load-displacement response of a woven composite preform with an aspect ratio λ = 2. In the present paper, the bias extension tests with various aspect ratios are described and both wrinkling and slippage failures are investigated. The present study not only aims to characterize the inter-yarn slippage, but also investigates the onset of the two competitive failure modes and their relations under different loading conditions, so as to deepen our understanding on the formability and large deformation pattern of woven composite preforms. BIAS EXTENSION TESTS Test Conditions The test sample was made from continuous E-glass fibers reinforced thermoplastic Polypropylene, as described in paper [8]. Besides λ = 2 ( mm 2 ), two other aspect ratios of rectangular specimens were used in the tests: λ = 1.33 ( mm 2 ), and λ = 1 ( mm 2 ). The tension load was applied along the direction 45 o inclined to the yarns, by using two steel plates for clamping. The loading speed was 10mm/min, and the loading width was kept as 115mm, smaller than the side length. Tests were implemented with a load cell of 1.5kN on Universal Testing Machine at room temperature. Test Results Figure 1. Bias extension test results under 10mm/min at 20 o C. Load vs. crosshead displacement curves under different aspect ratios are plotted in Figure 1. Smaller aspect ratio corresponds to wider specimen that has more material deformed especially at large deformation stage, which results in a larger external load. Comparing the three curves, the force finally decreases in the cases of λ = 2 and 1.33; while for λ = 1, test was stopped in the middle because the load exceeded the limit of load cell thus no force drop had been observed yet. Another phenomenon is that for λ = 2, wrinkling is almost invisible throughout the whole test; for λ = 1.33, wrinkling happened first followed by the inter-yarn slippage; but for λ = 1, no obvious slippage
3 was observed until the end of the test while the wrinkling was significant. It indicates that obvious inter-yarn slippage occurs on narrow specimens, and due to larger area of the wider specimens, slippage is harder to take place, which also agrees with our expectation. Deformation Evolution Photographs were taken during the tests to trace the deformation process of the material, and digital image correlation analysis was conducted. The calculated maximum shear strain increment fields over the specimen area together with the history of measured shear angle helped to identify a general deformation pattern (see Figure 2), where the top and bottom triangular regions remain undeformed, and the inter-yarn shear angle is γ in the center and γ/2 in the corner, respectively. The yarn bending effect along the boundaries of relevant regions can be neglected; therefore, different aspect ratios only result in different area of free regions. Particular attentions should be paid that this pattern is only valid within the initial phase of deformation before any failure occurs. Figure 2. General deformation pattern in bias extension tests. Together with the photographs, three or four typical deformation phases are identified relevant to densification, failure and post-failure phenomena on the sample, depending on the aspect ratio. For λ = 2, there are three typical phases (s denotes the crosshead displacement): (1) Phase I (0 < s < 45mm): 7 regions with different shear angles could be distinguished. Besides shear, additional increasing tension takes place along yarns. (2) Phase II (45mm < s < 70mm): Since the yarn tension reaches a critical value and the yarns in the central part are free-ended, they cannot suffer further tension, so that interyarn slippage starts from the middle of the sample and extends to both the top and bottom, which can be regarded as the onset of a slippage failure. (3) Phase III (s > 70mm): Shear deformation ceases and slippage area shrinks as represented by the non-uniformity of the deformation field. For λ = 1.33, there exist four typical phases: (1) Phase I (0mm < s < 45mm): The same as before except for larger area of the 4 freeend regions around the corners.
4 (2) Phase II (45mm < s < 65mm): Since the required energy for inter-yarn slippage is relatively large, wrinkling first occurs instead of slippage. (3) Phase III (65mm < s < 85mm): Due to the free end of yarns, slippage happens when the wrinkling gets significant at a larger extension. (4) Phase IV (s > 85mm): The slippage becomes non-uniform and localized. The case of λ = 1 is similar to that of λ = 1.33, except that slippage happens even later at s = 75mm, and the wrinkling is more serious. THEORETICAL PREDICTION OF FIRST FAILURE Test results show that inter-yarn slippage occurs for λ = 2, but in the cases of λ =1.33 and 1, wrinkling first occurs instead of the slippage. The theoretical prediction of initial failure with different aspect ratios is of great interest to explain the experimental observation, to regulate the forming conditions and to improve the formability. An energy method was adopted to predict the load-displacement response for λ = 2 [8], and it is applicable for any other aspect ratios. In the following, the energy method, whose feasibility has been verified in Refs [8, 9], is used again to determine the initial failure in the tests with three different aspect ratios. There are three possible deformation modes which dominate bias extensions: in-plane shear, out-of-plane wrinkling, and inter-yarn slippage. Different mechanisms can be reflected by their corresponding parts of energy during the fabric s deformation, so the material s behaviour has three possible bifurcations, and the real one renders the minimum consumed energy. In view of this basic consideration, the energy increments of the three modes should be estimated, respectively. First, we consider the case of λ = 2. According to the proposed deformation pattern, by neglecting the influence of additional yarn tension, the in-plane shear energy increment over the whole specimen is equal to dw s = dw ( γ ) A + dw ( γ / 2) A (1) s center s corner where d W s (γ ) is the shear energy increment per area obtained from the experimental result of the picture frame test [10]; A center and A corner are the areas of central and marginal parts, respectively. Since the central shear deformation is larger than the corner one, if wrinkling happens, it will first locate merely in the central region, thus the wrinkling energy increment is equal to dw wrinkle = dw γ ) A / 4 (2) wrinkle ( center where ) W wrinkle (γ d is the wrinkling energy increment in a fabric element [9]. To estimate the energy dissipated by inter-yarn slippage, it is assumed that although observed slippage always localizes in local regions, every fabric element which has the
5 tendency to slip should reach the same critical state exactly before slippage happens. Therefore, the energy increment dissipated by slipping is found to be dwf ( γ ) = µ A [ P( γ) + N( γ)] d 2t0 N( γ ) = 2µ 2 P( γ) + N0 w0 d = 2 w0 (cos[(90 γ dγ) 2] cos[(90 γ) 2]) cos[(90 γ) 2] (3) where P (γ ) is the transversely compressive force to yarns per area [8]; N (γ ) is the normally compressive force per over-lapping region; N 0 = 0.05N is the measured initial normally compressive force in a unit cell; d is the relative sliding displacement; µ = 0.35 is the sliding frictional coefficient between yarns; Σ represents the summation of the corresponding effective areas, which will be generally discussed in next Section; w 0 and t 0 are initial yarn width and thickness, respectively. By applying Equations (1), (2), (3), and canceling dγ for all cases, the nominal energy increments of the three deformation modes over the whole specimen are represented by the central shear angle as shown in Figure 3. It reveals that before central shear angle reaches 41 o, where the displacement is about 40mm, in-plane shear has the minimum energy increasing rate, which agrees with the real deformation in this stage; later on, the curve of slippage first intersects with the shear one, indicating that inter-yarn slippage will take place at this point, which is also in a good accordance with the experimental observation (displacement s = 45mm). Figure 3. Nominal energy increments of three possible deformation modes for λ = 2. As for λ = 1.33 and 1, the estimations of shear and slipping energy increments remain the same, except that relevant effective area increases with smaller λ, i.e., wider specimen. A main difference rests with the wrinkling energy. Since the loading width (115mm) at two sides is smaller than the width of the specimen (172.5mm for λ = 1.33 and 230mm for λ = 1), localized horizontal compressive stress will be induced in the
6 central region; as a result, the central region gets additional inward compression, which accelerates the onset of wrinkling. However, it is difficult to analytically obtain the internal compression due to the large deformation state and non-uniform fabric structure. In this regard, a simple equivalent force analysis in a macroscopic scale is utilized based on the textile structure. As sketched in Figure 4, the test process is regarded to be quasistatic, so every part of the specimen should keep equilibrium under external forces. As the left-side triangular part A is under tensions T along the two groups of crossing yarns directly from B and C, there must be another outward force F to keep it in balance. Contrarily, the central region receives the reactionary inward force, F, that accelerates wrinkling. Figure 4. Equivalent inward compressive force to the central region. For simplicity, an approximate assumption is made that the external tension F 2 is equal to the addition of all the static friction in parts A, B, D, and the friction is distributed uniformly with respect to area. Consequently, after subtracting the frictions in B and D, the remained tension to part A is T 0.3 F = (4) 2 where F is the total external force obtained from the experiment as a function of shear angle γ. Accordingly, the resultant inward compressive force to the central region is F = 0.3 F sin( π 4 γ 2) (5)
7 By employing the formula for the wrinkling energy increment [9], where F does negative work, the energy increment in a fabric element is found as 8EI cosγ dγ 3γ cosγ dw wrinkle = + 2 w0 µ N(1 + ) + 2Psinγ + 2µ P cosγ dγ D 2π π π γ 0.3F sin w0 cosγ dγ 4 2 (6) where EI = Nm 2, D 17.5µm, w 0 = 4.34mm, µ = 0.3, N = 0.05N. On the other hand, because the compressive force F only locates near the left vertex of the central region, and if the effect is supposed to decrease linearly from the left vertex to zero at the top vertex, the average of the force should be roughly halved with respect to the whole central region. Finally, the wrinkling energy increment of the whole specimen should be dw wrinkle 1 = 66 dwwrinkle (7) 2 where 66 is number of fabric elements in the central region. Based on the formulae given above, the nominal energy increments in the cases of λ = 1.33 and λ = 1 are plotted in Figure 5 and Figure 6, respectively. Comparing the energy increments of three possible deformation modes, it is clearly seen that wrinkling happens when the central shear angle reaches about 43 o for λ = 1.33 and 41 o for λ = 1. In the account of larger internal compression induced in the wider specimen, the required wrinkling energy is less than that in narrower one; consequently, the local wrinkling in wider specimen happens earlier. Referring the relationship between shear angle and displacement, our theoretical analysis predicts the critical displacement at wrinkling as 45mm for λ = 1.33 and 43mm for λ = 1, respectively, which agrees well with the experimental results. Throughout the whole test process, the curve of slipping energy is always not the minimal one, which interprets that slippage will not occur. However, the deformation pattern of the specimen, as well as each deformation mode, may greatly change after wrinkling, so the curves are no longer reliable. In this regard, the theoretical model can only be used to determine the onset of initial failure, while the material s post-failure behaviour is not our concern and indeed it is less important in the practical forming process.
8 Figure 5. Nominal energy increments of three possible deformation modes for λ = Figure 6. Nominal energy increments of three possible deformation modes for λ = 1. GENERAL CRITERION OF FAILURE IN BIAS EXTENSION Previous analysis has shown that the area of free-end and central regions is crucial to the failures, and whether slippage and wrinkling occurs or not depend on the relative magnitude of corresponding energies consumed. To express the energy increments as functions of the aspect ratio and loading width, a general case is considered, where the tensile loading width is H 0, sample width is W 0 (W 0 H 0 ), and sample length is L 0 (L 0 > H 0, otherwise two ends of yarns will be clamped in the fixture with no deformability), the required energy increment can be estimated by the map shown in Figure 7. The potential shear energy involves all the areas except the top and bottom undeformed triangles, where the shear angle is γ in the central region, and is γ/2 in all other regions. The wrinkling energy is estimated merely in the central region, taking into consideration of the localized inward compression as discussed above. To estimate the slipping energy, yarns are classified into two types: those represented in dashed line are completely freeended, which can slide both parallel to each other and with respect to the crossing ones; in other words, both P and N should be incorporated in the sliding friction; on the other hand, yarns in solid line are half free-ended, which can only slide with respect to the crossing groups, only with N being considered. Based on these idealizations,
9 corresponding effective areas of each deformation mode in different regions can be estimated, and the energy increments can be derived as functions of geometrical dimensions, H 0, W 0, L 0, and γ, with given material properties. Detailed expressions are skipped here to save space. General conclusions are that wide specimen with smaller aspect ratio benefits wrinkling and toughens inter-yarn slippage, and larger loading ratio makes wrinkling easier to happen rather than slippage. Figure 7. Deformation map of a general bias extension test. CONCLUSIONS Bias extension tests were conducted on the specimen of balanced plain woven textile composite preforms with different aspect ratios. For various aspect ratios and loading ratios, different first failure modes were observed from experiments. Large deformation process was analyzed with a general pattern proposed, where three or four typical phases can be identified. There are three possible deformation modes throughout the test, i.e., in-plane shear, out-of-plane wrinkling and inter-yarn slippage. Shear deformation and yarn tension pre-dominate the initial phase, and slippage or wrinkling happens afterwards beyond the limit of static friction and in-plane shear, respectively. In the post-failure phase, the deformation field becomes non-uniform, leading to a separation of specimen in a localized region. To build a theoretical model, the energy method has been utilized again to reveal the relative possibility of each deformation mode. From the theoretical results, the onset of first failure mode with different aspect ratios is predicted, demonstrating good agreement with the experiment. It is concluded that small loading ratio to the specimen causes localized inward compressive stress which spurs wrinkling, and that large area of free-ended region prevents early slippage. The significance of this study recommends a uniform loading condition in the forming of woven textile composite preforms during stamping, as well as fixed ends of yarns or larger area of free-ended regions if possible.
10 ACKNOWLEDGEMENTS The work reported in this paper is a part of a Hong Kong CERG project numbered HKUST6012/02E. The financial support from the Hong Kong Research Grant Council is gratefully acknowledged. The authors would also like to thank the Benchmark group led by Prof. J. Cao of Northwestern University, USA, for supplying the composite materials. References 1. Cogswell F.N. (1992). Thermoplastic Aromatic Polymer Composites. Butterworth-Heinemann. 2. Tucker C.L. (1997). Forming of Advanced Composites. Advanced Composites Manufacturing, Wiley, New York. 3. Gutowski T.G., Dillon G., Chey S., Li H. (1995). Laminate wrinkling scaling laws for ideal composites. Composites Manufacturing, 6: Arndt R.D. (1991). Fabric preforming for structural reaction injection molding. In: Proceedings of Conference on Advanced Composite Materials: New Developments and Applications. Detroit, Michigan, USA, Skelton J. (1976). Fundamentals of fabric shear. Textile Research Journal, 46: Potter KD. (1979). The influence of accurate stretch data for reinforcements on the production of complex structural mouldings. Composites, 10: Harrison P., Clifford M.J., Long A.C. (2004). Shear characterization of woven textile composites: a comparison between picture frame and bias extension experiments. Composites Science and Technology, 64: Zhu B., Yu T.X., Tao X.M. (2007). Large deformation and slippage mechanism of plain woven composite in bias extension. Composites Part A, 38: Zhu B., Yu T.X., Teng J., Tao X.M. (2009). Theoretical modelling of large shear deformation and wrinkling of plain woven composite. Journal of Composite Materials, 43(2): Zhu B., Yu T.X., Tao X.M. (2007). An experimental study of in-plane large shear deformation of woven fabric composite. Composites Science and Technology, 67:
DRAPING SIMULATION. Recent achievements and future trends. Dr. Sylvain Bel LGCIE University Lyon 1
DRAPING SIMULATION Recent achievements and future trends 1 Dr. Sylvain Bel LGCIE University Lyon 1 2 DRAPING SIMULATION Why? How? What? DRAPING SIMULATION WHY? Clamps Punch Fabric Die 1 2 Resin 3 4 Fig.
More informationA cooperative benchmark effort on testing of woven composites
A cooperative benchmark effort on testing of woven composites J. Cao, H.S. Cheng, T.X. Yu, B. Zhu, X.M. Tao, S.V. Lomov, Tz Stoilova, I. Verpoest, P. Boisse, Jérôme Launay, et al. To cite this version:
More informationBIAS EXTENSION TEST STANDARD
BIAS EXTENSION TEST STANDARD Xiongqi Peng and Jian Cao Advanced Materials Processing Laboratory Department of Mechanical Engineering Northwestern University Evanston, IL August 2003 For Internal Use 1.
More informationModeling non-isothermal thermoforming of fabricreinforced thermoplastic composites
Modeling non-isothermal thermoforming of fabricreinforced thermoplastic composites Dominic Schommer, Miro Duhovic, Joachim Hausmann Institut für Verbundwerkstoffe GmbH, Erwin-Schrödinger-Str., Building
More informationMeasurement of meso-scale deformations for modelling textile composites
CompTest 2004 Measurement of meso-scale deformations for modelling textile composites P Potluri, D A Perez Ciurezu, R Ramgulam Textile Composites Group University of Manchester Institute of Science & Technology
More informationAn overview of Carbon Fiber modeling in LS-DYNA. John Zhao October 23 th 2017
An overview of Carbon Fiber modeling in LS-DYNA John Zhao zhao@lstc.com October 23 th 2017 Outline Manufacturing of Carbon Fiber Compression molding *MAT_277 & 278 *MAT_293 *MAT_249 Resin transform molding
More informationSHEAR TENSION COUPLING IN BIAXIAL BIAS EXTENSION TESTS
SHER TENSION COUPLING IN IXIL IS EXTENSION TESTS P. Harrison *, P. Potluri Department of Mechanical Engineering, James Watt uilding (South), University of Glasgow, Glasgow G 8QQ, U.K. p.harrison@mech.gla.ac.uk
More informationModelling the nonlinear shear stress-strain response of glass fibrereinforced composites. Part II: Model development and finite element simulations
Modelling the nonlinear shear stress-strain response of glass fibrereinforced composites. Part II: Model development and finite element simulations W. Van Paepegem *, I. De Baere and J. Degrieck Ghent
More informationA SELF-INDICATING MODE I INTERLAMINAR TOUGHNESS TEST
A SELF-INDICATING MODE I INTERLAMINAR TOUGHNESS TEST P. Robinson The Composites Centre, Department of Aeronautics, Imperial College London South Kensington, London, SW7 2AZ, UK p.robinson@imperial.ac.uk
More informationTHERMOFORMING SIMULATION OF THERMOPLASTIC TEXTILE COMPOSITES
ECCM6-6 TH EUROPEAN CONFERENCE ON COMPOSITE MATERIALS, Seville, Spain, 22-26 June 204 THERMOFORMING SIMULATION OF THERMOPLASTIC TEXTILE COMPOSITES P. Boisse *, P. Wang, 2, N. Hamila, Laboratoire de Mécanique
More informationFailure analysis of serial pinned joints in composite materials
Indian Journal of Engineering & Materials Sciences Vol. 18, April 2011, pp. 102-110 Failure analysis of serial pinned joints in composite materials Alaattin Aktaş* Department of Mechanical Engineering,
More informationNormalisation Of Shear Test Data For Rate- Independent Compressible Fabrics
Normalisation Of Shear Test Data For Rate- Independent Compressible Fabrics Philip Harrison* 1, Jo Wiggers 2, Andrew C. Long 2 1 University of Glasgow - Room 09 James Watt (South) Building, Materials Engineering
More informationPullout Tests of Geogrids Embedded in Non-cohesive Soil
Archives of Hydro-Engineering and Environmental Mechanics Vol. 51 (2004), No. 2, pp. 135 147 Pullout Tests of Geogrids Embedded in Non-cohesive Soil Angelika Duszyńska, Adam F. Bolt Gdansk University of
More informationFlexural properties of polymers
A2 _EN BUDAPEST UNIVERSITY OF TECHNOLOGY AND ECONOMICS FACULTY OF MECHANICAL ENGINEERING DEPARTMENT OF POLYMER ENGINEERING Flexural properties of polymers BENDING TEST OF CHECK THE VALIDITY OF NOTE ON
More informationLab Exercise #5: Tension and Bending with Strain Gages
Lab Exercise #5: Tension and Bending with Strain Gages Pre-lab assignment: Yes No Goals: 1. To evaluate tension and bending stress models and Hooke s Law. a. σ = Mc/I and σ = P/A 2. To determine material
More informationNUMERICAL MODELLING OF COMPOSITE PIN- JOINTS AND EXPERIMENTAL VALIDATION
NUMERICAL MODELLING OF COMPOSITE PIN- JOINTS AND EXPERIMENTAL VALIDATION Fabrice PIERRON*, François CERISIER*, and Michel GRÉDIAC** * SMS/ Département Mécanique et Matériaux, École Nationale Supérieure
More informationLecture 15 Strain and stress in beams
Spring, 2019 ME 323 Mechanics of Materials Lecture 15 Strain and stress in beams Reading assignment: 6.1 6.2 News: Instructor: Prof. Marcial Gonzalez Last modified: 1/6/19 9:42:38 PM Beam theory (@ ME
More informationA HIGHER-ORDER BEAM THEORY FOR COMPOSITE BOX BEAMS
A HIGHER-ORDER BEAM THEORY FOR COMPOSITE BOX BEAMS A. Kroker, W. Becker TU Darmstadt, Department of Mechanical Engineering, Chair of Structural Mechanics Hochschulstr. 1, D-64289 Darmstadt, Germany kroker@mechanik.tu-darmstadt.de,
More informationNUMERICAL SIMULATION OF DAMAGE IN THERMOPLASTIC COMPOSITE MATERIALS
5 th European LS-DYNA Users Conference Composites NUMERICAL SIMULATION OF DAMAGE IN THERMOPLASTIC COMPOSITE MATERIALS Kevin Brown 1, Richard Brooks, Nicholas Warrior School of Mechanical, Materials and
More informationINVESTIGATION OF THE PROCESSING PARAMETERS OF A 3D WOVEN REINFORCEMENT
INVESTIGATION OF THE PROCESSING PARAMETERS OF A 3D WOVEN REINFORCEMENT Andreas Endruweit, Dhiren K. Modi and Andrew C. Long School of Mechanical, Materials and Manufacturing Engineering, University of
More informationEXPERIMENTAL EVALUATION OF SHEAR STRENGTH OF WOVEN WEBBINGS
EXPERIMENTAL EVALUATION OF SHEAR STRENGTH OF WOVEN WEBBINGS Kevin L. Peil +, Ever J. Barbero +, Eduardo M. Sosa* + Department of Mechanical and Aerospace Engineering, West Virginia University (WVU), Morgantown,
More informationExpansion of circular tubes by rigid tubes as impact energy absorbers: experimental and theoretical investigation
Expansion of circular tubes by rigid tubes as impact energy absorbers: experimental and theoretical investigation M Shakeri, S Salehghaffari and R. Mirzaeifar Department of Mechanical Engineering, Amirkabir
More informationQUESTION BANK Composite Materials
QUESTION BANK Composite Materials 1. Define composite material. 2. What is the need for composite material? 3. Mention important characterits of composite material 4. Give examples for fiber material 5.
More informationLOCKING AND STABILITY OF 3D TEXTILE COMPOSITE REINFORCEMENTS DURING FORMING
10th International Conference on Composite Science and Technology ICCST/10 A.L. Araújo, J.R. Correia, C.M. Mota Soares, et al. (Editors) IDMEC 015 LOCKING AND STABILITY OF 3D TEXTILE COMPOSITE REINFORCEMENTS
More informationFinite element analysis of diagonal tension failure in RC beams
Finite element analysis of diagonal tension failure in RC beams T. Hasegawa Institute of Technology, Shimizu Corporation, Tokyo, Japan ABSTRACT: Finite element analysis of diagonal tension failure in a
More informationA simplified finite element model for draping of woven material
Composites: Part A 35 (2004) 637 643 www.elsevier.com/locate/compositesa A simplified finite element model for draping of woven material S.B. Sharma, M.P.F. Sutcliffe* Department of Engineering, Cambridge
More informationModule III - Macro-mechanics of Lamina. Lecture 23. Macro-Mechanics of Lamina
Module III - Macro-mechanics of Lamina Lecture 23 Macro-Mechanics of Lamina For better understanding of the macromechanics of lamina, the knowledge of the material properties in essential. Therefore, the
More informationWhat make cloth hard to simulate?
Cloth Simulation What make cloth hard to simulate? Due to the thin and flexible nature of cloth, it produces detailed folds and wrinkles, which in turn can lead to complicated selfcollisions. Cloth is
More informationSpecial edition paper
Development of New Aseismatic Structure Using Escalators Kazunori Sasaki* Atsushi Hayashi* Hajime Yoshida** Toru Masuda* Aseismatic reinforcement work is often carried out in parallel with improvement
More informationThis is an author-deposited version published in: Eprints ID: 18486
Open Archive Toulouse Archive Ouverte (OATAO) OATAO is an open access repository that collects the work of Toulouse researchers and makes it freely available over the web where possible. This is an author-deposited
More informationAn Analytical Model for Long Tube Hydroforming in a Square Cross-Section Die Considering Anisotropic Effects of the Material
Journal of Stress Analysis Vol. 1, No. 2, Autumn Winter 2016-17 An Analytical Model for Long Tube Hydroforming in a Square Cross-Section Die Considering Anisotropic Effects of the Material H. Haghighat,
More informationPhysical Properties Testing Technical Bulletin
Technical Bulletin MANUFACTURER Raven Lining Systems 13105 E. 61 st Street, Suite A Broken Arrow, OK 74012 (918) 615-0020 TENSILE TESTING OF PLASTICS ASTM D638, ISO 527 Tensile tests measure the force
More informationRELATIONSHIP BETWEEN RADIAL COMPRESSIVE MODULUS OF ELASTICITY AND SHEAR MODULUS OF WOOD Jen Y. Liu Research Engineer
RELATIONSHIP BETWEEN RADIAL COMPRESSIVE MODULUS OF ELASTICITY AND SHEAR MODULUS OF WOOD Jen Y. Liu Research Engineer and Robert J. Ross Supervisory Research Engineer USDA Forest Service Forest Products
More informationSIMULATION OF THE PREFORMING STEP FOR FLAX DRY WOVEN FABRICS
SIMULATION OF THE PREFORMING STEP FOR FLAX DRY WOVEN FABRICS C. Tephany a*, D. Soulat b, P. Ouagne a, J. Gillibert a a Laboratoire PRISME, Université d Orléans, 8 rue Léonard de Vinci, 45072 Orléans cedex
More informationAnalysis of nonlinear shear deformations in CFRP and GFRP textile laminates
Loughborough University Institutional Repository Analysis of nonlinear shear deformations in CFRP and GFRP textile laminates This item was submitted to Loughborough University's Institutional Repository
More informationMECHANICAL FAILURE OF A COMPOSITE HELICOPTER STRUCTURE UNDER STATIC LOADING
MECHANICAL FAILURE OF A COMPOSITE HELICOPTER STRUCTURE UNDER STATIC LOADING Steven Roy, Larry Lessard Dept. of Mechanical Engineering, McGill University, Montreal, Québec, Canada ABSTRACT The design and
More informationThe bias-extension test for the analysis of in-plane shear properties of textile composite reinforcements and prepregs: a review
The bias-extension test for the analysis of in-plane shear properties of textile composite reinforcements and prepregs: a review P. Boisse, N. Hamila, E. Guzman-Maldonado, A Madeo, G. Hivet, F. Dell Isola
More informationDESIGN AND APPLICATION
III. 3.1 INTRODUCTION. From the foregoing sections on contact theory and material properties we can make a list of what properties an ideal contact material would possess. (1) High electrical conductivity
More information2 Experiment of GFRP bolt
16 TH INTERNATIONAL CONFERENCE ON COMPOSITE MATERIALS FATIGUE LIFE EVALUATION OF BOLT MADE OF WOVEN FABRIC FRP Takeshi INOUE*, Hiroaki NAKAI**, Tetsusei KURASHIKI**, Masaru ZAKO**, Yuji KOMETANI*** *Graduate
More informationModelling of ductile failure in metal forming
Modelling of ductile failure in metal forming H.H. Wisselink, J. Huetink Materials Innovation Institute (M2i) / University of Twente, Enschede, The Netherlands Summary: Damage and fracture are important
More information5. STRESS CONCENTRATIONS. and strains in shafts apply only to solid and hollow circular shafts while they are in the
5. STRESS CONCENTRATIONS So far in this thesis, most of the formulas we have seen to calculate the stresses and strains in shafts apply only to solid and hollow circular shafts while they are in the elastic
More informationA Novel Approach for Measurement of Fiber-on-fiber Friction
F98S-09 Page 1 A Novel Approach for Measurement of Fiber-on-fiber Friction Number: F98S-09 Competency: Fabrication Team Leader and members: Y. Qiu, NCSU; Y. Wang, Georgia Tech; J.Z. Mi, Cotton Inc. Graduate
More informationUniversity of Sheffield The development of finite elements for 3D structural analysis in fire
The development of finite elements for 3D structural analysis in fire Chaoming Yu, I. W. Burgess, Z. Huang, R. J. Plank Department of Civil and Structural Engineering StiFF 05/09/2006 3D composite structures
More informationMechanical Behavior of Circular Composite Springs with Extended Flat Contact Surfaces
Mechanical Behavior of Circular Composite Springs with Extended Flat Contact Surfaces Ping-Cheung Tse epartment of Mechanical Engineering, The Hong Kong Polytechnic University, Hunghom, Kowloon, Hong Kong
More informationNon-conventional Glass fiber NCF composites with thermoset and thermoplastic matrices. F Talence, France Le Cheylard, France
20 th International Conference on Composite Materials Copenhagen, 19-24th July 2015 Non-conventional Glass fiber NCF composites with thermoset and thermoplastic matrices. Thierry Lorriot 1, Jalal El Yagoubi
More informationInterface properties between a steel pre-stressing strand and an epoxy matrix.
Interface properties between a steel pre-stressing strand and an epoxy matrix. J. Van Vooren 1, B. Van Vooren 2, D. Van Hemelrijck 1, 1 Free University of Brussel, Dept. of Mechanics of Materials and Constructions,
More informationExperimental Research on the Shear Behavior of Laminated Glass with PVB Film Under Different Temperature
2017 Asia-Pacific Engineering and Technology Conference (APETC 2017) ISBN: 978-1-60595-443-1 Experimental Research on the Shear Behavior of Laminated Glass with PVB Film Under Different Temperature Qing
More informationPlane Strain Test for Metal Sheet Characterization
Plane Strain Test for Metal Sheet Characterization Paulo Flores 1, Felix Bonnet 2 and Anne-Marie Habraken 3 1 DIM, University of Concepción, Edmundo Larenas 270, Concepción, Chile 2 ENS - Cachan, Avenue
More informationPURE BENDING. If a simply supported beam carries two point loads of 10 kn as shown in the following figure, pure bending occurs at segment BC.
BENDING STRESS The effect of a bending moment applied to a cross-section of a beam is to induce a state of stress across that section. These stresses are known as bending stresses and they act normally
More informationINFLUENCE KINDS OF MATERIALS ON THE POISSON S RATIO OF WOVEN FABRICS
ISSN 1846-6168 (Print), ISSN 1848-5588 (Online) ID: TG-217816142553 Original scientific paper INFLUENCE KINDS OF MATERIALS ON THE POISSON S RATIO OF WOVEN FABRICS Željko PENAVA, Diana ŠIMIĆ PENAVA, Željko
More informationFibre Friction WHAT IS FIBRE
Fibre Friction WHAT IS FIBRE Fibre is a class of materials that are continuous filaments. Any thing having high length to width ratio. Diameter or width of fibre is negligible which cant be measured. Fibres
More informationPrediction of fabric hand characteristics using extraction principle
Indian Journal of Fibre & Textile Research Vol. 41, March 2016, pp. 33-39 Prediction of fabric hand characteristics using extraction principle Apurba Das a, Abhijit Majumdar & Sukumar Roy Department of
More informationCOMPOSITE REINFORCEMENT FORMING SIMULATION: A MULTISCALE APPROACH
COMPOSITE REINFORCEMENT FORMING SIMULATION: A MULTISCALE APPROACH N. Hamila A. Khan S. Gatouillat E. De Luycker E. Vidal-Sallé T. Mabrouki P. Boisse Université de Lyon, LaMCoS, INSA-Lyon Philippe.Boisse@insa-lyon.fr
More informationSlow Velocity Flow Fields in Composite Materials
Slow Velocity Flow Fields in Composite Materials A Coupled Problem by the Homogenization Method Noboru Kikuchi and His Associates The University of Michigan Ann Arbor, MI 48109, USA Major Contributors
More informationPREDICTION OF OUT-OF-PLANE FAILURE MODES IN CFRP
PREDICTION OF OUT-OF-PLANE FAILURE MODES IN CFRP R. R. Pinto 1, P. P. Camanho 2 1 INEGI - Instituto de Engenharia Mecanica e Gestao Industrial, Rua Dr. Roberto Frias, 4200-465, Porto, Portugal 2 DEMec,
More informationCrashworthiness of composite structures: Experiment and Simulation
Crashworthiness of composite structures: Experiment and Simulation Francesco Deleo, Bonnie Wade and Prof. Paolo Feraboli (UW) Dr. Mostafa Rassaian (Boeing R&T) JAMS 2010 The Joint Advanced Materials and
More informationMECHANICS OF MATERIALS. Prepared by Engr. John Paul Timola
MECHANICS OF MATERIALS Prepared by Engr. John Paul Timola Mechanics of materials branch of mechanics that studies the internal effects of stress and strain in a solid body. stress is associated with the
More informationPrediction of static response of Laced Steel-Concrete Composite beam using effective moment of inertia approach
Prediction of static response of Laced Steel-Concrete Composite beam using effective moment of inertia approach Thirumalaiselvi A 1, 2, Anandavalli N 1,2, Rajasankar J 1,2, Nagesh R. Iyer 2 1 Academy of
More informationASPECTS CONCERNING TO THE MECHANICAL PROPERTIES OF THE GLASS / FLAX / EPOXY COMPOSITE MATERIAL
5 th International Conference Advanced Composite Materials Engineering COMAT 2014 16-17 October 2014, Braşov, Romania ASPECTS CONCERNING TO THE MECHANICAL PROPERTIES OF THE GLASS / FLAX / EPOXY COMPOSITE
More informationSCALING EFFECTS IN THE LOW VELOCITY IMPACT RESPONSE OF FIBRE METAL
SCALING EFFECTS IN THE LOW VELOCITY IMPACT RESPONSE OF FIBRE METAL LAMINATES J. G. Carrillo 1, S. McKown 1, M. Mujib 1 and W. J. Cantwell 1. R. Day 2 1 Department of Engineering, University of Liverpool,
More informationNonlinearities in mechanical behavior of textile composites
Composite Structures 71 (25) 61 67 www.elsevier.com/locate/compstruct Nonlinearities in mechanical behavior of textile composites Enrico DÕAmato Energetics Departement, L Aquila University, 674 Monteluco
More informationPrediction of Elastic Constants on 3D Four-directional Braided
Prediction of Elastic Constants on 3D Four-directional Braided Composites Prediction of Elastic Constants on 3D Four-directional Braided Composites Liang Dao Zhou 1,2,* and Zhuo Zhuang 1 1 School of Aerospace,
More informationD : SOLID MECHANICS. Q. 1 Q. 9 carry one mark each. Q.1 Find the force (in kn) in the member BH of the truss shown.
D : SOLID MECHANICS Q. 1 Q. 9 carry one mark each. Q.1 Find the force (in kn) in the member BH of the truss shown. Q.2 Consider the forces of magnitude F acting on the sides of the regular hexagon having
More informationMODELING OF THE BEHAVIOR OF WOVEN LAMINATED COMPOSITES UNTIL RUPTURE
MODELING OF THE BEHAVIOR OF WOVEN LAMINATED COMPOSITES UNTIL RUPTURE Jean Paul Charles, Christian Hochard,3, Pierre Antoine Aubourg,3 Eurocopter, 375 Marignane cedex, France Unimeca, 6 rue J. Curie, 3453
More informationFCP Short Course. Ductile and Brittle Fracture. Stephen D. Downing. Mechanical Science and Engineering
FCP Short Course Ductile and Brittle Fracture Stephen D. Downing Mechanical Science and Engineering 001-015 University of Illinois Board of Trustees, All Rights Reserved Agenda Limit theorems Plane Stress
More informationMODELLING OF DRAPING AND DEFORMATION FOR TEXTILE COMPOSITES
MODELLING OF DRAPING AND DEFORMATION FOR TEXTILE COMPOSITES A. C. Long, M. J. Clifford, P. Harrison, C. D. Rudd School of Mechanical, Materials, Manufacturing Engineering and Management University of Nottingham,
More informationMechanics of Materials
Mechanics of Materials 2. Introduction Dr. Rami Zakaria References: 1. Engineering Mechanics: Statics, R.C. Hibbeler, 12 th ed, Pearson 2. Mechanics of Materials: R.C. Hibbeler, 9 th ed, Pearson 3. Mechanics
More informationIraq Ref. & Air. Cond. Dept/ Technical College / Kirkuk
International Journal of Scientific & Engineering Research, Volume 6, Issue 4, April-015 1678 Study the Increasing of the Cantilever Plate Stiffness by Using s Jawdat Ali Yakoob Iesam Jondi Hasan Ass.
More informationPRELIMINARY PREDICTION OF SPECIMEN PROPERTIES CLT and 1 st order FEM analyses
OPTIMAT BLADES Page 1 of 24 PRELIMINARY PREDICTION OF SPECIMEN PROPERTIES CLT and 1 st order FEM analyses first issue Peter Joosse CHANGE RECORD Issue/revision date pages Summary of changes draft 24-10-02
More informationFRICTION TESTING OF THERMOPLASTIC COMPOSITES
FRICTION TESTING OF THERMOPLASTIC COMPOSITES ULRICH SACHS MSc (a), SEBASTIAAN HAANAPPEL MSc (a), Dr. BERT RIETMAN (b) and Prof. REMKO AKKERMAN (a),(b) a) TPRC, University of Twente, Drienerlolaan 5, P.O.
More informationMULTI-SCALE MODELLING OF FIBRE BUNDLES
THE 19 TH INTERNATIONAL CONFERENCE ON COMPOSITE MATERIALS MULTI-SCALE MODELLING OF FIBRE BUNDLES N. D. Chakladar 1, P. Mandal 1 *, P. Potluri 2 1 School of Mechanical, Aerospace and Civil Engineering,
More informationMODELING THE FIBER SLIPPAGE DURING PREFORMING OF WOVEN FABRICS
MODELING THE FIBER SLIPPAGE DURING PREFORMING OF WOVEN FABRICS Chyi-Lang Lai and Wen-Bin Young * Department of Aeronautics and Astronautics National Cheng-Kung University Tainan, Taiwan 70101, ROC SUMMARY:
More informationInternational Conference on Mechanics and Civil Engineering (ICMCE 2014)
International Conference on Mechanics and Civil Engineering (ICMCE 2014) Parametric Design and Experimental Study for Weak Area Structure of Circle Composite Fragile Cover Ran CAO 1,a, Guang-Ming ZHOU
More informationAn integrated approach to the design of high performance carbon fibre reinforced risers - from micro to macro - scale
An integrated approach to the design of high performance carbon fibre reinforced risers - from micro to macro - scale Angelos Mintzas 1, Steve Hatton 1, Sarinova Simandjuntak 2, Andrew Little 2, Zhongyi
More informationHIGHLY ADAPTABLE RUBBER ISOLATION SYSTEMS
th World Conference on Earthquake Engineering Vancouver, B.C., Canada August -6, 24 Paper No. 746 HIGHLY ADAPTABLE RUBBER ISOLATION SYSTEMS Luis DORFMANN, Maria Gabriella CASTELLANO 2, Stefan L. BURTSCHER,
More informationStatic and Time Dependent Failure of Fibre Reinforced Elastomeric Components. Salim Mirza Element Materials Technology Hitchin, UK
Static and Time Dependent Failure of Fibre Reinforced Elastomeric Components Salim Mirza Element Materials Technology Hitchin, UK Introduction Fibre reinforced elastomers are used in many applications,
More informationD : SOLID MECHANICS. Q. 1 Q. 9 carry one mark each.
GTE 2016 Q. 1 Q. 9 carry one mark each. D : SOLID MECHNICS Q.1 single degree of freedom vibrating system has mass of 5 kg, stiffness of 500 N/m and damping coefficient of 100 N-s/m. To make the system
More informationReview Lecture. AE1108-II: Aerospace Mechanics of Materials. Dr. Calvin Rans Dr. Sofia Teixeira De Freitas
Review Lecture AE1108-II: Aerospace Mechanics of Materials Dr. Calvin Rans Dr. Sofia Teixeira De Freitas Aerospace Structures & Materials Faculty of Aerospace Engineering Analysis of an Engineering System
More information3. BEAMS: STRAIN, STRESS, DEFLECTIONS
3. BEAMS: STRAIN, STRESS, DEFLECTIONS The beam, or flexural member, is frequently encountered in structures and machines, and its elementary stress analysis constitutes one of the more interesting facets
More informationWrinkling Analysis of A Kapton Square Membrane under Tensile Loading
44th AIAA/ASME/ASCE/AHS Structures, Structural Dynamics, and Materials Confere 7-10 April 2003, Norfolk, Virginia AIAA 2003-1985 Wrinkling Analysis of A Kapton Square Membrane under Tensile Loading Xiaofeng
More informationHIGH VELOCITY IMPACT ON TEXTILE REINFORCED COMPOSITES
16 TH INTERNATIONAL CONFERENCE ON COMPOSITE MATERIALS HIGH VELOCITY IMPACT ON TEXTILE REINFORCED COMPOSITES Warnet L., Akkerman R., Ravensberg M. University of Twente, Faculty of Engineering Technology,
More informationThe Local Web Buckling Strength of Coped Steel I-Beam. ABSTRACT : When a beam flange is coped to allow clearance at the
The Local Web Buckling Strength of Coped Steel I-Beam Michael C. H. Yam 1 Member, ASCE Angus C. C. Lam Associate Member, ASCE, V. P. IU and J. J. R. Cheng 3 Members, ASCE ABSTRACT : When a beam flange
More informationNUMERICAL AND EXPERIMENTAL STUDY OF FAILURE IN STEEL BEAMS UNDER IMPACT CONDITIONS
Blucher Mechanical Engineering Proceedings May 2014, vol. 1, num. 1 www.proceedings.blucher.com.br/evento/10wccm NUMERICAL AND EXPERIMENTAL STUDY OF FAILURE IN STEEL BEAMS UNDER IMPACT CONDITIONS E. D.
More informationOpen-hole compressive strength prediction of CFRP composite laminates
Open-hole compressive strength prediction of CFRP composite laminates O. İnal 1, A. Ataş 2,* 1 Department of Mechanical Engineering, Balikesir University, Balikesir, 10145, Turkey, inal@balikesir.edu.tr
More informationDEFLECTION OF BEAMS WlTH SPECIAL REFERENCE TO SHEAR DEFORMATIONS
DEFLECTION OF BEAMS WlTH SPECIAL REFERENCE TO SHEAR DEFORMATIONS THE INFLUENCE OF THE FORM OF A WOODEN BEAM ON ITS STIFFNESS AND STRENGTH-I (REPRINT FROM NATIONAL ADVISORY COMMITTEE FOR AERONAUTICS REPORT
More informationAnalysis of parameters influencing the jamming effect in circular braids
This paper is part of the Proceedings of the 2 International Conference on nd High Performance and Optimum Design of Structures and Materials (HPSM 2016) www.witconferences.com Analysis of parameters influencing
More informationINDUSTRIAL FORMING SIMULATION OF MULTI-LAYERED UD NON-CRIMP-FABRICS. 13. LS-DYNA FORUM, , BAMBERG.
Sebastian Kreissl, Thomas Senner, Arnulf Lipp, Josef Meinhardt. INDUSTRIAL FORMING SIMULATION OF MULTI-LAYERED UD NON-CRIMP-FABRICS. 13. LS-DYNA FORUM, 07.10.2014, BAMBERG. OUTLINE. BMW i. Production Process
More informationANALYSIS OF WOVEN REINFORCEMENT PREFORMING USING AN EXPERIMENTAL APPROACH
ANALYSIS OF WOVEN REINFORCEMENT PREFORMING USING AN EXPERIMENTAL APPROACH G. Hivet 1, S. Allaoui 1, D. Soulat 1, A. Wendling 1, S. Chatel 2 1 Institut PRISME/MMH, Université d Orléans, 8 rue Léonard de
More information7.4 The Elementary Beam Theory
7.4 The Elementary Beam Theory In this section, problems involving long and slender beams are addressed. s with pressure vessels, the geometry of the beam, and the specific type of loading which will be
More informationMaterials and Structures. Indian Institute of Technology Kanpur
Introduction to Composite Materials and Structures Nachiketa Tiwari Indian Institute of Technology Kanpur Lecture 16 Behavior of Unidirectional Composites Lecture Overview Mt Material ilaxes in unidirectional
More informationCalculation of Damage-dependent Directional Failure Indices from the Tsai-Wu Static Failure Criterion
Van Paepegem, W. and Degrieck, J. (3. alculation of Damage-dependent Directional Failure Indices from the sai-wu Static Failure riterion. omposites Science and echnology, 63(, 35-3. alculation of Damage-dependent
More informationComputational Analysis for Composites
Computational Analysis for Composites Professor Johann Sienz and Dr. Tony Murmu Swansea University July, 011 The topics covered include: OUTLINE Overview of composites and their applications Micromechanics
More informationNORMAL STRESS. The simplest form of stress is normal stress/direct stress, which is the stress perpendicular to the surface on which it acts.
NORMAL STRESS The simplest form of stress is normal stress/direct stress, which is the stress perpendicular to the surface on which it acts. σ = force/area = P/A where σ = the normal stress P = the centric
More informationEXPERIMENTAL AND NUMERICAL STUDY OF THE ENERGY ABSORPTION CAPACITY OF PULTRUDED COMPOSITE TUBES
EXPERIMENTAL AND NUMERICAL STUDY OF THE ENERGY ABSORPTION CAPACITY OF PULTRUDED COMPOSITE TUBES D. Kakogiannis 1, D. Van Hemelrijck 1, J. Wastiels 1, S. Palanivelu 2, W. Van Paepegem 2, K. De Wolf 3, J.
More informationTENSILE TESTS (ASTM D 638, ISO
MODULE 4 The mechanical properties, among all the properties of plastic materials, are often the most important properties because virtually all service conditions and the majority of end-use applications
More informationDAMAGE MECHANICS MODEL FOR OFF-AXIS FATIGUE BEHAVIOR OF UNIDIRECTIONAL CARBON FIBER-REINFORCED COMPOSITES AT ROOM AND HIGH TEMPERATURES
DAMAGE MECHANICS MODEL FOR OFF-AXIS FATIGUE BEHAVIOR OF UNIDIRECTIONAL CARBON FIBER-REINFORCED COMPOSITES AT ROOM AND HIGH TEMPERATURES M. Kawai Institute of Engineering Mechanics University of Tsukuba,
More informationAn Analytical Study of Initial Shear Behavior of Plain Woven Hybrid Fabrics
JOURNAL OF TEXTILES AND POLYMERS, VOL. 4, NO., JANUARY 206 9 An Analytical Study of Initial Shear Behavior of Plain Woven Hybrid Fabrics Majid Tehrani-Dehkor and Hooshang Nosraty Abstract During recent
More informationME 2570 MECHANICS OF MATERIALS
ME 2570 MECHANICS OF MATERIALS Chapter III. Mechanical Properties of Materials 1 Tension and Compression Test The strength of a material depends on its ability to sustain a load without undue deformation
More informationA study of forming pressure in the tube-hydroforming process
Journal of Materials Processing Technology 192 19 (2007) 404 409 A study of forming pressure in the tube-hydroforming process Fuh-Kuo Chen, Shao-Jun Wang, Ray-Hau Lin Department of Mechanical Engineering,
More informationEVALUATION OF DAMAGE DEVELOPMENT FOR NCF COMPOSITES WITH A CIRCULAR HOLE BASED ON MULTI-SCALE ANALYSIS
THE 19 TH INTERNATIONAL CONFERENCE ON COMPOSITE MATERIALS EVALUATION OF DAMAGE DEVELOPMENT FOR NCF COMPOSITES WITH A CIRCULAR HOLE BASED ON MULTI-SCALE ANALYSIS T. Kurashiki 1 *, Y. Matsushima 1, Y. Nakayasu
More information