Electronic Supporting Information. Integrated Photon Upconversion Solar Cell via Molecular Self-Assembled Bilayers

Transcription

1 Electronic Supporting Information Integrated Photon Upconversion Solar Cell via Molecular Self-Assembled Bilayers Sean P. Hill, Tristan Dilbeck, Enric Baduell, Kenneth Hanson* Department of Chemistry and Biochemistry, Florida State University, Tallahassee, Florida, 3236, United States Contents 1. Materials and Dye Synthesis...Page S2 2. Photophysical and Electrochemical Measurements...Page S Table S1. Device performance...page S5 4. Figure S1. Current density-voltage response curves...page S6 5. Figure S2. Decay and recovery of DPPA on ZrO 2...Page S6 6. Figure S3. IPCE for TiO 2 -DPPA-Zn-PtTCPP...Page S7 7. Figure S4. IPCE for TiO 2 -DPPA...Page S7 8. Figure S5. IPCE for TiO 2 -PtTCPP...Page S8 9. Figure S6. Absorption spectra for PtTCPP loading overtime in a bilayer film..page S8 1. Figure S7. Emission spectra for ZrO 2 -PtTCPP and bilayer films...page S9 11. Figure S8. Emission spectra for ZrO 2 -(3)+PtTPP and ZrO 2 -DPPA+PtTPP...Page S9 12. Figure S9. Emission spectra for bilayer films with and w/out [Co(bpy) 3 ] 2+/3+...Page S1 13. Table S2. Photophysical properties of PtTPP and PtTCPP...Page S1 14. References...Page S11 S1

2 a. Materials and Dye Synthesis Materials: Zinc acetate dehydrate, H 2 PtCl 6, nitrosyl tetrafluoroborate, cobalt (II) chloride, ammonium hexafluorophosphate (Sigma-Aldrich), 2,2 bipyridine (Oxchem), Pt(II) meso-tetraphenylporphine, and Pt(II) meso-tetra(4-carboxyphenyl)porphine (Frontier Scientific), were purchased from their respective suppliers, in parentheses, and used as received. All other reagents and solvents (analytical reagent grade) have been purchased and used without further purification from Alfa Aesar. Fluorine-doped tin oxide (FTO) coated glass (sheet resistance 15 Ω -1 ) was purchased from Hartford Glass Co. Meltonix film (117-25), Ti-Nanoxide T solgel paste (11421) and Vac n Fill Syringe (6529) were purchased from Solaronix. Micro glass cover slides (18 18 mm) were obtained from VWR. ZrO 2 solgel paste was prepared following a previously reported procedure. 1 Dye Synthesis: 4,4 -(Anthracene-9,1-diyl)bis(4,1-phenylene) diphosphonic acid (DPPA) 2 and Tris-(2,2 -bipyridine)cobalt(ii) di(hexafluorophosphate) (Co(bpy) 3 (PF 6 ) 2 ) 3 were prepared by following previously published procedures. b. Photophysical and Electrochemical Measurements Energy Transfer Measurements: The efficiency of PtTPP or PtTCPP to DPPA energy transfer for ZrO 2 -DPPA-Zn-PtTCPP and ZrO 2 -DPPA with PtTPP in solution, respectively, was quantified using steady state emission experiments. The sensitizer was excited 51 nm light from a Xe lamp and emission was measured from 6-8 nm. Phosphorescence quenching was calculated using equation S1 where I SA is the integrated emission intensity from 6-8 nm for ZrO 2 -DPPA-Zn-PtTCPP or ZrO 2 -DPPA with S2

3 PtTPP in solution, and I S is the emission intensity for ZrO 2 -PtTCPP or ZrO 2 -(3) with PtTPP in solution. % Quenching = (1 I SA I S ) 1 (Eq. S1) For the heterogeneous PtTPP only sample, the surface of ZrO 2 was functionalized with P, P'-Terphenyl-4,4''-bis-phosphonic acid (3) which is a photo- and electrochemically inert surrogate for DPPA. 4 The addition of (3) was found to be necessary to prevent PtTPP aggregation on the surface of ZrO 2, which lead to quenching of the phosphorescence in the ZrO 2 with PtTPP samples. Incident Photon to Current Efficiency: IPCE was acquired every 5 nm (5 nm bandwidth) with excitation intensities measured at each wavelength (I ex ) to correct for variation throughout the spectrum. % IPCE was calculated using Equation S2. % IPCE = (J sc)(124) (I ex )(λ) (Eq. S2) Absorption Spectra: Data were recorded on an Agilent 8453 UV visible photo diode array spectrophotometer. Thin film absorption spectra were obtained by placing dry, derivatized TiO 2 and ZrO 2 slides perpendicular to the detection beam path. Steady-State Emission: Data were collected at room temperature using an Edinburgh FLS98 fluorescence spectrometer. The samples were excited using the output from either a housed 45 W Xe lamp/single grating (18 λ mm -1, 25 nm blaze) Czerny Turner monochromator or a Nd:YAG laser (Aixiz, AD-532-4T). The output from the Nd:YAG laser was passed through a variable neutral density filter (Edinburgh S3

4 F-B1 laser mount), a 2 mm diameter iris (Newport ID-1.) and then directed to the sample via a flip mirror. Emission from the sample was first passed through a long pass filter or a 532 nm notch filter (Thorlabs Inc., NF533-17), then a single grating (18 λ mm -1, 5 nm blaze) Czerny Turner monochromator and finally detected by a Peltiercooled Hamamatsu R928 photomultiplier tube. Laser intensities were measured using a power meter (Ophir Vega, 7Z156) with a high sensitivity power sensor (Ophir, 3A-FS 7Z2628). Time-Resolved Emission: The excited state lifetimes for PtTCPP in the bilayer on ZrO 2 and PtTPP in the presence of ZrO 2 -DPPA were acquired using the FLS98 s multichannel scaling (MCS) acquisition mode with 51 nm excitation from a 6 W microsecond flashlamp (pulse width < 2.5 µs) at a 1 Hz repetition rate. Emission was passed through a 57 nm long pass filter placed in front of the detector. Decay traces were fit using the Edinburgh software package. Amperometric i t. Data were collected using a CH Instruments CHI63E electrochemical analyzer using a two-electrode configuration (TiO 2 working, Pt counter) held at V applied potential. The samples were irradiated with either an AM1.5 solar simulator (Light Model oriel corrected with a standard air-mass filter) passing through a 375 nm or 495 nm long pass filters, with 532 nm from a Nd:YAG laser (Aixiz, AD-532-4T) or with 366 nm LED (ThorLabs M365L2-UV) used as the light source. The intensity of solar irradiance was controlled by varying the distance between the solar simulator source and sample. The laser light intensity was controlled using a neutral S4

5 density filter as described above for the photophysical measurements. A Model T132 Shutter Driver/Timer (UniBlitz) coupled to a mechanical shutter (Vincent Associates, VS25) was placed between the light source and sample to control 1 s light-dark intervals over a 7 s time period. Table S1. Performance characteristics of DSSCs containing monolayer and bilayer photoanodes under AM1.5 irradiation with 375nm and 495 nm long pass filters. Filter [nm] J sc [µa/cm 2 ] V oc [mv] η DPPA PtTCPP Bilayer DPPA PtTCPP Bilayer S5

6 Current Density (µa cm -2 ) 24 TiO 2 -DPPA TiO PtTCPP TiO 2 -DPPA-Zn-PtTCPP Voltage (mv) Figure S1. Current density-voltage response curves for TiO 2 -DPPA, TiO 2 -PtTCPP, and TiO 2 -DPPA-Zn-PtTCPP with [Co(bpy) 3 ] 2+/3+ inmecn under 1 sun (AM1.5) illumination with a 375 nm long pass filter. Absorbance ZrO 2 -DPPA 4.5 hr irradiation 2.5 hr heating Figure S2. Absorbance spectra for DPPA loaded onto ZrO 2 (black, square) after irradiation under white light for 4.5 hr (red, circle) followed by 2.5 hr heating at 7 C (blue, triangle). S6

7 IPCE (%) IPCE Absorptance Absorptance (%) Figure S3. IPCE (blue, square) and absorptance (red, circle) for TiO 2 -DPPA-Zn-PtTCPP with [Co(bpy) 3 ] 2+/3+ in MeCN. IPCE (%) IPCE Absorptance Absorptance (%) Figure S4. IPCE (blue, square) and absorptance (red, circle) for TiO 2 -DPPA with [Co(bpy) 3 ] 2+/3+ in MeCN. S7

8 IPCE (%) IPCE Absorptance Absorptance (%) Figure S5. IPCE (blue, square) and absorptance (red, circle) for TiO 2 -PtTCPP with [Co(bpy) 3 ] 2+/3+ in MeCN. a) 1.4 b) 1.4 Absorbance PtTCPP 1 min PtTCPP 2 min PtTCPP 3 min PtTCPP 4 min PtTCPP 6 min Normalized Absorbance PtTCPP 1 min PtTCPP 2 min PtTCPP 3 min PtTCPP 4 min PtTCPP 6 min Figure S6. Absorption spectra of ZrO 2 -DPPA-Zn-PtTCPP after soaking in 2 µm PtTCPP in DMSO for 1, 2 3, 4 and 6 minutes (a) as recorded and (b) normalized at 512 nm. S8

9 Intensity (counts) 1.2x1 5 1.x1 5 8.x1 4 6.x1 4 4.x1 4 2.x1 4 ZrO 2 -PtTCPP ZrO 2 -DPPA-Zn-PtTCPP Figure S7. Emission from ZrO 2 -PtTCPP (black) and ZrO 2 -DPPA-Zn-PtTCPP (red) in DMF under 51 nm excitation (57 nm long pass filter). Intensity (counts) 1.2x1 5 1.x1 5 8.x1 4 6.x1 4 4.x1 4 2.x1 4 ZrO 2 -(3) + PtTPP ZrO 2 -DPPA + PtTPP Figure S8. Emission from ZrO 2 -(3) + PtTPP (black) and ZrO 2 -DPPA + PtTPP (red) in DMF under 51 nm excitation (57 nm long pass filter). S9

10 Intensity (counts) 1.2x1 5 1.x1 5 8.x1 4 6.x1 4 4.x1 4 2.x1 4 Without [Co(bpy) 3 ] 2+/3+ With [Co(bpy) 3 ] 2+/ Figure S9. Emission from ZrO 2 -DPPA-Zn-PtTCPP without (black) and with (red) [Co(bpy) 3 ] 2+/3+ in MeCN under 532 nm laser excitation (532 nm notch filter). Table S2. Photophysical properties of PtTPP and PtTCPP. λ abs a [nm] [ε, 1 4 M -1 cm -1 ] λ em [nm] τ b [µs] Φ k r c [ 1 2 s -1 ] k nr d [ 1 4 s -1 ] E 1/2 ox [V vs NHE] E 1/2 (S 1 ) e E 1/2 (T 1 ) f PtTPP PtTCPP 41 (27.46), 59 (2.72), 539 (.73) 43 (27.55), 51 (2.9), 539 (.77) a Measured in a DMF solution at each peak maxima. b Lifetime from an exponential tail fit to the excited state decay (ex: 51 nm). c k r = Φ/τ. d k nr = (1-Φ)/τ. e The singlet excited state reduction potential. f The triplet excited state reduction potential. S1

11 References: (1) Heimer, T. A.; DArcangelis, S. T.; Farzad, F.; Stipkala, J. M.; Meyer, G. J. An Acetylacetonate-Based Semiconductor Sensitizer Linkage. Inorg. Chem. 1996, 35, (2) Hill, S. P.; Banerjee, T.; Dilbeck, T.; Hanson, K. Photon Upconversion and Photocurrent Generation via Self-Assembly at Organic-Inorganic Interfaces. J. Phys. Chem. Lett. 215, 6, 451. (3) Feldt, S. M.; Gibson, E. A.; Gabrielsson, E.; Sun, L.; Boschloo, G.; Hagfeldt, A. Design of Organic Dyes and Cobalt Polypyridine Redox Mediators for High- Efficiency Dye-Sensitized Solar Cells. J. Am. Chem. Soc. 21, 132, (4) Wang, J. C.; Murphy, I. A.; Hanson, K. Modulating Electron Transfer Dynamics at Dye Semiconductor Interfaces via Self-Assembled Bilayers. J. Phys. Chem. C 215, 119, 352. S11