Effects of TiO 2 and Nb 2 O 5 on Hydrogen Desorption of Mg(BH 4 ) 2

Similar documents
CYCLIC ADSORPTION AND DESORPTION OF METHANE AND CARBON DIOXIDE ON COCONUT SHELL ACTIVATED CARBON

MODIFIED LITHIUM BOROHYDRIDE FOR MOBILE HYDROGEN STORAGE

IV.D.2 Hydrogen Storage Materials for Fuel Cell-Powered Vehicles

Hydrogen desorption properties of Ca-N-H system

EXECUTIVE SUMMARY. especially in last 50 years. Industries, especially power industry, are the large anthropogenic

Thermodynamic and Kinetic Destabilization in LiBH 4 /Mg 2 NiH 4 : Promise for Borohydride-Based Hydrogen Storage

Direct Line-of-site Gas Desorption Study of LiBH 4 in Nanoporous Carbons: The Size Effect

Composite Materials based on Light Elements for Hydrogen Storage

Comparison of the Hydrogen Release Properties of Zn(BH 4 ) 2 -Added MgH 2 Alloy and Zn(BH 4 ) 2 and Ni-Added MgH 2 Alloy

Yiping Zhao and Yuping He

Report on Deliverable D 5.5

High-Pressure Volumetric Analyzer

PREPARATION OF NITROGEN ENRICHED HIERARCHICALLY NANOPOROUS CARBON FROM POLYBENZOXAZINE FOR METHANE STORAGE

Aluminum Chloride as effective dopant in Amide-based systems

Strategic use of CuAlO 2 as a sustained release catalyst for production of hydrogen from methanol steam reforming

Nanostructured complex hydride systems. for solid state hydrogen storage

Supplementary Information

Competitive Adsorption of Methane and Carbon Dioxide on Different Activated Carbons

Calorimetry. Chapter 2. Differential Scanning heat flux calorimetry

UPGRADING OF PETROLEUM RESIDUE BY NITROGEN DOPING FOR CO 2 ADSORPTION

A flexible MMOF exhibiting high selectivity for CO 2 over N 2, CH 4 and other small gases. Supporting Information

DFT modeling of novel materials for hydrogen storage

NanoEngineering of Hybrid Carbon Nanotube Metal Composite Materials for Hydrogen Storage Anders Nilsson

Synthesis of nano-sized anatase TiO 2 with reactive {001} facets using lamellar protonated titanate as precursor

Room Temperature Hydrogen Generation from Hydrous Hydrazine for Chemical Hydrogen Storage

Gavin Walker, David Grant, Tobias Price, Xuebin Yu, Vincent Legrand. HAL Id: hal

A COMPARISON OF CONVENTIONAL HEATING TECHNIQUES AND MICROWAVE IRRADIATION FOR THE DESORPTION OF LITHIUM BOROHYDRIDE AND LITHIUM BOROHYDRIDE COMPOSITES

Keywords: Adsorption; Carbon nanotubes; Desorption; Dynamics of adsorption and desorption; Hydrogen

Supporting Information

Supporting Information High Activity and Selectivity of Ag/SiO 2 Catalyst for Hydrogenation of Dimethyloxalate

Supplementary Information for

Dry-gel conversion synthesis of Cr-MIL-101 aided by grinding: High surface area high yield synthesis with minimum purification

ADSORPTION AND DESORPTION OF CO ON SOLID SORBENTS

Nobuko Hanada*, Takayuki Ichikawa, Hironobu Fujii. Graduate School of Advanced Sciences of Matter, Hiroshima University,

NMR and X-ray Diffraction Studies of Phases in the Destabilized LiH-Si System

1.1. Storage of hydrogen

Studies on Mo/HZSM-5 Complex catalyst for Methane Aromatization

Dehydrogenation properties of the LiNH 2 BH 3 /MgH 2 and LiNH 2 BH 3 / LiBH 4 bi component hydride systems for hydrogen storage applications

Supporting information A Porous Zr-cluster-based Cationic Metal-Organic Framework for Highly Efficient Cr 2 O 7

Supplementary Information. ZIF-8 Immobilized Ni(0) Nanoparticles: Highly Effective Catalysts for Hydrogen Generation from Hydrolysis of Ammonia Borane

C80. Calvet Calorimeter From ambient to 300 C. A trademark of KEP Technologies group

Experimental analysis of removal of SO 2 and NOx for nano Mg-Al composite oxides

Properties of a New Type of Plaster Containing Phase-Change Material

RSC Advances.

Experimental Methods and Analysis

Clean synthesis of propylene carbonate from urea and 1,2-propylene glycol over zinc iron double oxide catalyst

Characterization and High Throughput Analysis of Metal Hydrides for Hydrogen Storage. Steven James Barcelo

Final Draft of the original manuscript:

Urchin-like Ni-P microstructures: A facile synthesis, properties. and application in the fast removal of heavy-metal ions

Hydrogen content of CeCl 3 -doped sodium alanate powder samples measured in-situ by ATR-FTIR-spectroscopy and gravimetry during desorption

Reaction Behavior of the Li-N-H Hydrogen Storage System with Boron Nitride as an Additive

Composite MOF foams: the example of UiO-66/polyurethane

DEVELOPMENT OF CATALYSTS FOR ETHANE EPOXIDATION REACTION. Keywords: Ethylene oxide, Partial oxidation, Ethane epoxidation, Second metal.

Supporting Information

Selective aerobic oxidation of biomass-derived HMF to 2,5- diformylfuran using a MOF-derived magnetic hollow Fe-Co

Thermochemical Storage Technologies

BAE 820 Physical Principles of Environmental Systems

Thermal Analysis Excellence

Very low temperature CO oxidation over colloidally deposited gold nanoparticles on Mg(OH) 2 and MgO

RSC Advances PAPER. Superior destabilization effects of LiBH 4 with the addition of nano-sized nickel ferrite NiFe 2 O 4. 1.

Asian Journal on Energy and Environment

University of Alberta

dissolved into methanol (20 ml) to form a solution. 2-methylimidazole (263 mg) was dissolved in

Affects of Mechanical Milling and Metal Oxide Additives on Sorption Kinetics of 1:1 LiNH 2 /MgH 2 Mixture

A Third Generation Breathing MOF with Selective, Stepwise, Reversible and Hysteretic Adsorption properties

Supporting Information

Hydrogen Storage and Delivery in a Liquid Carrier Infrastructure

Fischer-Tropsch Synthesis over Co/ɣ-Al 2 O 3 Catalyst: Activation by Synthesis Gas

Application of the Transient Hot-Wire Technique for Measurement of Effective Thermal Conductivity of Catalyzed Sodium Alanate for Hydrogen Storage

Supplementary Information

Hydrogen as fuel carrier in PEM fuelcell for automobile applications

BIOENERGY II Temperature effect on hydrogen production from reactions between ethanol and steam in the presence of Pd- Ru/Nb O -TiO catalyst

Mechano-chemical synthesis of manganese borohydride (Mn(BH 4 ) 2 ) and inverse cubic spinel (Li 2 MnCl 4 ) in the

Study of Morphological Changes in MgH2 Destabilized LiBH4 Systems Using Computed X- ray Microtomography

Effect of porous texture on hydrogen adsorption in activated carbons

Lecture 35: Vapor power systems, Rankine cycle

Supporting Information

THE SOLVENT EFFECTS ON GRIGNARD REACTION

Research Article Thermodynamic Property Study of Nanostructured Mg-H, Mg-Ni-H, and Mg-Cu-H Systems by High Pressure DSC Method

GECP Hydrogen Project: "Nanomaterials Engineering for Hydrogen Storage"

Synthesis of highly b-oriented zeolite MFI films by suppressing. twin crystal growth during the secondary growth

Characterization of Solid State Drugs by Calorimetry

Synthesis and Characterization of Magnesium Substituted Aluminophosphate Molecular Sieves with AEL Structure

Investigation into NH 3 -MnCl 2 and NH 3 -CaCl 2 Reaction Rates for the Development of a Thermal Transformer

Hydrogen Adsorption and Storage on Porous Materials. School of Chemical Engineering and Advanced Materials. Newcastle University United Kingdom

Chlorohydrination of Allyl Chloride with HCl and H 2 O 2 to Produce. Dichloropropanols Catalyzed by Hollow TS-1 Zeolite

Having a High Mg/Al Molar Ratio

Development of Safe and Scalable Continuous-Flow Methods for. Palladium-Catalyzed Aerobic Oxidation Reactions

Role of Re and Ru in Re Ru/C Bimetallic Catalysts for the

nm

Supporting Information. Synthesis of Mg/ Al Layered Double Hydroxides for Adsorptive Removal of. Fluoride from Water: A Mechanistic and Kinetic Study

The Vacuum Sorption Solution

Stoichiometry ( ) ( )

AP Chemistry: Designing an Effective Hand Warmer Student Guide INTRODUCTION

Lecture Outline. 5.1 The Nature of Energy. Kinetic Energy and Potential Energy. 1 mv

A prospect for LiBH 4 as on-board hydrogen storage

Vacuum Pumps. Two general classes exist: Gas transfer physical removal of matter. Mechanical, diffusion, turbomolecular

Carbon Nanofibers as a Hydrogen Storage Medium for Fuel Cell Applications in the Transportation Sector

Explosion Properties of Highly Concentrated Ozone Gas. 1 Iwatani International Corporation, Katsube, Moriyama, Shiga , Japan

CHEM*3440. Thermal Methods. Thermogravimetry. Instrumental Components. Chemical Instrumentation. Thermal Analysis. Topic 14

Transcription:

International Journal of Chemical and Biological Engineering Effects of TiO and Nb O on Hydrogen Desorption of Mg(BH ) Wipada Ploysuksai, Pramoch Rangsunvigit, Santi Kulprathipanja Abstract In this work, effects of catalysts (TiO, and Nb O ) were investigated on the hydrogen desorption of Mg(BH ). LiBH and MgCl with : molar ratio were mixed by using ball milling to prepare Mg(BH ). The desorption behaviors were measured by thermo-volumetric apparatus. The hydrogen desorption capacity of the mixed sample milled for h was.78 wt% with a -step released. The first step occurred at C and the second step appeared at 7 C. The addition of wt% Nb O decreased the desorption temperature in the second step about C and increased the hydrogen desorption capacity to.8 wt% hydrogen. The addition of TiO also improved the desorption temperature in the second step and the hydrogen desorption capacity. It decreased the desorption temperature about 7 C and showed a high amount of hydrogen,.7 wt%, released from the mixed sample. The hydrogen absorption after desorption of Mg(BH ) was also studied under 9. MPa and C for h. T Keywords hydrogen storage, LiBH, metal hydride, Mg(BH ) I. INTRODUCTION HE acceleration of global climate change and the energy crisis caused by the wide use of fossil fuels have encouraged the development of hydrogen as a clean secondary energy source. Hydrogen, a renewable, high burning heat, energy source and low environmental pollution can be used as an alternative fuel for vehicles. One of the challenges in the development of the hydrogen economy is the storage of hydrogen with reliability and safety along with high density, low cost, and a fast releasing rate. As a target given by the U.S. Department of Energy (DOE), the storage criteria for vehicular applications are wt% storage capacity at a temperature below C with low cost and low toxicity []. Currently, four methods are available for hydrogen storage: high-pressure gas cylinders, liquid hydrogen in cryogenic tanks, absorption by metal hydride or adsorption on materials with a large surface area, and chemical hydrogen storage (including off-board regeneration). However, some storage methods cannot meet the requirement for hydrogen as a fuel W. P. is with The Petroleum and Petrochemical College; and Center for Petroleum, Petrochemicals, and Advanced Materials, Chulalongkorn University, Soi Chula, Phyathai Road, Pathumwan, Bangkok, Thailand (e-mail: airvipool@hotmail.com) P. R. is with Petroleum and Petrochemical College; and Center for Petroleum, Petrochemicals, and Advanced Materials, Chulalongkorn University, Bangkok, Thailand (Phone: +--8-9; fax: +-- 8-9;e-mail: pramoch.r@chula.ac.th) S. K. is with UOP, A Honeywell Company, East Algonquin Rd., Des Plaines, IL 7, USA) in car engines or aircraft turbines because of the low hydrogen uptake and ungovernable hydrogen desorption rate. For example, high pressure storage needs high strength containers and has a limited volume capacity including safety problems []. Therefore, chemical or physically combined storage of hydrogen in other materials has potential advantages over other storage methods because this process may provide high volumetric and gravimetric storage capacities. However, due to the strong interaction between the adsorbate and surface, reversibility can only be observed at high temperatures []. Hydrogen forms metal hydrides with some metals and alloys leading to solid-state storage under a moderate temperature and pressure that gives them the important safety advantage over the gas and liquid storage methods. Metal hydrides have higher hydrogen-storage density (. H atoms/cm for MgH ) than hydrogen gas (.99 H atoms/cm ) or liquid hydrogen (. H atoms/cm ). Hence, metal hydride storage is a safe, volume-efficient storage method for on-board vehicle applications. A group of Mg-based hydrides stands as a promising candidate for competitive hydrogen storage with reversible hydrogen capacity up to 7. wt% for on-board applications []. Furthermore, borohydrides have been considered interesting candidates for hydrogen storage applications due to their high gravimetric hydrogen content []. Among all possible complex hydride candidates, magnesium borohydride [Mg(BH ) ] seems to have the potential to satisfy the performance targets proposed by the U.S. Department of Energy because it contains not only high gravimetric (.8 wt%) and volumetric ( g/l) hydrogen densities, but also a low hydrogen binding enthalpy. Moreover, research results concerning the correlation between the thermodynamic stability of M(BH )n (M = Li, Na, K, Ca, Mg, Zn Sc, Zr and Hf; n = -) and the electronegativity of M suggest that Mg(BH ) is one of the most attractive borohydrides for hydrogen storage owing to its favorable desorption hydrogen enthalpy. However, the high decomposition temperature of about C makes it unfavorable for practical fuel cell applications []. To enhance the hydrogen storage capacity, the kinetics and cycle life including decrease their desorption temperature, modified Mg(BH ) has been investigated. The kinetics has been improved by adding an appropriate catalyst into the system and by ball-milling that introduces defects with improved surface properties. From the previous studies, attempts have been made to improve metal hydride properties including hydrogen-storage capacity, kinetics, cyclic behavior, toxicity, pressure and thermal response []. In this research, Mg(BH ) was 8

International Journal of Chemical and Biological Engineering synthesized by a dry process. The hydride was then investigated for its hydrogen storage properties. Effects of catalyst, ball-milling, temperature, and pressure on the hydrogen storage capacity, were reported. II. EXPERIMENTAL A.Sample Preparation For the mixture of LiBH and MgCl, the sample was prepared with a : molar ratio and mixed with and without a transition metal. A transition metal catalyst - Nb O and TiO - was included. The mixing was achieved by a ball-milling technique. For mixed samples, wt% Nb O or TiO was added to the sample and milled for and h. The starting materials were used as-received. In the milling process, the sample was milled using a centrifugal ball mill (Retsch ball mill model S, ml stainless steel vial, stainless steel ball with cm diameter) under nitrogen atmosphere with a ball to powder ratio of : and a rotation speed of rpm. All material handlings (including weighing and loading) were performed in a glove box filled with nitrogen to keep a low water vapor concentration and avoid exposing the samples to air. B.Experimental Set up The thermo-volumetric apparatus was used to study the gassolid interaction. The schematic diagram of the experimental set-up is shown in Fig.. The set-up consisted of a high pressure stainless reactor, which held the sample and part of stainless steel tube as a gas reservoir. The high pressure stainless steel reactor was heated from room temperature to C for the LiBH and MgCl mixture with a heating rate of C/min via a furnace controlled by a PID temperature controller. Inside the reactor, a K-type thermocouple was placed to measure the temperature. The pressure regulator with, psig maximum limit was installed to control the gas flow rate into the whole system. The pressure transducer was used to measure pressure of the system for measuring in the range of -, psig with.% global error. C.Hydrogen Sorption Data Collection The pressure transducers must be calibrated for each desorption experiment. Atmospheric pressure,.7 psi, was used as the reference pressure to set the zero span on the transducer to vacuum. The amount of sample used in each experiment was about. g. A sample was placed into the sample holder, and the sample holder volume was determined. The degassing procedure at about - torr and C was conducted to remove the remaining gas for at least an hour. The sample holder was initially pressurized with helium gas at psig. Hence, the valve between the manifold and the sample holder was closed. After that, hydrogen desorption was performed from C to the set point ( C for the LiBH and MgCl mixture) by a stepwise increase with a heating rate of C/min. A sample was held at C until no further hydrogen desorption was observed. While the above processes were continuing, the pressure values were recorded every min until the pressure in the sample holder was rather constant. The released pressure was cooled down to room temperature to avoid the gas expansion by heat before evaluating the hydrogen capacity. After completing hydrogen desorption, the sample was compressed under 9. MPa hydrogen (99.9999%) at a constant temperature of ºC for h for hydrogen adsorption. After that, both hydrogen desorption and absorption were repeated in order to investigate the reversibility. D.Characterization In order to identify phase transformation during hydrogen desorption and absorption of the samples, X-ray diffraction (XRD, Rigaku) measurement was used at the room temperature over a range of diffraction angles from to 7 with CuK- The desorption temperature, phase transformation temperature, and temperature that reactions occured were measured by differential scanning calorimetry (DSC 8, Mettler Toledo). III. RESULTS AND DISCUSSION A.Synthesis of Mg(BH ) To synthesize Mg(BH), a mixture of LiBH and MgCl was prepared with a : molar ratio by ball-milling at and h. The XRD patterns in Fig. provide the phase of the LiBH /MgCl mixture milled for and h and LiBH milled for h. The XRD patterns of the LiBH /MgCl mixture milled for and h (Fig. b and c) consists of LiMgCl and LiCl peaks whereas the peaks corresponding to LiBH (Fig. a) and MgCl disappear. It can be deduced that the ball milling process induces LiBH to react with MgCl through the following reaction [7]-[8]: LiBH + MgCl Mg(BH ) + LiCl () Fig. Schematic diagram of the experimental set-up Comparison between the XRD patterns of the LiBH /MgCl mixture milled for and h shows that the intensity of the sample ball milled for h (Fig. c) is lower than that ball milled for h (Fig. b). That is believed to be contributed from the partial decomposition of the LiBH /MgCl mixture to 9

International Journal of Chemical and Biological Engineering LiCl and H during the ball milling process. Therefore, the ball milling time of h is expected to be adequate to synthesize Mg(BH ). Intensity (a.u.) + Fig. X-ray diffraction patterns of LiBH milled for h, the LiBH /MgCl mixture milled for h and h The reason for the absence of a diffraction pattern of Mg(BH ) may be that the compound synthesized by the ball milling method is not crystallized sufficiently [9]. B.Hydrogen Desorption of Mg(BH ) The hydrogen desorption profiles of Mg(BH ) at different ball milling times are presented in Fig.. For the ball milling time of h (Fig. a), Mg(BH ) starts to decompose at C. The first desorption step occurs at C and releases about. wt% hydrogen. The second step releases. wt% hydrogen and takes place at 7 C, with a total amount of desorbed hydrogen about.78 wt% hydrogen. The results of Mg(BH ) ball milled for h (Fig. b) show similar hydrogen desorption profile to that ball milled for h. It starts to release at C, while the starts of the first and second desorption are at C and 7 C with the accumulated hydrogen of.97 and. wt%, respectively, and a total amount of desorbed hydrogen about.7 wt% hydrogen. These results indicate that the hydrogen desorbs in the following two steps [7]-[8]: Mg(BH ( st step) () ) MgH B H MgH Mg ( nd step) () H LiBH * LiCl LiMgCl + film 7 Degree ( ) Moreover, the results indicate that the mixing between LiBH and MgCl to synthesize MgBH results in the decrease in the desorption temperature compared to LiBH that show the desorption temperature at 8 C (Fig. c). However, LiBH shows a high hydrogen capacity about. wt% hydrogen. Desorbed hydrogen, wt% Fig. Hydrogen desorption profiles of the LiBH /MgCl mixture milled for h and h and LiBH milled for h The DSC profiles in Fig. show the phase transformation temperature of the LiBH /MgCl mixture milled for and h. The DSC profile of the LiBH /MgCl mixture milled for h (Fig. a) shows the first step of hydrogen desorption temperature at C and the second step at 77 C. For the mixture ball milled for h (Fig. b), the result shows hydrogen desorption temperature of the first and second steps at and 8 C, respectively. (mw) 7 Fig. Differential scanning calorimetry profiles of the LiBH /MgCl mixture milled for h and h The results from Fig. and exhibit that using different ball milling times results in similar hydrogen desorption behavior and desorption temperature. However, the LiBH /MgCl mixture milled for h shows a little higher hydrogen capacity than that milled for h. C.Hydrogen Desorption of Catalyzed Mg(BH ) It is well known that catalysts are an important factor that affects the desorption temperature of metal hydrides and complex metal hydrides []. This work further substantiates

International Journal of Chemical and Biological Engineering the effects of a catalyst on the desorption behaviors of Mg(BH ). The hydrogen desorption profiles of wt% Nb O - Mg(BH ) with and h ball milling times are presented in Fig.. The samples release hydrogen in two steps as the uncatalyzed sample. For wt% Nb O -Mg(BH ) ball milled for h (Fig. a), it starts to decompose at C. The first step desorption releases. wt% hydrogen and takes place at C, while the start of the second desorption is at 8 C with. wt% hydrogen and the total amount of desorbed hydrogen about.8 wt%. wt% Nb O -Mg(BH ) ball milled for h (Fig. b) shows the first desorption step at C and releases.79 wt% hydrogen, whereas the second step occurs at 7 C with.9 wt% hydrogen and the total desorbed hydrogen of.7 wt%. The results suggest that Nb O improves the desorption behaviors of Mg(BH ), which is to decrease the desorption temperature at the second step from 7 C (uncatalyzed) to 8 C and 7 C for wt% Nb O -Mg(BH ) ball milled for and h, respectively. The result also supports that the ball milling time of h is sufficient to prepare Mg(BH ) with the percent of Nb O. Therefore, the addition of Nb O contributes to fast hydrogen desorption with a significant decrease of desorption temperature about C, which is in agreement with that reported by Friedrichs et al., () []. Desorbed hydrogen (wt%) (d) Fig. Hydrogen desorption profiles of wt% Nb O -Mg(BH ) milled for h and h and hydrogen desorption profiles of the LiBH /MgCl mixture milled for h and h (d) TiO is one of the titanium catalysts that can improve the performance of metal hydride, and Fig. shows the hydrogen desorption profiles of wt% TiO -Mg(BH ) with and h ball milling times. Hydrogen desorbs in two steps same as the uncatalyzed sample. wt% TiO -Mg(BH ) ball milled for h (Fig. a) starts to decompose at C, and the first desorption step occurs at C and releases about. wt% hydrogen. The second step releases.7 wt% hydrogen at C with the total hydrogen of.7 wt%. wt% TiO - Mg(BH ) ball milled for h (Fig. b) shows similar hydrogen desorption profile to the one ball milled for h. It starts to desorb at C and the first desorption step appears at 9 C with. wt% hydrogen. The second step releases.7 wt% hydrogen at 7 C and provides the total hydrogen capacity of. wt%. The results indicate that TiO improves the desorption behaviors of Mg(BH ), which is to decrease the desorption temperature at the second step about 7 C and 7 C for the samples ball milled for h and h, respectively. Desorbed hydrogen (wt%) (d) Fig. Hydrogen desorption profiles of wt% TiO -Mg(BH ) milled for h and h and hydrogen desorption profiles of the LiBH /MgCl mixture milled for h and h (d) From the amount of desorbed hydrogen, it was found that the sample with wt% TiO releases higher amount of hydrogen than the undoped and wt% Nb O doped samples and also decreases the hydrogen desorption temperature of the hydride in the second step decomposition. IV. CONCLUSIONS In this research, the method to prepare Mg(BH ), the desorption behaviors and desorption temperature of Mg(BH ) and Mg(BH ) doping with catalysts (Nb O and TiO ) were investigated. Ball-milling technique for h is adequate for the synthesis of Mg(BH ) by mixing LiBH with MgCl at : molar ratio. The hydrogen desorption profiles of the Mg(BH ) showed two steps of hydrogen released. The first desorption step occurs at C and releases about. wt% hydrogen. The second step releases. wt% hydrogen and takes place at 7 C, with a total amount of desorbed hydrogen about.78 wt% hydrogen. Mg(BH ) doped with Nb O, wt%, showed a good desorption behaviors that is the second desorption temperature is decreased by C as compared with the uncatalyzed sample. Forthermore, doping with wt% TiO, not only exhibits the best desorption behaviors, but also shows the good hydrogen desorption capacity,. wt% hydrogen, and the second desorption temperature is decreased by 7 C when compared with the undoped sample. However, the absorption of dehydrogenated samples mixed with the catalysts cannot re-absorb hydrogen under H pressure 9. MPa at C.

International Journal of Chemical and Biological Engineering ACKNOWLEDGMENTS The authors would like to acknowledge the National Excellence Center for Petroleum, Petrochemicals, and Advance materials, Chulalongkorn University, Thailand. REFERENCES [] Ye, X., An, Y., and Xu, G. (). Kinetics of 9 - ethylcarbazole hydrogenation over Raney-Ni catalyst for hydrogen storage. Journal of Alloys and Compounds, 9,. [] Dong, J., Wang, X., Xu, H., Zhao, Q., and Li., J. (7). Hydrogen storage in several microporous zeolites. International Journal of Hydrogen Energy,, 998-. [] Hu, X., Fan, M., Towler,B.F., Radosz M., and Bell, D. A. (). Chapter 8 Hydrogen Adsorption and Storage. Coal Gasification and Its Applications., 88. [] Sakintuna, B., Darkrimb, F. L., Hirscherc, M. (7). Metal hydride materials for solid hydrogen storage: A review. International Journal of Hydrogen Energy,, -. [] Pistidda, C., Garroni, S., Dolci, F., Bardají, E. G., Khandelwal, A., Nolis, P., Dornheim, M., Gosalawit, R., Jensen, T., Cerenius, Y., Suriñach, S., Baro, M. D., Lohstroh, W., and Fichtner, M. (). Synthesis of amorphous Mg(BH ) from MgB and H at room temperature. Journal of Alloys and Compounds, 8,. [] Zhang, Z.G., Zhang, S.F., Wang, H., Liu, J.W., and Zhu, M. (). Feasibility study of the direct synthesis of Mg(BH ) complex hydrides by mechanical milling. International Journal of Hydrogen Energy,, 77 7. [7] Matsunaga, T., Buchter, F., Miwa, K., Towata, S., Orimod, S., and Züttel, A. (8). Magnesium borohydride: A new hydrogen storage. Renewable Energy,, 9-9. [8] Matsunaga, T., Buchter, F., Mauron, P., Bielman, M., Nakamori, Y., Orimoc, S., Ohba, N., Miwa, K., Towata, S., and Züttel, A. (8). Hydrogen storage properties of Mg[BH ]. Journal of Alloys and Compounds, 9, 8 88. [9] Li, H.-W., Kikuchi, K., Nakamori, Y., Miwa K, Towata, S., and Orimo, S. (8). Effects of ball milling and additives on dehydriding behaviors of well-crystallized Mg(BH ). Scripta Materialia, 7, 79-8. [] Friedrichs, O., Klassen, T., Sánchez-López, J.C., Bormann, R., Fernández, A. (). Hydrogen sorption improvement of nanocrystalline MgH by Nb O nanoparticles. Scripta Materialia,, 9 97.