Electronic Supporting Information (ESI) Porous Carbon Materials with Controllable Surface Area Synthsized from Metal-Organic Frameworks

Similar documents
A flexible MMOF exhibiting high selectivity for CO 2 over N 2, CH 4 and other small gases. Supporting Information

Supporting Information

Supplementary Information. ZIF-8 Immobilized Ni(0) Nanoparticles: Highly Effective Catalysts for Hydrogen Generation from Hydrolysis of Ammonia Borane

Supporting Information

Growth of 2D sheets of a MOF on graphene surfaces to yield composites with novel gas adsorption characteristics

dissolved into methanol (20 ml) to form a solution. 2-methylimidazole (263 mg) was dissolved in

Electronic Supplementary Information (ESI) From metal-organic framework to hierarchical high surface-area hollow octahedral carbon cages

Supporting Information. From Metal-Organic Framework to Nanoporous Carbon: Toward a Very High Surface Area and Hydrogen Uptake

Supporting Information

Microporous Manganese Formate: A Simple Metal-Organic Porous Material with High Framework Stability and Highly Selective Gas Sorption Properties

Fabrication of COF-MOF Composite Membranes and Their Highly. Selective Separation of H 2 /CO 2

Shape Assisted Fabrication of Fluorescent Cages of Squarate based Metal-Organic Coordination Frameworks

Metal-organic frameworks (MOFs) as precursors towards TiO x /C. composites for photodegradation of organic dye

Supplementary Information

Electronic Supplementary Information

Supporting Information. Integration of accessible secondary metal sites into MOFs for H 2 S removal

Photo-responsive MOFs: Light-induced switching of porous single crystals containing photochromic diarylethene

Supporting Information

Electronic Supplementary Information for. Non-interpenetrated IRMOF-8: synthesis, activation, and gas sorption

Electronic supplementary information

Ethers in a Porous Metal-Organic Framework

Electronic Supplementary Information

Supplementary Information

Synthesis of 2 ) Structures by Small Molecule-Assisted Nucleation for Plasmon-Enhanced Photocatalytic Activity

Room Temperature Hydrogen Generation from Hydrous Hydrazine for Chemical Hydrogen Storage

Dry-gel conversion synthesis of Cr-MIL-101 aided by grinding: High surface area high yield synthesis with minimum purification

Supplementary Information

A triazine-based covalent organic polymer for efficient CO 2 adsorption

Supplementary Information

Supplementary Information for

Supporting Information

A Highly Efficient Double-Hierarchical Sulfur Host for Advanced Lithium-Sulfur Batteries

Very low temperature CO oxidation over colloidally deposited gold nanoparticles on Mg(OH) 2 and MgO

Selective aerobic oxidation of biomass-derived HMF to 2,5- diformylfuran using a MOF-derived magnetic hollow Fe-Co

Electronic Supplementary Information

Sacrifical Template-Free Strategy

Supporting Information

Supporting Information. For. Preparation and Characterization of Highly Planar Flexible Silver

Reversible uptake of HgCl 2 in a porous coordination polymer based on the dual functions of carboxylate and thioether

Supporting Information

A Tunable Process: Catalytic Transformation of Renewable Furfural with. Aliphatic Alcohols in the Presence of Molecular Oxygen. Supporting Information

Selective Binding and Removal of Organic Molecules in a Flexible Polymeric Material with Stretchable Metallosalen Chains

An Ideal Electrode Material, 3D Surface-Microporous Graphene for Supercapacitors with Ultrahigh Areal Capacitance

Supporting Information

Supporting Information

Microporous Organic Polymers for Carbon Dioxide Capture

Chiral Nematic Cellulose / Gold Nanoparticle Composites from Mesoporous Photonic Cellulose

3D Porous Crystalline Polyimide Covalent Organic Frameworks for Drug Delivery

Supplementary Information. Large Scale Graphene Production by RF-cCVD Method

in a Porous Metal-Organic Framework [Zn 2 (BPnDC) 2 (bpy)]

Constructing covalent organic frameworks in water via dynamic covalent bonding

A Third Generation Breathing MOF with Selective, Stepwise, Reversible and Hysteretic Adsorption properties

Pd-P nanoalloys supported on porous carbon frame as efficient catalyst for benzyl alcohol oxidation

Easy synthesis of hollow core, bimodal mesoporous shell carbon nanospheres and their. application in supercapacitor

Electronic Supplementary Information (ESI)

Department of Chemistry of The College of Staten Island and The Graduate Center, The City University of

Supporting Information

Supporting Information

Supplementary Information

Supplementary Information

Supporting Information

A new tetrazolate zeolite-like framework for highly selective CO 2 /CH 4 and CO 2 /N 2 separation

Trapping Lithium into Hollow Silica Microspheres. with a Carbon Nanotube Core for Dendrite-Free

Supplementary Material for. Zinc Oxide-Black Phosphorus Composites for Ultrasensitive Nitrogen

Facile synthesis of polymer and carbon spheres decorated with highly dispersed metal nanoparticles

Electronic Supplementary Information

Supplementary Data. Size-controlled synthesis of MIL-101(Cr) nanoparticles with. enhanced selectivity for CO 2 over N 2

1. General Experiments... S2. 2. Synthesis and Experiments... S2 S3. 3. X-Ray Crystal Structures... S4 S8

A doping of phosphorus and/or sulfur into nitrogen-doped carbon for efficient oxygen reduction reaction in acid media

Electronic Supplementary Information. Pd(diimine)Cl 2 Embedded Heterometallic Compounds with Porous Structures as Efficient Heterogeneous Catalysts

Electronic Supporting Information

Electronic Supplementary Information. Enhanced Photocatalytic/photoelectrocatalytic Activities

DMOF-1 as a Representative MOF for SO 2 Adsorption in both Humid and Dry Conditions

Supporting Information. Nanoscale Kirkendall Growth of Silicalite-1 Zeolite Mesocrystals with. Controlled Mesoporosity and Size

Supporting Information for

Supplementary Data. Synthesis and post-synthetic modification of

Synthesis of Secondary and Tertiary Amine- Containing MOFs: C-N Bond Cleavage during MOF Synthesis

Highly efficient SERS test strips

Supporting Information. Rapid synthesis of metal-organic frameworks MIL-101(Cr) without the addition of solvent and hydrofluoric acid

Experimental details. General

University of Chinese Academy of Sciences, Beijing , China. To whom correspondence should be addressed :

Supporting Information

Electronic Supplementary Material (ESI) for Chemical Communications This journal is The Royal Society of Chemistry 2011

Supplementary Information T. Ebert, a A. Wollbrink, b A. Seifert, a R. John, a and S. Spange a

Electronic Supplementary Information. Facile Synthesis of Germanium-Graphene Nanocomposites. and Their Application as Anode Material for Lithium Ion

Supporting Information

Supporting Information

Supporting Information

Electronic supplementary information. A longwave optical ph sensor based on red upconversion

Rapid, Efficient Phase Pure Synthesis of Ca 2 AlNO 3 Layered Double Hydroxide

Supporting Information

Supporting Information for. Size-Dependent Oxidation State and CO Oxidation Activity of Tin

Functional Group Effects on Metal- Organic Framework Topology

Preparation of Nanofibrous Metal-Organic Framework Filters for. Efficient Air Pollution Control. Supporting Information

Significant Gas Uptake Enhancement by Post-Exchange of Zinc(II) with. Copper(II) within a Metal-Organic Framework

Supporting information. Mechanical Properties of Microcrystalline Metal-Organic Frameworks. (MOFs) Measured by Bimodal Amplitude Modulated-Frequency

A vanadium(iv) pyrazolate metal organic polyhedron with permanent porosity and adsorption selectivity

Supporting Information

Supporting Information. Carbon Imidazolate Framework-8 Nanoparticles for

SUPPORTING INFORMATION

Transcription:

Electronic Supporting Information (ESI) Porous Carbon Materials with Controllable Surface Area Synthsized from Metal-Organic Frameworks Seunghoon Lim, Kyungwon Suh, Yelin Kim, Minyoung Yoon, Hyeran Park, Danil N. Dybtsev,* Kimoon Kim* General methods All the reagents and solvents employed were commercially available and used as supplied without further purification. A tube furnace (MTI GSL-1600X50) was used for carbonization. Raman data was obtained on a Horiba Jobin-Yvon LabRam HR spectrometer. The powder XRD diffractograms were obtained on a Bruker D8 Advance system equipped with a Cu sealed tube (λ = 1.54178 Å). Following conditions were used: 40 kv, 40 ma, increment = 0.05º, scan speed = 3 deg/min. Gas sorption isotherms were recorded volumetrically with an automatic adsorption apparatus, Quantachrome Autosorb 1MP and BELSORP-max (BEL Japan). All gas sorption experiment was performed with high purity gases (N 2 : 99.999%, Linde Korea). C, H, N, S elemental analyses data were obtained using a VarioMICRO elemental analyzer. SEM images and energy dispersive X-ray spectroscopy (EDX) data were acquired on a JEOL JSM-6610 and QUANTAX 200, respectively. High-resolution TEM images were recorded on a JEOL-2200FS electron microscope operating at 200 kv. Synthesis of MOF precursors (1 6) Starting MOFs [Zn 4 O(bdc) 3 ] (1) [S1], [Zn 2 (bdc) 2 (dabco)] (2) [S2], [(Zn 4 O) 3 (bdc) 3 (btb) 4 ] (3) [S3] and [Zn 2 (bdc)(l-lac)(dmf)] (4) [S4] were prepared according to the literature. The synthetic conditions of [Zn 3 (bpdc) 3 (dmf) 2 ] (5) were modified from the literature procedure. [S5] A mixture of H 2 bpdc(1.92 g, 7.93 mmol) and Zn(NO 3 ) 2 6H 2 O (2.4 g, 8.1 mmol) was suspended in DMF (100 ml), and sonicated while heating to produce a clear solution, which was divided into 10.0 ml portions, and transferred to 10 scintillation vials. The reaction vial was then placed in an oven at 100 C for 1 day. Product 5 was isolated as large polyhedral colorless crystals. [Zn 3 (fumarate) 3 (dmf) 2 ] (6) was produced as a white powder upon heating a mixture of Zn(NO 3 ) 2 6H 2 O (1.0 g, 3.3 mmol) and fumaric acid (0.39 g, 3.4 mmol) in DMF (40 ml) at 100 C for 1 day. The resulting material was thoroughly washed with DMF and dried in air. Although the resulting material was non-crystalline, its chemical composition and formula based on TG and EA data are consistent with the reported formula. Elemental analysis data for 6: Found: C, 31.0; H, 2.8; N, 3.9. Calc. for C 18 H 22 NO 15 Zn 3 : C, 30.8; H, 3.2; N, 4.0%. A portion of solid sample 6 (245.5 mg) was calcinated in the air. The weight of the solid residue was found to be 92.9 mg (37.8%), calculated for ZnO: 35.7%. 1

Fig. S1 Simulated and experimental PXRD profiles of MOF precursors (a) 1, (b) 2, (c) 3, (d) 4, (e) 5, and (f) 6. 2

1600 1 2 3 4 5 6 1400 Amount adsorbed / cm 3 g -1 1200 1000 800 600 400 200 0 0.0 0.2 0.4 0.6 0.8 1.0 P / P 0 Fig. S2 N 2 gas adsorption (filled symbol) and desorption (open symbol) isotherms for 1 (square), 2 (circle), 3 (star), 5 (diamond), 6 (pentagon) at 77K and CO 2 gas adsorption and desorption of 4 (triangle) at 197K. Synthesis of carbon materials (1c 6c) The MOF precursors 1 6 were heated to 1100 C in a quartz tube furnace (diameter = 27 mm) with a heating rate of 10 C min -1 under Ar flow (flow rate = 200 ml min 1 ), carbonized for 8 h and naturally cooled down to room temperature. The resulting black powders (1c 6c, respectively) were collected. 6c 5c Relative Intensity 4c 3c 2c 1c 5 10 15 20 25 30 35 2 theta (degrees) Fig. S3 PXRD of carbon materials 1c (black), 2c (red), 3c (blue), 4c (pink), 5c (violet) and 6c (olive). 3

Electronic Supplementary Material (ESI) for Chemical Communications Fig. S4 TEM images of carbon materials (a) 1c, (b) 2c, (c) 3c, (d) 4c, (e) 5c, and (f) 6c. 4

Electronic Supplementary Material (ESI) for Chemical Communications Fig. S5 SEM images of carbon materials (a) 1c, (b) 2c, (c) 3c, (d) 4c, (e) 5c, and (f) 6c (inset: high magnification images). 5

Fig. S6 EDX spectra of the materials (a) 1 and 1c (b) 2 and 2c, (c) 3 and 3c, (d) 4 and 4c, (e) 5 and 5c, and (f) 6 and 6c (black line: experimental, orange line: expected). EDX spectra were obtained using 30 kv acceleration voltage. The EDX spectra demonstrated the absence of Zn metals in the porous carbon materials. 6 Electronic Supplementary Material (ESI) for Chemical Communications

Raman spectra Raman spectra were measured in backscattering geometry with a JY LabRam HR fitted with a liquid-nitrogen cooled CCD detector. The spectra were collected under ambient conditions using the 514.5 nm line of an argon-ion laser (Fig. S7). Fig. S7 Raman spectra of carbon materials 1c, 4c, and 5c. Green and gray lines highlight the D and G bands, respectively, due to sp 2 carbon atoms. [S6] Gas sorption experiments About 50 mg of samples were loaded in glass cell and activated at 120 C under dynamic vacuum (10-4 bar) overnight before measurement. Nitrogen sorption isotherms were recorded in the pressure range up to 10-3 100 kpa at 77 K. 7

Fig. S8 Pore-size distribution curves with adsorption volume V and pore diameter D of (a) 1c, (b) 2c, (c) 3c, (d) 4c, (e) 5c, and (f) 6c calculated by the SF method [S7] from N 2 adsorption isotherms. Reproducibility and stability study of a carbon material, 4c. For reproducibility test, porous carbon material 4c was prepared three times independently from different batches of precursor 4. N 2 gas sorption isotherms were measured for each batch. The isotherm data are summarized in Fig. S9a. The porous carbon 4c samples were immersed in H 2 O, HCl (0.1 M), KOH (0.1 M), Ce(SO 4 ) 2 (0.01 M water solution with several drops of H 2 SO 4 ) and H 3 PO 4 (0.01 M) for 1 day. After that thoroughly washed of the samples with distilled water (the absence of Cl, K, Ce, S or P in the corresponding carbon samples were analyzed by EDX spectra). The resulting samples were dried, activated at 120 C under dynamic vacuum (10-4 bar) overnight. The N 2 gas absorption isotherms are shown in Fig. S9b. The BET surface area of the resulting samples is provided in the Table S1. 8

Fig. S9 Reproducibility (a) and stability (b) test for 4c as indicated by N 2 sorption isotherm data at 77K. Adsorption (desorption) data are marked by filled (open) symbols, respectively. Table S1. BET surface areas of 4c treated with various chemicals. S BET (m 2 g -1 ) no treatment 1700 H 2 O 1670 KOH (base) 1720 HCl (acid) 1500 H 3 PO 4 (strong oxidizing agent) 800 Ce(SO 4 ) 2 (strong oxidizing agent) 930 References S1. H. Li, M. Eddaoudi, M. O'Keeffe and O. M. Yaghi, Nature, 1999, 402, 276. S2. D. N. Dybtsev, H. Chun and K. Kim, Angew. Chem., Int. Ed., 2004, 43, 5033. S3. K. Koh, A. G. Wong-Foy and A. J. Matzger, Angew. Chem., Int. Ed., 2008, 47, 677. S4. D. N. Dybtsev, A. L. Nuzhdin, H. Chun,; K. P. Bryliakov, E. P. Talsi, V. P. Fedin and K. Kim, Angew. Chem., Int. Ed., 2006, 45, 916. S5. S. M. Hawxwell, H. Adams and L. Brammer, Acta Crystallogr., Sect. B: Struct. Sci., 2006, 62, 808. S6. A. C. Ferrari, J. Robertson Phil. Trans. R. Soc. Lond. A, 2004, 362, 2477. S7. A. Saito, H. C. Foley AIChE J., 1991, 37, 429. 9