Electronic Supplementary Material (ESI) for Journal of Materials Chemistry A. This journal is The Royal Society of Chemistry 2018 Electronic Supplementary Information Magnesium-Regulated Oxygen Vacancies of Nickel Layered Double Hydroxides for Electrocatalytic Water Oxidation Liyong Chen,* Yingyue Zhang, Dezhi Li, Yanxin Wang, and Chunying Duan*
Materials and characterization methods All chemical reagents were used as received. Nafion solution (5 wt% in mixture of water and 2- propanol) was purchased from Sigma Aldrich. Nickel nitrate hexahydrate (Ni(NO 3) 2 6H 2O), magnesium nitrate hexahydrate (Mg(NO 3) 2 6H 2O), aluminum nitrate nonahydrate (Al(NO 3) 3 9H 2O), manganese (II) nitrate tetrahydrate (Mn(NO 3) 2 4H 2O), zinc nitrate hexahydrate (Zn(NO 3) 2 6H 2O), calcium nitrate tetrahydrate (Ca(NO 3) 2 4H 2O), 2-methylimidazole (Hmim), sodium hydroxide (NaOH), potassium permanganate (KMnO 4), sodium nitrate (NaNO 3), hydrogen peroxide (H 2O 2, 30 wt%), hydrazine hydrate (N 2H 4 H 2O, >80 wt%), sulfuric acid (H 2SO 4, 18.4 M), hydrogen chloride (HCl, 12 M), methanol, RuO 2, and natural graphite were purchased from Sinopharm Chemical Reagent Co., Ltd, China. Transmission electron microscopy (TEM) was used to characterize microstructures and morphologies of samples on a Tecnai F30 operated at 300 kv. Scanning electron microscopy (SEM) was performed on HITACHI UHR FE-SEM SU8220. X-ray diffraction (XRD) was carried out in a Rigaku D/Max 2400 automatic powder X-ray diffractometer with Cu-Kα radiation (λ = 1.5418 Å). The thickness of samples was estimated by atomic force microscopy (AFM, Park Systems XE-70) based on non-contact mode. The contents of metal elements were evaluated by inductively coupled plasma atomic emission spectroscopy (ICP-AES, Optima 2000DV). The composition and chemical state of samples was analyzed by X-ray photoelectron spectroscopy (XPS,Thermo ESCALAB 250Xi) with Al-Kα radiation (hν = 1486.6 ev). Electron spin resonance (ESR) spectra were collected on Bruker A200 at room temperature. Zeta potential was measured on Zetasizer Nano ZS90. Linear-sweep voltammetry (LSV), cyclic voltammetry (CV), and chronoamperometry were measured on a CHI760E electrochemical workstation using a conventional three-electrode cell. Electrochemical impedance spectroscopy (EIS) was investigated on a ZAHNER ENNIUM electrochemical workstation. Materials synthesis Synthesis of Ni-LDHs. Ni(NO 3) 2 6H 2O (1.454 g, 5 mmol) and Hmim (0.411 g, 5 mmol) were sequentially added to methanol (15 ml) with vigorously stirring to form a uniform solution in a 20 ml of Teflon-lined stainless steel autoclave. The resulting mixture was heated at 80 o C for 4 h. The final pale green product was collected by centrifugation, rinsed thrice by methanol, and dried in vacuum oven at 80 o C for 6 h before subjected to characterization. Synthesis of NiM-LDHs. Ni-LDHs doped with s-, p-, d-, and ds-block metals were prepared. In a typical synthetic procedure, Ni(NO 3) 2 6H 2O (1.454 g, 5 mmol), Mg(NO 3) 2 6H 2O (25.6 mg, 0.1 mmol) and Hmim (0.411 g, 5 mmol) were sequentially added to methanol (15 ml) with vigorously stirring to form a uniform solution in a 20 ml of Teflon-lined stainless steel autoclave. The resulting mixture was heated at 80 o C for 4 h. The final pale green product was collected by centrifugation, rinsed thrice by methanol, and dried in vacuum oven at 80 o C for 6 h before subjected to characterization. Other NiM-LDHs were prepared by using Mn(NO 3) 2 4H 2O, Zn(NO 3) 2 6H 2O, and Al(NO 3) 3 9H 2O to substitute for Mg(NO 3) 2 6H 2O under otherwise identical conditions. In the synthetic media, the molar ratio of Ni to M (such as Mg) were allowed to adjust and prepare various NiM-LDHs.
Fabrication of NiMg-LDHs/rGO hybrids. Graphene oxide (GO) was firstly prepared by a modified Hummers method. Briefly, natural graphite (0.5 g) and NaNO 3 (0.25 g) were mixed in concentrated H 2SO 4 (20 ml) with stirring while cooling in an ice-water bath, and then KMnO 4 (1.5 g) was gradually added. The temperature of the mixture was allowed to warm to room temperature, subsequently was transferred to water bath and heated at 35 o C for 30 min. After that, deionized water (30 ml) was added, and the suspension was heated at 90 o C for another 15 min. Another addition of deionized water (80 ml) and H 2O 2 (30 wt%, 0.5 ml) were sequentially added to the suspension under stirring for another 1 h. The suspension was filtered and washed with HCl (1 M) and deionized water several times until the ph was ~7. The collected solid was redispersed into deionized water (100 ml) by sonication for 1 h, and centrifuged at 5000 g for 15 min. GO sheets in the supernatant were kept for subsequent application. To prepare reduced graphene oxide (rgo), N 2H 4 H 2O (80 μl) was added to an aqueous GO suspension (1 g/l, 100 ml) in a round-bottom flask at room temperature, and the mixture was heated at 100 o C for 1 h. The precipitates were collected by filtering. The aqueous suspension of rgo (0.1 g/l, 2 ml) after sonication was added to NiMg-LDHs suspension (10 g/l, 2 ml) dropwise. The mixture was successively stirred for 1 h. The final product was washed with deionized water three times and dried in vacuum oven at 80 o C for 6 h before subjected to characterization. Electrochemical measurements Preparation of electrocatalyst inks: Ni-, NiM-LDHs, and NiM-LDHs/rGO (5 mg) were added to the mixture of water and ethanol with volume ratio of 1:1 (0.975 ml), and Nafion solution (0.025 ml, 5 wt%). The suspension was sonicated in an ultrasonic bath for 20 min to form a uniform electrocatalyst inks. Preparation of work electrodes: Glassy carbon (GC) electrodes (3 mm in diameter) were used as work electrodes, and were polished on a Nylon plate containing alumina and deionized water before utilization. The electrocatalyst ink (5 μl) was drop-casted on the surface of polished GC electrode rinsed with deionized water. The as-prepared work electrodes were naturally dried at room temperature for 1 h. Ag/AgCl (3.5 M KCl) and polished Pt wire were used as the reference electrode and the counter electrode in the conventional three-electron cell, respectively. Electrocatalytic oxygen evolution reaction (OER): All electrochemical measurements were performed in in 1 M KOH solution. ir-compensated LSV curves were collected with a sweep rate of 5 mv s -1 between 0.2 to 0.8 V vs. Ag/AgCl after 5 successive CV scans between 0.2 V and 0.5 V. CV curves were collected with variable sweep rate from 20 to 100 mv s -1 at an increment of 20 mv s -1 between 0.2 to 0.3 V vs. Ag/AgCl to assess the double-layer capacitance of electrocatalysts. EIS was studied at overpotential of 320 mv in the frequency range from 0.1 Hz to 100 khz with oscillation potential amplitudes of 5 mv. The durability was studied by successive CV scan for 1000 times at a potential windows of 0.46 to 0.56 V vs. Ag/AgCl at a scan rate of 50 mv s -1. The Tafel plots were calculated from LSV curves origniated from the equation of η = a + blgj. The potentials vs. reversible hydrogen electrode (RHE) were coverted according to the Nernst equation of E RHE =E Ag/AgCl + 0.0591pH + 0.197. The TOF (s -1 ) were calculated by the equation of TOF = I/(2Fn), where I is current in the LSV curves, F is the Faraday constant, and n is the molar amount of active sites.
Fig. S1 XRD patterns of Ni- and NiM-LDHs (molar ratio of 50:1 from Ni to M).
Fig. S2 TEM image of the curled edge of a NiMg-LDH sheet.
Fig. S3 (a) N 2 adsorption/desorption isotherms at 77 K of all Ni- and NiM-LDHs and (b) corresponding pore size distribution.
Fig. S4 TEM (top), SEM (middle) and AFM (bottom) images of (a, b, c) NiMn-LDHs, (d, e, f) NiZn-LDHs, and (g, h, i) NiAl-LDHs. Insets is the height cross-sectional profiles of sheets labeled in the AFM images.
Fig. S5 ir-compensated polarization curve of RuO 2 towards OER in 1.0 M KOH.
Fig. S6 Cyclic voltammetry (CV) curves of various LDHs in 1.0 M KOH at a scan rate of 100 mv s -1.
Fig. S7 CV curves measured with different scan rates of 20, 40, 60, 80, and 100 mv/s: (a) Ni- LDHs, (b) NiMg-LDHs, (c) NiMn-LDHs, (d) NiZn-LDHs and (e) NiAl-LDHs.
Fig. S8 The comparison of ir-compensated LSV curves of NiMg-LDHs before (red) and after (black) successive 1000 times CV scans.
Fig. S9 Survey XPS spectra of all samples.
Fig. S10 ESR spectra of Ni- and NiMg-LDHs.
Fig. S11 XRD pattern of the sample prepared from Ni(NO 3) 2, Ca(NO 3) 2 and Hmim in methanol.
Fig. S12 The sample of NiMg-LDHs prepared by a solvo/hydrothermal synthetic route: (a) SEM and (b) TEM images, (c) XRD pattern, and (d) XPS spectrum of O 1s.
Fig. S13 High resolution XPS spectra of O 1s and Ni 2p core levels of NiMg-LDHs prepared at different molar ratio from Ni to Mg: (a 1 and a 2) 100:1, (b 1 and b 2) 80:1, (c 1 and c 2) 50:1, (d 1 and d 2) 30:1, and (e 1 and e 2) 5:1.
Fig. S14 (a) ir-compensated LSV curves measured in 1 M KOH and (b) 10 and 20 of NiMg- LDHs prepared with different molar ratio from Ni to Mg.
Fig. S15 Thermogravimetric curve of NiMg-LDHs-(50:1).
Fig. S16 High-resolution XPS spectra of O 1s and Ni 2p core levels of NiMg-LDHs-(50:1) after thermal treatment under (a 1 and a 2) N 2 and (b 1 and b 2) O 2 atmospheres, respectively.
Fig. S17 ir-compensated LSV curves of NiMg-LDHs-(50:1) with and without thermal treatment under N 2 and O 2 atmospheres towards OER in 1.0 M KOH.
Fig. S18 High-resolution XPS spectra of Ni 2p and O 1s of (a, d) NiMn-LDHs, (b, e) NiZn-LDHs and (c, f) NiAl-LDHs.
Fig. S19 Zeta potential of (a) NiMg-LDHs and (b) rgo.
Fig. S20 (a) TEM and (b) SEM images and (c) XRD pattern and Raman spectrum of NiMg- LDHs/rGO hybrids.
Fig. S21 Electrocatalytic performance of NiMg-LDHs/rGO hybrids towards OER in 1.0 M KOH solution. (a) LSV curves with ir-compensation and (d) Tafel slopes