Lecture 15:The Tool-Narayanaswamy-Moynihan Equation Part II and DSC

Similar documents
Alfred University Dept. of Physics and Astronomy

Determination of the fictive temperature for a hyperquenched glass

SAMPLE ANSWERS TO HW SET 3B

DSC Methods to Quantify Physical Aging and Mobility in Amorphous Systems: Assessing Molecular Mobility


Sub -T g Relaxation in Thin Glass

Web Course Physical Properties of Glass. Range Behavior

Chemical reactors. H has thermal contribution, pressure contribution (often negligible) and reaction contribution ( source - like)

Landscape Approach to Glass Transition and Relaxation. Lecture # 4, April 1 (last of four lectures)

S A 0.6. Units of J/mol K S U /N

Thermal analysis of Li 2 O TeO 2 glass

Advanced Physical Chemistry CHAPTER 18 ELEMENTARY CHEMICAL KINETICS

MAT 122 Homework 7 Solutions

G. R. Strobl, Chapter 5 "The Physics of Polymers, 2'nd Ed." Springer, NY, (1997). J. Ferry, "Viscoelastic Behavior of Polymers"

Time-Dependent Statistical Mechanics 5. The classical atomic fluid, classical mechanics, and classical equilibrium statistical mechanics

8.044 Lecture Notes Chapter 5: Thermodynamcs, Part 2

Polymer Chemistry Research Experience. Support: NSF Polymer Program NSF (PI: Chang Ryu)/RPI Polymer Center

The effect of processing parameters on glass fiber birefringence development and relaxation

Differential Scanning Calorimetry

Viscoelastic Mechanical Analysis for High Temperature Process of a Soda-Lime Glass Using COMSOL Multiphysics

Chapter 5. On-line resource

Thermal and Structual Properties of Candidate Moldable Glass Types

CHEM 254 EXPERIMENT 4. Partial Molar Properties of Solutions

Energy Barriers and Rates - Transition State Theory for Physicists

Liquid to Glass Transition

Trial version. Temperature Sensing. How does the temperature sensor work and how can it be used to control the temperature of a refrigerator?

Common Definition of Thermal Analysis

PHYSICAL AGEING EFFECT IN Se 75 Te 20 In 5 CHALCOGENIDE GLASS

Rate of Heating and Cooling

Lecture 27. Transition States and Enzyme Catalysis

Temperature-Modulated Differential Scanning Calorimetry Analysis of High- Temperature Silicate Glasses

THEORY AND APPLICATIONS OF MODULATED TEMPERATURE PROGRAMMING TO THERMOMECHANICAL TECHNIQUES

Residual Stresses Near Holes In Tempered Glass Plates

UBC-SFU-UVic-UNBC Calculus Exam Solutions 7 June 2007

CHEM*3440. Thermal Methods. Thermogravimetry. Instrumental Components. Chemical Instrumentation. Thermal Analysis. Topic 14

DSC AS PROBLEM-SOLVING TOOL: BETTER INTERPRETATION OF Tg USING CYCLIC DSC

1. Introduction to Chemical Kinetics

2.2 THE DERIVATIVE 2.3 COMPUTATION OF DERIVATIVES: THE POWER RULE 2.4 THE PRODUCT AND QUOTIENT RULES 2.6 DERIVATIVES OF TRIGONOMETRIC FUNCTIONS

Temperature Sensing. How does the temperature sensor work and how can it be used to control the temperature of a refrigerator?

1. Use the Data for RNAse to estimate:

Glass Transformation-Range Behavior- Odds and Ends

Express the transition state equilibrium constant in terms of the partition functions of the transition state and the

Physics of disordered materials. Gunnar A. Niklasson Solid State Physics Department of Engineering Sciences Uppsala University

Homework Week 8 G = H T S. Given that G = H T S, using the first and second laws we can write,

Work and heat. Expansion Work. Heat Transactions. Chapter 2 of Atkins: The First Law: Concepts. Sections of Atkins

CHAPTER 9 LECTURE NOTES

Thermal Analysis. Short Courses POLYCHAR 25 Kuala Lumpur. Copyright 2017 by Jean-Marc Saiter

PHYSICAL AGING OF MISCIBLE POLYMER BLENDS. Christopher G. Robertson. Doctor of Philosophy In Department of Chemical Engineering

Implicit Differentiation and Related Rates

WHAT ARE THE PARAMETERS THAT GLASS TRANSITION TEMPERATURE OF CHALCOGENIDE GLASSES DEPEND ON? AN OVERVIEW

AMATH 351 Mar 15, 2013 FINAL REVIEW. Instructor: Jiri Najemnik

ChemE Chemical Kinetics & Reactor Design Solutions to Exercises for Calculation Session 3

Implicit Differentiation and Related Rates

Concept of the chemical potential and the activity of elements

Capturing the mechanical aging kinetics by thermal analysis

Major Concepts Calorimetry (from last time)

TAWN tests for quantitatively measuring the resolution and sensitivity of DSCs (version 2.1)

The glass transition as a spin glass problem

3.2 Systems of Two First Order Linear DE s

dy dt = a by y = a b

Applying Newton s Law of Cooling When The Target Keeps Changing Temperature, Such As In Stratospheric Ballooning Missions

Material Testing Overview (THERMOPLASTICS)

Physical aging of thermosetting powder coatings

Foundations of Chemical Kinetics. Lecture 30: Transition-state theory in the solution phase

Transient measurements using thermographic phosphors

A First Course on Kinetics and Reaction Engineering Unit 4. Reaction Rates and Temperature Effects

MATSCI 204 Thermodynamics and Phase Equilibria Winter Chapter #4 Practice problems

The University of Hong Kong Department of Physics. Physics Laboratory PHYS3550 Experiment No Specific Heat of Solids

MATH 1902: Mathematics for the Physical Sciences I

Measuring the Reaction Kinetics of Polyester/PCA-501(HAA) Powder Coatings With Dielectric Analysis (DEA)

G : Statistical Mechanics Notes for Lecture 3 I. MICROCANONICAL ENSEMBLE: CONDITIONS FOR THERMAL EQUILIBRIUM Consider bringing two systems into

Review of Lecture 5. F = GMm r 2. = m dv dt Expressed in terms of altitude x = r R, we have. mv dv dx = GMm. (R + x) 2. Max altitude. 2GM v 2 0 R.

Assignment 8. Tyler Shendruk December 7, 2010

Goals: To develop skills needed to find the appropriate differential equations to use as mathematical models.

Leaving Cert Differentiation

Title: Bulk Thermal Stability Characterization via the SBAT Apparatus

Chemical Equilibria. Chapter Extent of Reaction

Nucleation Behavior of Polypropylene with a Nan-O-Sil Additive Dr. Previn Shah, Rheoplast Associates

Maximum and Minimum Values

DEVELOPMENT OF IMPROVED METHODS FOR CHARACTERISING THE CURE OF COMPOSITE MATERIALS

5. Find the slope intercept equation of the line parallel to y = 3x + 1 through the point (4, 5).

Lecture 9 Examples and Problems

Gradient and Directional Derivatives October 2013

Experiment Flow Analysis

CH3511 EXPERIMENT: Determination of Thermal Properties Using a Differential Scanning Calorimeter

Lecture 6: Principal bundles

Chapter 8 Phase Diagram, Relative Stability of Solid, Liquid, and Gas

The Kinetics of B-a and P-a Type Copolybenzoxazine via the Ring Opening Process

Clausius Clapeyron Equation

THE SECOND LAW OF THERMODYNAMICS. Professor Benjamin G. Levine CEM 182H Lecture 5

Thermal Methods of Analysis

= 2e t e 2t + ( e 2t )e 3t = 2e t e t = e t. Math 20D Final Review

The morphology of PVDF/1Gra and PVDF/1IL/1Gra was investigated by field emission scanning

Lecture 4: Classical Illustrations of Macroscopic Thermal Effects. Heat capacity of solids & liquids. Thermal conductivity

Math 112 Group Activity: The Vertical Speed of a Shell

Predicting the future with Newton s Second Law

Effect of adding an ideal inert gas, M

12. Heat of melting and evaporation of water

[ A] 2. [ A] 2 = 2k dt. [ A] o

Chapter 6. Heat capacity, enthalpy, & entropy

Transcription:

Lecture 15:The Tool-Narayanaswamy-Moynihan Equation Part II and DSC March 9, 2010 Dr. Roger Loucks Alfred University Dept. of Physics and Astronomy loucks@alfred.edu

Thank you for taking me home! My eyes are completely open now! I understand the glass transition very well!!!!

First Let s Review p,h,t glass line p( T,0) dp dt p p eq dp dt = p p eq τ p( T, )= p eq ( T) super cooled liquid line ( equilibrium) T Temperature

We used these three equation. p( T,t)= p V ( T)+ p s ( T,t) p( T)= p eq ( T 0 )+α L ( T 0 )+α g ( T ) dp dt = p p eq τ d dt = T τ Tool s eq. p, H, V T 1 T 2 ( )= T 2 ( 0)= T 1

Initially Tool used τ = Kη = τ o e AT where η 0 and A are constants. Tool quickly realized that this did not account for the data. He postulated that η must depend on the Fictive temperature. If a liquid were cooled quickly, it would have a larger than a slower cooled liquid. This larger would correspond to a more open structure which would reduce the η. If the liquid were cooled slower, then the would be smaller and the structure is closer together and would have a larger η. To account for this, Tool (1946) assumed that a better choice of η would be η = η 0 e ( A 1 T +A 2 ) τ = τ 0 e ( A 1 T +A 2 ) where η 0 and A 1 and A 2 are constants. Tool s equation becomes d dt = T T f e A 1 T +A 2 τ 0 As clever as Tool s equation is, it can not account for the cross over experiments of Ritland. The reason for this lack of agreement is the single relaxation time.

Thermorheological Simplicity Define the relaxation response at a temperature T as R p ( T,t ) p T, p( T,0) p T, The range of R is 1 to 0, i.e. if t = 0, R = 1 and if t =, R = 0. The response R can typically be described by the stretched exponential R = e t b τ exp N a n e t τ n n =1 where τ exp is an experimentally determined parameter, 0 < b < 1. Stretched exponentials can be approximated by the Prony series where the a n s sum to 1. If all the τ n s have the same mathematical dependence on temperature then TRS results. To see this, rewrite the τ n R in the Prony series as τ/λ n so R becomes R = N a n e λ n t n =1 N τ = a n e λ nβ t where n =1 τ β

If the R for a system were measured at any value of T and then graphed as R vs. β, all of the R s at various T s would lie on top of one another, i.e. there would be one Master graph. R R For any T T 1 T 2 T 3 log t Log β Since there is one Master graph of R, define a reference temperature T r at which the Master graph would be measured. Call the time associated with this reference temperature ξ. Since the same graph would result at any temperature T, we can conclude that β = ξ τ r = t τ or more simply ξ = τ r τ t where ξ is called the reduced time.

We can view ξ in the following way. If a system relaxes by some amount at temperature T in a time t, ξ is the time that is needed for the system to relax the same amount at temperature T r, i.e. R( t,t)= R ξ,t r N R = a n n =1 e λ n t N τ = a n n =1 e λ nβ N = a n n =1 e λ ξ n τ r How can we extend this to temperature changes?

Defining a new response function M p ( t) p ( T,t 2 ) p T 2, p( T 2,0) p T 2, for T changes T 2 T 1 M has the same range as R, i.e. t = 0, M p = 1 and if t =, M p = 0. Using p( T)= p eq ( T)+α s ( T)= p( T 1 )+α L ( T T 1 )+α s ( T) And the conditions: t = 0, (0) = T 1 and ( ) = T 2 M p we becomes M p ( t)= T t f T 2 T 1 T 2

Narayanaswamy assumed that M p (t) obeys TRS! How? dξ = τ r [ ] dt Integrating this from 0 to t yields ξ = τ T t τ r t t dt' dt'= τ r 0 τ T t' 0 τ T t' [ ] [ ] M p in terms of the reduced time ξ M p ( t)= T t f T 2 T 1 T 2 M p ( ξ)= T ξ f T 2 T 1 T 2 ( ξ) T 2 = M p ( ξ) T While p( T,t)= p eq ( T)+α s ( t) T p T,ξ = p eq ( T)+α s ( ξ) T p( T 2,ξ)= p( T 2, ) α s TM p ( ξ)

Episode III: Revenge of the ξ To complete the derivation, imagine that the temperature is changed from some initial value of T o to some final value T in a series of N steps, i.e. T = T 0 + T 1 + T 2 +...+ T N = T 0 + T i N i=1 T 0 T 1 T 2 How can be extend (ξ) and p(t,ξ) to multiple temperature steps? T 3 p( T 2,ξ)= p( T 2, ) α s TM p ( ξ) t 1 t 2 t 3 p( T,ξ)= p( T, ) α s T 1 M p ( ξ ξ 1 )+... α s T N M p ( ξ ξ N ) N p( T,ξ)= p( T, ) α s T i M p ξ ξ i i=1

Using the chain rule and rewriting T i in terms of ξ yields T i = T ξ ξ i ξ i dt = dt dξ dξ N p( T,ξ)= p( T, ) α s T i M p ξ ξ i N p( T,ξ)= p( T, ) α s M p ξ ξ i i=1 i=1 T ξ ξ i ξ i ξ p( T,ξ)= p( T, ) α s M p ξ ξ' 0 dt dξ' dξ'

Likewise, the equation for fictive temperature becomes ( ξ) T 2 = M p ( ξ) T N = T T i M p ξ ξ i i=1 N = T M p ξ ξ i i=1 T ξ ξ i ξ i ξ = T M p ξ ξ' 0 dt dξ' dξ'

Recall in the last lecture, we stated that the fundamental flaw in Tool s equation is that it only has one relaxation time. Let s pretend that M p (ξ) is given by only one relaxation time, i.e. M p ( ξ)= e ξ τ r Substituting this M into Narayanaswamy s equation for the evolution of yields ξ = T M p ξ ξ' or 0 dt dξ' dξ'= T ξ e 0 ( ξ ξ ') τ r dt dξ' dξ' T = e ξ 0 ( ξ ξ ') τ r dt dξ' dξ' Taking the derivative with respect to ξ gives d dξ = 1 τ r e ( ξ ξ ') ξ τ r 0 dt dξ' dξ' d dξ = T τ r Tool s eq.

What did Narayanaswamy use for τ? τ p = τ 0 exp x H RT + ( 1 x ) H R where 0 < x < 1 Arrhenius term A dependence just like Tool! The Tool-Narayanaswamy-Moynihan equations are ξ p( T,ξ)= p( T, ) α s M p ξ ξ' 0 dt dξ' dξ' and = T M p ξ ξ' ξ 0 dt dξ' dξ' and some form for t p such as τ p = τ 0 exp x H RT + ( 1 x ) H R

DSC: Differential Scanning Calorimetry as a Black Box. By a black box, I mean 1) what are the inputs and 2) what is the output. Ignore the details of how the apparatus works. DSC Q( t) i.e. dq dt Unknown sample T( t) i.e. dt dt The output is the Q vs. t required to produce the specified T vs. t A given T vs. t is specified The ratio of the output to input is dq dt dt dt = dq dt = C p

How does a DSC work? The philosophy of the device. output Q t thermocouple A given V corresponds to a T Q = I X V X dt T X sample X T unknown T known Al V Q = I Al V Al dt Q = m Al c Al T Al I X V I Al input T t Feedback mechanism. If the V doesn t correspond to the correct T, the I X is changed.

The Empty Al pan acts as the reference sample Sealed Al pans containing the samples

Pans go in here

Before we explain how to measure and T g using a DSC, lets first examine some typical C p vs T results A) C p vs. or a linear cooled liquid i.e. a down scan T i α L = α V +α S = dh dt = C L P C P L t H 3 2 1 3 2 1 C P g T T α g = α V = dh dt = C g p < C P L

B) Linear heating a glass that was linearly cooled i.e. an up scan 1 2 3 4 T i H T t C P L C P g As the glass is relaxing toward the super cooled equilibrium line, heat is given off i.e. H is decreasing so this region is exothermic. T

C) A liquid cooled by a down quench T i = inal t 2 1 2 1 C P L H C P g inal T i = inal T i =

D) A linear up scan on an annealed glass T i t C P L H C P g T T g

What information does a C p vs T graph provide? Recall that C p = dh dt C p dt = dh T 2 C p T 1 T 1 T 2 dt = dh = H 2 H 1 = H If the system is a glass T 1 and a liquid at T 2, then H = H L -H g. How can we use this to find and T g? For example, how do you measure the and T g of a quenched glass?

Yuanzheng Yue s Enthalpy-Matching Method 1) Make a glass and quench it. The cooling rate and are unknown. What is the of this quenched glass? 2) Place a sample of the quenched glass into a DSC and heat the sample up to the liquid state at some fixed linear rate say 20 0 C/min or 10 0 C/min. Call the C p for this first upscan C p1. 3) Cool the liquid at the the same linear rate, i.e. say 20 0 C/min, to room temperature. 4) Reheat the cooled glass sample using at the same linear rate of 20 0 C/min back up to the liquid state. Call the C p for this second upscan C p2. The graph for C p2 will not have a severe of a dip since the glass has relaxed. 5) Graph of C p1 and C p2 vs. T curves.

H upscan 1 upscan 2 t

Applying Yue s technique is easy in practice. We ll set it up in steps. Why the technique works requires more effort. I ll explain what to do first before I give the explanation. First, calculate the integral C p2 is insensitive to since the glass was brought to the liquid state on the first upscan. T g 2 1 A C p C P T c 2 C p dt Clearly, this is just the area between the second and first upscans. C p C p 1 This dip will deepen if is higher since the glass will relax more on the first upscan. T c T e

Second, calculate the integral B C p,l C P,g T g dt The C P,g is the C P curve for the glass. It is found by extrapolating the C P2 curve before T g. To extrapolate the C P,g curve use the following fit C p,g = a + bt + c T 2 + d T 0.5 where the a, b, c and d are constants that must be determined experimentally T G C p C p 2 C p,l T G is given by the following method. Find the inflection point on the C P2 curve and draw a tangent. The T at which it intercepts C P,g is T g. C p,g B is the area of this trapezoid C p 1 T c

It turns out that integrals A and B are equal A = B 2 1 ( C P C P ) T c T e dt = C C P,L P,g T g dt To find, change the upper limit in the right integral until the two integrals are equal. When they equal, that value is! WHY????

To understand why these two integrals are equal, let s examine each integral separately. Start with B. B C P,L C P,g dt Recall from previous lectures that α p - α g = α s where α P = C P T g and α g = C g in our case. The structure/configuartion of the liquid that is quenched will change from to the T g. Past T g the relax times are too large for any appreciatable relaxation B C P,S dt = H structure to occur. Above the liquid is still in equilibrium. T g Further, H = E + p V and most of H comes from E since V is small compared so H structure E structure

Now let s consider the left integral A. T e 2 1 A C p C P T c dt Below T c both C p1 and C P2 are identical. Recall that the slopes of p vs T graphs for low T were all identical! Above T e, both C p1 and C P2 are identical since they are in the both liquids. The vibrational contributional to C p1 and C p2 are identical at a given T. Therefore, the vibrational contributions cancel and all that is left is the contribution from structural changes. Note that if the upper limit of this integral was extended to, the integral would not since C p1 = C P2 in the liquid region. Therefore, A is also equal to H structure. A = B Yue is very clever! This is an active area of work!!!!!!!