UNIVERSITI PUTRA MALAYSIA PREPARATION AND CHARACTERIZATION OF HIGH- DENSITY POLYETHYLENE/POLYSTYRENE/CLAY NANOCOMPOSITES SUSSAN AZIZY FS 2011 22
PREPARATION AND CHARACTERIZATION OF HIGH- DENSITY POLYETHYLENE/POLYSTYRENE/CLAY NANOCOMPOSITES BY SUSSAN AZIZY Thesis Submitted to the School of Graduate Studies, Universiti Putera Malaysia, in Fulfillment of the Requirements for the Master of Science January 2011
Abstract of thesis presented to the Senate of in fulfillment of the requirement for the degree of Master in Science PREPARATION AND CHARACTERIZATION OF HIGH -DENSITY POLYETHYLENE/ POLYSTYRENE/CLAY NANOCOMPOSITES By SUSSAN AZIZY January 2011 Chairman: Professor Wan Md Zin Wan Yunus, PhD Faculty: Science Polymer/clay nanocomposites, materials composed of polymer matrices and clay particles with which at least one dimension of the clay particles is in the nanometer range. The nanocomposites exhibit significant improvement of some properties compared to those of the original polymers. Blend of polyethylene (PE) and polystyrene (PS) are widely used in industry but suffer from some drawbacks such as low toughness and low service temperature. This work is an attempt to overcome the disadvantages of high density polyethylene/polystyrene (HDPE/PS) blends through the addition of clay by melt blending to produce HDPE/PS/clay nanocomposites. II
In order to improve compatibility between polymer and clay particles, sodium montmorillonite (Na-MMT) was modified by octadecylamine (ODA) to produce octadecylamine montmorillonite (ODA-MMT). Preparation of the nanocomposites was carried out by melt blending of the ODA-MMT and the HDPE/PS blends in the ratio of 80/20 using an internal mixer. The nanocomposites were characterized using transmission electron microscopy (TEM), x-ray diffraction (XRD), scanning electron microscopy (SEM), thermogravimetric analysis (TGA) and tensile testing. The x-ray data and TEM images of the nanocomposites exhibit that the polymer has been intercalated into MMT layers. The tensile strength and tensile modulus of the nanocomposites improve with the increase of organoclay content. Meanwhile, the percentage of elongation at break decreases with the addition of the filler. TGA results show thermal stability of the nanocomposites improves with the increase of organoclay content of up to 5.00 wt% compared to that of the polymer blend. The SEM micrographs reveal that the presence of organoclay slightly promotes the miscibility of the polymer phases and somewhat decreases the flexibility of nanocomposite. In order to improve further HDPE/PS nanocomposite properties, PE-gr-MA was added into the composites. The optimum concentration of PE-gr-MA, based on x-ray data and maximum tensile properties was 1.00 wt%. The x-ray and TEM results of the nanocomposites reveal that the nanocomposites have intercalated structure. The thermal stability and tensile properties of nanocomposites are enhanced compared to III
that of the original nanocomposites. The SEM micrographs show that the presence of PE-gr-MA greatly increases miscibility but decreases the flexibility of the nanocomposites. IV
Abstrak tesis yang dikemukakan kepada Senat sebagai memenuhi keperluan untuk ijazah Master Sains PENYEDIAAN DAN PENCIRIAN- POLIETILENA KETUMPATAN TINGGI/POLISTIRENA/TANAH LIAT NANOKOMPOSIT Oleh SUSSAN AZIZY January 2011 Pengerusi: Professor Wan Md Zin Wan Yunus, PhD Fakulti: Sains Polimer nanokomposit adalah komposit yang disediakan dari polimer dan tanah liat, dimana sekurang-kurangnya satu dimension tanah liat adalah berukuran nanometer. Nanokomposit biasanya mempamerkan ciri-ciri yang lebih baik berbanding dengan polimer asal. Adunan polietilena (PE) dan polistirena (PS) digunakan dengan meluas dalam industri tetapi mempunyai kelemahan seperti mempunyai kekuatan dan suhu penggunaan yang rendah. Kajian ini adalah usaha untuk mengatasi keburukan adunan HDPE/PS melalui pembentukan nanokomposit dengan kaedah pengadunan leburan. Untuk memperbaiki kebolehcampuran antara polimer dan tanah liat, natrium montmorilonit (Na-MMT) telah diubahsuai dengan oktadesilamina (ODA) untuk V
menghasilkan montmorilonit oktadesilamina (ODA-MMT). Kemudian nanokomposit disediakan dari ODA-MMT dan HDPE/PS pada nisbah 80/20 dengan menggunakan pengadun dalaman. Nanokomposit dicirikan dengan menggunakan mikroskopi penghantaran elektron (TEM), belauan sinar-x (XRD), mikroskopi pengimbasan elektron (SEM), analisis termogravimetri (TGA) dan ujian ketegangan. Data x-ray dan mikrograf TEM nanokomposit menunjukkan bahawa polimer telah disisipkan ke dalam lapisan MMT. Kekuatan tegangan dan modulus tegangan nanokomposit meningkat dengan penambahan kandungan tanah liat organik. Sementara itu, pemutusan pemanjangan mengecil dengan kenaikan kandungan pengisi. Keputusan TGA menunjukkan kestabilan haba nanokomposit menaik dengan peningkatan kandungan tanah liat organik sehingga 5.00 wt% berbanding dengan adunan polimer asal. Mikrograf SEM mendedahkan kehadiran tanah liat organik meninggikan kebolehcampuran antara muka polimer. Untuk meningkatkan lagi ciri-ciri nanokomposit, polietilena bercangkukan malik anhidrid (PE-gr-MA) digunakan dalam penyediaan komposit. Berdasarkan data x-ray dan ciri-ciri tegangan maksimum, 1.00 wt% PE-gr-MA adalah memadai untuk menghasilkan nanokomposit yang terbaik di mana kestabilan haba dan ciri-ciri tegangan nanokomposit ditingkatkan berbanding dengan nanokomposit asal. Mikrograf SEM menunjukkan kehadiran PE-gr-MA meningkatkan meninggikan kebolehcampuran antara muka polimer tetapi mengurangkan kebolehlenturan. VI
ACKNOWLEDGEMENTS Praise and gratitude be to ALLAH, almighty, without whose gracious help it would have been impossible to accomplish this work. I would like to express my sincere gratitude to my supervisor Prof. Dato Dr. Wan Md Zin Wan Yunus, who taught me not only analytical and polymer chemistry, but also about patience and perseverance. Thanks for all your time and advises. As such, I want to express gratitude to members of supervisory committee, Assoc. Prof. Dr. Mansor bin Ahmad and Assoc. Prof. Dr. Mohamad Zaki Ab. Rahman for their guidance and constant support through the research. I admire their devotion to science. I also thank to my research group, who shared with me not only their knowledge, also the laboratory space. In addition, I am also very grateful to my family, especially my husband for everything. In gratitude, finally I want to express to all the staff and lecturer of Department of Chemistry, Faculty of Science and that gave me the opportunity to study. I will fondly remember your support, knowledge, assistance, advice, and teaching. I thank the administrators, the Dean and staffs of the chemistry department for the assistance provided throughout the duration of my study at UPM. VII
I certify that an Examination Committee has met on 14.1.2011 to conduct the final examination of Sussan Azizy on her Master of Science thesis entitled Preparation and Characterization of High Density-Polyethylene/Polystyrene Blend/Clay Nanocomposites in accordance (Chairman) with Universiti Pertanian Malaysia (Higher Degree) Act 1980 and Universiti Pertanian Malaysia (Higher Degree) Regulations 1981. The Committee recommends that the student be awarded the Master of Science. Member of the Examination Committee were as follows: Md. Jelas Haron, PhD Professor Faculty of Science Nor Azowa Ibrahim, PhD Doctor Faculty of Science (Internal Examiner) Sidik Silong, PhD Associate professor Faculty of Science (Internal Examiner) Ishak Ahmad, PhD Associate professor Faculty of Science and Technology Universiti Kebangsaan Malaysia (External Examiner) HASANAH MOHD.GHAZALI, PhD Professor and Deputy Dean School of Graduate Studies Date VIII
This thesis was submitted to the Senate of and has been accepted as fulfillment of the requirement for the degree of Master of Science. The members of the Supervisory Committee were as follows: Wan Md Zin Wan Yunus, PhD Professor Faculty of Science (Chairman) Mohd Zaki Ab.Rahman, PhD Associate Professor Faculty of Science (Member) Mansor HJ.Ahmad, PhD Associate Professor Faculty of Science (Member) HASANAH MOHD.GHAZALI, PhD Professor and Dean School of Graduate Studies Date: 14 January 2011 IX
DECLARATION I declare that the thesis is my original work except for quotation and citation which have been dully acknowledged. I also declare that it has not been previously, and is not concurrently, submitted for any other degree at or at any other institution. SUSSAN AZIZY Date: 14 January 2011 X
TABLE OF CONTENTS ABSTRACT ABSTRAK ACKNOWLEDGEMENTS APPROVAL DECLARATION LIST OF TABLES LIST OF FIGURES LIST OF ABBREVIATIONS CHAPTER 1 INTRODUCTION 1.1 General Background 1 1.2 Research Approach 5 1.3 Objectives 5 2 LITERATURE REVIEW 2.1 Polyethylene 7 2.2 Polystyrene 8 2. 3 Polyethylene/Polystyrene Blend 9 2.4 Structure and Properties of Layered Silicate 11 2.5 Nanocomposites 13 2.6 Polymer Layered Silicate (PLS) Nanocomposites 14 2.6.1 Preparation of Polymer Layered Silicate 17 (PLS) Nanocomposites 2.6.2 Characterization of Polymer Layered Silicate (PLS) Nanocomposites 19 2.7 Polyethylene/Clay Nanocomposites 28 2.8 Polystyrene/Clay Nanocomposites 31 2. 9 Polymer Blends Based on Polyethylene/Clay Nanocomposites 33 Page II V VII VIII XIII XIV XV XVIII 3 MATERIALS AND METHODS XI
3.1 Materials 36 3.2 Preparation of Octadecyl Ammonium 36 Montmorillonite (ODA-MMT) 3.3 Preparation of HDPE/PS Blend 37 3.4 Preparation of HDPE/PS/Clay Composites 38 3.5 Preparation of HDPE/PS/Clay Composites with PEgr-MA 39 3.6 Characterization of Clay and HDPE/PS/Clay 40 Composites 3.6.1 X-Ray Diffraction (XRD) 40 3.6.2 Transmission Electron Microscopy (TEM) 40 3.6.3 Fourier Transforms Infrared (FTIR) 41 Spectroscopy 3.6.4 Thermogravimetric Analysis (TGA) 41 3.6.5 Tensile Properties Measurement 41 3.6.6 Scanning Electron Microscopy (SEM) 42 4 RESULTS AND DISCUSSION 4.1 Preparation of Organo-Montmorillonite (ODA-MMT) 43 4.2 Characterization of Organo-Montmorillonite (ODA- MMT) 43 4.2.1 X-Ray Diffraction Analysis 44 4.2.2 Fourier Transform Infrared (FTIR) 45 Spectroscopy 4.2.3 Thermogravimetric Analysis 48 4.3 Characterization of HDPE/PS/Clay Composites 51 4.3.1 X-Ray Diffraction Analysis 51 4.3.2 Transmission Electron Microscopy (TEM) Analysis 58 4.3.3 Scanning Electron Microscopy (SEM) 65 Analysis 4.3. 4 Tensile Properties 73 4.3.5 Thermogravimetric Analysis (TGA) 81 5 CONCLUSIONS AND FURTHER STUDY 5.1 Conclusions 90 5.2 Recommendations for Further Study 93 REFERENCES 94 BIO DATA OF STUDENT 106 XII