EXPERIMENTAL STUDY ON YOUNG S MODULUS E OF A POLYMER COMPOSITE REINFORCED BY NANO TITANIUM DIOXIDE PARTICLES

Similar documents
SOME RESEARCH ON FINITE ELEMENT ANALYSIS OF COMPOSITE MATERIALS

A RESEARCH ON NONLINEAR STABILITY AND FAILURE OF THIN- WALLED COMPOSITE COLUMNS WITH OPEN CROSS-SECTION

CHAPTER 4 MODELING OF MECHANICAL PROPERTIES OF POLYMER COMPOSITES

CHEM-C2410: Materials Science from Microstructures to Properties Composites: basic principles

Chapter Two: Mechanical Properties of materials

12/8/2009. Prof. A.K.M.B. Rashid Department of MME BUET, Dhaka

Samantha Ramirez, MSE. Stress. The intensity of the internal force acting on a specific plane (area) passing through a point. F 2

Kendra Erk is an Assistant Professor in the School of Materials Engineering at Purdue University in West Lafayette, Indiana.

STANDARD SAMPLE. Reduced section " Diameter. Diameter. 2" Gauge length. Radius

4.MECHANICAL PROPERTIES OF MATERIALS

Effect of electron-beam irradiation on the Mechanical properties of Poly (Ethylene-co- Vinyl Acetate) (EVA) - PPy polymer blends

N = Shear stress / Shear strain

MECE 3321 MECHANICS OF SOLIDS CHAPTER 3

Unified Quiz M4 May 7, 2008 M - PORTION

Module III - Macro-mechanics of Lamina. Lecture 23. Macro-Mechanics of Lamina

NORMAL STRESS. The simplest form of stress is normal stress/direct stress, which is the stress perpendicular to the surface on which it acts.

Introduction to Engineering Materials ENGR2000. Dr. Coates

6.4 A cylindrical specimen of a titanium alloy having an elastic modulus of 107 GPa ( psi) and

Module 7: Micromechanics Lecture 34: Self Consistent, Mori -Tanaka and Halpin -Tsai Models. Introduction. The Lecture Contains. Self Consistent Method

Buckling Behavior of 3D Randomly Oriented CNT Reinforced Nanocomposite Plate

THEME IS FIRST OCCURANCE OF YIELDING THE LIMIT?

Theory at a Glance (for IES, GATE, PSU)

Analysis of Flexural Properties of Carbon Fiber Reinforced / E-Poxy Composite Material

Hydrothermal ageing effects on flexural properties of GFRP composite laminates

UNIVERSITY OF SASKATCHEWAN ME MECHANICS OF MATERIALS I FINAL EXAM DECEMBER 13, 2008 Professor A. Dolovich

Theoretical and Numerical Vibration Investigation Study of Orthotropic Hyper Composite Plate Structure

Strain Gauges and Accessories

A CRITERION OF TENSILE FAILURE FOR HYPERELASTIC MATERIALS AND ITS APPLICATION TO VISCOELASTIC-VISCOPLASTIC MATERIALS

Dynamic analysis of Composite Micro Air Vehicles

EFFECT OF RETROFITTING ON FLEXURAL RIGIDITY OF RECTANGULAR FRP PLATES

Flexural properties of polymers

Non-conventional Glass fiber NCF composites with thermoset and thermoplastic matrices. F Talence, France Le Cheylard, France

UNIT I SIMPLE STRESSES AND STRAINS

Characterisation Programme Polymer Multi-scale Properties Industrial Advisory Group 22 nd April 2008

DEFORMATION CAPACITY OF OLDER RC SHEAR WALLS: EXPERIMENTAL ASSESSMENT AND COMPARISON WITH EUROCODE 8 - PART 3 PROVISIONS

CHEM-E2200: Polymer blends and composites Fibre architecture and principles of reinforcement

Coupling of plasticity and damage in glass fibre reinforced polymer composites

Strength of Material. Shear Strain. Dr. Attaullah Shah

MESH MODELING OF ANGLE-PLY LAMINATED COMPOSITE PLATES FOR DNS AND IPSAP

Outline. Tensile-Test Specimen and Machine. Stress-Strain Curve. Review of Mechanical Properties. Mechanical Behaviour

DRAPING SIMULATION. Recent achievements and future trends. Dr. Sylvain Bel LGCIE University Lyon 1

TABLE OF CONTENTS. Mechanics of Composite Materials, Second Edition Autar K Kaw University of South Florida, Tampa, USA

Development of a code to generate randomly distributed short fiber composites to estimate mechanical properties using FEM

ASPECTS CONCERNING TO THE MECHANICAL PROPERTIES OF THE GLASS / FLAX / EPOXY COMPOSITE MATERIAL

ME 243. Mechanics of Solids

This is the accepted version of a paper presented at 2014 IEEE Electrical Insulation Conference (EIC).

Analysis of high loss viscoelastic composites

ME 2570 MECHANICS OF MATERIALS

Enhancing Prediction Accuracy In Sift Theory

The influence of fiber undulation on the mechanical properties of FRP-laminates. Christian Fiebig, Michael Koch

Effects of Core Softness and Bimodularity of Fibreglass Layers on Flexural Stiffness of Polymer Sandwich Structures

Metric (S.I. Units System) English (U.S. Units System) Method PHYSICAL

PREDICTION OF OUT-OF-PLANE FAILURE MODES IN CFRP

Mechanical Properties

International Journal of Pure and Applied Sciences and Technology

MACROSCALE EXPERIMENTAL EVIDENCE OF A REDUCED- MOBILITY NON-BULK POLYMER PHASE IN NANOTUBE- REINFORCED POLYMERS

STUDY OF TERMOPHYSICAL PARAMETERS OF HARDENED POLYURETHANE FILLED BY SINGLE WALLED CARBON NANOTUBES. Karol KOVÁČ

SOME RESEARCH ON FINITE ELEMENT ANALYSIS OF COMPOSITE MATERIALS

Mechanical properties 1 Elastic behaviour of materials

Professor Nguyen Dinh Duc

Response of Carbon Nanotube (CNT) Ply Subjected to a Pulsed Magnetic Field

Effects of geometry and properties of fibre and matrix on overall. composite parameters

Analysis of contact deformation between a coated flat plate and a sphere and its practical application

Load Cell Design Using COMSOL Multiphysics

BE Semester- I ( ) Question Bank (MECHANICS OF SOLIDS)

A multiscale approach for composite materials as multifield continua

GB/T / ISO 527-1:1993

CALCULATION OF A SHEET PILE WALL RELIABILITY INDEX IN ULTIMATE AND SERVICEABILITY LIMIT STATES

Job No. Sheet No. Rev. CONSULTING Engineering Calculation Sheet

DEVELOPMENT OF SOPHISTICATED MATERIALS USING THE COMPUTER SIMULATION

Change in physico-mechanical and thermal properties of polyamide / silica nanocomposite film

The objective of this experiment is to investigate the behavior of steel specimen under a tensile test and to determine it's properties.

Stress-Strain Behavior

S E A L E D F L A T E X P A N S I O N J O I N T T A P E S

Effect of Specimen Dimensions on Flexural Modulus in a 3-Point Bending Test

1. A pure shear deformation is shown. The volume is unchanged. What is the strain tensor.

Supplementary Figures

Engineering Solid Mechanics

Prediction of Elastic Constants on 3D Four-directional Braided

Nanoindentation for Characterizing Wood & Related Systems

Fig. 1. Circular fiber and interphase between the fiber and the matrix.

Studies on Furan Polymer Concrete

PRESSURE VESSELS & PRESSURE CABINS FOR BLENDED WING BODIES

Keysight Technologies Instrumented Indentation Testing with the Keysight Nano Indenter G200. Application Note

Failure analysis of serial pinned joints in composite materials

IJSER 1. INTRODUCTION. M.Elhadary

Thermoelastic test results

OPTIMAL FIBER PLACEMENT INCLUDING EFFECTS OF EMBROIDERY

SIMULTANEOUS MEASUREMENT OF APPARENT THERMAL DIFFUSIVITY AND DISTORTION OF COMPOSITES AT HIGH TEMPERATURE

MODELING AND FEM ANALYSIS OF DYNAMIC PROPERTIES OF THERMALLY OPTIMAL COMPOSITE MATERIALS

Pharmaceutical compounding I Colloidal and Surface-Chemical Aspects of Dosage Forms Dr. rer. nat. Rebaz H. Ali

Mechanical Properties of Polymers. Scope. MSE 383, Unit 3-1. Joshua U. Otaigbe Iowa State University Materials Science & Engineering Dept.

Multi-level seismic damage analysis of RC framed structures. *Jianguang Yue 1)

Measurement of deformation. Measurement of elastic force. Constitutive law. Finite element method

Mechanical Properties of Materials

MATERIAL PROPERTIES. Material Properties Must Be Evaluated By Laboratory or Field Tests 1.1 INTRODUCTION 1.2 ANISOTROPIC MATERIALS

Name :. Roll No. :... Invigilator s Signature :.. CS/B.TECH (CE-NEW)/SEM-3/CE-301/ SOLID MECHANICS

In Situ Ultrasonic NDT of Fracture and Fatigue in Composites

Thermo-Mechanical Response of Functionally Graded Materials for Extreme Environments

Modeling of Composite Panel Under Fire and Compression

Transcription:

Vietnam Journal of Mechanics, VAST, Vol. 34, No. (202), pp. 9 25 EXPERIMENTAL STUDY ON YOUNG S MODULUS E OF A POLYMER COMPOSITE REINFORCED BY NANO TITANIUM DIOXIDE PARTICLES Nguyen Dinh Duc, Dinh Khac Minh 2 University of Engineering and Technology, VNU 2 Shipbuilding Science and Technology Institute Abstract. There are many formulas proposed by different authors in order to determine elastic modules for composite filler particles. This article aims to present the experiment s results and to review some formulas for determining Young s modulus of elasticity E of the polyester filler titanium dioxide particles composite. The results showed that there was a relatively good fit between theory and practice of some formulas. Keywords: Composite, polyester, titanium dioxide particles TiO 2, Young s modulus E.. INTRODUCTION Composite material consists of two or more distinct components to obtain a new material with better properties. Such components include matrix material and filled materials including fiber, fabric, particles, and so on. The matrix material aims to ensure the linkages among all the composite components, which will resist all external acting on the composite including heating, physical, and chemical loads, while the filled components are used to improve the mechanical properties (stiffness and strength) of the composite [, 2, 3]. The composite reinforcement components typically are composed of fiber, fabric, or particles. The fibers and fabrics increase the bearing capacity of the composite structure, while the particles often reduce crack, plastic deformation and increase the waterproofing capacity. Hence, the combination of fiber and particles in the composite material is able to make the composite product more perfect and meet the requirements of modern technology [4, 5, 6, 7]. Recently, the reinforce of polymers using piezoelectric particles, ferromagnetic particles, titanium dioxide particles,... not only increases the strength of the material but also makes the composite product own its new physical characteristics. Therefore, the authors are interested in studying the polymer composites reinforced by additional particles in this study [4, 5, 7]. When using composite materials, we need to determine their mechanical and physical properties, and also to find out their elastic module and Poisson s ratio that are the most significant mechanical properties of composite material. Composite with filled particles is often considered as an isotropic homogeneous elastic material, and it has two

20 Nguyen Dinh Duc, Dinh Khac Minh independent elastic constants, including Young s modulus (E) and Poisson s ratio. At present, many authors have proposed the different formulas to determine Young s modulus E of composites. In the article [5], the authors empirically tested the modulus E to the polystyrene and titanium dioxide particles composite. This article presents the results of an experimental testing for determining the Young s modulus of the polyester and titanium dioxide particles composite. 2. DETERMINATION OF YOUNG S MODULUS OF COMPOSITE MATERIALS Nowadays, many authors have stated formulas for determining Young s modulus of the particles composite [4, 5, 6]. We can summarize that currently there are three approaches for determining the elastic modules of composite material including experiments, inductive methods, and using mechanical models. The details of each approach are presented as the following: - The experimental approach. The advantage of this method is able to determine accurately the elastic modulus of composite. However, the main disadvantage of this method is that it does not reflect the influence of material composition on the composite material because composite is material comprised a variety of components. - The inductive methods. Based on the repeated experiments, the authors can predict the rules and give the formula for determining the elastic module E of the material. This approach is used more effectively with the materials which are surveyed, but less suitable for other materials. - Using mechanical models. In the mechanical model, the particles are usually the spherical particles. The advantage of this method is easy to determine the relationship between the components of composite materials and elastic modulus. Therefore, we can also calculate and predict their values which are a basis for calculating and optimizing the design of the characteristics for new material. However, the results calculated by the mechanical model depend on the model of calculation and such results may vary according to different composites. There are some popular formulas for determining Young s modulus of the composite filler particles as follows: i) Einstein and Guth []: ii) Guth [2]: E E E m ( +, 25 ). () E G E m ( + 2, 5 + 4, ξ 2 a). (2) iii) Kerner [3]: ] 5 ( ν m ) E K E m [ +, (3) ( )(8 0ν m ) where ν m Poisson s ratio of matrix material. iv) Quemeda [5]: E Q E m. ( 0, 5kξa 2 (4) ),

Experimental study on Young s modulus E of a polymer composite... 2 with k const (k 0.25). v) Thomas [5]: where where vi) Kristensen [6]: E T E m ( + 2, 5ξa + 0, 05ξ 2 a + 0, 00273 exp(6, 6 ) ). (5) E 5 ( ν m ) Ḡ E G m 9 K E Ḡ E 3 K E + Ḡ E, (6) ( G ) a ξ a G m 7 5ν m + (8 0ν m ) G a G m (K a K m )ξ a K E K m + + (K a K m ) ( K m + 4Gm 3 vii) Vanin - Nguyen Dinh Duc [4, 7]: E 9 KḠ 3 K + Ḡ K K m + 4ξ ag m L (3K m ) 4ξ a G ml (3K m ), Ḡ ξ a (7 5ν m)h + ξ a (8 0ν m )H here G m L K a K m G K a + 4G, H a m 8 0ν m + (7 5ν m ) G. m 3 G a In the equations () - (9), the terms E m, ν m, K m G m, G are, respectively, Young s modulus, the Poisson s ratio, volume module and shear modulus of matrix material. The subscript "a" belongs to the particle. In formulas () - (5), is the mass ratio of particle. Other while, ξ a in the formula (6) and (8)-(9) is volume ratio of particle. In our formula (8)-(9) [4, 7], we have taken into account the interaction between particle and matrix material. The values ξ a and is according to volume ratio and mass ratio, which are determined as below: ξ a V a V a + V m m m +, ρ a ρ a + m m + m mρ a + ρ a + m m m m (, ) ) ( ) +ρ a (7) (8) (9) (0)

22 Nguyen Dinh Duc, Dinh Khac Minh We have the correlation between the volume ratio and mass ratio as below: ξ a V a V a + V m + ρ a m m () where V m, V a are volumes of matrix polyester and Titanium oxide, respectively. ρ nd ρ a are densities of matrix polyester and Titanium oxide, respectively. 3.. Making the samples 3. EXPERIMENT AND RESULTS To verify Young s modulus for 3-phase composite, we tested the samples made of polyester AKAVINA and titanium dioxide, having properties shown in Table. Table. Properties of each composite component Composite components Young s modulus E Poisson s ratio ν Matrix polyester AKAVINA (Vietnam),43 GPa 0.345 Titanium dioxide TiO 2 (Australia) 5,58 GPa 0.20 The experiments were done at the Laboratory of Shipbuilding Technology Institute, Nha Trang University. The samples were made according to Vietnamese standard code: TCVN 6282:2008 [8]: - Add titanium dioxide particles to polyester: using magnetic mixer, the needed time for the mixture to be well blended is 5 minutes. The mixture then is poured into a smooth-wall mould. During the hardening process, a vacuum pump is used to remove gas and dust. - Ambient properties: room s temperature was (20±5 0 C), humidity was 65%±20%. - Preliminary checking before test: the mould is removed after 24 hours, the samples have smooth surface and uniform thickness and no void. Fig.. Dimensions of the composite sample The dimension of the sample is given in Fig..

Experimental study on Young s modulus E of a polymer composite... 23 3.2. Property tests The tests were done on HOUNSFEILD H50K-S tester whose maximum tensile load of 50000N (Fig. 2) using BS EN ISO 527-: 997 method. We experimented three cases, when the volume ratios of titanium oxide particles are 5%, 0% and 5% (the corresponding mass ratio is 8%, 3% and 42%). Seven samples are used for each case. Fig. 2. HOUNSFEILD H50K-S Tester - Ambient properties: room s temperature was (20±5 0 C), humidity was 65%±20%. - Test speed: mm/minute - Load range: 20000N - Extension range: 8.000 mm - Gauge length: 50mm 3.3. Post processing The tensile strength is calculated as σ k P F ( N/mm 2), here P is the ultimate tensile load and F is the cross area of the sample. The expression for the composite s Young s modulus E is E l ( ) P ( N/mm 2), F l here, l is the distance between the clamps, P is the variation of load and l is the absolute elongation. Since the number of samples is not large and the deviation between the tests is small, the final result will be calculated as the arithmetic mean of all the tests results, x average x + x 2 + x 3 + x 4 + x 5 + x 6 + x 7 7

24 Nguyen Dinh Duc, Dinh Khac Minh The theoretical results for Young s modulus with different particle volume ratios are given in Table 2. The columns (3), (6) and (9) are correspond to the three experimental values of the particle mass ratio 0.8; 0.3; 0.42. The experimental results are included. Table 2. The theoretical results and experimental results for YoungÒs modulus E with different particle volume ratio E 0 0, 0,8 0,2 0,3 0,3 0,4 0,42 0,5 () (2) (3) (4) (5) (6) (7) (8) (9) E E 430 608.8 746. 787.5 966.3 987.7 245.0 279.0 2323.8 2 E G 430 989. 2693.0 295.5 437.2 4508. 6086. 6467.8 8258.3 3 E K 433 773. 2093.5 2202.0 2753.4 2830.3 3488.6 3656.9 457.9 4 E Q 430 448. 488.2 505.3 6.3 628. 787.5 832.0 2080.0 5 E T 430 95.7 2585.3 2827.8 4363.9 4637.5 846.3 9545.4 2259.0 6 E Kr 430 474.6 53.8 526.6 588.3 596.5 662.5 678.3 753.4 7 E D 430 533.5 624.0 653.6 795.8 84.6 967.9 2005.0 282.4 8 E-Test 626.0 727.2 2052.5 Fig. 3. The experiment results of Young s modulus of the polyester/titanium dioxide composite for different particle mass ratios

Experimental study on Young s modulus E of a polymer composite... 25 Comparisons between the experimental results and the results calculated from formulas () - (6) and (8) of Young s modulus of the polyester composite reinforced with titanium dioxide particles are shown in Table 2 and Fig. 3. 4. CONCLUSION From the theoretical and experimental results represented in Table 2 and Fig. 3, we have some conclusions for the experiment of polyester-titanium dioxides composite as below: When the ratio of particles are small (less than 20%), the calculated results of elastic module E according to the formulas from () to (8)-(9) are quite consistent with the experiment results. The calculated results according to the formulas of Guth (2), Kerner (3) Thomas (5) are different from the experiment results when the ratio of particles is greater than 20%. The formulas for calculation of the Young s modulus values of composite of Einstein & Guth (), Quemada (4), Kristensen (6) and Vanin - Nguyen Dinh Duc (8)-(9) are consistent with the experimental results. In all above formulas for calculation of the Young s modulus values of composite, the formula (8)-(9) is the best consistent with the experiment. In the formula (8)-(9), the authors considered the interaction between particle and matrix polyester. The authors would like to thank the Laboratory of Technology, Shipbuilding Technology Institute of Nha Trang University for its assistance on experiments. REFERENCES [] L. E. Nielson, Mechanics properties of Polymers and Composites, Marcel Dekker, New York, 2 (974). [2] J. A. Manson, L. H. Sperling, Polymer Blends and Composite, Plenum, New York, (976). [3] Shackelford, James F. et al, Materials Science and Engineering Handbook, CRC Press LLC, (200). [4] Vanin G. A., Nguyen Dinh Duc, The theory of spherofibrous composite.: The input relations, hypothesis and models, J. Mechanics of composite materials, 32(3) (996) 29-305. [5] J. A. P. Selvin, Joseph Kuruvilla, Thomas Sabu, Mechanical properties of titanium dioxidefilled polystyrene micro composites, J. Materials letters, 58 (2004) 28-289. [6] R. M. Christensen, Mechanics of composite materials, Joln Wiley and Sons Inc. New York, (979). [7] Nguyen Dinh Duc, Mechanics of nano-composite materials, Journal of Science- Mathematic- Physics, Vietnam National University, Hanoi, 9(4) (2003) 3-8. [8] Vietnamese standards code TCVN 6282:2008 for testing and manufacturing ship made of composite polymer reinforced by glass fibers, Transportation Publishing House, Hanoi, (2008). Received January 9, 20