High Energy Density of All Screen-Printable Solid-State. Microsupercapacitor Integrated by Graphene/CNTs as. Hierarchical Electrodes

Similar documents
Flexible Asymmetrical Solid-state Supercapacitors Based on Laboratory Filter Paper

Supporting Information

Supporting Information

Supplementary Information for

Supporting Information

Construction of Microfluidic-Oriented Polyaniline Nanorod arrays. /Graphene Composite Fibers towards Wearable Micro-

Scalable Preparation of Hierarchical Porous Activated Carbon/graphene composite for High-Performance Supercapacitors

Inkjet Printed Highly Transparent and Flexible Graphene Micro- Supercapacitors

Tailorable and Wearable Textile Devices for Solar Energy Harvesting and Simultaneous Storage

Supporting Information

Flexible Quasi-Solid-State Planar Micro-supercapacitors Based

Supporting Information. Metal-Organic Frameworks Mediated Synthesis of One-Dimensional Molybdenum-Based/Carbon Composites for Enhanced Lithium Storage

Supporting Infromation

Supporting information

Facile synthesis of porous nitrogen-doped holey graphene as an efficient metal-free catalyst for the oxygen reduction reaction

Supporting Information

Hydrothermally Activated Graphene Fiber Fabrics for Textile. Electrodes of Supercapacitors

Facile synthesis of accordion-like Ni-MOF superstructure for highperformance

Supplementary Figure 1 XPS, Raman and TGA characterizations on GO and freeze-dried HGF and GF. (a) XPS survey spectra and (b) C1s spectra.

Supporting Information

Self-assembled pancake-like hexagonal tungsten oxide with ordered mesopores for supercapacitors

Super Flexible, High-efficiency Perovskite Solar Cells Employing Graphene Electrodes: Toward Future Foldable Power Sources

Co-vacancy-rich Co 1 x S nanosheets anchored on rgo for high-efficiency oxygen evolution

Supporting Information. Carbon nanofibers by pyrolysis of self-assembled perylene diimide derivative gels as supercapacitor electrode materials

Efficient Preparation of Large-Area Graphene Oxide Sheets for Transparent Conductive Films

Supporting information

Hierarchically mesoporous carbon nanopetal based electrodes for flexible. Electronic Supplementary Information

Supporting Information

Supporting Information. Integrated energy storage and electrochromic function in one flexible device: an energy storage smart window

Supporting Information. Phenolic/resin assisted MOFs derived hierarchical Co/N-doping carbon

Supporting Information for

Supporting Informantion

Pomegranate-Like N, P-Doped Nanospheres as Highly Active Electrocatalysts for Alkaline Hydrogen Evolution

Large-Scale Multifunctional Electrochromic-Energy Storage Device Based on Tungsten Trioxide Monohydrate Nanosheets and Prussian White

Supporting Information

Electric Power Generation via Asymmetric Moisturizing of Graphene. Oxide for Flexible, Printable and Portable Electronics

Honeycomb-like Interconnected Network of Nickel Phosphide Hetero-nanoparticles

Supplementary Figure S1. AFM image and height profile of GO. (a) AFM image

Supporting Information. Engineering Two-Dimensional Mass-Transport Channels

High-Performance Flexible Asymmetric Supercapacitors Based on 3D. Electrodes

Supplementary Figure 1. (a-b) EDX of Mo 2 and Mo 2

High-performance Supercapacitors Based on Electrochemicalinduced. Vertical-aligned Carbon Nanotubes and Polyaniline

Supporting Information. Cobalt Molybdenum Oxide Derived High-Performance Electrocatalyst

Journal of Materials Chemistry A ELECTRONIC SUPPLEMENTARY INFORMATION (ESI )

General Synthesis of Graphene-Supported. Bicomponent Metal Monoxides as Alternative High- Performance Li-Ion Anodes to Binary Spinel Oxides

Flexible ultrathin micro-supercapacitors based on laser-reduced graphene with superior electrochemical performance and aesthetic property

Supporting Information

Electrospun Mat of Polyvinyl Alcohol/Graphene Oxide for Superior Electrolyte Performance

Supporting Information

Kinetically-Enhanced Polysulfide Redox Reactions by Nb2O5. Nanocrystal for High-Rate Lithium Sulfur Battery

Self-floating nanostructural Ni-NiO x /Ni foam for solar thermal water evaporation

One-pot synthesis of bi-metallic PdRu tripods as an efficient catalyst for. electrocatalytic nitrogen reduction to ammonia

Supporting Information. Polyaniline-MnO 2 nanotubes hybrid nanocomposite as supercapacitor electrode material in acidic electrolyte

A new concept of charging supercapacitors based on a photovoltaic effect

Supporting Information

Materials Chemistry A

Pyridine-functionalized Fullerene Additive Enabling Coordination. Bulk Heterojunction Solar Cells

Facile Synthesis of Hybrid Graphene and Carbon Nanotube as. Metal-Free Electrocatalyst with Active Dual Interfaces for

Mechanically Strong Graphene/Aramid Nanofiber. Power

High Salt Removal Capacity of Metal-Organic Gel Derived. Porous Carbon for Capacitive Deionization

Supporting Information. Co 4 N Nanosheets Assembled Mesoporous Sphere as a Matrix for Ultrahigh Sulfur Content Lithium Sulfur Batteries

Supporting Information. Supercapacitors

Graphene Size-dependent Modulation of Graphene Framework Contributing to Superior. Thermal Conductivity of Epoxy Composite

Supporting Information

Electronic Supplementary Information

Supporting Information. Bi-functional Catalyst with Enhanced Activity and Cycle Stability for. Rechargeable Lithium Oxygen Batteries

Supplementary Information. Scalable Fabrication of High-Power Graphene Micro-Supercapacitors for. Flexible and On-Chip Energy Storage

Supporting information

Supplementary Figures

Supporting Information

Supporting Information

Hydrogenated CoO x Ni(OH) 2 nanosheet core shell nanostructures for high-performance asymmetric supercapacitors

Supporting information

Supporting material. Figures

Revelation of the Excellent Intrinsic Activity. Evolution Reaction in Alkaline Medium

Supporting Information

Cloth for High-Efficient Electrocatalytic Urea Oxidation

Supercapacitor Performance of Perovskite La 1-x Sr x MnO 3

Science and Technology, Dalian University of Technology, Dalian , P. R. China b

Electronic Supplementary Information

Electronic Supplementary Information

Electronic Supplementary Information

Highly Efficient Flexible Perovskite Solar Cells Using Solution-Derived NiO x Hole Contacts

Multiscale honeycomb structured activated carbon from nitrogen containing. mandarin peel: High-performance supercapacitors with extreme cycling

Lotus root-like porous carbon nanofiber anchored with CoP nanoparticles as all-ph hydrogen evolution electrocatalysts

Engineering NiS/Ni 2 P Heterostructures for Efficient Electrocatalytic Water Splitting

Metal Organic Framework-Derived Metal Oxide Embedded in Nitrogen-Doped Graphene Network for High-Performance Lithium-Ion Batteries

High Quality Thin Graphene Films from Fast. Research Center for Applied Sciences, Academia Sinica, Taipei, 11529, Taiwan

Low-cost and high energy density asymmetric supercapacitors based on polyaniline nanotubes and MoO 3 nanobelts

Supplementary Information. Unusual High Oxygen Reduction Performance in All-Carbon Electrocatalysts

SUPPLEMENTARY INFORMATION. Observation of tunable electrical bandgap in large-area twisted bilayer graphene synthesized by chemical vapor deposition

Efficient removal of typical dye and Cr(VI) reduction using N-doped

Supporting Information. Direct Observation of Structural Evolution of Metal Chalcogenide in. Electrocatalytic Water Oxidation

Supplementary Information

bifunctional electrocatalyst for overall water splitting

Perovskite Solar Cells Powered Electrochromic Batteries for Smart. Windows

Carbon-based nanocomposite EDLC supercapacitors

An Advanced Anode Material for Sodium Ion. Batteries

Department of Chemical Engineering, Tsinghua University, Beijing , P. R. China

Highly doped and exposed Cu(I)-N active sites within graphene towards. efficient oxygen reduction for zinc-air battery

Transcription:

Electronic Supplementary Material (ESI) for Journal of Materials Chemistry A. This journal is The Royal Society of Chemistry 2019 Supporting information High Energy Density of All Screen-Printable Solid-State Microsupercapacitor Integrated by Graphene/CNTs as Hierarchical Electrodes Jui-Kung Chih, Anif Jamaluddin #, Fuming Chen^, Jeng-Kuei Chang %, and Ching- Yuan Su #% * Dep. of Mechanical Engineering, National Central University, Tao-Yuan 32001, Taiwan # Graduate Institute of Energy Engineering, National Central University, Tao-Yuan 32001, Taiwan ^ School of Physics and Telecommunication Engineering, South China Normal University, Guangzhou 510006, China % Department of Materials Science and Engineering, National Chiao Tung University, Hsinchu 30010, Taiwan *To whom correspondence should be addressed: (C. Y. Su) cysu@ncu.edu.tw

Table S1. The comparison of BET surface area on ECG and CNTs/ECG. Figure S1. (a) The correlation of the sheet resistance with the various electrode conditions, and (b) the viscosity with increased the ratio of CNTs in ECG/CNTs composites.

Table S2 The parametric study on the geometric dimension of MSCs electrodes MSC devices without Ag current collector Device 1 3 5 6 7 8 9 number Width(W) 4 3 2 1.5 1 0.5 0.4 (mm) Interspace(I) 0.8 (mm) Length(L) 15.2 (mm) Capacitance (mf/cm 2 ) 1.7 1.8 3.4 3.7 4.4 4.7 4.5 MSC devices with Ag current collector Device number Width(W) (mm) Interspace(I) (mm) Length(L) (mm) Capacitance (mf/cm 2 ) 10 11 12 1 0.8 1 1.2 15.2 12.6 12.1 10.4 * Here the two terminal electrodes (T) with the fixed at 2 mm.

Figure S2. (a) CV curves, and (b) the capacitance comparison of the devices with the a different interspace. Figure S3. (a) CV curves, and (b) the capacitance comparison of the devices with and without Ag current collector.

Figure S4. (a) The CV curves for devices with pristine Ag electrode and the ECG/CNTs with and without Ag as a current collector. (b) The CV curves of pristine Ag electrodes at the various scan rate. Figure S5. The adhesive testing on (a-b)the 5M electrolyte and (c-d)the 2M electrolyte.

Figure S6. The XPS C1s core level spectrum on the as-prepared ECG and the conclude C/O ratio, oxygen bonding states. The sheet resistance of ECG film was measured on a glass substrate.

Figure S7. (a) The photo and (b) the OM image of MSCs device after coating electrolyte via screen printing methods. The (c) CV curves (d) EIS profiles of the MSCs device with screen-printed/drop-casted electrolyte. S8: The CV, GCD, EIS curves of MSC devices with optimized conditions A series of electrochemical measurements were performed to evaluate our device by two-electrode configuration. Figure S4a,b,d presented the CV, GCD and EIS curves of all screen-printable MSC, respectively. In Figure. 5a, the curves have a large closed area and near rectangular shape at a scan rate of 5 to 200 mv s -1, indicating the characteristics of electrochemical double-layer capacitive behavior. Also, the GCD curves (Fig. S8b) showed nearly triangular shape at different current densities varying from 0.05 to 0.8 ma/cm 2 and without any visible IR drop. The areal capacitance, calculated from the GCD curves (Fig. S8b), with rate capability was shown in Fig. S8c. Electrochemical impedance spectroscopy (EIS) confirmed the fast ion transport of ECG/CNT electrode which exhibiting a straight line closed the Z' axis at low frequency and a small equivalent series resistance (ESR) of 29.7 Ω in the high-frequency region (Fig. S8d). Note that the non-symmetric GCD curves and the relative lower coulombic efficiency was due to the existence of the internal resistance of ECG/CNTs electrode(eis curves shown in figure 8(c)) and the participation of reaction with oxygen functional groups on ECG. The relatively high charge resistance and functional groups was evidenced by the lower C/O ratio of as-prepared ECG, which seldom reduce its

electrical conductivity(figure S6). Figure S8. (a) CV curves, (b) GCD, (c) the rate capacitance from GCD curves, and (d) EIS profiles of the MSC with optimized conditions. Figure S9. The experimental setup for the bending test of an MSC device, where the radius(r) was defined and estimated.

Figure S10 (a) The correlation between the numbers of the stacking layer and thickness. (b) The corresponding CV curve and (c) the areal capacitance.

Table S3. The performance of the MSCs based on different materials and techniques. material thickness (µm) Electrolyte voltage window specific areal capacitance (mf/cm 2 ) specific stack capacitance (F/cm 3 ) Energy density (mwh/cm 3 ) Power density (W/cm 3 ) Patterning technique ECG/CNTs 1.00±0.3 PVA-H3PO4 (5M) 0-1.0 4.7 (5 mv*s -1 ) 47.0 6.5 0.62 Screen printing (This work) ECG/CNTs with Ag current collector 1.00±0.3 PVA-H3PO4 (2 M) 0-1.0 7.7 (5 mv*s -1 ) 77.3 10.7 3.17 rgo- PEDOT/PSS 1 57.90 PVA-H3PO4 (1.5M) 0-1.0 84.7 (5 mv*s -1 ) 14.6 2.26 1.21* Laser etching EEG 2 0.75 PSSH-H3PO4 0-1.0 0.7 (5 mv*s -1 ) 9.3* 0.64 0.27 Ink-jet printing

MPG 3 0.015 PVA-H2SO4 0-1.0 0.081 (10 mv*s -1 ) 17.9 2.50 495.00 Oxygen plasma etching via mask graphene- CNT 4 0.1 Na2SO4 (1M) 0-1.0 2.2 (0.2 V*s -1 ) 1.1 0.16 115.00 Photolithograph and CVD rgo-cnt 5 0.1 KCl (3M) 0-1.0 5.6 (10 mv*s -1 ) 6.1 0.68 ~77 Photolithograph and electrostatic spray PANI-G 6 5 H2SO4 0-1.0 196 (10 mv/s-1) 377 10.1 10.65 Oxygen plasma etching via ma EG/V2O5 7 0.3 PVA-LiCl 0.-1.0 3.9 (10 mv*s -1 ) 130.7 18.2 235 Oxygen plasma etching

LSG 8 7.6 PVA-H2SO4 0.-1.0 2.3 (16.8 ma*cm -3 ) 3.0 ~0.6 ~200 Laser writing BNG 9 0.008 PVA-H2SO4 0.-1.0 0.3904 (10 mv*s -1 )* 488 ~3.4 ~910 Oxygen plasma etching MnO2/OLC 10 10 PVA-H2SO4 0-0.8 7.0 (5 mv*s -1 ) 7.0 0.98* 0.85* Screen printing PANi 11 0.4 PVA-H2SO4 0-1.0 23.5 (0.1 ma*cm -2 )* 588 82 1250 Photolithography rgo/tio2 12 0.063 EMImNTF2 0-3.0 0.5 (50mV*s -1 ) 84.7 7.7 312 UV reduction

N-doping CVD graphene/ PVA-H3PO4 13 Mg(OH)2/GO 14 20 PVA-H3PO4 0-1.0 37.5 (5 mv*s -1 ) 10 PVA-H2SO4 0-0.8 6.65 (0.1 ma*cm -2 ) 18.75* 2.08 1.6* gravure printing 6.65* 1.41 0.3 gravure printing ECG/CNTs: electrochemical exfoliated graphene/carbon nanotube, EEG: electrochemically exfoliated graphene, B-LIG: boron-doped laser-induced graphene, MnO2/OLC: MnO2/onion like carbon, MPG: methaneplasma reduced graphene, EG/V2O5: exfoliated graphene/v2o5, LSG: laser-scribed graphene, BNG: nitrogen and boron co-doped graphene, PANI-G: polyaniline-functionalized graphene, PANi: polyaniline *Calculated based on the dimensions given in reference if the specific result were not given in the literature.

Reference 1. Y. Liu, B. Weng, Q. Xu, Y. Hou, C. Zhao, S. Beirne, K. Shu, R. Jalili, G. G. Wallace, J. M. Razal and J. Chen, Advanced Materials Technologies, 2016, 1, 1600166. 2. J. Li, S. Sollami Delekta, P. Zhang, S. Yang, M. R. Lohe, X. Zhuang, X. Feng and M. Ostling, ACS Nano, 2017, 11, 8249-8256. 3. Z. S. Wu, K. Parvez, X. L. Feng and K. Mullen, Nat. Commun., 2013, 4, 2487. 4. J. Lin, C. Zhang, Z. Yan, Y. Zhu, Z. Peng, R. H. Hauge, D. Natelson and J. M. Tour, Nano Letters, 2013, 13, 72-78. 5. M. Beidaghi and C. Wang, Advanced Functional Materials, 2012, 22, 4501-4510. 6. Z. S. Wu, K. Parvez, S. Li, S. Yang, Z. Y. Liu, S. H. Liu, X. L. Feng and K. Muellen, Advanced Materials, 2015, 27, 4054-4061. 7. P. Zhang, F. Zhu, F. Wang, J. Wang, R. Dong, X. Zhuang, O. G. Schmidt and X. Feng, Adv Mater, 2017, 29. 8. M. F. El-Kady and R. B. Kaner, Nat. Commun., 2013, 4, 1475. 9. Z.-S. Wu, K. Parvez, A. Winter, H. Vieker, X. Liu, S. Han, A. Turchanin, X. Feng and K. Müllen, Advanced Materials, 2014, 26, 4552-4558. 10. Y. Wang, Y. Shi, C. X. Zhao, J. I. Wong, X. W. Sun and H. Y. Yang, Nanotechnology, 2014, 25, 094010. 11. K. Wang, W. Zou, B. Quan, A. Yu, H. Wu, P. Jiang and Z. Wei, Advanced Energy Materials, 2011, 1, 1068-1072. 12. S. Wang, Z.-S. Wu, S. Zheng, F. Zhou, C. Sun, H.-M. Cheng and X. Bao, ACS Nano, 2017, 11, 4283-4291. 13. Q. Chang, L. Li, L. Sai, W. Shi and L. Huang, Advanced electronic Materials, 2018, 4, 1800059. 14. Z. Qi, H. Lei, C. Quanhong, S. Wangzhou, S. Leo and C. Qi, Nanotechnology, 2016, 27, 105401.