Dielectric characteristion of Benzoyl Glycine crystals

Similar documents
Thermal, electrical and photoconductivity properties of L-leucine hydrobromide (LEHBr): A semiorganic nonlinear optical single crystal

Growth and electrical properties of organic GOA crystals

Electrical properties of allyl thiourea doped KDP single crystals

STUDIES ON MECHANICAL AND ELECTRICAL PROPERTIES OF NLO ACTIVE L-GLYCINE SINGLE CRYSTAL

Chapter 6 ELECTRICAL CONDUCTIVITY ANALYSIS

Investigations on Non Linear Optical Crystal ADP Doped with Inorganic Compounds

Impedance Analysis and Low-Frequency Dispersion Behavior of Bi 4 Ti 3 O 12 Glass

DIELECTRIC AND AC CONDUCTION STUDIES OF LEAD PHTHALOCYANINE THIN FILM

Optical Conductivity and Dielectric Response of an Organic Aminopyridine NLO Single Crystal

AC Conductivity and Dielectric studies of Nickel Selenate Hexahydrate Single Crystal

Fabrício Mendes Souza a * Received: August 17, 2016; Revised: January 03, 2017; Accepted: February 02, 2017 KDP, )H 2

EFFECT OF ZnO ON DIELECTRIC PROPERTIES AND ELECTRICAL CONDUCTIVITY OF TERNARY ZINC MAGNESIUM PHOSPHATE GLASSES

Photoconductivity and IR Studies of 3-Nitroacetanilide Single Crystal : A Potential Organic Non-linear Optical Material

Dielectric Loss Studies and Electronic Properties of Mandelic Acid

Dielectric behaviour and a.c. conductivity in Cu x Fe 3 x O 4 ferrite

Dielectric Relaxation in Cd x InSe 9-x Chalcogenide Thin Films

Structural and Thermal Characterization of Polymorphic Er 2 Si 2 O 7 Asghari Maqsood

PREPARATION & DIELECTRIC STUDY OF UNDOPED SODIUM SILICATE

ANALYSIS OF DIELECTRIC, MODULUS, ELECTRO CHEMICAL STABILITY OF PVP ABSA POLYMER ELECTROLYTE SYSTEMS

AC impedance and dielectric spectroscopic studies of Mg 2+ ion conducting PVA PEG blended polymer electrolytes

CHAPTER-4 Dielectric Study

Transport and Magnetic Properties of La 0.85 Ca Mn 1-x Al x O 3 Manganites

Materials and Devices in Electrical Engineering

Ionic conductivity and hopping rate data for some NASICON analogues

First Order Hyperpolarizability and Homo-Lumo Analysis of L-Arginine Maleate (LArM) by Density Functional Theory Methods

Physical and Dielectric Properties of Silver Lithium Niobate Mixed Ceramic System

Thermal And Dielectric Studies on Beta Alanine Thiourea Oxalate Nlo Single Crystals

Scholars Research Library. Growth, structural, optical, mechanical and electrical properties of amino acid single crystal of γ- glycine

Frequency and Composition Dependence on the Dielectric Properties for Mg-Zn Ferrite.

Synthesis, Structural, Optical, Thermal and Electrical Properties of Urea Sulphamic Acid (USA) Single Crystal

CRYSTAL GROWTH, STRUCTURE AND CHARACTERIZATIONS OF AN ORGANIC OPTICAL L ALANINE OXALATE (LAO)

CHEM Principles of Chemistry II Chapter 10 - Liquids and Solids

CHAPTER 6 DIELECTRIC AND CONDUCTIVITY STUDIES OF ZIRCONIUM TIN TITANATE (ZST)

= (1) V = (12) Å 3 Z =4 Mo K radiation. Data collection. Refinement. R[F 2 >2(F 2 )] = wr(f 2 ) = S = reflections

A Study on the Structural, Electrical and Dielectric Properties of Fluorescein Dye as a New Organic Semiconductor Material

Structural and electrical properties of y(ni 0.7 Co 0.2 Cd 0.1 Fe 2 O 4 ) + (1-y)Ba 0.9 Sr 0.1 TiO 3 magnetoelectric composite

AC CONDUCTIVITY AND DIELECTRIC RELAXATION STUDIES OF SANDSTONE- A CORRELATION WITH ITS THERMOLUMINESCENCE

Chap. 7. Dielectric Materials and Insulation

A.C. Conductivity Measurement on Compressed Pellet of Pyrene

Materials and Devices in Electrical Engineering

International Journal of Scientific & Engineering Research, Volume 4, Issue 8, August ISSN

Electrical Properties of Pure and Glycine added KDP-ADP Mixed Crystals

Electrical Properties

Crystal Growth and Characterization of a Novel Non Linear Optical Single Crystal of Urea Phthalic Acid

Study of Mechanisms of Ion Transport in Ion Conducting Glasses

Chapter 10 Review Packet

Electrical conductivity in new imidazolium salts of dicarboxylic acids

MIT Amorphous Materials

Morphological and Electrical Studies Of Plasticized Biopolymer Electrolytes Based On Potato Starch : NH4Cl

MME 467: Ceramics for Advanced Applications

Nucleation kinetics and theoretical calculation of anorganometalliccadmium thiosemicarbazide bromide Hydrate (TSCCB) nonlinear optical single crystal

2008,, Jan 7 All-Paid US-Japan Winter School on New Functionalities in Glass. Controlling Light with Nonlinear Optical Glasses and Plasmonic Glasses

Electrical Conduction in Ceramic Materials 1 Ref: Barsoum, Fundamentals of Ceramics, Ch7, McGraw-Hill, 2000

Analysis and modelling of dielectric relaxation data using DCALC

Supplementary Figure 1. A photographic image of directionally grown perovskite films on a glass substrate (size: cm).

Name Chemistry Pre-AP. Notes: Solutions

Understanding Solid State Physics Additional Questions. Sharon Ann Holgate

Investigation on physico-chemical properties of semiorganic nonlinear optical L-lysine sulphate single crystal

Electrical material properties

Chapter IV. Ionic contribution to the Dielectric Properties of Nematic Liquid Crystals in Thin Cells

Dielectric behaviour of strontium tartrate single crystals

Supporting information

Substitution Effect on Dielectric Permittivity and AC Conductivity of Bi 2-x (CuPb) x Sr 2 Ca 2 Cu 3 O 10+δ Compound

(Introduction) Linear Optics and Nonlinear Optics

Comments on Growth and characterization of organic nonlinear optical crystal: L-Valinium salicylate (LVS) [Optik 125 (2014) ]

Introduction to Thermoelectric Materials and Devices

TEM CRAMS OF DISTINCTIVE NLO MATERIAL (SECOND HARMONIC GENERATIVE TYPE) BARIUM PARA NITROPHENOLATE(BPNP)

Impedance spectroscopy analysis of double perovskite Ho 2 NiTiO 6

International Journal of ChemTech Research CODEN (USA): IJCRGG ISSN: Vol.8, No.3, pp , 2015

Barrier Layer; PTCR; Diffuse Ferroelectric Transition.

Application of Linear, Nonlinear and Nanoscale Conductivity Spectroscopy for Characterising Ion Transport in Solid Electrolytes

Slide 1. Temperatures Light (Optoelectronics) Magnetic Fields Strain Pressure Displacement and Rotation Acceleration Electronic Sensors

Impedance spectroscopy analysis of Mg 4 Nb 2 O 9 with excess of MgO and different additions of V 2 O 5 for microwave and radio frequency applications.

dc Conductivity and dielectric properties of V 2 O 5 -Bi 2 O 3 -ZnO glass

Solid-State Diffusion and NMR

The Basic Capacitor. Dielectric. Conductors

Relaxor characteristics of ferroelectric BaZr 0.2 Ti 0.8 O 3 ceramics

SYED AMMAL ENGINEERING COLLEGE: RAMANATHAPURAM Dr.E.M.Abdullah Campus DEPARTMENT OF PHYSICS Question Bank Engineering physics II PH6251 (R-2013)

Chapter 10 Liquids and Solids. Problems: 14, 15, 18, 21-23, 29, 31-35, 37, 39, 41, 43, 46, 81-83, 87, 88, 90-93, 99, , 113

sin[( t 2 Home Problem Set #1 Due : September 10 (Wed), 2008

Scholars Research Library

Chemistry Institute B6, SUPRATECS, University of Liège, Sart-Tilman, B-4000 Liège, Belgium b

J. Price, 1,2 Y. Q. An, 1 M. C. Downer 1 1 The university of Texas at Austin, Department of Physics, Austin, TX

International Journal of ChemTech Research CODEN (USA): IJCRGG ISSN: Vol.8, No.1, pp , 2015

Carbonized Electrospun Nanofiber Sheets for Thermophones

Pelagia Research Library

Electrochemical methods : Fundamentals and Applications

Carrier Transport Mechanisms of a-gaas/ n-si Heterojunctions

Conductivity studies of lithium zinc silicate glasses with varying lithium contents

Frequency Dependence of Conductivity Characteristics of Seawater Ionic Solution under Magnetic Field

Chapter 10: Liquids and Solids

PHYSICS. Downloaded From: Time Allowed : 3 Hrs. Max. Marks 60

Supplementary Figures

Ge 3 O 12. C.P. 353, São Cristovão - SE, Brazil b Instituto de Física de São Carlos, Universidade de São Paulo

Chapter 3 Chapter 4 Chapter 5

Physical and dielectric properties of Bi 4 x R x Sr 3 Ca 3 Cu 2 O 10 glasses (x = 0.5 and R = Ag, Ni)

GLASS Asst. Lect. Shireen Hasan

Electro-conductive properties of cadmium octanoate composites with CdS nanoparticles

Optimization of Chemical Bath Deposited Bismuth Sulphide Thin Films on Glass Substrate

Lecture 3 Charged interfaces

Transcription:

Available online at www.scholarsresearchlibrary.com Scholars Research Library Archives of Applied Science Research, 1, (4): 119-17 (http://scholarsresearchlibrary.com/archive.html) ISSN 975-58X CODEN (USA) AASRC9 Dielectric characteristion of Benzoyl Glycine crystals S. Suresh *1, A. Ramanand 1, P. Mani and K. Anand 3 1 Department of Physics, Loyola College, Chennai, India Department of Physics, Hindustan University, Padur, India 3 Department of Physics, Sri Manaula Vinayagar Engineering College, Pondicherry, India ABSTRACT The variation of dielectric constant ε ) and,( ε the dielectric loss (tan δ), and the conductivity (σ ac ) of benzoyl glycine at different temperatures (35 C-135 C) in the frequency range (5 Hz 5 MHz) of the applied alternating current field is analyzed. The dependence of tan δ, ε and σ ac on temperature and frequency of the applied field (5 Hz 5 MHz) is established.the empirical equations obtained fit very well with the experimental data. These equations are suggestive of functional relationship between the dielectric parameters, ε tan δ and σ ac and the temperature and frequency of the applied field. Key words: Solution growth, X-ray diffraction, dielectric constant. INTRODUCTION New molecular organic compounds with one or more aromatic system in conjugated positions leading to highly efficient optical non-linearity have been actively studied for the past two decades [1]. The organic non linear optical materials play an important role in second harmonic generation, frequency mixing, electro-optic modulation, optical parametric oscillation and optical bi-stability []. Recently, an extremely large number of organic compounds with non-localized л-electron systems and a large dipole moment have been synthesized to realize the nonlinear susceptibility compared to the inorganic optical materials [3]. The first observation of SHG in an organic material was reported in 1964 in benzopyrene by Rentzepis and Pao [4].Two years later Orlov [5] reported SHG from hippuric acid. Hippuric acid also called N Benzoyl glycine, is a colorless NLO crystal with chemical formula C6H5CONHCH-COOH [6 7]. It crystallizes in orthorhombic structure with space group P 1 1 1 and lattice parameters a=8.874å, b=1.577å and c=9.117å [8]. Growth of Benzoyl chloride by double diffusion method in silica gel was reported earlier. [9, 1].To enables a material to be potentially useful for NLO applications, the material should be in bul single crystal form. Hence bul single crystals of benzoyl glycine 119

were grown by slow evaporation solution growth technique using N, N-dimethyl formamide as a solvent. The grown crystals were characterized by single crystal XRD analysis, dielectric and conductivity studies. The results are discussed in detail. MATERIALS AND MTHODS The starting material was synthesized according to equation [1] by stoichiometric incorporation of Glycine and Benzoyl chloride which were taen in the appropriate 1:1 ratio.to this 1 calculated amount of NaOH was added and a saturated solution was prepared. The purity of the synthesized salt was further recrystallized using N, N-dimethyl formamide as the solvent. Single crystals of Benzoyl glycine were grown by slow and controlled evaporation of the solvent using a constant temperature bath. The supersaturated solution was ept in a constant temperature bath at 3 C. Crystals obtained by spontaneous nucleation were used as seed crystals. The lattice parameters of the seed crystals were confirmed by single crystal x-ray analysis. These values match well with the reported values. [11].The grown crystal shown in Fig.1. CH NH COOH + C6H 5COCl C H CONHCH COOH NaCl H O 1% NaOH 6 5 + + (1) Fig. 1. BG grown crystal The Dielectric Constant The dielectric constant is calculated using the formula ε =Ct /ε A () Where C is the capacitance (F), t the thicness (m), A the area (m ), ε and the absolute permittivity in the free space having a value of 8.854 1 1 Fm 1. The imaginary dielectric constant ( ε ) of the material is calculated using the relation ε = ε tan δ (3) Where tan δ is the dielectric loss measured directly from the impedance analyzer. The alternating current (ac) conductivity σ ac is calculated using the relation σ ac = πf ε ε tan δ (4) 1

Where f is the frequency of the applied ac field (Hz). The activation energy of the crystal is calculated from an Arrhenius plot of ln σ using the relation [1] σ = σ exp [-E a /T] (5) Where σ is the conductivity at temperature T, E a the activation Energy for the electrical process and the Boltzmann s constant. RESULTS AND DISCUSSION Dependence of Dielectric constant and Dielectric loss on frequency The dependence of the dielectric constant,( ε ) imaginary dielectric constant,( ε ) and dielectric loss (tan δ) on frequency of the applied ac field was studied in the temperature range of 35 C 135 C and frequency range of 5 Hz 5 MHz. The data so obtained are recorded in Tables 1 and. The variation of the dielectric constant with frequency of the applied ac field is shown in Fig..The behavior of the material could be described with respect to frequency intervals, first in the lower frequency range 5Hz 1 Hz and second in the higher frequency range 1 Hz 5 MHz. In the lower frequency range (5 1 Hz), the following points may be noted: (i) At room temperature (35 C), the value of ε is very small, of the order of 487.59, showing hardly any dependence on frequency. At 85 C, the dielectric constant rises to a value of 578.66 at 5 Hz. It however, decreases as the frequency increases to 1 Hz, after which it shows a little dependence on frequency. At 135 C, ε is raised to 611.56 at 5 Hz which starts decreasing with frequency. Particularly after 1 Hz it attains saturation. (ii) In the higher frequency range (1 Hz 5 MHz), the value of the dielectric constant almost attains saturation at all the measured temperatures. From the above discussion it is clear that the dielectric constant of the material is strongly dependent on both temperature and frequency, provided the frequency of the applied ac field is in the lower frequency range of 5Hz-1 KHz. The dielectric constant decreases with frequency and achieves a maximum value of 611.56 at 5Hz, the rate of decrease being maximum at 85 C which is the transition temperature. Dielectric constant Dielectric constant 5 4 3 1 4 6 8 1 Frequency (Hz) Temp 35 C Temp 85 C Temp 135 C Figure. Variation of dielectric constant with frequency of the applied ac field 11

Table 1: Data on experimental and empirically calculated dielectric constant values ε ) and ( ε of benzoyl glycine crystal at various temperatures and frequencies f (Hz) 35 C 85 C 135 C 5 484.3 575.6 61.5 1 31.6 334.8 358.48 5 186.3.5.94 1 158.43 174.9 186.9 5 11.3 17.86 14.85 1 1.3 117.1 13.8 5 9.9 17.3 114.6 1 89.64 11. 111.1 5 86.5 94.11 14.1 1 8. 89. 95. 5 77.8 84.31 91.1 Table : Data on experimental (Ex) and empirically calculated (Th) dielectric loss (tan δ) and imaginary dielectric constant values ε ) and ( ε benzoyl glycine crystal at various temperatures and frequencies Temperature=35 C f (Hz) tan δ (Ex) ε ε tan δ(th) 5 4.838 484.3 343.4 4.83 1 3.398 31.6 155.48 3.4 5.566 186.3 478.4.57 1 1.58 158.43 5.31 1.58 5 1.6 11.3 135.5 1.3 1.878 1.3 89.81.88 5.51 9.9 47.5.51 1.65 89.64 3.75.7 5.17 86.5 14.8.17 1.9 8. 7.54.9 5.51 77.8 3.96.5 Temperature=85 C f (Hz) tan δ (Ex) ε Ε tan δ(th) 5 5.61 575.6 335.56 5.6 1 3.69 334.8 136.8 3.7 5.541.5 513.91.54 1 1.657 174.9 89.8 1.66 5 1.34 17.86 157.77 1.3 1.881 117.1 13.8.88 5.581 17.3 6.18.58 1.34 11. 3.71.3 5.18 94.11 17.1.18 1.13 89. 9.18.1 5.5 84.31 4.38.5 1

Temperature=135 C f (Hz) tan δ (Ex) ε Ε tan δ(th) 5 6.49 61.5 3963.36 6.49 1 4.13 358.48 1481.3 4.13 5.6.94 579.3.6 1.13 186.9 396.83.1 5 1.53 14.85 18.84 1.53 1.893 13.8 19.91.89 5.596 114.6 68.3.59 1.337 111.1 3.744.34 5.19 14.1 19.96.19 1.113 95. 1.73.11 5.67 91.1 6.1.6 Dielectric loss Dielectric loss 8 6 4 4 6 8 1 Frquency(Hz) Temp 35 C Temp 85 C Temp 135 C Figure.3. Dependence of dielectric loss on frequency (5 Hz- 5 MHz) of the applied field at different temperatures (35 C 135 C) Fig 3 shows the dependence of the dielectric loss on frequency in the range 5Hz-5MHz. It is interesting to find that the dielectric loss decreases with frequency at all temperatures ranging from 35 C-135 C. The maximum value of dielectric loss is 6.485 at a frequency of 5 Hz. Imaginary dielectric constant Imaginary Dielectric constant 5 4 3 1 4 6 8 1 Frequency (Hz) Temp 35 C Temp 85 C Temp 135 C Figure.4.Variation of imaginary dielectric constant ε with frequency at different temperatures (35 C- 135 C) 13

Fig 4 shows the variation of imaginary dielectric constant ( ε ) with frequency at different temperatures ranging from 35 C-135 C. The value of ε decreases in the frequency range 5Hz- 5MHz. This behavior is true at all the temperatures ranging from 35 C -135 C. D.C.Conductivity The study of electrical conductivity in crystalline solid helps to understand the nature of defects, carrier conduction, Fermi level, activation energy. Conductivity and diffusion in ionic crystalline solids are mainly due to the presence of point defects in the lattice. If the conductivity is due to different types of mobile charges then the electrical conductivity σ is given by σ = n q eµ (8) Where summation is taen over all the charged species, n indicates the number of mobile charges of the type having net charge q e and µ represents electrical mobility. For a charged particle, µ and D are related through Nernst Einstein equation as µ = D qe K T B (9) σ = D ( qe) n K B T (1) e σ = n q Z S (11) 6K BT Where z denotes jump frequency and s represents one jump distance. Defect free transparent crystals of appreciable size were selected and used for electrical conductivity measurements. The extended portions of the crystals were removed completely and the opposite faces were well polished and coated with good quality graphite to obtain ohmic contact. The D.C. conductivity measurements were carried out along the c-axis using the conventional two probe technique at various temperatures ranging from 4 C - 14 C. The dimensions of the crystal were measured using traveling microscope. The conductivity (σ ) of the crystal was calculated using the relation t σ = (1) RA Where, R is the measured resistance, d is the thicness of the sample crystal and A is the area of the face of the crystal in contact with the electrode. Plots between ln σ T and 1/T were found to be very nearly linear. So the conductivity values can be fitted to the equation σ T = σ exp( E / T ) (13) 14

Where, E is the activation energy, the Boltzmann constant, T the absolute temperature and σ a parameter depending on the material. The value of activation energy E for pure Benzoyl Glycine crystal was calculated as.168 ev. The electrical conductivity increases with increase in temperature. The defect concentration also increases exponentially with temperature and consequently the electrical conduction also increases. -4. ln σt -4.7-5. -5.7.5 3 3.5 1/T Figure. 5. Variation of ln σ T with 1/T for Benzoyl Glycine crystal A.C. Conductivity A.C. conductivity is one of the studies done on solids in order to characterize the bul resistance of the crystalline sample. The measurement of electrical conductivity using blocing electrode is a powerful method for determining both ionic and electronic conductivity of the materials. By proper choice of electrodes, either ionic or electronic transport is suppressed in a mixed conductor and the contribution to the conductivity by the non suppressed transport can be determined. The current through an ionic conducting material in a constant DC field decreases with time, because in dc measurement a space charge region is often setup as a result of a partial blocing of the ionic current by the electrodes. Therefore, the electrical characteristics of ionic conducting materials are studied by ac technique to avoid the necessity of developing the non blocing ion conducting electrodes for dc measurements. The electrical conductivity measurements are carried out with the same setup as that for dielectric measurement. The opposite faces of the specimen are coated with a thin layer of silver paint. This ensures good contact with the electrodes. The sample is placed over a copper base and a copper rod with spring arrangement is placed at the top of the specimen. The bottom plate and the upper copper rod serve as the electrodes. Ceramic beads covering the copper wire prevent it from touching the stainless steel tube to maintain thermal and electrical insulation. This setup is ept inside a muffle furnace. The temperature of the crystal is varied by changing the furnace current with the help of variable autotransformer, energized by a stabilized A.C. power supply. Measurements are taen after a period of one hour at each setting of the furnace current to ensure that a constant temperature is reached. An iron constant thermocouple is placed very close to the crystal to measure the temperature with an accuracy of ±.1 C. The ac conductivity σ ( ω ) of the material is given by: σ ( ω ) ωε ε tanδ = (14) 15

where ω = πf and f is the frequency of the applied alternating field, ε the dielectric constant of free space, ε the real part of dielectric constant, tanδ is the loss factor. The ac conductivity of the sample in the present study showed the frequency dependence, σ ac increases with increase in frequency. It has been reported that dispersion in the conductivity is the direct evidence for the hopping of charge carriers around the lattice imperfection. The dispersion in conductivity will occur when the carriers are not free to move through the sample.fig.6 shows variation of log σ vs. frequency at different temperatures. ac log σ -6-7 -8-9 -1-11 -1-13 -14 35ºC 85ºC 135ºC 5 1 15 log ω Figure.6.variation of log σ ac vs. frequency with different temperature CONCLUSION The dielectric constants ε ) and ε (, dielectric loss (tanδ) and conductivity (σac) of benzoyl glycine crystals are strongly dependent on temperature and frequency of the applied ac field, the variation depends on the ranges of temperature and frequency. The dielectric constant ε is dependent on both the temperature as well as frequency, provided the frequency of the applied field is in lower frequency range of 5 Hz to 1 KHz, the dielectric constant decreases with increasing frequency. In the higher frequency range 1KHz-5MHz, this dependence almost ceases to exist. The rate of variation of imaginary dielectric constant ( ε ) with temperature is strongly dependent on temperature and frequency of the applied field. The conductivity remains almost the same in the temperature range of 35 C-135 C corresponding to a frequency of 5MHz. The conductivity increases with temperature till 135 C. REFERENCES [1] Corento,A.;Jer phagon,j.; and Perigand A.; J.Chem.Phys., (1977),66,386. [] Rentzepis,P.M.; and Pao,Y.H. Appl. Phys. Lett. (1964),6,156. [3] Orlov,R.Yu.; Soviet. Phys. (1966)11, 41. [4] Ringertz, H.; Acta Cryst. (1971), B 7, 85. [5] Nagaraja,H.S.; Upadhyaya,V.; Mohan Rao,P.; Sreeramana Aithal,P.; and Bhat,A.P.; J. Cryst. Growth. (1998)193, 674. [6] Vijayan,N.;Ramesh Babu,R.; Gopalarishanan,R.;Ramasamy,P.;Ichimura, and Palanichamy, M., J. Cryst.Growth, (5),73, 564. 16

[7] Selvaraju, K.; Valluvan,R.; and Kumararaman,S.; Mat. Lett. (6),6, 1549. [8] Narayan Bhat,M.; and Dharmapraash,S.M.; J. Cryst. Growth,(),43, 1549. [9] Ramachandran,E.; and Natarajan,S.; Cryst. Res. Technol. (),37, 174. [1] Ramachandran,E.; and Natarajan,S.; Cryst. Res. Technol. (5),4, 765. [11] Ringertz,H.. Acta Cryst. (1971),B7, 85-91. [1] Verwey,E.J.W.and Heilman, J.Chem.Phys. (1947),15,174. 17