Improved Approximations in Thermal Properties for Single Screw Extrusion

Similar documents
Plastics Testing and Characterization Industrial Applications

Plastics Testing and Characterization Industrial Applications

H. W. Müllner (Sp), J. Eberhardsteiner, Technische Universität Wien (A); W. Fidi, Semperit Technische Produkte Ges.m.b.H. & Co. KG, Wimpassing (A)

On Relationship between PVT and Rheological Measurements of Polymer Melts

Measurement of heat transfer coefficients for polymer processing simulation

HIGH PRESSURE CAPILLARY RHEOMETRY ON WOOD PLASTIC COMPOSITES WITH VARIATION OF WOOD CONTENT AND MATRIX POLYMER ABSTRACT

Material Testing Overview (THERMOPLASTICS)

Application of Analytical Technique to Resolving the Flow Dynamics in Self-wiping Co-rotating Twin Screw Extruders

Rheology Of Reinforced Polypropylene Melt Flow

Material Testing Report SN 7131 ISOFIL HK 30 TTH0 WT0822

SIMULATIVE EVALUATION OF THE TEMPERATURE INFLUENCE ON DIFFERENT TYPES OF PRE-DISTRIBUTORS IN SPIRAL MANDREL DIES

All rights reserved, 2011, Century Extrusion. Why simulation? Limited availability and cost of API s

EFFECT OF TYPICAL MELT TEMPERATURE NON-UNIFORMITY ON FLOW DISTRIBUTION IN FLAT DIES

Polymer Reaction Engineering

Linear Control Design for a Plastic Extruder

MECHANICAL AND THERMAL PROPERTIES OF COMMERCIAL MULTILAYER PET/PP FILM IRRADIATED WITH ELECTRON-BEAM

Morphology Evolution in PS/LDPE Blends in a Twin Screw Extruder: Effects of Compatibilizer

Nanocomposites: A Single Screw Mixing Study of Nanoclay-filled Polypropylene

VOCs Emissions and Structural Changes of Polypropylene During Multiple Melt Processing

Moldflow Material Testing Report MAT2216 ISOFIL H 40 C2 F NAT

SILMALAB is a laboratory of analysis for plastics industry that takes advantage of the experience gained by our engineers in 30 years of work and

STUDY OF RHEOLOGICAL BEHAVIOR OF REPROCESSING HIGH IMPACT POLYSTYRENE

MATERIALS AND METHODS

Polymer Testing 28 (2009) Contents lists available at ScienceDirect. Polymer Testing. journal homepage:

An Adjustable Gap In-Line Rheometer

IN-LINE ULTRASONIC MONITORING OF POLYMER BLENDING IN A TWIN-SCREW EXTRUDER

Investigation of Polymer Long Chain Branching on Film Blowing Process Stability by using Variational Principle

MICROWAVE EFFECTS ON CFRP PROCESSING SUMMARY 1. MICROWAVE BACKGROUND

Injection Molding. Figure 1: Principles of injection molding. Injection molding cycle: part solidifies. Open Mold Eject Part Close Mold

High Pressure DSC Differential Scanning Calorimeter

DSC PT 10. Applications

Rheological Properties of ABS at Low Shear Rates: Effects of Phase Heterogeneity

Polymer Engineering (MM3POE)

Measuring the rheology of thermoplastic polymer melts

COMPUTATIONAL ANALYSIS AND DESIGN OF SINGLE SCREW EXTRUDERS HAVING SCREWS OF COMPLEX GEOMETRY WITH MIXING ELEMENTS

MODELING THREE-DIMENSIONAL NON-NEWTONIAN FLOWS IN SINGLE- SCREW EXTRUDERS

THE 3D VISCOELASTIC SIMULATION OF MULTI-LAYER FLOW INSIDE FILM AND SHEET EXTRUSION DIES

Modeling of Anisotropic Polymers during Extrusion

Influence of Calcium Carbonate Nanoparticles on the Crystallization of Olypropylene

Fracture mechanics analysis of arc shaped specimens for pipe grade polymers

Heat Transfer in Polymers

RHEOLOGY AS A POWERFULL TOOL FOR SCIENTIFIC AS WELL INDUSTRIAL CHARACTERISATION OF NEW MATERIALS BASED ON POLYMER-CLAY NANOCOMPOSITES.

ANALYSIS OF EXTRUSION PROBLEMS WITH FLOW SIMULATION

ANALYSIS ON PLANAR ENTRY CONVERGING FLOW OF POLYMER MELTS

Radiation Effects on Poly(propylene) (PP)/Ethylene Vinyl Acetate Copolymer (EVA) Blends

Characterization of extrusion flow using particle image velocimetry

Heat Transfer in Polymers

Effect of Rubber Content of ABS on the Mechanical Properties of ABS/Clay Nanocomposites

INFLUENCE OF PARTICLE SIZE IN MULTI-LAYER ROTATIONAL MOLDING WITH A MULTIPHASE INTERLAYER TO GENERATE MECHANICAL ADHESION

Introduction Wood K plus. Motivation. Results. Conclusions. J. Leßlhumer 1, J. Sinic 1, M. Reif 1, A. Haider 1, D. Cascorbi 2

Analysis of Polymers and Plastics. Innovation with Integrity. Quality Control & Failure Analysis FTIR

Continuous Manufacturing of Pharmaceuticals: Scale-up of a Hot Melt Extrusion Process

Thermal analysis unlocks the secrets of elastomers

Heat Transfer in Polymers

PROFILE EXTRUSION OF WPC S SUPPORTED BY RHEOLOGICAL AND SIMULATION DATA

3D Compression Molding

THERMAL CHARACTERIZATION OF GYPSUM COMPOSITES BY USING DIFFERENTIAL SCANNING CALORIMETRY

Rheology/Viscometry. Viscometry

INFLUENCE OF FLOWABILITY AND MAH-CONTENT OF MALEATED POLYOLEFINES ON RHEOLOGICAL AND MECHANICAL INTERACTION EFFECTS OF WOOD FILLERS IN POLYOLEFINES

Influence of Polymer Viscoelasticity on the Residence Distributions of Extruders

The Influence of Processing-History on the Main Melting Temperature and Secondary Melting Temperature Using DSC. Stephen Sansoterra

TRANSPORT BEHAVIOUR OF XYLENE THROUGH COMPATIBILIZED LOW DENSITY POLYETHYLENE COMPOSITE

Polymer Testing, 31 (6):

Determining Liquid Capacity 4 th Annual Pipeline Knowledge Retention Chris Sonneborn November 7, 2013

Shear rheology of polymer melts

Design, Testing and Pharmaceutical Applications of a Gas Pressure Controller Device for Solid - Gas Microcalorimetric Titration

Effects of Processing Conditions on Exfoliation and Rheological Behaviour of PBT-Clay Nanocomposites

Hot Runner Technology

The effect of melt compressibility on the mold filling of thin-walled parts

Study on the Pressure and Temperature Distribution of Solid-Plug Conveying Element on Centrifugal Extruder

The Characterization of Thermal Interface Materials using Thermal Conductivity for Within Sample and Batch to Batch Variation Analysis

GB/T / ISO 527-1:1993

Investigation of the numerical analysis for the ultrasonic vibration in the injection molding

Development of a continuous process for EPDM devulcanization in an extruder Sutanto, Poppy

A dynamic model of a vertical direct expansion ground heat exchanger

DEPC-MPR-043 Prediction of the Impact Performance of Plastics Mouldings, G D Dean and L E Crocker.

DSC AS PROBLEM-SOLVING TOOL: BETTER INTERPRETATION OF Tg USING CYCLIC DSC

2. State the direction of heat transfer between the surroundings and the water in the bottle from 7 a.m. to 3 p.m.

Melting and solidi cation of Pb nanoparticles embedded in an Al matrix as studied by temperature-modulated di erential scanning calorimetry

Analysis of Polymers and Plastics. Innovation with Integrity. Quality Control & Failure Analysis FT-IR

THE INFLUENCE OF CARBON NANOTUBES ON THE ELECTRICAL PROPERTIES OF INJECTION MOLDED THERMOPLASTIC POLYMER MATRIX. Jan VÁCHA, Jiří HABR

Numerical Study of a High Temperature Latent Heat Storage ( C) Using NaNO 3 -KNO 3 Binary Mixture

Polymer engineering syllabus (BSc)

ISO INTERNATIONAL STANDARD. Plastics Differential scanning calorimetry (DSC) Part 4: Determination of specific heat capacity

Multilayer Rheology Effects in Coextruded Structure Design

Optimization Technique for the Geometry of Twin Screw Cryogenic Extruder

Response Surface Models for Optimization of Wheat Straw- Polypropylene Composite Formulations

A NEW DISPERSIVE MIXER FOR SINGLE SCREW EXTRUDERS

MODELLING THE MECHANICAL AND THERMAL PROPERTIES OF SHORT FIBRE COMPOSITES

Effusivity is defined as the square root of the product of thermal conductivity, k, density,

Rheological Characterisation of the Flow Behaviour of Wood Plastic Composites in Consideration of Different Volume Fractions of Wood

VISCOELASTIC SIMULATIONS WITH INTEGRAL MODELS AT EXTREMELY HIGH SHEAR RATES

COMPUTATIONAL ANALYSIS AND DESIGN OF SINGLE SCREW EXTRUDERS HAVING SCREWS OF COMPLEX GEOMETRY WITH MIXING ELEMENTS

Calorimetry. Chapter 2. Differential Scanning heat flux calorimetry

UNDERSTANDING THE INTERFACIAL INTERACTIONS IN SILICA REINFORCED POLYPROPYLENE NANOCOMPOSITES

Entry Flow of Polyethylene Melts in Tapered Dies

Flow Induced Molecular Weight Fractionation during Capillary Flow of Linear Polymer Melt

RESEARCH PAPERS FACULTY OF MATERIALS SCIENCE AND TECHNOLOGY IN TRNAVA, SLOVAK UNIVERSITY OF TECHNOLOGY IN BRATISLAVA, 2017 Volume 25, Number 40

Universal Standard Protocols for Temperature and Material Characterization Calibration with Pharmaceuticals by Thermal Analysis

Rigorous calculation of LNG flow reliefs using the GERG-2004 equation of state

Transcription:

Improved Approximations in Thermal Properties for Single Screw Extrusion Modified on Friday, 01 May 2015 11:49 PM by mpieler Categorized as: Paper of the Month Improved Approximations in Thermal Properties for Single Screw Extrusion Eberhard Grünschloss* and María del Pilar Noriega ICIPC Plastics and Rubber Institute Carrera 49 No. 5 Sur 190, Medellin, Colombia, South America *Schweitzerstrasse 36, D 70619 Stuttgart, Germany Abstract Actual screw design software is capable to simulate the performance of a single screw extruder based on elaborated program codes. The aim of this work is to present improved approximations in relevant thermal properties for simulation and design of single extrusion screws in combination with analytical calculations appropriate for the industrial practice. The developed approximation functions for thermal properties, such as, specific heat capacity, enthalpy, thermal conductivity and density, were obtained looking for small number of parameters. A comparison between the improved approximation functions, existing known functions and measured data for some common polymer families is shown. Background The thermal properties of polymers affect the single screw extrusion process from the feeding zone to the metering and mixing zone. These properties have an effect on solids conveying, melting rate and melt conveying of an extruder screw. The melting rate of the polymer material has an important effect on extrusion melting efficiency and it is strongly affected by such properties as specific heat, thermal conductivity and density obtained from a p v T diagram. Specific heat capacity describes the amount of energy that it takes to raise the temperature of a polymer. LDPE requires an average of 2.596 J/(g.K) in the molten state, while PS requires 1.95 J/(g.K), [1]. Therefore, it takes almost 33 % more energy to raise the temperature of 1 g of LDPE than 1 g of PS. Additionally, it means that more power is necessary to process LDPE than PS at the same extrusion processing conditions like output in kg/h and melt temperature. It is well known that the specific heat capacity is the derivative of enthalpy with respect to temperature. Thermal conductivity is the ability of the polymer to conduct heat. In general, the polymers exhibit a low thermal conductivity. LDPE has an average thermal conductivity of 0.25 W/(m.K) in the molten state, while PS is 0.14 W/(m.K), [1]. Because LDPE has a higher thermal conductivity than PS, the heat flux for LDPE from barrel to polymer is higher. Solid and melt density can be obtained from p v T diagram, for example, Tait s equation of state. The density is found from reciprocal of specific volume. Nevertheless, other authors have shown in the literature that Tait s equation does not work well for semicrystalline polymers [2]. The research work of Sanchez Cho on equation of state for polymers seems to be until now the most accurate equation of state [2, 3]. Improved Approximations: The developed approximation functions for thermal properties were obtained looking for small number of parameters, and they are: specific heat capacity for solid state and molten state, enthalpy for solid state and molten state, thermal conductivity from the solid state to the molten state and density from the solid state to the molten state. The solid state enthalpy (H s ) is proposed as a fourparameter function as follows: A: Parameter in J/g B: Parameter in K C Parameter in K D: Parameter in K The enthalpy for molten state (Hm) is proposed as a two parameter function as follows:

F: Parameter in J/(g.K) E: Parameter in J/(g.K 2 ) The specific heat capacity for solid state (Cps) is suggested as a four parameter function: Where the parameters A, B, C and D are taken from the enthalpy function, A: Parameter in J/g B: Parameter in K C: Parameter in K D: Parameter in K The specific heat capacity for molten state (Cp m ) is suggested as a two parameter function: Where the parameter E is taken from the enthalpy function, E: Parameter in J/(g.K) The heat of fusion for semicrystalline polymers can be obtained graphically from the enthalpy function as shown in Fig. 1 for a HDPE. The heat of fusion is the amount of heat energy that is required to convert a polymer from a solid to a liquid or melt. The thermal conductivity (k) from the solid state to the molten state is proposed as one function with six parameters: A: Parameter in W/(m.K) B: Parameter in K C: Parameter in K D: Dimensionless parameter E: Dimensionless parameter F: Parameter in W/(m.K) This function is suitable for the range from room temperature up to typical melt temperatures in the single screw extrusion process. The solid state density (ρ s ) is obtained from reciprocal of specific volume (υ s ) and it is proposed as a six parameter model, as follows: A: Parameter in cm 3 /g B: Parameter in K

C: Parameter in bar D: Parameter in K E: Parameter in K F: Parameter in bar p: Pressure in bar The density for molten state (ρ m ) is obtained from reciprocal of specific volume (υ m ) and it is proposed as a threeparameter model after Spencer and Gilmore, as follows [4]: A: Parameter in cm 3 /g B: Parameter in bar C: Parameter in (bar.cm3) / (g.k) p: Pressure in bar The thermal diffusivity (α) can be calculated from previous functions, such as, specific heat, thermal conductivity and density. Other Authors have investigated extensions of some of the above mentioned equations or functions, [5, 6, 7]. The functions described in this work have been found more suitable for simulation and design of screws in single screw extrusion, and they were obtained looking for small number of parameters, what it is appropriate for the industrial practice. There is no fundamental theory behind the equations presented in this paper. This is reasonable because in practice the polymers are normally not pure but mixed with additives and reinforcing agents, blended with other polymers to combine their properties, etc. This will alter the polymer physics and complicate an appropriate fundamental theory. The previous approximation functions contribute to an easier single screw calculation to simulate the performance of a single screw extruder with regard to output, pressure build up, melting rate, heat transfer and melt temperature. These thermal functions can be used for the calculations in the screw melting zone, screw metering zone and extrusion die, Fig. 2, specially, for the prediction of pressure build up and melt temperature profile. Experimental Polypropylene: a polypropylene homopolymer reference 505P produced by SABIC with a Melt Index Flow, MFI, of 2.0 g/10 min at 230ºC/2.16 kg according to ISO 1133. This is a multipurpose grade for extrusion and injection molding applications. Modulated DSC: A Q200 Differential Scanning Calorimeter from TA Instruments was used for measuring total heat flow, enthalpy and heat capacity. Test conditions were carried out following the standard ASTM E 1269. A 10 mg of sample was heated from an initial temperature up to a final temperature under high purity nitrogen, using a heating rate of 20 C/min. An isotherm at final temperature is required during 5 minutes. Results The solid state enthalpy (Hs) and for molten state (Hm) for PP Ref. 505P proposed as two functions in previous numeral have converged to the following parameters: A: 971.49 J/g B: 350.44 K C: 475.11 K D: 15.18 K E: 0.0034 J/(g.K 2 )

F: 303.155 J/g The Fig. 3 shows the measured data and the obtained approximation functions. From the figure it is possible to observe that the approximation functions match the data very well. The specific heat capacity for solid state (Cp s ) and for molten state (Cp m ) for PP Ref. 505P proposed as two functions in previous numeral have the same parameter values for A, B, C, D and E than the enthalpy functions, since specific heat capacity is the derivative of enthalpy with respect to temperature. The Fig. 4 shows the obtained approximation functions from measured enthalpy data. This figure illustrates that the approximation functions match the data properly. The thermal conductivity (k) from the solid state to the molten state for a HDPE reported by VDMA [8] has met the following parameters: A: 0.19886 W/(m.K) B: 0.00538 1/K C: 0.00873 1/K D: 4.76 E: 16.81785 F: 0.25451 W/(m.K) The Fig. 5 shows the measured data and the obtained approximation function. From the figure it is possible to observe that the approximation function fits the data satisfactorily. The solid state density (ρ s ) for a PP measured by Borealis is obtained from reciprocal of specific volume and it has converged to the following parameters: A: 1.042 cm 3 /g B: 3540 K C: 2166 bar D: 422.1 K E: 8.364 K F: 353.3 bar The density for molten state (ρ m ) for a PP measured by Borealis is obtained from reciprocal of specific volume and it has met the following parameters: A: 0.9537 cm 3 /g B: 2435 bar C: 1.8542 (bar.cm3)/(g.k) The Fig. 6 shows the measured data and the obtained approximation functions for the solid and the molten state. From the figure it is clear that the approximation functions fit the data very well. The Fig. 7 is demonstrating the use of the above described thermal functions in combination with analytical calculations, [9], for the prediction of pressure build up in a single screw of D = 20 mm and L/D = 20 for PE processing. The left ordinate axis shows the screw pitch, the right ordinate axis shows the screw channel depth and the abscissa or X axis is the axial screw length. Solids bed profiles (SBP) could be obtained for several polymers and single screws using the experimental values of X/W versus L/D from a patented device compared to analytical melting models using the mentioned thermal functions, [10]. Conclusions This work presented improved approximations with reduced number of parameters in thermal properties that are relevant for simulation and design of single extrusion screws. These approximations in combination with analytical calculations are appropriate for the industrial practice, since they deliver accurate enough predictions of output and pressure build up of extruder screws, among others. There is no fundamental theory behind the equations shown in this paper. This is reasonable because in practice the polymers are normally not pure but mixed with additives and reinforcing agents, blended with other polymers to combine their properties, etc. This will alter the polymer physics and complicate an appropriate fundamental theory.

The developed approximation functions for thermal properties, such as, specific heat capacity, enthalpy, thermal conductivity and density, fitted the measured data very well. The authors gave an adequate mathematical representation of the measured data, suitable for inclusion in future analytical models and papers. References /1/ Kühnle, H. and Grünschloss, E., Berechnung der Austragszone von Einschneckenextrudern, Rheologie in der Kunststofftechnik, Technische Akademie Esslingen, Ostfildern, Germany, 1999 /2/ Zoller Paul, PVT Reltionship and Equations of State of Polymers, /3/ Cho, J. and Sanchez, I., PVT Relationship and Equations of State of Polymers /4/ Spencer, R.S. and Gilmore, G.D., Equation of state for high polymers, Journal of Applied Physics, 21, pp. 523 526, (1950). /5/ Sanchez, I. and Cho, J., A universal equation state for polymer liquids, Polymer, Vol. 36, No. 15, pp. 2929 2939, 2005 /6/ Naranjo, Alberto, Measurement of the Thermal Diffusivity of Thermoplastics under Processing Conditions, IKV Berichte aus der Kunststoffverarbeitung, Mainz, G., Germany, 2004 /7/ Sedlacek, T., et.al. On relationship between PVT and rheological measurements of polymer melts, Annual transactions of the Nordic Rheology Society, Vol. 13, 2005. /8/ VDMA, Thermodynamik, Carl Hanser Verlag, Munich, Germany, 1979 /9/ Grünschloss, E., Polymer Single Screw Extrusion: Modeling, Encyclopedia of Materials: Science and Technology, Elsevier Science Ltd., 2001 /10/ Noriega, María del Pilar, et. al., Method and device to visualize in line and quantify the polymer melting in plasticating screw machines without significantly affecting its thermal regime, U.S Patent No. 7314363, January 1, 2008. Acknowledgments Thanks are also due to the Instituto de Capacitación e Investigación del Plástico y del Caucho (ICIPC) in Medellín, Colombia, Institute for Plastics Technology (IKT) in Stuttgart, Germany, German Academic Exchange Service (DAAD) and ICETEX in Colombia for their valuable support to develop this research project. Nomenclature D Extruder diameter L/D Dimensionless Extruder length X/W Dimensionless screw channel width H s : Solid state enthalpy Hm: Enthalpy of the melt Cp s : Specific heat capacity of the solids Cp m : Specific heat capacity of the melt k: Thermal conductivity ρ s : Solid state density ρm: Density of the melt υ s : Specific volume of the solids υ m : Specific volume of the melt α: Thermal diffusivity R: Gas constant, 8.3144 J/(mol.K) p: Pressure T: Temperature LDPE: Low density polyethylene HDPE: High density polyethylene PP: Polypropylene PS: Polystyrene Key Words: Single screw extruder, thermal properties, specific heat capacity, enthalpy, density, thermal diffusivity, LDPE, HDPE, PP, PS

Figure 1: Graphically obtained heat of fusion for HDPE Figure 2: Zones in a single screw extruder Figure 3: Enthalpy of PP SABIC 505P: Measured data and approximations

Figure 4: Specific heat capacity of PP SABIC 505P: Approximations Figure 5: Thermal conductivity of HDPE: Measured data and approximation

Figure 6: p v T diagram of PP (Borealis): Measured data and approximations Figure 7: Pressure build up (ο) of a Ø20 mm screw for PE, channel depth ( ) and screw pitch (x) versus axial screw length Return to Paper of the Month.