1 Supporting information Interaction of Acid Gases SO, NO with Coordinatively Unsaturated Metal Organic Frameworks: M-MOF-74 (M= Zn, Mg, Ni, Co) Kui Tan 1, Sebastian Zuluaga, Hao Wang 3, Pieremanuele Canepa,3, Karim Soliman, Jeremy Cure 1, Jing Li 4, Timo Thonhauser,5, and Yves J. Chabal 1 1 Department of Materials Science & Engineering, University of Texas at Dallas, Richardson, Texas 75080, USA Department of Physics, Wake Forest University, Winston-Salem, NC 7109, USA 3 Materials Science Division, Lawrence Berkeley National Laboratory, Berkeley, CA 9470, USA 4 Department of Chemistry and Chemical Biology, Rutgers University, Piscataway, New Jersey 08854, USA 5 Department of Chemistry, Massachusetts Institute of Technology, Cambridge, MA, 0139, USA 1. Sample preparation and activation Zn-MOF-74: A mixture of zinc nitrate hexahydrate (0.4 g, 0.8 mmol),, 5- dihydroxyterephthalic (0.08 g, 0.4 mmol), 9 ml DMF and 1 ml H O were transferred into a 8 ml Teflon-lined autoclave. The autoclave was then sealed and heated to 10 C for 3 days. After filtering and washing with 0 ml DMF, the product was collected. Then the product was exchanged with 0 ml methanol in a glass vial every hs during daytime for 3 days. Mg-MOF-74: A mixture of magnesium nitrate hexahydrate (0.6 g, 1 mmol),, 5- dihydroxyterephthalic (0.1 g, 0.5 mmol), 7 ml tetrahydrofuran (THF), 3 ml water H O and ml 1 M NaOH solution was prepared in a 8 ml Teflon-lined autoclave. The autoclave was then sealed and heated to 100 C for 3 days. After filtering and washing with 0 ml THF, the product was collected and exchanged with methanol every hs during daytime for 3 days. Then the MOFs sample was stored in N glove box. Ni-MOF-74: A mixture of nickel nitrate hexahydrate (0.4 g, 0.8 mmol),, 5- dihydroxyterephthalic (0.08 g, 0.4 mmol), 9 ml DMF and 1 ml H O was prepared in a 8 ml Teflon-lined autoclave. The autoclave was then sealed and heated to 100 C for 3 days. After filtering and washing with 0 ml DMF, the product was collected and exchanged with methanol every hs during daytime for 3 days. Then the MOFs sample was stored in N glove box. Co-MOF-74: A mixture of cobalt nitrate hexahydrate (0.17 g, 0.6 mmol),, 5- dihydroxyterephthalic (0.06 g, 0.3 mmol), 9 ml DMF and 1 ml H O was prepared in a 8 ml Teflon-lined autoclave. The autoclave was then sealed and heated to 100 C for 3 days. After filtering and washing with 0 ml DMF, the product was collected and exchanged with methanol every hs during daytime for 3 days. Then the MOFs sample was stored in N glove box. The crystal structures of the three MOF-74 samples (Zn, Mg, Co, Ni) were measured by PXRD and compared to the simulated PXRD pattern of Ni-MOF-74 in reference 1, as shown in Figure
2 S. The XRD diffraction patterns of the samples we studied are in agreement with literature reports. The BET surface areas of the three compounds are measured by N isotherm. The values for Zn-, Mg-, Ni-, and Co-MOF-74 are 774, 1078, 913, and 1077 m /g, respectively. Table S1 summarize the values measured in this work and those measured in previous literature reports. Note that there have been many studies of MOF-74 with some variations in the activation processes, resulting in a range of BET surface areas. Clearly, the activation of MOF-74 structure containing coordinatively unsaturated metal sites is not as easy as for other MOFs such as M(bdc)(ted) 0.5. We used the same synthetic method with modified and more thorough solvent exchange. As a result, the values of surface areas for our sample MOF74-Co/Ni/Mg/Zn are in the range reported in the literature. The spectroscopic study of this work focuses on the interaction or reaction mechanism of acid SO, NO with available open metal sites. The interpretation derived from the results will therefore not be influenced if a small fraction of other metal sites are not open for adsorption because of possible incomplete activation.
3 Table S1. Summary of BET surface areas of M-MOF-74 (M= Mg, Co, Ni, Zn), compared with values reported in previous studies. M=Mg, Co, Ni BET surface area (m /g) Ref. Mg-MOF This work Co-MOF This work Ni-MOF This work Zn-MOF This work
4 Absorbance Absorbance Absorbance Absorbance. IR spectra of activated MOFs a 0.1 Zn- MOF-74 b 0.05 Mg- MOF c 0. Ni- MOF-74 d 0. Co- MOF Figure S1. IR adsorption spectra of activated MOF-74 samples referenced to pure KBr in vacuum.
5 Intensity (a.u.) aintensity (a.u.) Zn-MOF-74 Mg-MOF-74 (10) (300) theta b Co-MOF-74 (10) Ni-MOF-74 (300) theta A Figure S. Power X-ray diffraction patterns of Zn, Mg, Ni, Co-MOF-74 samples after both NO and SO exposures, measured right after the IR measurements and compared to as-synthesized and activated samples.
6 SO uptake mmol/g 3. Isotherm of SO in Mg-MOF Pressure (bar) Figure S3. SO adsorption and desorption isotherms of Mg-MOF-74 performed at room temperature. Filled and open symbols represent adsorption and desorption, respectively. References: 1. Dietzel, P. D. C.; Johnsen, R. E.; Fjellvag, H.; Bordiga, S.; Groppo, E.; Chavan, S.; Blom, R., Adsorption properties and structure of CO adsorbed on open coordination sites of metal-organic framework Ni (dhtp) from gas adsorption, IR spectroscopy and X-ray diffraction. Chemical Communications 008, (41), Lee, J. Y.; Olson, D. H.; Pan, L.; Emge, T. J.; Li, J., Microporous Metal Organic Frameworks with High Gas Sorption and Separation Capacity. Advanced Functional Materials 007, 17, (8), Caskey, S. R.; Wong-Foy, A. G.; Matzger, A. J., Dramatic Tuning of Carbon Dioxide Uptake via Metal Substitution in a Coordination Polymer with Cylindrical Pores. Journal of the American Chemical Society 008, 130, (33), Dietzel, P. D. C.; Besikiotis, V.; Blom, R., Application of metal-organic frameworks with coordinatively unsaturated metal sites in storage and separation of methane and carbon dioxide. Journal of Materials Chemistry 009, 19, (39), Perry, J. J.; Teich-McGoldrick, S. L.; Meek, S. T.; Greathouse, J. A.; Haranczyk, M.; Allendorf, M. D., Noble Gas Adsorption in Metal Organic Frameworks Containing Open Metal Sites. J. Phys. Chem. C. 014, 118, (), Yang, D.-A.; Cho, H.-Y.; Kim, J.; Yang, S.-T.; Ahn, W.-S., CO capture and conversion using Mg-MOF-74 prepared by a sonochemical method. Energy Environ. Sci. 01, 5, (4),
7 7. Li, L.; Yang, J.; Li, J.; Chen, Y.; Li, J., Separation of CO/CH4 and CH4/N mixtures by M/DOBDC: A detailed dynamic comparison with MIL-100(Cr) and activated carbon. Microporous and Mesoporous Materials 014, 198, (0), Britt, D.; Tranchemontagne, D.; Yaghi, O. M., Metal-organic frameworks with high capacity and selectivity for harmful gases. Proc. Natl. Acad. Sci. 008, 105, (33), Wu, X.; Bao, Z.; Yuan, B.; Wang, J.; Sun, Y.; Luo, H.; Deng, S., Microwave synthesis and characterization of MOF-74 (M = Ni, Mg) for gas separation. Microporous and Mesoporous Materials 013, 180, (0), Bao, Z.; Yu, L.; Ren, Q.; Lu, X.; Deng, S., Adsorption of CO and CH4 on a magnesium-based metal organic framework. Journal of Colloid and Interface Science 011, 353, (), Dietzel, P. D. C.; Blom, R.; Fjellvåg, H., Base-Induced Formation of Two Magnesium Metal- Organic Framework Compounds with a Bifunctional Tetratopic Ligand. European Journal of Inorganic Chemistry 008, 008, (3), Yazaydın, A. O. z. r.; Snurr, R. Q.; Park, T.-H.; Koh, K.; Liu, J.; LeVan, M. D.; Benin, A. I.; Jakubczak, P.; Lanuza, M.; Galloway, D. B.; Low, J. J.; Willis, R. R., Screening of Metal Organic Frameworks for Carbon Dioxide Capture from Flue Gas Using a Combined Experimental and Modeling Approach. Journal of the American Chemical Society 009, 131, (51), Liu, J.; Benin, A. I.; Furtado, A. M. B.; Jakubczak, P.; Willis, R. R.; LeVan, M. D., Stability Effects on CO Adsorption for the DOBDC Series of Metal Organic Frameworks. Langmuir 011, 7, (18), Díaz-García, M.; Mayoral, Á.; Díaz, I.; Sánchez-Sánchez, M., Nanoscaled M-MOF-74 Materials Prepared at Room Temperature. Crystal Growth & Design 014, 14, (5), Grant Glover, T.; Peterson, G. W.; Schindler, B. J.; Britt, D.; Yaghi, O., MOF-74 building unit has a direct impact on toxic gas adsorption. Chemical Engineering Science 011, 66, (),
High-throughput screening of small-molecule adsorption in MOF. Supplementary Materials
High-throughput screening of small-molecule adsorption in MF Supplementary Materials Pieremanuele Canepa, Calvin A. Arter, Eliot M. Conwill, Daniel H. Johnson, Brian A. Shoemaker, Karim Z. Soliman, and
More informationA flexible MMOF exhibiting high selectivity for CO 2 over N 2, CH 4 and other small gases. Supporting Information
A flexible MMOF exhibiting high selectivity for CO 2 over N 2, CH 4 and other small gases Jingming Zhang, a Haohan Wu, a Thomas J. Emge, a and Jing Li* a a Department of Chemistry and Chemical Biology,
More informationNew Materials and Process Development for Energy-Efficient Carbon Capture in the Presence of Water Vapor
New Materials and Process Development for Energy-Efficient Carbon Capture in the Presence of Water Vapor Randy Snurr, 1 Joe Hupp, 2 Omar Farha, 2 Fengqi You 1 1 Department of Chemical & Biological Engineering
More informationAdsorption Separations
Molecular Modeling and Design of Metal-Organic Frameworks for CO 2 Capture Randy Snurr Department of Chemical & Biological Engineering Northwestern University, Evanston, IL 60208 http://zeolites.cqe.northwestern.edu
More informationSupporting Information
Supporting Information Highly Selective Carbon Dioxide Sorption in an Organic Molecular Porous Material Hyunuk Kim, Yonghwi Kim, Minyoung Yoon, Soyoung Lim, Se Min Park, Gon Seo, Kimoon Kim*, National
More informationSupplementary Figure 1 / Crystal structure of Ni-MOF-74. (a) side view along c axis of hexagonal cell. (b) view perpendicular to the c axis.
Supplementary Figure 1 / Crystal structure of Ni-MOF-74. (a side view along c axis of hexagonal cell. (b view perpendicular to the c axis. Color scheme: blue, grey, red, and white spheres represent Ni,
More informationMicroporous Organic Polymers for Carbon Dioxide Capture
Microporous Organic Polymers for Carbon Dioxide Capture R. Dawson, E. Stöckel, J.R. Holst, D.J. Adams and A.I. Cooper Contents Synthetic Procedures Nitrogen isotherms CO 2 isotherms PXRD BET plots Pore
More informationA new tetrazolate zeolite-like framework for highly selective CO 2 /CH 4 and CO 2 /N 2 separation
Electronic Supplementary Material (ESI) for ChemComm. This journal is The Royal Society of Chemistry 2014 Electronic Supplementary Material (ESI) for ChemComm. Supporting Information A new tetrazolate
More informationSupporting Information
Electronic Supplementary Material (ESI) for Journal of Materials Chemistry A. This journal is The Royal Society of Chemistry 15 Supporting Information Co-MOF as sacrificial template: Manifesting new Co
More informationChemical Engineering Science
Chemical Engineering Science 66 (2) 63 7 Contents lists available at ScienceDirect Chemical Engineering Science journal homepage: www.elsevier.com/locate/ces building unit has a direct impact on toxic
More informationElectronic Supporting Information (ESI) Porous Carbon Materials with Controllable Surface Area Synthsized from Metal-Organic Frameworks
Electronic Supporting Information (ESI) Porous Carbon Materials with Controllable Surface Area Synthsized from Metal-Organic Frameworks Seunghoon Lim, Kyungwon Suh, Yelin Kim, Minyoung Yoon, Hyeran Park,
More informationDMOF-1 as a Representative MOF for SO 2 Adsorption in both Humid and Dry Conditions
DMOF-1 as a Representative MOF for SO 2 Adsorption in both Humid and Dry Conditions Julian Hungerford, Souryadeep Bhattacharyya, Uma Tumuluri, Sankar Nair, Zili Wu, and Krista S. Walton* School of Chemical
More informationSupplementary Information
Supplementary Information Stable aluminum metal-organic frameworks (Al-MOFs) for balanced CO 2 and water selectivity Haiwei Li, Xiao Feng, * Dou Ma, Mengxi Zhang, Yuanyuan Zhang, Yi Liu, Jinwei Zhang,
More informationSupporting Information
Electronic Supplementary Material (ESI) for RSC Advances. This journal is The Royal Society of Chemistry 2015 Supporting Information Novel Nanoporous Ferrocenyl Framework for Clean Energy Application Qingquan
More informationSupporting information A Porous Zr-cluster-based Cationic Metal-Organic Framework for Highly Efficient Cr 2 O 7
Electronic Supplementary Material (ESI) for ChemComm. This journal is The Royal Society of Chemistry 2015 Supporting information A Porous Zr-cluster-based Cationic Metal-Organic Framework for Highly Efficient
More informationElectronic Supplementary Information for. Non-interpenetrated IRMOF-8: synthesis, activation, and gas sorption
S1 Electronic Supplementary Information for Non-interpenetrated IRMOF-8: synthesis, activation, and gas sorption Jeremy I. Feldblyum, a,b Antek G. Wong-Foy, b and Adam J. Matzger a,b a Macromolecular Science
More informationElectronic Supplementary Information
Electronic Supplementary Material (ESI) for Journal of Materials Chemistry A. This journal is The Royal Society of Chemistry 2017 Electronic Supplementary Information Cation exchange MOF-derived nitrogen-doped
More informationSupplementary information for. Interaction of hydrogen with accessible metal sites in the metal-organic frameworks M 2 (dhtp) (CPO-27-M; M=Ni, Co, Mg)
Supplementary information for Interaction of hydrogen with accessible metal sites in the metal-organic frameworks M 2 (dhtp) (CPO-27-M; M=Ni, Co, Mg) Pascal D. C. Dietzel,* Peter A. Georgiev, Juergen Eckert,
More informationA flexible zinc tetrazolate framework with breathing behaviour on xenon adsorption and selective adsorption of xenon over other noble gases
Electronic Supplementary Material (ESI) for Journal of Materials Chemistry A. This journal is The Royal Society of Chemistry 2015 Electronic Supplementary Material (ESI) for J. Mater. Chem. A. Supporting
More informationAdsorptive separation of methanol-acetone on isostructural series of. metal-organic frameworks M-BTC (M = Ti, Fe, Cu, Co, Ru, Mo): A
Supporting information Adsorptive separation of methanol-acetone on isostructural series of metal-organic frameworks M-BTC (M = Ti, Fe, Cu, Co, Ru, Mo): A computational study of adsorption mechanisms and
More informationSupporting Information
Electronic Supplementary Material (ESI) for RSC Advances. This journal is The Royal Society of Chemistry 2015 Ligand-free N-arylation of heterocycles using metal-organic framework [Cu(INA) 2 ] as an efficient
More informationCompetitive co-adsorption of CO 2 with H 2 O, NH 3, SO 2, NO, NO 2, N 2, O 2, and CH 4 in M-MOF-74 (M= Mg, Co, Ni): the role of hydrogen bonding
Competitive co-adsorption of C 2 with H 2, NH 3, S 2, N, N 2, N 2, 2, and CH in M-MF-7 (M= Mg, Co, Ni): the role of hydrogen bonding Kui Tan, Sebastian Zuluaga, Qihan Gong, Yuzhi Gao, Nour Nijem, ± Jing
More informationElectronic Supporting Information for
Electronic Supporting Information for Microporous metal-organic open framework containing uncoordinated carbonyl groups as postsynthetic modification sites for cation exchange and Tb 3+ sensor Jianwei
More informationMOF-76: From Luminescent Probe to Highly Efficient U VI Sorption Material
MOF-76: From Luminescent Probe to Highly Efficient U VI Sorption Material Weiting Yang, a Zhi-Qiang Bai, b Wei-Qun Shi*, b Li-Yong Yuan, b Tao Tian, a Zhi-Fang Chai*, c Hao Wang, a and Zhong-Ming Sun*
More informationSupporting Information for. Linker-Directed Vertex Desymmetrization for the Production of Coordination Polymers. with High Porosity
Supporting Information for Linker-Directed Vertex Desymmetrization for the Production of Coordination Polymers with High Porosity Jennifer K. Schnobrich, Olivier Lebel,, Katie A. Cychosz, Anne Dailly,
More informationSynthesis of 2 ) Structures by Small Molecule-Assisted Nucleation for Plasmon-Enhanced Photocatalytic Activity
Electronic Supplementary Material (ESI) for ChemComm. This journal is The Royal Society of Chemistry 2015 Electronic Supplementary Information Synthesis of Au@UiO-66(NH 2 ) Structures by Small Molecule-Assisted
More informationSupporting information. Mechanical Properties of Microcrystalline Metal-Organic Frameworks. (MOFs) Measured by Bimodal Amplitude Modulated-Frequency
Supporting information Mechanical Properties of Microcrystalline Metal-Organic Frameworks (MOFs) Measured by Bimodal Amplitude Modulated-Frequency Modulated Atomic Force Microscopy Yao Sun, Zhigang Hu,
More informationSupporting Information
Supporting Information Functionalized Bimetallic Hydroxides Derived from Metal- Organic Frameworks for High Performance Hybrid Supercapacitor with Exceptional Cycling Stability Chong Qu,, Bote Zhao, Yang
More informationSupporting Information
Supporting Information Selective Propene Oligomerization with Nickel(II)-Based Metal-Organic Frameworks Anton N. Mlinar, a,+ Benjamin K. Keitz, b,+ David Gygi, b Eric D. Bloch, b Jeffrey R. Long,*,b Alexis
More informationMetal Organic Framework-Derived Metal Oxide Embedded in Nitrogen-Doped Graphene Network for High-Performance Lithium-Ion Batteries
Supporting Information for Metal Organic Framework-Derived Metal Oxide Embedded in Nitrogen-Doped Graphene Network for High-Performance Lithium-Ion Batteries Zhu-Yin Sui, Pei-Ying Zhang,, Meng-Ying Xu,
More informationSUPPORTING INFORMATION
Electronic Supplementary Material (ESI) for RSC Advances. This journal is The Royal Society of Chemistry 2015 SUPPORTIG IFORMATIO Expanding applications of zeolite imidazolate frameworks in catalysis:
More informationSelected Applications of Metal-Organic Frameworks in Sustainable Energy Technologies
Page 1 of 8 Page 1 of 8 Return to Web Version Selected Applications of Metal-Organic Frameworks in Sustainable Energy Technologies By: Stephen R. Caskey, Adam J. Matzger, Material Matters 2009, 4.4, 111.
More informationSupplementary Information
Electronic Supplementary Material (ESI) for ChemComm. This journal is The Royal Society of Chemistry 2016 Supplementary Information Rendering Non-Energetic Microporous Coordination Polymers Explosive Kyle
More informationSupporting Information
Supporting Information A strategy toward constructing bifunctionalized MF catalyst: post-synthesized modification of MFs on organic ligands and coordinatively unsaturated metal sites Baiyan Li, Yiming
More informationHaving a High Mg/Al Molar Ratio
SUPPORTING INFORMATION High-Temperature CO 2 Sorption on Hydrotalcite Having a High Mg/Al Molar Ratio Suji Kim, Sang Goo Jeon, and Ki Bong Lee*, Department of Chemical and Biological Engineering, Korea
More informationHigh Pressure Methane Adsorption on a Series of MOF-74: Molecular Simulation Study
The 14 th Iranian National Chemical Engineering Congress (IChEC 2012) Sharif University of Technology, Tehran, Iran, 16-18 October, 2012 High Pressure Methane Adsorption on a Series of MOF-74: Molecular
More informationCooperative Template-Directed Assembly of Mesoporous Metal-Organic Frameworks
Supporting Information Cooperative Template-Directed Assembly of Mesoporous Metal-Organic Frameworks Lin-Bing Sun, Jian-Rong Li, Jinhee Park, and Hong-Cai Zhou* Department of Chemistry, Texas A&M University,
More informationElectronic Supplementary Information (ESI)
Electronic Supplementary Material (ESI) for Chemical Science. This journal is The Royal Society of Chemistry 2017 Electronic Supplementary Information (ESI) Enhancing stability and porosity of penetrated
More informationSupporting Information. Nanoscale Kirkendall Growth of Silicalite-1 Zeolite Mesocrystals with. Controlled Mesoporosity and Size
Electronic Supplementary Material (ESI) for ChemComm. This journal is The Royal Society of Chemistry 2015 Supporting Information Nanoscale Kirkendall Growth of Silicalite-1 Zeolite Mesocrystals with Controlled
More informationSupporting Information
Supporting Information Controllable Adsorption of CO2 on Smart Adsorbents: An Interplay between Amines and Photoresponsive Molecules Lei Cheng, Yao Jiang, Shi-Chao Qi, Wei Liu, Shu-Feng Shan, Peng Tan,
More informationDry-gel conversion synthesis of Cr-MIL-101 aided by grinding: High surface area high yield synthesis with minimum purification
Electronic Supporting Informations (ESI): Dry-gel conversion synthesis of Cr-MIL-101 aided by grinding: High surface area high yield synthesis with minimum purification Jun Kim, Yu-Ri Lee and Wha-Seung
More informationSupporting Information
Electronic Supplementary Material (ESI) for Dalton Transactions. This journal is The Royal Society of Chemistry 2018 Supporting Information Rare metal-ion metathesis of tetrahedral Zn(II) core of a noncentrosymmetric
More informationSupplementary Information for
Supplementary Information for Microwave-Assisted Solvothermal Synthesis of Zirconium Oxide Based Metal-Organic Frameworks Weibin Liang and Deanna M. D Alessandro* School of Chemistry, The University of
More informationElectronic Supporting Information
Electronic Supporting Information Fluorescent Microporous Polyimides based on Perylene and Triazine for Highly CO 2 -Selective Carbon Materials Yaozu Liao, a Jens Weber b and Charl F.J. Faul a* a School
More informationMetal organic Frameworks as Adsorbents for Hydrogen Purification and Pre-Combustion Carbon Dioxide Capture
Supporting Information for: Metal organic Frameworks as Adsorbents for Hydrogen Purification and Pre-Combustion Carbon Dioxide Capture Zoey R. Herm, Joseph A. Swisher, Berend Smit, Rajamani Krishna, Jeffrey
More informationSupporting Information for the manuscript. Metastable interwoven mesoporous metal-organic frameworks
S1 Supporting Information for the manuscript Metastable interwoven mesoporous metal-organic frameworks Yabing He, ab Zhiyong Guo, b Shengchang Xiang, c Zhangjing Zhang, c Wei Zhou, d,e Frank R. Fronczek,
More informationWater Reaction Mechanism in Metal Organic Frameworks with Coordinatively Unsaturated Metal Ions: MOF-74
Water Reaction Mechanism in Metal Organic Frameworks with Coordinatively Unsaturated Metal Ions: MOF-74 Kui Tan 1, Sebastian Zuluaga 2, Qihan Gong 3, Pieremanuele Canepa 2, Hao Wang 3, Jing Li 3, Yves
More informationsensors ISSN by MDPI
Sensors 2006, 6, 318-323 sensors ISSN 1424-8220 2006 by MDPI http://www.mdpi.org/sensors Gas Sensing Properties of Ordered Mesoporous SnO 2 Thorsten Wagner 1,2,*, Claus-Dieter Kohl 1, Michael Fröba 2 and
More informationSUPPORTING INFORMATION
SUPPORTING INFORMATION Unusual pore structure and sorption behaviour in a hexanodal zinc-organic framework material Jinjie Qian a,b Feilong Jiang, a Linjie Zhang, a,b Kongzhao Su, a,b Jie Pan, a,b Qipeng
More informationSupporting Information
Supporting Information Control the Structure of Zr-Tetracarboxylate Frameworks through Steric Tuning Jiandong Pang,,,,# Shuai Yuan,,# Junsheng Qin, Caiping Liu, Christina Lollar, Mingyan Wu,*, Daqiang
More informationSupporting information
Supporting information Metal dependent structural flexibility and intrinsic dynamics in the M 2 (2,6-ndc) 2 (dabco) (M = Ni, Cu, Co, Zn) metal-organic frameworks Nicole Klein, a Herbert C. Hoffmann, a,
More informationSupporting Information
Electronic Supplementary Material (ESI) for ChemComm. This journal is The Royal Society of Chemistry 2014 Supporting Information A Highly stable Metal- and Nitrogen-doped Nanocomposite derived from Zn/Ni-ZIF-8
More informationQingdao Institute of Bioenergy and Bioprocess Technology, Chinese Academy of Science,
Supporting information A rht type Metal-Organic Framework based on Small Cubicuboctahedron Supermolecular Building Blocks and Adsorption Properties Liangjun Li a,b, Sifu Tang a, Xiaoxia Lv a,b, Min Jiang
More informationSupporting Information
A Calcium Coordination Framework Having Permanent Porosity and High CO 2 /N 2 Selectivity Debasis Banerjee, a, * Zhijuan Zhang, b Anna M. Plonka, c Jing Li, b, * and John B. Parise a, c, d, * (a) Department
More informationSupplementary Information
Supplementary Information Fabrication of Novel Rattle-Type Magnetic Mesoporous carbon Microspheres for Removal of Microcystins Xinghua Zhang and Long Jiang* Beijing National Laboratory for Molecular Science
More information1. General Experiments... S2. 2. Synthesis and Experiments... S2 S3. 3. X-Ray Crystal Structures... S4 S8
Electronic Supplementary Material (ESI) for Dalton Transactions. This journal is The Royal Society of Chemistry 2017 Electronic Supplementary Information Gate-Opening upon CO 2 Adsorption on a Metal Organic
More informationSupporting Information
Supporting Information Highly selective carbon dioxide adsorption in a water-stable Indium-organic framework material Jin-Jie Qian, a,bi Fei-Long Jiang, a Da-Qiang Yuan, a Ming-Yan Wu, a Shu-Quan Zhang,
More informationNew Journal of Chemistry Electronic Supplementary Information
Electronic Supplementary Material (ESI) for New Journal of Chemistry. This journal is The Royal Society of Chemistry and the Centre National de la Recherche Scientifique 2018 New Journal of Chemistry Electronic
More informationRSC Advances Supporting Information
Electronic Supplementary Material (ESI) for RSC Advances. This journal is The Royal Society of Chemistry 2015 RSC Advances Supporting Information Metal-organic framework MIL-1 doped with metal nanoparticles
More informationSupporting Information. Rapid synthesis of metal-organic frameworks MIL-101(Cr) without the addition of solvent and hydrofluoric acid
Supporting Information Rapid synthesis of metal-organic frameworks MIL-11(Cr) without the addition of solvent and hydrofluoric acid Kunyue Leng a, Yinyong Sun a *, Xiaolin Li a, Shun Sun a, Wei Xu b a
More informationMetal-Organic Frameworks and Porous Polymer Networks for Carbon Capture
Carbon Capture Workshop, Tuesday, April 3 rd, Texas A&M, Qatar Metal-Organic Frameworks and Porous Polymer Networks for Carbon Capture J. P. Sculley, J.-R. Li, J. Park, W. Lu, and H.-C. Zhou Texas A&M
More informationElectronic Supplementary Information
Electronic Supplementary Material (ESI) for Journal of Materials Chemistry A. This journal is The Royal Society of Chemistry 2014 Electronic Supplementary Information Micro- and mesoporous poly(schiff-base)s
More informationLocal Deprotonation Enables Cation Exchange, Porosity. Modulation and Tunable Adsorption Selectivity in a. Metal-Organic Framework
Supporting Information for Local Deprotonation Enables Cation Exchange, Porosity Modulation and Tunable Adsorption Selectivity in a Metal-Organic Framework Jun-Hao Wang,, Dong Luo, Mian Li, and Dan Li
More informationSelective Binding and Removal of Organic Molecules in a Flexible Polymeric Material with Stretchable Metallosalen Chains
Selective Binding and Removal of Organic Molecules in a Flexible Polymeric Material with Stretchable Metallosalen Chains Gao Li, Chengfeng Zhu, Xiaobing Xi and Yong Cui* School of Chemistry and Chemical
More informationEdinburgh Research Explorer
Edinburgh Research Explorer Development of a Semiautomated Zero Length Column Technique for Carbon Capture Applications Citation for published version: Hu, X, Brandani, S, Benin, AI & Willis, RR 2015,
More informationSupplementary Information
Supplementary Information Tuning the Luminescence of Metal-Organic Frameworks for Detection of Energetic Heterocyclic Compounds Yuexin Guo, Xiao Feng,*, Tianyu Han, Shan Wang, Zhengguo Lin, Yuping Dong,
More informationStructure-Property Relationships of Porous Materials for Carbon Dioxide Separation and Capture
Supporting Information Structure-Property Relationships of Porous Materials for Carbon Dioxide Separation and Capture Christopher E. Wilmer, 1 Omar K. Farha, 2 Youn-Sang Bae, 3,a Joseph T. Hupp, 2 and
More informationSupporting Information
S1 Submitted to J. Am. Chem. Soc. Supporting Information A porous coordination copolymer with over 5000 m 2 /g BET surface area Kyoungmoo Koh, Antek G. Wong-Foy, and Adam J. Matzger* Department of Chemistry,
More informationA high-efficient monoclinic BiVO 4 adsorbent for selective capture toxic selenite
Supporting Online Materials for A high-efficient monoclinic BiVO 4 adsorbent for selective capture toxic selenite Huan Ouyang, Yuanyuan Sun*, and Jianqiang Yu* Collaborative Innovation Center for Marine
More informationCovalent Organic Frameworks in 2013
2014 Super Literature Club@JIANG Lab, IMS Covalent Organic Frameworks in 2013 Presented by Dr. Shangbin Jin Feb. 7, 2014 1 Covalent Organic Frameworks Covalent-bond linked (B-O, C=N,...) Light-weight element
More informationNanoporous Sorbent and its Application for Hydrogen Storage at Ambient Temperature
Journal of Applied Chemical Research, 9, 3, 33-41 (2015) Journal of Applied Chemical Research www.jacr.kiau.ac.ir Synthesis and Characterization of Zn 3 Nanoporous Sorbent and its Application for Hydrogen
More informationEdinburgh Research Explorer
Edinburgh Research Explorer Development of a Semiautomated Zero Length Column Technique for Carbon Capture Applications Citation for published version: Hu, X, Brandani, S, Benin, AI & Willis, RR 015, 'Development
More informationPreparation of Nanofibrous Metal-Organic Framework Filters for. Efficient Air Pollution Control. Supporting Information
Preparation of Nanofibrous Metal-Organic Framework Filters for Efficient Air Pollution Control Supporting Information Yuanyuan Zhang, Shuai Yuan, Xiao Feng, Haiwei Li, Junwen Zhou, Bo Wang* Contents Section
More informationSupporting Information
Electronic Supplementary Material (ESI) for Journal of Materials Chemistry C. This journal is The Royal Society of Chemistry 2018 Supporting Information A difunctional metal organic framework with Lewis
More informationU Shwe Thein Date:04/27/2017 Approved: Prof. John C. MacDonald, advisor
Investigation of bulky carboxylic acid and amines as trapping agents for controlling the desorption of molecular guests from a porous metal-organic framework material A Major Qualifying Project Submitted
More informationHigh capacity hydrogen and nitric oxide adsorption and storage in a metal-organic framework
High capacity hydrogen and nitric oxide adsorption and storage in a metal-organic framework Bo Xiao, 1 Paul S. Wheatley, 1 Xuebo Zhao, Ashleigh J. Fletcher, Sarah Fox Adriano G Rossi, Ian L. Megson, 3
More informationA Third Generation Breathing MOF with Selective, Stepwise, Reversible and Hysteretic Adsorption properties
Supporting information for A Third Generation Breathing MOF with Selective, Stepwise, Reversible and Hysteretic Adsorption properties Suresh Sanda, Srinivasulu Parshamoni and SanjitKonar* Department of
More informationHollowing Out MOFs: Hierarchical Micro- and Mesoporous MOFs with Tailorable Porosity via Selective Acid Etching
Electronic Supplementary Material (ESI) for Chemical Science. This journal is The Royal Society of Chemistry 2017 Supporting Information Hollowing Out MOFs: Hierarchical Micro- and Mesoporous MOFs with
More informationSupporting Information
Supporting Information Exploring the detection of metal ions by tailoring the coordination mode of V-shaped thienylpyridyl ligand in three MOFs Li-Juan Han,, Wei Yan, Shu-Guang Chen, Zhen-Zhen Shi, and
More informationA triazine-based covalent organic polymer for efficient CO 2 adsorption
Electronic Supplementary Material (ESI) for Chemical Communications. This journal is The Royal Society of Chemistry 2015 Supporting Information A triazine-based covalent organic polymer for efficient CO
More informationSupporting Information
Supporting Information Hydrogen Storage in the Dehydrated Prussian Blue Analogues M 3 [Co(CN) 6 ] 2 (M = Mn, Fe, Co, Ni, Cu, Zn) Steven S. Kaye and Jeffrey R. Long* Dept. of Chemistry, University of California,
More informationSupplementary Information
Electronic Supplementary Material (ESI) for Green Chemistry. This journal is The Royal Society of Chemistry 2015 Supplementary Information Efficient vapor-assisted aging synthesis of functional and high
More informationSupple. KBr. C N) cm (s, p-phenenylene
Supple ementary Information Supplementary Figures Supplementary Figure S1. FTIR spectra of azo-cops. The spectra were recorded as KBr pellets. 3400 (s, free N H), 32000 (s, hydrogen bonded N H), 1610 (s,
More informationSupporting Information
Supporting Information Nitrogen-doped coal tar pitch based microporous carbons with superior CO 2 capture performance Dai Yu, Jun Hu, Lihui Zhou *, Jinxia Li, Jing Tang, Changjun Peng, and Honglai Liu
More informationSupplementary Material for. Zinc Oxide-Black Phosphorus Composites for Ultrasensitive Nitrogen
Electronic Supplementary Material (ESI) for Nanoscale Horizons. This journal is The Royal Society of Chemistry 2018 Supplementary Material for Zinc Oxide-Black Phosphorus Composites for Ultrasensitive
More informationFINAL PUBLISHABLE SUMMARY REPORT
Metal-organic frameworks (MOFs) have been an area of intense research over the past two decades and a large number of MOFs have been synthesized and reported since then. [1] These materials deserve special
More informationSupporting Online Material
Supporting Online Material Topology Guided Design and Syntheses of Highly Stable Mesoporous Porphyrinic Zirconium MOFs with High Surface Area. Tian-Fu Liu, a Dawei Feng, a Ying-Pin Chen, a,b Lanfang Zou,
More informationSupplementary Information for : Plasticization-resistant Ni 2 (dobdc)/polyimide composite membranes for CO 2 removal from natural gas
Electronic Supplementary Material (ESI) for Energy & Environmental Science. This journal is The Royal Society of Chemistry 2016 Supplementary Information for : Plasticization-resistant Ni 2 (dobdc)/polyimide
More informationSupporting Information
Electronic Supplementary Material (ESI) for RSC Advances. This journal is The Royal Society of Chemistry 2014 Supporting Information Au nanoparticles supported on magnetically separable Fe 2 O 3 - graphene
More informationSupplementary Figure 1. SEM and TEM images of the metal nanoparticles (MNPs) and metal oxide templates.
Supplementary Figure 1. SEM and TEM images of the metal nanoparticles (MNPs) and metal oxide templates. (a) 13 nm Au, (b) 60 nm Au, (c) 3.3 nm Pt, (d) ZnO spheres, (e) Al 2O 3 spheres and (f) Cu 2O cubes.
More informationSupporting Information
Supporting Information Development of a novel one-pot reaction system utilizing a bifunctional Zr-based metal-organic framework Takashi Toyao, Masakazu Saito, Yu Horiuchi* and Masaya Matsuoka* Department
More informationSynthesis and hydrogen-storage behavior of metal organic framework MOF-5
international journal of hydrogen energy 34 (2009) 1377 1382 Available at www.sciencedirect.com journal homepage: www.elsevier.com/locate/he Synthesis and hydrogen-storage behavior of metal organic framework
More informationMagnetite decorated graphite nanoplatelets as cost effective CO 2 adsorbent
Supplementary Information Magnetite decorated graphite nanoplatelets as cost effective CO 2 adsorbent Ashish Kumar Mishra and Sundara Ramaprabhu * Alternative Energy and Nanotechnology Laboratory (AENL),
More informationSupporting Information. Directing the Breathing Behavior of Pillared-Layered. Metal Organic Frameworks via a Systematic Library of
Supporting Information Directing the Breathing Behavior of Pillared-Layered Metal Organic Frameworks via a Systematic Library of Functionalized Linkers Bearing Flexible Substituents Sebastian Henke, Andreas
More informationSupporting Information. Integration of accessible secondary metal sites into MOFs for H 2 S removal
Electronic Supplementary Material (ESI) for Inorganic Chemistry Frontiers. This journal is the Partner Organisations 2014 Supporting Information Integration of accessible secondary metal sites into MOFs
More informationSupplementary Information. ZIF-8 Immobilized Ni(0) Nanoparticles: Highly Effective Catalysts for Hydrogen Generation from Hydrolysis of Ammonia Borane
Supplementary Information ZIF-8 Immobilized Ni() Nanoparticles: Highly Effective Catalysts for Hydrogen Generation from Hydrolysis of Ammonia Borane Pei-Zhou Li, a,b Kengo Aranishi, a and Qiang Xu* a,b
More informationHigh compressibility of a flexible Metal-Organic-Framework
-Supplementary info file- High compressibility of a flexible Metal-Organic-Framework Pablo Serra-Crespo a, Eli Stavitski b*, Freek Kapteijn a and Jorge Gascon a * a Catalysis Engineering Chemical Engineering
More informationSupporting Information
Electronic Supplementary Material (ESI) for CrystEngComm. This journal is The Royal Society of Chemistry 2018 Supporting Information 2-Methylimidazole-Assisted Synthesis of Two-Dimensional MOF-5 Catalyst
More informationFramework Isomerism in Vanadium Metal. Organic Frameworks: MIL-88B(V) and MIL- 101(V)
Supporting Information Framework Isomerism in Vanadium Metal Organic Frameworks: MIL-88B(V) and MIL- 101(V) Fabian Carson, a,b Jie Su, a,b Ana E. Platero Prats, a,b Wei Wan, a,b Yifeng Yun, a,b Louise
More informationElectronic Supplementary Information
Electronic Supplementary Information The directing effect of linking unit on building microporous architecture in tetraphenyladmantane-based poly(schiffbase) networks Guiyang Li, Biao Zhang, Jun Yan and
More information