CYCLIC ADSORPTION AND DESORPTION OF METHANE AND CARBON DIOXIDE ON COCONUT SHELL ACTIVATED CARBON
|
|
- Christiana Potter
- 6 years ago
- Views:
Transcription
1 CYCLIC ADSORPTION AND DESORPTION OF METHANE AND CARBON DIOXIDE ON COCONUT SHELL ACTIVATED CARBON Suwadee Uttaraphat a, Pramoch Rungsunvigit *,a,b, Boonyarach Kitiyanan a,b, Santi Kulprathipanja c a) The Petroleum and Petrochemical College, Chulalongkorn University b) Center of Excellence on Petrochemical and Materials Technology c) UOP, A Honeywell Company, Des Plaines, Illinois, U.S.A. Keywords: Adsorbed natural gas, Methane adsorption, Coconut shell activated carbon ABSTRACT Adsorbed Natural Gas (ANG) technology based on natural gas adsorption in porous materials at relatively MPa and at room temperature is challenging. In this work, cyclic adsorption and desorption of carbon dioxide and methane by using coconut shell activated carbon (CSAC) was investigated. For every cycle, pure carbon dioxide was fed into the packed bed column for one hour in the adsorption step. After that, the desorption step started by using pure methane for one hour. The cycle was repeated for ten times. The same results were shown in all cycles. In the adsorption step, carbon dioxide was adsorbed on the CSAC, and the breakthrough time was around 20 minutes. For the desorption step, methane slowly adsorbed on the CSAC while carbon dioxide continually desorbed out. After one hour of desorption step, carbon dioxide remained on the CSAC around 1-2 percent of the initial concentration. It can be concluded that methane can desorb carbon dioxide on the CSAC in many repetitions of adsorption and desorption. *pramoch.r@chula.ac.th INTRODUCTION Natural gas is a popular fuel and has been promoted for use in automobile field because of its environmental advantages, and it is a cheaper fuel than diesel or gasoline. It can be used as a fuel for many vehicles such as cars, trucks, and jet engines (Wang and Huang, 1999). However, natural gas has low-energy density (heat of combustion/volume), which constitutes a limitation for some applications (Solar et al., 2010). To make adsorbed natural gas (ANG) systems competitive to gasoline or diesel fuel, the cost of its storage and refueling systems must be reduced drastically. ANG technology based on natural gas adsorption on porous materials at relatively low pressures MPa and at room temperature is a challenge to the liquid fuel application (Vasiliev et al., 2000). In this work, the appropriate desorption time of adsorption and desorption of carbon dioxide and methane by using coconut shell activated carbon (CSAC) was repeated. First, pure carbon dioxide was fed into the packed bed column for one hour in the adsorption step. After that, the desorption step started by using pure methane for many hours. Moreover, the cyclic adsorption and desorption of carbon dioxide and methane was investigated. For every cycle, pure carbon dioxide was fed into the packed bed column for one hour in the adsorption step followed by the desorption step, using pure methane at the appropriate desorption time. The cycle was repeated for ten times. Petrochemical and Materials Technology Tuesday May 23, 2017, Pathumwan Princess Hotel, Bangkok, Thailand Page 1
2 EXPERIMENTAL A. Adsorbent Preparation CSAC was grinded and sieved to obtain a particle size of mesh. It was dried at 120 C for 24 hours to remove moisture. B. Adsorbent Characterization The surface area, total pore volume, and pore size distribution of the adsorbents was measured by a Quantachrom/Autosorb1-MP instrument. The adsorbents were first out gassed to remove the humidity on its surface under vacuum at 300 C for 16 hours prior to the analysis. After that, nitrogen was purged to adsorb on its surface. The volumepressure data was used to calculate the BET surface area, total pore volume, and pore size distribution. The morphology of the adsorbents was investigated by using the FE- SEM, Hitachi S-4800, with an accelerating voltage of 2 kv and varying magnifications of 500, 2,000, and 25,000. The adsorbents were coated with platinum under vacuum condition before observation. C. Adsorption Measurement Thermo-volumetric apparatus was constructed to study the gas-solid interaction between methane/carbon dioxide and potential solid adsorbents. The schematic of the experimental set-up for the dynamic adsorption of methane and carbon dioxide is shown in Figure 1. The set-up consisted of a high pressure stainless steel reactor, which held the sample and part of stainless steel tube as a gas reservoir. A pressure transducer was used to measure pressure of the system in the range of 0-3,000 psig with a 0.13% global error. A pressure regulator with 4,000 psig maximum limit was installed to control a gas flow rate into the whole system. Figure 1 Schematic of the experimental set-up for the dynamic adsorption of CH 4 and CO 2. Petrochemical and Materials Technology Tuesday May 23, 2017, Pathumwan Princess Hotel, Bangkok, Thailand Page 2
3 RESULTS AND DISCUSSION A. Adsorbent Characterizations Table 1 shows the summary of the BET surface area, total pore volume, micropore volume, and average pore diameter of the adsorbents. The averages of BET surface area, total pore volume, micropore volume, and average pore diameter of CSAC are 1,015 m 2 /g, cm 3 /g, cm 3 /g, and 22.1 Å, respectively. The micropore volume of CSAC is almost similar with the total pore volume, which could be confirmed by the pore size distribution, shown in the range of micropore. Table 1 BET surface area, total pore volume, micropore volume, and average pore diameter of investigated adsorbents Adsorbent BET surface area (m 2 /g) Physical characterization Total pore volume (cm 3 /g) Micropore volume (cm 3 /g) Average pore diameter (Å) CSAC (1) 1, CSAC (2) 1, Average 1, The SEM micrographs show that the CSAC has a high degree of porosity and contains the largest possible number of randomly distributed pores of various shapes and size, that cause the CSAC to be a porous material with an extended and extremely high surface area. Moreover, the SEM micrographs also show that the CSAC exhibits dust or impurity in the pores, which may block the pores, and the adsorbates (methane and carbon dioxide) cannot reach into the pores, resulted in the decrease in the adsorption capacity. (a) (b) (c) Figure 2 SEM micrographs for (a) magnification of 500, (b) magnification of 2,000, and (c) magnification of 25,000. Petrochemical and Materials Technology Tuesday May 23, 2017, Pathumwan Princess Hotel, Bangkok, Thailand Page 3
4 B. Desorption time by using methane as a desorbent Investigation on one cycle adsorption of pure methane and carbon dioxide by using coconut shell activated carbon (CSAC) was carried out in a stainless steel packed bed column with an inside diameter of 10.2 mm at atmospheric pressure and room temperature. Pure carbon dioxide was fed into packed bed column at the flow rate of 50 ml/min for one hour in the adsorption step after that the desorption step started by using pure methane with the same flow rate. To determine the proper desorption time, pure methane was fed into pack bed column until virtually no carbon dioxide was detected. Figure 3 Pure carbon dioxide adsorption and desorption by using pure methane at room temperature for CO 2 adsorption ( ), CO 2 desorption ( ), CH 4 adsorption in the desorption step ( ). From the results in Figure 3, CO 2 adsorption line shows that carbon dioxide is adsorbed on the CSAC, and the breakthrough time is around 20 minutes. For the desorption step, carbon dioxide is desorbed out by the time when methane is fed into the packed bed column. CO 2 desorption line shows all carbon dioxide comes out around 60 minutes after the desorption starts. Hence, the proper desorption time of the cyclic adsorption and desorption of carbon dioxide on the CSAC by methane as a desorbent should be one hour, and the desorption time that more than one hour does not play an important role on the carbon dioxide desorption by using pure methane at room temperature. On the other hand, methane is adsorbed on the CSAC, and the breakthrough time is less than 2.5 minutes. It can be seen that the breakthrough time of carbon dioxide is longer than methane because the activated carbon reaches its saturation slower, so the adsorption capacity of carbon dioxide on the CSAS is higher than methane. Petrochemical and Materials Technology Tuesday May 23, 2017, Pathumwan Princess Hotel, Bangkok, Thailand Page 4
5 C. Effect of methane adsorption on the cyclic adsorption and desorption of carbon dioxide on CSAC The cyclic adsorption and desorption of methane and carbon dioxide on the CSAC was followed and applied. For every cycle, pure carbon dioxide was fed into the packed bed column with the flow rate of 50 ml/min for one hour in the adsorption step. After that, the desorption step started by using pure methane with the same flow rate for one hour. The cycle was repeated for ten times. Figure 4 Adsorption and desorption of carbon dioxide and methane for 10 cycles, (Blue) CH 4, (Green) CO 2 for adsorption step, (Pink) CH4, and (Red) CO2 for desorption step. Figure 4 shows the same results in all cycles. In the adsorption step, carbon dioxide is adsorbed on the CSAC, and the breakthrough time is around 20 minutes. For the desorption step, methane is slowly adsorbed on the CSAC, while carbon dioxide continually desorbs out. After one hour of desorption step, carbon dioxide remains on the CSAC around 1-2 percent of the initial concentration. It can be concluded that methane can adsorb on the CSAC that fully saturated with carbon dioxide in many repetition of adsorption and desorption. CONCLUSIONS This research investigated on the cyclic adsorption and desorption of methane and carbon dioxide on coconut shell activated carbon (CSAC) by using methane as a Petrochemical and Materials Technology Tuesday May 23, 2017, Pathumwan Princess Hotel, Bangkok, Thailand Page 5
6 desorbent. Carbon dioxide is desorbed out by the time when methane is fed into the packed bed column. All carbon dioxide comes out around 60 minutes after the desorption starts. For ten repetitions, carbon dioxide is replaced by methane and remains on the CSAC only 1-2 percent, confirming methane can be used as a desorbent for the adsorption and desorption of methane and carbon dioxide on CSAC. ACKNOWLEDGEMENTS The authors would like to sincerely thank the National Research Council of Thailand; The 90 th Anniversary of Chulalongkorn University Fund and Grant for International Integration: Chula Research Scholar, Ratchadapiseksomphot Endowment Fund, Chulalongkorn University, Thailand; Center of Excellence on Petrochemicals and Materials Technology; The Petroleum and Petrochemical College, Chulalongkorn University, Thailand; UOP, A Honeywell Company, USA for providing support for this research work. REFERENCES Solar, C., Blanco, A.G., Vallone, A., and Sapag, K. (2010). Natural Gas, Vasiliev, L.L., Kanonchik, L.E., Mishkinis, D.A., and Rabetsky, M.I. (2000). International Journal of Thermal Sciences, 39(9 11), Wang, M.Q. and Huang, H.S. (1999). Center for Transportation Research, U.S. Department of Energy. Petrochemical and Materials Technology Tuesday May 23, 2017, Pathumwan Princess Hotel, Bangkok, Thailand Page 6
Competitive Adsorption of Methane and Carbon Dioxide on Different Activated Carbons
A publication of CHEMICAL ENGINEERING TRANSACTIONS VOL., Guest Editors: Petar Sabev Varbanov, Peng-Yen Liew, Jun-Yow Yong, Jiří Jaromír Klemeš, Hon Loong Lam Copyright, AIDIC Servizi S.r.l., ISBN 98-88-98--;
More informationPREPARATION OF NITROGEN ENRICHED HIERARCHICALLY NANOPOROUS CARBON FROM POLYBENZOXAZINE FOR METHANE STORAGE
PREPARATION OF NITROGEN ENRICHED HIERARCHICALLY NANOPOROUS CARBON FROM POLYBENZOXAZINE FOR METHANE STORAGE Norawit Kaewpornmongkol a and Thanyalak Chaisuwan *,a,b a The Petroleum and Petrochemical College,
More informationEffects of TiO 2 and Nb 2 O 5 on Hydrogen Desorption of Mg(BH 4 ) 2
International Journal of Chemical and Biological Engineering Effects of TiO and Nb O on Hydrogen Desorption of Mg(BH ) Wipada Ploysuksai, Pramoch Rangsunvigit, Santi Kulprathipanja Abstract In this work,
More informationEffects of Mixed Surfactants on Methane Hydrate Formation and Dissociation
151 A publication of CHEMICAL ENGINEERING TRANSACTIONS VOL. 52, 2016 Guest Editors: Petar Sabev Varbanov, Peng-Yen Liew, Jun-Yow Yong, Jiří Jaromír Klemeš, Hon Loong Lam Copyright 2016, AIDIC Servizi S.r.l.,
More informationUPGRADING OF PETROLEUM RESIDUE BY NITROGEN DOPING FOR CO 2 ADSORPTION
UPGRADING OF PETROLEUM RESIDUE BY NITROGEN DOPING FOR CO 2 ADSORPTION Nattha Chalermwat a,b, Thanyalak Chaisuwan a,b, Uthaiporn Suriyapraphadilok*,a,b a The Petroleum and Petrochemical College, Chulalongkorn
More informationHigh-Pressure Volumetric Analyzer
High-Pressure Volumetric Analyzer High-Pressure Volumetric Analysis HPVA II Benefits Dual free-space measurement for accurate isotherm data Free space can be measured or entered Correction for non-ideality
More informationDEVELOPMENT OF CATALYSTS FOR ETHANE EPOXIDATION REACTION. Keywords: Ethylene oxide, Partial oxidation, Ethane epoxidation, Second metal.
DEVELOPMENT OF CATALYSTS FOR ETHANE EPOXIDATION REACTION Kingsuda Mahunee a, Krittiya Pornmai a, Sitthiphong Pengpanich c, Sumaeth Chavade j* a,b a The Petroleum and Petrochemical College, Chulalongkorn
More informationPressure Swing Adsorption: A Gas Separation & Purification Process
Pressure Swing Adsorption: A Gas Separation & Purification Process Pressure swing adsorption is an adsorption-based process that has been used for various gas separation and purification purposes. Separation
More informationREMOVAL OF ALKALINE EARTH METALS BY USING POLYBENZOXAZINE AND CARBON-BASED NANOPOROUS MATERIALS
REMOVAL OF ALKALINE EARTH METALS BY USING POLYBENZOXAZINE AND CARBON-BASED NANOPOROUS MATERIALS Chanapon Pongteeraporn a, Sujitra Wongkasemjit a,b, Thanyalak Chaisuwan a,b a The Petroleum and Petrochemical
More informationACTIVATED CARBON FOR GAS ADSORPTION
IV International Seminar Heat Pipes, Heat Pumps, Refrigerators Minsk,Belarus, September 4-7, 2000 ACTIVATED CARBON FOR GAS ADSORPTION A.M. Safonova, N. K.Luneva * L.L. Vasiliev, D.A. Mishkinis ** * Institute
More informationThe Vacuum Sorption Solution
The Total Sorption Solution The Vacuum Sorption Solution The Vacuum Sorption Solution www.thesorptionsolution.com About the Technique DVS Vacuum - the only gravimetric system that supports static and dynamic
More informationDEVELOPMENT OF POLYELECTROLYTES COMPLEX MEMBRANE FOR SUPERCAPACITOR
DEVELOPMENT OF POLYELECTROLYTES COMPLEX MEMBRANE FOR SUPERCAPACITOR Pisut Wijitsettakun a, Stephan Thierry Dubas a a The Petroleum and Petrochemical College, Chulalongkorn University, Bangkok, Thailand
More informationStudying the Effect of H 2 SO 4 /H 2 O Ratio on the Properties of Positive Electrode in Lead-acid Battery
Iraqi Journal of Chemical and Petroleum Engineering Iraqi Journal of Chemical and Petroleum Engineering Vol.9 No.1 (March 2008) 45-49 ISSN: 1997-4884 University of Baghdad College of Engineering Studying
More informationEFFECTS OF POST-TREATMENT STEAMING ON CATALYTIC PERFORMANCE OF MODIFIED HZSM-5 CATALYSTS FOR THE CONVERSION OF n-pentane TO AROMATICS
EFFECTS OF POST-TREATMENT STEAMING ON CATALYTIC PERFORMANCE OF MODIFIED HZSM-5 CATALYSTS FOR THE CONVERSION OF n-pentane TO AROMATICS Chaninwut Kalajuck a, Siriporn Jongpatiwut*,a,b, Thirasak Rirksomboon
More informationTowards CO 2 Adsorption Enhancement via Polyethyleneimine Impregnation
Towards CO 2 Adsorption Enhancement via Polyethyleneimine Impregnation Supasinee Pipatsantipong, Pramoch Rangsunvigit, Santi Kulprathipanja Abstract To reduce the carbon dioxide emission into the atmosphere,
More informationMetal-Organic Frameworks and Porous Polymer Networks for Carbon Capture
Carbon Capture Workshop, Tuesday, April 3 rd, Texas A&M, Qatar Metal-Organic Frameworks and Porous Polymer Networks for Carbon Capture J. P. Sculley, J.-R. Li, J. Park, W. Lu, and H.-C. Zhou Texas A&M
More informationSYNTHESIS OF ZEOLITE FROM
SYNTHESIS OF ZEOLITE FROM COAL FLY ASH: ITS APPLICATION AS WATER SORBENT Thepparat Klamrassamee 1, Prasert Pavasant 2 and Navadol Laosiripojana 1 * 1 The Joint Graduate School of Energy and Environment,
More informationCarbon molecular sieves production and performance assessment in carbon dioxide separation
JOURNAL OF OPTOELECTRONICS AND ADVANCED MATERIALS Vol. 9, No. 7, July 2007, p. 2296-2301 Carbon molecular sieves production and performance assessment in carbon dioxide separation M. VĂDUVA *, V. STANCIU
More informationSupporting Information High Activity and Selectivity of Ag/SiO 2 Catalyst for Hydrogenation of Dimethyloxalate
Supporting Information High Activity and Selectivity of Ag/SiO 2 Catalyst for Hydrogenation of Dimethyloxalate An-Yuan Yin, Xiao-Yang Guo, Wei-Lin Dai*, Kang-Nian Fan Shanghai Key Laboratory of Molecular
More informationSupplementary Information
Electronic Supplementary Material (ESI) for Nanoscale. This journal is The Royal Society of Chemistry 2014 Supplementary Information A honeycomb-like porous carbon derived from pomelo peel for use in high-performance
More informationADSORPTION OF TOLUENE VAPOUR ON ACTIVATED CARBON FIBRE
ADSORPTION OF TOLUENE VAPOUR ON ACTIVATED CARBON FIBRE Hua-Cun Huang 1, Xiao-Ping Zhang 1 *, Zhi-Hui Wang 1, Shui-Xie Chen 2 1. Evironmental Science & Enineering Department, South China University of Technology,
More informationFigure 1. Pore size distribution
Product Information '2:(;Ã237,325(Ã/ÃDQGÃ9 Polymeric Adsorbents Dow has developed a new polymeric adsorbent type for the concentration of organics from air and water. Key features of these adsorbents are:
More informationUtilization of Rice Husk Ash Silica in Controlled Releasing Application
Journal of Metals, Materials and Minerals, Vol.9 No.2 pp.6-65, 29 Utilization of Rice Husk Ash Silica in Controlled Releasing Application Piyawan PRAWINGWONG, Chaiyan CHAIYA 2, Prasert REUBROYCHAROEN 3
More informationINVESTIGATION OF PREFERENTIAL SORPTION BEHAVIOUR OF CO 2 AND CH 4 ON COALS BY HIGH PRESSURE ADSORPTION/DESORPTION EXPERIMENTS WITH GAS MIXTURES
0350 INVESTIGATION OF PREFERENTIAL SORPTION BEHAVIOUR OF CO 2 AND CH 4 ON COALS BY HIGH PRESSURE ADSORPTION/DESORPTION EXPERIMENTS WITH GAS MIXTURES A. Busch, Y. Gensterblum, N. Siemons, B.M. Krooss, Aachen
More informationADSORPTION AND DESORPTION OF CO ON SOLID SORBENTS
ADSORPTION AND DESORPTION OF CO ON SOLID SORBENTS Ranjani Siriwardane (rsiiw@netl.doe.gov; 34-85-4513) Ming Shen (mshen@netl.doe.gov; 34-85-411) Edward Fisher (efishe@netl.doe.gov; 34-85-411) James Poston
More informationTHE STUDY OF ION SORPTION PERFORMANCES OF STOICHIOMETRIC AND NON-STOICHIOMETRIC POLYELECTROLYTE COMPLEXES.
THE STUDY OF ION SORPTION PERFORMANCES OF STOICHIOMETRIC AND NON-STOICHIOMETRIC POLYELECTROLYTE COMPLEXES. Pha-sita Plengplung a and Stephan T. Dubas *,a,b a The Petroleum and Petrochemical College, Chulalongkorn
More informationStudies on Mo/HZSM-5 Complex catalyst for Methane Aromatization
Journal of Natural Gas Chemistry 13(2004)36 40 Studies on Mo/HZSM-5 Complex catalyst for Methane Aromatization Qun Dong 1, Xiaofei Zhao 1, Jian Wang 1, M Ichikawa 2 1. Department of Petrochemical Engineering,
More informationPRODUCING ACTIVED CARBONS FROM PINECONES VIA CHEMICAL ACTIVATION. Abstract. Introduction. Experimental
PRODUCING ACTIVED CARBONS FROM PINECONES VIA CHEMICAL ACTIVATION Esin Apaydın Varol, Dept. of Chemical Engineering, Anadolu University, Eskisehir, Turkey Ersan Pütün, Dept. of Material Science and Engineering,
More informationMetal-Organic Frameworks for Adsorbed Natural Gas Fuel Systems. Hong-Cai Joe Zhou Department of Chemistry Texas A&M University
Metal-Organic Frameworks for Adsorbed Natural Gas Fuel Systems Hong-Cai Joe Zhou Department of Chemistry Texas A&M University 2 US primary energy consumption by fuel, 1980-2035 (quadrillion Btu per year)
More informationSupporting Information
Electronic Supplementary Material (ESI) for Energy & Environmental Science. This journal is The Royal Society of Chemistry 2018 Supporting Information One-of-A-Kind: A Microporous Metal-Organic Framework
More informationPolyethyleneimine Loading into High Internal Phase Emulsion Polymer for CO 2 Adsorption: Synthesis and Characterization of the PolyHIPE
A publication of CHEMICAL ENGINEERING TRANSACTIONS VOL. 29, 2012 Guest Editors: Petar Sabev Varbanov, Hon Loong Lam, Jiří Jaromír Klemeš Copyright 2012, AIDIC Servizi S.r.l., ISBN 978-88-95608-20-4; ISSN
More informationSupporting Information
Supporting Information Hypercrosslinked Organic Microporous Polymers Based on Alternative Copolymerization of Bismaleimide Hui Gao, Lei Ding, Wenqing Li, Guifeng Ma, Hua Bai and Lei Li *, College of Materials,
More informationSupporting Information
Supporting Information Unprecedented activation and CO 2 capture properties of an elastic single-molecule trap Mario Wriedt, a Julian P. Sculley, b Wolfgang M. Verdegaal, b Andrey A. Yakovenko b and Hong-Cai
More informationBACKGROUND GOALS AND OBJECTIVES
Padmavathi Iyengar has earned a M.Sc. in civil and environmental engineering and is now studying for her M.Sc. in geology at the University of Missouri in Kansas City. Her advisor is Dr. Jejung Lee and
More informationAmine-impregnated silica monolith with a hierarchical pore structure: enhancement of CO 2 capture capacity
1 Electronic Supplementary Information (ESI) Amine-impregnated silica monolith with a hierarchical pore structure: enhancement of CO 2 capture capacity for Chao Chen, Seung-Tae Yang, Wha-Seung Ahn* and
More informationPreparation and Characterization of Activated Carbon from the Prosopis juliflora Plant
Asian Journal of Chemistry Vol. 20, No. 3 (2008), 1702-1706 Preparation and Characterization of Activated Carbon from the Prosopis juliflora Plant A. JAFAR AHAMED* and K. RIAZ AHAMED Department of Chemistry,
More informationKMUTNB Int J Appl Sci Technol, Vol. 9, No. 4, pp , 2016
KMUTNB Int J Appl Sci Technol, Vol. 9, No. 4, pp. 255 259, 216 Research Article Effect of Strong Metal Support Interactions of Supported Ni and Ni-Co Catalyst on Metal Dispersion and Catalytic Activity
More informationAdsorption (Ch 12) - mass transfer to an interface
Adsorption (Ch 12) - mass transfer to an interface (Absorption - mass transfer to another phase) Gas or liquid adsorption (molecular) onto solid surface Porous solids provide high surface area per weight
More informationPorous Solids for Biogas Upgrading
WASTES: Solutions, Treatments and Opportunities 2 nd International Conference September 11 th 13 th 2013 Porous Solids for Biogas Upgrading J.A.C. Silva 1 and A.E. Rodrigues 2 1 Escola Superior de Tecnologia
More informationCarbon Dioxide Adsorption using Activated Carbon via Chemical Vapor Deposition Process
Article Carbon Dioxide Adsorption using Activated Carbon via Chemical Vapor Deposition Process Rewadee Anuwattana, 1,a Chaiwat Patkool 2, and Petchporn Chawakitchareon 2,b 1 Environment and Resources Technology
More informationNanoporous TiO 2 Nanoparticle Assemblies with Mesoscale Morphologies: Nano-Cabbage versus Sea-Anemone
Electronic Supplementary Material (ESI) for Nanoscale. This journal is The Royal Society of Chemistry 2014 Supplemental Documents Nanoporous TiO 2 Nanoparticle Assemblies with Mesoscale Morphologies: Nano-Cabbage
More informationExperimental Methods and Analysis
Chapter 3 28 Experimental Methods and Analysis 1. Equipment The fundamental basis of quantitative adsorption analysis is the measurement of excess adsorption isotherms. Each isotherm comprises a series
More informationAtmospheric Analysis Gases. Sampling and analysis of gaseous compounds
Atmospheric Analysis Gases Sampling and analysis of gaseous compounds Introduction - External environment (ambient air) ; global warming, acid rain, introduction of pollutants, etc - Internal environment
More informationAdsorption equilibrium and dynamics of toluene vapors onto three kinds of silica gels
IOP Conference Series: Materials Science and Engineering PAPER OPEN ACCESS Adsorption equilibrium and dynamics of toluene vapors onto three kinds of silica gels To cite this article: K L Yan and Q Wang
More informationEffect of Temperature on the Adsorption and Desorption Characteristics of Methyl Iodide over TEDA-Impregnated Activated Carbon
Carbon Science Vol. 2, No. 1 March 2001 pp. 9-14 Effect of Temperature on the Adsorption and Desorption Characteristics of Methyl Iodide over TEDA-Impregnated Activated Carbon Geun-Il Park H, In-Tae Kim,
More informationCHAPTER 4 CHEMICAL MODIFICATION OF ACTIVATED CARBON CLOTH FOR POTENTIAL USE AS ELECTRODES IN CAPACITIVE DEIONIZATION PROCESS
CHAPTER 4 CHEMICAL MODIFICATION OF ACTIVATED CARBON CLOTH FOR POTENTIAL USE AS ELECTRODES IN CAPACITIVE DEIONIZATION PROCESS 4.1 INTRODUCTION Capacitive deionization (CDI) is one of the promising energy
More informationCHANGES IN SURFACE PROPERTIES OF KAOLIN MINERAL IN DEALUMINATION PROCESS BY SULFURIC ACID TREATMENT
Clay Science 5, 163-169 (1978) 163 CHANGES IN SURFACE PROPERTIES OF KAOLIN MINERAL IN DEALUMINATION PROCESS BY SULFURIC ACID TREATMENT MIN CHE CHON Chon Engineering Co., Ltd., Seoul Korea AND TATSURO TSURU
More informationSupporting Information
Electronic Supplementary Material (ESI) for Chemical Communications. This journal is The Royal Society of Chemistry 2018 Supporting Information Precise-Control Synthesis of α-/β-mno 2 Materials by Adding
More informationSynthesis of a Zeolite Column with a Monolithic Microhoneycomb Structure Using the Ice Template Method
Synthesis of a Zeolite Column with a Monolithic Microhoneycomb Structure Using the Ice Template Method Shin R. Mukai, Shinya Murata, Kazufusa Onodera and Izumi Yamada *1 Graduate School of Engineering,
More informationDetermination of Effective Diffusion Coefficient of Methane Adsorption on Activated Carbon
World Applied Sciences Journal 17 (9): 1109-1114, 2012 ISSN 1818-4952 IDOSI Publications, 2012 Determination of Effective Diffusion Coefficient of Methane Adsorption on Activated Carbon Alireza Azimi and
More informationAdsorption of Hg 0 on the Unburned Carbon with HF Acid Leaching
Journal of Minerals & Materials Characterization & Engineering, Vol. 3, No.1, pp 41-51, 24 jmmce.org Printed in the USA. All rights reserved Adsorption of Hg on the Unburned Carbon with HF Acid Leaching
More informationElucidation of the Influence of Ni-Co Catalytic Properties on Dry Methane Reforming Performance
925 A publication of CHEMICAL ENGINEERING TRANSACTIONS VOL. 43, 2015 Chief Editors: Sauro Pierucci, Jiří J. Klemeš Copyright 2015, AIDIC Servizi S.r.l., ISBN 978-88-95608-34-1; ISSN 2283-9216 The Italian
More informationDESORPTION OF BURITI OIL (Mauritia flexuosa, Mart.) From ALUMINA USING SUPERCRITICAL CO 2
DESORPTION OF BURITI OIL (Mauritia flexuosa, Mart.) From ALUMINA USING SUPERCRITICAL CO 2 1 Cunha, M.A.E.; 2 Machado, N. T*.; 2 Araújo, M. E, 3 França, L.F. 1 University of the State of Pará.Center for
More informationSelective Hydrogenation of 1-Hexyne Using Pd-Cu and Pd- W Supported on Alumina Catalysts
847 A publication of CHEMICAL ENGINEERINGTRANSACTIONS VOL. 32, 13 Chief Editors:SauroPierucci, JiříJ. Klemeš Copyright 13, AIDIC ServiziS.r.l., ISBN 978-88-9568-23-5; ISSN 1974-9791 The Italian Association
More informationCovalent-Organic Frameworks: Potential Host Materials for Sulfur Impregnation in Lithium-Sulfur Batteries
Electronic Supplementary Material (ESI) for Journal of Materials Chemistry A. This journal is The Royal Society of Chemistry 2014 Covalent-Organic Frameworks: Potential Host Materials for Sulfur Impregnation
More informationUrchin-like Ni-P microstructures: A facile synthesis, properties. and application in the fast removal of heavy-metal ions
SUPPORTING INFORMATION Urchin-like Ni-P microstructures: A facile synthesis, properties and application in the fast removal of heavy-metal ions Yonghong Ni *a, Kai Mi a, Chao Cheng a, Jun Xia a, Xiang
More informationSupporting information
Supporting information Hierarchical Macro-meso-microporous ZSM-5 Zeolite Hollow Fibers With Highly Efficient Catalytic Cracking Capability Jia Liu, a Guiyuan Jiang,* a Ying Liu, a Jiancheng Di, b Yajun
More informationHydrogen Adsorption and Storage on Porous Materials. School of Chemical Engineering and Advanced Materials. Newcastle University United Kingdom
Hydrogen Adsorption and Storage on Porous Materials K. M. Thomas. School of Chemical Engineering and Advanced Materials H2FC SUPERGEN Conference Birmingham University, 16-18 th December 2013 Newcastle
More informationSeparation Benzene and Toluene from BTX using Zeolite 13X
Iraqi Journal of Chemical and Petroleum Engineering Iraqi Journal of Chemical and Petroleum Engineering Vol.9 No.3 (September 27) 7-24 ISSN: 997-4884 University of Baghdad College of Engineering Separation
More informationStrategic use of CuAlO 2 as a sustained release catalyst for production of hydrogen from methanol steam reforming
Electronic Supplementary Material (ESI) for ChemComm. This journal is The Royal Society of Chemistry 2018 Electronic Supplementary Information Strategic use of CuAlO 2 as a sustained release catalyst for
More informationLecture 7. Sorption-Separation Equipment
Lecture 7. Sorption-Separation Equipment Adsorption - Stirred-tank, slurry operation - Cyclic fixed-bed batch operation - Thermal (temperature)-swing adsorption - Fluidizing bed for adsorption and moving
More informationA high-efficient monoclinic BiVO 4 adsorbent for selective capture toxic selenite
Supporting Online Materials for A high-efficient monoclinic BiVO 4 adsorbent for selective capture toxic selenite Huan Ouyang, Yuanyuan Sun*, and Jianqiang Yu* Collaborative Innovation Center for Marine
More informationPREPARATION OF ACTIVATED CARBON FROM PULP AND PAPER MILL WASTES TO BE TESTED FOR THE ADSORPTION OF VOCS
PREPARATION OF ACTIVATED CARBON FROM PULP AND PAPER MILL WASTES TO BE TESTED FOR THE ADSORPTION OF VOCS A. GREGÓRIO *, A. GARCIA-GARCIA #, D. BOAVIDA *, I. GULYURTLU * AND I. CABRITA * * Department of
More informationSynthesis of ordered microporous carbons via template technique
Synthesis of ordered microporous carbons via template technique Zhou Ying, Yao Qimei, Qiu Jieshan *, Guo Hongchen, Sun Zongwei Carbon Research Laboratory, Center for Nano Materials and Science, School
More informationPreparation of biomass derived porous carbon: Application for methane energy storage
Edith Cowan University Research Online ECU Publications Post 013 016 Preparation of biomass derived porous carbon: Application for methane energy storage Yong Sun Edith Cowan University, y.sun@ecu.edu.au
More informationKeywords: Adsorption; Carbon nanotubes; Desorption; Dynamics of adsorption and desorption; Hydrogen
International Journal of Technology (2015) 7: 1128-1136 ISSN 2086-9614 IJTech 2015 ADSORPTION CAPACITY AND ITS DYNAMIC BEHAVIOR OF THE HYDROGEN STORAGE ON CARBON NANOTUBES Mahmud Sudibandriyo 1*, Praswasti
More informationSUPERCRITICAL CARBON DIOXIDE DESORPTION OF XYLENE FROM ZEOLITE
SUPERCRITICAL CARBON DIOXIDE DESORPTION OF XYLENE FROM ZEOLITE Stéphane VITU and Danielle BARTH ( * ) Institut National Polytechnique de Lorraine Ecole Nationale Supérieure des Industries Chimiques Laboratoire
More informationAlumina & Pseudoboehmite & Molecular sieve
Activated Alumina & Activated alumina, Pseudoboehmite & Molecular sieve Pseudoboehmite & Molecular sieve Quality and advanced Technology About XiangRun Catalyst & Adsorbent Why Choose Xiangrun? Zibo XiangRun
More informationHiden Isochema. Gravimetric Gas & Vapor Sorption Analyzers. Hiden Isochema IGA Series. Advancing Sorption Analysis
Technical Specifications The IGA-1 is designed for gravimetric mixed gas sorption, as well as single component vapor sorption analysis, and powerfully combines the features of the IGA-1, IGA-2 and IGA-3.
More informationEXECUTIVE SUMMARY. especially in last 50 years. Industries, especially power industry, are the large anthropogenic
EXECUTIVE SUMMARY Introduction The concentration of CO 2 in atmosphere has increased considerably in last 100 years, especially in last 50 years. Industries, especially power industry, are the large anthropogenic
More informationAn Ideal Electrode Material, 3D Surface-Microporous Graphene for Supercapacitors with Ultrahigh Areal Capacitance
Supporting Information An Ideal Electrode Material, 3D Surface-Microporous Graphene for Supercapacitors with Ultrahigh Areal Capacitance Liang Chang, 1 Dario J. Stacchiola 2 and Yun Hang Hu 1, * 1. Department
More informationElectronic Supplementary Information (ESI)
Electronic Supplementary Information (ESI) Experimental Materials Synthesis: The α-fe 2 O 3 MSHSs hollow microspheres were prepared by a spray drying method followed by annealing in air. In a typical synthesis
More informationFigure 1 Cinnamaldehyde hydrogenation pathways
CATALYTIC ACTIVITY OF Ni x Sn y INTERMETALLICS Anchernsiri Noomnual a,b, Sakollapath Pithakratanayothin a, Thanyalak Chaisuwan a,b, Sujitra Wongkasemjit*,a,b a The Petroleum and Petrochemical College,
More informationAbstract. Introduction
REMOVAL OF Pb +2 IONS FROM AQUEOUS SOLUTIONS BY ACTIVATED CARBONS PRODUCED FROM PEANUT SHELLS Ayşe Eren Pütün, Dept. of Chemical Engineering, Anadolu University, Eskisehir, Turkey Esin Apaydın Varol, Dept.
More informationA stable dual-functional system of visible-light-driven Ni(II) reduction to a nickel nanoparticle catalyst and robust in situ hydrogen production
Electronic Supporting Information A stable dual-functional system of visible-light-driven Ni(II) reduction to a nickel nanoparticle catalyst and robust in situ hydrogen production Chuanjun Wang, a Shuang
More informationph-depending Enhancement of Electron Transfer by {001} Facet-Dominating TiO 2 Nanoparticles for Photocatalytic H 2 Evolution under Visible Irradiation
S1 ph-depending Enhancement of Electron Transfer by {001} Facet-Dominating TiO 2 Nanoparticles for Photocatalytic H 2 Evolution under Visible Irradiation Masato M. Maitani a *, Zhan Conghong a,b, Dai Mochizuki
More informationError in the Estimation of Effective Diffusion Coefficients from Sorption Measurements*
Error in the Estimation of Effective Diffusion Coefficients from Sorption Measurements* D. BOBOK and E. BESEDOVÁ Department of Chemical and Biochemical Engineering, Faculty of Chemical Technology, Slovak
More informationMethods of pollution control and waste management - laboratory. Adsorptive removal of volatile organic compounds from gases streams
Methods of pollution control and waste management - laboratory Adsorptive removal of volatile organic compounds from gases streams Manual for experiment 17 dr Hanna Wilczura-Wachnik and dr inż. Jadwiga
More informationExplosion Properties of Highly Concentrated Ozone Gas. 1 Iwatani International Corporation, Katsube, Moriyama, Shiga , Japan
Explosion Properties of Highly Concentrated Ozone Gas Kunihiko Koike 1*, Masaharu Nifuku 2, Koichi Izumi 1, Sadaki Nakamura 1, Shuzo Fujiwara 2 and Sadashige Horiguchi 2 1 Iwatani International Corporation,
More informationElectronic Supporting information (ESI) for
Electronic Supporting information (ESI) for Experimental assessment of physical upper limit for hydrogen storage capacity at 20 K in densified MIL-101 monoliths Hyunchul Oh a, Dan Lupu b, Gabriela Blanita
More informationACTIVATED CARBON AND HYDROGEN ADSORPTION STORAGE
ACTIVATED CARBON AND HYDROGEN ADSORPTION STORAGE L. L. VASILIEV, L. E. KANONCHIK, А. G. KULAKOV, D. A. MISHKINIS Laboratory of Porous Media Luikov Heat & Mass Transfer Institute, National Academy of Sciences,
More informationGas Chromatography Separation of H 2 -D 2 -Ar Using Pd/K
Gas Chromatography Separation of H 2 -D 2 -Ar Using Pd/K FTP/P1-06 X. J. Qian 1), D. L. Luo 1), C. Qin 1), G. Q. Huang 1), W. Yang 1) 1) China Academy of Engineering Physics, Mianyang, SiChuan, P.R.China
More informationThermochemical Storage Technologies
Thermochemical Storage Technologies Andreas Hauer Ecostock 2006, Stockton, New Jersey, USA Content Thermal energy storage technologies Direct / indirect thermal energy storage Thermochemical Storage: Closed
More informationTO-15 Checklist Determination of VOCs in Air by GC-MS
LAB ID: DATE: LAB NAME: ASSESSOR NAME: Method Number: TO-15 Checklist Determination of VOCs in Air by GC-MS SOP Number: Revision Number: SOP Date: Personnel records observed: Data records observed: Revision
More informationEvaluation of the Characteristic of Adsorption in a Double-Effect Adsorption Chiller with FAM-Z01
Journal of Materials Science and Chemical Engineering, 2016, 4, 8-19 http://www.scirp.org/journal/msce ISSN Online: 2327-6053 ISSN Print: 2327-6045 Evaluation of the Characteristic of Adsorption in a Double-Effect
More informationEQUILIBRIUM ADSORPTION OF METHANE AND CARBON DIOXIDE ON 5A MOLECULAR SIEVE
Volume3 December 2007 EQUILIBRIUM ADSORPTION OF METHANE AND CARBON DIOXIDE ON 5A MOLECULAR SIEVE Dr. Abbas Khalaf Mohammed Shua'ab Chemical Engineering Department, Baghdad University, P. O. Box 47024,
More informationPreparation of Activated Carbon for Electric Double Layer Capacitors
36 China Steel Technical Report, No. 25, Preparation pp. 36-41, of Activated (2012) Carbon for ElectricDouble Layer Capacitors Preparation of Activated Carbon for Electric Double Layer Capacitors WEN-CHANG
More informationCHARACTERIZATION OF 3A MOLECULAR SIEVE USING TRISTAR MICROMERITICS DEVICE
CHARACTERIZATION OF 3A MOLECULAR SIEVE USING TRISTAR MICROMERITICS DEVICE Sh. Azarfar 1i, S. Mirian 2, H. Anisi 3, R. Soleymani 4, S. Sadighi 5 1i, 4 Research & Development division, Nitelpars.Co (Fateh
More informationSOPHISTICATED DESIGN, INTUITIVE OPERATION, RESEARCH-GRADE RESULTS
SOPHISTICATED DESIGN, INTUITIVE OPERATION, RESEARCH-GRADE RESULTS ASAP 2020 Plus: Accelerated Surface Area and Porosimetry System The Micromeritics ASAP 2020 Plus integrates a variety of automated gas
More informationDeveloping Carbon Tolerance Catalyst for Dry Methane Reforming
745 A publication of CHEMICAL ENGINEERING TRANSACTIONS VOL. 32, 2013 Chief Editors: Sauro Pierucci, Jiří J. Klemeš Copyright 2013, AIDIC Servizi S.r.l., ISBN 978-88-95608-23-5; ISSN 1974-9791 The Italian
More informationPetroleum Thermodynamic Research Group
Petroleum Thermodynamic Research Group Labs 6-128 & 6-133 Chemical and Materials Engineering (CME) Bldg. The Petroleum Thermodynamic Research Group investigates the properties of hydrocarbon resources
More informationROLE OF HETEROGENEOUS CATALYSTS IN CHEMICAL INDUSTRIES- A REVIEW
ROLE OF HETEROGENEOUS CATALYSTS IN CHEMICAL INDUSTRIES- A REVIEW Priya Das 1, Yagnesh Joshi 2, Darshan Sarang 3, Dr. Yogesh Rotliwala 4 Student, Chemical Engg. Dept., SNPITRC, Bardoli, Gujarat, India 1
More informationElectronic Supporting Information (ESI) Porous Carbon Materials with Controllable Surface Area Synthsized from Metal-Organic Frameworks
Electronic Supporting Information (ESI) Porous Carbon Materials with Controllable Surface Area Synthsized from Metal-Organic Frameworks Seunghoon Lim, Kyungwon Suh, Yelin Kim, Minyoung Yoon, Hyeran Park,
More informationInternational Journal of Scientific Research and Modern Education (IJSRME) ISSN (Online): (www.rdmodernresearch.com) Volume I, Issue I,
OXYGEN CONCENTRATORS A STUDY Mohammed Salique*, Nabila Rumane**, RohanBholla***, Siddharth Bhawnani**** & Anita Kumari***** Chemical Engineering Department, Thadomal Shahani Engineering College, Off Linking
More informationReduction of SO 2 Emission Using CuO/γ-Al 2 O 3 Adsorbent: Case Study on Combustion of Algae Biomass Having High Sulfur Content
326 J. Jpn. Inst. Energy, Vol. Journal 96, No. of 8, the 2017 Japan Institute of Energy, 96, 326-331(2017) Technical Report Special articles: Asian Conference on Biomass Science 特集 : アジアバイオマス科学会議 Reduction
More informationControlling Interfacial Contact and Exposed Facets for. Enhancing Photocatalysis via 2D-2D Heterostructure
Electronic Supplementary Material (ESI) for Chemical Communications. This journal is The Royal Society of Chemistry 2015 Electronic Supplementary Information Controlling Interfacial Contact and Exposed
More informationCo-Ni/Al 2 O 3 catalysts for CO 2 methanation at atmospheric pressure
Co-Ni/Al 2 O 3 catalysts for CO 2 methanation at atmospheric pressure K. Nifantiev, O. Byeda, B. Mischanchuk, E. Ischenko a Taras Shevchenko National university of Kyiv, Kyiv, Ukraine knifantiev@gmail.com
More informationStorage of Hydrogen, Methane and Carbon Dioxide in Highly Porous Covalent Organic Frameworks for Clean Energy Applications
Storage of Hydrogen, Methane and Carbon Dioxide in Highly Porous Covalent Organic Frameworks for Clean Energy Applications (Supporting Information: 33 pages) Hiroyasu Furukawa and Omar M. Yaghi Center
More informationAvailable online at I-SEEC Proceeding - Science and Engineering (2013) 89 94
Available online at www.iseec2012.com I-SEEC 2012 Proceeding - Science and Engineering (2013) 89 94 Proceeding Science and Engineering www.iseec2012.com Science and Engineering Symposium 4 th International
More informationDry-gel conversion synthesis of Cr-MIL-101 aided by grinding: High surface area high yield synthesis with minimum purification
Electronic Supporting Informations (ESI): Dry-gel conversion synthesis of Cr-MIL-101 aided by grinding: High surface area high yield synthesis with minimum purification Jun Kim, Yu-Ri Lee and Wha-Seung
More information