1 Supporting Information: Supplementary Figure 1. (a) TEM and (b) HRTEM image of the Pd nanocube seeds. Inset of (b): the FFT pattern. (c) Magnified image of the square region highlighted in (b).
2 Supplementary Figure 2. (a) Low- and (b) high-magnification TEM images, and (c) histogram of the size distributions of Pd nanocube seeds. (d) Low- and (e) high-resolution TEM images, and (f) histogram of the size distributions of as-prepared Pd nanocages after 1 hr of etching the Pd nanocube seeds.
3 Supplementary Figure 3. TEM images of a Pd nanocage obtained at three tilt angles of 0, 20, and 40. All scale bars are 5 nm. Simulated nanocage structures along with TEM images are shown above. From these images, the three-dimensional (3D) characteristics of Pd nanocages were unambiguously demonstrated.
4 Supplementary Figure 4. EDX spectrum of the as-prepared Pd nanocages after 1 hr etching of Pd nanocube seeds.
5 Supplementary Figure 5. HRTEM image of the Pd nanocage shows the single crystalline structure along the [100] axis, where {200} facets are resolved.
6 Supplementary Figure 6. An inverse FFT image corresponding to Fig. 4-c.
7 Supplementary Figure 7. FTIR spectra of CTAB crystals, and Pd nanocubes and Pd nanocages. Peak positions and widths of C-CH 2 asymmetric and symmetric stretching vibrations of the methylene chain of CTAB can be used to assess the nature of surfactant packing on solid surfaces. The lower vibrational frequency and the narrower bandwidth of the crystalline surfactant correspond to more ordered structures of the methylene chains of CTAB.
8 Supplementary Figure 8. (a) UV-Vis spectra of the supernatant before and after the etching treatment of Pd seeds. The UV-Vis spectrum of CTA + [PdX 4 ] 2- in octanol (116 µm) is also shown as control. (b) UV- Vis spectra of a series of CTA + [PdX 4 2- ] in the concentration from 0 to 180 mm in octanol. (c) Plots of the absorbance at 250 nm and 340 nm with the concentration of CTA + [PdX 4 2- ] in octanol.
9 Supplementary Figure 9. The effect of solvents on the shape evolution of 12 nm Pd seeds. Experiments were performed in (a) EG and (b) EG/octanol (1:1) solvents, respectively. All other conditions are the same with the one in Fig. 4.
10 Supplementary Figure 10. Typical 1 HNMR spectra of the products obtained from PhB(OH) 2 and iodotoluene via Suzuki coupling reaction catalyzed by Pd nanocages at 50 C temperature.
11 Supplementary Figure 11. Schematic illustration of the preparation of NovaSyn TGR resin-supported aryl iodide and its application for the three phase test. First, 4-iodobenzoic acid is conjugated with NovaSyn TGR resin 1 to produce the compound 2. Then, in the three phase test, if phenylboronic acid reacts with the compound 2 via the Suzuki coupling reaction in the presence of free Pd atoms or Pdorganic complexes as catalysts in solution, the compound 3 will be formed. If there are no homogeneous Pd active species in solution, this reaction will not be catalyzed and thus the compound 2 will remain unchanged. The product, whether compound 5 or compound 6, can be determined by GC MS after cleaving them from the resin. The compound 4 is a cleaved part of resin side.
12 Supplementary Figure 12. (a) Typical gas chromatogram for the final product after the three phase test and TFA cleavage (see Supplementary Fig. 11 for the reaction steps). The resin (0.01 mmol) was undergone the three phase test in the standard condition (0.6 mmol PhB(OH) 2, 0.3 mmol iodotoluene, 1 mmol K 2 CO 3, 10 µg Pd nanocages (0.03 mol%), 5 ml 80% ethanol aqueous solution, 50 C, 2 h). It should be noted that three phase tests for other samples, i.e., the sample without iodotoluene and another sample including iodobenzene (0.6 mmol PhB(OH) 2, 0.3 mmol iodobenzene, 1 mmol K 2 CO 3, 10 µg Pd nanocages (0.03 mol%), 5 ml 80% ethanol aqueous solution, 25 C, 2 h), show similar gas chromatogram. (b) Gas chromatogram of commercial biphenyl-4-carboxamide (6 in Supplementary Fig. 11). The peak at 5.03 min was assigned to biphenyl-4-carboxamide. (c) Mass spectrum of the 2.43 min peak of the chromatogram in (a). (d) Mass spectrum of the 4.01 min peak of the chromatogram in (a). Analysis of each spectrum confirms that (c) represents the dodecane internal standard, while (d) represents 4- iodobenzamide (5 in Supplementary Fig. 11). Lack of 5.03 min peak in (a) suggested that no resin-bound aryl iodide 2 was converted into biphenylamide (3 in Supplementary Fig. 11). These results indicate that no release and capture of active species (Pd atoms or Pd-organic complexes) occurs in the solution phase during the three phase tests, and the coupling reactions only take place on the nanoparticle surface.
13 Supplementary Figure 13. Typical 1 HNMR spectrum for the final product after the three phase test and TFA cleavage. The resin (0.01 mmol) was undergone the three phase test in the standard condition (0.6 mmol PhB(OH) 2, 0.3 mmol iodotoluene, 1 mmol K 2 CO 3, 10 µg Pd nanocages (0.03 mol%), 5 ml 80% ethanol aqueous solution, 50 C, 2 h). This spectrum supports that only unreacted reactant of aryl iodide (5 in Supplementary Fig. 11) was detected after cleaving bonds with the resin and no resin-bound aryl iodide (2 in Supplementary Fig. 11) was converted into the product of biphenylamide (3 in Supplementary Fig. 11).
14 Supplementary Figure 14. (a) Low- and (b) high-magnification TEM images, and (c) EDX of Au nanocube seeds. Inset of (b) is a selected-area electron diffraction (SAED) image of Au nanocubes that agrees with the diffraction pattern of Au crystals. (d) TEM images of Au nanocages after etching Au nanocubes following the same procedure used for Pd nanocage fabrication. Inset of (d) is a SAED image of Au nanocages. (e) (g) High magnification TEM images of a Au nanocage (highlighted with an arrow in (d)) obtained at different tilt angles of 0, 30, and 60 along y axis.
15 Supplementary Figure HNMR spectra of the products obtained from PhB(OH) 2 and iodobenzene via Suzuki coupling reaction catalyzed by Pd nanocages at room temperature.
Supporting Information:
Electronic Supplementary Material (ESI) for Nanoscale. This journal is The Royal Society of Chemistry 2014 Supporting Information:. FigS1:TEM images of Pd conacve nanocube of three different sizes synthesised
More informationSupporting Information
Supporting Information Highly Cross-Linked Imidazolium Salts Entrapped Magnetic Particles Preparation and Applications Paola Agrigento, a Matthias Josef Beier, b Jesper T. N. Knijnenburg, c Alfons Baiker
More informationElectronic Supplementary Information
Electronic Supplementary Information Surfactant-free single-nano-sized colloidal Cu nanoparticles for use as an active catalyst of Ullmann-coupling reaction Yuto Isomura, a Takashi Narushima, b Hideya
More informationTitle of file for HTML: Supplementary Information Description: Supplementary Figures and Supplementary References
Title of file for HTML: Supplementary Information Description: Supplementary Figures and Supplementary References Supplementary Figure 1. SEM images of perovskite single-crystal patterned thin film with
More informationSupporting Information
Electronic Supplementary Material (ESI) for Chemical Communications. This journal is The Royal Society of Chemistry 2016 Supporting Information Single-crystalline Pd square nanoplates enclosed by {100}
More informationa b c Supplementary Figure S1
a b c Supplementary Figure S1 AFM measurements of MoS 2 nanosheets prepared from the electrochemical Liintercalation and exfoliation. (a) AFM measurement of a typical MoS 2 nanosheet, deposited on Si/SiO
More informationSelf-Assembly of Single Amino acid-pyrene Conjugates with Unique Structure-Morphology Relationship
Electronic Supplementary Material (ESI) for Soft Matter. This journal is The Royal Society of Chemistry 2017 Self-Assembly of Single Amino acid-pyrene Conjugates with Unique Structure-Morphology Relationship
More informationMagnetic nanoparticle-supported proline as a recyclable and recoverable ligand for the CuI catalyzed arylation of nitrogen nucleophiles
Magnetic nanoparticle-supported proline as a recyclable and recoverable ligand for the CuI catalyzed arylation of nitrogen nucleophiles Gagan Chouhan, Dashan Wang and Howard Alper* Centre for Catalysis
More informationSupplementary Information
Supplementary Information Fabrication of Novel Rattle-Type Magnetic Mesoporous carbon Microspheres for Removal of Microcystins Xinghua Zhang and Long Jiang* Beijing National Laboratory for Molecular Science
More informationTEM image of derivative 1 and fluorescence spectra of derivative 1 upon addition of
Electronic Supplementary Material (ESI) for Green Chemistry. This journal is The Royal Society of Chemistry 2016 Supramolecular ensemble of PBI derivative and Cu 2 O NPs: Potential photo catalysts for
More informationESI. Core-Shell Polymer Nanoparticles for Prevention of GSH Drug Detoxification and Cisplatin Delivery to Breast Cancer Cells
Electronic Supplementary Material (ESI) for Nanoscale. This journal is The Royal Society of Chemistry 2015 ESI Core-Shell Polymer Nanoparticles for Prevention of GSH Drug Detoxification and Cisplatin Delivery
More informationShaping Single-crystalline Trimetallic Pt Pd Rh Nanocrystals toward. High-efficiency C C Splitting of Ethanol in Conversion to CO 2
Supporting Information Shaping Single-crystalline Trimetallic Pt Pd Rh Nanocrystals toward High-efficiency C C Splitting of Ethanol in Conversion to CO 2 Wei Zhu,, Jun Ke,, Si-Bo Wang, Jie Ren, Hong-Hui
More informationSupplementary Materials for
advances.sciencemag.org/cgi/content/full/3/8/e1700732/dc1 This PDF file includes: Supplementary Materials for Oriented assembly of anisotropic nanoparticles into frame-like superstructures Jianwei Nai,
More informationSupporting Information
Supporting Information for "Size-Controlled Pd Nanoparticle Catalysts Prepared by Galvanic Displacement into a Porous Si-Iron Oxide Nanoparticle Host." Taeho Kim, a Xin Fu, b David Warther, a and Michael
More informationUniversity of Groningen
University of Groningen "Giant Surfactants" Created by the Fast and Efficient Functionalization of a DNA Tetrahedron with a Temperature-Responsive Polymer Wilks, Thomas R.; Bath, Jonathan; de Vries, Jan
More informationRESULTS AND DISCUSSION Characterization of pure CaO and Zr-TiO 2 /CaO nanocomposite
RESULTS AND DISCUSSION 4.1. Characterization of pure CaO and Zr-TiO 2 /CaO nanocomposite 4.1.1. Scanning electron microscopy analysis (SEM) SEM images of prepared CaO are shown in Fig. 4.1 (a and b). CaO
More informationCu 2 O/g-C 3 N 4 nanocomposites: An insight into the band structure tuning and catalytic efficiencies
Electronic Supplementary Material (ESI) for Nanoscale. This journal is The Royal Society of Chemistry 216 Cu 2 O/g-C 3 N 4 nanocomposites: An insight into the band structure tuning and catalytic efficiencies
More informationSupplementary Figure 1. SEM and TEM images of the metal nanoparticles (MNPs) and metal oxide templates.
Supplementary Figure 1. SEM and TEM images of the metal nanoparticles (MNPs) and metal oxide templates. (a) 13 nm Au, (b) 60 nm Au, (c) 3.3 nm Pt, (d) ZnO spheres, (e) Al 2O 3 spheres and (f) Cu 2O cubes.
More informationSupplementary Figure 2. (a) XRD patterns of the MOF and the simulated Ni-MOF-74
Supplementary Figure 1. Low-magnification TEM image of Pt-Ni frame @ MOF. The scale bar is 200 nm. Supplementary Figure 2. (a) XRD patterns of the Pt-Ni @ MOF and the simulated Ni-MOF-74 pattern. (b) XRD
More information[Supplementary Information] One-Pot Synthesis and Electrocatalytic Activity of Octapodal Au-Pd Nanoparticles
[Supplementary Information] One-Pot Synthesis and Electrocatalytic Activity of Octapodal Au-Pd Nanoparticles Jong Wook Hong, Young Wook Lee, Minjung Kim, Shin Wook Kang, and Sang Woo Han * Department of
More informationSupporting Information
Electronic Supplementary Material (ESI) for Dalton Transactions. This journal is The Royal Society of Chemistry 2017 Supporting Information Sulfonato-imino copper(ii) complexes : fast and general Chan-
More informationSupporting Information
Electronic Supplementary Material (ESI) for CrystEngComm. This journal is The Royal Society of Chemistry 217 Supporting Information Catalyst preparation A certain of aqueous NiCl 2 6H 2 O (2 mm), H 2 PtCl
More informationSupporting Information
Supporting Information Experimental Materials: For the gold nanocuboids, the chemicals gold (ш) chloride trihydrate, sodium borohydride, cetyltrimethylammonium bromide, copper sulfate, L-ascorbic acid
More information1-amino-9-octadecene, HAuCl 4, hexane, ethanol 55 o C, 16h AuSSs on GO
Supplementary Figures GO Supplementary Figure S1 1-amino-9-octadecene, HAuCl 4, hexane, ethanol 55 o C, 16h AuSSs on GO Schematic illustration of synthesis of Au square sheets on graphene oxide sheets.
More informationSupporting Information:
Supporting Information: Columnar Self-assembly of Cu 2 S Hexagonal Nanoplates Induced by Tin (IV)-X Complex Inorganic Surface Ligand Xiaomin Li, Huaibin Shen, Jinzhong Niu, Sen Li, Yongguang Zhang, Hongzhe
More informationSupplementary Figure 1. A photographic image of directionally grown perovskite films on a glass substrate (size: cm).
Supplementary Figure 1. A photographic image of directionally grown perovskite films on a glass substrate (size: 1.5 4.5 cm). 1 Supplementary Figure 2. Optical microscope images of MAPbI 3 films formed
More informationSupporting Information
Electronic Supplementary Material (ESI) for Nanoscale. This journal is The Royal Society of Chemistry 2015 Supporting Information Stefanos Mourdikoudis, a,b Mariana Chirea, a Daniele Zanaga, c Thomas Altantzis,
More informationShape-selective Synthesis and Facet-dependent Enhanced Electrocatalytic Activity and Durability of Monodisperse Sub-10 nm Pt-Pd Tetrahedrons and Cubes
Supporting Information Shape-selective Synthesis and Facet-dependent Enhanced Electrocatalytic Activity and Durability of Monodisperse Sub-10 nm Pt-Pd Tetrahedrons and Cubes An-Xiang Yin, Xiao-Quan Min,
More informationSupporting Information. Solution-Based Growth of Monodisperse Cube-Like BaTiO 3 Colloidal Nanocrystals
Supporting Information Solution-Based Growth of Monodisperse Cube-Like BaTiO 3 Colloidal Nanocrystals Shiva Adireddy, Baobao Cao, Cuikun Lin, Weilie Zhou and Gabriel Caruntu* Chemistry Department and the
More informationSupplementary Information for. Silver Nanoparticles Embedded Anti-microbial Paints Based on Vegetable Oil
Supplementary Information for Silver Nanoparticles Embedded Anti-microbial Paints Based on Vegetable Oil Ashavani Kumar #, Praveen Kumar Vemula #, Pulickel M. Ajayan, George John * Department of Chemistry,
More informationElectronic Supplementary Information
Electronic Supplementary Material (ESI) for Nanoscale. This journal is The Royal Society of Chemistry 2014 Electronic Supplementary Information One-pot synthesis of ultralong coaxial Au@Pt nanocables with
More informationPhoton Energy Threshold in Direct Photocatalysis with Metal Nanoparticles Key Evidence from Action Spectrum of the Reaction
Supporting Information Photon Energy Threshold in Direct Photocatalysis with Metal Nanoparticles Key Evidence from Action Spectrum of the Reaction Sarina Sarina, a Esa Jaatinen, a Qi Xiao, a,b Yi Ming
More informationC-C Coupling on Single-Atom-Based Heterogeneous Catalyst
Supporting Information C-C Coupling on Single-Atom-Based Heterogeneous Catalyst Xiaoyan Zhang,,, Zaicheng Sun, Bin Wang, ǁ Yu Tang, Luan Nguyen, Yuting Li and Franklin Feng Tao*, Department of Chemical
More informationSupporting Information
Electronic Supplementary Material (ESI) for RSC Advances. This journal is The Royal Society of Chemistry 2015 Supporting Information An Anode Buffer Layer with Size-Controlled Ag Nanoparticles for Polymer
More informationSupplementary Information
Supplementary Information CoFe 2 O 4 -ZnS nanocomposite: a magnetically recyclable photocatalyst Kula Kamal Senapati, Chandan Borgohain, and Prodeep Phukan Department of Chemistry, Gauhati University,
More informationSupplementary Information. Seeding Approach to Noble Metal Decorated Conducting Polymer Nanofiber Network
Supplementary Information Seeding Approach to Noble Metal Decorated Conducting Polymer Nanofiber Network Zhen Liu, Selcuk Poyraz, Yang Liu, Xinyu Zhang* Department of Polymer and Fiber Engineering, Auburn
More informationDouble Mesoporous Silica Shelled Spherical/Ellipsoidal Nanostructures: Synthesis and Hydrophilic/Hydrophobic Anticancer Drug Delivery
Supporting information for Supplementary Material (ESI) for Journal of Materials Chemistry Double Mesoporous Silica Shelled Spherical/Ellipsoidal Nanostructures: Synthesis and Hydrophilic/Hydrophobic Anticancer
More informationSupporting Information
Supporting Information An Extremely Active and General Catalyst for Suzuki Coupling Reactions of Unreactive Aryl Chlorides Dong-Hwan Lee and Myung-Jong Jin* School of Chemical Science and Engineering,
More informationSUPPORTING INFORMATION. Additive-Free Dehydrogenation of Formic Acid at. Room Temperature
SUPPORTING INFORMATION MnO x -Promoted PdAg Alloy Nanoparticles for the Additive-Free Dehydrogenation of Formic Acid at Room Temperature Ahmet Bulut, Mehmet Yurderi, Yasar Karatas, Zafer Say, Hilal Kivrak,
More informationSupporting Information
Electronic Supplementary Material (ESI) for Journal of Materials Chemistry A. This journal is The Royal Society of Chemistry 2017 Supporting Information Cyclic Molecule Aerogels: A Robust Cyclodextrin
More informationPermeable Silica Shell through Surface-Protected Etching
Permeable Silica Shell through Surface-Protected Etching Qiao Zhang, Tierui Zhang, Jianping Ge, Yadong Yin* University of California, Department of Chemistry, Riverside, California 92521 Experimental Chemicals:
More informationSuzuki coupling reactions catalyzed by poly(n-ethyl-4-vinylpyridinium) bromide stabilized palladium nanoparticles in aqueous solution
express Polymer Letters Vol.2, No.4 (2008) 251 255 Available online at www.expresspolymlett.com DOI: 10.3144/expresspolymlett.2008.30 Suzuki coupling reactions catalyzed by poly(n-ethyl-4-vinylpyridinium)
More informationA Fluorescence Turn-On Sensor for the Detection of Palladium Ions that Operates Through In-Situ Generation of Palladium Nanoparticles
This journal is The Royal Society of Chemistry 214 Supporting Information for A Fluorescence Turn-On Sensor for the Detection of Palladium Ions that Operates Through In-Situ Generation of Palladium Nanoparticles
More informationSupplementary Figure S1: Particle size distributions of the Pt ML /Pd 9 Au 1 /C
a 2 15 before cycle test mean particle size: 3.8 ± 1.2 nm b 2 15 after.6v - 1.V 1k cycle test mean particle size: 4.1 ± 1.5 nm Number 1 total number: 558 Number 1 total number: 554 5 5 1 2 3 4 5 6 7 8
More informationEncapsulation of enzyme in metal ion-surfactant nanocomposites for
Electronic Supplementary Material (ESI) for ChemComm. This journal is The Royal Society of Chemistry 2017 Supporting information for Encapsulation of enzyme in metal ion-surfactant nanocomposites for catalysis
More informationSupporting Information
Supporting Information Fabrication of Cubic Nanocages and Nanoframes by Dealloying Au/Ag Alloy Nanoboxes with an Aqueous Etchant Based on Fe(NO 3 ) 3 or NH 4 OH Xianmao Lu, 1,2 Leslie Au, 1 Joseph McLellan,
More informationSupporting Information
Electronic Supplementary Material (ESI) for Journal of Materials Chemistry A. This journal is The Royal Society of Chemistry 2018 Supporting Information Adding refractory 5d transition metal W into PtCo
More informationSupporting Information. A Facile Methodology for Engineering the Morphology of CsPbX 3 Perovskite Nanocrystals under Ambient Condition
Supporting Information A Facile Methodology for Engineering the Morphology of CsPbX 3 Perovskite Nanocrystals under Ambient Condition Sudipta Seth and Anunay Samanta School of Chemistry, University of
More informationSupplementary Materials for
advances.sciencemag.org/cgi/content/full/4/10/eaas9319/dc1 Supplementary Materials for Transformation of alcohols to esters promoted by hydrogen bonds using oxygen as the oxidant under metal-free conditions
More informationElectronic Supplementary Information. Pd(diimine)Cl 2 Embedded Heterometallic Compounds with Porous Structures as Efficient Heterogeneous Catalysts
Electronic Supplementary Information Pd(diimine)Cl 2 Embedded Heterometallic Compounds with Porous Structures as Efficient Heterogeneous Catalysts Sheng-Li Huang, Ai-Quan Jia and Guo-Xin Jin* Experimental
More informationNovel Nickel-Palladium Catalysts Encased in a Platinum Nanocage
Electronic Supplementary Material (ESI) for RSC Advances. This journal is The Royal Society of Chemistry 2014 Electronic Supplementary Information (ESI) Novel Nickel-Palladium Catalysts Encased in a Platinum
More informationSupplementary Information
Supplementary Information Direct Synthesis of a Macroscopic Array of Naked Ag Nanoparticles Omar Ayyad,* a,b,c David Muñoz-Rojas, a Pedro Gómez-Romero* a,c Experimental details Polyvinylpyrrolidone (PVP40T-500G,
More informationA General Synthesis of Discrete Mesoporous Carbon Microspheres through a Confined Self- Assembly Process in Inverse Opals
A General Synthesis of Discrete Mesoporous Carbon Microspheres through a Confined Self- Assembly Process in Inverse Opals Zhenkun Sun,, Yong Liu, Bin Li, Jing Wei, Minghong Wang, Qin Yue, Yonghui Deng,
More informationElectronic Supplementary Information
Electronic Supplementary Material (ESI) for Nanoscale. This journal is The Royal Society of Chemistry 2014 Electronic Supplementary Information for Trace Amount Pd(ppm)-Catalyzed Sonogashira, Heck and
More informationAgampodi S. De Silva Indrasekara 1,2, Sean F Johnson 1, Ren A Odion 1,2, Tuan Vo-Dinh 1,2,3*
Supporting Information: Manipulation of the geometry and modulation of the optical response of surfactant-free gold nanostars: a systematic bottom-up synthesis Agampodi S. De Silva Indrasekara 1,2, Sean
More informationElectronic Supplementary Information (ESI) Green synthesis of shape-defined anatase TiO 2 nanocrystals wholly exposed with {001} and {100} facets
Electronic Supplementary Information (ESI) Green synthesis of shape-defined anatase TiO 2 nanocrystals wholly exposed with {001} and {100} facets Lan Wang, a Ling Zang, b Jincai Zhao c and Chuanyi Wang*
More informationSub-10-nm Au-Pt-Pd Alloy Trimetallic Nanoparticles with. High Oxidation-Resistant Property as Efficient and Durable
Electronic Supplementary Material (ESI) for ChemComm. This journal is The Royal Society of Chemistry 2014 Electronic Supplementary Information Sub-10-nm Au-Pt-Pd Alloy Trimetallic Nanoparticles with High
More informationSupporting Information for: Emulsion-assisted synthesis of monodisperse binary metal nanoparticles
Supporting Information for: Emulsion-assisted synthesis of monodisperse binary metal nanoparticles Zhen Yin, Ding Ma* and Xinhe Bao* Synthesis of the PdCu nanoparticles: All synthesis was carried out under
More informationSupplementary Information
Supplementary Information Supplementary Figure 1. X-ray diffraction patterns of (a) pure LDH, (b) AuCl 4 ion-exchanged LDH and (c) the Au/LDH hybrid catalyst. The refined cell parameters for pure, ion-exchanged,
More informationSupporting Information
Supporting Information Interaction effects of mesoporous silica nanoparticles with different morphologies on human red blood cells Madhura Joglekar, Robert A. Roggers, Yannan Zhao, and Brian G. Trewyn
More informationMaterials and Instrumentation. Preparation of ferrofluid [1] Preparation of polymer magnetic nanoparticles. Preparation of NHC ligand [2]
Electronic Supplementary Material (ESI) for Green Chemistry. This journal is The Royal Society of Chemistry 204 Materials and Instrumentation. All the reagents and solvents were purchased from Sinopharm
More informationSupporting Information. Cells. Mian Wang, Yanglei Yuan, Hongmei Wang* and Zhaohai Qin*
Electronic Supplementary Material (ESI) for Analyst. This journal is The Royal Society of Chemistry 2015 Supporting Information Fluorescent and Colorimetric Probe Containing Oxime-Ether for Pd 2+ in Pure
More informationDivision of Fuel Cells, Dalian National Laboratory for Clean Energy, Dalian Institute of Chemical Physics, Chinese
Electronic Supplementary Material (ESI) for RSC Advances. This journal is The Royal Society of Chemistry 2016 Supporting information Tuned Depositing Ag clusters on ZrO 2 Nanocrystals from Silver Mirror
More informationSupporting Information
Supporting Information A Rational Design of Highly Controlled Suzuki-Miyaura Catalyst-Transfer Polycondensation for Precision Synthesis of Polythiophenes and their Block Copolymers: Marriage of Palladacycle
More informationSupplementary Materials. Synthesis of Reusable Silica Nanosphere-Supported Pt(IV) Complex for. Formation of Disulfide Bonds in Peptides
Supplementary Materials Synthesis of Reusable Silica Nanosphere-Supported Pt(IV) Complex for Formation of Disulfide Bonds in Peptides Xiaonan Hou, Xiaowei Zhao, Yamei Zhang, Aiying Han, Shuying Huo*, and
More informationFabrication and characterization of poly (ethylene oxide) templated nickel oxide nanofibers for dye degradation
Electronic Supplementary Material (ESI) for Environmental Science: Nano. This journal is The Royal Society of Chemistry 2014 Supplementary Information Fabrication and characterization of poly (ethylene
More informationGeneral experimental Procedures: Materials
Electronic Supplementary Material (ESI) for Chemical Communications. This journal is The Royal Society of Chemistry 2015 Aggregates of pentacenequinone derivative as reactors for the preparation of Ag@Cu
More informationSupporting Information
Electronic Supplementary Material (ESI) for Journal of Materials Chemistry A. This journal is The Royal Society of Chemistry 214 Supporting Information AgPd nanoparticles supported on MIL-11 as high performance
More informationPd Supported on Carbon Nitride Boosts the Direct Hydrogen Peroxide Synthesis
Supporting Information Pd Supported on Carbon Nitride Boosts the Direct Hydrogen Peroxide Synthesis Rosa Arrigo,* Manfred E. Schuster, Salvatore Abate, Gianfranco Giorgianni, Gabriele Centi, Siglinda Perathoner,
More informationElectronic Supplementary Information
Electronic Supplementary Material (ESI) for Journal of Materials Chemistry A. This journal is The Royal Society of Chemistry 2017 Electronic Supplementary Information Probing the Surface Reactivity of
More informationSupplementary Figure 1 H 2 evolving instrument. A closed gas circulation and evacuation system for H2 evolution.
Supplementary Figure 1 H 2 evolving instrument. A closed gas circulation and evacuation system for H2 evolution. 400 H 2 evolution rate ( mol h -1 ) 350 300 250 200 150 100 50 0 1 2 3 4 5 6 7 8 9 10 11
More informationStudy on the Selective Hydrogenation of Nitroaromatics to N-aryl hydroxylamines using a Supported Pt nanoparticle Catalyst
Electronic Supplementary Material (ESI) for Catalysis Science & Technology. This journal is The Royal Society of Chemistry 204 Supporting Information Study on the Selective Hydrogenation of Nitroaromatics
More informationSupporting Information. Graphene Oxide-Palladium Modified Ag-AgBr: A Novel Visible-Light- Responsive Photocatalyst for the Suzuki Coupling Reaction**
Electronic Supplementary Material (ESI) for RSC Advances. This journal is The Royal Society of Chemistry 2014 Supporting Information Graphene Oxide-Palladium Modified Ag-AgBr: A Novel Visible-Light- Responsive
More informationSupplementary Figure 1. Cross-section SEM image of the polymer scaffold perovskite film using MAI:PbI 2 =1:1 in DMF solvent on the FTO/glass
Supplementary Figure 1. Cross-section SEM image of the polymer scaffold perovskite film using MAI:PbI 2 =1:1 in DMF solvent on the FTO/glass substrate. Scale bar: 1 m. Supplementary Figure 2. Contact angle
More informationSupporting information
Electronic Supplementary Material (ESI) for Faraday Discussions. This journal is The Royal Society of Chemistry 2015 Supporting information Phase diagram studies When selecting the surfactant its stability
More informationElectronic Supplementary Material. Methods. Synthesis of reference samples in Figure 1(b) Nano Res.
Electronic Supplementary Material Shaped Pt Ni nanocrystals with an ultrathin Pt-enriched shell derived from one-pot hydrothermal synthesis as active electrocatalysts for oxygen reduction Jun Gu 1,, Guangxu
More informationSUPPORTING INFORMATION
SUPPORTING INFORMATION A Sustainable Approach to Waste-Minimized Sonogashira Cross-Coupling Reaction Based on Recoverable/Reusable heterogeneous Catalytic/Base System and Acetonitrile Azeotrope Vadym Kozell,
More informationOne-step seeded growth of Au nanoparticles with widely tunable sizes
Electronic Supplementary Information (ESI) One-step seeded growth of Au nanoparticles with widely tunable sizes Chuanbo Gao, John Vuong, Qiao Zhang, Yiding Liu and Yadong Yin* Department of Chemistry,
More informationElectronic Supplementary Information For. Facile fabrication of glycopolymer-based iron oxide nanoparticles
Electronic Supplementary Material (ESI) for Polymer Chemistry. This journal is The Royal Society of Chemistry 2016 Electronic Supplementary Information For Facile fabrication of glycopolymer-based iron
More informationCHAPTER 4. SYNTHESIS, CHARACTERIZATION OF TiO 2 NANOTUBES AND THEIR APPLICATION IN DYE SENSITIZED SOLAR CELL
93 CHAPTER 4 SYNTHESIS, CHARACTERIZATION OF TiO 2 NANOTUBES AND THEIR APPLICATION IN DYE SENSITIZED SOLAR CELL 4.1 INTRODUCTION TiO 2 -derived nanotubes are expected to be applicable for several applications,
More informationSupporting Information
Supporting Information Enhanced Stability of Immobilized Pt Nanoparticles on Carbon Nanotubes through Nitrogen Heteroatoms on Doped Carbon Supports Wen Shi, Kuang-Hsu Wu, Junyuan Xu ǁ, Qiang Zhang, Bingsen
More informationSupplementary Information (ESI) Synthesis of Ultrathin Platinum Nanoplates for Enhanced Oxygen Reduction Activity
Electronic Supplementary Material (ESI) for Chemical Science. This journal is The Royal Society of Chemistry 2017 Supplementary Information (ESI) Synthesis of Ultrathin Platinum Nanoplates for Enhanced
More informationAluminum Foil: A Highly Efficient and Environment- Friendly Tea Bag Style Catalyst with High TON
Supporting Information Pd @ Aluminum Foil: A Highly Efficient and Environment- Friendly Tea Bag Style Catalyst with High TON Fan Lei, Yi Rong, Yu Lei,* Wu Yulan, Chen Tian, and Guo Rong General Remarks.
More informationSupporting Information
Electronic Supplementary Material (ESI) for Polymer Chemistry. This journal is The Royal Society of Chemistry 2014 Supporting Information Synthesis of Donor-Acceptor Conjugated Copolymers Based on Benzo[1,2-b:4,5-b
More informationSupporting Information
Electronic Supplementary Material (ESI) for Journal of Materials Chemistry B. This journal is The Royal Society of Chemistry 2017 Supporting Information Core-Shell Gold Nanocubes for Point Mutation Detection
More informationSupporting information
Supporting information imetallic AuRh nanodendrites consisting of Au icosahedron cores and atomically ultrathin Rh nanoplate shells: synthesis and light-enhanced catalytic activity Yongqiang Kang 1,2,
More informationElectronic Supplementary Information
Electronic Supplementary Information 5 An alternative hydrolytic synthesis route for uniform metal selenide nanoparticles Sandip Kumar Pahari, Provas Pal, Arka Saha, Sourindra Mahanty,* and Asit Baran
More informationInfluence of Nanoscale Structuralisation on the Catalytic Performance of ZIF-8: A Cautionary Surface Catalysis Study
Electronic Supplementary Material (ESI) for CrystEngComm. This journal is The Royal Society of Chemistry 2018 Supplementary Information for Influence of Nanoscale Structuralisation on the Catalytic Performance
More informationMokone Mmola, Marilize Le Roes-Hill, Kim Durrell, John J. Bolton, Nicole Sibuyi, Mervin E. Meyer, Denzil R. Beukes and Edith Antunes
S1 of S14 Supplementary Materials: Enhanced Antimicrobial and Anticancer Activity of Silver and Gold Nanoparticles Synthesised Using Sargassum incisifolium Aqueous Extracts Mokone Mmola, Marilize Le Roes-Hill,
More information1G (bottom) with the phase-transition temperatures in C and associated enthalpy changes (in
Supplementary Figure 1. Optical properties of 1 in various solvents. UV/Vis (left axis) and fluorescence spectra (right axis, ex = 420 nm) of 1 in hexane (blue lines), toluene (green lines), THF (yellow
More informationSupplementary Figure 1 a-c, The viscosity fitting curves of high-molecular-weight poly(vinyl alcohol) (HMW-PVA) (a), middle-molecular-weight
Supplementary Figure 1 a-c, The viscosity fitting curves of high-molecular-weight poly(vinyl alcohol) (HMW-PVA) (a), middle-molecular-weight poly(vinyl alcohol) (MMW-PVA) (b) and low-molecular-weight poly(vinyl
More informationSupporting Information
Supporting Information Highly Sensitive, Reproducible, and Stable SERS Sensors Based on Well-Controlled Silver Nanoparticles Decorated Silicon Nanowire Building Blocks Xue Mei Han, Hui Wang, Xue Mei Ou,
More informationDepartment of Chemistry of The College of Staten Island and The Graduate Center, The City University of
Electronic Supplementary Material (ESI) for Journal of Materials Chemistry A. This journal is The Royal Society of Chemistry 2014 Fe 3 O 4 /Carbon quantum dots hybrid nanoflowers for highly active and
More informationElectronic Supplementary Information
Electronic Supplementary Information General and highly active catalyst for mono and double Hiyama coupling reactions of unreactive aryl chlorides in water Dong-Hwan Lee, Ji-Young Jung, and Myung-Jong
More informationSupporting Information
Supporting Information Fluorescent Carbon Nanoparticle: Synthesis, Characterization and Bio-imaging Application S.C. Ray (a),*, Arindam Saha, Nikhil R. Jana * and Rupa Sarkar Centre for Advanced Materials,
More informationVisible-light Driven Plasmonic Photocatalyst Helical Chiral TiO 2 Nanofibers
Visible-light Driven Plasmonic Photocatalyst Ag/AgCl @ Helical Chiral TiO 2 Nanofibers Dawei Wang, Yi Li*, Gianluca Li Puma, Chao Wang, Peifang Wang, Wenlong Zhang, and Qing Wang Fig. S1. The reactor of
More informationPalladium Schiff Base Complexes: Potential catalysts for C-C bond reactions
Palladium Schiff Base Complexes: Potential catalysts for C-C bond reactions Moosun S. B., Bhewa, B. S., Bhowon M. G., Jhaumeer Laulloo S. * University of Mauritius, Reduit, Mauritius Email address: sabina@uom.ac.mu
More informationSUPPLEMENTARY INFORMATION
Anisotropic phase segregation and migration of Pt in nanocrystals en route to nanoframe catalysts Zhiqiang Niu 1, Nigel Becknell 1, Yi Yu 1,2, Dohyung Kim 3, Chen Chen 1,4, Nikolay Kornienko 1, Gabor A.
More informationSupporting Information
Electronic Supplementary Material (ESI) for Green Chemistry. This journal is The Royal Society of Chemistry 2014 Supporting Information A novel enzymatic approach to develop a lignin-based adhesive for
More informationElectronic Supplementary Information. Precursor Salt Assisted Syntheses of High-Index Faceted Concave Hexagon and Nanorod like Polyoxometalates
Electronic Supplementary Material (ESI) for Nanoscale. This journal is The Royal Society of Chemistry 2014 Electronic Supplementary Information Precursor Salt Assisted Syntheses of High-Index Faceted Concave
More information