Lecture #7: Basic Notions of Fracture Mechanics Ductile Fracture
|
|
- Lesley Reeves
- 5 years ago
- Views:
Transcription
1 Lecture #7: Basic Notions of Fracture Mechanics Ductile Fracture by Dirk Mohr ETH Zurich, Department of Mechanical and Process Engineering, Chair of Computational Modeling of Materials in Manufacturing
2 Basic Notions of Fracture Mechanics
3 Fracture Mechanics Fracture mechanics is a branch of mechanics that is concerned with the study of the propagation of cracks and growth of flaws. The starting point of a fracture mechanics analysis therefore is a structure with a pre-existing crack or flaw. Central questions in fracture mechanics are for example: Under which mechanical loads does a preexisting crack propagate? What is the maximum size of a crack that can be tolerated in a structure that is subject to a known mechanical load such that the crack does not propagate? crack 3 3 3
4 Griffith theory an energy approach Griffith s (191) made an attempt to come up with a fracture criterion for brittle solids by writing down the energy balance during the growth of a crack. Consider an isotropic linear elastic plate subject to uniaxial tension and let W 0 denote the elastic strain energy stored in that system. According to Inglis (1913) analysis, the introduction of a through thickness crack of length a reduces the elastic strain energy (energy release) by a t E da a da t 4 4 4
5 Griffith theory Introducing the free surface energy per unit area, s, the total energy of the system then reads U tot t E U0 a 4at s After differentiating with respect to a, we obtain the rate of change of the total energy as a function of the crack length and the applied stress du da tot t a E 4t s da a da t 5 5 5
6 du da tot t a E Griffith theory 4t Note that for small flaws and for low applied stresses, the surface energy term dominates, i.e. the total energy of the system would increase as the crack advances. However, when the critical condition du tot /da=0 is met, the change in total energy becomes negative (energy release). s : Dynamic behavior of materials and structures da a da According to Griffith, this condition defines the onset of unstable crack growth. The critical far field stress for fracture initiation therefore reads t a 4t s 0 E c s E a t
7 Linear Elastic Fracture Mechanics (LEFM) The stress fields in the vicinity of cracks in elastic media can be calculated using linear elastic stress analysis. In particular, the analytical solutions have been developed for three basic modes of fracture: Mode I opening mode Mode II in-plane shear mode Mode III out-of-plane shear mode 7 7 7
8 Linear elastic fracture mechanics The leading terms of analytical solutions for the crack tip stress fields are typically expressed through the product of a radial and circumferential term. For example, the stress field for Mode I plane stress loading reads x y a r a r cos cos 1 sin sin 1 sin sin 3 3 xy a r cos sin cos
9 Linear elastic fracture mechanics y a r cos 1 sin sin 3 Note that the governing terms all exhibit a singularity at the crack tip, lim r0 ij crack r / a 9 9 9
10 Stress Intensity Factor The limit r0 K I : lim r y 0 is called stress intensity factor. It characterizes the magnitude of the stresses at the crack tip. An analog factor can be defined for Mode II and Mode III fracture. In the above example, we have y[ 0] a r and thus K I a The expressions of the stress intensity factor for different crack shapes and loading conditions can be found in many textbooks
11 Fracture toughness : Dynamic behavior of materials and structures In linear elastic fracture mechanics, it is assumed that a crack propagates if the stress intensity factor reaches a critical value, KI K c The critical value K C for Mode I fracture under plane strain conditions is called fracture toughness. Its units are MPa m. It is considered as a material property which is measured using Single Edge Notch Bend (SENB) or Compact Tension (CT) specimens, see ASTM E-399 standard
12 K-dominance : Dynamic behavior of materials and structures The stress intensity factor characterizes only the leading term of the stress field near the crack tip. The exact solution for the neartip fields includes also non-singular higher order terms K ij[, r] fij[ ] r higher order terms The annular region within which the singular terms (socalled K-fields) dominate is described by the radius r K of the zone of K-dominance. crack r / a exact K-field 1 1 1
13 Small scale yielding condition The K-fields can still be meaningful even if the real mechanical system is different from that assumed in the theoretical analysis. Examples include situations where the crack is not sharp; the material deforms plastically micro-cracks are present near the crack tip The condition of applicability of linear elastic fracture mechanics is that the radius r p of the zone of inelastic deformation at the crack tip must be well confined inside the region of K-dominance. rp r K
14 An alternative to fracture mechanics The classical fracture mechanics approach is based on the assumption that failure is the outcome of the growth of a preexisting crack (and that all materials contain flaws). An alternative approach consists of assuming that a solid is initially crack-free. Phenomenological fracture criteria in terms of macroscopic stresses and strains are then often employed to predict the onset of fracture. A simple example of a phenomenological criterion for brittle solids is to assume that fracture initiates when the maximum principal stress exceeds a critical value, I crit
15 Ductile Fracture
16 Fracture in Automotive Applications Shear induced fracture (Courtesy of ThyssenKrupp) FLD Bending under tension (Courtesy of US Steel) Fractures on tight radii during stamping cannot be predicted by Forming Limit Diagram (FLD) Usually termed as shear fracture, presents little necking, shows slant fracture
17 Interrupted tension experiments Flat notched tensile specimens (1.4mm initial thickness) 0mm 500mm
18 RD RD Th Th 50mm
19 50mm RD Th
20 Surface versus Cross-section View Signature of voids on fracture surface! BUT: Almost no voids just below fracture surface! 0 0 0
21 Failure Mechanism Summary e=0. 1 e~ Onset of necking 4 e>1.0. Void volume fraction increases (more nucleation) 3. Shear localization 4. Void sheet failure Define strain to fracture as strain at the onset of shear localization 1 1 1
22 A Think Model of the Ductile Fracture Process initial porosity growth & nucleation primary localization growth & nucleation secondary localization nucleation & growth final fracture
23 Definition of strain to fracture initial porosity growth & nucleation primary localization growth & nucleation secondary localization nucleation & growth final fracture Strain to fracture = macroscopic equiv. plastic strain at instant of first localization RVE 3 3 3
24 Tomographic observations xxx aluminum 4 4 4
25 Void evolution in a plastic solid. void evolution depends on stress state 5 5 5
26 Decomposition of the Stress Tensor HYDROSTATIC PART (average stress) DEVIATORIC PART (differences among stresses) σ III (σ III σ m ) σ I σ II σ m σ m = + σ m (σ I σ m ) (σ II σ m ) σ m = σ I + σ II + σ III
27 Effect of Stress State on Void Evolution HYDROSTATIC PART controls void growth is characterized by: σ m STRESS TRIAXIALITY η = σ m തσ DEVIATORIC PART controls shape change is characterized by: LODE PARAMETER 7 7 7
28 Definition of Lode Parameter τ σ N σ III σ II σ I σ II σ N Maximum shear stress (radius of biggest circle): Normal stress on plane of max. shear (center of biggest circle) Position of the intermediate principal stress: τ = σ I σ III σ N = σ I + σ III L = σ II σ N τ LODE PARAMETER 8 8 8
29 Which states have the same Lode parameter? Uniaxial tension σ σ σ m = σ/3 η = 1/3 തσ = σ σ II = σ III = 0 L = 1 Plane strain tension σ σ/ σ m = σ/ η = 1/ 3 തσ = 3/σ σ II = (σ I + σ III )/ L = 0 Pure shear σ/ σ/ σ m = 0 η = 0 തσ = 3/σ σ II = (σ I + σ III )/ L =
30 Lode angle parameter Stress triaxiality: m III s III plane I II III Normalized third stress invariant 7 J 3 3 Lode angle parameter 1 arccos( ) I II s I s II
31 Lode angle parameter Lode parameter (Lode, 196) II I L I III III III s III plane I II III s II Lode angle parameter 1 arccos( ) L I II s I axisymmetric tension 0 generalized shear 1 axisymmetric compression III II I III II I III II I
32 Plane stress states For isotropic materials, the stress tensor is fully characterized by three stress tensor invariants, { I1, J, J 3} or { I, II, III} while the stress state is characterized by the two dimensionless ratios of the invariants, e.g. { I1 / J, J 3 / J 3/ } or {, } or /, / } { II I III I with I J and arccos 3 3/ J J 3 3 3
33 Plane stress states Under plane stress conditions, one principal stress is zero. The stress state may thus be characterized by the ratio of the two nonzero principal stresses. As a result, the stress triaxiality and the Lode angle parameter are no longer independent for plane stress, i.e. we have a functional relationship [] axisymmetric tension (1 Biaxial comp. ( I 0 Tensioncompression ( II 0 generalized shear (0 Biaxial tension ( III 0 axisymmetric compression (
34 Unit Cell with Central Void : Dynamic behavior of materials and structures Results from Localization Analysis Stresses on Plane of Localization Linear Mohr-Coulomb approximation
35 Hosford-Coulomb Ductile Fracture Model Principal stress space,, } { I II III τ + c(σ I + σ III ) = b തσ Hf Hosford- Mohr-Coulomb Coordinate transformation Haigh-Westergaard Mixed strain-stress space {,, } space,, e } f [, ] f Isotropic hardening law k[ e p ] e f 1 k { p [, ] f f e f
36 Hosford-Coulomb Ductile Fracture Model General form von Mises equivalent plastic strain to fracture e e [,, a, b, c] f f e f Stress triaxiality Lode angle parameter 3 material parameters Detailed expressions e g f HC b g 1 c [, ] HC 1 n 1 1 a 1 a 1 a f f f f f f a c f f I II II III I III I III f I [ ] cos (1 ) 3 6 f II [ ] cos (3 ) 3 6 [ ] cos (1 ) f
37 Hosford-Coulomb Ductile Fracture Model Influence of parameter b a=1.3 c=0.05 b=0.5 b=0.4 b=0.3 b=0. b = strain to fracture for uniaxial tension (or equi-biaxial tension)
38 Hosford-Coulomb Ductile Fracture Model Influence of parameter a c 0.1 a a a Can easily adjust the depth of the plane strain valley Compare: Mohr-Coulomb a 1 c 0. c 0.35 a 0.8 c 0 c 0.1 a
39 Hosford-Coulomb Ductile Fracture Model Influence of parameter c c=0.1 c=0. a=1.3 n=0.1 c=0.05 c=
40 Hosford-Coulomb Ductile Fracture Model Rapid calibration guideline Step I: Identify b Step II: Identify a Step III: Identify c a= c=0 b=0.4 c=0 b=0.4 a=1.15 b=0.4 a=1.15 c=
41 Hosford-Coulomb Ductile Fracture Model Excel program for calibration
42 Hosford-Coulomb Ductile Fracture Model 3D View e f D View e f plane stress plane stress heart of the model: e e [, ] f f 4 4 4
43 Damage Accumulation Define damage indicator e f e [, ] f D de e [, ] f p D D 0 1 (initial) (fracture) Example: uniaxial tension VIDEO
44 Damage Accumulation Define damage indicator e f e [, ] f D de e [, ] f p D D 0 1 (initial) (fracture) Example: uniaxial compression followed by tension VIDEO
45 Damage Accumulation Define damage indicator e f e [, ] f D de e [, ] f p D D 0 1 (initial) (fracture) Example: uniaxial compression followed by tension Non-linear loading path effect!
46 Reading Materials for Lecture #7 S. Suresh, Fatigue of Materials, Cambridge University Press, and S.J. Marcadet,
Lecture #8: Ductile Fracture (Theory & Experiments)
Lecture #8: Ductile Fracture (Theory & Experiments) by Dirk Mohr ETH Zurich, Department of Mechanical and Process Engineering, Chair of Computational Modeling of Materials in Manufacturing 2015 1 1 1 Ductile
More informationA rate-dependent Hosford-Coulomb model for predicting ductile fracture at high strain rates
EPJ Web of Conferences 94, 01080 (2015) DOI: 10.1051/epjconf/20159401080 c Owned by the authors, published by EDP Sciences, 2015 A rate-dependent Hosford-Coulomb model for predicting ductile fracture at
More informationMMJ1133 FATIGUE AND FRACTURE MECHANICS E ENGINEERING FRACTURE MECHANICS
E ENGINEERING WWII: Liberty ships Reprinted w/ permission from R.W. Hertzberg, "Deformation and Fracture Mechanics of Engineering Materials", (4th ed.) Fig. 7.1(b), p. 6, John Wiley and Sons, Inc., 1996.
More informationMechanics of Earthquakes and Faulting
Mechanics of Earthquakes and Faulting Lectures & 3, 9/31 Aug 017 www.geosc.psu.edu/courses/geosc508 Discussion of Handin, JGR, 1969 and Chapter 1 Scholz, 00. Stress analysis and Mohr Circles Coulomb Failure
More informationMMJ1133 FATIGUE AND FRACTURE MECHANICS A - INTRODUCTION INTRODUCTION
A - INTRODUCTION INTRODUCTION M.N.Tamin, CSMLab, UTM Course Content: A - INTRODUCTION Mechanical failure modes; Review of load and stress analysis equilibrium equations, complex stresses, stress transformation,
More informationPlasticity R. Chandramouli Associate Dean-Research SASTRA University, Thanjavur
Plasticity R. Chandramouli Associate Dean-Research SASTRA University, Thanjavur-613 401 Joint Initiative of IITs and IISc Funded by MHRD Page 1 of 9 Table of Contents 1. Plasticity:... 3 1.1 Plastic Deformation,
More informationINCREASING RUPTURE PREDICTABILITY FOR ALUMINUM
1 INCREASING RUPTURE PREDICTABILITY FOR ALUMINUM Influence of anisotropy Daniel Riemensperger, Adam Opel AG Paul Du Bois, PDB 2 www.opel.com CONTENT Introduction/motivation Isotropic & anisotropic material
More informationExperiments and Numerical Simulations on Stress-State-Dependence of Ductile Damage Criteria
Experiments and Numerical Simulations on Stress-State-Dependence of Ductile Damage Criteria Michael Brünig, Steffen Gerke and Daniel Brenner Abstract The paper deals with a series of new experiments and
More informationFailure surface according to maximum principal stress theory
Maximum Principal Stress Theory (W. Rankin s Theory- 1850) Brittle Material The maximum principal stress criterion: Rankin stated max principal stress theory as follows- a material fails by fracturing
More informationMechanics of Earthquakes and Faulting
Mechanics of Earthquakes and Faulting www.geosc.psu.edu/courses/geosc508 Surface and body forces Tensors, Mohr circles. Theoretical strength of materials Defects Stress concentrations Griffith failure
More informationFailure from static loading
Failure from static loading Topics Quiz /1/07 Failures from static loading Reading Chapter 5 Homework HW 3 due /1 HW 4 due /8 What is Failure? Failure any change in a machine part which makes it unable
More information1. Background. is usually significantly lower than it is in uniaxial tension
NOTES ON QUANTIFYING MODES OF A SECOND- ORDER TENSOR. The mechanical behavior of rocks and rock-like materials (concrete, ceramics, etc.) strongly depends on the loading mode, defined by the values and
More informationPressure Vessels Stresses Under Combined Loads Yield Criteria for Ductile Materials and Fracture Criteria for Brittle Materials
Pressure Vessels Stresses Under Combined Loads Yield Criteria for Ductile Materials and Fracture Criteria for Brittle Materials Pressure Vessels: In the previous lectures we have discussed elements subjected
More informationFCP Short Course. Ductile and Brittle Fracture. Stephen D. Downing. Mechanical Science and Engineering
FCP Short Course Ductile and Brittle Fracture Stephen D. Downing Mechanical Science and Engineering 001-015 University of Illinois Board of Trustees, All Rights Reserved Agenda Limit theorems Plane Stress
More informationA Simple and Accurate Elastoplastic Model Dependent on the Third Invariant and Applied to a Wide Range of Stress Triaxiality
A Simple and Accurate Elastoplastic Model Dependent on the Third Invariant and Applied to a Wide Range of Stress Triaxiality Lucival Malcher Department of Mechanical Engineering Faculty of Tecnology, University
More informationFME461 Engineering Design II
FME461 Engineering Design II Dr.Hussein Jama Hussein.jama@uobi.ac.ke Office 414 Lecture: Mon 8am -10am Tutorial Tue 3pm - 5pm 10/1/2013 1 Semester outline Date Week Topics Reference Reading 9 th Sept 1
More informationBone Tissue Mechanics
Bone Tissue Mechanics João Folgado Paulo R. Fernandes Instituto Superior Técnico, 2016 PART 1 and 2 Introduction The objective of this course is to study basic concepts on hard tissue mechanics. Hard tissue
More informationChapter 6: Plastic Theory
OHP Mechanical Properties of Materials Chapter 6: Plastic Theory Prof. Wenjea J. Tseng 曾文甲 Department of Materials Engineering National Chung Hsing University wenjea@dragon.nchu.edu.tw Reference: W. F.
More informationCONSIDERATIONS CONCERNING YIELD CRITERIA INSENSITIVE TO HYDROSTATIC PRESSURE
CONSIDERATIONS CONCERNING YIELD CRITERIA INSENSITIVE TO HYDROSTATIC PRESSURE ADRIAN SANDOVICI, PAUL-DORU BARSANESCU Abstract. For distinguishing between pressure insensitive and pressure sensitive criteria,
More informationClassical fracture and failure hypotheses
: Chapter 2 Classical fracture and failure hypotheses In this chapter, a brief outline on classical fracture and failure hypotheses for materials under static loading will be given. The word classical
More informationModule 5: Failure Criteria of Rock and Rock masses. Contents Hydrostatic compression Deviatoric compression
FAILURE CRITERIA OF ROCK AND ROCK MASSES Contents 5.1 Failure in rocks 5.1.1 Hydrostatic compression 5.1.2 Deviatoric compression 5.1.3 Effect of confining pressure 5.2 Failure modes in rocks 5.3 Complete
More informationExamination in Damage Mechanics and Life Analysis (TMHL61) LiTH Part 1
Part 1 1. (1p) Define the Kronecker delta and explain its use. The Kronecker delta δ ij is defined as δ ij = 0 if i j 1 if i = j and it is used in tensor equations to include (δ ij = 1) or "sort out" (δ
More informationBrittle Deformation. Earth Structure (2 nd Edition), 2004 W.W. Norton & Co, New York Slide show by Ben van der Pluijm
Lecture 6 Brittle Deformation Earth Structure (2 nd Edition), 2004 W.W. Norton & Co, New York Slide show by Ben van der Pluijm WW Norton, unless noted otherwise Brittle deformation EarthStructure (2 nd
More informationFracture Mechanics, Damage and Fatigue Non Linear Fracture Mechanics: J-Integral
University of Liège Aerospace & Mechanical Engineering Fracture Mechanics, Damage and Fatigue Non Linear Fracture Mechanics: J-Integral Ludovic Noels Computational & Multiscale Mechanics of Materials CM3
More informationGISSMO Material Modeling with a sophisticated Failure Criteria
GISSMO Material Modeling with a sophisticated Failure Criteria André Haufe, Paul DuBois, Frieder Neukamm, Markus Feucht Dynamore GmbH Industriestraße 2 70565 Stuttgart http://www.dynamore.de Motivation
More informationCracks Jacques Besson
Jacques Besson Centre des Matériaux UMR 7633 Mines ParisTech PSL Research University Institut Mines Télécom Aγνωστ oς Θεoς Outline 1 Some definitions 2 in a linear elastic material 3 in a plastic material
More informationLecture #10: Anisotropic plasticity Crashworthiness Basics of shell elements
Lecture #10: 151-0735: Dynamic behavior of materials and structures Anisotropic plasticity Crashworthiness Basics of shell elements by Dirk Mohr ETH Zurich, Department of Mechanical and Process Engineering,
More informationChapter 2 A Continuum Damage Model Based on Experiments and Numerical Simulations A Review
Chapter 2 A Continuum Damage Model Based on Experiments and Numerical Simulations A Review Michael Brünig Abstract The paper summarizes the author s activities in the field of damage mechanics. In this
More informationFracture mechanics fundamentals. Stress at a notch Stress at a crack Stress intensity factors Fracture mechanics based design
Fracture mechanics fundamentals Stress at a notch Stress at a crack Stress intensity factors Fracture mechanics based design Failure modes Failure can occur in a number of modes: - plastic deformation
More informationConcept Question Comment on the general features of the stress-strain response under this loading condition for both types of materials
Module 5 Material failure Learning Objectives review the basic characteristics of the uni-axial stress-strain curves of ductile and brittle materials understand the need to develop failure criteria for
More informationMAE 322 Machine Design. Dr. Hodge Jenkins Mercer University
MAE 322 Machine Design Dr. Hodge Jenkins Mercer University What is this Machine Design course really about? What you will learn: How to design machine elements 1) Design so they won t break under varying
More informationElastic-Plastic Fracture Mechanics. Professor S. Suresh
Elastic-Plastic Fracture Mechanics Professor S. Suresh Elastic Plastic Fracture Previously, we have analyzed problems in which the plastic zone was small compared to the specimen dimensions (small scale
More informationCritical applied stresses for a crack initiation from a sharp V-notch
Focussed on: Fracture and Structural Integrity related Issues Critical applied stresses for a crack initiation from a sharp V-notch L. Náhlík, P. Hutař Institute of Physics of Materials, Academy of Sciences
More informationGeology 229 Engineering Geology. Lecture 5. Engineering Properties of Rocks (West, Ch. 6)
Geology 229 Engineering Geology Lecture 5 Engineering Properties of Rocks (West, Ch. 6) Common mechanic properties: Density; Elastic properties: - elastic modulii Outline of this Lecture 1. Uniaxial rock
More informationStress Concentration. Professor Darrell F. Socie Darrell Socie, All Rights Reserved
Stress Concentration Professor Darrell F. Socie 004-014 Darrell Socie, All Rights Reserved Outline 1. Stress Concentration. Notch Rules 3. Fatigue Notch Factor 4. Stress Intensity Factors for Notches 5.
More informationFatigue and Fracture
Fatigue and Fracture Multiaxial Fatigue Professor Darrell F. Socie Mechanical Science and Engineering University of Illinois 2004-2013 Darrell Socie, All Rights Reserved When is Multiaxial Fatigue Important?
More informationAdvanced Strength of Materials Prof S. K. Maiti Mechanical Engineering Indian Institute of Technology, Bombay. Lecture 27
Advanced Strength of Materials Prof S. K. Maiti Mechanical Engineering Indian Institute of Technology, Bombay Lecture 27 Last time we considered Griffith theory of brittle fracture, where in it was considered
More informationLecture #2: Split Hopkinson Bar Systems
Lecture #2: Split Hopkinson Bar Systems by Dirk Mohr ETH Zurich, Department of Mechanical and Process Engineering, Chair of Computational Modeling of Materials in Manufacturing 2015 1 1 1 Uniaxial Compression
More informationModule 5: Theories of Failure
Module 5: Theories of Failure Objectives: The objectives/outcomes of this lecture on Theories of Failure is to enable students for 1. Recognize loading on Structural Members/Machine elements and allowable
More informationFatigue calculations in ANSYS Workbench. Martin Eerme
Fatigue calculations in ANSYS Workbench Martin Eerme What is fatigue? In materials science, fatigue is the progressive and localized structural damage that occurs when a material is subjected to cyclic
More informationANSYS Mechanical Basic Structural Nonlinearities
Lecture 4 Rate Independent Plasticity ANSYS Mechanical Basic Structural Nonlinearities 1 Chapter Overview The following will be covered in this Chapter: A. Background Elasticity/Plasticity B. Yield Criteria
More informationMAE 322 Machine Design Lecture 2. Dr. Hodge Jenkins Mercer University
MAE 322 Machine Design Lecture 2 Dr. Hodge Jenkins Mercer University Statics Load Failure Theories to Understand Maximum Normal Stress (MNS) Maximum Shear Stress (MSS) Distortion Energy (DE) Coulomb-Mohr
More informationMultiaxial Fatigue. Professor Darrell F. Socie. Department of Mechanical Science and Engineering University of Illinois at Urbana-Champaign
Multiaxial Fatigue Professor Darrell F. Socie Department of Mechanical Science and Engineering University of Illinois at Urbana-Champaign 2001-2011 Darrell Socie, All Rights Reserved Contact Information
More informationLecture Triaxial Stress and Yield Criteria. When does yielding occurs in multi-axial stress states?
Lecture 5.11 Triaial Stress and Yield Criteria When does ielding occurs in multi-aial stress states? Representing stress as a tensor operational stress sstem Compressive stress sstems Triaial stresses:
More informationEffect of the intermediate principal stress on fault strike and dip - theoretical analysis and experimental verification
Effect of the intermediate principal stress on fault strike and dip - theoretical analysis and experimental verification B. Haimson University of Wisconsin, USA J. Rudnicki Northwestern University, USA
More informationLinear Elastic Fracture Mechanics
Measure what is measurable, and make measurable what is not so. - Galileo GALILEI Linear Elastic Fracture Mechanics Krishnaswamy Ravi-Chandar Lecture presented at the University of Pierre and Marie Curie
More informationCrack Tip Plastic Zone under Mode I Loading and the Non-singular T zz -stress
Crack Tip Plastic Zone under Mode Loading and the Non-singular T -stress Yu.G. Matvienko Mechanical Engineering Research nstitute of the Russian Academy of Sciences Email: ygmatvienko@gmail.com Abstract:
More informationChapter 7. Highlights:
Chapter 7 Highlights: 1. Understand the basic concepts of engineering stress and strain, yield strength, tensile strength, Young's(elastic) modulus, ductility, toughness, resilience, true stress and true
More informationA novel approach to predict the growth rate of short cracks under multiaxial loadings
A novel approach to predict the growth rate of short cracks under multiaxial loadings F. Brugier 1&2, S. Pommier 1, R. de Moura Pinho 2, C. Mary 2 and D. Soria 2 1 LMT-Cachan, ENS Cachan / CNRS / UPMC
More informationStatic Failure (pg 206)
Static Failure (pg 06) All material followed Hookeʹs law which states that strain is proportional to stress applied, until it exceed the proportional limits. It will reach and exceed the elastic limit
More informationTectonics. Lecture 12 Earthquake Faulting GNH7/GG09/GEOL4002 EARTHQUAKE SEISMOLOGY AND EARTHQUAKE HAZARD
Tectonics Lecture 12 Earthquake Faulting Plane strain 3 Strain occurs only in a plane. In the third direction strain is zero. 1 ε 2 = 0 3 2 Assumption of plane strain for faulting e.g., reverse fault:
More informationNumerical modeling of standard rock mechanics laboratory tests using a finite/discrete element approach
Numerical modeling of standard rock mechanics laboratory tests using a finite/discrete element approach S. Stefanizzi GEODATA SpA, Turin, Italy G. Barla Department of Structural and Geotechnical Engineering,
More informationStress concentrations, fracture and fatigue
Stress concentrations, fracture and fatigue Piet Schreurs Department of Mechanical Engineering Eindhoven University of Technology http://www.mate.tue.nl/ piet December 1, 2016 Overview Stress concentrations
More informationLecture #6: 3D Rate-independent Plasticity (cont.) Pressure-dependent plasticity
Lecture #6: 3D Rate-independent Plasticity (cont.) Pressure-dependent plasticity by Borja Erice and Dirk Mohr ETH Zurich, Department of Mechanical and Process Engineering, Chair of Computational Modeling
More information5. STRESS CONCENTRATIONS. and strains in shafts apply only to solid and hollow circular shafts while they are in the
5. STRESS CONCENTRATIONS So far in this thesis, most of the formulas we have seen to calculate the stresses and strains in shafts apply only to solid and hollow circular shafts while they are in the elastic
More informationMaterial is perfectly elastic until it undergoes brittle fracture when applied stress reaches σ f
Material is perfectly elastic until it undergoes brittle fracture when applied stress reaches σ f Material undergoes plastic deformation when stress exceeds yield stress σ 0 Permanent strain results from
More informationModule-4. Mechanical Properties of Metals
Module-4 Mechanical Properties of Metals Contents ) Elastic deformation and Plastic deformation ) Interpretation of tensile stress-strain curves 3) Yielding under multi-axial stress, Yield criteria, Macroscopic
More informationThe Frictional Regime
The Frictional Regime Processes in Structural Geology & Tectonics Ben van der Pluijm WW Norton+Authors, unless noted otherwise 1/25/2016 10:08 AM We Discuss The Frictional Regime Processes of Brittle Deformation
More informationMassachusetts Institute of Technology Department of Mechanical Engineering Cambridge, MA 02139
Massachusetts Institute of Technology Department of Mechanical Engineering Cambridge, MA 02139 2.002 Mechanics and Materials II Spring 2004 Laboratory Module No. 6 Fracture Toughness Testing and Residual
More informationME 535 Project Report Numerical Computation of Plastic Zone Shapes in Fracture Mechanics. V.V.H. Aditya ( ) Rishi Pahuja ( ) June 9, 2014
ME 535 Project Report Numerical Computation of Plastic Zone Shapes in Fracture Mechanics V.V.H. Aditya (137301) Rishi Pahuja (137303) June 9, 014 Abstract The purpose of this project is to numerically
More informationMathematical Relations Related to the Lode. Parameter for Studies of Ductility
Advanced Studies in Theoretical Physics Vol. 0, 06, no., - 4 HIKARI Ltd, www.m-hikari.com http://dx.doi.org/0.988/astp.06.50 Mathematical Relations Related to the Lode Parameter for Studies of Ductility
More information* Many components have multiaxial loads, and some of those have multiaxial loading in critical locations
Why do Multiaxial Fatigue Calculations? * Fatigue analysis is an increasingly important part of the design and development process * Many components have multiaxial loads, and some of those have multiaxial
More informationReference material Reference books: Y.C. Fung, "Foundations of Solid Mechanics", Prentice Hall R. Hill, "The mathematical theory of plasticity",
Reference material Reference books: Y.C. Fung, "Foundations of Solid Mechanics", Prentice Hall R. Hill, "The mathematical theory of plasticity", Oxford University Press, Oxford. J. Lubliner, "Plasticity
More informationStructural Metals Lab 1.2. Torsion Testing of Structural Metals. Standards ASTM E143: Shear Modulus at Room Temperature
Torsion Testing of Structural Metals Standards ASTM E143: Shear Modulus at Room Temperature Purpose To determine the shear modulus of structural metals Equipment Tinius-Olsen Lo-Torq Torsion Machine (figure
More informationCHAPTER 2 Failure/Fracture Criterion
(11) CHAPTER 2 Failure/Fracture Criterion (12) Failure (Yield) Criteria for Ductile Materials under Plane Stress Designer engineer: 1- Analysis of loading (for simple geometry using what you learn here
More informationTentamen/Examination TMHL61
Avd Hållfasthetslära, IKP, Linköpings Universitet Tentamen/Examination TMHL61 Tentamen i Skademekanik och livslängdsanalys TMHL61 lördagen den 14/10 2000, kl 8-12 Solid Mechanics, IKP, Linköping University
More informationBulk Metal Forming II
Bulk Metal Forming II Simulation Techniques in Manufacturing Technology Lecture 2 Laboratory for Machine Tools and Production Engineering Chair of Manufacturing Technology Prof. Dr.-Ing. Dr.-Ing. E.h.
More informationVolume 2 Fatigue Theory Reference Manual
Volume Fatigue Theory Reference Manual Contents 1 Introduction to fatigue 1.1 Introduction... 1-1 1. Description of the applied loading... 1-1.3 Endurance curves... 1-3 1.4 Generalising fatigue data...
More informationMultiscale modeling of failure in ABS materials
Institute of Mechanics Multiscale modeling of failure in ABS materials Martin Helbig, Thomas Seelig 15. International Conference on Deformation, Yield and Fracture of Polymers Kerkrade, April 2012 Institute
More informationTreatment of Constraint in Non-Linear Fracture Mechanics
Treatment of Constraint in Non-Linear Fracture Mechanics Noel O Dowd Department of Mechanical and Aeronautical Engineering Materials and Surface Science Institute University of Limerick Ireland Acknowledgements:
More informationApplication of Three Dimensional Failure Criteria on High-Porosity Chalk
, 5-6 May 00, Trondheim, Norway Nordic Energy Research Programme Norwegian U. of Science and Technology Application of Three Dimensional Failure Criteria on High-Porosity Chalk Roar Egil Flatebø and Rasmus
More informationStudies on the affect of Stress Triaxiality on Strain Energy Density, and CTOD under Plane Stress Condition Subjected to Mixed Mode (I/II) Fracture
Studies on the affect of Stress Triaxiality on Strain Energy Density, and CTOD under Plane Stress Condition... Studies on the affect of Stress Triaxiality on Strain Energy Density, and CTOD under Plane
More informationMechanics of Earthquakes and Faulting
Mechanics of Earthquakes and Faulting www.geosc.psu.edu/courses/geosc508 Overview Milestones in continuum mechanics Concepts of modulus and stiffness. Stress-strain relations Elasticity Surface and body
More informationAN ABSTRACT OF A THESIS HYDROSTATIC STRESS EFFECTS IN METAL PLASTICITY
AN ABSTRACT OF A THESIS HYDROSTATIC STRESS EFFECTS IN METAL PLASTICITY Phillip A. Allen Master of Science in Mechanical Engineering Classical metal plasticity theory assumes that hydrostatic pressure has
More informationFRACTURE OF CRACKED MEMBERS 1. The presence of a crack in a structure may weaken it so that it fails by fracturing in two or more pieces.
Aerospace Structures Fracture Mechanics: An Introduction Page 1 of 7 FRACTURE OF CRACED MEMBERS 1. The presence of a crack in a structure may weaken it so that it fails by fracturing in two or more pieces.
More informationFracture Mechanics, Damage and Fatigue: Composites
University of Liège Aerospace & Mechanical Engineering Fracture Mechanics, Damage and Fatigue: Composites Ludovic Noels Computational & Multiscale Mechanics of Materials CM3 http://www.ltas-cm3.ulg.ac.be/
More informationME 2570 MECHANICS OF MATERIALS
ME 2570 MECHANICS OF MATERIALS Chapter III. Mechanical Properties of Materials 1 Tension and Compression Test The strength of a material depends on its ability to sustain a load without undue deformation
More informationMechanics of Materials Primer
Mechanics of Materials rimer Notation: A = area (net = with holes, bearing = in contact, etc...) b = total width of material at a horizontal section d = diameter of a hole D = symbol for diameter E = modulus
More informationAnisotropic plasticity, anisotropic failure and their application to the simulation of aluminium extrusions under crash loads
Anisotropic plasticity, anisotropic failure and their application to the simulation of aluminium extrusions under crash loads Paul Du Bois, Consulting engineer Oasys LS-DYNA Users Meeting 28th January
More informationAfter lecture 16 you should be able to
Lecture 16: Design of paper and board packaging Advanced concepts: FEM, Fracture Mechanics After lecture 16 you should be able to describe the finite element method and its use for paper- based industry
More information**********************************************************************
Department of Civil and Environmental Engineering School of Mining and Petroleum Engineering 3-33 Markin/CNRL Natural Resources Engineering Facility www.engineering.ualberta.ca/civil Tel: 780.492.4235
More informationDonald P. Shiley School of Engineering ME 328 Machine Design, Spring 2019 Assignment 1 Review Questions
Donald P. Shiley School of Engineering ME 328 Machine Design, Spring 2019 Assignment 1 Review Questions Name: This is assignment is in workbook format, meaning you may fill in the blanks (you do not need
More informationTHE BEHAVIOUR OF REINFORCED CONCRETE AS DEPICTED IN FINITE ELEMENT ANALYSIS.
THE BEHAVIOUR OF REINFORCED CONCRETE AS DEPICTED IN FINITE ELEMENT ANALYSIS. THE CASE OF A TERRACE UNIT. John N Karadelis 1. INTRODUCTION. Aim to replicate the behaviour of reinforced concrete in a multi-scale
More informationIntroduction to fracture mechanics
Introduction to fracture mechanics Prof. Dr. Eleni Chatzi Dr. Giuseppe Abbiati, Dr. Konstantinos Agathos Lecture 6-9 November, 2017 Institute of Structural Engineering, ETH Zu rich November 9, 2017 Institute
More informationDEFORMATION THEORY OF PLASTICITY
DEFORMATION THEORY OF PLASTICITY ROBERT M. JONES Professor Emeritus of Engineering Science and Mechanics Virginia Polytechnic Institute and State University Blacksburg, Virginia 240610219 Bull Ridge Publishing
More informationSandia Fracture Challenge: blind prediction and full calibration to enhance fracture predictability
Sandia Fracture Challenge: blind prediction and full calibration to enhance fracture predictability The MIT Faculty has made this article openly available. Please share how this access benefits you. Your
More informationUse Hooke s Law (as it applies in the uniaxial direction),
0.6 STRSS-STRAIN RLATIONSHIP Use the principle of superposition Use Poisson s ratio, v lateral longitudinal Use Hooke s Law (as it applies in the uniaxial direction), x x v y z, y y vx z, z z vx y Copyright
More informationTopics in Ship Structures
Topics in Ship Structures 8 Elastic-lastic Fracture Mechanics Reference : Fracture Mechanics by T.L. Anderson Lecture Note of Eindhoven University of Technology 17. 1 by Jang, Beom Seon Oen INteractive
More informationTensile stress strain curves for different materials. Shows in figure below
Tensile stress strain curves for different materials. Shows in figure below Furthermore, the modulus of elasticity of several materials effected by increasing temperature, as is shown in Figure Asst. Lecturer
More informationEngineering Solid Mechanics
}} Engineering Solid Mechanics 1 (2013) 1-8 Contents lists available at GrowingScience Engineering Solid Mechanics homepage: www.growingscience.com/esm Impact damage simulation in elastic and viscoelastic
More informationBasic studies of ductile failure processes and implications for fracture prediction
Basic studies of ductile failure processes and implications for fracture prediction J. ZUO, M. A. SUTTON and X. DENG Department of Mechanical Engineering, University of South Carolina, Columbia, SC 2928,
More informationAvailable online at ScienceDirect. 20th European Conference on Fracture (ECF20) Yu.G. Matvienko*
Available online at www.sciencedirect.com ScienceDirect Procedia Materials Science 3 ( 014 ) 141 146 0th European Conference on Fracture (ECF0) The Effect of the non-singular T-stress components on crack
More informationG1RT-CT A. BASIC CONCEPTS F. GUTIÉRREZ-SOLANA S. CICERO J.A. ALVAREZ R. LACALLE W P 6: TRAINING & EDUCATION
A. BASIC CONCEPTS 6 INTRODUCTION The final fracture of structural components is associated with the presence of macro or microstructural defects that affect the stress state due to the loading conditions.
More informationCh 4a Stress, Strain and Shearing
Ch. 4a - Stress, Strain, Shearing Page 1 Ch 4a Stress, Strain and Shearing Reading Assignment Ch. 4a Lecture Notes Sections 4.1-4.3 (Salgado) Other Materials Handout 4 Homework Assignment 3 Problems 4-13,
More informationSpherical Pressure Vessels
Spherical Pressure Vessels Pressure vessels are closed structures containing liquids or gases under essure. Examples include tanks, pipes, essurized cabins, etc. Shell structures : When essure vessels
More information20. Rheology & Linear Elasticity
I Main Topics A Rheology: Macroscopic deformation behavior B Linear elasticity for homogeneous isotropic materials 10/29/18 GG303 1 Viscous (fluid) Behavior http://manoa.hawaii.edu/graduate/content/slide-lava
More informationRecent Developments in Damage and Failure Modeling with LS-DYNA
Recent evelopments in amage and Failure Modeling with LS-YNA r. André Haufe ynamore GmbH Frieder Neukamm, r. Markus Feucht aimler AG Paul ubois Consultant r. Thomas Borvall ERAB 1 Technological challenges
More information7.6 Stress in symmetrical elastic beam transmitting both shear force and bending moment
7.6 Stress in symmetrical elastic beam transmitting both shear force and bending moment à It is more difficult to obtain an exact solution to this problem since the presence of the shear force means that
More informationDevelopment, implementation and Validation of 3-D Failure Model for Aluminium 2024 for High Speed Impact Applications
Development, implementation and Validation of -D Failure Model for Aluminium 2024 for High Speed Impact Applications Paul Du Bois, Murat Buyuk, Jeanne He, Steve Kan NCAC-GWU th International LS-DYNA Users
More informationExperimental study of mechanical and thermal damage in crystalline hard rock
Experimental study of mechanical and thermal damage in crystalline hard rock Mohammad Keshavarz Réunion Technique du CFMR - Thèses en Mécanique des Roches December, 3 nd 2009 1 Overview Introduction Characterization
More information