DEF coupled to thermal history: Recent advances
|
|
- Abigail Boyd
- 5 years ago
- Views:
Transcription
1 DEF coupled to thermal history: Recent advances François Toutlemonde, Badreddine Kchakech*, Othman Omikrine-Metalssi, Renaud-Pierre Martin IFSTTAR / Paris-Est University * Ph.D. co-sponsored by IFSTTAR and EDF, presently at Marrakech private University
2 Delayed Ettringite Formation (DEF) as coupled to T Autogenous expansive reaction (no necessary supply of external sulphates) leading to cracking and serious serviceability and structural capacity concerns. DEF affects structures submitted to early-age ettringite destabilization (T >~ 65 C) e.g. in case of bad controlled thermal curing of precast elements or massive structures DEF risk is proven on cement paste, mortar (Barbarulo 2002, Famy 1999) and only isolated results on concrete, when heating occurs at a mature stage (T > ~ 65 C) DEF is known as qualitatively affected by maximum temperature reached and heating duration. Non fully satisfactory models (Baghdadi 2008, Martin 2012) Quantification is required for : Precise reassessment (coupling law) Adjusted prevention guidelines Confirmation of a threshold value? Confirmation of pessimum effect? Clarification of mechanism(s) 2
3 Experimental program Jointly sponsored Additional data to Baghdadi s, Brunetaud s, Martin s and Pavoine s PhDs Prism specimens 11 x 11 x 22 cm w/ automated axial swelling monitoring Various thermal treatments at early age and 100 days (mature stage) 3 specimens for each condition kept in separate water baths to promote swelling Trapezoidal-shaped temperature profiles applied 2 hour after casting or at 100 days: (T max 61 to 86 C, 1 to 28 days duration) T plateau controlled w/ deviation < 0,15 C Heating process controlled w/ deviation < 0,5 % Satisfactory control of the treatment process! + Realistic temperature profiles for validation Companion specimens for physical / mechanical characterization: Tensile and compressive strengths Poisson s ratio, Young s modulus Porosity, control of alkali leaching 3
4 Experimental program Jointly sponsored Both mixes: W/C = 0.46 Porosity 15.5 % Siliceous, non ASR-reactive aggregate Concrete SO 3 (% C) C 3 A (% C) Na 2 O eq (% C) R1 f c28 = 50.5 MPa f c99 = 52.0 MPa R0 f c28 = 52.4 MPa f c99 = 63.9 MPa Thermal treatments T ( C) Duration of the plateau at maximal T (days) 61 C (early) (R1 +R0) - 66 C (early) (R1) - 71 C (early) 2 (R1) 7 (R1) 12 (R1) 14 (R1) 28 (R1) 81 C (early) 1 (R1+R0) 3 (R1+R0) 5 (R1) 7 (R1+R0) 14 (R1 + R0) 81 C (late) 1 (R1+R0) 3 (R1+R0) - 7 (R1+R0) 14 (R1) 86 C (late) (R1) - - 4
5 Raw results: Influence of maximum temperature Highly non-linear response: for this concrete, threshold between 61 and 66 C Very low scatter Latency times lower for higher maximum temperature Pessimum effect confirmed on the amplitude of final expansion 5 5
6 Raw results: Influence of heating duration (71 C) Latency and characteristic times lower for longer heating durations Pessimum effect of heating duration confirmed on amplitude of final expansion 6 6
7 Raw results: Influence of heating duration (81 C) Latency and characteristic times lower for longer heating durations (except 14 days) Pessimum effect of heating duration confirmed on amplitude of final expansion 7 7
8 Confirmation of high combined sensitivity to Tmax and duration Expansion (%) R1_J_V_74 R1_J_V_ Time (Days) R1_J_V_74 (Thermal treatment Tmax=74 C immersed in a water bath in an oven) vs. R1_J_V_79 (Thermal treatment Tmax=79 C in heated pool) 8 8
9 Raw results: R1, late heat treatment 2.0% 1.8% 1.6% Expansion (%) 1.4% 1.2% 1.0% 0.8% 0.6% 0.4% 0.2% 0.0% Time (days) R1_T_81_1 R1_T_81_3 R1_T_81_7 R1_T_81_14 R1_T_86_5 R1_T_V_79 Confirmed risk of significant expansion for R1 after heating when mature Pessimum effect with respect to final expansion (decreases after 7 days) Similar kinetics whatever the thermal treatment duration 9 9
10 Raw results: R0, late heat treatment Expansion (%) 0.20% 0.18% 0.16% 0.14% 0.12% 0.10% 0.08% 0.06% 0.04% 0.02% 0.00% Time (days) R0_T_81_1 R0_T_81_3 R0_T_81_7 Confirmed risk of significant expansion for R0 after heating when mature Pessimum effect with respect to final expansion (3 days > 7 days) Immediate swelling initiation whatever the thermal treatment duration 10
11 Processing: Quantitative description of the results 1.0% 0.9% 0.8% 0.7% 0.6% 0.5% 0.4% 0.3% 0.2% 0.1% 0.0% Expansion (%) 1 e ε() t = εhyd + ε 1 β L c 1+ e?? ε (t) = function of T(t) t τc t α e ( t τ ) τ?? ε,τ L,τ C, α, β = functions of T(t) Experimental data Proposed model improved from Brunetaud, 2005 Time (days) Example of parameters calibration (R1_J_81_14) ε (%) 0,89 τ L (days) 53 τ C (days) 15 α (days) 98 β 1,00 ε Hyd (%) 0,001 Deviation 1,66E-06 11
12 T(t): Which integrated indicator could make sense? Total supplied energy (T 0 =20 C) «DEF-effective» thermal energy (T 0 =65 C) Effective Thermal Energy (ETE) = < T(t)-T 0 > dt T 0 optimized for the reference R1 concrete to obtain master curves = 65 C Simplified assumption as compared to an Arrhenius-type activation of ettringite dissolution 12
13 R1, early age heating: ε vs. effective thermal energy Ultimate expansion (%) 2.0% 1.8% 1.6% 1.4% 1.2% 1.0% 0.8% 0.6% 0.4% 0.2% 0.0% 81 C 71 C 81 C_3 jr 81 C_5 jr 71 C_12 jr Martin C_7 jr 71 C_7 jr 71 C_14 jr 81 C_1 jr V_79 71 C_28 jr 81 C_14 jr 71 C_2 jr < T(t)-T 0 > dt T 0 =65 C Time (days) Effective Thermal Energy ( C.h) 13
14 Confirmed sense: R1 & R0 mixes + results from the literature (early age) Similar master curve for R1, Baghdadi & Al Shamaa R0 lower expansion 14
15 Results: τ L vs. effective thermal energy (early age) τ L vs. ETE: Relevance of a single master curve? 15
16 Results: τ C vs. effective thermal energy (early age) Single curve for R1 and similar mixes, higher τ C for R0 mix (less reactive)? 16
17 Early age vs. late heating: ε vs. ETE The pessimum effect with respect to final expansion seems to be shifted from thermal treatment at early age to treatment at a mature stage: Higher energy required for sulphates extraction / ettringite destabilization? 17
18 Early age vs. late heating: τ L vs. ETE τ L shorter than for early age heating in both cases, almost constant for R1 τ L (for R1, early age heating) tends to the value for late heat treatment for longlasting treatments τ L very high for R0 early age heating 1 day (650 days) 18
19 Early age vs. late heating: τ C vs. ETE For R0 badly conditioned S-shaped curves for late heating, indeterminate τ C For R1 τ c shorter than for early age heating, almost constant 19
20 Analysis: ultimate expansion, pessimum effect Some specimens observed using X-Ray Diffraction: confirms the origin of observed expansions as ettringite (DEF) consistent with the possible explanation of the pessimum effect on final expansion, by stable combination of aluminates (hydrogarnets) yet to be confirmed in a more quantitative way Shots Number R1_J_81_1_1 R1_J_81_3_1 R1_J_81_7_1 R1_J_81_14_1 AFt Q= Quartz P= Portlandite B=Brownmillerite AFt= Ettringite K=Katoite B AFt P + AFt K Q B + AFt Q 4 11 Angle (2θ) Proposal of a quantitative estimation of ε based on available reactants, accounting for the influence of alkali content 20
21 Proposed interpretation (early age) 21
22 Proposed model applied to R1 heated at early age 22
23 Proposed model extended to other mixes heated at early age Promising possible prediction of ultimate expansion, to be further validated 23
24 Effects of early / late heating Kinetics controlled by accessibility of sulphates? Early age heating Short duration SO4 2- hidden in LD CSH Semi-fine capillary pores τ L and τ C hardly influenced by the late treatment duration: the mature cement paste «host» of DEF might keep High τ L, τ c Early age heating Long duration similar, conversely to the early age SO4 2- at border of HD CSH heating case where size of capillary Wide capillary pores pores is critical Low τ L, τ c Low expansion amplitude for reduced late heating durations: the energy No early age heating required to destabilize ettringite might be Heating at mature stage higher than when heating is applied during setting, because ettringite might have a stronger structure and be better Short duration SO4 2- at the place of AFt Fine capillary pores Low τ L, τ c if any linked to other hydrates? Sulphates No early age heating might have kept on site? Heating at mature stage Long duration Low latency time in case of late SO4 2- at border of LD CSH heating due to the low porosity available Fine capillary pores for hosting delayed ettringite formed? Low τ L, τ c 24
25 Conclusions Results on concrete heated at early age help concluding that: The effective thermal energy makes sense as a global influent parameter on DEF expansion Master curves including a pessimum effect on ε can be quantitatively described consistently with probable mechanisms The concept of temperature threshold (around 65 C, mainly influenced by alkali content) is relevant (high non-linearity) For concrete heated at a mature stage: The risk of significant DEF-induced expansion is quantitatively confirmed in case of late heating + water A pessimum effect with respect to final expansion has been observed with possible similar origin as for early-age heated concrete Characteristic and latency times are shorter than for early-age heated concrete exhibiting DEF, and the treatment duration has negligible influence on the kinetics Future tasks: Complete chemical analyses to clarify where expansive species are formed and whether they migrate in the pores (role of water and alkalis) Confirm the predictive capability of the developed model with further data of ultimate expansion Implement ETE-dependence of ε in the model for re-assessment 25
Neutron Tomography Measurement of Delayed Ettringite Formation in Concrete
Neutron Tomography Measurement of Delayed Ettringite Formation in Concrete Richard A. Livingston Materials Science & Engineering Dept University of Maryland 14th ISNDCM Marina del Rey, CA, June 24, 2015
More informationMonitoring of the creep and the relaxation behaviour of concrete since setting time, part 1: compression
Author manuscript, published in " " Monitoring of the creep and the relaxation behaviour of concrete since setting time, part : compression C. Boulay, M. Crespini, B. Delsaute 2, S. Staquet 2 IFSTTAR-Paris,
More informationNote: For further information, including the development of creep with time, Annex B may be used.
..4 Creep and shrinkage ()P Creep and shrinkage of the concrete depend on the ambient humidity, the dimensions of the element and the composition of the concrete. Creep is also influenced by the maturity
More informationMulti-scale Study of Calcium Leaching in Cement Pastes with Silica Nanoparticles
Multi-scale Study of Calcium Leaching in Cement Pastes with Silica Nanoparticles J.J. Gaitero, W. Zhu, and I. Campillo * Abstract. Calcium leaching is a degradation process consisting in the progressive
More informationAGGREGATE EXPANSIVITY DUE TO SULFIDE OXIDATION - I. REACTION SYSTEM AND RATE MODEL
AGGREGATE EXPANSIVITY DUE TO SULFIDE OXIDATION - I. REACTION SYSTEM AND RATE MODEL I. Casanova, L. Agulló and A. Aguado Departament d Enginyeria de la Construcció, Edifici C1, Universitat Politècnica de
More informationNUMERICAL SIMULATION OF CONCRETE EXPOSED TO HIGH TEMPERATURE DAMAGE AND EXPLOSIVE SPALLING
NUMERICAL SIMULATION OF CONCRETE EXPOSED TO HIGH TEMPERATURE DAMAGE AND EXPLOSIVE SPALLING Prof. Joško Ožbolt 1 Josipa Bošnjak 1, Goran Periškić 1, Akanshu Sharma 2 1 Institute of Construction Materials,
More informationYuko Ogawa, Ryoichi Sato and Kenji Kawai Institute of Engineering, Hiroshima University, Japan
Early Age Deformation, its Resultant Stress and Creep Properties of Concrete with and without Internal Curing Subjected to High Temperature History at an Early Age Yuko Ogawa, Ryoichi Sato and Kenji Kawai
More informationNondestructive Monitoring of Setting and Hardening of Portland Cement Mortar with Sonic Methods
Nondestructive Monitoring of Setting and Hardening of Portland Cement Mortar ith Sonic Methods Thomas Voigt, Northestern University, Evanston, USA Surendra P. Shah, Northestern University, Evanston, USA
More informationCONCRETE IN THE MIDDLE EAST
CONCRETE IN THE MIDDLE EAST ALKALI REACTIVITY IN CONCRETE STRUCTURES Presented by : Eng. ELIE J. SFEIR INTRODUCTION What is the Alkali-Reactivity? The alkali reaction is a chemical reaction between some
More informationHealth Monitoring of Early Age Concrete
1 Health Monitoring of Early Age Concrete Surendra P. Shah Northwestern University, Illinois, USA Keynote CONSEC 04, Seoul, June 30, 2004. 2 Scope of Research Test method for in-situ testing of early age
More informationChapter. Materials. 1.1 Notations Used in This Chapter
Chapter 1 Materials 1.1 Notations Used in This Chapter A Area of concrete cross-section C s Constant depending on the type of curing C t Creep coefficient (C t = ε sp /ε i ) C u Ultimate creep coefficient
More informationAn Investigation on the Alkali-Silica Reactivity of Đzmir Region Aggregates
Cement and Concrete Technology in the 2000 s Second International Symposium, 6-10 September, 2000. Istanbul, Turkey An Investigation on the Alkali-Silica Reactivity of Đzmir Region Aggregates Selçuk Türkel
More informationLECTURE NO. 4-5 INTRODUCTION ULTRASONIC * PULSE VELOCITY METHODS
LECTURE NO. 4-5 ULTRASONIC * PULSE VELOCITY METHODS Objectives: To introduce the UPV methods To briefly explain the theory of pulse propagation through concrete To explain equipments, procedures, calibrations,
More informationPozzolanic reactions between natural and artificial aggregate and the concrete matrix
2007 World of Coal Ash (WOCA), May 7-10, 2007, Northern Kentucky, USA http://www.flyash.info Pozzolanic reactions between natural and artificial aggregate and the concrete matrix Nambu Masateru 1, Kato
More informationCOUPLED PHYSICAL AND GEOCHEMICAL MODEL FOR EXTERNAL SULFATE ATTACK IN CONCRETE
- Technical Paper - COUPLED PHYSICAL AND GEOCHEMICAL MODEL FOR EXTERNAL SULFATE ATTACK IN CONCRETE Yogarajah ELAKNESWARAN *1, Tetsuya ISHIDA *2 ABSTRACT In this study, a coupled physical and geochemical
More informationEARLY AGE THERMAL CRACK CONTROL IN MASS CONCRETE
EARLY AGE THERMAL CRACK CONTROL IN MASS CONCRETE A.W.R.M.G.W.D.B. Girihagama * and S.M.A. Nanayakkara University of Moratuwa, Colombo, Sri Lanka *E-mail: danu.girihagama.uom @ gmail.com, TP: +94711352729
More informationLecture 13 Portland Cement Based Paste Systems
Hydration, Porosity and Strength of Cementitious Materials Prof. Sudhir Mishra and Prof. K. V. Harish Department of Civil Engineering Indian Institute of Technology, Kanpur Lecture 13 Portland Cement Based
More informationWikipedia.org BUILDING STONES. Chapter 4. Materials of Construction-Building Stones 1
Wikipedia.org BUILDING STONES Chapter 4 Materials of Construction-Building Stones 1 What is Stone? Stone is a concretion of mineral matter. Used either as a; Construction material, Manufacture of other
More informationNon-Destructive Assessment of Residual Strength of Thermally Damaged Concrete Made with Different Aggregate Types
IOP Conference Series: Materials Science and Engineering PAPER OPEN ACCESS NonDestructive Assessment of Residual Strength of Thermally Damaged Concrete Made with Different Aggregate Types To cite this
More informationStudy of immobilization mechanism of chloride ion with different concentration of chloride ion using cement with powder admixtures
Study of immobilization mechanism of chloride ion with different concentration of chloride ion using cement with powder admixtures Takeshi IYODA and Yuto KOMIYAMA --, Toyosu Koto-ku, Tokyo, Japan, 88,
More informationChapter 2 Concrete with Recycled Aggregates: Experimental Investigations
Chapter 2 Concrete with Recycled Aggregates: Experimental Investigations Carmine Lima, Marco Pepe, Ciro Faella and Enzo Martinelli Abstract The mechanical behaviour of Recycled Aggregate Concrete (RAC)
More informationThe Revision of the French Recommendations for the Prevention of Delayed Ettringite Formation Bruno GODART & Loïc DIVET
The Revision of the French Recommendations for the Prevention of Delayed Ettringite Formation Bruno GODART & Loïc DIVET JCI-RILEM International Workshop, CONCRACK5, April 24-26, 2017, Japan 1 Introduction
More informationTECHNICAL NOTE. ph of Potassium Acetate Deicing Solution
TECHNICAL NOTE TECH NOTE NO: 36 TITLE: AUTHORS: CONTACT: ph of Potassium Acetate Deicing Solution Li Ai and Leslie Struble L. J. Struble, University of Illinois, Dept of Civil & Environmental Engineering
More informationTemperature Measurements in the Production of Quality Concrete
Temperature Measurements in the Production of Quality Concrete John McClafferty PE (AZ) GCC - (915) 540-6975 January 13 & 14, 2017 NMSU Samuel P. Maggard Quality Concrete School 10/25/2016 1 1) Relevant
More informationEVALUATION OF DAMAGES DUE TO ALKALI-SILICA REACTION WITH ACOUSTICS TECHNIQUES. DEVELOPMENT OF A NEW NONLINEAR METHOD.
EVALUATION OF DAMAGES DUE TO ALKALI-SILICA REACTION WITH ACOUSTICS TECHNIQUES. DEVELOPMENT OF A NEW NONLINEAR METHOD. Apedovi S. Kodjo (1, 2), Patrice Rivard (1), Frederic Cohen-Tenoudji (3) and Jean-Louis
More informationA DISCRETE MODEL FOR ALKALI-SILICA-REACTION IN CONCRETE
VIII International Conference on Fracture Mechanics of Concrete and Concrete Structures FraMCoS-8 J.G.M. Van Mier, G. Ruiz, C. Andrade, R.C. Yu and X.X. Zhang (Eds) A DISCRETE MODEL FOR ALKALI-SILICA-REACTION
More informationSHRINKAGE EIGENSTRESSES AND HARDENING OF CONCRETE
International Conference on Material Science and 64th RILEM Annual Week in Aachen MATSCI 199 SHRINKAGE EIGENSTRESSES AND HARDENING OF CONCRETE P. Paulini, University Innsbruck, Institute of Construction
More informationHardened Concrete. Lecture No. 16
Hardened Concrete Lecture No. 16 Fatigue strength of concrete Modulus of elasticity, Creep Shrinkage of concrete Stress-Strain Plot of Concrete At stress below 30% of ultimate strength, the transition
More informationTHE COURSE OF THE ALKALI-AGGREGATE REACTION IN THE PRESENCE OF LITHIUM NITRATE
riginal papers THE CURSE F THE ALALI-AGGREGATE REACTIN IN THE PRESENCE F LITHIUM NITRATE Z. WSIA, # J. ZAPAŁA-SŁAWETA ielce University of Technology, Faculty of Civil Engineering and Architecture, ielce,
More information13 AN ELECTROCHEMICAL METHOD FOR ACCELERATED TESTING OF CHLORIDE DIFFUSIVITY IN CONCRETE
13 AN ELECTROCHEMICAL METHOD FOR ACCELERATED TESTING OF CHLORIDE DIFFUSIVITY IN CONCRETE TIEWEI. ZHANG and ODD E. GJ@RV Division of Building Materials, The Norwegian Institute of Technology - NTH N - 7034
More informationINFLUENCE OF AGGREGATE INTERFACE IN CONCRETE ON PERMEABILITY
OS2-4 INFLUENCE OF AGGREGATE INTERFACE IN CONCRETE ON PERMEABILITY Koki Tagomori (1), Takeshi Iyoda (2) (1) Graduate school of Engineering, Shibaura Institute of Technology, Japan (2) Department of Civil
More informationEFFECTS OF THE CATHODIC CURRENT ON ALKALI-SILICA AGGREGATE REACTION
Journal of Marine Science and Technology, Vol. 23, No. 2, pp. 183-19 (215) 183 DOI: 1.6119/JMST-14-422-1 EFFECTS OF THE CATHODIC CURRENT ON ALKALI-SILICA AGGREGATE REACTION Jiang-Jhy Chang, Weichung Yeih,
More informationInvestigation of Potential Alkali-Carbonate Reaction in Carbonate Rocks by Rock Cylinder Method
International Journal of Engineering and Applied Sciences (IJEAS) Investigation of Potential Alkali-Carbonate Reaction in Carbonate Rocks by Rock Cylinder Method U S Vidyarthi, Ravi Agarwal, N Sivakumar
More informationON THE CHEMISTRY OF DELAYED ETTRINGITE FORMATION
ON THE CHEMISTRY OF DELAYED ETTRINGITE FORMATION H.Y. Ghorab Faculty of Science,Helwan University G&W Science & Engineering Company, Cairo, Egypt Abstract Basic research was carried out on the chemistry
More informationME 243. Mechanics of Solids
ME 243 Mechanics of Solids Lecture 2: Stress and Strain Ahmad Shahedi Shakil Lecturer, Dept. of Mechanical Engg, BUET E-mail: sshakil@me.buet.ac.bd, shakil6791@gmail.com Website: teacher.buet.ac.bd/sshakil
More informationAPPENDIX C. Modified ASTM C 1260 Test Method to Evaluate Aggregate Reactivity in Presence of Deicer Solutions
APPENDIX C Modified ASTM C 1260 Test Method to Evaluate Aggregate Reactivity in Presence of Deicer Solutions INTERIM TEST PROTOCOL Modified ASTM C 1260 Test Method to Evaluate Aggregate Reactivity in Presence
More informationNon-Destructive Electrical Methods to Determine the Quality of Concrete
Athens Journal of Technology & Engineering X Y Non-Destructive Electrical Methods to Determine the Quality of Concrete By Sreekanta Das William Clements Govinda Raju There is a great need to explore and
More informationThe Pennsylvania State University. The Graduate School. College of Engineering. A Dissertation in. Civil Engineering.
The Pennsylvania State University The Graduate School College of Engineering CHARACTERIZING SATURATED MASS TRANSPORT IN FRACTURED CEMENTITIOUS MATERIALS A Dissertation in Civil Engineering by Alireza Akhavan
More informationEstimates of Parameters Used By Model B3
Appendix C Estimates of Parameters Used By Model B3 C.1 Equations Used By B3 Model B3 (Bažant and Baweja 1995a, Bažant and Baweja 2000a) covers creep and shrinkage of concrete, including their coupling.
More informationEffect of different molarities of Sodium Hydroxide solution on the Strength of Geopolymer concrete
American Journal of Engineering Research (AJER) e-issn : 23-847 p-issn : 23-936 Volume-4, Issue-3, pp-139-145 www.ajer.org Research Paper Open Access Effect of different molarities of Sodium Hydroxide
More informationStudies on Furan Polymer Concrete
Studies on Furan Polymer Concrete Rajesh Katiyar 1, Shobhit Shukla 2 1Associate Professor, Department of Chemical engineering, H.B.T.U., Kanpur-208002, India 2Research Scholar, Department of Chemical engineering
More informationDamage of porous stones by salt crystallization
Computational Methods and Experimental Measurements XVII 333 Damage of porous stones by salt crystallization M. Keppert, M. Čáchová, J. Fořt, D. Koňáková, Z. Pavlík & R. Černý Department of Materials Engineering
More informationNumerical Simulation on Concrete Pouring Process of Self-Compacting Concrete-Filled Steel Tube
Numerical Simulation on Concrete Pouring Process of Self-Compacting Concrete-Filled Steel Tube B.H. Qi Building Research Institute, Angang Construction Group, Anshan Liaoning, China J.Z. Fu& S. Yan School
More informationResearch done at Berkeley
Research done at Berkeley Mathematical model using double layer theory Neutron diffraction of reactive aggregates Soft X-ray microscopy of the expansive gels Characterization of the ASR gel Repair strategies
More informationSTRUTURAL DURABILITY, DEFORMATION PROPERTIES AND FRACTURE MECHANICS PARAMETERS OF ADVANCED SILICATE MATERIALS
STRUTURAL DURABILITY, DEFORMATION PROPERTIES AND FRACTURE MECHANICS PARAMETERS OF ADVANCED SILICATE MATERIALS E. Shinkevich (1), Y. Zaytsev (2), E. Lutskin (1), G. Bondarenko (3), A. Tymnyak (1) (1) Odessa
More informationA Dynamic Method Determining Equilibrium Moisture Content of Porous Materials
A Dynamic Method Determining Equilibrium Moisture Content of Porous Materials Shinsaku Tada *1 and Kazumasa Watanabe * *1 Texte, Inc., -6-44-3, Misawa, Hino, Tokyo 191-3, Japan * Tottori University of
More informationREGRESSION MODELING FOR STRENGTH AND TOUGHNESS EVALUATION OF HYBRID FIBRE REINFORCED CONCRETE
REGRESSION MODELING FOR STRENGTH AND TOUGHNESS EVALUATION OF HYBRID FIBRE REINFORCED CONCRETE S. Eswari 1, P. N. Raghunath and S. Kothandaraman 1 1 Department of Civil Engineering, Pondicherry Engineering
More informationEffect of Natural Zeolite as Partial Replacement of Portland Cement on Concrete Properties
Effect of Natural Zeolite as Partial Replacement of Portland Cement on Concrete Properties Eva Vejmelková 1, Tereza Kulovaná 1, Dana Koňáková 1, Martin Keppert 1, Martin Sedlmajer 2, Robert Černý 1 1 Czech
More informationREVISED VIEW ON CHEMICAL SHRINKAGE
REVISED VIEW ON CHEMICAL SHRINKAGE S. Zhutovsky and K. Kovler National Building Research Institute - Faculty of Civil and Environmental Engineering Technion - Israel Institute of Technology, Haifa 32000,
More informationAlkali-Silica Reaction In Concrete
Alkali-Silica Reaction In Concrete By KAUSHAL KISHORE Materials Engineer, Roorkee The problem of Alkali-silica reaction was believed to be non-existent in India till 1983, when its occurrence was diagnosed
More informationAlternative Method to Estimate Alkali-Silica Reactivity of Active- Chert Aggregates
Fourth International Conference on Sustainable Construction Materials and Technologies http://www.claisse.info/proceedings.htm SCMT4 Las Vegas, USA, August 7-11, 16 Alternative Method to Estimate Alkali-Silica
More informationConcrete Technology Prof. B. Bhattacharjee Department of Civil Engineering Indian Institute of Technology, Delhi
Concrete Technology Prof. B. Bhattacharjee Department of Civil Engineering Indian Institute of Technology, Delhi Lecture - 25 Strength of Concrete: Factors Affecting Test Results Welcome to module 6, lecture
More informationCIVE 2700: Civil Engineering Materials Fall Lab 2: Concrete. Ayebabomo Dambo
CIVE 2700: Civil Engineering Materials Fall 2017 Lab 2: Concrete Ayebabomo Dambo Lab Date: 7th November, 2017 CARLETON UNIVERSITY ABSTRACT Concrete is a versatile construction material used in bridges,
More informationRequirements for Mass Concrete Construction in Alabama
60 th Transportation Conference Requirements for Mass Concrete Construction in Alabama By: Anton K. Schindler, Ph.D., P.E. Professor and HRC Director Department of Civil Engineering Auburn University Co-Authors:
More informationULTRASONIC PULSE METHOD THE CEMENT STRENGTH EVALUATION TOOL
ULTRASONIC PULSE METHOD THE CEMENT STRENGTH EVALUATION TOOL Jiri BROZOVSKY (1), Jiri ZACH (1) (1) TIBME, FCE, Brno University of Technology,and Czech Republic Abstract The spectrum of control and laboratory
More informationCreep and aging in nonlinear models for concrete
Creep and aging in nonlinear models for concrete Andrzej Truty Thomas Zimmermann Krzysztof Podleś Jan Szarliński Cracow University of Technology and ZACE Services ZACE Services prof.em. Cracow University
More informationInfluence of various acids on the physico mechanical properties of pozzolanic cement mortars
Sādhanā Vol. 32, Part 6, December 2007, pp. 683 691. Printed in India Influence of various acids on the physico mechanical properties of pozzolanic cement mortars STÜRKEL, B FELEKOǦLU and S DULLUÇ Department
More information3D Finite Element analysis of stud anchors with large head and embedment depth
3D Finite Element analysis of stud anchors with large head and embedment depth G. Periškić, J. Ožbolt & R. Eligehausen Institute for Construction Materials, University of Stuttgart, Stuttgart, Germany
More informationMECHANICAL PROPERTIES OF CONCRETE WITH SAP PART II: MODULUS OF ELASTICITY
MCHANICAL PROPRTIS OF CONCRT WITH SAP PART II: MODULUS OF LASTICITY Marianne Tange Hasholt (1), Morten H. Seneka Jespersen (1) and Ole Mejlhede Jensen (1) (1) Technical University of Denmark, Lyngby, Denmark
More informationMICROMECHANICAL MODELS FOR CONCRETE
Chapter 5 MICROMECHANICAL MODELS FOR CONCRETE 5.1 INTRODUCTION In this chapter three micromechanical models will be examined. The first two models are the differential scheme and the Mori-Tanaka model
More informationTECHNICAL PAPER INVESTIGATION INTO THE VALIDATION OF THE SHELL FATIGUE TRANSFER FUNCTION
Authors: TECHNICAL PAPER INVESTIGATION INTO THE VALIDATION OF THE SHELL FATIGUE TRANSFER FUNCTION Anthony Stubbs (Presenter), BE(Hons), Masters student, University of Canterbury. aps49@student.canterbury.ac.nz.
More informationCHAPTER 4 STATISTICAL MODELS FOR STRENGTH USING SPSS
69 CHAPTER 4 STATISTICAL MODELS FOR STRENGTH USING SPSS 4.1 INTRODUCTION Mix design for concrete is a process of search for a mixture satisfying the required performance of concrete, such as workability,
More informationEvaluation of Flexural Stiffness for RC Beams During Fire Events
3 rd International Structural Specialty Conference 3 ième conférence internationale spécialisée sur le génie des structures Edmonton, Alberta June 6-9, 202 / 6 au 9 juin 202 Evaluation of Flexural Stiffness
More informationApplication of Ultra-Sonic Pulse Velocity Techniques for Concrete Quality Measurements
Application of Ultra-Sonic Pulse Velocity Techniques for Concrete Quality Measurements Uday Bhise, Engineer. NDT; Durocrete Engineering Services Pvt. Ltd. Introduction This method of testing was originally
More informationBasic Examination on Assessing Mechanical Properties of Concrete That Has Suffered Combined Deterioration from Fatigue and Frost Damage
5th International Conference on Durability of Concrete Structures Jun 30 Jul 1, 2016 Shenzhen University, Shenzhen, Guangdong Province, P.R.China Basic Examination on Assessing Mechanical Properties of
More informationConcrete pathologies. Concrete chemical degradation causes. Alkali-silica reaction in concrete
Concrete pathologies The concrete is not an inert material: LABORATORY AND MICROSTRUCTURAL TESTS ON THE DETECTION AND PREDICTION OF AAR António Santos Silva 1 & Isabel Fernandes 2 1 - Materials Department,
More informationEFFECT OF LITHIUM BASED ADMIXTURE ON ALKALI AGGREGATE REACTION IN CONCRETE - A STATE OF ART REPORT
International Journal of Civil Engineering and Technology (IJCIET) Volume 8, Issue 9, September 2017, pp. 299 304, Article ID: IJCIET_08_09_035 Available online at http://http://www.iaeme.com/ijciet/issues.asp?jtype=ijciet&vtype=8&itype=9
More informationAPPLICATION OF ULTRASONIC METHODS FOR EARLY AGE CONCRETE CHARACTERISATION
The 8 th International Conference of the Slovenian Society for Non-Destructive Testing»Application of Contemporary Non-Destructive Testing in Engineering«September 1-3, 005, Portorož, Slovenia, pp. 99-108
More informationStrain-Based Design Model for FRP-Confined Concrete Columns
SP-230 57 Strain-Based Design Model for FRP-Confined Concrete Columns by N. Saenz and C.P. Pantelides Synopsis: A constitutive strain-based confinement model is developed herein for circular concrete columns
More informationConcrete Engineering and Technology Prof. Sudhir Misra Department of Civil Engineering Indian Institute of Technology, Kanpur
Concrete Engineering and Technology Prof. Sudhir Misra Department of Civil Engineering Indian Institute of Technology, Kanpur Lecture - 24 Alkali aggregate reaction (Part 1 of 2) And welcome to another
More informationSTUDY ON EFFECTS OF NONLINIAR DISTRIBUTION AND SLAB THICKNESS ON THERMAL STRESS OF AIRPORT CONCRETE PAVEMENT
STUDY ON EFFECTS OF NONLINIAR DISTRIBUTION AND SLAB THICKNESS ON THERMAL STRESS OF AIRPORT CONCRETE PAVEMENT TSUBOKAWA, Yukitomo Airport Department, National Institute for Land and Infrastructure Management,
More informationWINTER 16 EXAMINATION
Model ject Code: Important Instructions to examiners: ) The answers should be examined by key words and not as word-to-word as given in the model answer scheme. ) The model answer and the answer written
More informationStrength of Material. Shear Strain. Dr. Attaullah Shah
Strength of Material Shear Strain Dr. Attaullah Shah Shear Strain TRIAXIAL DEFORMATION Poisson's Ratio Relationship Between E, G, and ν BIAXIAL DEFORMATION Bulk Modulus of Elasticity or Modulus of Volume
More informationPart 7. Nonlinearity
Part 7 Nonlinearity Linear System Superposition, Convolution re ( ) re ( ) = r 1 1 = r re ( 1 + e) = r1 + r e excitation r = r() e response In the time domain: t rt () = et () ht () = e( τ) ht ( τ) dτ
More informationEXPERIMENTS ON SHEAR-FLEXURAL BEHAVIORS OF MODEL CAST IN PLACE CONCRETE PILES
13 th World Conference on Earthquake Engineering Vancouver, B.C., Canada August 1-6, 2004 Paper No. 1403 EXPERIMENTS ON SHEAR-FLEXURAL BEHAVIORS OF MODEL CAST IN PLACE CONCRETE PILES Toshihiko YAMAMOTO
More informationEFFECT OF THE TEST SET-UP ON FRACTURE MECHANICAL PARAMETERS OF CONCRETE
Fracture Mechanics of Concrete Structures Proceedings FRAMCOS-3 AEDIFICATIO Publishers, D-79104 Freiburg, Germany EFFECT OF THE TEST SET-UP ON FRACTURE MECHANICAL PARAMETERS OF CONCRETE V. Mechtcherine
More informationDETERMINATION OF MORTAR SATURATION METHODS BASED ON MRI SCANNING IMAGE
410 Journal of Marine Science and Technology, Vol. 21, No. 4, pp. 410-416 (2013) DOI: 10.6119/JMST-012-0522-1 DETERMINATION OF MORTAR SATURATION METHODS BASED ON MRI SCANNING IMAGE Hsiang-Wei Chiang and
More informationAnalytical Study on Flexural Strength of Reactive Powder Concrete
Analytical Study on Flexural Strength of Reactive Powder Concrete Jagannathasn Saravanan, S.Sathiyapriya Abstract The Flexural strength of Reactive powder concrete specimens is done routinely; it is performed
More informationA STUDY FOR PREVENTING THE RISK OF ALKALI-SILICA REACTION DUE TO THE AGGREGATE PLANNED TO BE USED IN MASS CONCRETE OF DERINER DAM AND HEPP PROJECT
A STUDY FOR PREVENTING THE RISK OF ALKALI-SILICA REACTION DUE TO THE AGGREGATE PLANNED TO BE USED IN MASS CONCRETE OF DERINER DAM AND HEPP PROJECT Aydin SAGLIK, M. Fatih KOCABEYLER General Directorate
More informationCOMPARISONS OF LINEAR REGRESSION MODELS FOR PROPERTIES OF ALKALI- ACTIVATED BINDER CONCRETE
COMPARISONS OF LINEAR REGRESSION MODELS FOR PROPERTIES OF ALKALI- ACTIVATED BINDER CONCRETE Arkamitra Kar Birla Institute of Technology and Science - Pilani, Telangana, India Udaya B. Halabe West Virginia
More informationA Simple Approach to Modeling Chloride Diffusion into Cracked Reinforced Concrete Structures
Journal of Civil Engineering Research 215, 5(5): 97-15 DOI: 1.5923/j.jce.21555.1 A Simple Approach to Modeling Chloride Diffusion into Cracked Reinforced Conete Structures Thuy Ninh Nguyen, Hoang Quoc
More information= 0.7 (6) = 0.62 (7) = 0.60 (8)
Research Journal of Applied Sciences, Engineering and Technology 8(11): 1294-1298, 2014 DOI:10.19026/rjaset.8.1099 ISSN: 2040-7459; e-issn: 2040-7467 2014 Maxwell Scientific Publication Corp. Submitted:
More informationNumerical Prediction of Crack Width in Massive Concrete Member due to Heat of Hydration
Graduate Member School due to of Heat Environmental of Hydration Studies Nagoya University Maruyama Laboratory Numerical Prediction of Crack Width in Massive Concrete Ingi Jang * 1 Ippei Maruyama* 1 *
More informationA MICROMECHANIC MODEL FOR CHARACTERIZATION OF CEMENT PASTE AT EARLY AGE VALIDATED WITH EXPERIMENTS
A MICROMECHANIC MODEL FOR CHARACTERIZATION OF CEMENT PASTE AT EARLY AGE VALIDATED WITH EXPERIMENTS Guang Ye Delft University of Technology, the Netherlands Zhihui Sun ACBM, Northwestern University, USA
More informationUNIVERSITY OF SASKATCHEWAN ME MECHANICS OF MATERIALS I FINAL EXAM DECEMBER 13, 2008 Professor A. Dolovich
UNIVERSITY OF SASKATCHEWAN ME 313.3 MECHANICS OF MATERIALS I FINAL EXAM DECEMBER 13, 2008 Professor A. Dolovich A CLOSED BOOK EXAMINATION TIME: 3 HOURS For Marker s Use Only LAST NAME (printed): FIRST
More informationA PARAMETRIC STUDY ON BUCKLING OF R/C COLUMNS EXPOSED TO FIRE
Proceedings of the International Conference in Dubrovnik, 15-16 October 215 A PARAMETRIC STUDY ON BUCKLING OF R/C COLUMNS EXPOSED TO FIRE Lijie Wang, Robby Caspeele, Luc Taerwe Ghent University, Department
More informationHEALTH MONITORING OF EARLY AGE CONCRETE
HEALTH MONITORING OF EARLY AGE CONCRETE Thomas Voigt, Zhihui Sun, Surendra P. Shah Center for Advanced Cement-Based Materials Northwestern University, Illinois, USA Abstract The setting and hardening process
More informationLithium Salt for Reactive Aggregates in Concrete
Lithium Salt for Reactive Aggregates in Concrete Nader Ghafoori 1 and Mohammad Islam 2 1 Professor, University of Nevada, Las Vegas, Department of Civil Engineering, Box 454015, 4505 Maryland Parkway,
More informationAPPLICATION OF THERMAL METHODS IN THE CHEMISTRY OF CEMENT: KINETIC ANALYSIS OF PORTLANDITE FROM NON- ISOTHERMAL THERMOGRAVIMETRC DATA
The First International Proficiency Testing Conference Sinaia, România 11 th 13 th October, 2007 APPLICATION OF THERMAL METHODS IN THE CHEMISTRY OF CEMENT: KINETIC ANALYSIS OF PORTLANDITE FROM NON- ISOTHERMAL
More informationThe University of Texas at Austin
r The University of Texas at Austin College of Engineering COEFFICIENT OF THERMAL EXPANSION FOR FOUR BATCH DESIGNS AND ONE SOLID GRANITE SPECIMEN by A Report Prepared for FOSTER YEOMAN LIMITED by the CENTER
More informationStudy on Solidification Mechanism of Chloride Salt in Base Course. Material of Cement-Fly-ash-Flushed-by-Seawater
Advanced Materials Research Online: 2011-05-12 ISSN: 1662-8985, Vols. 236-238, pp 755-761 doi:10.4028/www.scientific.net/amr.236-238.755 2011 Trans Tech Publications, Switzerland Study on Solidification
More informationPrevention of the quality of cement from chemical and mineralogical parameters of the clinker
International Journal of Innovation and Applied Studies ISSN 2028-9324 Vol. 10 No. 4 Mar. 2015, pp. 1291-1298 2015 Innovative Space of Scientific Research Journals http://www.ijias.issr-journals.org/ Prevention
More informationIMPROVEMENT OF HARDENED CONCRETE DURABILITY BY NANOSILICA ELECTROMIGRATION
IMPROVEMENT OF HARDENED CONCRETE DURABILITY BY NANOSILICA ELECTROMIGRATION M. Sánchez-Moreno 1, M. C. Alonso 1, I Diaz 2 and R. González 2 1 Research Centre on Safety and Durability of Structures and Materials,
More informationQuality control based on electrical resistivity measurements
Quality control based on electrical resistivity measurements Miguel FERREIRA Ph.D. Assistant Professor Department of Civil Engineering, University of Minho Campus de Azurém, 4-58, Guimarães, Portugal rmf@civil.uminho.pt
More informationConstitutive and Damage Accumulation Modeling
Workshop on Modeling and Data needs for Lead-Free Solders Sponsored by NEMI, NIST, NSF, and TMS February 15, 001 New Orleans, LA Constitutive and Damage Accumulation Modeling Leon M. Keer Northwestern
More informationThe UCD community has made this article openly available. Please share how this access benefits you. Your story matters!
Provided by the author(s) and University College Dublin Library in accordance with publisher policies., Please cite the published version when available. Title Reactivity assessment of aggregates : the
More informationAvailable online at ScienceDirect. Procedia Materials Science 11 (2015 )
Available online at www.sciencedirect.com ScienceDirect Procedia Materials Science 11 (2015 ) 594 599 5th International Biennial Conference on Ultrafine Grained and Nanostructured Materials, UFGNSM15 Investigation
More informationEntrance exam Master Course
- 1 - Guidelines for completion of test: On each page, fill in your name and your application code Each question has four answers while only one answer is correct. o Marked correct answer means 4 points
More information6/17/2016. Aggregates & ASR Types, Properties, and Testing. Abstract. Presented by. Larry Sutter Professor Materials Science & Engineering
Aggregates & ASR Types, Properties, and Testing Presented by Larry Sutter Professor Abstract The physical and chemical properties of aggregates play an important role in determining their suitability for
More informationPROBABILISTIC DURABILITY ANALYSIS OF CEMENTITIOUS MATERIALS UNDER COMBINED SULFATE ATTACK AND CALCIUM LEACHING 10149
PROBABILISTIC DURABILITY ANALYSIS OF CEMENTITIOUS MATERIALS UNDER COMBINED SULFATE ATTACK AND CALCIUM LEACHING 10149 S. Sarkar 1, S. Mahadevan 1, J.C.L. Meeussen 2, H. van der Sloot 2, K. Brown 1, D. S.
More information