Discrete ply modelling of open hole tensile tests

Size: px
Start display at page:

Download "Discrete ply modelling of open hole tensile tests"

Transcription

1 Discrete ply modelling of open hole tensile tests Victor Achard, Christophe Bouvet, Bruno Castanié, Clément Chirol To cite this version: Victor Achard, Christophe Bouvet, Bruno Castanié, Clément Chirol. Discrete ply modelling of open hole tensile tests. Composite Structures, Elsevier, 24, vol. 3, pp <.6/j.compstruct >. <hal-63573> HAL Id: hal Submitted on 5 Sep 24 HAL is a multi-disciplinary open access archive for the deposit and dissemination of scientific research documents, whether they are published or not. The documents may come from teaching and research institutions in France or abroad, or from public or private research centers. L archive ouverte pluridisciplinaire HAL, est destinée au dépôt et à la diffusion de documents scientifiques de niveau recherche, publiés ou non, émanant des établissements d enseignement et de recherche français ou étrangers, des laboratoires publics ou privés.

2 Open Archive Toulouse Archive Ouverte (OATAO) OATAO is an open access repository that collects the work of Toulouse researchers and makes it freely available over the web where possible. This is an author-deposited version published in: Eprints ID: 985 To link to this article: DOI:.6/j.compstruct URL: To cite this version: Achard, Victor and Bouvet, Christophe and Castanié, Bruno and Chirol, Clément Discrete ply modelling of open hole tensile tests. (24) Composite Structures, vol. 3. pp ISSN Any correspondence concerning this service should be sent to the repository administrator:

3 Discrete ply modelling of open hole tensile tests Victor Achard b,c, Christophe Bouvet a, Bruno Castanié b,, Clément Chirol c a Université de Toulouse, INSA, UPS, Mines Albi, ISAE, ICA (Institut Clément Ader), ISAE, Avenue Edouard Belin, F-355 Toulouse, France b Université de Toulouse, INSA, UPS, Mines Albi, ISAE, ICA (Institut Clément Ader), INSA, 35 Avenue de Rangueil, 377 Toulouse, France c Université de Toulouse, INSA, UPS, Mines Albi, ISAE, ICA (Institut Clément Ader), AIRBUS France, 36 Route de Bayonne, 3 Toulouse, France a r t i c l e i n f o a b s t r a c t Keywords: Laminate Failure Open-hole tensile test Discrete modelling The Discrete Ply Modelling (DPM) method, previously applied with success to out-of-plane loading such as impact or pull-through, is used to model open hole tensile tests. According to the literature, this kind of test is relevant to assess the efficiency of a modelling strategy. Four different stacking sequences are tested and the failure scenario and patterns are well predicted. The main advantages of DPM are the very small number of parameters required and the robustness of the models. The main drawback is the computation cost.. Introduction The open hole tensile test is a challenge for the virtual testing of composites []. The complex failure modes and patterns described, for example in US-Mil-Hbk 7 [2], depend on many parameters, such as fibres and resin, stacking sequence, hole diameters, Width/Diameter ratios, ply thickness, and others. To correctly model this test, the approaches should be able to find the failure scenarios and, especially, to capture sub-critical damage developing before the final failure of the specimen [3]. Modelling strategies must not only be able to take account of the damage modes of laminated structures (fibre breakage, matrix cracking and splitting, delamination) and their interactions but also capture the stress gradients at the hole edge. This papers aims to apply the method of Discrete Ply Modelling (DPM), originally developed for the impact on laminates, to the open-hole tensile test. In recent years, many of the latest modelling techniques have been applied to this test case. Hu et al. [4] used it to demonstrate the effectiveness of peridynamics [5] for modelling fracture in laminates. Abisset et al [6] tested a damage meso-model on the experimental results of Hallet and Wisnom [,3]. Despite good correlation, the authors pointed out that models based on damage mechanics have difficulties in correctly representing the splitting and intra- and inter-ply interactions otherwise than by ad hoc coefficients. This point has also been highlighted by Van der Meer and Sluys [7]. Therefore, several modelling strategies have recently been developed to better take the discontinuous nature of the damage in laminates into account. In 28, the method of discrete ply Corresponding author. Tel.: address: bruno.castanie@insa-toulouse.fr (B. Castanié). modelling was proposed by Bouvet et al. [8] for modelling low velocity/low energy impacts on laminates stacked with unidirectional plies. A refined and complex mesh is made with an element per ply and interfaces for matrix cracking and delamination. In this way, the coupling between intra- and inter-laminar damage is naturally taken into account. Mapping areas of matrix cracking chosen a priori assumes that diffuse damage is not taken into account. Moreover, only through-the-ply cracks are assumed to be important for damage propagation. This approach predicts splitting very correctly and naturally, as was shown when it was applied to pull-through [9]. In this case, however, the edge of the hole was not correctly modelled and this point should be improved. In the latest developments of the approach, its robustness has been validated []. It has been extended to compression after impact [] by a modification of the breaking law of fibre in compression. Finally, by considering the non-closure of matrix cracks, permanent indentation after impact can be calculated [2]. This type of discrete modelling has also been used by Wisnom and Hallet [] to model the failure of open-hole specimens. However, in this first approach, the paths of possible failures are limited. Other researchers have tried to take account of the discrete nature of the damage of composite structures. Prabhakar and Waas [3] propose a triangular finite element enabling matrix crack failure by a splitting of the element in two parts. The approach has been validated on open-hole tensile test specimens fully oriented at 9, 45 or. This stacking limits the scope of the approach for the moment but, nevertheless, the use of elements enabling splitting is developing. Most of the very recent approaches are based on XFEM [4]. Van der Meer [5,6] uses phantom node elements (a variation on XFEM) to model matrix cracking. Associated with cohesive elements for delamination, this method eliminates

4 the complexity of the mesh of DPM. This method has also been validated on open-hole tensile tests performed by Wisnom and Hallet [3]. Recently this approach has been extended to the representation of diffuse damage [7]. Iarve, Swindeman et al. [8 2] used regularized X-FEM, which differs from the previous approach by interpolation functions that are based on the integration of the initial Gauss scheme. According to the authors, the cracks remain encapsulated within the element and this provides a straightforward three-dimensional implementation. Once again, the open tensile test was used for validation and very good correlation was found with this approach. An analysis of the recent literature shows that recent research has been strongly oriented towards discrete numerical methods for modelling failures in laminates. In this paper, open hole tensile tests are performed with four different stacking sequences and are analysed by means of the DPM method. The following section gives details of the tests and samples. Then DPM is presented and compared with experimental results. Failure scenarios and the influence of the position of the plies are discussed. 2. Experimental analysis The specimens were made from layers of unidirectional, intermediate modulus carbon/epoxy prepreg composites. Four types of stacking sequences were studied and are given in Table. Two laminates were highly oriented at and the other two were quasi-isotropic with a different layout in thickness. The second orientation was obtained by cutting at 9 from the first. The choice of these layups was based on benchmark industrial laminates. The thicknesses ranged from. mm to 2.6 mm. The layups Iso-Q, Q 2-Iso-, oriented and 2 were draped with.3-mm-thick plies and layup Oriented was draped with.8-mm-thick plies. The specimen geometry is given in Fig., where the dimensions are in mm. A 4.2-mm hole was drilled at the centre. The machining quality was guaranteed by the use of new carbide tooling, with a sacrificial plate affixed and tightened on each side of the laminate to limit the damage (particularly delamination). The machining quality was verified by X-ray and no damage induced during drilling was found. The edges of the specimens were trimmed using a diamond disc. The absence of damage on the edges was checked with the aid of a binocular. Local reinforcement, made of 4 fibreglass plies at, was bonded to the specimen. The quasi-static tests were performed at a speed of mm.min on a kn Instron machine at ambient temperature and humidity (Fig. 2). The hole deformation was measured by an Instron extensometer fixed symmetrically to the median planes of the test specimens (Fig. 2). The forces applied were measured by the load cell of the machine. Three tests were performed up to final failure for each layup. The dispersion found (CV) on the reference specimens was low (<4%) but, for the open-hole specimen, it was very low (<%). It seems that the presence of the hole had the effect of reducing the variance. The moduli also showed little dispersion (<3%). The stress/strain experimental responses are plotted in Fig. 3. For each layup, the stresses were normalized. The four laminates had fairly Fig.. Specimen description. equivalent behaviour: a first linear response without apparent loss of rigidity followed by a chaotic plateau showing a series of damage events before final failure of the specimen. The sharp drop in force that occurred at the end of the plate is not shown on these curves because the extensometer could not capture it. For highly oriented specimens, the plateau was short. If structural failure is defined as the first occurrence where a load drop of more than 5% is recorded in a quasi-static test [9], the dispersion is very small (about %). Failure patterns and X-ray analyses that were performed on stopped tests are presented in the model validation subsection. Table Laminate stacking sequences. Laminate Lay up Number of plies Overall thickness (mm) Oriented [ 45///45//9/45/ 45/9//45// / 45] Oriented 2 [45/ 45///9/// 45/45] 9.43 Q-isotropic [/45/9/ 45] 2s 6 2. Q-isotropic 2 [9/ 45//45] 2s 6 2. Fig. 2. Position of the extensometer on tensile specimen and view of the test.

5 Normalized stress,8,6,4 Q-iso Open-hole 3 Open-hole 3,2 Open-hole 2,2 Open-hole 2 Open-hole Open-hole,5,5,5 Strain (%) Strain (%) Normalized stress,8,6,4 Q-iso 2 Normalized stress,8,6,4 Oriented,2 Open-hole 3 Open-hole 3 Open-hole 2,2 Open-hole 2 Open-hole Open-hole,,5,,5,,5,,5 2, Strain (%) Normalized stress,8,6,4 Oriented 2 Strain (%) Fig. 3. Tension behaviour of the four types of open-hole specimens. 3. Numerical modelling The DPM approach has already been explained in several papers [8 2] and only its general principles and its adaptation to the current problem are presented here. In their first paper, Bouvet et al. [8] presented a discrete 3D impact model which was simulated with the Abaqus v6.9 explicit solver and a user-defined Vumat subroutine. In their model, three major failure modes observed in composite impact tests were considered: (i) fibre failure in intraply, (ii) matrix cracking in intra-ply, and (iii) delamination in inter-ply. The mesh construction from their previous work was maintained (Fig 4(a)). The nodes were uniformly stacked in rows and columns for all oriented plies. However, the shapes of the mesh were different: and 9 plies were meshed in a square shape, while 45 and 45 plies were meshed in a parallelogram shape in order to follow the fibre direction and to have coincident nodes in adjacent plies (Fig. 4(b)). The fibre failure was assigned to volume elements C3D8, with zero-thickness cohesive elements of delamination, COH3D8, horizontally inserted between them. Also, vertical zero-thickness cohesive elements COH3D8 were placed between volume element strips in the fibre direction to impose the region of matrix cracking, as shown in Fig. 4(a). The presence of a hole required an adaptation of the in-house meshing program. In [9], the representation of the hole was very poor. However, it did not impact the structural response because of the pull-through loading. For the problem of the open hole tensile test, a good representation of the hole was a prerequisite. Practically, this good representation was obtained by a projection of the nodes adjacent to the hole. If the node/perimeter distance was less than the size of an element, the node was generated and projected on the theoretical perimeter. Otherwise, it was not created. The direction of projection depended on the principal direction of the fold considered in order to maintain the parallelism between slices of matrix cracking elements. In this way, an acceptable model of the hole was obtained (see Fig. 5). In the plies, the method required Delamination (interface elements) 3 y y 2 ply 45 ply (a) x x (b) y y Matrix cracking (interface elements) Fibre failure (volume elements) 9 ply -45 ply x x [ ] 2 ply [9 ] 2 ply Fig. 4. (a) Modelling of impact damage and element types and (b) mesh shape in each oriented ply.

6 the creation of several triangular elements near the hole edge (and some quadrangles), which could be distorted according to the discretization imposed. The delamination elements were subsequently created between adjacent plies. Near the hole, according to the mesh size and the size of the hole, some elements of delamination could be very small and distorted, creating numerical problems, so these elements were simply removed. For the specimens used in the present study, after a convergence study, the size of the elements was chosen as mm 2, leading to a total number of elements between 3, and 43, according to the number of plies (see Fig. 5). 3.. Modelling of matrix cracking As previously mentioned, the matrix cracking is taken into account using vertical non-thickness interface elements between 2 consecutive volume elements (Fig. 4a). Then the interface degradation is rough: if the material is safe, the stiffnesses of these matrix cracking interfaces are considered very high (typically 6 MPa/ mm) and these stiffnesses are put to zero if matrix crack exists. And this failure is driven thanks to standard failure criterion, similar to Hashin s criteria [2], evaluated in the neighbouring volumic elements: hr t i þ 2 þ s2 þ lt s2 tz 6 ðþ Y T ðs L Þ 2 where r t is the transverse stress, s lt and s tz the shear stresses in the (lt) and (tz) planes, h i + is the positive value, Y T is the transverse failure stress and S L is the shear failure stress of the ply. In fact, this classical quadratic criterion was written with stresses at each Gauss point of the 2 neighbouring volume elements and the interface was broken when the criterion was reached at one of these points Modelling of fibre failure As the critical energy release rate is high at fibre failure [22], it was necessary to dissipate this energy in the model. Additional interface elements could have been used but would have induced very complex meshing. To avoid using such interfaces, fibre failure was taken into account through classical continuum damage mechanics but with an original formulation between the integration points of the element to dissipate a constant energy release per unit area. This approach can be compared to the methods with characteristic element length that allow modelling to be independent of the mesh size [23,24]. Then, in order to be able to dissipate the critical energy released due to fibre fractures per unit area of crack, the behaviour laws of the 8 integration points of a volume element were driven together. In this case, the law was written only in opening mode I (Fig. 6), but could be generalized to other fracture modes: Z V Z e T I r l de l! dv ¼ S G fibre;t Ic where r l (e l ) is the longitudinal stress (strain), V (S) is the volume (section) of the element, e T I is the strain of total degradation of the fibre stiffness (Fig. 6) and G fibre,t Ic is the energy release rate in opening mode in the direction of the fibres. It can be noted that volumic elements with 8 Gauss points have been chosen to obtain a good bending behaviour with only one element in the ply thickness. Afterwards, the stiffness in the direction of the fibres was degraded by means of a damage variable d f : r l ¼ ð d f Þ ðh ll e l þ H lt e t þ H lz e z Þ where H ll, H lt and H lz are the stiffnesses in the longitudinal direction. This damage variable is classically evaluated using the longitudinal strain in order to obtain a linear decrease in the longitudinal stress (Fig. 6): d f ¼ et I e l e T ð4þ e l e T I e T where e I T is the strain of total degradation of the fibre stiffness evaluated from Eq. (2) and e T is the strain of damage initiation. Moreover, fibre failure due to compression or shear stresses is not taken into account in this release of the model since it is based on reference cases where these types of fibre failure do not seem to appear. Nevertheless, these failure types could be taken into account for other tests, as in fibre failure under compressive loading for compression after impact []. ð2þ ð3þ Interface elements (a) Interface elements 45 Projected nodes Projected nodes (b) (c) Fig. 5. (a) Discrete ply modelling of an open hole specimen (a) global view, (b) ply, and (c) 45 ply.

7 Fibre failure σ l time = t 8 i T m ax( ε ) = ε i= i ε : Longitudinal strain at integration point rep ε : Representative strain (max. at integration point) t : Time increment at undergoing damage t : Time increment at damage initiation t : Time increment at final failure H Damage initiation time = t ( d f ) H Final failure Section : S (a) Volume : V T ε rep i ε = m ax( ε ) (b) 8 i= time = t T ε I ε l Fig. 6. Principle of fibres failure (a) and behaviour law in the longitudinal direction (b) Modelling of delamination The formation of delamination is generally related with matrix cracking. For the present discrete modelling, even if there is no parameter coupling delamination and matrix cracking, the discontinuity still allows this interaction to take place. Delamination normally occurs between differently oriented plies. It was therefore simulated in interface elements, joining nodes of lower and upper volume ply elements. Through the energy dissipation of fracture mechanics, the criterion of delamination was simulated as linear coupling in three modes based on a power law criterion of mixed-mode delamination propagation with the energy release rate: mode I was in the thickness direction normal to the delamination plane, while mode II and mode III were in the in-plane direction: G I G del Ic þ G II G del IIc þ G III ¼ G del IIIc where GI, GII, GIII are the energy release rate of delamination in modes I, II and III, respectively. GI c del, GII c del, GIII c del are the critical energy release rates of delamination in modes I, II and III, respectively. Moreover, the modes II and III are supposed to be equal (GII c del = GIII c - del ). In this case, the material parameters needed for modelling are given in Table 2. Only five elastic characteristics and 8 parameters related to failure are required. The values of these material parameters come from classical experimental tests from the literatures [22,25 27]. 4. Model validation and discussion Model validation will be performed by comparing the experimental results and the DPM computation in terms of stress vs. strain responses, post-mortem failure patterns and damage maps at structural failure. Then, a detailed analysis of failure scenarios for the four layups will be proposed and the influence of the position of the plies in the thickness will be discussed. The calculation was performed with Abaqus explicit. After a sensitivity study, the rate of application of the load was set at.25 m s. The computation time was then spread over a period ranging from 3 to 2 h on 8 CPUs. 4.. Model validation Stress/strain responses are compared in Fig. 7 for all laminates. The comparison in the elastic part is, of course, very acceptable for all layups. In terms of ultimate tensile stress (UTS), the error varies between 2.8% (Oriented ) and 8% (Q- Iso). Therefore, the model ð5þ Table 2 Material properties. Material properties Density Deliberately reduced Orthotropic elastic properties T E Tensile Young s modulus in fibre direction 63 GPa C E Compressive Young s modulus in fibre 45 GPa direction E 2 Transverse Young s modulus 8.5 GPa v 2 Poisson ratio.35 G 22 Shear modulus 4.2 GPa Matrix cracking Y T Transverse tensile strength 55 MPa S L In-plane shear strength 5 MPa Fibre failure e T (%) e C (%) fibre,t G Ic fibre,c G Ic Delamination del G Ic del G II,c Tensile strain in fibre direction at damage initiation Compressive strain in fibre direction at damage initiation Fracture toughness for mode I in traction Fracture toughness for mode I in compression Interface fracture toughness for opening mode (I) Interface fracture toughness for shear mode (II and III) 2.%.96% 33 N/mm 8 N/mm.65 N/mm 2.8 N/mm captures the final rupture modes well. However, the model has some difficulty in following the plateau. Two examples of final failure patterns are given in Figs. 8 and 9 and the computation of the damage at this step is also shown. For the first example (quasi-isotropic 2), the failure occurs along a line at 45 (Fig. 8(a)). This line corresponds to the cracked area of the matrix in the ply (Fig. 8(b)), together with a narrow region of delaminated interface between the ply and the adjacent ply at 45 (Fig. 8(c)). It is also interesting to note that the zone of fibre failure captured by the model is also at 45 (Fig. 8(d)), which corresponds well with the observed line break. In the second case, corresponding to thick oriented layup, the failure is more complex. The failure pattern is shown in Fig. 9(a). The breakages of the ply are very disordered but is also consistent with the results of DPM modelling (Fig. 9(c)). In the two plies, according to the computation, at UTS, splitting occurs everywhere (Fig. 9(d)), which is also consistent with some aspects of the final failure pattern. Delaminations are visible at the edges of the specimen (Fig. 9(b)) and correspond to [/9]

8 Normalized stress,8,6,4 Oriented / DPM Oriented / Exp data Oriented 2 / DPM Oriented 2 / Exp data Q-iso / DPM Q-iso / Exp data Q-iso 2 / DPM Q-iso 2 / Exp data model in terms of location and size of cracks (in the range of 8 4 mm). A zoom on the photos also showed cracking at 45 for these laminates, in particular for the first oriented layup. For the quasi-iso laminates, the dense matrix cracking zone near the hole is captured. The main 45 splits are also found. We can therefore consider that, globally, the model is able to represent the matrix cracking state at structural failure. In conclusion, direct application of the DPM approach allows the tensile behaviour of open hole specimens to be correctly represented up to failure. In the next subsection, the rupture scenario and the importance of the position of the plies with this model will be discussed for the four laminates Discussion of failure scenario and ply location,2,2,4,6,8,2,4,6,8 Strain (%) Fig. 7. DPM comparison with experimental stress/strain relations. interfaces which, according to the DPM computation (Fig. 9(e)), are also completely delaminated. As the final failure of this laminate is explosive, dynamic phenomena may have occurred and randomized the fracture surface of the plies. Nevertheless, globally, the model predicts the final pattern correctly. The comparison in terms of matrix cracking is shown in Fig. at structural failure. Analysis of the quasi-iso 2 laminates could not be performed due to lack of material. In all cases, the X-ray analysis highlights the main splits very clearly. It is probable that the secondary cracks closed because of a certain plasticity provided by the high proportion of thermoplastic phase in the resin used, which prevented revealing liquid from penetrating sufficiently into small cracks. The comparison is thus primarily qualitative. The main splitting at for oriented laminates is correctly captured by the When laminated specimens are subjected to tension, the structural and ultimate failures are related to the state of damage of the plies. Other plies are often already severely damaged without visible loss of stiffness on the stress/strain curves. However, for laminates with open holes, Hallet et al. [] have shown that this so-called sub-critical damage influences the failure mode of the laminate (brittle, pull-out or delamination) and finally the ultimate load level. In this study, the evolution of sub-critical damage was essentially identical for the four layups. However, they could be influenced by the presence or absence of splitting in the plies. In Fig., the evolution of matrix cracking is shown for a 9 ply (column ), a 45 ply (column 2) and a 45 ply with an adjacent ply which splits (column 3). Rapid growth of the cracking in the plies at 9 and ±45 is noted first. This cracking is particularly severe in the 9 ply, in which the damage propagates rapidly from the hole edge in a butterfly-wing pattern. Then, cracks appear at the free edge and the ply is almost completely damaged before UTS. The DPM modelling shows that this mode of damage of the 9 ply is almost identical for the four configurations and thus independent of adjacent plies. Regarding cracking in the ±45 plies (Fig. ), we note that it spreads transversely along the specimen, from the hole edge to the free edges, generating a characteristic X pattern (columns 2 and 3). This type of damage has already Quasi-iso 2 (a) (b) (c) (d) Fig. 8. Comparison of failure pattern at UTS for quasi-iso 2 layup [/45/9/ 45] 2s (a) bottom view, (b) matrix cracking, (c) delamination in /45 interface, and (d) fibre failure in outer ply.

9 Fig. 9. Comparison of failure pattern at UTS for Oriented 2 layup [45/ 45///9/// 45/45] (a) bottom view, (b) side view, (c) fibre failure in [ 2 ] plies, (d) matrix cracking in [ 2 ] plies, and (e) delamination at [/9] interface. Oriented / DPM,8 Oriented / Exp data Oriented 2 / DPM Oriented 2 / Exp data Q-iso / DPM Q-iso / Exp data Normalized stress,6,4,2,5,5 Strain (%) Fig.. DPM matrix cracking comparison with experimental X-ray at structural failure. been found in the literature [6]. However, when the ply at 45 is not adjacent to a ply at, the propagation is diffuse (Fig., column 2). Where a ply is adjacent to a 45 ply (Fig., column 3), the propagation is much more rapid and also more discrete. This difference in behaviour can be attributed to the splits in the plies, which are also discrete but will change the distribution of local stresses and interact with the adjacent 45 ply, thus influencing the final pattern of cracking at 45. Therefore, it is now timely to consider the different modes of damage in the plies that lead to the final failure. In the following subsections, damage to plies adjacent to plies will not be presented again. Positions of the plies are very different in the 4 different laminates of the industrial benchmark (Fig. 2). In cases A, B, D and G, plies are inside the material, in case C, the ply is on the surface and, in cases E and F, the thickness is doubled. The easiest scenario to analyse (quasi-isotropic 2) will be presented first and the most complex (Oriented ) last, following the order used in Fig Failure scenario of quasi-isotropic 2 laminate The plies studied in this laminate (type A or B, Fig. 2) are internal and their interfaces are the same ( 45 / /45 ). The cracking pattern of 45 and 9 is similar to those given previously in Fig. and is not recalled here. Damage in the ply is shown in Fig. 3. Matrix cracking in the plies begins early but does not propagate and remains confined to one or two bands of elements

10 Fig.. Matrix cracking in 9 plies (column ), 45 plies (column 2) and 45 with splitting in the adjacent ply. at the hole edge. When the load increases, there is first a brutal propagation of the cracked area of the matrix in conjunction with the first fibre failures. Simultaneously, delamination occurs in a similar shape in the /45 and 45 /9 interfaces. This damage creates a sufficient loss of stiffness to be identified as structural failure. At this stage, approximately 2% of the net section is broken. Beyond this limit, simultaneous progressive propagation of the different types of damage is observed at an angle of 45. The damaged area is confined to a relatively narrow band (Fig. 3). Finally, the area of broken fibres reaches the free edges, generating the final failure of the specimen. Computation also shows that matrix cracking in the ply takes place before delamination, as is the Fig. 2. Position of the ply in different layups.

11 Fig. 3. Failure scenario for q-iso 2. Columns and 2 respectively: matrix cracking and fibre failure in ply. Columns 3 and 4 respectively: delamination at interfaces /45 and 9 / 45. case for impact behaviour of laminates, and thus drives the delamination propagation Failure scenario of quasi-isotropic laminate In this laminate, a ply is internal (see D, Fig 2) and its adjacent interfaces are identical to the configurations A and B ( 45 / / 45 ). Another ply is stacked at the external surface (see C, Fig. 2) with a single /45 interface. The DPM computation shows that the damage process in internal ply D is identical to that in plies A and B. The damage evolution of ply C and fibre failure of the inner ply, D, are shown in columns, 2 and 4 respectively of Fig. 4. The evolution of delaminations at the interface ( /45 ) of ply C is also given in column 3 of this figure. The outer ply splits with two matrix cracks initiating early at the hole edge and propagating in the direction of loading. Delamination follows the same geometry in a confined area before structural failure. At this stage, the outer ply fibre failure occurs later but more suddenly (many elements are destroyed at the same time) than that of the inner ply. Therefore, for ply D, as for plies A and B, there is a brutal first failure then gradual failure of the fibre. In addition, as for the Q-isotropic 2 laminate, structural failure is caused by the failure of a some of the ply fibres out of the net section. In contrast, the outer ply has two splits, which seem to delay local failure of fibres by locally reducing the effects of stress concentration near the hole and redirecting stress flow. So, for this second quasi-isotropic laminate, it is logical that the structural failure should occur at the same load as in the previous quasi-iso laminate. The drop in force is smaller for this second layup as net sections of the two outer plies are almost intact. When the load increases, the fibres of the D-type ply gradually break with an angle of 45. The final failure of the outer plies is more sudden but more delayed, which explains why, experimentally, the UTS of this layup is greater than the other quasi-isotropic layup (see Fig. 7). Regarding delaminated areas, it is noted that, for /45 interfaces located just below the outer, the shape follows the cracked area of the matrix (see Fig. 4). The calculation also shows that, for this laminate, matrix cracking occurs earlier than delamination. Other interfaces present smaller delaminated areas with shapes that are mainly similar to the matrix cracked areas of ±45 plies and identical to those observed on laminate q-iso Failure scenario of Oriented 2 laminate This configuration creates a new loading environment for plies (ply type E, Fig. 2). Two plies are superposed (.254 mm thick instead of.27 mm) and the interfaces are different: / 45 and /9. This new environment results in a new process of matrix cracking, where splitting is coupled with transverse propagation. However, unlike the situation for single ply C, the

12 Fig. 4. Failure scenario for q-iso. Columns and 2 respectively: matrix cracking and fibre failure in outer ply. Columns 3: delamination at interfaces /45 (outer ply). Colum 4: fibre failure of inner ply. splitting is much more developed, i.e. longer and narrower, before structural failure (Fig. 5, column ). Some fibres are broken in the vicinity of the hole edge but the damage does not propagate until structural failure occurs (Fig. 5, column 2). At structural failure, all types of damage (matrix cracking, delamination at the interfaces of plies, and fibre breakage, Fig. 5) increase suddenly. The net section is then reduced to about 5%, which causes a decrease in the load. As loading continues up to UTS, matrix cracking propagates to the free edges and fibre breakage occurs randomly. Once again, during the damage process, the shape of the delamination of the /9 interface exactly follows the cracked region of the plies. In column 4, the evolution of the delamination of the first interface near the outer surface is also shown. An X shape is observed with a very limited extent. This configuration is compatible with the fracture surface at 45 of the outer plies visible in Fig. 9(a) Failure scenario of Oriented laminate For this laminate, there is a new loading configuration for the plies (plies type F and G, Fig. 2). For plies F the thickness is even greater than previously (2.8, i.e..36 mm). Moreover, these plies are located just under the outer surface of the laminate and have 45 / / /45 interfaces (similarly to plies A, B and D). Ply G is located deeper in the laminate and its 45 / /9 interfaces are similar to those of ply E.

13 Fig. 5. Failure scenario for Oriented 2. Column and 2 respectively: matrix cracking and fibre failure in plies. Column 3: delamination at interfaces [ ] 2 /9. Column 4: delamination at outer interface 45 / 45. For both types of plies, the first damages are longitudinal splittings (Fig. 7, columns and 3). For the inner ply, G, splitting extends over a fairly short length, initially without fibre failure. When the load increases, matrix cracking propagates transversely, causing the failure of some elements of fibre on less than about % of the net section (Fig. 6, pre-failure). This failure is visible on a zoom of the stress strain curve provided by the model (Fig. 6). However, this damage is not sufficient to cause structural failure. When the load increases again, the transverse propagation of transverse cracking continues, accompanied by the gradual failure of the fibre of ply G. Then a stage of damage stabilization of this ply is reached. Nevertheless, the final failure is not caused directly by this ply. For ply F, there is crack propagation with thin splitting along the total length of the specimen (Fig. 7, column ). The presence of such splitting has the effect of strongly reducing the stresses on fibre elements near the hole. Thus, the integrity of these plies is kept when the load increases. At UTS, there is a very sudden break of

14 Inner ply [ ] Pre-failure Outer ply [ ]2 Global failure these outer plies (Fig. 6), causing first structural failure and ultimately the overall failure. The damage is not symmetrical in this case, probably because of numerical dynamic effects. However, this dispersion is consistent with the post-mortem pattern. The process of delamination of the 45 / 45 interface (Fig. 7, column 4) is also provided. The process involved here is very different from that observed on the Oriented 2 laminate, which was just below the outer surface of the laminate. Here, delamination is initiated at the hole edge but also at the free edges. 5. Conclusion Structural failure Fig. 6. Fibre failure at structural failure and global failure of Oriented layup. This paper presents the direct extension of the DPM approach to open hole tensile tests, without modification. The only adjustment was to refine the mesh near the hole. The capacity of the DPM was evaluated on an industrial benchmark of four very different laminates. Good agreement was found between the numerical and experimental results, with good prediction of ultimate Tensile stresses and failure patterns. The numerical model was used to make a refined analysis of the damage scenario for each laminate. Fig. 7. Failure scenario for Oriented. Columns and 2 respectively: matrix cracking and fibre failure in [ ] 2 outer plies. Column 3: matrix cracking for inner ply. Column 4: delamination at outer interface 45 / 45.

15 The importance of the position of plies in the thickness of the laminate was thus demonstrated. In particular, it was shown that the plies placed near or at the outer surface split more easily, so the stress concentration near the hole diminished and the final failure was delayed. Therefore, it can be said that the plies are protected inside the laminate. The model also showed that the general patterns of damage of 45 and 9 plies adjacent to plies were generally quite similar, with a difference only when the plies split, thus modifying local stress fields. We also found that matrix cracking in a ply always occurred slightly before delamination at adjacent interfaces. It is likely that local scenarios are identical to those identified in impact [8]. This also explains, a posteriori, why the approach gave good results: the model has good ability to address the inter- and intralaminar coupling. The robustness of the model should now be tested on a more comprehensive benchmark applying the same philosophy as Rivallant et al. []. The authors also suggest extending the validation of this approach to more complex phenomenology of failure, as in the case of offset failure in a filled hole in compression [28], and to composite structures under complex loading [29]. Acknowledgements The academic authors thank Airbus Operation S.A.S. for its support, especially Clément Chirol and Bernard Bourthoumieux. References [] Hallett SR, Green BG, Jiang W-G, Cheung KH, Wisnom MR. The open hole tensile test: a challenge for virtual testing of composite. Int J Fract 29;58:69 8. [2] MIL-HDBK-7. Military handbook, polymer matrix composites. US Department of Defense; 994. [3] Wisnom MR, Hallett SR. The role of delamination in strength, failure mechanism and hole size effect in open hole tensile tests on quasi-isotropic laminates. Compos Part A 29;4: [4] Hu Y-L, Yu Y, Wang H. Peridynamic analytical method for progressive damage in notched composite laminates. Compos. Struct. 24;8:8. [5] Madenci E, Oterkus E. Peridynamic theory and its applications. Springer; 23. [6] Abisset E, Daghia F, Ladevèze P. On the validation of a damage mesomodel for laminated composites by means of open-hole tensile tests on quasi-isotropic laminates. Compos Part A 2;42: [7] Van der Meer FP, Sluys LJ. Continuum models for the analysis of progressive failure in composite laminates. J Compos Mater 29;43: [8] Bouvet C, Castanié B, Bizeul M, Barrau J-J. Low velocity impact modelling in laminate composite panels with discrete interface elements. Int J Solids Struct 29;46(4 5): [9] Adam L, Bouvet C, Castanié B, Daidié A, Bonhomme E. Discrete ply model of circular pull-through test of fasteners in laminates. Compos Struct 22;94(): [] Hongkarnjanakul N, Bouvet C, Rivallant S. Validation of low velocity impact modelling on different stacking sequences of CFRP laminates and influence of fibre failure. Compos Struct 23;6: [] Rivallant S, Bouvet C, Hongkarnjanakul N. Failure analysis of CFRP laminates subjected to compression after impact: FE simulation using discrete interface elements. Compos Part A 23;55: [2] Bouvet C, Rivallant S, Barrau J-J. Low velocity impact modeling in composite laminates capturing permanent indentation. Compos Sci Technol 22;72(6): [3] Prabhakar P, Waas AM. A novel continuum-decohesive finite element for modeling in-plane fracture in fiber reinforced composites. Compos Sci Technol 23;83:. [4] Moës N, Belytschko T. Extended finite element method for cohesive crack growth. Eng Fract Mech 22;69(7): [5] Van der Meer FP, Sluys LJ, Hallett SR, Wisnom MR. Computational modeling of complex failure mechanisms in laminates. J Compos Mater 22;46(5): [6] Van der Meer FP, Sluys LJ. A phantom node formulation with mixed mode cohesive law for splitting in laminates. J Fract 29;58(2):7 24. [7] Van der Meer FP, Dávila CG. Cohesive modeling of transverse cracking in laminates under in-plane loading with a single layer of elements per ply. Int J Solids Struct 23;5: [8] Iarve EV. Mesh independent modeling of cracks by using higher order shape functions. Int J Numer Methods Eng 23;56(4): [9] Iarve EV, Gurvich MR, Mollenhauer DH, Rose CA, Davilà CG. Mesh independent matrix cracking and delamination modeling in laminated composites. Int J Numer Methods Eng 2;88(8): [2] Swinderman MJ, Iarve EV, Brockman RA, Mollenhauer DH, Hallet RH. Strength prediction in open hole composite laminates by using discrete damage modeling. AIAA J 23;5(4): [2] Hashin Z, Rotem A. A fatigue failure criterion for fiber-reinforced materials. J Compos Mater 973;7: [22] Pinho ST, Robinson P, Iannucci L. Fracture toughness of the tensile and compressive fibre failure modes in laminated composites. Compos Sci Technol 26;66: [23] Bazant ZP, Oh BH. Progressive crack and band theory for fracture of concrete. Mater Struct 983;6: [24] Lapczyk I, Hurtado JA. Progressive damage modelling in fiber-reinforced materials. Compos Part A 27;38: [25] Raimondo L, Iannucci L, Robinson P, Curtis PT. A progressive failure model for mesh-size-independent FE analysis of composite laminates subject to lowvelocity impact damage. Compos Sci Technol 22;72: [26] Shi Y, Swait T, Soutis C. Modelling damage evolution in composite laminates subjected to low velocity impact. Compos Struct 22;94(9): [27] Hexply Ò product data. < [28] Castanié B, Crézé S, Risse L, Barrau JJ, Lachaud F. Experimental analysis of failures in filled hole compression tests of carbon/epoxy laminate. Compos Struct 2;92(5):92 9. [29] Castanié B, Barrau J-J, Jaouen J-P, Rivallant S. Combined shear/compression structural testing of asymmetric sandwich structures. Exp Mech 24;44(5):

Tensile behaviour of anti-symmetric CFRP composite

Tensile behaviour of anti-symmetric CFRP composite Available online at www.sciencedirect.com Procedia Engineering 1 (211) 1865 187 ICM11 Tensile behaviour of anti-symmetric CFRP composite K. J. Wong a,b, *, X. J. Gong a, S. Aivazzadeh a, M. N. Tamin b

More information

INITIATION AND PROPAGATION OF FIBER FAILURE IN COMPOSITE LAMINATES

INITIATION AND PROPAGATION OF FIBER FAILURE IN COMPOSITE LAMINATES THE 19 TH INTERNATIONAL CONFERENCE ON COMPOSITE MATERIALS INITIATION AND PROPAGATION OF FIBER FAILURE IN COMPOSITE LAMINATES E. Iarve 1,2*, D. Mollenhauer 1, T. Breitzman 1, K. Hoos 2, M. Swindeman 2 1

More information

THE ROLE OF DELAMINATION IN NOTCHED AND UNNOTCHED TENSILE STRENGTH

THE ROLE OF DELAMINATION IN NOTCHED AND UNNOTCHED TENSILE STRENGTH THE ROLE OF DELAMINATION IN NOTCHED AND UNNOTCHED TENSILE STRENGTH M. R. Wisnom University of Bristol Advanced Composites Centre for Innovation and Science University Walk, Bristol BS8 1TR, UK M.Wisnom@bristol.ac.uk

More information

Open-hole compressive strength prediction of CFRP composite laminates

Open-hole compressive strength prediction of CFRP composite laminates Open-hole compressive strength prediction of CFRP composite laminates O. İnal 1, A. Ataş 2,* 1 Department of Mechanical Engineering, Balikesir University, Balikesir, 10145, Turkey, inal@balikesir.edu.tr

More information

Discrete ply model of circular pull-through test of fasteners in laminates

Discrete ply model of circular pull-through test of fasteners in laminates Discrete ply model of circular pull-through test of fasteners in laminates Louis Adam, Christophe Bouvet, Bruno Castanie, Alain Daidie, Elodie Bonhomme To cite this version: Louis Adam, Christophe Bouvet,

More information

This is a publisher-deposited version published in: Eprints ID: 4094

This is a publisher-deposited version published in:  Eprints ID: 4094 This is a publisher-deposited version published in: http://oatao.univ-toulouse.fr/ Eprints ID: 4094 To cite this document: WEISS Ambrosius, TRABELSI Walid, MICHEL Laurent, BARRAU Jean-Jacques, MAHDI Stéphane.

More information

REPRESENTING MATRIX CRACKS THROUGH DECOMPOSITION OF THE DEFORMATION GRADIENT TENSOR IN CONTINUUM DAMAGE MECHANICS METHODS

REPRESENTING MATRIX CRACKS THROUGH DECOMPOSITION OF THE DEFORMATION GRADIENT TENSOR IN CONTINUUM DAMAGE MECHANICS METHODS 20 th International Conference on Composite Materials Copenhagen, 19-24 th July 2015 REPRESENTING MATRIX CRACKS THROUGH DECOMPOSITION OF THE DEFORMATION GRADIENT TENSOR IN CONTINUUM DAMAGE MECHANICS METHODS

More information

Cure Monitoring and SHM of Carbon Fiber Reinforced Polymer Part I : Impedance Analysis and Multiphysic Sensitivity

Cure Monitoring and SHM of Carbon Fiber Reinforced Polymer Part I : Impedance Analysis and Multiphysic Sensitivity Cure Monitoring and SHM of Carbon Fiber Reinforced Polymer Part I : Impedance Analysis and Multiphysic Sensitivity Mahamadou Mounkaila, Thierry Camps, Sonia Sassi, Philippe Marguerès, Philippe Olivier,

More information

FLOATING NODE METHOD AND VIRTUAL CRACK CLOSURE TECHNIQUE FOR MODELING MATRIX CRACKING- DELAMINATION MIGRATION

FLOATING NODE METHOD AND VIRTUAL CRACK CLOSURE TECHNIQUE FOR MODELING MATRIX CRACKING- DELAMINATION MIGRATION THE 19 TH INTERNATIONAL CONFERENCE ON COMPOSITE MATERIALS FLOATING NODE METHOD AND VIRTUAL CRACK CLOSURE TECHNIQUE FOR MODELING MATRIX CRACKING- DELAMINATION MIGRATION N. V. De Carvalho 1*, B. Y. Chen

More information

Strength of GRP-laminates with multiple fragment damages

Strength of GRP-laminates with multiple fragment damages Strength of GRP-laminates with multiple fragment damages S. Kazemahvazi, J. Kiele, D. Zenkert Kungliga Tekniska Högskolan, KTH 100 44 Stockholm, Sweden sohrabk@kth.se SUMMARY The strength of glass fibre

More information

ADVANCES IN THE PROGRESSIVE DAMAGE ANALYSIS OF COMPOSITES

ADVANCES IN THE PROGRESSIVE DAMAGE ANALYSIS OF COMPOSITES NAFEMS WORLD CONGRESS 13, SALZBURG, AUSTRIA ADVANCES IN THE PROGRESSIVE DAMAGE ANALYSIS OF M. Bruyneel, J.P. Delsemme, P. Jetteur (LMS Samtech, Belgium); A.C. Goupil (ISMANS, France). Dr. Ir. M. Bruyneel,

More information

University of Bristol - Explore Bristol Research. Early version, also known as pre-print

University of Bristol - Explore Bristol Research. Early version, also known as pre-print Hallett, S. R., & Wisnom, M. R. (2006). Numerical investigation of progressive damage and the effect of layup in notched tensile tests. Journal of Composite Materials, 40 (14), 1229-1245. DOI: 10.1177/0021998305057432

More information

DYNAMIC DELAMINATION OF AERONAUTIC STRUCTURAL COMPOSITES BY USING COHESIVE FINITE ELEMENTS

DYNAMIC DELAMINATION OF AERONAUTIC STRUCTURAL COMPOSITES BY USING COHESIVE FINITE ELEMENTS DYNAMIC DELAMINATION OF AERONAUTIC STRUCTURAL COMPOSITES BY USING COHESIVE FINITE ELEMENTS M. Ilyas, F. Lachaud 1, Ch. Espinosa and M. Salaün Université de Toulouse, ISAE/DMSM, 1 avenue Edouard Belin,

More information

DAMAGE SIMULATION OF CFRP LAMINATES UNDER HIGH VELOCITY PROJECTILE IMPACT

DAMAGE SIMULATION OF CFRP LAMINATES UNDER HIGH VELOCITY PROJECTILE IMPACT 18 TH INTERNATIONAL CONFERENCE ON COMPOSITE MATERIALS DAMAGE SIMULATION OF CFRP LAMINATES UNDER HIGH VELOCITY PROJECTILE IMPACT A. Yoshimura 1*, T. Okabe, M. Yamada 3, T. Ogasawara 1, Y. Tanabe 3 1 Advanced

More information

PREDICTION OF OUT-OF-PLANE FAILURE MODES IN CFRP

PREDICTION OF OUT-OF-PLANE FAILURE MODES IN CFRP PREDICTION OF OUT-OF-PLANE FAILURE MODES IN CFRP R. R. Pinto 1, P. P. Camanho 2 1 INEGI - Instituto de Engenharia Mecanica e Gestao Industrial, Rua Dr. Roberto Frias, 4200-465, Porto, Portugal 2 DEMec,

More information

Prediction of failure in notched CFRP laminates under multi-axial loading. J L Y Tan, V S Deshpande and N A Fleck*,

Prediction of failure in notched CFRP laminates under multi-axial loading. J L Y Tan, V S Deshpande and N A Fleck*, Prediction of failure in notched CFRP laminates under multi-axial loading J L Y Tan, V S Deshpande and N A Fleck*, Cambridge University Engineering Dept., Trumpington St., Cambridge, CB2 1PZ, UK * Corresponding

More information

Nonlocal computational methods applied to composites structures

Nonlocal computational methods applied to composites structures Nonlocal computational methods applied to composites structures Norbert Germain, Frédéric Feyel, Jacques Besson To cite this version: Norbert Germain, Frédéric Feyel, Jacques Besson. Nonlocal computational

More information

A 3D Discrete Damage Modeling Methodology for Abaqus for Fatigue Damage Evaluation in Bolted Composite Joints

A 3D Discrete Damage Modeling Methodology for Abaqus for Fatigue Damage Evaluation in Bolted Composite Joints A 3D Discrete Damage Modeling Methodology for Abaqus for Fatigue Damage Evaluation in Bolted Composite Joints Eugene Fang 1, Ling Liu 1, Michael Stuebner 1, Jim Lua 1 1 Global Engineering and Materials,

More information

NUMERICAL INVESTIGATION OF DELAMINATION IN L-SHAPED CROSS-PLY COMPOSITE BRACKET

NUMERICAL INVESTIGATION OF DELAMINATION IN L-SHAPED CROSS-PLY COMPOSITE BRACKET NUMERICAL INVESTIGATION OF DELAMINATION IN L-SHAPED CROSS-PLY COMPOSITE BRACKET M.Gümüş a*, B.Gözlüklü a, D.Çöker a a Department of Aerospace Eng., METU, Ankara, Turkey *mert.gumus@metu.edu.tr Keywords:

More information

Impact and Crash Modeling of Composite Structures: A Challenge for Damage Mechanics

Impact and Crash Modeling of Composite Structures: A Challenge for Damage Mechanics Impact and Crash Modeling of Composite Structures: A Challenge for Damage Mechanics Dr. A. Johnson DLR Dr. A. K. Pickett ESI GmbH EURO-PAM 99 Impact and Crash Modelling of Composite Structures: A Challenge

More information

IMPACT ON LAMINATED COMPOSITE PLATES: COMPARISON OF TEST AND SIMULATION RESULTS OBTAINED WITH LMS SAMTECH SAMCEF

IMPACT ON LAMINATED COMPOSITE PLATES: COMPARISON OF TEST AND SIMULATION RESULTS OBTAINED WITH LMS SAMTECH SAMCEF V ECCOMAS Thematic Conference on the Mechanical Response of Composites COMPOSITES 015 S.R. Hallett and J.J.C. Remmers (Editors) IMPACT ON LAMINATED COMPOSITE PLATES: COMPARISON OF TEST AND SIMULATION RESULTS

More information

This is an author-deposited version published in: Eprints ID: 12129

This is an author-deposited version published in:   Eprints ID: 12129 Open Archive Toulouse Archive Ouverte (OATAO) OATAO is an open access repository that collects the work of Toulouse researchers and makes it freely available over the web where possible. This is an author-deposited

More information

A RESEARCH ON NONLINEAR STABILITY AND FAILURE OF THIN- WALLED COMPOSITE COLUMNS WITH OPEN CROSS-SECTION

A RESEARCH ON NONLINEAR STABILITY AND FAILURE OF THIN- WALLED COMPOSITE COLUMNS WITH OPEN CROSS-SECTION A RESEARCH ON NONLINEAR STABILITY AND FAILURE OF THIN- WALLED COMPOSITE COLUMNS WITH OPEN CROSS-SECTION H. Debski a*, J. Bienias b, P. Jakubczak b a Faculty of Mechanical Engineering, Department of Machine

More information

Simulation of Dynamic Delamination and Mode I Energy Dissipation

Simulation of Dynamic Delamination and Mode I Energy Dissipation Simulation of Dynamic Delamination and Mode I Energy Dissipation Muhammad Ilyas, Christine Espinosa 1, Frédéric Lachaud and Michel Salaün Université de Toulouse ISAE, DMSM, 1 Avenue Edouard Belin, 3154

More information

EXPERIMENTAL AND NUMERICAL STUDY OF OBLIQUE IMPACT ON HELICOPTER BLADES INFLUENCE OF THE CURVATURE

EXPERIMENTAL AND NUMERICAL STUDY OF OBLIQUE IMPACT ON HELICOPTER BLADES INFLUENCE OF THE CURVATURE EXPERIMENTAL AND NUMERICAL STUDY OF OBLIQUE IMPACT ON HELICOPTER BLADES INFLUENCE OF THE CURVATURE F. Pascal a, P. Navarro a*, S. Marguet a, J.F. Ferrero a, J. Aubry b, S. Lemaire b a Université de Toulouse,

More information

Numerical simulation of delamination onset and growth in laminated composites

Numerical simulation of delamination onset and growth in laminated composites Numerical simulation of delamination onset and growth in laminated composites G. Wimmer, C. Schuecker, H.E. Pettermann Austrian Aeronautics Research (AAR) / Network for Materials and Engineering at the

More information

This is an author-deposited version published in: Eprints ID: 2797

This is an author-deposited version published in:   Eprints ID: 2797 Open Archive Toulouse Archive Ouverte (OATAO) OATAO is an open access repository that collects the work of Toulouse researchers and makes it freely available over the web where possible. This is an author-deposited

More information

BIAXIAL STRENGTH INVESTIGATION OF CFRP COMPOSITE LAMINATES BY USING CRUCIFORM SPECIMENS

BIAXIAL STRENGTH INVESTIGATION OF CFRP COMPOSITE LAMINATES BY USING CRUCIFORM SPECIMENS BIAXIAL STRENGTH INVESTIGATION OF CFRP COMPOSITE LAMINATES BY USING CRUCIFORM SPECIMENS H. Kumazawa and T. Takatoya Airframes and Structures Group, Japan Aerospace Exploration Agency 6-13-1, Ohsawa, Mitaka,

More information

Basic concepts and models in continuum damage mechanics

Basic concepts and models in continuum damage mechanics Basic concepts and models in continuum damage mechanics Djimedo Kondo, Hélène Welemane, Fabrice Cormery To cite this version: Djimedo Kondo, Hélène Welemane, Fabrice Cormery. Basic concepts and models

More information

COMPARISON OF COHESIVE ZONE MODELS USED TO PREDICT DELAMINATION INITIATED FROM FREE-EDGES : VALIDATION AGAINST EXPERIMENTAL RESULTS

COMPARISON OF COHESIVE ZONE MODELS USED TO PREDICT DELAMINATION INITIATED FROM FREE-EDGES : VALIDATION AGAINST EXPERIMENTAL RESULTS COMPARISON OF COHESIVE ZONE MODELS USED TO PREDICT DELAMINATION INITIATED FROM FREE-EDGES : VALIDATION AGAINST EXPERIMENTAL RESULTS A. Uguen 1, L. Zubillaga 2, A. Turon 3, N. Carrère 1 1 Laboratoire Brestois

More information

PLY LEVEL UNCERTAINTY EFFECTS ON FAILURE OF COMPOSITE

PLY LEVEL UNCERTAINTY EFFECTS ON FAILURE OF COMPOSITE 7th European Workshop on Structural Health Monitoring July 8-11, 2014. La Cité, Nantes, France More Info at Open Access Database www.ndt.net/?id=17206 PLY LEVEL UNCERTAINTY EFFECTS ON FAILURE OF COMPOSITE

More information

Multi Disciplinary Delamination Studies In Frp Composites Using 3d Finite Element Analysis Mohan Rentala

Multi Disciplinary Delamination Studies In Frp Composites Using 3d Finite Element Analysis Mohan Rentala Multi Disciplinary Delamination Studies In Frp Composites Using 3d Finite Element Analysis Mohan Rentala Abstract: FRP laminated composites have been extensively used in Aerospace and allied industries

More information

NUMERICAL MODELLING OF COMPOSITE PIN- JOINTS AND EXPERIMENTAL VALIDATION

NUMERICAL MODELLING OF COMPOSITE PIN- JOINTS AND EXPERIMENTAL VALIDATION NUMERICAL MODELLING OF COMPOSITE PIN- JOINTS AND EXPERIMENTAL VALIDATION Fabrice PIERRON*, François CERISIER*, and Michel GRÉDIAC** * SMS/ Département Mécanique et Matériaux, École Nationale Supérieure

More information

Detection and Survey of Interface Defects Within a Pavement Structure with Ultrasonic Pulse Echo

Detection and Survey of Interface Defects Within a Pavement Structure with Ultrasonic Pulse Echo Detection and Survey of Interface Defects Within a Pavement Structure with Ultrasonic Pulse Echo Jean Michel Simonin, Géraldine Villain To cite this version: Jean Michel Simonin, Géraldine Villain. Detection

More information

Finite element modelling of infinitely wide Angle-ply FRP. laminates

Finite element modelling of infinitely wide Angle-ply FRP. laminates www.ijaser.com 2012 by the authors Licensee IJASER- Under Creative Commons License 3.0 editorial@ijaser.com Research article ISSN 2277 9442 Finite element modelling of infinitely wide Angle-ply FRP laminates

More information

ISSN: ISO 9001:2008 Certified International Journal of Engineering Science and Innovative Technology (IJESIT) Volume 2, Issue 4, July 2013

ISSN: ISO 9001:2008 Certified International Journal of Engineering Science and Innovative Technology (IJESIT) Volume 2, Issue 4, July 2013 Delamination Studies in Fibre-Reinforced Polymer Composites K.Kantha Rao, Dr P. Shailesh, K. Vijay Kumar 1 Associate Professor, Narasimha Reddy Engineering College Hyderabad. 2 Professor, St. Peter s Engineering

More information

INTERNATIONAL JOURNAL OF APPLIED ENGINEERING RESEARCH, DINDIGUL Volume 2, No 1, 2011

INTERNATIONAL JOURNAL OF APPLIED ENGINEERING RESEARCH, DINDIGUL Volume 2, No 1, 2011 Interlaminar failure analysis of FRP cross ply laminate with elliptical cutout Venkateswara Rao.S 1, Sd. Abdul Kalam 1, Srilakshmi.S 1, Bala Krishna Murthy.V 2 1 Mechanical Engineering Department, P. V.

More information

Introduction to Engineering Materials ENGR2000. Dr. Coates

Introduction to Engineering Materials ENGR2000. Dr. Coates Introduction to Engineering Materials ENGR2 Chapter 6: Mechanical Properties of Metals Dr. Coates 6.2 Concepts of Stress and Strain tension compression shear torsion Tension Tests The specimen is deformed

More information

Prediction of impact-induced delamination in cross-ply composite laminates using cohesive interface elements

Prediction of impact-induced delamination in cross-ply composite laminates using cohesive interface elements Prediction of impact-induced delamination in cross-ply composite laminates using cohesive interface elements F. Aymerich, F. Dore, P. Priolo To cite this version: F. Aymerich, F. Dore, P. Priolo. Prediction

More information

Keywords: CFRP, compressive failure, kink-band, cohesive zone model. * Corresponding author

Keywords: CFRP, compressive failure, kink-band, cohesive zone model. * Corresponding author THE 19 TH INTERNATIONAL CONFERENCE ON COMPOSITE MATERIALS AN EXPERIMENTAL METHOD TO DETERMINE THE CRITICAL ENERGY RELEASE RATE ASSOCIATED WITH LONGITUDINAL COMPRESSIVE FAILURE IN CFRP D. Svensson 1 *,

More information

SKIN-STRINGER DEBONDING AND DELAMINATION ANALYSIS IN COMPOSITE STIFFENED SHELLS

SKIN-STRINGER DEBONDING AND DELAMINATION ANALYSIS IN COMPOSITE STIFFENED SHELLS SKIN-STRINER DEBONDIN AND DELAMINATION ANALYSIS IN COMPOSITE STIFFENED SHELLS R. Rikards, K. Kalnins & O. Ozolinsh Institute of Materials and Structures, Riga Technical University, Riga 1658, Latvia ABSTRACT

More information

Prediction of Delamination Growth Behavior in a Carbon Fiber Composite Laminate Subjected to Constant Amplitude Compression-Compression Fatigue Loads

Prediction of Delamination Growth Behavior in a Carbon Fiber Composite Laminate Subjected to Constant Amplitude Compression-Compression Fatigue Loads Prediction of Delamination Growth Behavior in a Carbon Fiber Composite Laminate Subjected to Constant Amplitude Compression-Compression Fatigue Loads J. Raju 1*, D.S. Sreedhar 2, & C.M. Manjunatha 1 1

More information

Non-conventional Glass fiber NCF composites with thermoset and thermoplastic matrices. F Talence, France Le Cheylard, France

Non-conventional Glass fiber NCF composites with thermoset and thermoplastic matrices. F Talence, France Le Cheylard, France 20 th International Conference on Composite Materials Copenhagen, 19-24th July 2015 Non-conventional Glass fiber NCF composites with thermoset and thermoplastic matrices. Thierry Lorriot 1, Jalal El Yagoubi

More information

Discrete Element Modelling of a Reinforced Concrete Structure

Discrete Element Modelling of a Reinforced Concrete Structure Discrete Element Modelling of a Reinforced Concrete Structure S. Hentz, L. Daudeville, F.-V. Donzé Laboratoire Sols, Solides, Structures, Domaine Universitaire, BP 38041 Grenoble Cedex 9 France sebastian.hentz@inpg.fr

More information

This work is licensed under a Creative Commons Attribution-NonCommercial-NoDerivatives 4.0 International licence

This work is licensed under a Creative Commons Attribution-NonCommercial-NoDerivatives 4.0 International licence Girão-Coelho AM. Finite element guidelines for simulation of delamination dominated failures in composite materials validated by case studies. Archives of Computational Methods in Engineering 2016, 1-26.

More information

PERFORMANCE OF COMPOSITE PANELS SUBJECTED TO UNDERWATER IMPULSIVE LOADING

PERFORMANCE OF COMPOSITE PANELS SUBJECTED TO UNDERWATER IMPULSIVE LOADING PERFORMANCE OF COMPOSITE PANELS SUBJECTED TO UNDERWATER IMPULSIVE LOADING F. Latourte, D. Grégoire, R. Bellur-Ramaswamy, H.D. Espinosa* Northwestern University, 2145 Sheridan Road, Evanston IL 60202 (*)

More information

NORMAL STRESS. The simplest form of stress is normal stress/direct stress, which is the stress perpendicular to the surface on which it acts.

NORMAL STRESS. The simplest form of stress is normal stress/direct stress, which is the stress perpendicular to the surface on which it acts. NORMAL STRESS The simplest form of stress is normal stress/direct stress, which is the stress perpendicular to the surface on which it acts. σ = force/area = P/A where σ = the normal stress P = the centric

More information

FASTENER PULL-THROUGH FAILURE IN GFRP LAMINATES

FASTENER PULL-THROUGH FAILURE IN GFRP LAMINATES 18 TH INTERNATIONAL CONFERENCE ON COMPOSITE MATERIALS FASTENER PULL-THROUGH FAILURE IN GFRP LAMINATES G. Catalanotti 1*, P.P. Camanho 1, P. Ghys 2, A.T. Marques 1 1 DEMec, Faculdade de Engenharia, Universidade

More information

MODELING DYNAMIC FRACTURE AND DAMAGE IN A FIBER-REINFORCED COMPOSITE LAMINA WITH PERIDYNAMICS

MODELING DYNAMIC FRACTURE AND DAMAGE IN A FIBER-REINFORCED COMPOSITE LAMINA WITH PERIDYNAMICS University of Nebraska - Lincoln DigitalCommons@University of Nebraska - Lincoln Mechanical & Materials Engineering Faculty Publications Mechanical & Materials Engineering, Department of 011 MODELING DYNAMIC

More information

Computational Analysis for Composites

Computational Analysis for Composites Computational Analysis for Composites Professor Johann Sienz and Dr. Tony Murmu Swansea University July, 011 The topics covered include: OUTLINE Overview of composites and their applications Micromechanics

More information

Fracture Behaviour of FRP Cross-Ply Laminate With Embedded Delamination Subjected To Transverse Load

Fracture Behaviour of FRP Cross-Ply Laminate With Embedded Delamination Subjected To Transverse Load Fracture Behaviour of FRP Cross-Ply Laminate With Embedded Delamination Subjected To Transverse Load Sriram Chintapalli 1, S.Srilakshmi 1 1 Dept. of Mech. Engg., P. V. P. Siddhartha Institute of Technology.

More information

MODELING OF THE BEHAVIOR OF WOVEN LAMINATED COMPOSITES UNTIL RUPTURE

MODELING OF THE BEHAVIOR OF WOVEN LAMINATED COMPOSITES UNTIL RUPTURE MODELING OF THE BEHAVIOR OF WOVEN LAMINATED COMPOSITES UNTIL RUPTURE Jean Paul Charles, Christian Hochard,3, Pierre Antoine Aubourg,3 Eurocopter, 375 Marignane cedex, France Unimeca, 6 rue J. Curie, 3453

More information

Failure Analysis of Unidirectional Composite Pinned- Joints

Failure Analysis of Unidirectional Composite Pinned- Joints 217 IJEDR Volume, Issue 4 ISSN: 2321-9939 Failure Analysis of Unidirectional Composite Pinned- Joints 1 Sai Ashok.M, 2 Mr. U. Koteswara Rao 1 M-tech Machine Design, 2 Associate Professor & Asst. COE 1

More information

On measurement of mechanical properties of sound absorbing materials

On measurement of mechanical properties of sound absorbing materials On measurement of mechanical properties of sound absorbing materials Nicolas Dauchez, Manuel Etchessahar, Sohbi Sahraoui To cite this version: Nicolas Dauchez, Manuel Etchessahar, Sohbi Sahraoui. On measurement

More information

Implementation of fatigue model for unidirectional laminate based on finite element analysis: theory and practice

Implementation of fatigue model for unidirectional laminate based on finite element analysis: theory and practice Focussed on Multiaxial Fatigue and Fracture Implementation of fatigue model for unidirectional laminate based on finite element analysis: theory and practice D. Carrella-Payan, B. Magneville, M. Hack,

More information

Abstract. 1 Introduction

Abstract. 1 Introduction Contact analysis for the modelling of anchors in concrete structures H. Walter*, L. Baillet** & M. Brunet* *Laboratoire de Mecanique des Solides **Laboratoire de Mecanique des Contacts-CNRS UMR 5514 Institut

More information

THE MUTUAL EFFECTS OF SHEAR AND TRANSVERSE DAMAGE IN POLYMERIC COMPOSITES

THE MUTUAL EFFECTS OF SHEAR AND TRANSVERSE DAMAGE IN POLYMERIC COMPOSITES THE 19 TH INTERNATIONAL CONFERENCE ON COMPOSITE MATERIALS THE MUTUAL EFFECTS OF SHEAR AND TRANSVERSE DAMAGE IN POLYMERIC COMPOSITES L.V. Smith 1 *, M. Salavatian 1 1 School of Mechanical and Materials

More information

BEARING STRENGTH ASSESSMENT OF COMPOSITE MATERIAL THROUGH NUMERICAL MODELS

BEARING STRENGTH ASSESSMENT OF COMPOSITE MATERIAL THROUGH NUMERICAL MODELS BEARING STRENGTH ASSESSMENT OF COMPOSITE MATERIAL THROUGH NUMERICAL MODELS Euler S. Dias*, Carlos A. Cimini Jr.* * Federal University of Minas Gerais, Dept. of Structural Engineering, Belo Horizonte -

More information

Numerical Analysis of Composite Panels in the Post-Buckling Field taking into account Progressive Failure

Numerical Analysis of Composite Panels in the Post-Buckling Field taking into account Progressive Failure Copyright c 007 ICCES ICCES, vol.1, no.3, pp.93-98, 007 Numerical Analysis of Composite Panels in the Post-Buckling Field taking into account Progressive Failure C. Bisagni 1 Summary The research here

More information

Prediction of Elastic Constants on 3D Four-directional Braided

Prediction of Elastic Constants on 3D Four-directional Braided Prediction of Elastic Constants on 3D Four-directional Braided Composites Prediction of Elastic Constants on 3D Four-directional Braided Composites Liang Dao Zhou 1,2,* and Zhuo Zhuang 1 1 School of Aerospace,

More information

Failure analysis of serial pinned joints in composite materials

Failure analysis of serial pinned joints in composite materials Indian Journal of Engineering & Materials Sciences Vol. 18, April 2011, pp. 102-110 Failure analysis of serial pinned joints in composite materials Alaattin Aktaş* Department of Mechanical Engineering,

More information

NUMERICAL AND EXPERIMENTAL ANALYSES OF MULTIPLE DELAMINATIONS IN CURVED COMPOSITE LAMINATES

NUMERICAL AND EXPERIMENTAL ANALYSES OF MULTIPLE DELAMINATIONS IN CURVED COMPOSITE LAMINATES THE 19 TH INTERNATIONAL CONFERENCE ON COMPOSITE MATERIALS NUMERICAL AND EXPERIMENTAL ANALYSES OF MULTIPLE DELAMINATIONS IN CURVED COMPOSITE LAMINATES A. Baldi 1 *, A. Airoldi 1, P. Belotti 1, P. Bettini

More information

PROGRESSIVE DAMAGE ANALYSES OF SKIN/STRINGER DEBONDING. C. G. Dávila, P. P. Camanho, and M. F. de Moura

PROGRESSIVE DAMAGE ANALYSES OF SKIN/STRINGER DEBONDING. C. G. Dávila, P. P. Camanho, and M. F. de Moura PROGRESSIVE DAMAGE ANALYSES OF SKIN/STRINGER DEBONDING C. G. Dávila, P. P. Camanho, and M. F. de Moura Abstract The debonding of skin/stringer constructions is analyzed using a step-by-step simulation

More information

Advanced modelling for design helping of heterogeneous CLT panels in bending

Advanced modelling for design helping of heterogeneous CLT panels in bending Advanced modelling for design helping of heterogeneous CLT panels in bending Lorenzo Franzoni, Arthur Lebée, Gilles Forêt, Florent Lyon To cite this version: Lorenzo Franzoni, Arthur Lebée, Gilles Forêt,

More information

An investigation of the mechanical behaviour of carbon epoxy cross ply cruciform specimens under biaxial loading

An investigation of the mechanical behaviour of carbon epoxy cross ply cruciform specimens under biaxial loading An investigation of the mechanical behaviour of carbon epoxy cross ply cruciform specimens under biaxial loading A. Makris, C. Ramault, D. Van Hemelrijck Department of Mechanics of Materials and Constructions,

More information

Modelling the nonlinear shear stress-strain response of glass fibrereinforced composites. Part II: Model development and finite element simulations

Modelling the nonlinear shear stress-strain response of glass fibrereinforced composites. Part II: Model development and finite element simulations Modelling the nonlinear shear stress-strain response of glass fibrereinforced composites. Part II: Model development and finite element simulations W. Van Paepegem *, I. De Baere and J. Degrieck Ghent

More information

Finite Element Analysis of FRP Debonding Failure at the Tip of Flexural/Shear Crack in Concrete Beam

Finite Element Analysis of FRP Debonding Failure at the Tip of Flexural/Shear Crack in Concrete Beam Marquette University e-publications@marquette Civil and Environmental Engineering Faculty Research and Publications Civil and Environmental Engineering, Department of 12-1-2013 Finite Element Analysis

More information

FRACTURE TOUGHNESS OF ADHESIVE BONDED COMPOSITE JOINTS UNDER MIXED MODE LOADING.

FRACTURE TOUGHNESS OF ADHESIVE BONDED COMPOSITE JOINTS UNDER MIXED MODE LOADING. FRACTURE TOUGHNESS OF ADHESIVE BONDED COMPOSITE JOINTS UNDER MIXED MODE LOADING. X. J. Gong, F. Hernandez, G. Verchery. ISAT - Institut Supérieur de l Automobile et des Transports, LRMA - Laboratoire de

More information

Inductive thermography nondestructive testing applied to carbon composite materials: multiphysics and multiscale modeling

Inductive thermography nondestructive testing applied to carbon composite materials: multiphysics and multiscale modeling Inductive thermography nondestructive testing applied to carbon composite materials: multiphysics and multiscale modeling H.K. Bui, G Berthiau, D Trichet, G Wasselynck To cite this version: H.K. Bui, G

More information

Passive Damping Characteristics of Carbon Epoxy Composite Plates

Passive Damping Characteristics of Carbon Epoxy Composite Plates Journal of Materials Science and Engineering A 6 (-) 35-4 doi:.765/6-63/6.-.5 D DAVID PUBLISHING Passive Damping Characteristics of Carbon Epoxy Composite Plates Dileep Kumar K * and V V Subba Rao Faculty

More information

SDM 2013 Student Papers Competition Modeling fiber-matrix splitting failure through a mesh-objective continuum-decohesive finite element method

SDM 2013 Student Papers Competition Modeling fiber-matrix splitting failure through a mesh-objective continuum-decohesive finite element method Structures, Structural Dynamics, and Materials and Co-located Conferences April 8-11, 2013, Boston, Massachusetts 54th AIAA/ASME/ASCE/AHS/ASC Structures, Structural Dynamics, and Materials Conference AIAA

More information

Numerical Analysis of Delamination Behavior in Laminated Composite with Double Delaminations Embedded in Different Depth Positions

Numerical Analysis of Delamination Behavior in Laminated Composite with Double Delaminations Embedded in Different Depth Positions Numerical Analysis of Delamination Behavior in Laminated Composite with Double Delaminations Embedded in Different Depth Positions Numerical Analysis of Delamination Behavior in Laminated Composite with

More information

IMPROVEMENTS OF THE VARIABLE THERMAL RESISTANCE

IMPROVEMENTS OF THE VARIABLE THERMAL RESISTANCE IMPROVEMENTS OF THE VARIABLE THERMAL RESISTANCE V. Szekely, S. Torok, E. Kollar To cite this version: V. Szekely, S. Torok, E. Kollar. IMPROVEMENTS OF THE VARIABLE THERMAL RESIS- TANCE. THERMINIC 2007,

More information

Antipodal radiation pattern of a patch antenna combined with superstrate using transformation electromagnetics

Antipodal radiation pattern of a patch antenna combined with superstrate using transformation electromagnetics Antipodal radiation pattern of a patch antenna combined with superstrate using transformation electromagnetics Mark Clemente Arenas, Anne-Claire Lepage, Xavier Begaud To cite this version: Mark Clemente

More information

A MULTISCALE DAMAGE MODEL FOR THE ANALYSIS OF LAMINATED COMPOSITE STRUCTURES ON THE MICROSCALE

A MULTISCALE DAMAGE MODEL FOR THE ANALYSIS OF LAMINATED COMPOSITE STRUCTURES ON THE MICROSCALE A MULTISCALE DAMAGE MODEL FOR THE ANALYSIS OF LAMINATED COMPOSITE STRUCTURES ON THE MICROSCALE P. Ladevèze 1,2, M. Trovalet 1, G. Lubineau 1 1 LMT-Cachan (ENS Cachan/CNRS/UPMC/Pres Universud Paris) 61

More information

Composite Damage Material Modeling for Crash Simulation: MAT54 & the Efforts of the CMH-17 Numerical Round Robin

Composite Damage Material Modeling for Crash Simulation: MAT54 & the Efforts of the CMH-17 Numerical Round Robin Composite Damage Material Modeling for Crash Simulation: MAT54 & the Efforts of the CMH-17 Numerical Round Robin 2014 Technical Review Bonnie Wade (UW) Prof. Paolo Feraboli AMTAS (JAMS) Crashworthiness

More information

KINK BAND FORMATION OF FIBER REINFORCED POLYMER (FRP)

KINK BAND FORMATION OF FIBER REINFORCED POLYMER (FRP) KINK BAND FORMATION OF FIBER REINFORCED POLYMER (FRP) 1 University of Science & Technology Beijing, China, niukm@ustb.edu.cn 2 Tsinghua University, Department of Engineering Mechanics, Beijing, China,

More information

Modeling Hailstone Impact onto Composite Material Panel Under a Multi-axial State of Stress

Modeling Hailstone Impact onto Composite Material Panel Under a Multi-axial State of Stress Modeling Hailstone Impact onto Composite Material Panel Under a Multi-axial State of Stress Authors Marco ANGHILERI * Luigi-M L CASTELLETTI * Andrea MILANESE * and Andrea SEMBOLONI * Affiliation * Politecnico

More information

A micromechanical approach to describe internal erosion effects in soils

A micromechanical approach to describe internal erosion effects in soils A micromechanical approach to describe internal erosion effects in soils Luc Scholtès, Pierre-Yves Hicher, Luc Sibille To cite this version: Luc Scholtès, Pierre-Yves Hicher, Luc Sibille. A micromechanical

More information

Discrete Modeling of the Crushing of Nomex Honeycomb Core and Application to Impact and Post-impact Behavior of Sandwich Structures

Discrete Modeling of the Crushing of Nomex Honeycomb Core and Application to Impact and Post-impact Behavior of Sandwich Structures Discrete Modeling of the Crushing of Nomex Honeycomb Core and Application to Impact and Post-impact Behavior of Sandwich Structures Bruno Castanié, Yulfian Aminanda, Jean-Jacques Barrau, Pascal Thevenet

More information

Modeling of Interfacial Debonding Induced by IC Crack for Concrete Beam-bonded with CFRP

Modeling of Interfacial Debonding Induced by IC Crack for Concrete Beam-bonded with CFRP Proceedings of the World Congress on Engineering 21 Vol II WCE 21, June 2 - July 1, 21, London, U.K. Modeling of Interfacial Debonding Induced by IC Crack for Concrete Beam-bonded with CFRP Lihua Huang,

More information

Approximation SEM-DG pour les problèmes d ondes elasto-acoustiques

Approximation SEM-DG pour les problèmes d ondes elasto-acoustiques Approximation SEM-DG pour les problèmes d ondes elasto-acoustiques Helene Barucq, Henri Calandra, Aurélien Citrain, Julien Diaz, Christian Gout To cite this version: Helene Barucq, Henri Calandra, Aurélien

More information

RELIABILITY ANALYSIS IN BOLTED COMPOSITE JOINTS WITH SHIMMING MATERIAL

RELIABILITY ANALYSIS IN BOLTED COMPOSITE JOINTS WITH SHIMMING MATERIAL 25 TH INTERNATIONAL CONGRESS OF THE AERONAUTICAL SCIENCES RELIABILITY ANALYSIS IN BOLTED COMPOSITE JOINTS WITH SHIMMING MATERIAL P. Caracciolo, G. Kuhlmann AIRBUS-Germany e-mail: paola.caracciolo@airbus.com

More information

MODal ENergy Analysis

MODal ENergy Analysis MODal ENergy Analysis Nicolas Totaro, Jean-Louis Guyader To cite this version: Nicolas Totaro, Jean-Louis Guyader. MODal ENergy Analysis. RASD, Jul 2013, Pise, Italy. 2013. HAL Id: hal-00841467

More information

Characterization of the local Electrical Properties of Electrical Machine Parts with non-trivial Geometry

Characterization of the local Electrical Properties of Electrical Machine Parts with non-trivial Geometry Characterization of the local Electrical Properties of Electrical Machine Parts with non-trivial Geometry Laure Arbenz, Abdelkader Benabou, Stéphane Clenet, Jean Claude Mipo, Pierre Faverolle To cite this

More information

Numerical modeling of diffusion within composite media

Numerical modeling of diffusion within composite media Numerical modeling of diffusion within composite media Miljan Milosevic To cite this version: Miljan Milosevic. Numerical modeling of diffusion within composite media. 2nd ECCOMAS Young Investigators Conference

More information

RHEOLOGICAL INTERPRETATION OF RAYLEIGH DAMPING

RHEOLOGICAL INTERPRETATION OF RAYLEIGH DAMPING RHEOLOGICAL INTERPRETATION OF RAYLEIGH DAMPING Jean-François Semblat To cite this version: Jean-François Semblat. RHEOLOGICAL INTERPRETATION OF RAYLEIGH DAMPING. Journal of Sound and Vibration, Elsevier,

More information

Numerical Simulation of the Mode I Fracture of Angle-ply Composites Using the Exponential Cohesive Zone Model

Numerical Simulation of the Mode I Fracture of Angle-ply Composites Using the Exponential Cohesive Zone Model Numerical Simulation of the Mode I Fracture of Angle-ply Composites Using the Exponential Cohesive Zone Model Numerical Simulation of the Mode I Fracture of Angle-ply Composites Using the Exponential Cohesive

More information

5 ADVANCED FRACTURE MODELS

5 ADVANCED FRACTURE MODELS Essentially, all models are wrong, but some are useful George E.P. Box, (Box and Draper, 1987) 5 ADVANCED FRACTURE MODELS In the previous chapter it was shown that the MOR parameter cannot be relied upon

More information

Crash and Impact Simulation of Composite Structures by Using CAE Process Chain

Crash and Impact Simulation of Composite Structures by Using CAE Process Chain Crash and Impact Simulation of Composite Structures by Using CAE Process Chain Madhukar Chatiri 1, Thorsten Schütz 2, Anton Matzenmiller 3, Ulrich Stelzmann 1 1 CADFEM GmbH, Grafing/Munich, Germany, mchatiri@cadfem.de

More information

COMPRESSIVE BEHAVIOR OF IMPACT DAMAGED COMPOSITE LAMINATES

COMPRESSIVE BEHAVIOR OF IMPACT DAMAGED COMPOSITE LAMINATES 16 TH INTERNATIONAL CONFERENCE ON COMPOSITE MATERIALS COMPRESSIVE BEHAVIOR OF IMPACT DAMAGED COMPOSITE LAMINATES Hiroshi Suemasu*, Wataru Sasaki**, Yuuichiro Aoki***, Takashi Ishikawa**** *Department of

More information

Stress Dependency on the Ultrasonic Wave Velocity and Attenuation of Fe-C System

Stress Dependency on the Ultrasonic Wave Velocity and Attenuation of Fe-C System Stress Dependency on the Ultrasonic Wave Velocity and Attenuation of Fe-C System S. Takahashi, K. Takahashi To cite this version: S. Takahashi, K. Takahashi. Stress Dependency on the Ultrasonic Wave Velocity

More information

In Situ Ultrasonic NDT of Fracture and Fatigue in Composites

In Situ Ultrasonic NDT of Fracture and Fatigue in Composites ECNDT 26 - Mo.2.6.5 In Situ Ultrasonic NDT of Fracture and Fatigue in Composites I. SOLODOV, K. PFLEIDERER, and G. BUSSE Institute for Polymer Testing and Polymer Science (IKP), Non-destructive Testing

More information

Module III - Macro-mechanics of Lamina. Lecture 23. Macro-Mechanics of Lamina

Module III - Macro-mechanics of Lamina. Lecture 23. Macro-Mechanics of Lamina Module III - Macro-mechanics of Lamina Lecture 23 Macro-Mechanics of Lamina For better understanding of the macromechanics of lamina, the knowledge of the material properties in essential. Therefore, the

More information

Experimental analysis of CFRP laminates subjected to Compression After Impact: the role of impact-induced cracks in failure

Experimental analysis of CFRP laminates subjected to Compression After Impact: the role of impact-induced cracks in failure Experimental analysis of CFRP laminates subjected to Compression After Impact: the role of impact-induced cracks in failure Samuel Rivallant, Christophe Bouvet, Elias Abi Abdallah, Bernhard Broll, Jean-Jacques

More information

FCP Short Course. Ductile and Brittle Fracture. Stephen D. Downing. Mechanical Science and Engineering

FCP Short Course. Ductile and Brittle Fracture. Stephen D. Downing. Mechanical Science and Engineering FCP Short Course Ductile and Brittle Fracture Stephen D. Downing Mechanical Science and Engineering 001-015 University of Illinois Board of Trustees, All Rights Reserved Agenda Limit theorems Plane Stress

More information

DEM modeling of penetration test in static and dynamic conditions

DEM modeling of penetration test in static and dynamic conditions DEM modeling of penetration test in static and dynamic conditions Quoc Anh Tran, Bastien Chevalier, Pierre Breul To cite this version: Quoc Anh Tran, Bastien Chevalier, Pierre Breul. DEM modeling of penetration

More information

SSRG International Journal of Mechanical Engineering (SSRG-IJME) volume1 issue5 September 2014

SSRG International Journal of Mechanical Engineering (SSRG-IJME) volume1 issue5 September 2014 Finite Element Modeling for Delamination Analysis of Double Cantilever Beam Specimen Mohammed Waseem H.S. 1, Kiran Kumar N. 2 1 Post Graduate Student, 2 Asst. Professor Dept. of Mechanical Engineering,

More information

A SELF-INDICATING MODE I INTERLAMINAR TOUGHNESS TEST

A SELF-INDICATING MODE I INTERLAMINAR TOUGHNESS TEST A SELF-INDICATING MODE I INTERLAMINAR TOUGHNESS TEST P. Robinson The Composites Centre, Department of Aeronautics, Imperial College London South Kensington, London, SW7 2AZ, UK p.robinson@imperial.ac.uk

More information

MECE 3321 MECHANICS OF SOLIDS CHAPTER 3

MECE 3321 MECHANICS OF SOLIDS CHAPTER 3 MECE 3321 MECHANICS OF SOLIDS CHAPTER 3 Samantha Ramirez TENSION AND COMPRESSION TESTS Tension and compression tests are used primarily to determine the relationship between σ avg and ε avg in any material.

More information