POLYURETHANE SURFACE TREATMENT ON TWO KINDS OF BASALT FIBER COMPOSITE AND MECHANICAL PROPERTIES COMPARISON
|
|
- Duane Long
- 5 years ago
- Views:
Transcription
1 POLYURETHANE SURFACE TREATMENT ON TWO KINDS OF BASALT FIBER COMPOSITE AND MECHANICAL PROPERTIES COMPARISON Ting YANG 1, Zhenjin CUI 1,Jiahui YANG 2, Yuqiu YANG 2, Hiroyuki HAMADA 1 1 Kyoto Institute of Technology, Matsugasaki, Sakyo-ku, Kyoto JAPAN 2 Donghua University, 2999 North Renmin Road, Songjiang District, Shanghai CHINA ABSTRACT Basalt fiber is a kind of fiber that has excellent mechanical properties and outstanding chemistry stability. So this fiber can be used as the reinforcement of composites. Basalt fiber s cost is much lower than carbon fiber, but its tensile strength is close to carbon fiber. Furthermore, China is rich in basalt mineral resources. In general, basalt fiber has promising development prospect. Nowadays, Basalt fiber is obtained increasing attention worldwide as a kind of promising reinforced fiber in composite field, which has the excellent mechanical properties, chemical resistance, comparative low cost, easily processing and abundance resource. In this paper, two kinds of basalt fabric, bulked yarn woven fabric and normal basalt fiber-woven fabric were used to fabricate composites. In specially, polyurethane dispersion (PUD) was used as the surface modification in composites. Two kinds of treated BFRP and virgins were tested by tensile test and scanning electron microscope (SEM) respectively. Comparison and analysis have been carried out in order to discuss the different influence by PUD surface treatment between two kinds of basalt fabric composites and the change of mechanical property by changing the PUD treatment s pick-up ratio and improved mechanical and thermal properties compared with virgins. 1 INTRODUCTION Fiber can improve composite s mechanical properties because it is strength is higher than resin, but only when fiber and resin have a good combination, composite s mechanical properties can be sufficiently improved, so the interface/interphase in fiber reinforced composites plays a very important role in determining the composite mechanical properties[1-3]. In order to achieve the best composite mechanical properties, many efforts have been made to improve interfacial properties. Fiber surface treatments are often used to create a fiber/matrix interface possessing different characteristics so that the fiber strength is utilized effectively under an optimum bonding. Therefore, it s critical to investigate the influences of surface treatment on composites mechanical properties. There are many surface treatment methods can be used in composites, including silane coupling agent and chemical sizing agent. In this paper, we used one of the chemical sizing agents---the polyurethane (PUD) surface treatment on the basalt fiber-woven fabric. It is considered that polyurethane have a good compatibility with epoxy matrix resin. However, there were few reports focused on its effect as surface treatment. In this research, polyurethane was applied as the surface treatment for basalt fiber reinforced epoxy matrix. The effects on composite s physical and mechanical properties were investigated and analyzed. 1
2 2 FABRICATION OF COMPOSITE 2.1 Material Polyurethane was used as surface treatment agent. Thermosetting bisphenol-a epoxy (JER828) and amine-system harder (JER-W) was applied as the matrix system in a ratio of 100:24. There are two kinds of basalt cloth were used in this study for composite reinforcement. One kind is bulked yarn woven fabric and another is normal basalt fiber woven fabric. Before surface treatment the basalt fiber-woven fabric was wiped out through acetone, and one type of each kind of basalt cloth didn t use PUD treatment wasn t wiped out through acetone. 2.2 Surface treatment of basalt fiber cloth These two kinds of composite reinforcement are used for PUD surface treatment. Prior to molding, the weight of pre-cut basalt cloth was measured as M0 followed by soaking into the different PUD solutions completely for 10 seconds. Clean tissue was used to wipe out the redundant solution on treated basalt cloth surface after taking out from the bath. Subsequently, the treated basalt cloth were put in convection oven for solvent s evaporation for 1.5 hour at 140 C. Finally, the weight of treated basalt cloth Mp was measured again for reference. Evaluation equation for polyurethane particle s pick- up ratio (P%) at unit basalt cloth weight was defined as Eq.1 In this formula, Mp corresponded treated-weight of basalt fiber-woven fabric after drying in oven, M0 corresponded to non-treat weight. The dilution ratio and pick-up ratio was summarized and provided in Table 1 and Table Fabrication of basalt/epoxy composites Hand layup and hot press molding technical was used for the preparation of basalt-cloth reinforced thermosetting epoxy resin matrix composites. Firstly, mixed epoxy and harder were put into the vacuum oven for 20 minutes at 70 in order to increase the liquidity for better mixing, impregnation and getting rid of the entrapped air-bubble. Afterwards, one layer of treated or non-treat fabric with the size of 250mm x 250mm was impregnated into matrix resin within 2-3 minutes to keep the matrix resin s fluidity. And then impregnated composite sheets were cured by hot press machine with applied force of 170 Newton. After being initially cured at 100 for 2 hours, molded panels were post-curved at 175 for 4 hours. The fiber content of composites was provided in Table 3 and Table 4. 2
3 Table 1 Surface treatment dilution ratio (normal basalt fiber woven fabric) Dilution ratio (PUD : Pick-up ratio Distilled) --- (no acetone wash) Untreated 1:7 (acetone wash) 0.31% 1:3 (acetone wash) 0.93% 1:0 (acetone wash) 9.09% Table 2 Surface treatment dilution ratio (bulked yarn basalt fiber woven fabric) Dilution ratio (PUD : Distilled) Pick-up ratio --- (no acetone wash) Untreated --- ( acetone wash) Only wash 1:7 (acetone wash) 1.16% 1:0 (acetone wash) 10.34% 1:3 (no acetone wash) 2.27% Table 3 Fiber volume content of composites (normal basalt fiber woven fabric) Sample Untreated PUD 0.31% PUD 0.93% PUD 9.09% V f 62.4% 69.9% 71.2% 45.7% Table 4 Fiber volume content of composites (bulked yarn basalt fiber woven fabric) Sample Untreated Only wash PUD PUD No wash+pud 1.16% 10.34% 2.27% V f 47.2% 55.2% 49.3% 45.0% 43.2% 3
4 3 EXPERIMENTAL 3.1 Measurement of composites tensile test For each type, 3 pieces of specimens with the geometry of 20mm x 200mm (width X length) were tested and the mean value of the data obtained was taken as the measured result (Gauge length is 100mm). And strain gauges were attached on the center of sample in order to obtain comparative accurate strain data. Tensile test was carried out on an Instron universal testing machine at a speed of 1 mm/min and the test room temperature is Fracture section observation After tensile test, the fracture surface of the tested samples was sputtered with gold for electron conductivity before observation. The cross sectional observations of molded sample after tensile test were carried out by using a field emission scanning electron microscope. The observations were focused on matrix fusion, state of resin impregnation, fiber/matrix interfacial interactions, and fracture morphologies to characterize interfacial bonding properties. 4 RESULTS AND DISCUSSIONS 4.1 Normal basalt fiber woven fabric composites The 4 types tensile stress-strain (S-S) curves for normal basalt fiber woven fabric composites were gathered in the Fig.1. From these curves, it s easily to find that with increasing of PUD pick-up ratio, the mechanical properties of materials achieved significantly improved. According to the Fig.2, it s worthwhile to note that the PUD surface treatment lead to higher Young modulus, but the modulus of 9.09wt% type dropped dramatically. The main reason was considered to the fiber volume content of this material is lower than other three materials. Nevertheless, the modulus is still higher than the sample without a surface treatment. As shown in Fig.3 is the tensile strength comparison among different PUD pick-up ratio, strength become higher when PUD pick-up ratio rose. However, though lower fiber volume content of 9.09wt% type, its tensile strength still enhanced a lot. Fig.1 Tensile stress-strain curves of normal basalts woven fabric composite with different PU treatment 4
5 Fig.2 tensile modulus comparison of normal basalts woven fabric composite with different PU treatment Fig.3 tensile strength comparison of normal basalts woven fabric composite with different PU treatment 4.2 Bulked yarn basalt fiber woven fabric composites The tensile stress-strain (S-S) curves of bulked yarn basalt fiber woven fabric composites were gathered in the Fig.4. From these curves, it s easily to find that with a low PUD pick-up ratio, the mechanical properties of materials is better than washed one, but when PUD pick-up ratio is too high, the strength began to down. The no washed and directly treated by PUD sample s called silane + PUD, and from curves it is showed that with two kinds of surface treatment agent treated, the mechanical properties is not good. As shown in Fig.5 and Fig.6 is the tensile modulus and strength comparison among different PUD pick-up ratio and washed sample, no washed sample, it s worthwhile to note that strength and modulus become higher than no washed sample s with low PUD pick-up ratio, but when PUD pick-up ratio continued to rise, the strength and modulus began to down. 5
6 Fig.4 Tensile stress-strain curves of bulked yarn basalts woven fabric composite with different PU treatment Fig.5 tensile modulus comparison of bulked yarn basalts woven fabric composite with different PU treatment Fig.6 tensile strength comparison of bulked yarn basalts woven fabric composite with different PU treatment 6
7 4.3 The mechanical properties comparison of two kinds of basalt fiber woven fabric composites From these figures, it is easily to find that, for normal basalt fiber woven fabric composites, PUD surface treatment has a great influence for materials mechanical properties, but for bulked yarn basalt fiber woven fabric composites, a good influence is very small. When PUD pick-up ratio is two high, the mechanical properties even become worse than no treatment. The reason lead to this is after PUD surface treatment, cloth will become harder than before, it s not good for fabrication by hand layup. Because a harder surface will lead to more bubbles. For normal basalt cloth, the influence is very small, but for bulked yarn, because it has a loose structure, so if the cloth becomes hard, it is difficult to make bubbles out from composite when fabrication. 4.4 Morphologies of BF/Epoxy composites tensile fracture The SEM images in Fig.7 shows that the surface morphologies of untreated and 0.39wt%, 0.93wt% and 9.09wt% PUD pick-up ratio treated basalt reinforced composites. It was easy to find after surface treatment, the resin on the fiber become more and the adhesion between fiber and resin is better as PUD pick-up ratio rising. And the SEM images in Fig.8 shows that the interface is becoming better with PUD surface treatment than washed by acetone sample. Fig.7 SEM observation of normal basalts woven fabric composite 7
8 Fig.8 SEM observation of bulked yarn basalts woven fabric composite 5 CONCLUSIONS In this research,through the tensile test, the basic mechanics property of two kinds basalt with different PUD pick-up ratio reinforced thermosetting epoxy were investigated. From the analysis of this paper, the following conclusions could be obtained. (1) For normal basalt cloth composite, it s easily to find that with increasing of PUD pick-up ratio, the mechanical properties of materials achieved significantly improved. (2) For bulked yarn basalt cloth composite, it is shows that that with a low PUD pick-up ratio the mechanical properties of materials is better than washed one, but when PUD pick-up ratio is too high, the strength began to down. And from curves it is showed that with two kinds of surface treatment agent treated, the mechanical property is not good. (3) For normal basalt fiber woven fabric composites, PUD surface treatment has a great influence for materials mechanical properties, but for bulked yarn basalt fiber woven fabric composites, a good influence is very small. The reason is bulked yarn cloth has a loose structure, and PUD surface treatment lead the cloth becomes hard, so it is difficult to make bubbles out from composite when fabrication. REFERENCES 1) Wacker G, Bledzki A K, Chate A. Effect of interphase on the transverse Young's modulus of glass/epoxy composites[j]. Composites Part A: Applied Science and Manufacturing, 1998, 29(5): ) James L.Thomason, Glass Fibre Sizings (A Review of the Scientific Literature), August ) J.G. Iglesias, J. Gonzalez-Benito, A.J. Aznar, J. Bravo, and J. Baselga, Journal of Colloid and Interface Science 250, (2002) 4) F.M. Zhao, N. Takeda, Composites: Part A 31 (2000)
Keywords: textile composites, braided fabric, dynamic property, fracture aspect, matrix hybrid
Mechanical Properties and Fracture Behavior of Hybrid Braided Composite Tube Yuki Sasaki, Yoshitaka Tanaka, Akio Ohtani, Asami Nakai, Hiroyuki Hamada Kyoto Institute of Technology Matsugasaki, Sakyo-ku,
More informationFLEXURAL BEHAVIOR OF NEEDLE PUNCH GLASS/JUTE HYBRID MAT COMPOSITES
FLEXURAL BEHAVIOR OF NEEDLE PUNCH GLASS/JUTE HYBRID MAT COMPOSITES Defang Zhao 1, Kai Mao 1, Zhilan Xu 1, Zhiyuan Zhang 1, Yuqiu Yang 2, Hiroyuki Hamada 1 1 Advanced Fibro-Science, Kyoto Institute of Technology,
More informationIMPROVEMENT IN MECHANICAL PROPERTIES OF MODIFIED GRAPHENE/EPOXY NANOCOMPOSITES
18 TH INTERNATIONAL CONFERENCE ON COMPOSITE MATERIALS IMPROVEMENT IN MECHANICAL PROPERTIES OF MODIFIED 1 Introduction Since first successfully separated from graphite by micromechanical cleavage [1], graphene
More informationDAMAGE MECHANICS MODEL FOR OFF-AXIS FATIGUE BEHAVIOR OF UNIDIRECTIONAL CARBON FIBER-REINFORCED COMPOSITES AT ROOM AND HIGH TEMPERATURES
DAMAGE MECHANICS MODEL FOR OFF-AXIS FATIGUE BEHAVIOR OF UNIDIRECTIONAL CARBON FIBER-REINFORCED COMPOSITES AT ROOM AND HIGH TEMPERATURES M. Kawai Institute of Engineering Mechanics University of Tsukuba,
More informationMECHANICAL PROPERTIES OF LIGHTWEIGHT COMPOSITES REINFORCED WITH MICRO GLASS BALLOONS
MEHANIAL PROPERTIES OF LIGHTWEIGHT OMPOSITES REINFORE WITH MIRO GLASS BALLOONS OZAWA, Y. 1, WATANABE, M. 2, KIKUHI, T. 3, YABUKI, K. 4 1 epartment of Human Support System, Fukushima University, 1, Kanayagawa,
More informationMICROMECHANICAL DEFORMATIONS IN PARTICULATE FILLED POLYMERS: THE EFFECT OF ADHESION
MICROMECHANICAL DEFORMATIONS IN PARTICULATE FILLED POLYMERS: THE EFFECT OF ADHESION K. Renner, J. Móczó, B. Pukánszky Laboratory of Plastics and Rubber Technology, Department of Physical Chemistry and
More informationHalloysite. Nanotubes Epoxy. NanoComposites
Halloysite Halloysite Nanotubes Nanotubes Epoxy Epoxy NanoComposites NanoComposites Songshan Zeng Christopher Reyes Songshan Zeng Christopher Reyes Epoxy Chemistry Epoxy systems consist of a liquid epoxy
More informationASPECTS CONCERNING TO THE MECHANICAL PROPERTIES OF THE GLASS / FLAX / EPOXY COMPOSITE MATERIAL
5 th International Conference Advanced Composite Materials Engineering COMAT 2014 16-17 October 2014, Braşov, Romania ASPECTS CONCERNING TO THE MECHANICAL PROPERTIES OF THE GLASS / FLAX / EPOXY COMPOSITE
More informationHydrothermal ageing effects on flexural properties of GFRP composite laminates
Indian Journal of Engineering & Materials Sciences Vol. 20, October 2013, pp. 415-424 Hydrothermal ageing effects on flexural properties of GFRP composite laminates P Sampath Rao* & M Manzoor Hussain Department
More informationSTRESS ANALYSIS OF BONDED JOINTS IN PULTRUDED GRP COMPONENTS
16 TH INTERNATIONAL CONFERENCE ON COMPOSITE MATERIALS STRESS ANALYSIS OF BONDED JOINTS IN PULTRUDED GRP COMPONENTS S.W. Boyd*, J. M. Dulieu-Barton*, O. T. Thomsen**, A.Gherardi* [J.M. Dulieu-Barton]: janice@soton.ac.uk
More informationapplied as UV protective films
Nanocomposite gels via in-situ photoinitiation and disassembly of TiO 2 -Clay composites with polymers applied as UV protective films Chuanan Liao, Qing Wu, Teng Su, Da Zhang, Qingsheng Wu and Qigang Wang*
More informationInfluence of Functionalized Silanes on Mechanical Properties of Wood Sawdust Reinforced ABS Composites
Influence of Functionalized Silanes on Mechanical Properties of Wood Sawdust Reinforced ABS Composites Pichaya Kimchiang Department of Materials Science and Engineering, Faculty of Engineering and Industrial
More informationA SELF-INDICATING MODE I INTERLAMINAR TOUGHNESS TEST
A SELF-INDICATING MODE I INTERLAMINAR TOUGHNESS TEST P. Robinson The Composites Centre, Department of Aeronautics, Imperial College London South Kensington, London, SW7 2AZ, UK p.robinson@imperial.ac.uk
More informationEFFECT OF THERMAL FATIGUE ON INTRALAMINAR CRACKING IN LAMINATES LOADED IN TENSION
EFFECT OF THERMAL FATIGUE ON INTRALAMINAR CRACKING IN LAMINATES LOADED IN TENSION J.Varna and R.Joffe Dept of Applied Physics and Mechanical Engineering Lulea University of Technology, SE 97187, Lulea,
More informationFailure analysis of serial pinned joints in composite materials
Indian Journal of Engineering & Materials Sciences Vol. 18, April 2011, pp. 102-110 Failure analysis of serial pinned joints in composite materials Alaattin Aktaş* Department of Mechanical Engineering,
More informationGB/T / ISO 527-1:1993
Translated English of Chinese Standard: GB/T1040.1-2006 www.chinesestandard.net Sales@ChineseStandard.net GB NATIONAL STANDARD OF THE PEOPLE S REPUBLIC OF CHINA ICS 83.080.01 G 31 GB/T 1040.1-2006 / ISO
More informationStrain Gauges and Accessories
Strain Gauges and Accessories Nurgül Er nurguel.er@hbm.com www.hbm.com 19.03.2008, Folie 1 Hottinger Baldwin Messtechnik GmbH Nurgül Er How to find the right strain gauge a wide range of of strain gauges
More informationChange in physico-mechanical and thermal properties of polyamide / silica nanocomposite film
International Journal of Engineering Research and Development e-issn: 2278-067X, p-issn: 2278-800X, www.ijerd.com Volume 7, Issue 6 (June 2013), PP. 01-05 Change in physico-mechanical and thermal properties
More informationDepartment of Mechanical Engineering, Imperial College London, London SW7 2AZ, UK
5 th Australasian Congress on Applied Mechanics, ACAM 2007 10-12 December 2007, Brisbane, Australia Toughening mechanisms in novel nano-silica epoxy polymers A.J. Kinloch 1, B.B. Johnsen 1, R.D. Mohammed
More informationNano-materials in Polymer Composites for High-Volume Applications
Nano-materials in Polymer Composites for High-Volume Applications Kyriaki Kalaitzidou Associate Professor G.W. Woodruff School of Mechanical Engineering and School of Materials Science and Engineering
More informationRHEOLOGICAL CHARACTERIZATION OF THERMOSETTING RES- IN SYSTEM WITH THERMOPLASTIC FUNCTIONAL LAYER
21 st International Conference on Composite Materials Xi an, 20-25 th August 2017 RHEOLOGICAL CHARACTERIZATION OF THERMOSETTING RES- IN SYSTEM WITH THERMOPLASTIC FUNCTIONAL LAYER W. Surjoseputro 1, G.
More informationThermal Properties Of Epoxy Based Adhesive Reinforced With
Thermal Properties Of Epoxy Based Adhesive Reinforced With We have made it easy for you to find a PDF Ebooks without any digging. And by having access to our ebooks online or by storing it on your computer,
More informationEVALUATION OF GLASS FIBER/EPOXY INTERFACIAL STRENGTH USING A CRUCIFORM SPECIMEN
6 TH INTERNATIONAL CONFERENCE ON COMPOSITE MATERIALS EVALUATION OF GLASS FIBER/EPOXY INTERFACIAL STRENGTH USING A CRUCIFORM SPECIMEN Shinji Ogihara*, Yoriaki Sakamoto ** and Hajime Kato ** *Department
More informationCitation Journal of Adhesion, 81(6):
Bonding Properties of Liquid Crys Title esins Having Different Phase Stru int version) HARADA, Miyuki, WATANABE, Yutaka, Author(s) u Citation Journal of Adhesion, 81(6): 587-5 Issue Date 2005 URL http://hdl.handle.net/10112/6951
More informationSHEAR CAPACITY OF REINFORCED CONCRETE COLUMNS RETROFITTED WITH VERY FLEXIBLE FIBER REINFORCED POLYMER WITH VERY LOW YOUNG S MODULUS
SHEAR CAPACITY OF REINFORCED CONCRETE COLUMNS RETROFITTED WITH VERY FLEXILE FIER REINFORCED POLYMER WITH VERY LOW YOUNG S MODULUS Hu Shaoqing Supervisor: Susumu KONO ** MEE8165 ASTRACT FRP with low Young
More informationNon-conventional Glass fiber NCF composites with thermoset and thermoplastic matrices. F Talence, France Le Cheylard, France
20 th International Conference on Composite Materials Copenhagen, 19-24th July 2015 Non-conventional Glass fiber NCF composites with thermoset and thermoplastic matrices. Thierry Lorriot 1, Jalal El Yagoubi
More informationState Key Laboratory of Organic-Inorganic Composites, Beijing University of Chemical. Technology, Beijing , China
Improving interfacial and mechanical properties of T800 carbon fiber reinforced itaconic acid-based epoxy resin composites by introducing cellulose nanomaterials onto the surface of fibers Lu kangyi a,
More informationFibre-matrix interfacial adhesion on composite properties in natural fibre composites
Fibre-matrix interfacial adhesion on composite properties in natural fibre composites Le Quan Ngoc TRAN 1,2,a, Xiaowen YUAN 1,b*, Debes BHATTACHARYYA 3,c, Carlos A. FUENTES 2,d, Aart Willem VAN VUURE 2,e,
More informationTensile Properties of Thermoplastic-Laminated Composites Based on a Polypropylene Matrix Reinforced with Continuous Twaron Fibers
Tensile Properties of Thermoplastic-Laminated Composites Based on a Polypropylene Matrix Reinforced with Continuous Twaron Fibers J. L. MENA-TUN, P. I. GONZALEZ-CHI Centro de Investigación Científica de
More informationA Transparent Perovskite Light Emitting Touch-
Supporting Information for A Transparent Perovskite Light Emitting Touch- Responsive Device Shu-Yu Chou, Rujun Ma, Yunfei Li,, Fangchao Zhao, Kwing Tong, Zhibin Yu, and Qibing Pei*, Department of Materials
More informationCHEM-C2410: Materials Science from Microstructures to Properties Composites: basic principles
CHEM-C2410: Materials Science from Microstructures to Properties Composites: basic principles Mark Hughes 14 th March 2017 Today s learning outcomes To understand the role of reinforcement, matrix and
More informationMODELLING INTERACTION EFFECT OF NANOSILICA PARTICLES ON NANOSILICA/EPOXY COMPOSITE STIFFNESS
MODELLING INTERACTION EFFECT OF NANOSILICA PARTICLES ON NANOSILICA/EPOXY COMPOSITE STIFFNESS Mulyadi a*, I. Gitman a, C. Pinna a, C. Soutis b a Department of Mechanical Engineering, The University of Sheffield,
More informationThermal and mechanical properties of several phthalonitrile resin system
Thermal and mechanical properties of several phthalonitrile resin system Heng Zhou, Feng Liu, Yuehai Li, Tong Zhao* Institute of Chemistry, Chinese Academy of Sciences, Beijing, 100190, China Abstract:An
More informationTHE ROLE OF THE EPOXY RESIN: CURING AGENT RATIO ON COMPOSITE INTERFACIAL STRENGTH AND THERMAL PERFORMANCE
Munich, Germany, 26-30 th June 2016 1 THE ROLE OF THE EPOXY RESIN: CURING AGENT RATIO ON COMPOSITE INTERFACIAL STRENGTH AND THERMAL PERFORMANCE Ross F. Minty 1, James L. Thomason 2 and Liu Yang 3 1 University
More informationSingle fibre tensile testing
Single fibre tensile testing Justine Beauson Section of Composites and Materials Mechanics, Department of Wind Energy Introduction Fibre properties Fibre orientation Matrix properties Mechanical performance
More informationA NEW GENERATION OF CONSTRUCTION MATERIALS: CARBON NANOTUBES INCORPORATED TO CONCRETE AND POLYMERIC MATRIX
A NEW GENERATION OF CONSTRUCTION MATERIALS: CARBON NANOTUBES INCORPORATED TO CONCRETE AND POLYMERIC MATRIX Javier Grávalos, Juan Manuel Mieres and Santiago González R&D Department, NECSO Entrecanales Cubiertas
More informationAminopropyltrimethoxysilane-Functionalized Boron Nitride. Nanotube Based Epoxy Nanocomposites with Simultaneous High
Electronic Supplementary Material (ESI) for Journal of Materials Chemistry A. This journal is The Royal Society of Chemistry 2018 Electronic Supplementary Information (ESI) Aminopropyltrimethoxysilane-Functionalized
More informationIN VITRO DEGRADATION AND EROSION OF DEGRADABLE LACTATE SEGMENTED POLYURETHANES
Journal of Optoelectronics and Advanced Materials Vol. 7, No. 6, December 2005, p. 2803-2808 IN VITRO DEGRADATION AND EROSION OF DEGRADABLE LACTATE SEGMENTED POLYURETHANES V. Melnig *, L. Obreja, A. Garlea
More informationThermal Properties Of Epoxy Based Adhesive Reinforced With
Thermal Properties Of Epoxy Based Adhesive Reinforced With We have made it easy for you to find a PDF Ebooks without any digging. And by having access to our ebooks online or by storing it on your computer,
More informationPREPARATION OF CARBON FIBER SIZING AGENT AND CHARACTERIZATION OF ITS PROPERTIES Kunming Yang 1, Peng Li 2, Xiaoping Yang
21 st International onference on omposite Materials Xi an, 20-25 th August 2017 PREPARATIN F ARBN FIBER SIZING AGENT AND HARATERIZATIN F ITS PRPERTIES State Key Laboratory of rganic-inorganic omposites,
More informationComposite Materials Research Laboratory, State University of New York at Buffalo, Buffalo, NY , USA
Composite Interfaces, Vol. 7, No. 4, pp. 257 275 (2000) VSP 2000. Discontinuous surface-treated submicron-diameter carbon filaments as an interlaminar filler in carbon fiber polymer-matrix composites for
More informationInfluence of Nanoparticle s Surface Composition on the Properties of Epoxide Based Adhesives
Influence of Nanoparticle s Surface Composition on the Properties of Epoxide Based Adhesives A. Hartwig, J. Trautmann, M. Sebald har@ifam.fraunhofer.de EUADH 2008 - xford September 2008 utline Introduction
More informationMATERIALS SCIENCE POLYMERS
POLYMERS 1) Types of Polymer (a) Plastic Possibly the largest number of different polymeric materials come under the plastic classification. Polyethylene, polypropylene, polyvinyl chloride, polystyrene,
More informationNOVEL PHENYLETHYNYL IMIDE SILANES AS COUPLING AGENTS FOR TITANIUM ALLOY
NOVEL PHENYLETHYNYL IMIDE SILANES AS OUPLING AGENTS FOR TITANIUM ALLOY. Park*, S. E. Lowther, J. G. Smith Jr., J. W. onnell, P. M. Hergenrother, and T. L. St. lair *National Research ouncil, omposites
More informationInteractions Between Surface Treated Ultrafine Mineral Filler and Silicone Rubber Matrix
Interactions Between Surface Treated Ultrafine Filler and Silicone Rubber Matrix Interactions Between Surface Treated Ultrafine Filler and Silicone Rubber Matrix Jihuai Wu*, Zhen Shen, Congrong Wei, Yike
More informationCompression Molding of Green Composite made of Wood Shavings
Compression Molding of Green Composite made of Wood Shavings S. Nonaka, T. Kimura Division of Fibro Science, Kyoto Institute of Technology Kyoto, 606-8585, Japan m8651033@edu.kit.ac.jp SUMMARY The purpose
More informationPolymer engineering syllabus (BSc)
Polymer engineering syllabus (BSc) First semester Math 1 Physics 1 Physics 1 lab General chemistry General chemistry lab workshop Second semester Math 2 Physics 2 Organic chemistry 1 Organic chemistry
More informationDRAPING SIMULATION. Recent achievements and future trends. Dr. Sylvain Bel LGCIE University Lyon 1
DRAPING SIMULATION Recent achievements and future trends 1 Dr. Sylvain Bel LGCIE University Lyon 1 2 DRAPING SIMULATION Why? How? What? DRAPING SIMULATION WHY? Clamps Punch Fabric Die 1 2 Resin 3 4 Fig.
More informationA Facile Method of Synthesizing Size-controlled Hollow Cyanoacrylate Nanoparticles for Transparent Superhydrophobic/Oleophobic Surfaces
Electronic Supplementary Material (ESI) for RSC Advances. This journal is The Royal Society of Chemistry 2016 Supplementary Information A Facile Method of Synthesizing Size-controlled Hollow Cyanoacrylate
More informationElectronic Supplementary Information for New Journal of Chemistry
Electronic Supplementary Material (ESI) for New Journal of Chemistry. This journal is The Royal Society of Chemistry and the Centre National de la Recherche Scientifique 2015 Electronic Supplementary Information
More informationOPTIMAL FIBER PLACEMENT INCLUDING EFFECTS OF EMBROIDERY
THE 19 TH INTERNATIONAL CONFERENCE ON COMPOSITE MATERIALS OPTIMAL FIBER PLACEMENT INCLUDING EFFECTS OF EMBROIDERY T. Nishida 1 T. Ieda 2 * A. Senba 2 1 Department of Aerospace Engineering Nagoya University
More informationTeorie netkaných textilií
Property [ ] Property [ ] 5/28/2013 Teorie netkaných textilií Composites, nanocomposites Dr. László Mészáros Budapest University of Technology and Economics Faculty of Mechanical Engineering Department
More informationUltra-stretchable, bio-inspired ionic skins enable working stably in various harsh environments
Electronic Supplementary Material (ESI) for Journal of Materials Chemistry A. This journal is The Royal Society of Chemistry 2018 Electronic Supplementary Information (ESI) for Journal of Materials Chemistry
More informationMechanical Properties of Epoxy/Al 2 O 3 Nanocomposites
Mechanical Properties of Epoxy/Al 2 O 3 Nanocomposites M. J. Kadhim*, A. K. Abdullah, I. A. Al-Ajaj, and A. S. Khalil Department of Physics, College of Science, Baghdad University, Baghdad, Iraq. Abstract
More informationSHEAR TENSION COUPLING IN BIAXIAL BIAS EXTENSION TESTS
SHER TENSION COUPLING IN IXIL IS EXTENSION TESTS P. Harrison *, P. Potluri Department of Mechanical Engineering, James Watt uilding (South), University of Glasgow, Glasgow G 8QQ, U.K. p.harrison@mech.gla.ac.uk
More informationA CRITERION OF TENSILE FAILURE FOR HYPERELASTIC MATERIALS AND ITS APPLICATION TO VISCOELASTIC-VISCOPLASTIC MATERIALS
MTS ADHESIVES PROGRAMME 1996-1999 PERFORMANCE OF ADHESIVE JOINTS Project: PAJ1; Failure Criteria and their Application to Visco-Elastic/Visco-Plastic Materials Report 2 A CRITERION OF TENSILE FAILURE FOR
More informationDEVELOPMENT OF THERMOELASTIC STRESS ANALYSIS AS A NON-DESTRUCTIVE EVALUATION TOOL
DEVELOPMENT OF THERMOELASTIC STRESS ANALYSIS AS A NON-DESTRUCTIVE EVALUATION TOOL S. Quinn*, R.K. Fruehmann and J.M. Dulieu-Barton School of Engineering Sciences University of Southampton Southampton SO17
More information2 Experiment of GFRP bolt
16 TH INTERNATIONAL CONFERENCE ON COMPOSITE MATERIALS FATIGUE LIFE EVALUATION OF BOLT MADE OF WOVEN FABRIC FRP Takeshi INOUE*, Hiroaki NAKAI**, Tetsusei KURASHIKI**, Masaru ZAKO**, Yuji KOMETANI*** *Graduate
More informationImprovement of the chemical, thermal, mechanical and morphological properties of polyethylene terephthalate graphene particle composites
Bull. Mater. Sci. (2018) 41:67 https://doi.org/10.1007/s12034-018-1587-1 Indian Academy of Sciences Improvement of the chemical, thermal, mechanical and morphological properties of polyethylene terephthalate
More informationComposite Materials. Fibre-Matrix Interfaces. There is nothing there really except the two of you (or the fiber and matrix).
Composite Materials Fibre-Matrix Interfaces There is nothing there really except the two of you (or the fiber and matrix). Composite Parameters Fibre properties Composite Interfaces Matrix properties Fibre
More informationSYNTHESIS OF AN AZO DYE revisited (1 or 2 credits)
SYNTHESIS OF AN AZO DYE revisited (1 or 2 credits) This lab you can revisit the fist experiment of this quarter and synthesize more azo dyes of your choice. The old procedure is given below followed by
More informationMicrowave absorbing properties of activated carbon fibre polymer composites
Bull. Mater. Sci., Vol. 34, No. 1, February 2011, pp. 75 79. c Indian Academy of Sciences. Microwave absorbing properties of activated carbon fibre polymer composites TIANCHUN ZOU, NAIQIN ZHAO, CHUNSHENG
More informationINFLUENCE OF INTERPHASE MATERIAL PROPERTY GRADIENTS ON THE MICROMECHANICS OF FIBROUS THERMOSETTING-MATRIX COMPOSITES
INFLUENCE OF INTERPHASE MATERIAL PROPERTY GRADIENTS ON THE MICROMECHANICS OF FIBROUS THERMOSETTING-MATRIX COMPOSITES F. Yang and R. Pitchumani* Composites Processing Laboratory Department of Mechanical
More informationPrediction of Elastic Constants on 3D Four-directional Braided
Prediction of Elastic Constants on 3D Four-directional Braided Composites Prediction of Elastic Constants on 3D Four-directional Braided Composites Liang Dao Zhou 1,2,* and Zhuo Zhuang 1 1 School of Aerospace,
More informationALIGNED FLAX FIBRE/POLYLACTATE COMPOSITES A MATERIALS MODEL SYSTEM TO SHOW THE POTENTIAL OF BIOCOMPOSITES IN ENGINEERING APPLICATIONS
ALIGNED FLAX FIBRE/POLYLACTATE COMPOSITES A MATERIALS MODEL SYSTEM TO SHOW THE POTENTIAL OF BIOCOMPOSITES IN ENGINEERING APPLICATIONS Bo Madsen 1, Hans Lilholt 1, Anders Thygesen 2, Elaine Arnold 3, Brendon
More informationINFLUENCE OF CLAY ON MECHANICAL PROPERTIES OF POLYVINYL(ALCOHOL)/ MONTMORILLONITE MEMBRANES
INFLUENCE OF CLAY ON MECHANICAL PROPERTIES OF POLYVINYL(ALCOHOL)/ MONTMORILLONITE MEMBRANES Maria C. Carrera 1*, Eleonora Erdmann 1, Hugo A. Destéfanis 1 Marcos L. Dias 2, Victor J. R. R. Pita 2 1 Instituto
More informationInternational Journal of Pure and Applied Sciences and Technology
Int. J. Pure Appl. Sci. Technol., 17(2) (2013), pp. 36-44 International Journal of Pure and Applied Sciences and Technology ISSN 2229-6107 Available online at www.ijopaasat.in Research Paper Polyamide/Clay
More informationAdhesion Improvement on Smooth Cu Wiring Surfaces of Printed Circuit Boards
[Technical Paper] Adhesion Improvement on Smooth Cu Wiring Surfaces of Printed Circuit Boards Motoaki Tani*, Shinya Sasaki*, and Keisuke Uenishi** *Next-Generation Manufacturing Technologies Research Center,
More informationIndentation Energy in Bending of Sandwich Beams with Composite Laminated Faces and Foam Core
Indentation Energy in Bending of Sandwich Beams with Composite Laminated Faces and Foam Core M. SADIGHI, H. POURIAYEVALI, and M. SAADATI Dept. of Mechanical Engineering, Amirkabir University of Tech, Tehran,
More informationRevised. Degradation Behavior of Epoxy Lining Materials under. Corrosive Conditions Intended for Biomass Gas Plant
Revised Degradation Behavior of Epoxy Lining Materials under Corrosive Conditions Intended for Biomass Gas Plant Tomoya YUI 1*, Aysha SHARMIN 1, Masatoshi KUBOUCHI 1*, Saiko AOKI 1, Takashi NABEI 2 1 Tokyo
More informationOptimization of delamination factor in drilling of carbon fiber filled compression molded GFRP composite
Optimization of delamination in drilling of carbon fiber filled compression molded GFRP composite Anurag Gupta 1 Ajay Singh Verma Sandeep Chhabra Ranjeet Kumar Assistant professor, Department of Mechanical
More informationSOME RESEARCH ON FINITE ELEMENT ANALYSIS OF COMPOSITE MATERIALS
Mechanical Testing and Diagnosis ISSN 2247 9635, 2012 (II), Volume 3, 79-85 SOME RESEARCH ON FINITE ELEMENT ANALYSIS OF COMPOSITE MATERIALS Valeriu DULGHERU, Viorel BOSTAN, Marin GUŢU Technical University
More informationControlled self-assembly of graphene oxide on a remote aluminum foil
Supplementary Information Controlled self-assembly of graphene oxide on a remote aluminum foil Kai Feng, Yewen Cao and Peiyi Wu* State key Laboratory of Molecular Engineering of Polymers, Department of
More information3D Compression Molding
Autodesk Simulation Moldflow Insight 2014 3D Compression Molding Executive summary In this work, the simulation results from a program developed for the three-dimensional analysis of compression molding
More informationBen W. Kim 1 and John A. Nairn 2
J. Materials Science, submitted (2002) Author prepared reprint Experimental Verification of the Effects of Friction and Residual Stress on the Analysis of Interfacial Debonding and Toughness in Single
More informationBIAS EXTENSION TEST STANDARD
BIAS EXTENSION TEST STANDARD Xiongqi Peng and Jian Cao Advanced Materials Processing Laboratory Department of Mechanical Engineering Northwestern University Evanston, IL August 2003 For Internal Use 1.
More informationSynthesis and Properties of Polymethyl Methacrylate/Nanodiamond Composite Material
International Conference on Electromechanical Control Technology and Transportation (ICECTT 2015) Synthesis and Properties of Polymethyl Methacrylate/Nanodiamond Composite Material Lifang Ma 1,2,a, Guoliang
More informationEFFECTS OF FIBRE SIZING ON DAMAGE DEVELOPMENT IN UNIDIRECTIONAL GLASS/EPOXY COMPOSITES
EFFECTS OF FIBRE SIZING ON DAMAGE DEVELOPMENT IN UNIDIRECTIONAL GLASS/EPOXY COMPOSITES M. Kharrat 1,3, T. Monlèon 1,2, L. Carpentier 3, A. Chateauminois 1 and M.L. Maspoch 2 1 Laboratoire d Ingéniérie
More informationDecomposition Mechanism of Epoxy Resin in Nitric Acid for Recycling
Decomposition Mechanism of Epoxy Resin in Nitric Acid for Recycling Weirong Dang I, Masatoshi Kubouchi I, Shurou Yamamoto I, Hideki Sembokuya I, Kazuyoshi Arai and Ken Tsuda Department of Chemical Engineering,
More informationOut life 30 days at 70 F (21 C) Shelf life 6 months at 40 F (4 C) 12 months at 0 F (-18 C)
4708 250-300 F (120-150 C) High T g Epoxy Resin System Typical applications General aviation Aerospace Industrial Sporting goods Out life 30 days at 70 F (21 C) Shelf life 6 months at 40 F (4 C) 12 months
More informationIntroduction Wood K plus. Motivation. Results. Conclusions. J. Leßlhumer 1, J. Sinic 1, M. Reif 1, A. Haider 1, D. Cascorbi 2
1 st Workshop - Basics for Chemistry of Wood Surface Modification April 25-26, 2012, Kuchl/Salzburg, Austria Surface modification of WPC products to improve bonding strength J. Leßlhumer 1, J. Sinic 1,
More informationDynasylan SIVO 110. Description. Product Information. SIVO SOL Technology for coating systems
Dynasylan SIVO 110 +49-69-218-5656 SIVO SOL Technology for coating systems Description Dynasylan SIVO 110 resembles a multifunctional, basically VOC-free, water-borne sol-gel system. It is composed of
More informationAdvanced General Aviation Transport Experiments
Advanced General Aviation Transport Experiments B-Basis Design Allowables for Wet Layup / Field Repair Fiber Reinforced Composite Material Systems 3K Plain Weave Carbon Cloth / MGS 418 AGATE-WP3.3-033051-115
More informationSynolite 1408-P-1. Product data. DSM Composite Resins
Synolite 8-P- Chemical/physical nature Synolite 8-P- is a low viscous, pre-accelerated, promoted, thixotropic, medium reactive unsaturated polyester resin based on orthophthalic acid. An LSE additive and
More informationMechanical Behaviors Study of Epoxy Resins Reinforced with Nano-SiO 2 Particles Jian Zheng, Xiong Chen, Deng Jia, Xin Tong
International Conference on Materials, Environmental and Biological Engineering (MEBE 2015) Mechanical Behaviors Study of Epoxy Resins Reinforced with Nano-SiO 2 Particles Jian Zheng, Xiong Chen, Deng
More informationSIMULTANEOUS MEASUREMENT OF APPARENT THERMAL DIFFUSIVITY AND DISTORTION OF COMPOSITES AT HIGH TEMPERATURE
SIMULTANEOUS MEASUREMENT OF APPARENT THERMAL DIFFUSIVITY AND DISTORTION OF COMPOSITES AT HIGH TEMPERATURE V. Urso Miano, G.A. Jones and A. G. Gibson School of Mechanical & Systems Engineering, Newcastle
More informationProject PAJ2 Dynamic Performance of Adhesively Bonded Joints. Report No. 3 August Proposed Draft for the Revision of ISO
NPL Report CMMT(A)81 Project PAJ2 Dynamic Performance of Adhesively Bonded Joints Report No. 3 August 1997 Proposed Draft for the Revision of ISO 11003-2 Adhesives - Determination of Shear Behaviour of
More informationThermoset Resins and Their Composites
ACCE 22, September 13-14, 14, 22 Bio-based Thermoset Resins and Their Composites M. Misra,, L. T. Drzal, A. K. Mohanty,, L. Belchler, G. Mehta,, J-P. J Latere Dwan sisa Michigan State University 21 Engineering
More informationNondestructive Testing and Performance Prediction of Soybean Stalk Board
Nondestructive Testing and Performance Prediction of Soybean Stalk Board Wei Lu, a Jia Yao, a, * Xiangdong Liu, a Lili Ma, a and Yuhua Wang b Crop straw-reinforced industrial materials can be effectively
More informationSYNTHESIS OF AN AZO DYE revisited (1 or 2 credits)
SYNTHESIS OF AN AZO DYE revisited (1 or 2 credits) This lab you can revisit the fist experiment of this quarter and synthesize more azo dyes of your choice. The old procedure is given below followed by
More informationEffects of Basalt Fibres on Mechanical Properties of Concrete
Effects of Basalt Fibres on Mechanical Properties of Concrete A. M. El-Gelani 1, C.M. High 2, S. H. Rizkalla 3 and E. A. Abdalla 4 1,4 University of Tripoli, Civil Engineering Department, Tripoli, Libya
More informationflame retardant vinyl ester resin
Abstract Research Journal of Material Sciences ISSN 30 6055 Vol. 5(), 7-, February (07) Studies on flame retardant vinyl ester resin Patel R.H. * and Sevkani V.R. Department of Materials Science, Sardar
More informationMultilayer Wiring Technology with Grinding Planarization of Dielectric Layer and Via Posts
Tani et al.: Multilayer Wiring Technology with Grinding Planarization (1/6) [Technical Paper] Multilayer Wiring Technology with Grinding Planarization of Dielectric Layer and Via Posts Motoaki Tani, Kanae
More informationStudy on the heat resistance and mechanical properties of polytriazole resin. matrix composite influenced by graphene oxide
21 st International Conference on Composite Materials Xi an, 20-25 th August 2017 Study on the heat resistance and mechanical properties of polytriazole resin matrix composite influenced by graphene oxide
More informationEpoxy resins for electrotechnical applications
Epoxy resins for electrotechnical applications Epoxy resins for electrotechnical applications ELANTAS Europa offers a complete range of of products that can be used in in electrical engineering for the
More informationNUMERICAL MODELLING OF COMPOSITE PIN- JOINTS AND EXPERIMENTAL VALIDATION
NUMERICAL MODELLING OF COMPOSITE PIN- JOINTS AND EXPERIMENTAL VALIDATION Fabrice PIERRON*, François CERISIER*, and Michel GRÉDIAC** * SMS/ Département Mécanique et Matériaux, École Nationale Supérieure
More informationTolonate X FLO 100. Bio-based & low viscosity aliphatic isocyanate polymer
Tolonate X FLO 100 Bio-based & low viscosity aliphatic isocyanate polymer Discover the of Tolonate TM X FLO 100 Tolonate X FLO 100 is a new, partially bio-based, solvent-free and low viscosity aliphatic
More informationEffects of Chemical Solutions on the Toughness of Polypropylene
Polymer Journal, Vol. 37, No. 2, pp. 877 886 (25) Effects of Chemical Solutions on the Toughness of Polypropylene Hirokazu WADA, y Yasuo SUZUKI, Kenzo OKAMOTO, and Masaru ISHIKAWA Department of Polymer
More informationAvailable online at ScienceDirect. Procedia Engineering 105 (2015 )
Available online at www.sciencedirect.com ScienceDirect Procedia Engineering 105 (2015 ) 829 834 6th BSME International Conference on Thermal Engineering (ICTE 2014) Strain energy release rate and mode-i
More informationISSN: ISO 9001:2008 Certified International Journal of Engineering Science and Innovative Technology (IJESIT) Volume 2, Issue 4, July 2013
Delamination Studies in Fibre-Reinforced Polymer Composites K.Kantha Rao, Dr P. Shailesh, K. Vijay Kumar 1 Associate Professor, Narasimha Reddy Engineering College Hyderabad. 2 Professor, St. Peter s Engineering
More information